Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Tunable Mechanical Metamaterials through Hybrid Kirigami Structures


Inspired by the art of paper cutting, kirigami provides intriguing tools to create materials with unconventional mechanical and morphological responses. This behavior is appealing in multiple applications such as stretchable electronics and soft robotics and presents a tractable platform to study structure-property relationships in material systems. However, mechanical response is typically controlled through a single or fractal cut type patterned across an entire kirigami sheet, limiting deformation modes and tunability. Here we show how hybrid patterns of major and minor cuts creates new opportunities to introduce boundary conditions and non-prismatic beams to enable highly tunable mechanical responses. This hybrid approach reduces stiffness by a factor of ~30 while increasing ultimate strain by a factor of 2 (up to 750% strain) relative to single incision patterns. We present analytical models and generate general design criteria that is in excellent agreement with experimental data from nanoscopic to macroscopic systems. These hybrid kirigami materials create new opportunities for multifunctional materials and structures, which we demonstrate with stretchable kirigami conductors with nearly constant electrical resistance up to >400% strain and magnetoactive actuators with extremely rapid response (>10,000% strain s−1) and high, repeatable elongation (>300% strain).


The ability to tune the stiffness and deformation behavior of materials is critical to diverse applications from stretchable electronics and soft robotics to tissue engineering and biomedical devices1,2,3,4,5,6,7. Recently, techniques building upon principles in kirigami, the Japanese art of paper cutting, have demonstrated that the addition of cuts to materials enables elastic softening, large deformations, and the generation of 3D structures from 2D sheets across a range of length scales8,9,10,11,12,13,14,15. This enables the utilization of inextensible or functional components to create deformable devices such as reconfigurable electronics, optoelectronics, and sensors16,17,18,19,20,21,22,23,24,25,26,27. As kirigami features generate geometric deformations that dominate the inherent material elasticity, properties and structures of kirigami metamaterials are controlled by the pattern and orientation of the cuts. This has been examined by recent efforts to concentrate deformations on either the bending of beams defined by cuts or by the rotation of hinges that separate these features28,29,30,31,32,33,34,35. However, exploring the synergistic coupling of these deformation modes has been limited and further cut architecture modification has the potential to provide significant gains in stiffness tunability and deformability in kirigami metamaterials.

Here we show that the addition of minor cuts to kirigami structures provides a mechanism to control kirigami deformation modes for highly tunable mechanical response. We investigate this approach in polymeric films by adding minor cuts near the ends of major cuts to prescribe boundary conditions and create non-prismatic kirigami beams. This reduces stiffness by a factor of 30 and increases ultimate tensile strain by a factor of 2 relative to single incision patterns. Experimental results are supported by theoretical predictions in which the addition of minor cuts of various lengths and proximity to major cuts provides an analogous response to varying boundary conditions and beam geometry. We generalize these equations and provide design rules for kirigami films with tunable stiffness and extension responses and find excellent agreement between predictions and experimental measurements from nanoscopic to macroscopic kirigami materials. This approach and corresponding design criteria provide a simple and scalable method for the control of stiffness and deformation of materials without changing sample size, major pattern geometry, or material composition. We demonstrate the utility of this approach in stretchable electronics with highly stretchable conductors for deformable kirigami circuitry and in programmable matter with a rapid magnetoactive soft actuator. Both examples show that minor cuts enable a significant enhancement in deformability and stiffness control.


Kirigami patterns are created in polyethylene terephthalate (PET) sheets (E ≈ 2.6 GPa) with a CO2 laser cutter. The patterned cuts consist of an array of transverse long major cuts, which define beams, and longitudinal short minor cuts, which prescribe beam shape and the rigidity of boundary conditions between beams. As seen in Fig. 1a, the addition of minor cuts significantly modifies the deformation behavior of kirigami film, resulting in a lower stiffness and higher elongation than a kirigami film consisting only of major cuts. Specifically, when hanging weights, a kirigami system consisting of only major cuts shows negligible strain (ε ≈ 0%) until the force reaches 0.4 N. In contrast, a modified system with major and minor cuts begins extending at a far lower force (≈0.1 N) and reaches strains over 270% at a force of 0.4 N. The minor cuts also increase the ultimate extensibility of the films, as seen in Fig. 1b.

