Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Tailoring carbon nanotubes optical properties through chirality-wise silicon ring resonators


Semiconducting single walled carbon nanotubes (s-SWNT) have an immense potential for the development of active optoelectronic functionalities in ultra-compact hybrid photonic circuits. Specifically, s-SWNT have been identified as a very promising solution to implement light sources in the silicon photonics platform. Still, two major challenges remain to fully exploit the potential of this hybrid technology: the limited interaction between s-SWNTs and Si waveguides and the low quantum efficiency of s-SWNTs emission. Silicon micro-ring resonators have the potential capability to overcome these limitations, by providing enhanced light s-SWNT interaction through resonant light recirculation. Here, we demonstrate that Si ring resonators provide SWNT chirality-wise photoluminescence resonance enhancement, releasing a new degree of freedom to tailor s-SWNT optical properties. Specifically, we show that judicious design of the micro-ring geometry allows selectively promoting the emission enhancement of either (8,6) or (8,7) SWNT chiralities present in a high-purity polymer-sorted s-SWNT solution. In addition, we present an analysis of nanometric-sized silicon-on-insulator waveguides that predicts stronger light s-SWNT interaction for transverse-magnetic (TM) modes than for conventionally used transverse-electric (TE) modes.


Driven by their outstanding electrical properties, semiconducting single walled carbon nanotubes (s-SWNTs) are being widely investigated for the realization of ultra-compact field effect transistors (FET), reaching the nanoscale1,2, with very high on-off current ratios3. Nevertheless, s-SWNTs also exhibit very interesting optical properties. For instance, s-SWNT are direct band gap semiconductors providing absorption, photo- and electro-luminescence at room temperatures from the visible to the mid-infrared wavelengths, which makes them a suitable material for the realization of on-chip light sources and detectors4,5,6,7. Indeed, just by properly choosing the applied voltage, the same s-SWNT-based device can be operated as a FET, light emitting diode (LED) or photodetector8. In addition, carbon nanotubes can have exceptional thermal conductivity that has already been exploited to demonstrate electrically driven emitters with direct modulation speeds in the GHz range9. Furthermore, s-SWNTs present intrinsically fast nonlinear Stark and Kerr effects10,11 that could enable the realization of low-power-consumption high performance electro-optical modulators. In addition, SWNTs have been widely used for the implementation of high-performance saturable absorbers in mode-locked lasers12,13,14. This features pose s-SWNTs as a very interesting nano-material for the realization of compact optoelectronic devices. Among the photonic platforms to exploit the outstanding properties of s-SWNT, silicon photonics has several advantages: its mature large-volume fabrication processes, ultra-compact optical waveguides and potential for integration with microelectronics. Hence, the hybrid s-SWNT integration on silicon photonic platform could open a new route towards the widespread of compact on-chip opto-electronic transceivers.

The band gap of s-SWNT is determined by their chirality. In fact, s-SWNT can have emission and absorption wavelengths all along the datacom (around 1300 nm wavelength)15,16,17 and telecom (around 1500 nm wavelength)8,18,19 ranges. Thus, proper s-SWNT chirality selection is a key feature for the realization of performing photonic devices. In this context, polymer-assisted selection techniques are a very interesting approach yielding high-purity s-SWNT solutions (with negligible traces of metallic carbon nanotubes)20 that are compatible with wafer-scale deposition processes21. Nonetheless, these solutions typically contain various s-SWNT chiralities. For instance, using Poly-9,9-di-n-octyl-fluorenyl-2,7-diyl (PFO) it is possible to select s-SWNTs with chiralities of (8,6), emitting around 1200 nm wavelength, and (8,7), emitting around 1300 nm wavelength. However, single s-SWNT chirality selection remains a challenge22,23,24.

Resonance enhancement of s-SWNT emission has been reported in micro-ring resonators25,26 and photonics crystal cavities17,27, that exploit tight light confinement and resonant light recirculation to maximize device-light-SWNT interaction. In this work, we demonstrate that integration with Si micro-ring resonators also provides SWNT chirality-dependent interaction enhancement, allowing further tunability of the optical properties of hybrid Si-s-SWNT photonic devices. We experimentally demonstrated that a proper design of the micro-resonator geometry allows promoting the resonance enhancement of either (8,6) or (8,7) s-SWNT chiralities present in PFO-sorted s-SWNT solution. These results open a new route towards single-chirality selection in hybrid Si-SWNT devices, even if the SWNT solution contains various chiralities.

Interaction between s-SWNT and Si photonic waveguides is governed by the s-SWNT geometry and the waveguide mode field distribution. The very large aspect ratio of s-SWNTs, with nanometer-scale diameters and micrometer-scale lengths, makes them behave like dipoles. This means that the maximum emission (and absorption) occurs for an electromagnetic field aligned to the long s-SWNT axis28,29. Therefore, Si photonic waveguides aiming to efficiently interact with s-SWNTs should support modes with a large evanescent field parallel to the s-SWNTs. Conventional Si waveguides support quasi-transverse electric (TE) modes, with electric field (transversal to the light propagation) oriented parallel to the chip surface, and quasi-transverse magnetic (TM) modes, with transversal electric field perpendicular to the chip surface. Most of the s-SWNT deposition methods (drop casting, spin coating, dielectrophoresis) result in networks of s-SWNTs arranged along the chip surface. Thus, previous works on the integration of s-SWNTs and Si photonic structures focused on the use of TE modes. This way, s-SWNTs have been efficiently coupled to the TE modes of conventional strip waveguides30, slot26 and strip31 micro-ring resonators or 1-D27 and 2-D17 photonic crystal cavities. However, TE modes concentrate most of the evanescent field in the vertical waveguide walls (see Fig. 1a), having a strong interaction with the sidewall roughness arising from the etching process, thus resulting in comparatively high propagation loss. Conversely, TM modes concentrate most of the evanescent field in the horizontal walls (see Fig. 1b), thereby allowing lower propagation loss32. In addition, for the same waveguide dimensions, e.g. 220 nm thick and 350 nm wide waveguide, TM modes are typically more delocalized, having a larger overlap with the surrounding medium. The problem is that optimizing the interaction between s-SWNTs and the dominant component of the electric field in TM modes (perpendicular to the chip surface) would require placing the s-SWNTs vertically on the waveguide top surface (see inset in Fig. 1b). This ideal scenario, although possible, is technologically challenging and compromises the feasibility of the approach. Here, we propose a new route to circumvent this limitation by exploiting the hybrid nature of the optical modes in SOI waveguides with sub-wavelength scale core dimensions. The proposed approach is to exploit the longitudinal electric field component in TM modes to interact with SWNTs aligned parallel to the chip surface, thereby obviating the need for technologically challenging vertical SWNT deposition. Owing to the vast index difference between Si and SiO2 and the ultra-tight confinement in 220-nm-thick SOI nanowires, (quasi-)TM modes can have a strong electric field component longitudinal to the light propagation. This longitudinal mode field component, parallel to the chip surface, can be advantageously exploited to interact with s-SWNTs. Indeed, we show that TM modes can provide a longitudinal electric field on top of the Si waveguides (where the s-SWNTs are placed), equal or even larger than the transverse electric field in TE modes. Here, we exploit the large index contrast of the SOI platform and waveguide geometry engineering to demonstrate that, opposite to the common knowledge, TM optical modes can efficiently interact with drop-casted s-SWNTs arranged along the chip surface. We also developed a selective deposition technique that provides simple and tight control of the regions where s-SWNTs interact with the Si waveguides, minimizing detrimental light absorption from non-excited SWNTs. We theoretically and experimentally studied the s-SWNTs interaction with SOI micro-ring resonators, implemented with strip waveguides optimized to maximize the longitudinal TM component and optimized to yield resonant-enhancement at specific wavelength ranges corresponding to either (8,6) or (8,7) s-SWNT chiralities.

Figure 1

Electric field distribution for waveguide width of Wwg = 350 nm, normalized to the total mode power, and figure of merit ξcladd,p as a function of waveguide width for (a) transversal Ex, (b) transversal Ey and (c) longitudinal Ez components of both fundamental TE and TM modes at wavelength of 1300 nm. Insets schematically show preferred SWNTs orientation for maximized light-SWNTs interaction for each component of the electric field.


First, we optimize the waveguide cross section to maximize the longitudinal TM component, Ez, on top of the waveguide. To do so, we follow the conventional approach in active hybrid Si photonic devices and calculate the dielectric energy confinement in the active region, SWNT in this case33. We define the figure of merit ξcladd,p which accounts for the percentage of the dielectric energy confinement on top of the Si waveguide (slashed region in Fig. 1). We calculate ξcladd,p for each electric field component (Ep with p = x, y, z for the Ex, Ey and Ez components respectively as

$${\xi }_{cladd,p}=\frac{{\int }_{cladd}\varepsilon ({\rm{x}},{\rm{y}}){|{E}_{p}({\rm{x}},{\rm{y}})|}^{2}{\rm{dxdy}}}{{\int }_{total}\varepsilon ({\rm{x}},{\rm{y}})[{|{E}_{x}({\rm{x}},{\rm{y}})|}^{2}+{|{E}_{y}({\rm{x}},{\rm{y}})|}^{2}+{|{E}_{z}({\rm{x}},{\rm{y}})|}^{2}]{\rm{dxdy}}},$$

