Abstract
In this study, a novel approach to the fabrication of a multimodal temperature and force sensor on ultrathin, conformable and flexible substrates is presented. This process involves coupling a charge-modulated organic field-effect transistor (OCMFET) with a pyro/piezoelectric element, namely a commercial film of poly-vinylene difluoride (PVDF). The proposed device is able to respond to both pressure stimuli and temperature variations, demonstrating the feasibility of the approach for the development of low-cost, highly sensitive and conformable multimodal sensors. The overall thickness of the device is 1.2 μm, being thus able to conform to any surface (including the human body), while keeping its electrical performance. Furthermore, it is possible to discriminate between simultaneously applied temperature and pressure stimuli by coupling sensing surfaces made of poled and unpoled spin-coated PVDF-trifluoroethylene (PVDF-TrFE, a PVDF copolymer) with OCMFETs. This demonstrates the possibility of creating multimodal sensors that can be employed for applications in several fields, ranging from robotics to wearable electronics.
Similar content being viewed by others
Introduction
The increasing ubiquity of portable and wearable technologies has resulted in an increasing interest in flexible, conformable and lightweight electronic devices. Since the discovery of conductive polymers1, a significant amount of research effort has been devoted to devices that can be conformed to different substrates, resulting in the development of new techniques for the fabrication of flexible photovoltaic modules2, displays3 and printed circuits4,5. Furthermore, the recent rise of the so-called “tattoo electronics” has pushed further the innovation on flexible and ultra-conformable electronic devices that can be transferred onto the skin, particularly meant for biomedical applications.
Organic electronics represents the natural candidate for the fulfillment of the increasing needs of this emerging application field, since the employed materials are usually biocompatible, transparent and intrinsically flexible. Furthermore, within this field innovative fabrication techniques offer unprecedented versatility, allowing the realization of a broad range of different devices onto large areas and at low cost6.
An interesting example of this new trend is represented by the work of John Roger’s group, who has investigated materials that are able to replicate the mechanical properties of the skin by proposing a novel approach towards the development of a variety of conformable “epidermal electronic systems”. These systems are specifically engineered in order to adhere to the skin and they include several kinds of electronic devices, such as sensors, light-emitting diodes, photodetectors7.
Other interesting approaches have been proposed to design ultra-flexible electronics for biomedical applications, such as the one proposed by Campana et al.8, who presented a conformable organic electrochemical transistor (OECT) on a fully resorbable bioscaffold manufactured using poly (L-lactide-co-glycolide) for recording electrocardiographic (ECG) data. Kaltenbrunner et al.9 introduced an ultra-flexible and extremely stress-resilient electronic circuit fabricated on a very thin polyethylene naphthalate sheet (1.2 µm). Recently, Lai et al. successfully fabricated complementary inverters and single-stage amplifiers with a sub-micrometer thickness on polymer nanosheets for epidermal electronics applications10. Using a different approach, Someya’s group fabricated tactile sensing films as thin as 300 nm on Parylene C substrates that can be transferred to human skin without causing dermal irritation11.
Beside the application of organic sensors in bio-electronics and wearable electronics, an increasing effort has been focused on the development of novel approaches for the fabrication of an “electronic skin” that can replicate the sense of touch12,13,14,15,16,17,18,19,20 for prosthetics applications, human-robot interactions and rehabilitation. In particular, tactile systems have been investigated as tools to transduce information about an object (such as shape, temperature, superficial texture, etc.) through physical interaction. An ideal tactile sensor should be capable of simulating the sensing behavior of the human skin in terms of the spatial resolution and sensitivity and dynamic range for sensing force and temperature18.
Despite the various approaches that have been employed so far12,13,14,15,16,17,18,19,20, fabricating tactile sensors on ultra-conformable substrates remains a challenge. Most of the devices that have been previously developed for pressure and temperature transduction for tactile applications are based on coupled piezoresistive/pyroresistive devices21,22,23,24,25 or the combination of piezoelectric and pyroelectric materials26,27. Although these electronic devices do offer flexibility, they are fabricated using materials that have thickness values of several microns or high elastic moduli, therefore failing to provide conformability, which is necessary for epidermal applications.
