Abstract
Phase change random access memory (PCRAM) has gained much attention as a candidate for nonvolatile memory application. To develop PCRAM materials with better properties, especially to draw closer to dynamic random access memory (DRAM), the key challenge is to research new high-speed phase change materials. Here, Scandium (Sc) has been found it is helpful to get high-speed and good stability after doping in Sb2Te alloy. Sc0.1Sb2Te based PCRAM cell can achieve reversible switching by applying even 6 ns voltage pulse experimentally. And, Sc doping not only promotes amorphous stability but also improves the endurance ability comparing with pure Sb2Te alloy. Moreover, according to DFT calculations, strong Sc-Te bonds lead to the rigidity of Sc centered octahedrons, which may act as crystallization precursors in recrystallization process to boost the set speed.
Similar content being viewed by others
Introduction
Recently, with the increasing requirements of dealing with tons of information on the Internet, intelligent devices and portable computers are developing very fast. Among the numerous nonvolatile memories that are used in commercial devices, Flash memory is the mainstream technology. Nevertheless, with the feature size of integrated circuit scaling down, it is approaching its dimension extreme1. Hence, it is necessary to develop new nonvolatile memory technology. As one of promising candidate technologies, phase change random access memory (PCRAM) possesses superior properties, such as low cost, high scalability and high integration level2,3. It has been published that PCRAM can still realize reversible switching performance in a tiny cell (<2 nm)4. Thus, PCRAM is a very prospective storage technology to reform the current nonvolatile memory market.
PCRAM works through distinguishing the resistance difference between amorphous (high resistive) and crystalline (low resistive) states5. Phase change material is the key of PCRAM. Hence, the phase transition process with different mechanisms6,7,8 has been a hot research area for several years. For each of these materials, Ge2Sb2Te5 (GST) alloy is the most mature material with good comprehensive properties. Both vacancies and Te have been considered to play an important role in the fast phase transition process of GST9. As commercialized phase change material, GST still has some flaws like relatively slow crystallization speed (~50 ns)10 and low data retention temperature (~85 °C)11, and so on, which hinder its widely applications in PCRAM. Hence, researchers never stop developing new materials for getting better and better properties. Sb2Te alloy as a basic member of phase change material family, shows high crystallization speed, which is attributed to its growth dominated crystallization mechanism12. However, poor amorphous stability and data retention cut off the possibility of its potential application in PCRAM without optimization13. In some previous studies, doping is beneficial to increase the crystallization temperature of base materials, such as doping N14,15, Cu16 and W17. But after doping, phase separation is always accompanied, impeding the further improvement of crystallization speed, deteriorating device performance, and decreasing cycling times18. Ti doping was also found to increase the crystallization speed owing to Ti centered atomic motifs in both amorphous and crystalline state19. Later calculation work predicts that Y dopants match well with parent Sb2Te3 structure and increase the stability of Sb2Te3 in the phase change process20. Furthermore, a recent report from Science points out that Sc-doped Sb2Te3 phase change material without phase separation has a very rapid SET speed reaching up to 700 picoseconds21 Among the equilibrium phases of Sb-Te system, Sb2Te alloy has >50 °C higher crystallization temperature than Sb2Te3 one. Hence, in this paper, Sc element was also been chosen as a dopant into Sb2Te alloy. We hope that through the adjustment of substrate material, the new one could have better thermal stability, and also useful for speed improvement in Sb2Te alloy.
Results
The sheet resistance as a function of temperature (R-T) for Sb2Te and Sc0.1Sb2Te films (~100 nm) was measured to clarify the influence of doping on the thermal stability as depicted in Fig. 1(a). The sharp drop of the resistance happens around the crystallization temperature (T c ), which significantly shifts to higher temperature after doping Sc. According to the derivative of logarithmic sheet resistance with respect to temperature (dlgR/dT), the T c of Sb2Te and Sc0.1Sb2Te films are estimated to be 156.1 °C and 174.9 °C, respectively, indicating better amorphous stability after Sc doping. Figure 1(b) shows the 10-year data retention characteristics for Sb2Te and Sc0.1Sb2Te films. Based on the Arrhenius equation: t = τ·exp(E a /k B T), where t is the 50% criterion failure time, τ is the proportional time constant, \({E}_{a}\) is the crystallization activation energy, \({k}_{B}\) is the Boltzmann constant, T is the absolute temperature. After Sc doping, the activation energy \({E}_{a}\) increases from 2.44 eV to 3.00 eV. By extrapolating the data retention time to 10 years, the data retention temperature for Sc0.1Sb2Te film is estimated to be 92.7 °C, demonstrating a better thermal stability than that of Sb2Te (63.8 °C) and conventional GST (85 °C) alloy. Apart from better thermal stability, four orders of magnitude resistance difference leave enough margins for identifying the high resistance and low resistance states.
From microstructural side, thermally-induced phase transition processes were investigated by in-situ transmission electron microscope (TEM) technique for Sb2Te and Sc0.1Sb2Te films (~15 nm) with a heating rate of 10 °C/min. Figure 2 shows TEM bright-field (BF) images and the corresponding selected area electron diffraction (SAED) patterns for Sb2Te (a-c) and Sc0.1Sb2Te (d-f) films at different temperature. Pure Sb2Te film starts to crystallize with an explosive crystal growth at 140 °C (Fig. 2b), and the grain size is in about several hundred nanometers scale. After the temperature increases to 200 °C (Fig. 2c), the grain size of Sb2Te film is almost the same comparing with Fig. 2b, because its crystallization process has already finished around 140 °C. As for Sc0.1Sb2Te film, it starts to crystallize at 160 °C with numerous nanocrystals (<~10 nm) as shown in Fig. 2d. Though these nanocrystals grow a little (<~15 nm) as temperature rises up to 200 °C (Fig. 2e), the grain size of Sc0.1Sb2Te is still much smaller than that of Sb2Te after crystallization. In addition, both of the SAED patterns in Fig. 2c,f can be indexed as hexagonal (h-) Sb2Te structure (JCPDS No. 80–1722). No extra diffraction rings appear in Fig. 2f, which demonstrates that Sc0.1Sb2Te film is a single h-phase without phase separation. The XRD result of crystallized Sc0.1Sb2Te film, as shown in Fig. S1, further confirms that Sc0.1Sb2Te has the same structure as Sb2Te. That is, Sc doping significantly affects the crystallization behavior of Sb2Te film without forming any new phase or new structure. Beyond that, a crystallized film with three times more of Sc doping level, as much as 11% (Sc0.4Sb2Te), was investigated to inspect the distribution of Sc atoms by using of STEM-EDS mapping in TEM as shown in Fig. S2. Even at a higher doping level, the crystalline structures of Sc0.4Sb2Te and Sc0.1Sb2Te remain the same from SAED pattern side. This EDS results give more direction on uniform distributed Sc, Sb and Te elements without obvious phase separation appearing in nanometer scale.
In order to understand the interplay between Sc atoms and Sb2Te lattice, XPS experiment was applied to investigate the bonding state of crystallized Sb2Te and Sc0.1Sb2Te films. Figure 3 shows the binding energy of Sb 3d and Te 3d core levels for Sb2Te and Sc0.1Sb2Te films. The C 1 s peak at 284.8 eV is used as a reference. After Sc doping, both peaks of Sb 3d shift to lower energies (~0.2 eV for Sb 3d5/2, ~0.25 eV for Sb 3d3/2). Similar results are observed in the binding energies for Te 3d (~0.25 eV for both Te 3d5/2 and Te 3d3/2). Usually, binding energy will decrease when an atom bonds to another one with a lower electro-negativity. Since the electro-negativity of Sc (1.36) is smaller than that of Sb (2.05) and Te (2.12), Sc atoms is very likely to bond with Sb and Te atoms in Sc0.1Sb2Te film after crystallization, resulting in the decrease of binding energy for Sb and Te elements. Considering that the electro-negativity difference (ΔS) of Sc-Te and Sc-Sb is much bigger than Sb-Te, and a large ΔS between two atoms would increase nucleation probability22,23. More nuclei are likely to generate after Sc doping, and the intergrowth of nuclei produces more grain boundaries, which will suppress the subsequent crystal growth significantly. This may be contributing to explain the much smaller grain size distribution after Sc doping as shown in Fig. 2f.
Anyway, good device performances are the key to application. Figure 4a shows the resistance-voltage curves of Sc0.1Sb2Te alloy based PCRAM cell with different pulse widths (the falling edge of the voltage pulse is 3 ns). Both set and reset voltages slightly shift to a higher value when the pulse width decreases. But most of all, even 6 ns electrical voltage pulse can still induce reversible phase transformation in this PCRAM device. Comparing to conventional GST (crystallization speed of ~ 50 ns)10 and Sb2Te (crystallization speed of ~ 20 ns)13, Sc0.1Sb2Te based PCRAM cell exhibits faster operation speed. Besides, endurance up to 3.3 × 105 cycles without failure (Fig. 4b) also demonstrates that Sc0.1Sb2Te alloy has great potential for PCRAM application24.
Discussion
To further verify the location of doped Sc atoms, Ab initial method was carried out to theoretically predict the most probable site by calculating the formation energy (\({E}_{f}\)) in each site. Rather than simulating the exact experiment composition, we introduce a single Sc atom at various lattice sites in a Sb2Te supercell with lattice parameter of 12.816◊12.816◊ 17.633(Å3) to evaluate the effects of doped Sc atom. In the Sb2Te supercell, there are seven possible dopant sites for Sc atoms, Sb1, Sb2, Sb3, Te1, Te2 and In1, In2 (shown in Fig. S3a). Sb and Te with subscript mean the substitution doping in which the Sc atom replaces Sb or Te, whereas In1 and In2 mean the Sc atom enters the interstitial site. The formation energy of each structure after relaxed was calculated and shown in Fig. S3b. The \({E}_{f}\) was obtained according to the following equation:
Here \({E}_{un \mbox{-} doped}\) and \({E}_{Sc \mbox{-} doped}\) denote the total energies of the relaxed structure before and after Sc doping. \({E}_{{Sc}}\) denotes the chemical potential of doped Sc, \({E}_{{Sb}/{Te}}\) denotes the chemical potential of Sb or Te being replaced, while it is zero for interstitial doping. As shown in Fig. S3b, the \({E}_{f}\) for Sb1 is −2.482/2.583 eV for Sb/Te rich, which is much lower than all of the other conditions. Thus, Sb1 is the most energetically favorable position for the doped Sc atom. To identify the bonding information of Sc0.1Sb2Te when Sc substitutes Sb1, the charge density difference (CDD) of relaxed structure was illustrated in Fig. 5. Their corresponding 2D charge density plot was shown in Fig. S4, which shows that Sc and Sb are bound with Te through a bond point25. In order to show the chemical environment of Sc, we present the nine layers that exist in the Sb2Te h-structure along C axis. As shown in Fig. 5b,c, there is only tenuous charge present in three of the Sb-Te bonds which is in distinct contrast with the noticeable charge accumulation at the bond center between Sc and Te. The original Sb-centered octahedron shows three strong (3.045 Å) bonds and three weak bonds (3.159 Å). However, the Sc-centered octahedron shows six identical strong bonds (2.98 Å), the strong Sc-Te bonds lead to the rigidity of Sc-centered octahedrons. Even they may not necessarily be intact in the melt-quenched amorphous phase, yet the Sc-centered octahedrons can still be the subcritical embryos owe to their lowest formation energy. So the reconstruction of Sc-centered octahedrons is more advantageous than that of Sb-centered motifs in the recrystallization process. The existence of large amounts of precursors will refine the crystalline size, thus increase the grain boundaries which will accommodate more stress produced in phase change process of PCRAM device. Moreover, smaller grain size will increase the interface-area-to-volume ratios to facilitate the hetero-crystallization at the grain boundaries, further accelerating the crystallization speed. This may explain why the SET speed of Sc0.1Sb2Te based PCRAM device (6 ns) is faster than Sb2Te based one (20 ns). However, after 3.3 × 105 cycles, the non-uniform electronic fields in the active mushroom shape area might lead to a reallocation of elements, thus appear Sb2Te large grains that can result in device failure.
Comparing with Sc0.2Sb2Te3 material, Sb2Te alloy in this study was choosing as the parent material instead of Sb2Te3 alloy, considering the Sb2Te’s thermal stability is better. Sc0.2Sb2Te3 material can change from amorphous state to face centered cubic (f-) phase, and then to the stable h-phase with the increase of temperature. The 700 picoseconds set speed21 only involves phase change process between amorphous and f-phase, which is a metastable state like f-GST phase. Avoiding f-to-h phase transition is very important in PCRAM device, with an emphasis on preventing grain growth26. Hence, in this paper, Sc0.1Sb2Te material can reach 6 nanoseconds set speed without intermediate phase, benefiting from its strong Sc-centered cluster. It has high-speed and good thermal stability together, which may point out some direction for the future design of PCRAM devices.
Conclusion
In this paper, Sc doped Sb2Te film was investigated to verify its application in PCRAM. After Sc doping, the thermal stability of Sb2Te alloy was improved, and the 10-year data retention time was increased. The crystalline Sc0.1Sb2Te film exhibits a single phase without phase separation. Sc0.1Sb2Te based PCRAM cell can still realize stable reversible switching behaviors even at 6 ns. Two orders of resistance difference between set and reset state makes it easy to distinguish “0” and “1”. Furthermore, endurance up to 3.3 × 105 cycles makes Sc0.1Sb2Te a promising material for PCRAM application.
Methods
Sb2Te and Sc doped Sb2Te films was deposited on SiO2/Si (100) substrates and carbon coated TEM grid by co-sputtering Sc and Sb2Te targets using RF sputtering system at room temperature. The composition of the deposited films, BF images and SAED patterns were characterized by JEOL-2100F TEM with energy dispersive spectroscopy (EDS). The bonding situation of Sb2Te and Sc0.1Sb2Te alloy was evaluated by X-ray photoelectron spectroscopy (XPS) with Al Kα radiation. T-shaped PCRAM cells with a tungsten bottom electrode (190 nm in diameter) were fabricated using 130 nm CMOS technology. Afterwards, Sc0.1Sb2Te film (about 55 nm), TiN film (10 nm) and Al top electrode (300 nm) were sequentially deposited. Resistance-voltage curves and programming cycles were monitored with Keithley 2400 and Tektronix AWG 5002B. Calculations in this work was investigate by using density functional theory (DFT)27. The Vienna Ab-initio Simulations Package (VASP)28 was used for calculations. The projector augmented wave (PAW)29 pseudopotentials were used to describe electron-ion interactions. For the exchange-correlation energies between electrons, the Perdew-Burke-Ernzerhof (PBE)30 function was employed. The energy cut offs were chosen to be 450 eV and 350 eV for relaxation and static calculation. A supercell containing 3◊3◊1 unit cells of Sb2Te was constructed for relaxation. The 5◊5◊3 K point mesh with Gamma centered was used. The relaxation was performed until the total energy converged to within 1 meV.
References
Lu, C. Y., Hsieh, K. Y. & Liu, R. Future challenges of flash memory technologies. Micro. Engin. 86, 283–286 (2009).
Wuttig, M. & Yamada, N. Phase-change materials for rewriteable data storage. Nat. Mater. 6, 824–832 (2007).
Giusca, C. E. et al. Confined crystals of the smallest phase-change material. Nano Lett. 13, 4020–4027 (2013).
Czubatyj, W., Hudgens, S. J., Dennison, C., Schell, C. & Lowrey, T. Nanocomposite phase-change memory alloys for very high temperature data retention. IEEE Electron Device Lett. 31, 869–871 (2010).
Atwood, G. Phase-Change Materials for Electronic Memories. Science 321, 210–211 (2008).
Sun, Z. et al. Pressure-induced reversible amorphization and an amorphous – amorphous transition in Ge2Sb2Te5 phase-change memory material. Proc. Natl. Acad. Sci. USA 108, 10410–10414 (2011).
Sun, Z., Zhou, J., Mao, H. & Ahuja, R. Peierls distortion mediated reversible phase transition in GeTe under pressure. Proc. Natl. Acad. Sci. USA 109, 5948–52 (2012).
Sun, Z., Zhou, J., Blomqvist, A., Johansson, B. & Ahuja, R. Fast crystallization of chalcogenide glass for rewritable memories. Appl. Phys. Lett 93, 061913 (2008).
Sun, Z., Zhou, J., Blomqvist, A., Johansson, B. & Ahuja, R. Formation of Large Voids in the Amorphous Phase-Change Memory Ge2Sb2Te5 Alloy. Phys. Rev. Lett. 102, 75504 (2009).
Kim, I. S. et al. High performance PRAM cell scalable to sub-20nm technology with below 4F2 cell size, extendable to DRAM applications. Symp. VLSI Tech. Dig. t19b3, 203–204 (2010).
Friedrich, I., Friedrich, I., Weidenhof, V. & Weidenhof, V. Structural transformations of Ge2Sb2Te5 lms studied by electrical resistance measurements. J. App. Phys. 87, 4130–4134 (2000).
Pieterson, L. V., Lankhorst, M. H. R., Schijndel, M. V. & Kuiper, A. E. T. Phase-change recording materials with a growth-dominated crystallization mechanism: A materials overview. J. App. Phys. 97, 083520 (2000).
Liu, G. et al. Solid-State Electronics The investigations of characteristics of Sb2Te as a base phase-change material. Solid State Electron. 135, 31–36 (2017).
Zhu, M. et al. N-doped Sb2Te phase change materials for higher data retention. J. Alloys. Compd. 509, 10105–10109 (2011).
Sun, Z. et al. Stable nitride complex and molecular nitrogen in N doped amorphous Ge2Sb2Te5. Appl. Phys. Lett 93, 241908 (2008).
Raoux, S., Salinga, M., Jordan-Sweet, J. L. & Kellock, A. Effect of Al and Cu doping on the crystallization properties of the phase change materials SbTe and GeSb. J. App. Phys. 101, 1–6 (2007).
Ding, K. et al. The impact of W doping on the phase change behavior of Sb2Te3. J. Alloys. Compd. 688, 22–26 (2016).
Nam, S.-W. et al. Phase separation behavior of Ge2Sb2Te5 line structure during electrical stress biasing. Appl. Phys. Lett. 92, 111913 (2008).
Zhu, M. et al. One order of magnitude faster phase change at reduced power in Ti-Sb-Te. Nat. Commun. 5, 1–6 (2014).
Li, Z., Si, C., Zhou, J., Xu, H. & Sun, Z. Yttrium doped Sb2Te3: A promising material for phase change memory. ACS Appl. Mater. Interfaces. 8(39), 26126–26134 (2016).
Rao, F. et al. Reducing the stochasticity of crystal nucleation to enable subnanosecond memory writing. Science 1427, 1–9 (2017).
Peng, C. et al. W-Sb-Te phase-change material: A candidate for the trade-off between programming speed and data retention. Appl. Phys. Lett. 101, 122108 (2012).
Hirotsune, A. et al. Optimization of Crystallization Characteristics for Phase-Change Optical Disk with Ag–Ge–Sb–Te Recording Film. J. Appl. Phys. 46, 6652–6657 (2007).
Wang, W. et al. Enabling Universal Memory by Overcoming the Contradictory Speed and Stability Nature of Phase-Change Materials. Sci. Rep. 2, 360 (2012).
Sa, B., Zhou, J., Sun, Z., Tominaga, J. & Ahuja, R. Topological insulating in GeTe/Sb2Te3 phase-change superlattice. Phys. Rev. Lett. 109, 1–5 (2012).
Zheng, Y. et al. Surface Energy Driven Cubic- to-Hexagonal Grain Growth of Ge2Sb2Te5 thin film. Sci. Rep. 7(1), 5915 (2017).
Hohenberg, P. & Kohn, K. Inhomogeneous electron gas. Phys. Rev. B. 7, 1912–1919 (1973).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B. 47, 558–561 (1993).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B. 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Acknowledgements
This work was supported by “The National Key Research and Development Program of China (17YFB0405601)”.
Author information
Authors and Affiliations
Contributions
X.C. prepared the film samples and fabricated the PCRAM cells and did the electrical measurement and wrote the paper. Y.C. and Y.Z., X.C. carried out the in-situ TEM heating and EDS mapping measurements. Y.C. and X.L. revised this paper. M.Z. gave suggestions on writing this paper. Y.W., G.L., T.G. and K.R. gave the author much help in the device fabrication. The DFT calculation was done with the help of X.L. and T.L. and L.W. The project was initiated and conceptualized by Y.C. and Z.S.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Chen, X., Zheng, Y., Zhu, M. et al. Scandium doping brings speed improvement in Sb2Te alloy for phase change random access memory application. Sci Rep 8, 6839 (2018). https://doi.org/10.1038/s41598-018-25215-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-25215-z
This article is cited by
-
Phenomenology of M–N rule and high-field conduction in Ge–Te–Se–Sc rare-earth doped glasses
Journal of Materials Science: Materials in Electronics (2024)
-
Study on the Crystallization Behavior of Sb2Te Thin Films for Phase-Change Memory Applications
Journal of Electronic Materials (2023)
-
Kinetics study and thermal analysis of novel phase-change materials with scandium as chemical modifier
Journal of Thermal Analysis and Calorimetry (2023)
-
Robust thermal stability in DRAM-like Sb2Te-based phase change memory by Hafnium modified
Journal of Materials Science: Materials in Electronics (2022)
-
Ta-Doped Sb2Te Allows Ultrafast Phase-Change Memory with Excellent High-Temperature Operation Characteristics
Nano-Micro Letters (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.