where ε is medium permittivity. As conventionally done when modeling these polymer-sorted SWNTs17,25,26, we considered a homogeneous top cladding with a refractive index of 1.6 (similar to that of polyfluorene34), which emulates the scenario of drop casting deposition. We fixed the Si waveguide thickness to 220 nm, and varied the waveguide width from 250 nm to 500 nm (Wwg in Fig. 1). Figure 1 shows the ξcladd,p, calculated with an eigenmode solver tool35, as a function of the waveguide width for a wavelength of 1300 nm. The transversal Ey component from the TM mode has the largest figure of merit, \({\xi }_{cladd,y}\sim \mathrm{12 \% }\). However, optimal interaction with the Ey field would require vertically aligned SWNTs (see inset of Fig. 1b), which makes this solution technologically challenging. Conversely, for both, transversal Ex and longitudinal Ez components, the preferred SWNTs orientations are parallel to the chip surface (see inset of Fig. 1a and c), which makes them very interesting for scenarios relying on planar deposition techniques (drop casting, spin coating, etc). According to our calculations, the figure of merit for the Ez component in the TM mode can be larger than that of Ex component in the TE mode, which is conventionally optimized for hybrid SWNT integration. We then chose a waveguide width of Wwg = 350 nm, that presents a figure of merit of \({\xi }_{cladd,z}\ge \mathrm{4.5 \% }\) (with \({\xi }_{cladd,x}\sim \mathrm{0.5 \% }\) and \({\xi }_{cladd,y}\sim \mathrm{12 \% }\)), close to the maximum for TM mode with a total dielectric energy confinement in the cladding of 20%. Moreover, this waveguide width provides single-mode operation and good optical confinement that keep low losses and sharp bending. Electric field distributions for all components of TE and TM modes for the selected waveguide are shown in the top panels of Fig. 1.

Then we shaped up the TM response of micro-ring resonators implemented with the optimized waveguide. The goal was to yield a strong light matter interactions in a specific bandwidth, matching the emission range of a given s-SWNT chirality. By adjusting the geometry of the micro-ring, it was then possible to tune the optimal micro-resonator wavelength, releasing an extra degree of freedom to selectively promote light s-SWNT interaction for only (8,6) or (8,7) s-SWNT present in our solution, with emission around 1200 nm and 1300 nm, respectively. As schematically depicted in the inset of Fig. 2, we used an all-pass ring-resonator configuration where the ring resonator waveguide, with waveguide width of Wring, was evanescently coupled to an access strip waveguide (width of Wbus), separated from the ring by a gap distance G.

Figure 2

Simulated resonant extinction ratio for TM modes, defined as the ratio between on-resonance and off-resonance transmission, considering G between 80 nm and 260 nm. Inset: Schematic view of micro-ring resonator with bus waveguide.

The resonant behavior of a coupled micro-ring resonator is strongly dependent on the coupling between the ring and the bus waveguide. Light recirculation inside the ring (hence energy storage, and electric field enhancement) is maximal when coupling between the ring and the bus equals the loss inside the ring (critical coupling condition)36. Aiming to yield selective resonance enhancement of the SWNT emission, we decided to implement an asymmetric coupling scheme. To do this, we set a bus waveguide width of Wbus = 270 nm and ring waveguide width of Wring = 350 nm (providing strong ξcladd,z). As the bus and ring waveguides have different widths, modes propagating through them have different phase propagation constants, precluding perfect phase matching. This results in a lower power coupling between the waveguides and a shorter beat-length (distance for maximum power transfer between the waveguides). For the short couplers used here, the coupling strength is directly proportional to the overlap between the modes of the bus and ring waveguides. The mode profile is more deconfined for longer wavelengths, resulting in larger overlaps, therefore stronger coupling. On the other hand, it can be shown that the bandwidth of the coupler is related to the beat-length dispersion37. Thus, this asymmetric configuration yields a strong chromatic dispersion of the bus-to-ring coupling ratio, i.e., for a given bus-to-ring gap (G), critical coupling condition is achieved for a comparatively narrow bandwidth. Hence, we can choose the wavelength range where resonant light recirculation (thus light-SWNT interaction) is maximized just by properly choosing the gap G between the ring and the bus waveguide. We chose a ring radius of R = 5 μm, that yields a free spectral range (wavelength separation between consecutive resonances) of 12 nm, easily discernible with standard spectrometer. Figure 2 shows the resonance extinction ratio for TM modes, calculated with the finite difference time domain (FDTD) tool35. It can be seen that critical coupling condition (corresponding to deep resonances with extinction ratio greater than 30 dB) was achieved for narrow wavelength ranges of 10 nm, with optimum range moving towards shorter wavelengths for decreasing gap widths.

We fabricated different ring resonators varying the bus-to-ring gap (G) between 80 nm and 270 nm. Tapered waveguides are used to inject/extract light through the chip facet, with a coupling loss of 10 dB. This insertion loss may be reduced, e.g. by implementing high-efficiency fiber-chip grating couplers38. Propagation loss of the Si waveguides is in the 3–5 dB/cm, range, which is compatible with envisioned datacom and telecom applications39. As described in Methods, we defined interaction windows in the coupling region between the bus waveguide and ring resonator and deposited a high-purity s-SWNT solution.

The linear response of the devices was experimentally characterized using a tunable laser and automatic data acquisition system, CT400 from Yenista (see Methods and the inset in Fig. 3a). Input light polarization was set by a polarization controller. Light was injected and extracted from the chip using tapered Si waveguides and lensed fibers (10 dB loss per facet). Note that because of the limited range of our tunable source (between 1260 nm and 1350 nm) we were not able to inspect the region around 1200 nm wavelength, corresponding to the emission of (8,6) s-SWNT. Figure 3b shows the measured resonance extinction ratio in our micro-rings with drop-casted s-SWNT, as a function of the wavelength for different bus-to-ring gaps. The optimum wavelength range shifts to shorter wavelengths for decreasing gaps. Results in Fig. 3 show that the critical coupling condition is met for a narrow wavelength range, with optimum wavelength that increases with the gap, in good agreement with our calculations. The ring resonators with s-SWNTs yield quality factors for TM modes of \(Q\sim 4000\) and extinction ratio of 10 dB at around 1300 nm wavelength for a bus-to-ring gap between 200 nm and 250 nm. On the other hand, the best quality factor for TE polarization is around \(Q\sim 4000\), with a gap of 100 nm. The difference with calculated values shown in Fig. 2, can be attributed to scattering losses due to sidewall roughness and absorption in the s-SWNT, not considered in the simulations. Similar ring resonators without s-SWNT typically yield quality factor, Q, up to 10000. The small interaction window, of 1.5μm radious used for the deposition of SWNTs did not induce excess loss to the ring transmission. However, the perturbation produced by the presence of the s-SWNTs (mainly due to absroption loss) is enough to reduce the quality factor of the resonances.

Figure 3

Measured linear spectral response for TM mode of Si micro-ring resonators with bus waveguide width of Wbus = 270 nm, ring waveguide width of Wring = 350 nm, ring radius of R = 5 μm for (a) fixed bus-to-ring gap of G = 220 nm, and (b) bus-to-ring gap varying between 80 nm and 270 nm. Dashed line indicates position of spectrum for gap G = 220 nm, shown in (a).

Then the resonant enhancement of the s-SWNTs photoluminescence in the ring resonators was characterized. For comparison, Fig. 4a shows the normalized photoluminescence of the high purity s-SWNTs solution deposited onto an unpatterned SOI sample under pumping excitation at wavelength of 735 nm. The s-SWNTs emission presented two wideband emission regions around 1200 nm and 1300 nm wavelengths corresponding to the two main s-SWNT chiralities available in the sample, (8,6) and (8,7), respectively. The characterization of the photoluminescence response of our Si micro-ring resonators was performed by pumping the s-SWNTs layer from the surface, focusing the light coming from a Ti:Sa laser with an objective. We used an objective microscope with a magnification of 50X and NA of 0.55 that generated an excitation beam with a radius of 1.5 μm. We collected the generated photoluminesce at the facet of the chip using a polarization-maintaining lensed fiber and polarization splitter to discern contribution from TE and TM modes. TE and TM modes have different effective index and group index. This means that ring resonances, thus emission enhancement, occur at different wavelengths with a different free spectral range (distance between consecutive resonances). Therefore, if there was some TE signal passing through the polarization splitter, its contribution would be shifted compared with respect to the TM one. Note that illuminating the SWNTs with the Ti:Sa laser changes their absorption properties, offsetting the optimal coupling gap, compared with the linear measurements shown in Fig. 3. Here, we compared the photoluminescence spectrum of a micro-ring resonator with gap of G = 250 nm, in the optimal photoluminescence enhancement region for 1300 nm wavelength, when the polarization of the excitation beam was aligned with the transversal component (perpendicular to the waveguide) or longitudinal Ez component (aligned along the waveguide). As shown in Fig. 4b, tuning the pump beam polarization from transversal (Ex) to longitudinal (Ez) components it was possible to favor the excitation of the TM modes in the ring. These results are in good agreement with near-field scanning experiments that exploited a similar effect to image TM modes in Si micro-ring resonators40. In the following experiments we kept the pump beam aligned with the longitudinal Ez component.

Figure 4

(a) Normalized photoluminescence signal of SWNTs solution drop casted on unpatterned SOI sample. Excitation wavelength of 735 nm with vertical excitation/collection. Inset: Schematic view unpatterned SOI sample with a scheme of excitation of SWNTs and collection of the PL from surface. (b) Photoluminescence spectrum for a ring resonator of radius R = 5 μm and bus-to-ring gap G = 250 nm. The excitation is performed from the chip surface with a wavelength of 735 nm and the generated photoluminescence signal coupled to bus waveguide is collected from the chip facet. Collected photoluminescence signal when pump laser is transversal and longitudinal with respect to the propagation axis are represented in red and blue lines respectively. Inset: Schematic view of ring resonator coupled to a bus waveguide with both polarization schemes, transversal (aligned with the Ex component) and longitudinal (parallel to Ez component).

In Fig. 5a we plot the upper envelope of the photoluminescence signal collected at the output bus waveguide for different gaps between the ring and the bus waveguide. Each of the rings will have slightly different resonant wavelength (mainly arising from small fabrication imperfections), by representing upper envelope we remove this spurious effect, yielding smoother plots that make the gap effect clearer. In Fig. 5b and c we show two examples of measured spectrum and calculated upper envelope. From Fig. 5a, it is apparent that, as expected from the micro-ring design, smaller gaps yield stronger photoluminescence signal for (8,6) s-SWNTs, while larger gaps promote emission from (8,7) chirality. Note that the photoluminescence signal around 1250 nm wavelength is weak, compared to 1200 nm and 1290 nm wavelength where (8,6) and (8,7) chiralities emit. Thus, it is not possible to clearly see the smooth resonant wavelength shift predicted by simulations in Fig. 2.

Figure 5

(a) Normalized photoluminescence spectrum of SWNTs deposited on Si micro-ring resonators with bus waveguide width of Wbus = 270 nm, ring waveguide width of Wring = 350 nm, ring radius of R = 5 μm, and bus-to-ring gap, G varying between 80 nm and 270 nm. SWNTs are excited at 735 nm wavelength from the chip surface using a microscope objective and the generated PL is collected from the chip facet with polarization maintaining lensed fiber. Detail of collected PL for (b) G = 260 nm, and (c) G = 90 nm. (d) Figure of merit estimated from measurements.

To compare the photoluminescence resonant enhancement for (8,6) and (8,7) chiralities, we have defined the resonance enhancement factor, α, as the ratio between on-resonance (ION) and off-resonance (IOFF) intensities, as

$$\alpha =\frac{{I}_{ON}}{{I}_{OFF}}.$$

We computed this factor for wavelengths around 1200 nm, α(1200), and 1290 nm, α(1290). Then we defined the figure of merit, γ, as the ratio between the resonance enhancement factors for this two wavelengths:

$$\gamma =10\,\mathrm{log}(\frac{\alpha (1290)}{\alpha (1200)}).$$

In Fig. 5d we display the figure of merit γ, estimated from measurements, as a function of the bus-to-ring gap. Smaller gaps favor resonance enhancement of s-SWNTs with (8,6) chirality (\(\gamma < 0\)), with emission around 1200 nm wavelength, while larger gaps promote the resonant enhancement of s-SWNTs with (8,7) chirality (\(\gamma > 0\)), with emission around 1300 nm wavelength. Furthermore, we can observe in Fig. 5d how the maximum enhancement, smoothly shifts towards longer wavelengths, as the gap increases, in good agreement with calculations shown in Fig. 2.


The outstanding electrical and optical properties of s-SWNT make them a very promising solution for photonics and more especially for the silicon photonics. Despite the great development of polymer-based s-SWNT processing techniques, yielding quasi-impurity-free solutions, single SWNT chirality selection remains an issue. In this work, we experimentally demonstrated that by integrating the s-SWNT onto Si micro-ring resonators, it is possible to realize SWNT chirality-wise resonant enhancement of the emission, allowing an added SWNT chirality selection mechanism. We experimentally show, for the first time, that by combining a novel selective deposition process (based on localized interaction windows and drop casting) and engineered Si waveguides for the ring resonator and bus waveguide, we selectively promote the resonant enhancement of either (8,6) or (8,7) s-SWNT chiralities present in our solution. Unlike previously reported hybrid Si-SWNT devices17,27,30,31, the ring resonators presented here exploit the strong longitudinal electric field component of the TM mode to interact with the SWNT. By providing selective chirality selection and efficient interaction with TM modes, these results unlock two new degrees of freedom to implement s-SWNT-based devices for the silicon photonics platform. This technique could be further improved in the future, e.g. by implementing slot ring resonators that may result in nearly a 60% resonant enhancement increase26.


The s-SWNTs were prepared using a polymer-sorting technique that provides high purity solutions containing s-SWNTs emitting around 1200 nm wavelength, chirality of (8,6), and 1300 nm wavelength, chirality of (8,7)41. We started the process with a commercial s-SWNT powder (HiPCO from Unydim), mixed with the polymer Poly-9,9-di-n-octyl-fluorenyl-2,7-diyl (PFO, Sigma-Aldrich) and toluene. The mixture, with the ratio of s-SWNT (5 mg): PFO (20 mg): toluene (30 ml), was homogenized by sonication and the supernatant solution was collected after 1 hour of ultracentrifugation at 150000 g. Finally, we drop-casted the purified s-SWNTs solution onto the Si chip and annealed 15 minutes at 180 °C.

The ring resonators were fabricated in silicon-on-insulator (SOI) wafers with 220 nm thick silicon film and 2 μm thick buried oxide layer. The photonic structures were defined by electron beam lithography followed by inductively coupled plasma etching. A hydrogen silses-quioxane (HSQ) cladding, with refractive index of 1.45 and thickness of 800 nm, was deposited by spin coating and an additional lithography step was performed to form small circular aperture in the coupling regions between the micro-ring resonators and the bus waveguides. The HSQ cladding isolated the waveguide from the deposited s-SWNTs everywhere except in the interaction windows, which have a diameter of 3 μm, matching the size of the Ti:Sa excitation spot for pumping. This scheme ensured that all s-SWNTs interacting with the Si micro-resonators were under the excitation illumination, minimizing extra losses arising from unwanted absorption from non-excited s-SWNTs.

The linear response of the micro-ring resonators was characterized by injecting the light from a tunable Yenista laser source (1260 nm–1350 nm wavelength) and collecting the transmitted signal with polarization maintaining lensed fibers through input and output waveguides at the chip facets. The responses of the devices were collected using an automatic data acquisition system, CT400 from Yenista. Polarization of the light injected into the chip was controlled with a polarization rotator and polarizer at the input. To characterize the resonant enhancement of SWNTs photoluminescence, SWNTs were excited from the surface of the chip with a continuous wave Titane Sapphire (Ti:Sa) laser and the generated photoluminescence coupled to the waveguide was collected at the chip facet through the output bus waveguide using a polarization maintaining lensed fiber. The Ti:Sa excitation beam passed through a polarization beam splitter, to control the polarization state, through a low pass wavelength filter, to remove higher order harmonics of the laser, and was finally focused onto the chip surface with a microscope objective (50x, NA = 0.55, excitation beam diameter of 1.5 μm). The pump power, measured before the objective, was 1.5 mW and the wavelength was chosen to match the S22 excitonic transition of SWNTs (around 735 nm wavelength). The collected spectrum was analyzed with a 320 mm long spectrometer with a 950 lines/mm grating, coupled to a nitrogen-cooled InGaAs array with 512 pixels. All experiments were realized at room temperature and air condition.


  1. 1.

    Qiu, C. et al. Scaling carbon nanotube complementary transistors to 5-nm gate lengths. Science 355, 271–276 (2017).

    Article  PubMed  ADS  CAS  Google Scholar 

  2. 2.

    Cao, Q., Tersoff, J., Farmer, D. B., Zhu, Y. & Han, S.-J. Carbon nanotube transistors scaled to a 40-nanometer footprint. Science 356, 1369–1372 (2017).

    Article  PubMed  ADS  CAS  Google Scholar 

  3. 3.

    Qiu, C. et al. Carbon nanotube feedback-gate field-effect transistor: Suppressing current leakage and increasing on/off ratio. ACS Nano 9, 969–977 (2015).

    Article  PubMed  CAS  Google Scholar 

  4. 4.

    Liu, Y. et al. Room temperature infrared imaging sensors based on highly purified semiconducting carbon nanotubes. Nanoscale 7, 6805–6812 (2015).

    Article  PubMed  ADS  CAS  Google Scholar 

  5. 5.

    Wang, S. et al. High-performance carbon nanotube light-emitting diodes with asymmetric contacts. Nano Lett. 11, 23–29 (2010).

    Article  PubMed  ADS  CAS  Google Scholar 

  6. 6.

    Wang, F. et al. High conversion efficiency carbon nanotube-based barrier-free bipolar-diode photodetector. ACS Nano 10, 9595–9601 (2016).

    Article  CAS  Google Scholar 

  7. 7.

    Mueller, T. et al. Efficient narrow-band light emission from a single carbon nanotube p–n diode. Nature Nanotech. 5, 27–31 (2010).

    Article  ADS  CAS  Google Scholar 

  8. 8.

    Balestrieri, M. et al. Polarization-sensitive single-wall carbon nanotubes all-in-one photodetecting and emitting device working at 1.55 μm. Adv. Funct. Mater. 27, 1702341 (2017).

    Article  CAS  Google Scholar 

  9. 9.

    Mori, T., Yamauchi, Y., Honda, S. & Maki, H. An electrically driven, ultrahigh-speed, on-chip light emitter based on carbon nanotubes. Nano Lett. 14, 3277–3283 (2014).

    Article  PubMed  ADS  CAS  Google Scholar 

  10. 10.

    Yoshida, M., Kumamoto, Y., Ishii, A., Yokoyama, A. & Kato, Y. K. Stark effect of excitons in individual air-suspended carbon nanotubes. Appl. Phys. Lett. 105, 161104 (2014).

    Article  ADS  CAS  Google Scholar 

  11. 11.

    Margulis, V. A., Gaiduk, E. & Zhidkin, E. Quadratic electro-optic effects in semiconductor carbon nanotubes. Phys. Lett. A 258, 394–400 (1999).

    Article  ADS  CAS  Google Scholar 

  12. 12.

    Chiu, J.-C. et al. Concentration effect of carbon nanotube based saturable absorber on stabilizing and shortening mode-locked pulse. Opt. Express 18, 3592–3600 (2010).

    Article  PubMed  ADS  CAS  Google Scholar 

  13. 13.

    Cheng, K.-N. et al. Single- and double-walled carbon nanotube based saturable absorbers for passive mode-locking of an erbium-doped fiber laser. Laser Phys. 23, 045105-1–045105-9 (2013).

    ADS  Google Scholar 

  14. 14.

    Cheng, K.-N., Lin, Y.-H., Yamashita, S. & Lin, G.-R. Harmonic order-dependent pulsewidth shortening of a passively mode-locked fiber laser with a carbon nanotube saturable absorber. Photon. Technol. Lett. 4, 1542–1552 (2013).

    Google Scholar 

  15. 15.

    Lee, H. W. et al. Selective dispersion of high purity semiconducting single-walled carbon nanotubes with regioregular poly (3-alkylthiophene) s. Nature Comm. 2, 541 (2011).

    Article  CAS  Google Scholar 

  16. 16.

    Gomulya, W. et al. Semiconducting single-walled carbon nanotubes on demand by polymer wrapping. Adv. Mater. 25, 2948–2956 (2013).

    Article  PubMed  CAS  Google Scholar 

  17. 17.

    Hoang, T. H. C. et al. Narrow-linewidth carbon nanotube emission in silicon hollow-core photonic crystal cavity. Opt. Lett. 42, 2228–2231 (2017).

    Article  PubMed  ADS  Google Scholar 

  18. 18.

    Mistry, K. S., Larsen, B. A. & Blackburn, J. L. High-yield dispersions of large-diameter semiconducting single-walled carbon nanotubes with tunable narrow chirality distributions. ACS Nano 7, 2231–2239 (2013).

    Article  PubMed  CAS  Google Scholar 

  19. 19.

    Tange, M., Okazaki, T. & Iijima, S. Selective extraction of semiconducting single-wall carbon nanotubes by poly (9, 9-dioctylfluorene-alt-pyridine) for 1.5 μm emission. ACS Appl. Mater. Interfaces 4, 6458–6462 (2012).

    Article  PubMed  CAS  Google Scholar 

  20. 20.

    Fong, D. & Adronov, A. Recent developments in the selective dispersion of single-walled carbon nanotubes using conjugated polymers. Chem. Sci (2017).

  21. 21.

    Brady, G. J. et al. Polyfluorene-sorted, carbon nanotube array field-effect transistors with increased current density and high on/off ratio. ACS Nano 8, 11614–11621 (2014).

    Article  PubMed  CAS  Google Scholar 

  22. 22.

    Subbaiyan, N. K. et al. Role of surfactants and salt in aqueous two-phase separation of carbon nanotubes toward simple chirality isolation. ACS Nano 8, 1619–1628 (2014).

    Article  PubMed  CAS  Google Scholar 

  23. 23.

    Tu, X., Manohar, S., Jagota, A. & Zheng, M. DNA sequence motifs for structure-specific recognition and separation of carbon nanotubes. Nature 460, 250–253 (2009).

    Article  PubMed  ADS  CAS  Google Scholar 

  24. 24.

    Ao, G., Streit, J. K., Fagan, J. A. & Zheng, M. Differentiating left-and right-handed carbon nanotubes by DNA. J. Am. Chem. Soc. 138, 16677–16685 (2016).

    Article  PubMed  CAS  Google Scholar 

  25. 25.

    Noury, A., Le Roux, X., Vivien, L. & Izard, N. Enhanced light emission from carbon nanotubes integrated in silicon micro-resonator. Nanotechnology 26, 345201 (2015).

    Article  PubMed  CAS  Google Scholar 

  26. 26.

    Durán-Valdeiglesias, E. et al. Integration of carbon nanotubes in silicon strip and slot waveguide micro-ring resonators. IEEE Trans. Nanotechnol 15, 583 (2016).

    Article  ADS  CAS  Google Scholar 

  27. 27.

    Miura, R. et al. Ultralow mode-volume photonic crystal nanobeam cavities for high efficiency coupling to individual carbon nanotube emitters. Nature Comm. 5, 5580 (2014).

    Article  CAS  Google Scholar 

  28. 28.

    Misewich, J. et al. Electrically induced optical emission from a carbon nanotube FET. Science 300, 783–786 (2003).

    Article  PubMed  ADS  CAS  Google Scholar 

  29. 29.

    Barkelid, M., Steele, G. A. & Zwiller, V. Probing optical transitions in individual carbon nanotubes using polarized photocurrent spectroscopy. Nano Lett. 12, 5649–5653 (2012).

    Article  PubMed  ADS  CAS  Google Scholar 

  30. 30.

    Gaufres, E. et al. Light emission in silicon from carbon nanotubes. ACS Nano 6, 3813–3819 (2012).

    Article  PubMed  CAS  Google Scholar 

  31. 31.

    Noury, A., Le Roux, X., Vivien, L. & Izard, N. Controlling carbon nanotube photoluminescence using silicon microring resonators. Nanotechnology 25, 215201 (2014).

    Article  PubMed  ADS  CAS  Google Scholar 

  32. 32.

    Densmore, A. et al. A silicon-on-insulator photonic wire based evanescent field sensor. IEEE Photon. Technol. Lett. 18, 2520–2522 (2006).

    Article  ADS  CAS  Google Scholar 

  33. 33.

    Osgood, R. M. et al. Engineering nonlinearities in nanoscale optical systems: physics and applications in dispersion-engineered silicon nanophotonic wires. Adv. Opt. Photonics 1, 162–235 (2009).

    Article  ADS  CAS  Google Scholar 

  34. 34.

    Campoy-Quiles, M., Etchegoin, P. & Bradley, D. D. Exploring the potential of ellipsometry for the characterisation of electronic, optical, morphologic and thermodynamic properties of polyfluorene thin films. Synth. Met. 155, 279–282 (2005).

    Article  CAS  Google Scholar 

  35. 35.

    Mode Solutions. Vancouver: Lumerical Solutions Inc.

  36. 36.

    Bogaerts, W. et al. Silicon microring resonators. Laser & Photon. Rev. 6, 47–73 (2012).

    Article  ADS  CAS  Google Scholar 

  37. 37.

    Zhang, W., Serna, S., Le Roux, X., Vivien, L. & Cassan, E. Highly sensitive refractive index sensing by fast detuning the critical coupling condition of slot waveguide ring resonators. Opt. Lett. 41, 532–535 (2016).

    Article  PubMed  ADS  CAS  Google Scholar 

  38. 38.

    Benedikovic, D. et al. L-shaped fiber-chip grating couplers with high-directionality and low-reflectivity fabricated with deep-UV lithography. Opt. Lett. 42, 3439–3442 (2017).

    Article  PubMed  ADS  PubMed Central  Google Scholar 

  39. 39.

    Zhang, W. et al. Silicon photonics R&D and manufacturing on 300-mm wafer platform. J. Light. Technol. 34, 286–295 (2016).

    Article  Google Scholar 

  40. 40.

    La China, F. et al. Near-field Fano-imaging of TE and TM modes in silicon microrings. ACS Photonics 2, 1712–1718 (2015).

    Article  CAS  Google Scholar 

  41. 41.

    Izard, N. et al. Semiconductor-enriched single wall carbon nanotube networks applied to field effect transistors. Appl. Phys. Lett. 92, 243112 (2008).

    Article  ADS  CAS  Google Scholar 

Download references


This work was supported by the FET project FP7 618025 CARTOON and by the European Research Council (ERC) POPSTAR-grant agreement N° 647342. The sample fabrication has been performed at the Plateforme de Micro-Nano-Technologie/C2N, which is partially funded by the “Conseil Général de l’Essonne”. This work was partly supported by the French RENATECH network. Authors thank Anne-Lise Coutrot from Laboratoire Charles Fabry, France and Stéphane Xavier from Thales Research & Technology, France for their fruitful help in device fabrication.

Author information




W.Z., E.C. and S.S. performed the optical simulations. X.L.R., W.Z. and E.D.V. fabricated the Si samples. E.D.V. and A.F. prepered the SWNT solution. The photoluminescence characterization was performed by E.D.V. with the help of C.A.R., W.Z. and L.V. The data analisys was performed by E.D.V., C.A.R., W.Z., E.C., L.V., D.M.M., N.C., F.B. and M.G. All authors discussed the results and contributed to writing the manuscript.

Corresponding author

Correspondence to Laurent Vivien.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Durán-Valdeiglesias, E., Zhang, W., Alonso-Ramos, C. et al. Tailoring carbon nanotubes optical properties through chirality-wise silicon ring resonators. Sci Rep 8, 11252 (2018).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing