Introduction

Superconductivity and magnetism are two long range order phenomena which do not seem to be compatible at first sight. In spite of this perspective, the coexistence of both cooperative effects in the same material was foreseen and studied long time ago1. A pioneering experimental work was reported by Matthias et al.2. Taking into account these results, Anderson and Shul3 found the conditions for spin alignment in the superconducting state in the case of rare earth magnetic moments diluted in a superconductor. Years later, long range order magnetism and superconductivity were found in ternary rare earth compounds4. Magnetism with reentrant superconductivity behavior5, as well as ferromagnetism and superconductivity coexistence6 without reentrant behavior were reported in these ternary rare earth crystals. After the finding of these pioneer compounds many materials have been found where both cooperative phenomena are present. Very different compounds can be quoted, some examples are RuSr2GdCu2O8 and UGe27,8. Nowadays, the most interesting finding is the iron-based compound family9, as well as the coexistence and emergence of both phenomena in very peculiar sites, as for example interfaces10. In this scenario of interplay and coexistence between magnetism and superconductivity, another remarkable advance was foreseen by Matthias and Suhl11. These authors suggested that the superconducting regions extend only through the thicknesses of the ferromagnetic domain walls. This interesting idea was worked out and expanded by Tachiki et al.12, Kulic13 and Buzdin et al.14,15. These authors found that the crucial parameter is the superconducting coherence length; they concluded that the comparison between this length and the domain wall or the domain size precludes or enhances the coexistence of superconductivity and magnetism.

Eventually, over the years the interplay between magnetism and superconductivity has evolved from competition to collaboration. The role played by magnetism in promoting superconductivity has called the attention of many researchers. In this way, the new scenario opened by magnetic/superconducting nanostructured hybrids has allowed tailoring superconducting properties almost at will by using the appropriate design of the nanomagnets. A simple example is to use applied magnetic fields to compensate, at the nanoscale, the stray fields coming from the nanomagnets. In this way, external magnetic fields promote superconductivity instead of preventing it16,17,18 giving rise to the so-called magnetic-field-induced superconductivity. The combination of nanomagnets in contact with superconductors has generated a complete and mature field where researchers have been able to obtain remarkable achievements; a couple of examples could be control of vortex motion19,20,21,22, and vortex-antivortex interplay23,24,25. In this work, we have fabricated arrays of nanomagnets embedded in superconducting films and we have taken the opposite approach, we have explored whether or not we can obtain information of the magnetic states of nanomagnets using the motion of superconducting vortices as a probe. Belkin et al.26 have reported the influence of magnetic domain structure on vortex dynamics. In the present work, we are going one step further and we show that vortex lattice motion detects subtle differences linked to the strengths and configurations of the stray magnetic fields generated by nanomagnets. The increased pinning is due to weakened superconductivity. This weakened superconductivity is due to superconducting currents induced by the local magnetic field gradients at the domain walls and edges of nanomagnets26,27.

In nanomagnets, the domain sizes are usually governed by magnetostatic effects related to geometry and size of the magnetic nanoelement28. This gives rise to simple magnetic configurations, such as single domain, vortex state, etc, in which the domain size is comparable to the patterned element size. Stray fields created by each magnetic element and the order in the periodic array can be used to tune periodic pinning effects in the superconducting/magnetic hybrid29. An interesting but unexplored option would be to reduce magnetic domains below typical patterned element size (100 nm to 1000 nm). This can be done with materials which exhibit perpendicular magnetic anisotropy (PMA). Domain size can be varied from a few nm to several μm with a large variety of geometrical configurations (parallel stripes, labyrinths, bubbles, single domain …) depending on the interplay between material parameters (saturation magnetization MS, anisotropy KN and disorder), element geometry (thickness and lateral dimensions) and magnetic history22,23,24,25,26,27,28,29,30. In a film, domain configuration is governed by Q, the ratio of perpendicular magnetic anisotropy KN to magnetostatic energy Q = 2KN0MS2 and by the effect of disorder on nucleation and propagation processes of reversed domains31. High Q values (of the order 2 to 10) can be found, for example, in Co/Pd multilayers32,33,34,35 with high out-of-plane remanence (MR ≈ MS) and large domain sizes during magnetization reversal36. A smaller domain size regime can be accessed in lower Q materials such as NdCo amorphous alloys (Q in the 0.1–1.5 range, depending on temperature and composition)37,38. These films display reduced remanent magnetization (MR below 0.1 MS) characteristic of stripe domain patterns, with very small domain sizes39. In summary, Co/Pd multilayers and (NdCo) films exhibit very different magnetic scenarios, since the former shows well defined and strong perpendicular magnetic anisotropy (high values of Q) and large domain sizes, and the latter shows a weak perpendicular magnetic anisotropy (low values of Q) and small domain sizes. Therefore, we are dealing with two limit situations: a) stray fields with high strengths and covering large and well defined areas and b) stray fields with low strengths and covering small and disordered areas.

