Figure 2 | Scientific Reports

Figure 2

From: Electrochemical and Friction Characteristics of Metallic Glass Composites at the Microstructural Length-scales

Figure 2

Bulk wear results showing the (a) wear rate and coefficient of friction for 5 N load and (b) corresponding 3D optical profiler image at the end of test; (c) wear rate and coefficient of friction for 10 N load and (d) corresponding 3D optical profiler image. Wear volume loss in the 10 N test condition was significantly higher than the 5 N test condition, although friction values were similar.