Figure 1
figure 1

Tunable kirigami materials through hybrid structures. (a) Photographs of kirigami sheets with (left) only major cuts (Fig. 2a (design i)) and (right) hybrid structures of major and minor cuts (Fig. 2a (design v)). The same increasing weights (10 g, 20 g, and 40 g) are attached to each kirigami sheet to demonstrate mechanical response. Major cuts are highlighted in blue and the minor cuts are highlighted in red in the insets. (b) Load (P) versus strain (ε) for kirigami materials with design i of w = 3 mm (blue curve) and with design v of w = 3 mm and l m /2w = 0.75 (red curve). Geometric parameters are described in Fig. 2a. The inset shows the initial regime of the P - ε plot and the slope indicates the effective in-plane stiffness.

We consider the kirigami sheet as an array of slender beams with rectangular cross-section defined by the major cuts. Each beam is characterized by length l M , width w, and thickness t with elastic modulus E. The spacing d between major cuts along the transverse direction and the thickness of samples are constant throughout the experiment (d = 2 mm, t = 0.13 mm). The length of minor cuts (l m ) is selected according to the dimensionless geometric parameter l m /2w = 0, 0.25, 0.5, 0.75 and five different minor cut arrangements are investigated: (i) no minor cuts, (ii) minor cuts in between major cuts in alternating rows and (iii) all rows, (iv) minor cuts intersecting major cuts in alternating rows and v) all rows (Fig. 2a). Figure 1b shows a representative force-extension plot of a patterned sheet with and without minor cuts. Initially, the patterned sheet deforms with each beam bending in plane through the opening of cuts and rotation of plain regimes via hinges. As extension increases the in-plane beam bending becomes energetically more costly than out-of-plane bending28,30, resulting in an elastic instability and a transition to out-of-plane beam bending (See Fig. S1 for close-up images of the structure under low strain). This continues until the deformation fully extends each beam, at which point the structure becomes loaded in tension, resulting in strain hardening and ultimately failure.

Figure 2
figure 2

Hybrid kirigami stiffness and ultimate strain. (a) A schematic of a kirigami structure with geometric parameters and different designs. Data point symbol represents each beam size, which is defined by major cuts, data point interior represents different minor cut designs, and data point color represents the ratio of minor cut length over width of beam. (b) Effective in-plane stiffness \(\overline{K}\) versus l m /(2w) for varying pattern designs, with l M  = 20 mm, w = d = 2 mm, and l m  = 0–3 mm. Dashed/dotted/solid lines represent Equation 2 with FFE (α = 16), PPE (α = 4), and non-prismatic beam/pinned end condition (α ≈ 0.8), respectively. (c) \(\overline{K}/(Et)\) versus (w/l M ) with varying major and minor cut conditions, dashed/dotted/solid lines represent the same α values as in component (c). (d) Ultimate strain (ε ULT ) versus w/l M , where lines represent Equation 3 with various γ values as specified in the legend.

To analyze the mechanical behavior of these kirigami structures we consider an array of slender beams, where the stiffness of a single beam scales as \(k\cong E{w}^{3}t/{l}_{M}^{3}\), where E is the elastic modulus and l M , w, and t are length, width, and thickness of the beam, respectively28. The effective in-plane stiffness \(\overline{K}\) of the patterned sheet is calculated by considering of the number of beams and their arrangement (N B /N rows ) such that:

$$\overline{K}=\alpha \frac{{N}_{B}}{{N}_{rows}}\frac{E{w}^{3}t}{{l}_{M}^{3}}$$

where N B is the number of beams in each row, N rows is the number of rows along the loading direction, and α is a numerical coefficient which is dependent on boundary conditions and beam shape. As the major cuts define the primary beam dimensions l, w, t, minor cuts are introduced to explore the tunability of α. Figure 2b illustrates the stiffness dependence of a kirigami sheet on minor cuts as a function of the dimensionless minor cut parameter l m /(2w). Here, a kirigami sheet without minor cuts shows the highest stiffness while as minor cuts are introduced the stiffness decreases as l m /(2w) increases. Additionally, at each value of l m /(2w), stiffness decreases as the minor cuts intersect the major cuts and as the number of minor cuts increases. We consider that in the absence of minor cuts the ends of each beam are restrained from rotation and the in-plane bending occurs through the opening of major cuts and is analogous to a fixed-fixed end condition (FFE). As minor cuts are introduced near beam ends the FFE boundary conditions relax as the hinge regions are softened and can no longer support bending moments resulting in a transition to pinned-pinned end conditions (PPE). This leads to deformations through the opening of major and minor cuts. To quantitatively describe this behavior the numerical coefficient α is calculated and is found to range between FFE (α = 16) and PPE condition (α = 4) (See Fig. S2 for derivations). When these bounds are plotted in Fig. 2b it is seen that the data falls within the bounds of these conditions for design i-iv, supporting the analogy of minor cuts to beam boundary conditions.

We further explore beam geometry by applying a kirigami design to create non-prismatic beams (Figs 2a(v) and S3). In most cases, non-prismatic beams with varying moments of inertia along the length are employed for enhancing mechanical strength and stiffness36. In contrast, we utilize this approach in the kirigami system to further reduce stiffness and obtain an ultra-soft kirigami structure. This is achieved by introducing minor cuts onto the beam midspan without changing major cut length. The design decreases the area moment of inertia in regions where the bending moment is largest, resulting in an enhanced softening effect on the PPE condition. Upon calculating, the numerical coefficient α is ≈0.8 (Fig. S3), which is lower than the PPE condition (α = 4), and is consistent with the trend in the data in Fig. 2b.

Upon rearrangement of equation (1) the relation between effective stiffness and geometric parameters is \(\overline{K}/Et=\alpha \tfrac{{N}_{B}}{{N}_{rows}}{(w/{l}_{M})}^{3}\). Figure 2c presents a log-log plot of our experimental data with 52 combinations of major (two different lengths l M  = 20 mm, 30 mm and three different widths w = 2 mm, 3 mm, and 4 mm) and minor cuts and shows that the data for prismatic beams collapses into the range bounded by FFE and PPE conditions. Some deviation from this prediction is observed as l M  ≤ 5w, which was also observed by Isobe et al.28, as the beam begins to violate the slender beam assumption. The stiffness is greatly reduced by constructing kirigami structures with non-prismatic beams. When design (v) with 0.75 l m /(2w) is adopted, which shows the smallest moment of inertia in the midspan of our designs, the stiffness decreases by a factor of ≈22–30 compared to systems consisting only of major cuts. The stiffness data for this non-prismatic beam continues to follow the scaling prediction with α ≈ 0.8. Additionally, the ultra-soft kirigami structure shows significantly reduced stiffness compared to a design with just major cuts throughout the entire strain range (see Fig. S4). These dramatic changes in stiffness through the α parameter by controlling boundary conditions and moment of inertia along the beam greatly increases design flexibility of kirigami materials, especially in systems with size limitations or fabrication constraints.

In addition to the control of initial stiffness, kirigami structures can also tune the ultimate strain (ε ULT ) of materials. Figure 2d illustrates the ultimate strain of each system with different geometries and arrays of minor cuts as a function of a dimensionless major cut parameter w/l M . As the width-length ratio w/l M decreases, the ultimate strain increases as beams become relatively longer with regards to their cross-section (wt), resulting in larger axial displacements. In addition, the ultimate strain is affected by the array of minor cuts. The lowest ultimate strain is achieved utilizing only major cuts, whereas the highest is achieved for hybrid cuts with design v and l m /(2w) = 0.75. To predict ultimate strain where kirigami sheets break, we derive a model based on beam geometry at ultimate strain. Here, we assume w, \(d\ll {l}_{M}\) and expand previous models29 to include minor cuts and the reduction of ε ULT by edge effects such that:

$${\varepsilon }_{ULT}\cong \frac{({N}_{rows}-\mathrm{2)}\,({l}_{M}+\gamma {l}_{m})}{2{N}_{rows}w}-1$$

where γ is a numerical coefficient to account for the contribution of minor cuts to ε ULT ; γ = 0 in the absence of minor cuts (design i), γ = 1 or 2 in the presence of minor cuts in alternating rows (design iv) or every row (design v), respectively (Full derivation in Figs S5 and S6). Upon plotting ε ULT as a function of w/l M , we find excellent agreement between the experimental data and Equation 2. When minor cuts are included it enables further rotation of hinge regions by opening of minor cuts, as indicated by the increase in ε ULT for a fixed value of beam aspect ratio (w/l M ). Further, we find that the force at break of low to moderate aspect ratio beams (w/l M  ≥ 0.15) is not significantly influenced by minor cuts, with a slight decrease for very slender beams (w/l M  ≤ 0.1) (Fig. S7), which we attribute to the thin hinge regions. To increase the force capacity of these films the ends of the cuts could be modified with rounded or engineered corners, which has previously been demonstrated to reduce stress concentrations and delay fracture34. Thus, minor cuts provide an additional means to increase and tune the strain at break for kirigami materials.


To provide a general relationship for the design of kirigami structures consisting of arrays of beams for high extensibility and low stiffness, we combine Equations 1 and 2 such that:

$$\frac{{\varepsilon }_{ULT}}{\overline{K}}=\frac{1}{E\alpha }\,(\frac{{N}_{rows}}{{N}_{B}})\,(\frac{{l}_{M}+\gamma {l}_{m}}{2w}-1)\,\frac{{l}_{M}^{3}}{{w}^{3}t}$$

Equation 3 shows that the mechanical response of kirigami structures is controlled by the geometry (l M , w, t) and arrangement (N rows , N B ) of beams, which are defined by major cuts, the arrangement/length of minor cuts (α, l m , γ), and the elastic properties (E) of the film. The ε ULT /\(\overline{K}\) metric presented in Equation 3 is useful for understanding the soft mechanical response of materials. Here, materials with high extensibility and low stiffness will give large values of \({\varepsilon }_{ULT}/\overline{K}\), providing a means to compare material compliance. This is useful for fields such as stretchable and wearable electronics and soft robotics, where relative compliance can be used as a material selection tool37.

Upon plotting \({\varepsilon }_{ULT}/\overline{K}\) as a function of major and minor cut geometry in Fig. 3a, we find good agreement between the predictions and experimental data, where α provides a mechanism to tune the ratio of \({\varepsilon }_{ULT}/\overline{K}\) for a fixed beam geometry. As this equation is composed of geometric and material properties we expect the predictions to function over a wide range of scales from nanoscopic to macroscopic size scales. By rearranging Equation 3 to normalize for the number of beams in the system, we plot diverse experimental and simulation data from kirigami studies in literature along with our data in Fig. 3b. We observe that all the data with only major patterns collapse into a region bounded by α = 4 and α = 16 while the addition of minor cuts is captured with α = 0.8. This analysis describes the behavior of kirigami materials from sub-nanometer to millimeter film thickness with diverse material classes. Although nano-scale effects may influence the scaling at nanometer dimensions, the presented results and analysis provide evidence for the scalability of kirigami materials across tremendous length scales. Further experimentation with nano-scale 2D materials, such as graphene8, could be utilized as model systems to further explore the theoretical predictions at small scales.

Figure 3
figure 3

Generalized design criteria across length scales. (a) Mechanical property \({\varepsilon }_{ULT}/\overline{K}\) versus a combined geometric parameter for all the data in this work, where lines represent Equation 3. (b) Scaling plot showing agreement between Equation 3 and experimental/simulation data from kirigami materials in the literature and from the current work, across a wide range of length scales and material classes.

As our kirigami films are mechanically compliant and highly deformable, they enable opportunities to create multifunctional materials for soft and stretchable electronics and components for soft robotics. To investigate their use as stretchable conductors we add a conductive liquid metal electrode on top of kirigami films with a range of minor cut conditions and measure electrical resistance as a function of strain. We find that the electrical resistance of all the samples remains largely unchanged upon deformation, but the addition of minor cuts allows the stiffness and ultimate strains to be tuned (Fig. 4). In the case of an ultra-soft kirigami film, the electrical resistance increases by less than 10% up to a strain of 380%. The viability of kirigami as stretchable interconnects is demonstrated with a LED circuit (Fig. 4c), where the addition of minor cuts allows for strains up to ~400%, compared to ~230% with only major cuts. The LED is illuminated up to the breaking strain, showing the potential to create kirigami interconnects with easily tunable stiffness and deformation properties for stretchable electronic applications.

Figure 4
figure 4

Multifunctional materials through hybrid kirigami materials. (a) Load versus strain plot for kirigami stretchable electrodes with various hybrid designs. The inset shows the tunable stiffness in the initial regime (l M  = 20 mm, l m  = 4.5 mm, w = 3 mm). (b) Normalized resistance versus strain plot showing that the electrical resistance for each design remains largely constant through failure. (c) Demonstration of hybrid kirigami structures as stretchable interconnects under axial deformation up to 380% strain. (d) High speed photographs of a magnetoactive hybrid kirigami structure made of Fe-PDMS with design v (l M  = 15 mm, l m  = 1.3 mm, w = 0.9 mm, and t = 0.82 mm) in response to a magnetic field. (e) Strain versus time plot of the patterned sample during the first cycle and (f) during the initial cycling and after ~1000 cycles (final cycles) maintaining a large deformation (~330%). (g) Strain rate versus time plot of the sample during the initial cycles and final cycles, showing rapid motion in response to a magnetic field.

Furthermore, we show how our kirigami materials can be used as actuators or reconfigurable matter by creating magnetoactive soft actuators. Samples are fabricated by embedding Fe microparticles into a matrix of polydimethylsiloxane (PDMS) and then laser machining kirigami patterns into the cured composite. When a kirigami actuator with hybrid cut patterns (design v) is activated by an electromagnet, the sheet rapidly elongates to 330% strain in ~0.1 s with a maximum strain rate during the cycle greater than 10,000% s−1 (Fig. 4d,e and Video S1). By alternating the magnetic field on/off at 1 s intervals, the hybrid kirigami actuator is activated and released over 1,000 cycles without degradation in speed or stroke (Fig. 4f,g). This approach to adaptive soft actuators enables an unique and exceptional combination of high-speed actuation, large deformation, and stable reversibility, outperforming nearly all other soft matter actuators and morphing technologies38,39. By further tuning hybrid cut structures and material choice the actuators can respond and adapt to different stimuli across a range of length scales, providing a rich design space for multifunctional materials and structures.

The synergistic mechanical coupling of hybrid major and minor cuts in kirigami materials enables highly tunable mechanical metamaterials. These hybrid structures can introduce effective boundary conditions and non-prismatic structures which can be quantitatively captured by the numerical coefficient α, which in the current work was varied in the range of 0.8 ≤ α ≤ 16. However, α can be further controlled and decreased to create softer kirigami structures by increasing the length and number of minor cuts to further increase the proportion of regions where the moment of inertia is small. This approach can be used to increase the mechanical response of materials to external stimuli such as mechanical force, magnetic or electrical fields, or chemical triggers. We show how these hybrid structures can be used to create ultra-soft and highly deformable multifunctional materials such as stretchable conductors with nearly invariable resistance to extreme strain and actuators with rapid response and high elongation. The mechanical response of hybrid kirigami materials is well captured by our analytical expressions and leads to compact design criteria which can be used to efficiently create kirigami-based materials for diverse applications across a wide range of length scales.


Materials and mechanical measurements

Kirigami sheets are prepared by laser cutting (Epilog Laser Fusion M2, 75 watt) PET films (Grainger, E = 2.6 ± 0.1 GPa). The elastic modulus of pristine PET films is calculated from the initial, linear regime (\(\varepsilon \ll \mathrm{1 \% }\)) of a force-extension plot, captured with a 10 kN load cell on an Instron 5944. The kirigami patterns on the PET film consist of slender beams (l M  = 20, 30 mm) with rectangular cross-section (w = 2, 3, 4 mm, t = 0.13 mm). N B (=2) is the number of beams in each row and N rows (=30) is the number of rows along the loading direction. The patterned region had lengths of N rows w\(\cong \) 60, 90, 120 mm and widths of 2l M  + 3d\(\cong \) 46, 66 mm. Pristine regions at both ends of kirigami patterns are clamped during testing. Three samples are tested under uniaxial tension for each design and geometry (Fig. 2a) using an Instron 5944 mechanical testing machine with a 50 N load cell at a displacement rate of 1 mm/s. Mechanical parameters are analyzed and calculated using MATLAB.

Stretchable electronics demonstration

PET kirigami films are spray coated with an eutectic indium-gallium (EGaIn) electrode and thin copper film leads are attached to the plain regions of the kirigami sheets for electrical measurements. Kirigami films are clamped into the grips of an Instron 5944 as in the mechanical measurements and resistance is measured with a four-point probe method by attaching leads to the copper tape at each end of the sample. Electrical data is collected with a Keithley 2460 (Keithley Instruments. Inc.) and is synchronized with the mechanical measurements with a digital trigger. Furthermore, the electronics shown in Fig. 4c are fabricated by soldering LEDs onto copper film at each end of the sample.

Kirigami actuator

The kirigami actuator is composed of a single layer of patterned magneto-elastomer composite. It is a 820 μm thick film of polydimethylsiloxane (PDMS) elastomer (Sylgard 184 with a 10:1 base-to-curing agent ratio; Dow Corning) with 70% w/w 1 μm Fe microparticles (US Research Nanomaterials Inc.). The sample is prepared by hand-mixing the PDMS and microparticles with a rod for 10 min followed by vacuum mixing in a planetary mixer (FlackTek Inc.; DAC 400.2 VAC) for complete dispersion. The Fe-PDMS mixture is cast onto a clean glass plate to form an even layer using a thin-film applicator (ZUA 2000; Zehntner Testing Instruments). This is cured at 70 °C for 4 h. and then patterned with a CO2 laser cutter to generate kirigami films. The magnetic field is generated by an electromagnet (Bunting Magnetics Co.) connected to a DC power supply providing a step function current of 4.0 A for 1 s and then off for 1 s. For high cycle testing, the magnet is powered off periodically to prevent overheating. The slow motion of the actuator was recorded at 240 fps with iPhone 6 and the recorded video was analyzed with a video analysis tool (Tracker; Open Source Physics).


  1. Someya, T., Bao, Z. & Malliaras, G. G. The rise of plastic bioelectronics. Nat. 540, 379–385 (2016).

    ADS  CAS  Article  Google Scholar 

  2. Tonazzini, A. et al. Variable Stiffness Fiber with Self-Healing Capability. Adv. Mater. 10142–10148 (2016).

  3. Su, Y. et al. In-Plane Deformation Mechanics for Highly Stretchable Electronics. Adv. Mater. 29, 1604989 (2017).

    Article  Google Scholar 

  4. Morin, S. A. et al. Camouflage and display for soft machines. Sci. 337, 828–832 (2012).

    ADS  CAS  Article  Google Scholar 

  5. Dickey, M. D. Emerging applications of liquid metals featuring surface oxides. ACS Appl. Mater. Interfaces 6, 18369–18379 (2014).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  6. Chan, E. P., Walish, J. J., Thomas, E. L. & Stafford, C. M. Block copolymer photonic gel for mechanochromic sensing. Adv. Mater. 23, 4702–4706 (2011).

    CAS  Article  PubMed  Google Scholar 

  7. Mosadegh, B. et al. Pneumatic networks for soft robotics that actuate rapidly. Adv. Funct. Mater. 24, 2163–2170 (2014).

    CAS  Article  Google Scholar 

  8. Blees, M. K. et al. Graphene kirigami. Nat. 524, 204–207 (2015).

    ADS  CAS  Article  Google Scholar 

  9. Virk, K. et al. SILICOMB PEEK Kirigami cellular structures: mechanical response and energy dissipation through zero and negative stiffness. Smart Mater. Struct. 22, 084014 (2013).

    ADS  Article  Google Scholar 

  10. Castle, T., Sussman, D. M., Tanis, M. & Kamien, R. D. Additive lattice kirigami. Sci. Adv. 2, e1601258–e1601258 (2016).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  11. Sussman, D. M. et al. Algorithmic lattice kirigami: A route to pluripotent materials. Proc. Natl. Acad. Sci. 112, 7449–7453 (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  12. Neville, R. M., Scarpa, F. & Pirrera, A. Shape morphing Kirigami mechanical metamaterials. Sci. Reports 6, 31067 (2016).

    ADS  CAS  Article  Google Scholar 

  13. Castle, T. et al. Making the cut: Lattice kirigami rules. Phys. Rev. Lett. 113, 245502 (2014).

    ADS  Article  PubMed  Google Scholar 

  14. Hanakata, P. Z., Qi, Z., Campbell, D. K. & Park, H. S. Highly stretchable MoS2 kirigami. Nanoscale 8, 458–463 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  15. Liu, Y., Shaw, B., Dickey, M. D. & Genzer, J. Sequential self-folding of polymer sheets. Sci. Adv. 3, 1–7 (2017).

    CAS  Google Scholar 

  16. Lamoureux, A., Lee, K., Shlian, M., Forrest, S. R. & Shtein, M. Dynamic kirigami structures for integrated solar tracking. Nat. Commun. 6, 8092 (2015).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  17. Someya, T. et al. Conformable, flexible, large-area networks of pressure and thermal sensors with organic transistor active matrixes. Proc. Natl. Acad. Sci. United States Am. 102, 12321–12325 (2005).

    ADS  CAS  Article  Google Scholar 

  18. Sareh, S. & Rossiter, J. Kirigami artificial muscles with complex biologically inspired morphologies. Smart Mater. Struct. 22, 014004 (2013).

    ADS  Article  Google Scholar 

  19. Iwata, Y. & Iwase, E. Stress-Free Stretchable Electronic Device. Micro Electro Mech. Syst. (MEMS) 2017 IEEE, 231–234 (2017).

  20. Firouzeh, A. & Paik, J. The Design and Modeling of a Novel Resistive Stretch Sensor with Tunable Sensitivity. IEEE Sensors J. 15, 6390–6398 (2015).

    CAS  Article  Google Scholar 

  21. Song, Z. et al. Kirigami-based stretchable lithium-ion batteries. Sci. Reports 5, 10988 (2015).

    ADS  CAS  Article  Google Scholar 

  22. Lee, Y. K. et al. Chemical Sensing Systems that Utilize Soft Electronics on Thin Elastomeric Substrates with Open Cellular Designs. Adv. Funct. Mater. 27, 1605476 (2017).

    Article  Google Scholar 

  23. Yamamoto, Y. et al. Printed multifunctional flexible device with an integrated motion sensor for health care monitoring. Sci. Adv. 2, e1601473–e1601473 (2016).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  24. Saha, B., Baek, S. & Lee, J. Highly Sensitive Bendable and Foldable Paper Sensors Based on Reduced Graphene Oxide. ACS Appl. Mater. & Interfaces 9, 4658–4666 (2017).

    CAS  Article  Google Scholar 

  25. Guo, H. et al. All-in-One Shape-Adaptive Self-Charging Power Package for Wearable Electronics. ACS Nano 10, 10580–10588 (2016).

    CAS  Article  PubMed  Google Scholar 

  26. Wang, W. et al. Kirigami/Origami-Based Soft Deployable Reflector for Optical Beam Steering. Adv. Funct. Mater. 27, 1604214 (2017).

    Article  Google Scholar 

  27. Dias, M. A. et al. Kirigami Actuators. Soft Matter., (2017).

  28. Isobe, M. & Okumura, K. Initial rigid response and softening transition of highly stretchable kirigami sheet materials. Sci. Reports 6, 24758 (2016).

    ADS  CAS  Article  Google Scholar 

  29. Shyu, T. C. et al. A kirigami approach to engineering elasticity in nanocomposites through patterned defects. Nat. Mater. 14, 785–789 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  30. Rafsanjani, A. & Bertoldi, K. Buckling-Induced Kirigami. Phys. Rev. Lett. 118, 084301 (2017).

    ADS  Article  PubMed  Google Scholar 

  31. Cho, Y. et al. Engineering the shape and structure of materials by fractal cut. Proc. Natl. Acad. Sci. 111, 17390–17395 (2014).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  32. Tang, Y. et al. Programmable Kiri-Kirigami Metamaterials. Adv. Mater. 1604262 (2016).

  33. Gatt, R. et al. Hierarchical Auxetic Mechanical Metamaterials. Sci. Reports 5, 8395 (2015).

    CAS  Article  Google Scholar 

  34. Tang, Y. et al. Design of Hierarchically Cut Hinges for Highly Stretchable and Reconfigurable Metamaterials with Enhanced Strength. Adv. Mater. 27, 7181–7190 (2015).

    CAS  Article  PubMed  Google Scholar 

  35. Hwang, D.-G., Trent, K. & Bartlett, M. D. Kirigami-inspired Structures for Smart Adhesion. ACS Appl. Mater. Interfaces, acsami, 7b18594, (2018).

  36. Gere, J. M. & Timoshenko, S. P. Mechanics of Materials, 4th edn. (PWS Publishing Company, 1997).

  37. Bartlett, M. D. et al. High thermal conductivity in soft elastomers with elongated liquid metal inclusions. Proc. Natl. Acad. Sci. 114, 2143–2148 (2017).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  38. Nguyen, V. Q., Ahmed, A. S. & Ramanujan, R. V. Morphing soft magnetic composites. Adv. Mater. 24, 4041–4054 (2012).

    CAS  Article  PubMed  Google Scholar 

  39. Zhao, Q. et al. An instant multi-responsive porous polymer actuator driven by solvent molecule sorption. Nat. communications 5, 4293 (2014).

    Google Scholar 

Download references


Funding for this research is provided by Iowa State University of Science and Technology through startup funds and a 3 M Non-Tenured Faculty Award.

Author information

Authors and Affiliations



D.H. and M.D.B. designed research; D.H. performed research; D.H. and M.D.B. analyzed data; D.H. and M.D.B. wrote the paper.

Corresponding author

Correspondence to Michael D. Bartlett.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hwang, DG., Bartlett, M.D. Tunable Mechanical Metamaterials through Hybrid Kirigami Structures. Sci Rep 8, 3378 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing