Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Enhanced photocatalytic dye degradation and hydrogen production ability of Bi25FeO40-rGO nanocomposite and mechanism insight


A comprehensive comparison between BiFeO3-reduced graphene oxide (rGO) nanocomposite and Bi25FeO40-rGO nanocomposite has been performed to investigate their photocatalytic abilities in degradation of Rhodamine B dye and generation of hydrogen by water-splitting. The hydrothermal technique adapted for synthesis of the nanocomposites provides a versatile temperature-controlled phase selection between perovskite BiFeO3 and sillenite Bi25FeO40. Both perovskite and sillenite structured nanocomposites are stable and exhibit considerably higher photocatalytic ability over pure BiFeO3 nanoparticles and commercially available Degussa P25 titania. Notably, Bi25FeO40-rGO nanocomposite has demonstrated superior photocatalytic ability and stability under visible light irradiation than that of BiFeO3-rGO nanocomposite. The possible mechanism behind the superior photocatalytic performance of Bi25FeO40-rGO nanocomposite has been critically discussed.


High expenses associated with fabrication of complex optoelectronic devices, coupled with their poor conversion efficiency, limits the use of abundant solar energy from the sun1,2,3,4,5. Besides overcoming these obstacles, the researchers have focused on converting solar energy into a more usable and reproducible form which is also inexpensive to store. Interestingly, substrateless photocatalyst powders suspended in earth-abundant water can absorb the sunlight incident on them and electrochemically split the water molecules to produce hydrogen and oxygen6,7. Storing the generated hydrogen, a green fuel, is also easy and inexpensive. Furthermore, these photocatalyst powders can be used to degrade different industrial pollutants which are excessively harmful to our environment8,9,10,11,12,13,14. Since photocatalysts have been able to manifest a great potential in the production of hydrogen by splitting water molecules and degradation of environmental pollutants, investigations on their photocatalytic properties have been carried out for both energy-related and environmental applications12,13,15,16,17. Metal oxide photocatalysts are being studied extensively for their enhanced catalytic abilities supplemented by highly stable nature under the electrochemical reaction conditions16,17. An efficient photocatalyst is expected to have a large surface area, superior sensitivity to the visible region of the solar spectrum, appropriate band energetics, and agile carrier transport to inhibit recombination processes15,17,18,19. While graphene is not well-suited for optical applications due to the absence of band gap, its enormous surface area and extraordinary transport properties can be used to supplement the photocatalytic abilities of metal oxides11,14,20,21,22,23,24,25. Investigations on the in-situ growth of metal oxide nanoparticles on the 2D lattice of graphene have unveiled incredible improvements in morphology, optical sensitivity, adsorption capabilities, and electron transport characteristics over the pristine metal oxide nanoparticles23,24,25,26,27,28. Furthermore, engineering the work function of graphene implied that it is capable of modifying the energy bands of a semiconductor by forming heterojunction29,30,31,32.

Among numerous metal oxides, the ones belonging to perovskite and sillenite structures have drawn more interest as photocatalysts as they have shown good optical response and great stability16,17,33,34,35. Bismuth ferrite (BFO) is one such family of metal oxide that shows both perovskite (BiFeO3) and sillenite (Bi25FeO40) structures36,37. Both perovskite BiFeO3 and sillenite Bi25FeO40 have reasonably narrow band gaps of 2.1  2.7 eV and 1.8  2.0 eV respectively as reported in previous investigations38,39,40,41. The sillenite Bi25FeO40 has a better optical absorption capability due to the smaller band gap. However, the ferroelectric nature of perovskite BiFeO3 helps it in developing a superior resistance to recombination processes38,42. Until now, it has been challenging to synthesize both BiFeO3 and Bi25FeO40 nanoparticles with excellent phase-purity due to the difficulties associated with controlling the synthesis parameters, in particular, synthesis temperature42,43,44,45. Moreover, unfavorable band energetics of both BiFeO3 and Bi25FeO40 have also limited their use in energy-related applications, e.g., photocatalytic hydrogen production from water. Notably, graphene lattice may work as a center for heterogeneous nucleation to favor single-phase growth of either perovskite or sillenite structure depending on the synthesis conditions46,47,48. The formation of a heterojunction with graphene may improve the photocatalytic hydrogen production ability of both BiFeO3 and Bi25FeO40 by reducing their work functions and modifying the band energetics. Inspired by the possibility of such improvements, we have incorporated reduced graphene oxide (rGO) with both BiFeO3 and Bi25FeO40 to fabricate their nanocomposites. We have demonstrated a hydrothermal synthesis process for BFO-rGO nanocomposites that can be utilized to obtain both perovskite (BiFeO3-rGO) and sillenite (Bi25FeO40-rGO) structures by tuning the hydrothermal reaction temperature38. In this present investigation, we have compared the performance of BiFeO3-rGO and Bi25FeO40-rGO nanocomposites to that of both pristine BiFeO3 nanoparticles and commercially available Degussa P25 titania nanoparticles in photocatalytic degradation of Rhodamine B (RhB) dye and photocatalytic hydrogen production via water-splitting. Here, RhB dye has been used as a proxy to the industrial pollutants to benchmark the photocatalytic ability of the bismuth ferrite-rGO photocatalysts in environmental applications. Through a series of experiments, we have observed that Bi25FeO40-rGO nanocomposite exhibits a considerably better visible light driven photocatalytic performance in both dye degradation and hydrogen production than those of BiFeO3-rGO nanocomposite, BiFeO3 nanoparticles, and Degussa P25 nanoparticles. Furthermore, we have critically assessed the possible mechanism behind the superior photocatalytic performance of Bi25FeO40-rGO nanocomposite.

Results and Discussions

Materials characterization

The crystallographic structure of the synthesized nanomaterials has been investigated by obtaining their X-ray diffraction (XRD) patterns as shown in Fig. 1. The diffraction peaks exhibited by both BiFeO3 and BiFeO3-rGO conform to the single-phase perovskite structure (R3c space group) of BiFeO3 (JCPDS card No. 86–1518). On the other hand, the diffraction peaks of Bi25FeO40-rGO are in good agreement with single-phase sillenite structure (I23 space group) of Bi25FeO40 (JCPDS card No. 46–0416). Reduction of GO can be observed for both nanocomposites as the characteristic peak of GO at (002) is absent in the corresponding patterns. The average particle size of the synthesized nanomaterials has been obtained from particle size histograms extracted from their field emission scanning electron microscopy (FESEM) images. Incorporation of rGO has reduced the average particle size of BiFeO3-rGO (40 nm) and Bi25FeO40-rGO (20 nm) nanocomposites compared to that of pure BiFeO3 nanoparticles (70 nm) as shown in Supplemental Fig. S1. Comparatively smaller particle size implies larger surface to volume ratio which is a necessary property of an efficient photocatalyst. The mechanism behind inhibition of particle growth due to the inclusion of rGO has been presented elsewhere38.

Figure 1

XRD patterns of GO, BiFeO3 at 180 °C, sillenite Bi25FeO40-rGO at 180 °C, and perovskite BiFeO3-rGO nanocomposite at 200 °C. The theoretically calculated patterns for BiFeO3 of space group R3c and Bi25FeO40 of space group I23 have also been included for comparison of phases.

X-ray photoelectron spectroscopy (XPS) has been performed on the synthesized nanomaterials to analyze the formation of different bonds on their surface. Figure 2(a–c) presents the O 1s spectra of BiFeO3 nanoparticles, BiFeO3-rGO, and Bi25FeO40-rGO nanocomposites. The peaks for both Bi-O and Fe-O bonds occur at around 529 eV and 530 eV respectively for all the samples. This result is consistent with the values reported in the literature49,50,51. As shown in Fig. 2(b,c), the presence of a peak around 531 eV can be attributed to the formation of COOR bond, i.e., the formation of a composite with graphene52. Figure 2(d–f) shows the C 1s spectra of Bi25FeO40-rGO, BiFeO3-rGO nanocomposites, and GO respectively. As shown in Fig. 2(f), the C-O peak is almost as strong as the C-C peak in GO. However, the intensity of the C-O peak is significantly reduced in both nanocomposites as shown in Fig. 2(d,e) while the intensity of the COOR peak does not change significantly. The dominance of the C-C peak compared to the C=O and COOR peaks implies that GO has been considerably reduced and the honeycomb structure of graphene has also been nearly restored. This partial reduction of GO can be attributed to the nature of reduction, e.g., the hydrothermal process. The hydrothermal process reduces the GO sheets by decomposing the C=O and COOR bonds53. Higher thermal energy provided by a higher process temperature favors faster and greater reduction53,54,55,56,57,58,59. However, a process temperature that is higher than 180 °C would be unfavorable for the single phase growth of Bi25FeO40-rGO nanocomposite38. Although single phase BiFeO3-rGO nanocomposite can be synthesized at a higher temperature, the higher growth rate may cause the particles to grow larger and even agglomerate. In addition to the higher expenses associated with a higher temperature process, we may face further difficulty in the synthesis process as the control over the particle size and morphology might be lost. Besides, the process also removes carbon atoms from the carbon plane in the form of CO2 and splits the graphene sheet into smaller pieces59,60. The dangling carbon atoms at the end of the smaller graphene sheets may be oxidized again and contribute to the COOR bonds present in the surface of the composites.

Figure 2

XPS spectra of the core level O 1s of (a) BiFeO3, (b) perovskite BiFeO3-rGO nanocomposite, (c) sillenite Bi25FeO40-rGO nanocomposite, and core level C 1s of (d) perovskite BiFeO3-rGO nanocomposite, (e) sillenite Bi25FeO40-rGO nanocomposite, and (f) GO.

Since XPS analyzes the bond properties of the surface (within 3–5 nm) of a sample rather than its bulk, an analysis like FTIR spectroscopy would be more useful for studying the presence of different functional groups in the nanocomposites. Hence, FTIR spectroscopy has also been performed on GO and the nanocomposites to verify the reduction of GO into rGO conclusively. The components and functional groups have been identified from the FTIR spectra as shown in Fig. 3. The vibrational band ranging from 1053 to 1220 cm−1 can be attributed to the presence of different types of C-O bonds. In addition, the vibrational bands at 1718 cm−1 and 3441 cm−1 can be assigned to the presence of C=O and −OH bonds respectively61,62,63,64,65. As evident from Fig. 3, the peaks for each of these oxidized species are considerably smaller in the spectra of the nanocomposites compared to that of GO. Notably, the peak due to C=O and COOR bonds is significantly smaller than that of GO for both nanocomposites. Hence, the FTIR spectra prove that even the C=O and COOR bonds have also been considerably reduced. FTIR characterization, in conjunction with the XPS characterization, leads us to the conclusion that GO has been reduced to a significant extent during the formation of the nanocomposites.

Figure 3

FTIR spectra of GO, BiFeO3-rGO nanocomposite, and Bi25FeO40-rGO nanocomposite.

Photocatalytic Degradation Activity and Stability

BiFeO3 nanoparticles, BiFeO3-rGO, and Bi25FeO40-rGO nanocomposites have been used as the photocatalysts to perform degradation of RhB dye under visible light irradiation. For comparison, Bi25FeO40 nanoparticles and commercially available Degussa P25 titania nanoparticles were also used to conduct the RhB dye degradation experiment under the same experimental conditions. Figure 4(a) presents the time-dependent UV-vis absorbance spectra of RhB when Bi25FeO40-rGO is used as the photocatalyst. Figure 4(b) shows the photocatalytic efficiency of BiFeO3 nanoparticles, Bi25FeO40 nanoparticles, P25 titania nanoparticles, BiFeO3-rGO nanocomposite and Bi25FeO40-rGO nanocomposite in the degradation of RhB. As observed in Fig. 4(b), BiFeO3 nanoparticles, Bi25FeO40 nanoparticles, BiFeO3-rGO and Bi25FeO40-rGO nanocomposites can degrade 60%, 62%, 78%, and 87% of the RhB dye respectively after 4 hours of irradiation compared to the 6% degradation achieved by commercially available Degussa P25 titania nanoparticles. The degradation rates of the photocatalysts have also been calculated from Fig. 4(c) using the Langmuir-Hinshelwood model. The degradation rates are found to be 6.4 × 10−4 min−1, 2.83 min−1, 2.88 min−1, 4.45 min−1, and 5.91 min−1 for Degussa P25, BiFeO3, Bi25FeO40, BiFeO3-rGO, and Bi25FeO40-rGO respectively. Notably, Bi25FeO40-rGO displays the highest photocatalytic degradation ability as it exhibits a 108%, 104%, and 33% greater degradation rate compared to that of BiFeO3, Bi25FeO40, and BiFeO3-rGO respectively.

Figure 4

(a) Time-dependent absorbance spectra of RhB solution under visible light irradiation with Bi25FeO40-rGO nanocomposite photocatalyst, (b) Degradation of RhB by photocatalytic activity of blank, BiFeO3, Bi25FeO40, BiFeO3-rGO, Bi25FeO40-rGO, and Degussa P25 with irradiation time, (c) Pseudo-first order kinetics fitting data for RhB photodegradation by blank, BiFeO3, Bi25FeO40, BiFeO3-rGO, Bi25FeO40-rGO, and Degussa P25 (d) Recyclability of BiFeO3-rGO and Bi25FeO40-rGO for 3 successive runs.

In addition to the superior degradation ability, a photocatalyst is expected to be stable under the reaction conditions to be considered for practical applications. Since the stability of BiFeO3 as a photocatalyst is well known, only BiFeO3-rGO and Bi25FeO40-rGO nanocomposites were subject to the recyclability test. As observed in Fig. 4(d), BiFeO3-rGO exhibits a small loss in degradation ability during each successive cycle. However, Bi25FeO40-rGO shows excellent stability with negligible loss in photocatalytic ability after 3 consecutive cycles. Since Bi25FeO40-rGO nanocomposite has shown a comparatively higher photocatalytic degradation ability and better stability than BiFeO3-rGO nanocomposite, we believe that it can be considered for different practical applications such as environmental pollutant degradation, hydrogen production via water-splitting, etc.

Photocatalytic Hydrogen Production Test Analysis

A photocatalytic hydrogen production experiment has also been performed using the synthesized nanomaterials. Figure 5 presents the amount of hydrogen gas (ml/g) generated after 4 hours of visible light irradiation. Photocatalytic hydrogen production of BiFeO3, BiFeO3-rGO, and Bi25FeO40-rGO has also been compared to that of a standard photocatalyst, Degussa P25 titania nanoparticles66. Figure 5 presents the amount of hydrogen produced by BiFeO3, BiFeO3-rGO, Bi25FeO40-rGO and Degussa P25 under the same experimental conditions. In addition to the high photocatalytic degradation ability, Bi25FeO40-rGO nanocomposite demonstrates the highest volume of hydrogen production which is almost 3.5 times greater than that of Degussa P25 nanoparticles.

Figure 5

The volume of evolved hydrogen versus irradiation time for Degussa P25, BiFeO3, BiFeO3-rGO, and Bi25FeO40-rGO.

Comparison of Optical Band gap

The photocatalytic behavior of the prepared catalysts in both dye degradation and hydrogen production can be rationalized by analyzing their optical absorption, band edge positions, and possible mechanisms to suppress the recombination processes. The optical band gaps of BiFeO3, Bi25FeO40, BiFeO3-rGO and Bi25FeO40-rGO are found to be 2.1 eV, 1.8 eV, 1.8 eV and 1.65 eV respectively. The UV-vis absorbance spectra of these materials have been provided in the Supplemental Fig. S238,67. Hence, with a smaller band gap, Bi25FeO40-rGO nanocomposite possesses greater optical absorption ability compared to that of BiFeO3-rGO nanocomposite and BiFeO3 nanoparticles. In addition to absorbing photons belonging to the infrared region of the solar spectrum, the band gap of 1.65 eV enables the Bi25FeO40-rGO nanocomposite in nearly reaching the Shockley-Queisser limit which states that maximum solar energy conversion can be achieved optoelectronically with a material that has an optical band gap of 1.34 eV68,69,70,71.

Photocatalytic Mechanism

The optical band gap is a crucial parameter for gaining an insight into the photocatalytic ability of a material. However, the potentials of the valence band maxima (VBM) and conduction band minima (CBM) also play significant roles in catalyzing the redox reactions in the electrolyte system. Absorption of a photon with energy greater than or equal to the band gap of a material excites an electron from the valence band to its conduction band, i.e., creates an electron-hole pair. The reduction half-reaction commences when the photogenerated electron has a potential that exceeds the reduction potential of the redox couple. Similarly, the photogenerated hole is required to possess a potential that exceeds the redox potential of the oxidation half-reaction. Efficient photocatalytic degradation ability of the nanocomposites can be better understood by analyzing the redox reactions in the electrolyte system that govern the degradation of RhB dye. Photocatalytic degradation of RhB is, in fact, a collection of specific redox reactions. Among these redox reactions, two are particularly important33. First, the photogenerated electron can react with the surface adsorbed O2 (redox potential: −0.16 V vs. NHE) to form \({{\rm{O}}}_{2}^{-}\), which will further react with RhB to cause degradation33. Second, the photogenerated holes can react with the OH ionized from the water molecules to produce OH (redox potential: 2.38 V vs. NHE). This OH can further oxidize the RhB molecules. Therefore, a photocatalyst needs to possess a CBM < −0.16 V to drive the first reaction and VBM > 2.38 V to drive the second one efficiently.

These prerequisites necessitate an investigation of the potentials of the VBM and CBM of the synthesized photocatalysts. The Fermi energy of the pure BiFeO3 and Bi25FeO40 can be calculated theoretically from the equation, EF = χ − EC72,73. Here, χ is the absolute electronegativity of the semiconductor which can be found from the geometric mean of the absolute electronegativity of the constituent elements, and EC is the energy of a free electron in hydrogen scale which is approximately 4.5 eV. While usually, Fermi energy lies midway between the CBM and VBM of a semiconductor, first-principles studies of several sillenites show that the energy of their VBM coincides with the Fermi energy74. Hence, the energies of CBM and VBM of BiFeO3 were obtained by simply adding and subtracting 0.5Eg to its Fermi energy whereas for Bi25FeO40, VBM was considered equal to the Fermi energy and CBM was determined by adding Eg to the VBM. {CBM, VBM} of BiFeO3 and Bi25FeO40 has been determined to be {0.51 V, 2.61 V} and {−0.06 V, 1.74 V} respectively. Therefore, pure BiFeO3 can perform only the second redox reaction of RhB degradation since it has VBM > 2.38 V and CBM > −0.16 V. Infusion of rGO influences the valence and conduction band structure of the pure BiFeO3 and Bi25FeO40 nanoparticles. Introduction of C 2p orbital of rGO causes both valence and conduction band potentials to raise upward as shown in a previous first-principle investigation on BaTiO3-rGO composite75. We propose that similar interactions may have taken place in the BiFeO3-rGO and Bi25FeO40-rGO nanocomposites. Furthermore, this shift in the band positions can be viewed from a different perspective. Figure 6(a) shows the formation of a heterojunction between graphene and a semiconductor where Fermi energies of graphene and the semiconductor have been denoted as EFG and EFS respectively. If EFG > EFS, electrons will be transferred to the semiconductor from graphene during the formation of the heterojunction until the system reaches the equilibrium Fermi energy, EF76. This electron transfer at the heterointerface will give rise to the formation of a surface dipole77,78,79 as shown in Fig. 6(a). For a bulk semiconductor, the electric field that arises from the surface dipole will cause band bending that will uniformly change the potentials of vacuum, CBM, and VBM. However, for a nanostructured semiconductor, nearly flatband conditions are observed at the heterojunction since its dimensions are not large enough to change the potentials of CBM and VBM80,81. Consequently, the electric field brings the vacuum level closer to both CBM and VBM. This shift in the potential of vacuum level will reduce the CBM of the nanostructured semiconductor as shown in Fig. 6(a). Since Fermi energy of pristine graphene (0 V vs. NHE)70,71 is greater than the Fermi energies of both BiFeO3 and Bi25FeO40, the model described above predicts that upward band-shifting should take place during the formation of both nanocomposites. This upward shift makes the VBM < 2.38 V for both nanocomposites, rendering them unable to perform the second redox reaction of RhB degradation using the photogenerated holes. Therefore, the high photocatalytic degradation performance by the nanocomposites should be attributed to the first reaction. Due to the upward band-shifting, CBM potentials of both nanocomposites become sufficiently negative (CBM < −0.16 V) which drives the photogenerated electrons in performing the first redox reaction of RhB degradation. Figure 6(b) consolidates the estimated CBM and VBM potentials of all the synthesized nanomaterials as well as the redox potentials of different redox half-reactions of our interest. Notably, negative CBM potential is one of the most important conditions for efficient photocatalytic hydrogen production via water-splitting. As observed in Fig. 5, our experimental results from photocatalytic hydrogen production test also support the prediction made by our model as the nanocomposites demonstrate considerably higher hydrogen production compared to that of pure BiFeO3 nanoparticles.