The paper is organized as follows: In the results section, first we present the experimental results of sample A (Nb film/Co-Pd multilayer) and then the experimental results of sample B (Nb film/NdCo alloy). In the discussion section we analyze the experimental data for both samples. This discussion section is followed by a long summary and conclusions section where we present the most relevant outcomes. In the last section the fabrication and experimental methods are explained.

Results

Sample A (Nb film/Co-Pd multilayer)

The array of Co/Pd triangles has been prepared in two different magnetic configurations. First, the sample has been measured in the “as grown” state, with remanence MR ≈ 0. This demagnetized state is reached in the usual way by minor hysteresis loops decreasing the strength of the applied magnetic field up to zero. A Magnetic Force Microscopy (MFM) image of the as grown state (Fig. 1(a)) shows that each triangle is broken up into a small number of black/white contrast regions (two or three) that correspond to large domains with opposite out-of-plane magnetization of sizes similar to the triangle dimensions very similar to multidomain states observed in CoPt dots40. Domain configuration is uncorrelated from triangle to triangle, indicative of a disordered magnetic state. This will be labelled as “Sample A - as grown”. Second, the sample has been saturated with a strong out-of-plane Hz magnetic field (30 kOe) and brought down to remanence (labelled as “sample A – Hz remanence”). In this case, a more ordered configuration appears (see the remanent MFM image in Fig. 1(b) In this image magnetic contrast is weaker, corresponding to positive Mz orientation in most triangles. A broad a white contrast region can be seen at the triangle centers, corresponding to a mostly out-of-plane magnetization state28,40. The out-of-plane hysteresis loop of the patterned array of Co/Pd triangles presents a high value of the remanent magnetization MR = 0.85 MS, in agreement with the MFM characterization.

Figure 1
figure 1

MFM image of Co/Pd triangles at 300 K: (a) as grown; (b) at remanence after out-of-plane saturation.

Material properties of Co/Pd multilayers are only weakly temperature dependent below room temperature (both saturation magnetization41 and perpendicular magnetic anisotropy42). Thus, taking into account that the magnetic configuration of the Co/Pd triangles depends on the interplay between magnetostatic energy (given by shape and saturation magnetization), exchange and anisotropy energies that are only weakly temperature dependent, we can assume that room temperature magnetic configuration does not change significantly as temperature goes down to 4 K. Therefore, given the weak temperature dependence of the magnetic properties of Co/Pd multilayers41,42, these magnetic configurations stay invariant as the temperature is lowered down to 4 K in order to study the behavior of the hybrid superconducting/magnetic system.

Magnetotransport measurements have been carried out in the hybrid sample Nb film on top of the array of triangles made with Co-Pd multilayers, at constant temperature close to the superconducting critical temperature, where the effect of the periodic pinning due to the array overcomes the random intrinsic pinning and the resistance minima appear43,44,45 (see methods). Figure 2 shows the experimental results in the sample A - as grown. Remarkably, the resistance minima are absent. Figure 3 shows the magnetoresistance in the case sample A – Hz remanence. Two experimental facts can be underlined: i) sharp and well-defined resistance minima appear (notice the log scale in Y-axis), evenly spaced at the expected value 36 Oe, obtained from B = n Φ0, Φ0 being the quantum fluxoid (Φ0  = 2.07 10−7 gauss cm2) and n being the density of pinning centers; i.e. n = 1/(a × b) (a, b being the sides of the rectangle unit cell of the array). ii) The R(H) curves are symmetrically shifted from the zero magnetic field value, when the remanent magnetization (Mz) is changed from up to down.