Another important requirement for e-skin applications is the possibility of simultaneously transducing different types of stimuli with high reliability. To this aim, Graz et al.28 developed a bifunctional device for temperature and pressure detection using two integrated piezoelectric/pyroelectric sensing elements based on a composite foil of poly-vinylene difluoride-trifluoroethylene (PVDF-TrFE, a ferroelectric material) and a piezoelectric ceramic coupled to a transistor structure. Lee et al.29 depicted a highly sensitive multifunctional tactile sensor based on PVDF and ZnO nanostructures with graphene electrodes. The main advantages of using piezoelectric/pyroelectric sensing elements rely on their good high frequency responses and their high sensitivities30. Very recently, Zhao and Zhu developed an electronic skin with multifunctional sensors based on a pair of platinum (Pt) variable resistances integrated in a Wheatstone bridge. This system is able to simultaneously detect temperature and pressure variations with negligible hysteresis and high sensitivity31.
In this study, a particular kind of organic thin-film transistor (OTFT) called organic charge-modulated field-effect transistor (OCMFET) is coupled to different piezoelectric/pyroelectric polymers, such as PVDF and PVDF-TrFE, to obtain ultra-thin multimodal force and temperature sensors. During the last ten years, the OCMFET has been tested for several sensing and bio-sensing applications including pH sensing32,33, DNA hybridization sensing34, force transduction35 and electrogenic-cells activity detection36. The device proposed in this study offers significant advantages over the previously reported systems:
-
1.
The overall thickness of the device is 1.2 µm, which allows it to meet the above-mentioned conformability requirement.
-
2.
In contrast to other FET-based approaches, the sensing and the amplification elements are here physically separated; this prevents the external stimulus (temperature and/or force) from affecting the intrinsic characteristics of the semiconductor.
-
3.
The device itself is based on a single sensitive material (PVDF), which has both piezoelectric and pyroelectric properties37. This allows a single fabrication process to be used for both temperature and pressure sensing.
-
4.
The signal transduction mechanism does not strictly depend on the specific semiconductor in use. Therefore, this design choice gives the possibility of developing devices based on a similar concept with different fabrication technologies using not only organic materials but also inorganic or hybrid materials.
We here describe the optimization process of the layout that has been made on such a peculiar transducer in order to obtain the best performance in terms of sensitivity. We also provide a complete mechanical and thermal characterization of the sensor, with the intent of demonstrating the suitability of the proposed approach for e-skin applications.
Results
The OCMFET is a floating-gate OTFT in a bottom-gate/bottom-contact configuration that is biased using a control capacitor. As shown in Fig. 1, a key feature of the OCMFET is represented by its elongated floating gate such that the sensing area (i.e. the part of the floating gate in which the actual transduction happens) is far from the transistor area. The mechanism of OCMFET operation is related to a variation of the transistor threshold voltage VTH that is induced by a charge variation (ΔQS) occurring on the sensing area, which in turn causes a charge variation (ΔQT) under the transistor region. It is possible to derive the relationship between the control gate voltage VCG, the induced charge Qi and the transistor’s effective threshold voltage VTHF starting from Gauss’ law:
where Qf is the total charge in the floating gate, VFG is the floating gate voltage, VD is the drain voltage, CCG is the capacitance of the control capacitor, CSF and CDF are the parasitic capacitors between the floating gate and the source and the drain electrodes. Is then possible to express the floating gate voltage as follows:
The effective threshold voltage is now easily derivable from the following set of equations:
where CCG/CTOT \(\cong \) 1 (the parasitic capacitances are in fact negligible with respect to CCG). If all the terms are constant, but the charge Qi change, the threshold voltage shift can be written as:
One of the main advantages that is offered by the use of this structure (especially with respect to the passive thermal resistors) is that the charge induced on the sensing area is locally amplified by the transistor itself. Furthermore, the control gate can be used to minimize the spread of the electrical parameters (i.e. the threshold voltage and mobility) due to the fabrication process by impose the same over-threshold condition to all the devices in an array configuration.