Figure 6

(a) Band-shifting of a nanocomposite while forming a junction with graphene (b) Energy band diagram of BiFeO3 nanoparticles, BiFeO3-rGO, and Bi25FeO40-rGO nanocomposites.

Since pure BiFeO3 has a positive CBM potential, it is intuitively confusing to notice that it can also produce hydrogen by water-splitting. A positive CBM potential indicates that only the states at the minima of the conduction band have positive potential. However, there should be several other allowed states in the conduction band with negative potential. When photons with appropriate energy are incident on a material, the electrons of valence band will gain enough energy to reach those states with negative potential and participate in the production of hydrogen. However, these photons, of course, must have energies that are higher than the band gap energy. Therefore, these energies may not lie in the visible range of the solar spectrum. Since the intensity of the incident photons of sunlight decreases considerably with the increase in photon energy beyond visible range, the number of available photons for such transitions is considerably smaller. Besides, these allowed transitions may even be indirect and therefore have smaller transition probability than the near band gap transitions. Therefore, while pure BiFeO3 and several other semiconductors with positive CBM potential may be able to produce hydrogen via water-splitting, their efficiency will be significantly smaller than that of the semiconductors with negative CBM potential. This hypothesis is also evident when we compare the results of photocatalytic degradation of RhB and photocatalytic hydrogen generation. While both BiFeO3-rGO and Bi25FeO40-rGO nanocomposites exhibit a similar trend of photocatalytic activities during both experiments, BiFeO3 shows a comparatively poorer performance in hydrogen production than that of RhB degradation. This inconsistent performance of BiFeO3 can be better understood if we take a keen look at its VBM potential(2.61 V). Since BiFeO3 has a VBM potential that exceeds 2.38 V, the holes generated by incident photons with energy greater than its band gap of 2.1 eV are sufficient for photodegradation of RhB. However, as mentioned above, photons with much higher energy than 2.1 eV are necessary to commence the production of hydrogen. This inherent shortcoming of BiFeO3 nanoparticles eventually reduces their efficiency in photocatalytic hydrogen production.

Due to the high electronegativity of oxygen atoms, many metal oxides with narrow band gaps such as α-Fe2O3, BiVO4, WO3, etc. have positive CBM potentials that suppress their ability in water-splitting. Our proposed model predicts that formation of nanocomposites with rGO may shift their CBM potentials to negative values and trigger the suppressed photocatalytic hydrogen production ability of these metal oxides. This model unveils a novel mechanism behind the superior photocatalytic abilities of semiconductor-rGO nanocomposites.

Effective suppression of recombination processes is another important characteristic of a good photocatalyst. BiFeO3 is a ferroelectric material that possesses a spontaneous inherent electric field. This electric field can spatially separate the photogenerated electrons and holes to reduce the probability of recombination82. A previous first-principles investigation revealed that the recombination processes in a sillenite are suppressed due to an intraband transition of the photogenerated hole74. We believe that this suppression of recombination processes would also apply to Bi25FeO40. Besides, the formation of a composite with rGO causes the photogenerated electrons to move to the rGO sheet where the superior electron mobility of the restored honeycomb structure can help the electron transport to the redox couples26,27,28,38,79. As shown in Fig. S3, steady-state photoluminescence (PL) spectra of the photocatalyst samples justify our hypothesis as the nanocomposites show considerably smaller PL peak intensities compared to that of pure BiFeO3 nanoparticles. Smaller PL peak intensity implies that a smaller number of photogenerated electrons and holes are radiatively recombined. Therefore, we believe that the photogenerated electron-hole pairs are more effectively separated when a composite with rGO is formed.


We have demonstrated a low temperature versatile hydrothermal technique for synthesizing highly efficient visible light photocatalysts of bismuth ferrite-rGO nanocomposite family whose phase can be controlled by tuning the synthesis temperature. Merging rGO sheets with each of the pristine BiFeO3 and Bi25FeO40 nanoparticles has resulted in better morphology, superior optical absorption, and favorable band edge shifts. The improvements associated with inclusion of rGO have also been reflected on the photocatalytic ability of the nanocomposites as they demonstrated considerably better degradation of RhB dye as well as greater hydrogen production by water-splitting over both pure BiFeO3 nanoparticles and a standard photocatalyst, Degussa P25 titania. Furthermore, Bi25FeO40-rGO nanocomposite has shown 3.5 times greater photocatalytic hydrogen production compared to that of Degussa P25 titania nanoparticles. Moreover, a theoretical model has been proposed to explain the band-shifting phenomenon which may prove to be significant in understanding the superior photocatalytic performance of different metal oxide-rGO nanocomposites.