Figure 2
figure 2

Magnetoresistance of sample A-as grown (Nb film/[Co/Pd] multilayer triangles) Tc(H = 0) = 8.42 K.

Figure 3
figure 3

Magnetoresistance of sample A – Hz remanence (Nb film/[Co/Pd] multilayer triangles) Tc(H = 0) = 8.42 K.

Recently, del Valle et al. have reported two interesting findings on commensurability effects in hybrid samples fabricated with arrays in contact with superconducting films46. First, periodic roughness in the superconducting film is enough to generate resistivity minima. According to this result a matching effect should be observed in hybrid sample A-as grown (Nb film/[Co/Pd] multilayer triangles). In this sample the periodic roughness is obtained by the triangular array embedded in the Nb film. Therefore, the periodic array has to induce commensurability effect between the vortex lattice and the array and resistance minima should be observed. Figure 2 shows that this matching effect is absent. The second finding reported in46 is that preserving the local order is crucial to achieve matching effects. If the local order is not retained the magnetoresistance minima vanish. These two findings are a hint to explain the lack of magnetoresistance minima in sample A-as grown. As seen in Fig. 1 (a) the demagnetized state of sample A shows nanomagnets with large areas of up and down stray fields but with different distribution from one triangle to another. The array of triangles does not show any local magnetic order at all. The effect of random distribution of the stray fields, which are different in each triangle, is strong enough to overcome the slowdown of the vortex motion (resistance minima) which should happen at certain magnetic field values (commensurability effect). Therefore, we can conclude that the geometrical matching effect is weaker than the effect of the random magnetic pinning potentials. In this case, the lack of local magnetic order suppress the effect induced in the vortex lattice dynamics by the periodic roughness on the hybrid sample.

The resistivity minima appear when the sample is at the remanent state after saturation, see Fig. 3. The most remarkable effect is the asymmetry of the signal and the strong shift with the applied magnetic field. Morgan and Ketterson47 reported an asymmetry in critical currents when the array of magnetic nanodots shows out-of-plane magnetization. Actually, Fig. 3 is a clear proof of the existence of magnetic-field-induced superconductivity16,17,18. In hybrid sample A the applied magnetic field enhances the critical temperature from Tc (H = 0) = 8.42 K to Tc (H = 240 Oe) = 8. 50 K, see48, being 240 Oe the compensation field. Moreover, the superconducting vortex motion discriminates between upward (positive) or downward (negative) magnetization at remanence. The magnetoresistance shift to positive or negative values of the magnetic field is a good fingerprint of the remanent magnetization direction.

Sample B (Nb film/NdCo alloy)

The magnetic configuration of sample B at different temperatures has been obtained from micromagnetic simulations performed with MuMax3 code49 as reported in50. At each temperature constant MS and Kn values are used, obtained from the experimental characterization of single Nd-Co films39,50. Material microstructure in Rare Earth-Transition Metal alloys is usually described in terms of random magnetic anisotropy models51,52. Thus, to simulate microstructural disorder, the sample has been divided into a random set of exchange coupled “grains” of average size 12 nm and easy anisotropy axes randomly distributed around the average out-of-plane magnetization direction in a cone of width Δα (typically of the order of 15°). Figure 4(a) shows a micromagnetic calculation of the as-grown magnetict state of NdCo triangle (55 nm thick, 650 nm side) using room temperature (RT) material parameters MS(RT) and KN(RT). The triangle is divided in up/down (white/black) stripe domains that do not show any global preferred orientation due to the absence of an applied field. Only, near the borders, stripes tend to orient either parallel or perpendicular to the triangle edges, as expected for energy minimization53. Stripe width is quite regular, in the 50–80 nm range, almost an order of magnitude smaller than triangle size. These smaller domains are the result of magnetostatic energy minimization. They significantly reduce the stray field created by the magnetic triangles on the Nb film in the hybrid magnetic/superconducting sample both in intensity and in spatial range31.

Figure 4
figure 4

Micromagnetic simulations of NdCo triangles: (a) at room temperature with Q(RT) = 0.3 starting from a disorder state at zero field; (b) at low temperature with Q(LT) = 1.4 starting from state in (a) at zero field; (c) at low temperature with Q(LT) = 1.4 starting from an out-of-plane saturated state in high field (μ0Hz = 3 T) and reducing H down to zero along a hysteresis loop. Images show the magnetization configuration at the central plane of the triangle, black/white contrast corresponds to −MS/+MS out of plane magnetization, respectively. The size of the triangle is exactly the same that the fabricated NdCo triangle. Note that domain boundaries are Bloch walls inside the sample, see (d) arrow sketch, with small Neel caps near the surface31. Walls become sharper as temperature is reduced.

The low temperature magnetic configuration in “sample B-as grown” has been simulated starting with the configuration in Fig. 4(a) and gradually changing material parameters from the ones at room temperature to the ones at low temperature values, without any external applied field (i.e. gradually increasing MS from MS(RT) to MS(LT) and KN from KN(RT) to KN(LT)).

The result is shown in Fig. 4(b). The magnetic state at room temperature is frozen when the temperature is lowered; i. e. the global disorder at room temperature remains at low temperature. The only change obtained, decreasing temperature, is that domain walls between up and down domains become narrower due to the larger KN. A fully different picture appears when the state “sample B – Hz remanence” is simulated; see Fig. 4(c).

In this case, the sample is saturated, at low temperature, with a strong out of plane field and the magnetic configuration is simulated as the field is decreased down to remanence along a hysteresis loop. As can be seen, reversed magnetic domains are strongly disordered both in size and position within the triangle. This can be attributed to the lower mobility of the narrower low temperature domain walls that become more easily pinned at material defects.

Micromagnetic simulations in arrays with increasing degree of microstructural disorder give interesting insight into the different magnetic behavior of samples A and B at low temperatures (both of them with Q > 1, i.e. stronger anisotropy than magnetostatic energy terms). Figure 5 shows the reduced remanent magnetization MR/MS of triangles with Q = 1.4 and increasing Δα, i.e. increasing disorder in easy anisotropy axes. For low Δα, i.e. ordered material with well aligned easy axes, MR/MS ≈ 1 and no reversed domains are observed at remanence (with a behavior equivalent to the high remanence Co/Pd alloys). Only for Δα above 10°, microstructural disorder becomes large enough to favor nucleation of reversed domains inside the triangle as the field is reduced from saturation to remanence (corresponding to the low remanence values of Nd-Co alloys).

Figure 5
figure 5

Remanent magnetization of Nd-Co triangles (LT Q = 1.4) as a function of magnetic disorder (Δα is the angular width of the random distribution of easy anisotropy axes). Reversed domains are only observed for Δα above 10°. The line is a guide to the eye.

In sample B (NdCo alloy) the behavior of the magnetoresistance clearly deviates from the behavior recorded in sample A (Co-Pd multilayer) in both states. Figure 6 shows the magnetoresistance in sample B-as grown state. Sharp resistance minima appear and they follow the well-known behavior reported in many hybrid systems45 and references therein. That is, the periodicity of the minima is related to matching effects with the array. We have to remember that in sample A-as grown the minima are absent.

Figure 6
figure 6

Magnetoresistance of sample B-as grown (Nb film/NdCo alloy triangles). Temperatures from up to down curves: 8.57 K, 8.53 K, 8.50 K, 8.44 K and 8.35 K. Tc (H = 0) = 8.61 K.

Figure 7 shows the magnetoresistance data in sample B – Hz remanence. That is, the data are recorded after zero-field cooling up to 10 K and then applying an out of plane saturating magnetic field (30 kOe) and reducing the field to zero. Interestingly, in this remanent state of the NdCo alloy nanotriangles, the magnetoresistance curves in the hybrid sample follow an unexpected trend. The usual behavior is a strong enhancement of the pinning effects when the temperature is decreased45 and references therein. In sample B – Hz remanence the opposite happens; the matching effect vanishes decreasing the temperature.

Figure 7
figure 7

Magnetoresistance measurements for sample B – Hz remanence state (Nb film/NdCo alloy triangles). Temperatures from up to down curves: 8.53 K, 8.48 K, 8.43 K and 8.35 K. Tc (H = 0) = 8.61 K.

Discussion

The main results can be summarized as follows: i) as grown states display a complete different behavior. In one case, strong anisotropy (sample A), matching effects are absent; but in the case of moderate magnetic anisotropy (sample B), matching effects are present and follow the usual behavior. ii) HZ remanent state of the sample with strong anisotropy (sample A) gives rise to a R(H) curve strongly shifted, while in the case of moderate anisotropy (sample B) the minima are symmetric but they vanish decreasing the temperature.

We can explain this complex behavior taking into account the interplay between disorder and order of pinning magnetic potentials generated by stray magnetic fields, as well as, the competition between two characteristic length scales: the magnetic domain sizes and the superconducting vortex core dimension.

As Fig. 6 shows, sample B – as grown exhibits the usual behavior of the vortex dynamics on periodic arrays reported in the literature (see for instance in45 and references therein). The superconducting vortex lattice matches with the array unit cell and well-defined magnetoresistance minima appear which are easier detected decreasing the temperature.

The most remarkable difference between sample A and sample B is that the latter shows a moderate out of plane magnetic anisotropy and consequently the distribution of stray fields up and down is weaker than in sample A (see Fig. 4). This smoother combination produces a less effective effect of the stray fields on the vortex dynamics than in sample A. So the magnetic contribution to matching effects is smaller than in sample A and the geometrical pinning potentials govern the vortex dynamics. Therefore, the vortex dynamics behaves as usual45.

To shed light on these differences between these two systems an estimation, by micromagnetic simulations, of the stray field strength variations have been performed in two situations: magnetic stray fields on top of the triangles and out of the triangles. In sample A (Nb film/Co-Pd multilayer), with no external field and at a height z = 50 nm (in the center of the Nb film), the calculation shows that the stray field is in the 600–1000 Oe range on top of the triangles, and around 250–350 Oe in the interstitial areas, among triangles. This means that each triangle generates a magnetic flux around 5 Φ0, enough to induce 5 vortex-antivortex pairs and in good agreement with the experimental shifted magnetoresistance ad the results reported by del Valle et al.48. In the case of sample B (Nb film/NdCo alloy) the stray field generated by a 55 nm thick NdCo film at the mid-plane (height z = 50 nm) of the 100 nm Nb film is of the order of 300 Oe in average on top of each magnetic triangles domains and the stray field is 40 Oe in the interstitial region among triangles at 50 nm height (in the center of the Nb film). This value is too low to generate interstitial vortices (anti-vortices) in these regions, as can be seen by the zero-shift magnetoresistance curves, which means that there is not compensation field in this sample. In addition, the values of the stray fields are a clue to explain the magnetoresistance differences in the as-grown states. In sample A the disorder of strong stray fields overcomes the geometric order and the matching effect vanishes, conversely in sample B the smaller stray field strength does not preclude the matching effect and the periodic pinning effect induces the resistivity minima.

More interesting is the magnetoresistance behavior in the case of sample B – Hz remanence (see Fig. 7). The most remarkable effect is that decreasing the temperature, the minima disappear. To explain this striking finding we have to deal with a new parameter: the size of the superconducting vortices. As was noticed in the introduction section, in principle, two mechanisms can be taken into account: i) the induced screening supercurrents needed to expel the stray magnetic fields and ii) the interplay between the coherence length (vortex core) and the magnetic domain or wall domain sizes. It turns out that the latter mechanism has been named by several authors11,12,13,14,15 as the clue to explain the coexistence between superconductivity and magnetism. The vortex cores have to be commensurable with the magnetic domain sizes. Figure 7 shows a crossover from a regime in which resistance minima are observed to another regime in which minima are absent. This crossover happens decreasing the temperature. That is the vortex core shrinks. In our analysis, it is crucial to obtain an estimation of the vortex cores, i. e. the superconducting coherence lengths. The temperature dependence of the superconducting coherence length ξ (T) can be obtained as usual from the measurement of the upper critical field temperature dependence, Hc2(T), see54. The temperature dependence of the coherence length ξ (T) is plotted in Fig. 8. The shadow area represents the region where the coherence lengths are of the order or smaller than the domain sizes which can be estimated around 70 nm, see Fig. 4(c) and37,38,39,50. Interestingly, the crossover temperature is similar to the temperature where the resistance minima disappear. This experimental result can be double checked measuring the temperature dependence of the critical currents. Minima in resistances correspond to maxima in critical currents. Inset in Fig. 8 shows Ic (H) at constant temperature in the relevant temperature interval. We can observe the same temperature crossover that is found in the magnetoresistance (Fig. 8 inset). Hence, we can conclude that the vortices with core dimensions larger than the domain sizes average over the magnetic landscapes and they only follow the geometrical matching effects; but when the vortex cores shrink they begin to interact with the random magnetic domains and the magnetoresistance minima vanish.

Figure 8
figure 8

Sample B (Nb film/NdCo alloy). Y-axis coherence length (ξ). X-axis reduced temperature Tc(H = 0) = 8.61 K. Shading area shows lengths smaller than the sizes of the magnetic domains. Inset: Sample B (Nb film/NdCo alloy). Y-axis critical currents (Ic). X-axis applied magnetic fields. Temperatures from down to up curves: 8.56 K, 8.52 K, 8.43 K and 8.35 K. Tc(H = 0) = 8.61 K. Voltage criterion to obtain Ic is V = 3 × 10−7 V.

It is interesting to note that superconducting vortices are sensitive to the subtle differences in disorder between as grown and Hz-remanence states: minima only vanish due to the disorder in the magnetic state for the latter state, in which magnetic domains are disordered both in size and position. In the as grown state, that retains certain degree of uniformity in domain size, minima are still present.

Conclusions

Our work deals with the interplay between commensurate pinning (created by the periodic triangle array) and order-disorder magnetic pinning created by the domain structure of two different materials. Two different length scales are involved in this order-disorder competition that are analyzed using either Co-Pd multilayer or NdCo alloy.

Disorder on a length scale comparable with nanomagnet size and array unit cell dimensions

This is achieved with a Co/Pd sample in the as-grown state: there are only one or two domains per triangle with sizes of several hundreds of nm, i.e. comparable to array unit cell (800 nm): Previous works46 had shown that physical displacement of the pinning sites on a length scale comparable with the array length scale quench periodic pinning and minima in the resistivity disappear. The results for sample A (Figs 1a and 2) show an alternative method to create disorder on this same length scale (using the domains within each Co/Pd triangle) but with a clear advantage over the method used in46: Magnetic disorder is erasable with a magnetic field (as shown in Fig. 3) in contrast with topographic disorder that is fixed once the sample is fabricated. Magnetic domain size also governs the spatial extension of the stray field in the superconductor. Single domain state comparable to element size (Fig. 3) creates an effective magnetic field on the Nb films that displaces the magnetoresistance curve either to positive or negative field values.

Disorder on a length scale smaller than nanomagnets size and array unit cell dimensions (but comparable to vortex size at low temperatures)

The different behavior between sample A (Pd-Co multilayer) and sample B (NdCo alloy) clearly show that domain size is an important factor in magnetic pinning effect. Three important novel experimental facts are observed:

  1. a.

    Small magnetic domains do not create asymmetries in the magnetoresistance curve (neither in the as-grown or remanent states). This is a direct consequence of small mixed up/down domains that minimize magnetostatic energy so that the stray field barely extends beyond the magnetic triangles.

  2. b.

    Periodic pinning depends on the averaging of the effective magnetic pinning potential over vortex size (with a crossover when vortex size is of the order of magnetic domains). If the magnetic domain size is smaller than the coherence length (vortex core) the local order parameter in the superconductor cannot follow such rapid spatial modulations and the vortex “sees” an uniform order parameter, i.e. there is no pinning (as pinning depends on the gradients of the order parameter in the superconductor55). This is in agreement with earlier global measurements17 and locally images by STM in56.

  3. c.

    Subtle differences in magnetic disorder result in very different superconducting pinning behavior: 1) as-grown NdCo triangles display disordered stripes frozen from the high temperature configuration (Q = 0.3 at RT) in which orientation order is lost but there is a certain order in stripe domain position (stripe width is fixed and stripes tend to meet triangle borders either parallel or perpendicular) and 2) Hz-remanent NdCo triangles with magnetic disorder both in size and domain position/orientation. This second kind of disordered magnetic state is able to compete effectively with periodic pinning (no minima are observed at low temperatures) as long as vortex size is small enough to interact with the smaller domains in each triangle.

Finally, we want to stress that superconducting vortex dynamics can discriminate among magnetic states in arrays of nanomagnets: different remanent states of the magnetic arrangement of nanomagnets and subtle magnetic differences produce qualitatively different responses in the superconducting vortex dynamics since superconducting vortex lattice motion probes both the local magnetic state of nanomagnets and the ordered or disordered magnetic state in array of nanomagnets.

Methods

The periodic arrays of magnetic triangles have been fabricated by e-beam lithography and lift off on Si (100) substrates, as reported before, see for instance48. The equilateral triangles (650 nm sides) are arranged following a rectangular unit cell of 800 nm × 700 nm. The two different magnetic systems [Co/Pd multilayer (sample A) and NdCo alloy (sample B)] have been deposited by dc magnetron sputtering on Si (100) substrates, see details in29 and37,38,39 respectively. On top of these arrays, Nb film was grown by magnetron sputtering with 100 nm thickness, with a base pressure of 5 × 10−8 Torr. Finally, for electric transport measurements, an 8-terminal cross-shaped bridge was defined using optical lithography and Ar/SF6 (1:2) Reactive Ion Etching. The area of the bridge is 40 μm × 40 μm. In sample A the magnetic layer is a {Co [0.4 nm]/Pd [0.6 nm]} with total thickness 40 nm, deposited by sputtering from single Co and Pd targets. This Co/Pd multilayer is a magnetic system with perpendicular anisotropy and with saturation magnetization Ms (RT) = 5 × 105 A/m57. Co and Pd layer thicknesses and sputtering pressure during growth were selected to optimize out-of-plane remanent magnetization. In a Co/Pd multilayer film of similar composition MR is 0.95MS (obtained from an out-of-plane hysteresis loop measured with a SQUID magnetometer at 5 K), characteristic of very strong perpendicular magnetic anisotropy (PMA) as was reported in the literature29,32,33,34,35,36. In sample B, the magnetic layer is a Nd16Co84 film with 55 nm thickness, deposited by sputtering from Nd-Co target of a similar composition50. Nd16Co84 is a soft ferromagnetic alloy with MS(RT) = 7 × 105 A/m and PMA KN(RT) = 105 J/m3 at room temperature (RT), i.e. Q(RT) = 0.3 corresponding to a weak PMA material. Equilibrium domain configuration consists of parallel stripes with alternating up-down magnetization and width in the 50–60 nm range37,38,39 depending on sample thickness39,58. In the demagnetized state, stripe domains become branched and curved in a labyrinth configuration37 but they retain its characteristic width given by the competition between magnetostatic and anisotropy energies. At low temperatures (LT) (10 K), the anisotropy in the material increases up to KN(LT) = 1.8 × 106 J/m3 at 10 K37,38, with MS(LT) = 1.4 × 106 A/m. Thus, at low temperature Q increases up to Q = 1.4 which corresponds to a material with moderate anisotropy. In NdCo films of similar composition, out-of-plane remanence at low temperature presents relatively low values, of the order of 0.1 MS37,38, characteristic of strong disorder that favors reversed domain nucleation at positive fields and a disordered multidomain state at remanence.

Superconducting vortex motion is the proposed “experimental technique” to detect the magnetic states of these systems. Magneto-transport R(H) experiments, R being the resistance, were done with a magnetic field H applied perpendicular to the substrate in a liquid helium system with superconducting magnet48. The applied magnetic field does not modify the remanent magnetic state of the samples. The vortex lattice is set in motion by a driven current applied perpendicular to the base of the triangles. The dc magnetoresistance exhibits commensurability effects43,44,45 in which dissipation minima develop as a consequence of the geometrical matching between the vortex lattice and the underlying periodic structure. At these matching fields, the vortex-lattice motion slows down, and R(H) sharp minima appear at well-defined and equally spaced values of the applied field H. The first matching field is the one for which the density of vortex lattice equals the density of pinning centers.We have chosen triangular shape for the nanomagnet instead the usual circular dots, since equilateral triangles are a good reference for selecting the driving current direction and the vortex motion, as well as the magnetic stripe domain directions, since stripes prefer to meet triangle borders either parallel or perpendicular40.