As a preliminary test, the influence of the floating gate layout on the sensor response was examined to properly design the sensor architecture for a specific application. As extensively explained in a recent study from this group33, the charge in the sensing area (AS) determines a superficial charge variations (Δσ) in the transistor area (AT), the control gate area (ACG) and the remaining parts of the floating gate (collectively indicated as AEXT), according to the following expression:
To investigate the hypothesis that only a negligible charge redistribution occurs in the external areas, three different OCMFET structures having the same transistor, sensing and control-gate areas but different dimensions of the remaining floating-gate areas (AEXT) were fabricated, as depicted in Fig. 1. In Table S1 in Supplementary Materials is reported a complete description of the floating gate, control gate, transistor and sensing areas for each type of OCMFET structure. The number of devices tested is higher than 5 for each layout. By coupling one plate of the PVDF capacitor to the sensing area, a considerable charge is induced in the floating gate due to the intrinsic polarization of PVDF. This modulates the concentration of charge carriers in the OFET channel, which alters its threshold voltage. The VTH variation was evaluated for the three different AEXT before and after connecting them to the PVDF capacitor. As illustrated in Fig. 1, no correlation was observed between ΔVTH and the size of AEXT within the range tested. In such a situation, Equation 2 can be simplified by considering the charge under the control gate to be fixed, as follows:
This experimentally confirms the hypothesis in33.
Following this preliminary evaluation, the device was implemented as a multimodal temperature and force/pressure sensor based on the following principle: when a temperature or force variation occurs on the PVDF film, a charge separation is induced across the film due to the pyroelectric/piezoelectric properties of the material. This charge, depending on its sign, influences the carrier density within the transistor channel, thus causing a modulation of the transistor’s field effect. According to this mechanism, the threshold voltage shifts in response to a thermal or mechanical stress on the capacitor due to the piro-/piezoelectric property of PVDF, resulting in a modulation of the output current of the OCMFET and IDS.
The devices have been initially characterised separately as force and temperature sensors. The temperature and force variations were induced on the PVDF film using a Peltier cell and a mechanical indenter (IMADA Digital Force Gauge) respectively. For this characterisation we tested 10 devices, and for each device we performed 5 cycles of temperature/force measurements. All the devices used in our experiments were operated with VDS = VGS = −2V. As explained in Fig. 2a,b and c, the electro-thermal characterization has been performed by gradually increasing (or decreasing) the temperature while IDS was monitored. Each temperature step induces a corresponding change in IDS, which eventually reaches a steady-state when the temperature stabilizes. The results of this characterization demonstrate that the proposed approach can be used for temperature monitoring within the range 8 °C–50 °C, which is the temperature range that is required for most tactile applications38. Interestingly, as reported in the graph in Fig. 2(c), we observed a clear and reproducible linear response to the applied thermal stimuli. Such an approach turns out to be feasible also for mechanical sensing, as shown in Fig. 2e,f where the electromechanical characterization of the sensor is presented. The applied force was precisely measured using a dynamometer to obtain a reliable calibration curve. The results depict that the sensor is able to detect applied forces in the range of 1–5 N (corresponding to 40 kPa–200 kPa), which is consistent with the required target range for tactile applications. Again, the obtained response turned out to be linear and highly reproducible.
With the intent of proving that the proposed approach can be actually employed for practical applications, the capability of the sensor to discriminate between temperature and force variations that were applied simultaneously was also investigated. The sensing area of the OCMFET was placed on a Peltier cell that was fixed to the sample holder of a mechanical indenter. In this way, the temperature of the sensing area is monitored while a measurable force can be simultaneously exerted on the same area (Fig. 3). Initially, the sensing area was kept at a constant temperature (T = 22 °C) while being mechanically stimulated using a force of either 1, 3 or 5 N. As expected, the value of IDS varies proportionally with the magnitude of the applied force. The temperature of the sensing area was then linearly increased (with a temperature variation rate \( \sim \) 1.5 °C/min) from 22 °C to 50 °C, causing a linear decrease of the output current, while the mechanical stimulus was applied (1, 3 or 5 N). The results illustrated in Fig. 3a shows that the sensor is able to respond to applied pressures simultaneously during thermal stimulation with good reproducibility (see inset). As depicted in Fig. 3b, the sensitivities to thermal and mechanical stimuli (ST and SF, respective), defined as
lie in very different ranges, namely 70 nA/°C and 6 nA/N (corresponding to 0.15 nA/kPa), respectively. Moreover, the response to an applied force does not appear to be significantly affected by the temperature of the sensing area. Interestingly, considering the typical force range that is required for tactile applications (0.01–5 N)39, it can be observed that a temperature variation as low as 1 °C elicits a higher current variation than a pressure stimulus of 10 N, thus making, in realistic tactile applications, the two responses easily distinguishable by employing a simple signal processing routine. However, in order to be able to simultaneously record and distinguish pressure and temperature without any previous knowledge on the magnitude of the stimuli, we propose an alternative approach consisting of building a “pixel” containing two OCMFETs: one with a poled PVDF-TrFE layer spin-coated onto the sensing area and one with the same spin-coated PVDF-TrFE layer but unpoled (Fig. 4a). The reasons behind this solution stem from the different behavior of the same material before and after the poling procedure and the choice of using the copolymer PVDF-TrFE allows the use of an easier poling procedure compared to what is required for standard PDVF40. Moreover, it has been demonstrated that spin coated PVDF-TrFE thin films show a high β-phase formation without electrical poling, which correspond to high piezoelectricity41. In fact, even without the poling step, PVDF-TrFE samples present a residual polarization which increases as the annealing time increases42. As reported in Fig. S3 in Supplementary Materials, Raman spectra of our PVDF-TrFE unpoled samples annealed for 120 minutes @60 °C, @100 °C and @140 °C, show the presence of an evident reduction of paraelectric alpha-phase—peak at about 800 cm−1 43—and an increase of a piezoelectric beta-phase—peak at 840 cm−1 41—with the increase of the annealing temperature. On the other hand, it has been demonstrated that PVDF-TrFE pyroelectricity decades with the increase of annealing temperature44,45. As depicted in Fig. 4b,c, unpoled PVDF-TrFE is insensitive to temperature stimuli but retains its sensitivity to mechanical stimuli due to the intrinsic piezoelectricity of the sensing element. By fabricating a pixel structure containing two devices—one that is only sensitive to pressure and the other that is sensitive to both pressure and temperature—it is possible to discriminate between the two stimuli by evaluating the difference between the two signals. The calibration curves and sensitivities of an OCMFET with the PVDF-TrFE layer deposited onto the sensing area are showed in Fig. 4d–f. Similar to the previous tests, the devices were able to sense temperatures and forces in the ranges that are relevant to tactile applications, also showing, as expected, different sensitivities to thermal and force stimuli. Furthermore, it is in principle possible to discriminate between the two stimuli, regardless of their dynamics using a simple pixel configuration. The most significant advantage of this approach is that this multi sensing device can be fabricated using only one kind of electronic device and material, making the system very simple, convenient and practical for use in epidermal applications.
Finally, to demonstrate the suitability of the proposed sensor architecture for tactile applications, the sensor was transferred onto a volunteer subject’s skin and its response to a thermal stimulus was measured. Figure 5a depicts that the fabricated sensor structure can be conformably transferred onto human skin due to its overall micrometer-scale thickness, and shows that such devices can be positioned onto a fingertip with a high level of conformability and adherence to the skin.
Moreover, the intrinsic electrical characteristics of the OCMFET (without the sensing element connected to the floating gate) do not change upon transferring it to the skin, as depicted in Fig. 5b. In addition, as showed in Fig. S4 in Supplementary Materials, the device can be bent with very small bending radii (lower than 0.02 cm) with no significant variations in the OCMFET electrical characteristics, even after more than 200 cycles. After coupling the PVDF to the sensing area, a qualitative test was performed to evaluate the capability of the sensor to detect temperature variations. In particular, either a warm or cold object was placed in proximity of the sensing area while monitoring the sensor’s output. As shown in Fig. 5c, the results demonstrate that IDS increases when a warm stimulus is brought near the sensor, and, conversely, decreases when the cold object is presented to the sensing area instead. This qualitative experiment, though preliminary, demonstrates that the intrinsic electrical performance of the transistor is preserved (and the sensing capabilities of the OCMFET are maintained) after transferring the sensing system directly onto the human skin.
Discussion
In conclusion, a multimodal device for both temperature and force sensing has been developed. The sensor can be conformably transferred onto various surfaces, such as the human skin, due to its micrometer-scale thickness with no significant changes in the properties of the device. Complete thermal and electromechanical characterizations of the sensor in the typical ranges that are required for tactile applications (8 °C–50 °C and 1–5 N, respectively) were successfully conducted. Moreover, an easy and convenient approach for the simultaneous detection of the two stimuli has been proposed, thus demonstrating the possibility of using such a PVDF-TrFE/OCMFET system for multimodal tactile applications such as e-skin and epidermal electronics.
Methods
To fabricate the sensors, poly ethylene naphtalate (PEN - Goodfellow) was used as a carrier substrate. A soap solution (2 wt.% in water) was spin-coated onto the carrier substrate in order to reduce the adhesion of the subsequently deposited Parylene C layer to the carrier substrate, thus facilitating its removal at the end of the fabrication process. Parylene C, which was chosen as the substrate for the micro-scale transistors, was then deposited on the carrier substrate by chemical vapour deposition using a Labcoater 2 SCS PDS 2010 (Specialty Coating System) to obtain an, ultra-thin (thickness ≅ 900 nm) substrate. The core of the sensing system is an aluminum floating gate electrode, which is deposited and patterned using standard photolithography. The dielectric layer comprises a 6 nm-thick Al2O3 layer that was developed by thermal treatment and 150 nm-thick Parylene C film. After the dielectric layer deposition, gold source and drain electrodes were patterned on the Parylene C film using the same standard photolithographic process used for the floating gate fabrication. For the experimental session described in the first part of the manuscript, a 28 μm-thick poled PVDF film (Measurement Specialties Inc., MEAS; area = 5 × 5 mm2) was glued to the sensing area of the transistor using a conductive silver paste.
For the PVDF-TrFE experiments, a solution of 10 wt.% of 70/30 PVDF-TrFE (Piezotech, ARKEMA Group) was dissolved in DMSO and spin-coated onto the OCMFET sensing area. The solvent was evaporated at 140 °C for 2 h, obtaining a PVDF-TrFE layer with a final thickness of approximately 3 μm. Gold top electrodes were evaporated and patterned onto the PVDF-TrFE polymer using a shadow mask. The poling process was performed at 80 °C, and a voltage was applied across the polymer in incremental steps of 50 V at 10-min intervals up to 200 V. For all the devices, 6,13-Bis(triisopropylsilylethynyl)pentacene (TIPS Pentacene, Sigma-Aldrich) was used as a p-type organic semiconductor. A solution of 0.5 wt.% of TIPS Pentacene in anisole was drop-casted onto the channel area. The fabricated devices were finally released from the carrier substrate by dry peeling with the aid of an adhesive tape frame.
Raman scattering measurements were carried out in backscattering geometry using a 532.0 nm line by a wavelength stabilized diode module (LASOS DPSS series) coupled with a Reflecting Bragg Grating (Optigrate–Braggrade 405) to narrow the laser line. Measurements were performed at room temperature with a triple spectrometer Jobin-Yvon Dilor integrated system with a spectral resolution of about 1 cm−1. Spectra were recorded in the Stokes region by a 1200 groove/mm grating monochromator and a LNcooled charge coupled device (CCD) detector system.
The study was performed following the principles outlined in the Helsinki Declaration of 1975, later revised in 2000. All participants signed up an informed consent form before the experimental activity began, after being informed about the aims and procedures of the experiments.
References
Shirakawa, H., Louis, E. J., MacDiarmid, A. G., Chiang, C. K. & Heeger, A. J. Synthesis of electrically conducting organic polymers: halogen derivatives of polyacetylene, (CH)x. J. Chem. Societ. Chem. Comm. pp. 578–580 (1977).
Khan, S. et al. Electret field enhanced organic photovoltaic cells. In Photovoltaic Specialists Conference (PVSC), 2011 37th IEEE, pp. 000 719–000 722 (2011).
Fujisaki, Y. et al. Flexible active matrix organic light-emitting diode display using air-stable organic semiconductor of dinaphtho[2, 3-b: 2, 3-f]thieno[3, 2-b]- thiophene. Electron Devices, IEEE Transactions on, vol. 59, no. 12, pp. 3442–3449 (2012).
Sirringhaus, H. et al. High-Resolution Inkjet Printing of All-Polymer Transistor Circuits. Science. 29(5499), 2123–2126 (2000).
Manda, S. & Noh, Y. Printed organic thin-film transistor-based integrated circuits. Sem. Sci. Techn. 30 (2015).
Nathan, A. et al. Flexible Electronics: The Next Ubiquitous Platform. Proceedings of the IEEE 100 (2012).
Kim, D. H. et al. Epidermal Electronics. Science. 333(6044), 838–843 (2011).
Campana, A., Crames, T., Simon, D. T., Berggren, M. & Biscarini, F. Electrocardiographic Recording with Conformable Organic Electrochemical Transistor Fabricated on Resorbable Bioscaffold. Advanc. Mater. 26(23) (2014).
Kaltenbrunner, M. et al. An ultra-lightweight design for imperceptible plastic electronics. Nature 499, 458–463 (2013).
Lai, S. et al. Ultra-conformable Organic Field-Effect Transistors and circuits for epidermal electronic applications. Organ. Electron. 46, 60–67 (2017).
Nawrocki, R. A., Matsuhisa, N., Yokota, T. & Someya, T. 300-nm Imperceptible, Ultraflexible, and Biocompatible e-Skin Fit with Tactile Sensors and Organic Transistors. Advanc. Electron. Mater 2 (2016).
Barbaro, M., Caboni, A., Cosseddu, P., Mattana, G. & Bonfiglio, A. Active devices based on organic semiconductors for werable applications. Information Technology in Biomedicine, IEEE Transactions on 14(3), 758–766 (2010).
Schwartz, G. et al. Flexible polymer transistors with high pressure sensitivity for application in electronic skin and health monitoring’. Nature Comm. 4, 1859 (2013).
Someya, T. et al. A large area, flexible pressure sensor matrix with organic field-effect transistors for artificial skin applications. Proceedings of the National Academy of Sciences of the United States of America 101(27), 9966–9970 (2004).
Cosseddu, P., Viola, F., Lai, S., Raffo, L. & Bonfiglio, A. A Temperature Transducer based on a low-voltage Organic Thin-Film Transistor Detecting Pyroelectric Effect. IEEE Electron Device Letters 35(12) December (2014).
Cosseddu, P. et al. Tactile Sensors With Integrated Piezoelectric Polymer and low voltage Organic Thin-Film Transistors. 13th IEEE Sensors Conference, SENSORS 2014, Valencia 2–5 (2014).
Hua, Q. et al. Skin-inspired highly stretchable and conformable matrix networks for multifunctional sensing. Nature Comm. 9, 244 (2018).
Chortos, A., Liu, J. & Bao, Z. Pursuing prosthetic electronic skin. Nature Mater 15, 937–950 (2016).
Wang, X. et al. Recent Progress in Electronic Skin. Adv. Sci. 2, 1500169 (2015).
Dahiya, R. S. & Valle, M. Robotic tactile sensing: technologies and system. Springer Science & Business Media (2012).
Loi, A. et al. Matrices of inkjet printed OFETs for the realization of artificial robotic skin. Materials Research Society Symposium Proceedings, MRS Proceedings https://doi.org/10.1557/opl.2012.1300.
Gong, X. X. et al. Flexible strain sensor with high performance based on PANI/PDMS films. Organ. Electron. 42, 51–56 (2017).
Park, J. et al. Giant Tunneling Piezoresistance of Composite Elastomers with Interlocked Microdome Arrays for Ultrasensitive and Multimodal Electronic Skins. ACS Nano 8(5), 4689–4697 (2014).
Dankoco, M. D., Tesfay, G. Y., Benevent, E. & Bendahan, M. Temperature sensor realized by inkjet printing process on flexible substrate. Mat. Sci. Eng. B 205, 1–5 (2016).
Vuorinen, T., Niittynen, J., Kankkunen, T., Kraft, T. M. & Mantysalo, M. Inkjet-Printed Graphene/PEDOT:PSS Temperature Sensors on a Skin-Conformable Polyurethane Substrate. Scient. Rep. 6, 35289 (2016).
Khan, S., Lorenzelli, L. & Dahiya, R. S. Screen printed flexible pressure sensors skin. 25th Annual SEMI Advanced Semiconductor Manufacturing Conference (ASMC) 219–224 (2014).
Yang, Y., Zhou, Y., Wu, J. M. & Wang, Z. L. Single micro/nanowire pyroelectric nanogenerators as self-powered temperature sensors. ACS Nano 6, 8456–8461 (2012).
Graz, I. et al. Flexible active-matrix cells with selectively poled bifunctional polymer-ceramic nanocomposite for pressure and temperature sensing skin. J. Appl. Phys. 106, 034503 (2009).
Lee, J. S., Shin, K. Y., Cheong, O. J., Kim, J. H. & Jang, J. Highly Sensitive and Multifunctional Tactile Sensor Using Free-standing ZnO/PVDF Thin Film with Graphene Electrodes for Pressure and Temperature Monitoring. Scient. Repor. 5(7887) (2015)
Tiwana, M. I., Redmond, S. J. & Lovell, N. H. A review of tactile sensing technologies with applications in biomedical engineering. Sens & Actuat. A 179, 17–31 (2012).
Zhao, S. & Zhu, R. Flexible bimodal sensor for simultaneous and independent perceiving of pressure and temperature stimuli. Advanc. Mater. Techn. (2017).
Caboni, A., Orgiu, E., Barbaro, M. & Bonfiglio, A. Flexible Organic Thin-Film Transistors for pH Monitoring. IEEE Sens. J. 9(12) (2009).
Spanu, A. et al. A reference-less pH sensor based on an organic field effect transistor with tunable sensitivity. Organ. Electron. 48, 188–193 (2017).
Lai, S. et al. Ultralow Voltage, OTFT-Based Sensor for Label-Free DNA Detection. Advan. Mater. 25(1), 103–107 (2013).
Spanu, A. et al. A high-sensitivy tactile sensor based on piezoelectric polymer PVDF coupled to an ultra-low voltage organic transistor. Organ Electron. 36, 57–60 (2016).
Spanu, A. et al. An organic transistor-based system for reference-less electrophysiological monitoring of excitable cells. Scient. Repor. 5 (2015).
Kawai, H. The Piezoelectricity of Poly(Vinylidene Fluoride). Japan. J. Appl. Phys. 8, 975–976 (1963).
Smith, I. D. & Johnson, K. O. Thermal sensibility and Thermoreceptors. J. Investig. Dermatol. 69(1), 146–153 (1977).
Hammock, M. L., Chortos, A., Tee, B. C. K., Tok, J. B. H. & Bao, Z. The Evolution of Electronic Skin (E-Skin): A Brief History, Design Considerations, and Recent Progress. Advanc. Mater. 25(42), 5997–6038 (2013).
Krause, M. et al. PbTiO3 – P(VDF-TrFE) – Nanocomposites for Pressure and Temperature Sensitive Skin. Ferroelectrics 419(1), 23–27 (2011).
Sharma, T., Je, S., Gill, B. & Zhang, J. X. J. Patterning piezoelectric thin film PVDF–TrFE based pressure sensor for catheter application. Sens & Actuat. A. 177, 87–92 (2012).
Ducrot, P., Dufour, I. & Ayela, C. Optimization of PVDF-TrFE processing conditions for the fabrication of organic MEMS resonators. Scient. Repor. 6(19426) (2016).
Qian, J. et al. Unveiling the piezoelectric nature of polar α-phase P(VDF-TrFE) at quasi-two-dimensional limit. Scient. Repot. 8(532) (2018).
Ibos, L. et al. Annealing or Storage influence on pyroelectricity of ferroelectric PVDF and PVDF-TrFE Copolymer. Ferroelectrics 320, 15–21 (2005).
Bai, G. et al. Tuned dielectric, pyroelectric and piezoelectric properties of ferroelectric P(VDF-TrFE) thin films by using a mechanical load. Journal of Applied Physics 111, 044102 (2012).
Author information
Authors and Affiliations
Contributions
F.V. coordinated the writing of the article, designed and carried out the experimental sessions and fabricated the samples. He also contributed to discuss the device working model and evaluate and discuss the results. A.S. contributed to discuss the device working model, the experiments design and the experimental results. He also contributed to write the article. P.C.R. designed and carried out the Raman spectroscopy measurements and contributed to the evaluation and interpretation of the experimental results. He also contributed to write the paper. A.B. contributed to discuss the working model. She also contributed to write the article. P.C. coordinated the work and contributed to the evaluation and interpretation of the experimental results. He also contributed to write the paper.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Viola, F.A., Spanu, A., Ricci, P.C. et al. Ultrathin, flexible and multimodal tactile sensors based on organic field-effect transistors. Sci Rep 8, 8073 (2018). https://doi.org/10.1038/s41598-018-26263-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-26263-1
This article is cited by
-
Multimodal force and temperature tactile sensor based on a short-channel organic transistor with high sensitivity
Scientific Reports (2023)
-
Ultra-flexible graphene/nylon/PDMS coaxial fiber-shaped multifunctional sensor
Nano Research (2023)
-
A sub-150-nanometre-thick and ultraconformable solution-processed all-organic transistor
Nature Communications (2021)
-
Electrolyte-gated transistors for enhanced performance bioelectronics
Nature Reviews Methods Primers (2021)
-
Tactile and temperature sensors based on organic transistors: Towards e-skin fabrication
Frontiers of Physics (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.