Synthesis of BiFeO3 nanoparticles, BiFeO3-rGO, and Bi25FeO40-rGO nanocomposites

Synthesis of BiFeO3 nanoparticles, BiFeO3-rGO, and Bi25FeO40-rGO nanocomposites was carried out using the hydrothermal technique. Bi(NO3)3.5H2O (Sigma-Aldrich, 98.0%) and Fe(NO3)3.9H2O (Sigma-Aldrich, 98.0%) were used as precursors during synthesis of pure BiFeO3 nanoparticles. Graphene oxide (GO) synthesized using modified Hummer’s method was used as an additional precursor for the synthesis of the desired nanocomposites. Pure BiFeO3 nanoparticles were synthesized at a hydrothermal reaction temperature of 180 °C. Most interestingly, a synthesis temperature of 180 °C yielded the Bi25FeO40-rGO nanocomposite whereas the BiFeO3-rGO nanocomposite required an elevated temperature of 200 °C. The synthesis procedure and effects of hydrothermal reaction temperature on the crystal structure of the nanocomposites have been elucidated in our previous investigation38.

Characterizations Techniques

Structural characterization of the prepared samples was performed by obtaining their X-ray diffraction (XRD) patterns using a diffractometer (PANalytical Empyrean) with a Cu X-ray source (Wavelength, λ: Kα1 = 1.540598 Å and Kα2 = 1.544426 Å). Field emission scanning electron microscopy (FESEM) imaging of the samples was performed using a scanning electron microscope (XL30SFEG; Philips, Netherlands). The FESEM images were analyzed to determine the morphology of the nanomaterials. ImageJ software was used to analyze the size of the particles. X-ray photoelectron spectroscopy (XPS) was used to investigate the surface chemical states of synthesized nanomaterials. Fourier transform infrared (FTIR) spectroscopy (Shimadzu, IRSpirit-T) was also performed in the wavenumber range of 1000 cm−1 to 4000 cm−1 for studying the presence of different functional groups. Steady-state photoluminescence (PL) spectroscopy (Hitachi, F-700 FL spectrophotometer) was used to investigate the photogenerated carrier recombination of the nanomaterials. The excitation wavelength used for PL spectroscopy was 400 nm.

Photocatalytic degradation test

A photocatalytic degradation test was performed on Rhodamine B (RhB) dye using the synthesized nanomaterials as photocatalyst following the typical procedures. A solution was prepared by dissolving 10 mg RhB in 50 ml of distilled water. An aliquot of 5 ml was extracted from the solution to measure its absorbance using a UV-vis spectrophotometer. The intensity of the absorbance peak (553 nm) can be considered proportional to the amount of RhB present in the solution. This method was used each time when it was required to determine the remnant amount of RhB in the solution. Then the solution was magnetically stirred in dark conditions for 30 minutes to obtain a homogeneous solution. 40 mg of photocatalyst was then added to the solution and again stirred for 30 minutes to ensure adsorption-desorption equilibrium between photocatalyst and RhB. The photocatalysis process was initiated by irradiating the suspension with a Mercury-Xenon lamp (Hamamatsu L8288, 500 W). The UV portion of the light was filtered out with a UV cut-off filter (<400 nm). The degradation of RhB dye was monitored by carrying out absorbance measurements of the suspension at every 30 minutes interval. However, the photocatalyst nanomaterials were precipitated from the suspension using a centrifuge machine at 5500 rpm for 10 minutes before measuring its absorbance. Prior to recycling the photocatalyst, the remnant photocatalyst nanomaterials in the suspension were separated by centrifugation, washed with distilled water and dried afterward.

Photocatalytic hydrogen generation test

Photocatalytic hydrogen production test was performed in a slurry-type photochemical reactor. 20 mg of photocatalyst sample was dispersed into 30 ml deionized water, and the suspension was stirred magnetically to obtain homogeneity. The inert atmosphere required for photocatalytic hydrogen production was ensured by purging the system with argon gas for 30 minutes. The suspension was irradiated with visible light by a Mercury-Xenon lamp (Hamamatsu L8288, 500 W) coupled with a UV cut-off filter (<400 nm). The generated gas was extracted at an interval of 30 minutes for 4 hours and evaluated by a gas chromatography (GC) device equipped with a thermal conductivity detector (TCD) and a gas analyzer. The amount of generated hydrogen gas was determined in ml H2/g catalyst.


  1. 1.

    El-Khouly, M. E., El-Mohsnawy, E. & Fukuzumi, S. Solar energy conversion: From natural to artificial photosynthesis. Journal of Photochemistry and Photobiology C: Photochemistry Reviews 31, 36–83, (2017).

    Article  CAS  Google Scholar 

  2. 2.

    Henry, C. H. Limiting efficiencies of ideal single and multiple energy gap terrestrial solar cells. Journal of Applied Physics 51, 4494–4500, (1980).

    ADS  Article  CAS  Google Scholar 

  3. 3.

    Polman, A., Knight, M., Garnett, E. C., Ehrler, B. & Sinke, W. C. Photovoltaic materials: Present efficiencies and future challenges. Science 352, (2016).

  4. 4.

    Liu, W., Song, M. S., Kong, B. & Cui, Y. Flexible and stretchable energy storage: recent advances and future perspectives. Advanced Materials 29 (2017).

  5. 5.

    Arteconi, A. et al. Thermal energy storage coupled with PV panels for demand side management of industrial building cooling loads. Applied Energy 185, 1984–1993 (2017).

    Article  Google Scholar 

  6. 6.

    Shaban, M., Rabia, M., El-Sayed, A. M. A., Ahmed, A. & Sayed, S. Photocatalytic properties of PbS/graphene oxide/polyaniline electrode for hydrogen generation. Scientific Reports 7, 14100, (2017).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  7. 7.

    Xiang, Q., Cheng, F. & Lang, D. Hierarchical Layered WS2/Graphene-Modified CdS Nanorods for Efficient Photocatalytic Hydrogen Evolution. ChemSusChem 9, 996–1002, (2016).

    Article  PubMed  CAS  Google Scholar 

  8. 8.

    Wang, W., Wang, Z., Liu, J., Zhang, Z. & Sun, L. Single-step One-pot Synthesis of Graphene Foam/TiO2 Nanosheet Hybrids for Effective Water Treatment. Scientific Reports 7, 43755, (2017).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  9. 9.

    Shen, H. et al. Influence of interface combination of RGO-photosensitized SnO2 @RGO core-shell structures on their photocatalytic performance. Applied Surface Science 391, 627–634, (2017).

    ADS  Article  CAS  Google Scholar 

  10. 10.

    Xu, D., Cheng, B., Wang, W., Jiang, C. & Yu, J. Ag2CrO4/g-C3N4/graphene oxide ternary nanocomposite Z-scheme photocatalyst with enhanced CO2 reduction activity. Applied Catalysis B: Environmental 231, 368–380, (2018).

  11. 11.

    Song, S. et al. Structure effect of graphene on the photocatalytic performance of plasmonic Ag/Ag2CO3-rGO for photocatalytic elimination of pollutants. Applied Catalysis B: Environmental 181, 71–78, (2016).

  12. 12.

    Aleksandrzak, M., Kukulka, W. & Mijowska, E. Graphitic carbon nitride/graphene oxide/reduced graphene oxide nanocomposites for photoluminescence and photocatalysis. Applied Surface Science 398, 56–62, (2017).

    ADS  Article  CAS  Google Scholar 

  13. 13.

    Wan, Y., Liang, C., Xia, Y., Huang, W. & Li, Z. Fabrication of graphene oxide enwrapped Z-scheme Ag2SO3/AgBr nanoparticles with enhanced visible-light photocatalysis. Applied Surface Science 396, 48–57, (2017).

    ADS  Article  CAS  Google Scholar 

  14. 14.

    Liu, Y., Shi, Y., Liu, X. & Li, H. A facile solvothermal approach of novel Bi2S3/TiO2/RGO composites with excellent visible light degradation activity for methylene blue. Applied Surface Science 396, 58–66, (2017).

    ADS  Article  CAS  Google Scholar 

  15. 15.

    Ni, M., Leung, M. K. H., Leung, D. Y. C. & Sumathy, K. A review and recent developments in photocatalytic water-splitting using TiO2 for hydrogen production. Renewable and Sustainable Energy Reviews 11, 401–425, (2007).

    Article  CAS  Google Scholar 

  16. 16.

    Osterloh, F. E. Inorganic nanostructures for photoelectrochemical and photocatalytic water splitting. Chemical Society Reviews 42, 2294–2320, (2013).

    Article  PubMed  CAS  Google Scholar 

  17. 17.

    Anpo, M., Shima, T., Kodama, S. & Kubokawa, Y. Photocatalytic hydrogenation of propyne with water on small-particle titania: size quantization effects and reaction intermediates. Journal of Physical Chemistry 91, 4305–4310 (1987).

    Article  CAS  Google Scholar 

  18. 18.

    Maeda, K. & Domen, K. New non-oxide photocatalysts designed for overall water splitting under visible light. The Journal of Physical Chemistry C 111, 7851–7861 (2007).

    Article  CAS  Google Scholar 

  19. 19.

    Harada, H. & Ueda, T. Photocatalytic activity of ultra-fine rutile in methanol-water solution and dependence of activity on particle size. Chemical Physics Letters 106, 229–231, (1984).

    ADS  Article  CAS  Google Scholar 

  20. 20.

    Geim, A. K. & Novoselov, K. S. The rise of graphene. Nature Materials 6, 183 (2007).

    ADS  Article  PubMed  CAS  Google Scholar 

  21. 21.

    Geim, A. K. Graphene: status and prospects. Science 324, 1530–1534 (2009).

    ADS  Article  PubMed  CAS  Google Scholar 

  22. 22.

    Dreyer, D. R., Ruoff, R. S. & Bielawski, C. W. From conception to realization: an historial account of graphene and some perspectives for its future. Angewandte Chemie International Edition 49, 9336–9344 (2010).

    Article  PubMed  CAS  Google Scholar 

  23. 23.

    Xiang, Q., Yu, J. & Jaroniec, M. Graphene-based semiconductor photocatalysts. Chemical Society Reviews 41, 782–796, (2012).

    Article  PubMed  CAS  Google Scholar 

  24. 24.

    Thirugnanam, N. & Yan Wu, H. S. Photocatalytic degradation of Brilliant Green dye using CdSe quantum dots hybridized with graphene oxide under sunlight irradiation. Chinese Journal of Catalysis 38, 2150–2159, (2017).

    Article  CAS  Google Scholar 

  25. 25.

    Li, X., Shen, R., Ma, S., Chen, X. & Xie, J. Graphene-based heterojunction photocatalysts. Applied Surface Science 430, 53–107, (2018).

    ADS  Article  CAS  Google Scholar 

  26. 26.

    Wang, P. et al. One-step synthesis of easy-recycling TiO2-rGO nanocomposite photocatalysts with enhanced photocatalytic activity. Applied Catalysis B: Environmental 132, 452–459 (2013).

    Article  CAS  Google Scholar 

  27. 27.

    Wei, J. et al. Enhanced performance of light-controlled conductive switching in hybrid cuprous oxide/reduced graphene oxide (Cu2O/rGO) nanocomposites. Optics Letters 42, 911–914 (2017).

    ADS  Article  PubMed  Google Scholar 

  28. 28.

    Azarang, M., Shuhaimi, A., Yousefi, R. & Sookhakian, M. Effects of graphene oxide concentration on optical properties of ZnO/RGO nanocomposites and their application to photocurrent generation. Journal of Applied Physics 116, 084307 (2014).

    ADS  Article  CAS  Google Scholar 

  29. 29.

    Low, J., Cheng, B., Yu, J. & Jaroniec, M. Carbon-based two-dimensional layered materials for photocatalytic CO2 reduction to solar fuels. Energy Storage Materials 3, 24–35, (2016).

  30. 30.

    Garg, R., Dutta, N. K. & Choudhury, N. R. Work function engineering of graphene. Nanomaterials 4, 267–300 (2014).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  31. 31.

    Jo, G. et al. Tuning of a graphene-electrode work function to enhance the efficiency of organic bulk heterojunction photovoltaic cells with an inverted structure. Applied Physics Letters 97, 253 (2010).

    Google Scholar 

  32. 32.

    Yu, Y.-J. et al. Tuning the graphene work function by electric field effect. Nano Letters 9, 3430–3434 (2009).

    ADS  Article  PubMed  CAS  Google Scholar 

  33. 33.

    Ren, X. et al. Controlled growth of LaFeO3 nanoparticles on reduced graphene oxide for highly efficient photocatalysis. Nanoscale 8, 752–756, (2016).

    ADS  Article  PubMed  CAS  Google Scholar 

  34. 34.

    Hou, D. et al. Electrospun sillenite Bi12MO20(M = Ti, Ge, Si) nanofibers: general synthesis, band structure, and photocatalytic activity. Physical Chemistry Chemical Physics 15, 20698–20705 (2013).

    Article  PubMed  CAS  Google Scholar 

  35. 35.

    Ahsan, R., Mitra, A., Omar, S., Rahman Khan, M. Z. & Basith, M. A. Sol-gel synthesis of DyCrO3 and 10% Fe-doped DyCrO3 nanoparticles with enhanced photocatalytic hydrogen production abilities. RSC Advances 8, 14258–14267, (2018).

    Article  CAS  Google Scholar 

  36. 36.

    Gao, F. et al. Visible–Light Photocatalytic Properties of Weak Magnetic BiFeO3 Nanoparticles. Advanced Materials 19, 2889–2892 (2007).

    Article  CAS  Google Scholar 

  37. 37.

    Huang, F. et al. Peculiar magnetism of BiFeO3 nanoparticles with size approaching the period of the spiral spin structure. Scientific Reports 3 (2013).

  38. 38.

    Jalil, M. A. et al. Temperature-dependent phase transition and comparative investigation on enhanced magnetic and optical properties between sillenite and perovskite bismuth ferrite-rGO nanocomposites. Journal of Applied Physics 122, 084902, (2017).

    ADS  Article  CAS  Google Scholar 

  39. 39.

    Sun, A. et al. Magnetic Bi25FeO40-graphene catalyst and its high visible-light photocatalytic performance. RSC Advances 3, 4332–4340 (2013).

    Article  CAS  Google Scholar 

  40. 40.

    Wu, Y., Luo, H., Jiang, X., Wang, H. & Geng, J. Facile synthesis of magnetic Bi25FeO40/rGO catalyst with efficient photocatalytic performance for phenolic compounds under visible light. RSC Advances 5, 4905–4908 (2015).

    Article  CAS  Google Scholar 

  41. 41.

    Irfan, S. et al. The gadolinium (Gd3+) and Tin (Sn4+) Co-doped BiFeO3 nanoparticles as new solar light active photocatalyst. Scientific Reports 7, 42493 (2017).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  42. 42.

    Basith, M. A., Kurni, O., Alam, M. S., Sinha, B. L. & Ahmmad, B. Room temperature dielectric and magnetic properties of Gd and Ti co-doped BiFeO3 ceramics. Journal of Applied Physics 115, 024102, (2014).

    ADS  Article  CAS  Google Scholar 

  43. 43.

    Basith, M. et al. Simple top-down preparation of magnetic Bi0.9Gd0.1Fe1−xTixO3 nanoparticles by ultrasonication of multiferroic bulk material. Nanoscale 6, 14336–14342 (2014).

    ADS  Article  PubMed  CAS  Google Scholar 

  44. 44.

    Zhang, L. et al. Hydrothermal synthesis, influencing factors and excellent photocatalytic performance of novel nanoparticle-assembled Bi25MO40 tetrahedrons. CrystEngComm 17, 6527–6537 (2015).

    Article  CAS  Google Scholar 

  45. 45.

    Basith, M. et al. The 10% Gd and Ti co-doped BiFeO3: a promising multiferroic material. Journal of Alloys and Compounds 694, 792–799 (2017).

    Article  CAS  Google Scholar 

  46. 46.

    He, L. et al. Growth of TiO2 nanorod arrays on reduced graphene oxide with enhanced lithium-ion storage. Journal of Materials Chemistry 22, 19061–19066 (2012).

    Article  CAS  Google Scholar 

  47. 47.

    Yang, X.-F., Yang, J.-H., Zaghib, K., Trudeau, M. L. & Ying, J. Y. Synthesis of phase-pure Li2MnSiO4 @ C porous nanoboxes for high-capacity Li-ion battery cathodes. Nano Energy 12, 305–313 (2015).

    Article  CAS  Google Scholar 

  48. 48.

    Purushothaman, K. K., Saravanakumar, B., Babu, I. M., Sethuraman, B. & Muralidharan, G. Nanostructured CuO/reduced graphene oxide composite for hybrid supercapacitors. RSC Advances 4, 23485–23491 (2014).

    Article  CAS  Google Scholar 

  49. 49.

    Han, S. & Sung Kim, C. Weak ferromagnetic behavior of BiFeO3 at low temperature. Journal of Applied Physics 113, 17D921 (2013).

    Article  CAS  Google Scholar 

  50. 50.

    Ji, W., Li, M., Zhang, G. & Wang, P. Controlled synthesis of Bi25FeO40 with different morphologies: growth mechanism and enhanced photo-Fenton catalytic properties. Dalton Transactions 46, 10586–10593, (2017).

    Article  PubMed  CAS  Google Scholar 

  51. 51.

    Zhang, N. et al. Enhanced visible light photocatalytic activity of Gd-doped BiFeO3 nanoparticles and mechanism insight. Scientific Reports 6, 26467 (2016).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  52. 52.

    Dai, J., Xian, T., Di, L. & Yang, H. Preparation of BiFeO3-graphene nanocomposites and their enhanced photocatalytic activities. Journal of Nanomaterials 2013, 1 (2013).

    Google Scholar 

  53. 53.

    Pei, S. & Cheng, H.-M. The reduction of graphene oxide. Carbon 50, 3210–3228, (2012).

    Article  CAS  Google Scholar 

  54. 54.

    Becerril, H. A. et al. Evaluation of solution-processed reduced graphene oxide films as transparent conductors. ACS Nano 2, 463–470 (2008).

    Article  PubMed  CAS  Google Scholar 

  55. 55.

    Mattevi, C. et al. Evolution of electrical, chemical, and structural properties of transparent and conducting chemically derived graphene thin films. Advanced Functional Materials 19, 2577–2583 (2009).

    Article  CAS  Google Scholar 

  56. 56.

    Yang, D. et al. Chemical analysis of graphene oxide films after heat and chemical treatments by X-ray photoelectron and Micro-Raman spectroscopy. Carbon 47, 145–152 (2009).

    Article  CAS  Google Scholar 

  57. 57.

    Wang, X., Zhi, L. & Müllen, K. Transparent, conductive graphene electrodes for dye-sensitized solar cells. Nano Letters 8, 323–327 (2008).

    ADS  Article  PubMed  CAS  Google Scholar 

  58. 58.

    Pan, D., Zhang, J., Li, Z. & Wu, M. Hydrothermal route for cutting graphene sheets into blue-luminescent graphene quantum dots. Advanced Materials 22, 734–738 (2010).

    Article  PubMed  CAS  Google Scholar 

  59. 59.

    Kudin, K. N. et al. Raman spectra of graphite oxide and functionalized graphene sheets. Nano Letters 8, 36–41 (2008).

    ADS  Article  PubMed  CAS  Google Scholar 

  60. 60.

    Schniepp, H. C. et al. Functionalized single graphene sheets derived from splitting graphite oxide. The Journal of Physical Chemistry B 110, 8535–8539 (2006).

    Article  PubMed  CAS  Google Scholar 

  61. 61.

    Zhang, Q. et al. Constructing the magnetic bifunctional graphene/titania nanosheet-based composite photocatalysts for enhanced visible-light photodegradation of MB and electrochemical ORR from polluted water. Scientific Reports 7, 12296, (2017).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  62. 62.

    Congyang Zou, S. L., Shen, Z., Zhang, Y. & Jiang, N. Wenchao Ji. Efficient removal of ammonia with a novel graphene-supported BiFeO3 as a reusable photocatalyst under visible light. Chinese Journal of Catalysis 38, 20–28, (2017).

    Article  Google Scholar 

  63. 63.

    Sun, Q., Wang, P., Yu, H. & Wang, X. In situ hydrothermal synthesis and enhanced photocatalytic H2-evolution performance of suspended rGO/g-C3N4 photocatalysts. Journal of Molecular Catalysis A: Chemical 424, 369–376, (2016).

    Article  CAS  Google Scholar 

  64. 64.

    Xu, Y. et al. The synergistic effect of graphitic N and pyrrolic N for the enhanced photocatalytic performance of nitrogen-doped graphene/TiO2 nanocomposites. Applied Catalysis B: Environmental 181, 810–817, (2016).

  65. 65.

    Ruiyang Zhang, W. W., Dawei, Li, Fan, Dong & Ying, Zhou Three-dimensional MoS2/reduced graphene oxide aerogel as a macroscopic visible-light photocatalyst. Chinese Journal of Catalysis 38, 313–320, (2017).

    Article  Google Scholar 

  66. 66.

    Deng, J., Banerjee, S., Mohapatra, S. K., Smith, Y. R. & Misra, M. Bismuth iron oxide nanoparticles as photocatalyst for solar hydrogen generation from water. Journal of Fundamentals of Renewable Energy and Applications 1 (2011).

  67. 67.

    Ahsan, R., Khan, M. Z. R. & Basith, M. A. Determination of optical band gap of powder-form nanomaterials with improved accuracy. Journal of Nanophotonics 11, 046016 (2017).

    ADS  Article  Google Scholar 

  68. 68.

    Shockley, W. & Queisser, H. J. Detailed Balance Limit of Efficiency of p-n Junction Solar Cells. Journal of Applied Physics 32, 510–519, (1961).

    ADS  Article  CAS  Google Scholar 

  69. 69.

    Ruppel, W. & Wurfel, P. Upper limit for the conversion of solar energy. IEEE Transactions on Electron Devices 27, 877–882, (1980).

    ADS  Article  Google Scholar 

  70. 70.

    Shen, Y. et al. Evolution of the band-gap and optical properties of graphene oxide with controllable reduction level. Carbon 62, 157–164 (2013).

    Article  CAS  Google Scholar 

  71. 71.

    Maeda, K. in Photocatalysis: Fundamentals and Perspectives 295–317 (The Royal Society of Chemistry, 2016).

  72. 72.

    Nethercot, A. H. Prediction of Fermi Energies and Photoelectric Thresholds Based on Electronegativity Concepts. Physical Review Letters 33, 1088–1091 (1974).

    ADS  Article  CAS  Google Scholar 

  73. 73.

    Butler, M. & Ginley, D. Principles of photoelectrochemical, solar energy conversion. Journal of Materials Science 15, 1–19 (1980).

    ADS  Article  CAS  Google Scholar 

  74. 74.

    Deng, H., Hao, W. & Xu, H. First-principles calculations of novel sillenite compounds Bi24MO40 (M = Se or Te). Rare Metals 30, 135–139 (2011).

    Article  CAS  Google Scholar 

  75. 75.

    Rastogi, M., Bowen, C., Kushwaha, H. & Vaish, R. First principles insights into improved catalytic performance of BaTiO3-graphene nanocomposites in conjugation with experimental investigations. Materials Science in Semiconductor Processing 51, 33–41 (2016).

    Article  CAS  Google Scholar 

  76. 76.

    Li, X. & Zhu, H. The graphene-semiconductor Schottky junction. Physics Today 69, 46–51 (2016).

    Article  CAS  Google Scholar 

  77. 77.

    Leung, T. C., Kao, C. L., Su, W. S., Feng, Y. J. & Chan, C. T. Relationship between surface dipole, work function and charge transfer: Some exceptions to an established rule. Physical Review B 68, 195408 (2003).

    ADS  Article  CAS  Google Scholar 

  78. 78.

    Kim, S., Sinai, O., Lee, C.-W. & Rappe, A. M. Controlling oxide surface dipole and reactivity with intrinsic nonstoichiometric epitaxial reconstructions. Physical Review B 92, 235431 (2015).

    ADS  Article  CAS  Google Scholar 

  79. 79.

    Li, X., Yu, J., Wageh, S., Al-Ghamdi Ahmed, A. & Xie, J. Graphene in Photocatalysis: A Review. Small 12, 6640–6696, (2016).

    Article  PubMed  CAS  Google Scholar 

  80. 80.

    Bisquert, J., Garcia-Belmonte, G. & Fabregat-Santiago, F. Modelling the electric potential distribution in the dark in nanoporous semiconductor electrodes. Journal of Solid State Electrochemistry 3, 337–347, (1999).

    Article  CAS  Google Scholar 

  81. 81.

    Giménez, S. & Bisquert, J. Photoelectrochemical Solar Fuel Production. (Springer, 2016).

  82. 82.

    Miller, D. A. B. et al. Band-Edge Electroabsorption in Quantum Well Structures: The Quantum-Confined Stark Effect. Physical Review Letters 53, 2173–2176 (1984).

    ADS  Article  CAS  Google Scholar 

Download references


This work was financially supported by the Infrastructure Development Company Limited (IDCOL), Dhaka, Bangladesh and the Ministry of Education, Government of Bangladesh (Grant No. PS 14267).

Author information




M. A. Basith conceived the idea and designed the project. M. A. Basith and Ragib Ahsan analyzed the experimental results and wrote the manuscript. Ishrat Zarin contributed to prepare the initial draft of the manuscript. M.A. Jalil performed some of the experiments under the supervision of M. A. Basith. Finally, all authors approved the manuscript.

Corresponding author

Correspondence to M. A. Basith.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material


Supplementary Information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Basith, M.A., Ahsan, R., Zarin, I. et al. Enhanced photocatalytic dye degradation and hydrogen production ability of Bi25FeO40-rGO nanocomposite and mechanism insight. Sci Rep 8, 11090 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing