# Theoretical prediction of a charge-transfer phase transition

## Abstract

Phase transition materials are attractive from the viewpoints of basic science as well as practical applications. For example, optical phase transition materials are used for optical recording media. If a phase transition in condensed matter could be predicted or designed prior to synthesizing, the development of phase transition materials will be accelerated. Herein we show a logical strategy for designing a phase transition accompanying a thermal hysteresis loop. Combining first-principles phonon mode calculations and statistical thermodynamic calculations considering cooperative interaction predicts a charge-transfer phase transition between the A–B and A+–B phases. As an example, we demonstrate the charge-transfer phase transition on rubidium manganese hexacyanoferrate. The predicted phase transition temperature and the thermal hysteresis loop agree well with the experimental results. This approach will contribute to the rapid development of yet undiscovered phase transition materials.

## Introduction

Phase transition phenomena such as spin-crossover, charge-transfer, metal–insulator, and crystal–amorphous transitions have been aggressively studied1,2,3,4,5,6,7,8,9,10,11,12,13,14,15. Phase transition materials are attractive from the viewpoint of practical applications because external stimuli such as light, pressure, or an electric field can switch the physical properties of the material16,17,18,19,20,21,22,23,24,25,26,27,28,29,30,31,32,33,34,35,36,37,38,39. For example, crystal–amorphous phase transition materials are used in optical memories and resistance random access memories1,2. Spin-crossover complexes have been studied as color switching materials6,7,8,16,17,18,19,20, while lambda-trititanium-pentoxide has potential in optical memory devices and heat storage applications28,35. Cyanide-bridged bimetallic assemblies exhibit charge-transfer phase transitions10,11,12,21,22,23,24,25. One cyanide-bridged bimetallic assembly, rubidium manganese hexacyanoferrate, shows a charge-transfer phase transition, which can be induced by light, pressure, or an electric field39,40,41,42,43,44.

However, questions remain in phase transition materials research. Can phase transition materials be designed? Can switching materials originating from bistability be predicted? Herein we consider a strategy to predict phase transitions. Estimations of thermodynamic parameters, such as enthalpy, entropy, and Gibbs free energy, are necessary to predict phase transitions. Additionally, the cooperative interaction inside the crystal at the phase transition must be evaluated to predict a thermal hysteresis loop. In this study, we predict a charge-transfer phase transition on rubidium manganese hexacyanoferrate as a demonstration system using a combination method between first-principles calculations and statistical thermodynamic calculations. To confirm our prediction, we synthesize the material and evaluate the validity of our prediction.

As a first step, we considered a flowchart of a logical strategy to predict the charge-transfer phase transition between the A–B phase (α-phase) and its valence isomer where one electron transfers from A to B, i.e., A+–B phase (β-phase) (Fig. 1). On the basis of first-principles calculation of the electronic structure and phonon modes, the crossover temperature between the Gibbs energies for the α-phase (G α(T)) and β-phase (G β(T)) corresponding to the phase transition temperature (T p) is predicted. As a second step, to determine whether a system has a thermal hysteresis, the statistical thermodynamic Slichter-Drickamer (SD) model45, which is one of the mean-field regular solution models, is adopted. In the SD model, the excess enthalpy, ΔH E, is expressed by γx(1− x), where γ is the interaction parameter due to the interaction between the A–B and A+–B units, and x is the fraction of the A+–B unit. To evaluate γ, we need to consider the virtual transient phase (tr-phase), such as the A–B–A+–B phase. From the results of SD model calculations, whether a thermal hysteresis loop appears or not can be determined. The detail explanation of the strategy mentioned above are described in the Methods section.

In the case of rubidium manganese hexacyanoferrate, the α- and β-phases correspond to the FeII(S = 0)–CN–MnIII(S = 2) phase (FeII–MnIII phase) and the FeIII(S = 1/2)–CN–MnII(S = 5/2) phase (FeIII–MnII phase), respectively. Hereafter, we try to predict the charge-transfer phase transition between the FeII–MnIII and FeIII–MnII phases.

## Results and Discussion

### First-principles electronic structure calculations of the FeII–MnIII and FeIII–MnII phases

To calculate the formation enthalpies of the FeII–MnIII and FeIII–MnII phases at zero kelvin, $${H}_{\text{F,}{\text{Fe}}^{\text{II}}{\text{Mn}}^{\text{III}}}$$ and $${H}_{\text{F,}{\text{Fe}}^{\text{II}\text{I}}{\text{Mn}}^{\text{II}}}$$, first-principles electronic structure calculations were performed using the Vienna ab initio Simulation Package (VASP). We adopted a screened Coulomb hybrid functional calculation of the Heyd–Scuseria–Ernzerhof (HSE06) hybrid functional as the calculation method (see Methods). HSE06 was selected because the formation enthalpies of the FeII–MnIII and FeIII–MnII phases must be compared precisely. The hybrid functional calculation is suitable because it calculates the formation enthalpy with a higher accuracy and does not require tuning parameters (such as UJ in GGA + U). The obtained values of $${H}_{\text{F,}{\text{Fe}}^{\text{II}}{\text{Mn}}^{\text{III}}}$$ and $${H}_{\text{F,}{\text{Fe}}^{\text{II}\text{I}}{\text{Mn}}^{\text{II}}}$$ are −14476.69 kJ mol−1 and −14454.33 kJ mol−1, respectively.

### First-principles phonon mode calculations of the FeII–MnIII and FeIII–MnII phases

The phonon modes of the FeII–MnIII phase with a tetragonal structure in the $$I\bar{\text{4}}m\text{2}$$ space group (Fig. 2a (upper panel) and Table S1) were calculated by first-principles calculations using the Phonon code with GGA + U/PBE. The FeII–MnIII phase has 29 optical phonon modes and 3 acoustic phonon modes. Figure 2a (lower panel) shows the calculated phonon density of states of the FeII–MnIII phase. Furthermore, the transition probabilities of the optical phonon modes were calculated. From the obtained transition probabilities, the IR active optical spectra were determined (Fig. 3, blue lines). In the spectra, the phonon modes due to the symmetric bending and asymmetric bending modes of Fe–C≡N–Mn appear in the region of 100–650 cm−1, while the phonon modes due to the stretching mode of C≡N appear in the region of 2050–2250 cm−1 (Fig. 3(i)–(iii)). As representative examples, Movie S1 shows the atomic movements of the phonon modes at 302.4 cm−1, 525.0 cm−1, and 2130 cm−1, respectively.

The phonon modes of the FeIII–MnII phase with a cubic structure (space group, $$F\bar{\text{4}}\text{3}m$$) were calculated (Fig. 2b upper and Table S2). The FeIII–MnII phase has 16 optical phonon modes and 3 acoustic phonon modes. Figure 2b (lower panel) shows the calculated phonon density of states of the FeIII–MnII phase. The IR active optical spectrum was calculated from the transition probabilities (Fig. 3, red lines). In the spectra, the phonon modes corresponding to the symmetric bending and asymmetric bending modes of Fe–C≡N–Mn appear in the region of 100–650 cm−1, while one peak appears due to the stretching mode of C≡N in the region of 2150–2200 cm−1 (Fig. 3(iv)–(vi)). As representative examples, Movie S2 shows the atomic movements of the phonon modes at 189.2 cm−1, 411.2 cm−1, and 2179 cm−1, respectively. From the results of the phonon mode calculations for the FeII–MnIII and FeIII–MnII phases, the vibrational enthalpy H vib(T) and vibrational entropy S vib(T) curves are obtained.

### Prediction of the phase transition and evaluation of the phase transition temperature

Based on the first-principles electronic structure calculations and phonon mode calculations, we considered whether the charge-transfer induced phase transition occurs in rubidium manganese hexacyanoferrate. From the sum of the formation enthalpy (H F) and the vibrational enthalpy (H vib(T)), the temperature dependence of the enthalpy (H(T)) of each phase was obtained (Fig. 4a). On the other hand, the entropy (S(T)) of each phase was obtained as the sum of S vib(T) (Fig. 4b) and the contribution from the orbital degeneracy and the spin multiplicity (S os). The S os value for the FeII–MnIII phase is Rln5 due to FeII(1 A 1g) and MnIII(5 B 1g), while that for FeIII–MnII phase is Rln36 due to FeIII(2 T 2g) and MnII(6 A 1g) (Supplementary Information). Using these thermodynamic parameters, the Gibbs free energies of the FeII–MnIII phase and the FeIII–MnII phase were evaluated. As shown in Fig. 5a, the $${G}_{{\text{Fe}}^{\text{II}}{\text{Mn}}^{\text{III}}}$$(T) and $${G}_{{\text{Fe}}^{\text{III}}{\text{Mn}}^{\text{II}}}$$(T) curves show a crossover at a specific temperature. This calculation predicts that the present system may show a charge-transfer phase transition at T p = 325 K. At T p, transition enthalpy and transition entropy are ∆H = 18.43 kJ mol−1 and ∆S = 56.44 J K−1 mol−1, respectively. The FeII–MnIII phase is stable below T p, while the FeIII–MnII phase becomes stable above T p.

### Evaluation of a thermal hysteresis loop in the phase transition

As a second step, we considered whether a thermal hysteresis loop appears in the present system. The x value of ΔH E(T) = γx(1 − x) corresponds to the fraction of the FeIII–MnII phase, and γ is an interaction parameter between the FeII–MnIII and FeIII–MnII units. To obtain the γ value, we need to consider an intermediate phase between the FeII–MnIII and FeIII–MnII phases. Here, we set a virtual transient phase of (A–B layer)-by-(A+–B layer) structure (i.e., (FeII–MnIII layer)-by-(FeIII–MnII layer) structure) (Figure S1). The enthalpy of this virtual transient phase (H tr(T)) was calculated by first-principles electronic structure calculations and phonon mode calculation. From the relation of $${\rm{\Delta }}{H}^{E}(T)={H}_{{\rm{tr}}}(T)-({H}_{{{\rm{Fe}}}^{{\rm{II}}}{{\rm{Mn}}}^{{\rm{III}}}}(T)+{H}_{{{\rm{Fe}}}^{{\rm{III}}}{{\rm{Mn}}}^{{\rm{II}}}}(T))/2$$, ΔH E(T) is 7.85 kJ mol−1 at T = 325 K (Fig. 5b(i),(ii)), and the γ value is estimated to be 31.4 kJ mol−1 (=γ 0). Using the γ 0 value, the thermal hysteresis loop was calculated based on the SD model (Fig. 5b(iii)). Additionally, we also calculated the x vs. T curves by adopting smaller interaction parameters such as γ 0/2, γ 0/3, γ 0/4, and γ 0/10. Figure 5b(iv)–(viii) show the calculated thermal hysteresis loops for various interaction parameter values. With increasing the γ value, the x vs. T curve changes from a gradual continuous phase change to a first-order phase transition, and eventually to a phase transition with a thermal hysteresis loop.

For example, in the case of the x vs. T curve with γ (=γ 0/3) = 10.5 kJ mol−1, the FeIII–MnII phase transits to FeII–MnIII phase at 263 K (≡ T : defined as the phase transition temperature in the cooling process), whereas the FeII–MnIII phase transits to FeIII–MnII phase at 364 K (≡ T : defined as the phase transition temperature in the warming process). The width of the thermal hysteresis loop (ΔT = T T ) is 101 K. In the case of γ (=γ 0/2) = 15.7 kJ mol−1, the values of T , T , and ΔT are 132 K, 416 K, and 284 K, respectively. Therefore, the calculation results predict that a charge-transfer induced phase transition should occur in rubidium manganese hexacyanoferrate and that a thermal hysteresis loop should appear due to a large interaction parameter value.

### Synthesis of rubidium manganese hexacyanoferrate

To confirm the prediction, we synthesized rubidium manganese hexacyanoferrate. The target compound was prepared according to a modified synthetic method from our previous report41. An aqueous solution of manganese(II) chloride (0.1 mol dm−3) was reacted with a mixed aqueous solution of potassium ferricyanide (0.1 mol dm−3) and rubidium chloride (1.2 mol dm−3). Elemental analysis shows that the formula of the obtained compound is Rb0.94Mn[Fe(CN)6]0.98·0.3H2O: Calculated; Rb, 23.06; Mn, 15.77; Fe, 15.71; C, 20.27; N, 23.64%: Found; Rb, 22.96; Mn, 15.86; Fe, 15.78; C, 20.09; N, 23.50%. The X-ray powder diffraction pattern with Rietveld analysis indicates that the crystal structure at room temperature is cubic ($$F\bar{\text{4}}\text{3}m$$) with a lattice constant of a = 10.5639(3) Å (Figure S2).

As an additional sample, Rb0.97Mn[Fe(CN)6]0.99∙0.3H2O was prepared using a different synthetic technique involving polyethylene glycol monolaurate (PGM)46. A PGM solution containing an aqueous solution of MnCl2 (0.2 mol dm−3) and RbCl (1 mol dm−3), and a PGM solution containing aqueous solution of K3[Fe(CN)6] (0.2 mol dm−3) and RbCl (1 mol dm−3) were mixed. A precipitate was obtained by centrifuging, washing in methanol, and drying in air. The X-ray powder diffraction pattern shows that the crystal structure at room temperature is cubic ($$F\bar{\text{4}}\text{3}m$$) with a lattice constant of a = 10.5606(1) Å46.

### IR spectra of rubidium manganese hexacyanoferrate

The variable temperature optical phonon spectra were measured using IR spectrometry. The spectra of Rb0.94Mn[Fe(CN)6]0.98·0.3H2O are shown in Fig. 6a. Absorption peaks are observed in the IR spectra of the FeII–MnIII phase measured at 100 K, at 170, 230, 300, 465, 545, and 610 cm−1, which are assigned to the symmetric bending and asymmetric bending modes of FeII–C≡N–MnIII (Fig. 6a, blue lines). In the high-energy region, one broad peak is observed around 2100 cm−1, which is assigned to the C≡N stretching mode. On the other hand, the IR absorption spectra for the FeIII–MnII phase measured at 300 K are shown with red lines in Fig. 6a. The observed spectra correspond well with the calculated spectra. Therefore, the absorption peaks are assigned as follows: the peaks at 190, 415, and 530 cm−1 are assigned to the symmetric bending and asymmetric bending modes of FeIII–C≡N–MnII, and the peak at 2152 cm−1 is assigned to the C≡N stretching mode. As for the C≡N stretching mode, the Raman activity is also confirmed by Raman spectroscopy (Figure S3).

### Observation of the phase transition and thermal hysteresis loop for Rb0.94Mn[Fe(CN)6]0.98·0.3H2O and Rb0.97Mn[Fe(CN)6]0.99∙0.3H2O

The variable temperature IR spectra and the FeIII–MnII phase fraction vs. T plots of Rb0.94Mn[Fe(CN)6]0.98·0.3H2O are shown in Fig. 6b and c, respectively. By increasing T at a heating rate of +0.5 K min−1, the FeIII–MnII phase appears at 304 K (≡T ↑,obs: defined as the temperature with 50% of FeIII–MnII phase in the warming process). With decreasing T, the FeII–MnIII phase appears at 213 K (≡T ↓,obs: defined as the temperature with 50% fraction in the cooling process). The phase transition temperature, defined as T p,obs = (T ↑,obs + T ↓,obs)/2, is 259 K. This T p,obs value is 80% of the predicted phase transition temperature of T p = 325 K mentioned above. The width of the thermal hysteresis loop, defined as ∆T obs = T ↑,obsT ↓,obs, of this system is 91 K. It is noted that, the width of the thermal hysteresis loop ΔT is not a unique value but is spread in the range of 79 K ≤ ΔT ≤ 117 K as shown in Fig. 6d. Such a broadness of ΔT corresponds to the width of the calculated hysteresis loop with γ in the range of 9.7 kJ mol−1 ≤ γ ≤ 10.4 kJ mol−1.

Rb0.97Mn[Fe(CN)6]0.99∙0.3H2O shows a phase transition with T ↑,obs = 301 K, T ↓,obs = 178 K, and then T p,obs = 240 K. The hysteresis width ∆T obs is a large value of 123 K (Fig. 6e). This ∆T obs value is close to the calculated ∆T value with γ = 11.3 kJ mol−1 (=γ 0/2.8). Additionally, in the thermal hysteresis, components of ∆T approaching 150 K are also included, i.e., 117 K ≤ ΔT ≤ 150 K (Fig. 6f), which corresponds to 11.0 kJ mol−1 ≤ γ ≤ 12.2 kJ mol−1. The results of these two samples show that the γ value is in the range of γ 0/3 < γ < γ 0/2, indicating that the theoretical prediction is reasonable.

Let us consider γ in the present system. It is known that γ can be expressed as γ = 2 γ αβγ ααγ ββ, where γ αα is the interaction parameter between α-sites, γ αβ is the interaction parameter between α- and β-sites, and γ ββ is the interaction parameter between β-sites47. The following effects are known as the origins of the interaction at the atomic level: electrostatic interaction between coordinated molecules48, intermolecular coupling of the molecular distortions49,50,51, elastic interaction between metal ions of different spins52,53,54, and electron–phonon coupling55. In the light of these reports, the origin of γ in the present charge-transfer phase transition system is considered as electrostatic interaction among charge-transferred sites (MnIII/II and FeII/III), Jahn-Teller distortion on MnIII, and elastic interaction between metal ions of different spins.

The magnitude of the γ value depends on the structure of the assumed virtual transient phase. Although there are some differences between the predictions and the experimental results, the calculations agree with the observations fairly well, indicating that a prediction of a phase transition is possible using the present strategy. As an additional note, there are defects in the real systems of Rb0.94Mn[Fe(CN)6]0.98·0.3H2O and Rb0.97Mn[Fe(CN)6]0.99∙0.3H2O, which are considered to weaken the interaction parameter compared to the ideal crystal structure of RbMn[Fe(CN)6] (Figure S4). Furthermore, such defects in the crystal have a possibility of causing domain nucleation and accelerating domain growth56. In this case, the width of thermal hysteresis loop would become narrower compared to the ideal crystal system.

## Conclusion

In this study, we proposed a logical strategy to design a phase transition material accompanying a thermal hysteresis loop. The strategy is as follows: (i) The thermodynamic parameters of enthalpy, entropy, and Gibbs energy are calculated by first-principles electronic structure calculations and phonon mode calculations, and the possibility of a phase transition and the transition temperature are evaluated. (ii) Then, whether the system has a thermal hysteresis or not and the width of the thermal hysteresis loop are determined using a statistical thermodynamic mean-field theory.

As a demonstration, we investigated the charge-transfer phase transition on a rubidium manganese hexacyanoferrate. The predicted phase transition temperature and the thermal hysteresis loop agree well with the experimental results. The approach shown in this paper could be applied to structural phase transitions such as charge-transfer, spin-transition, metal-insulator phase transitions, etc., and will contribute to the rapid development of yet undiscovered phase transition materials. Moreover, if the flowchart for a logical strategy to predict the phase transition shown in this study is eventually implemented to artificial intelligence (AI), numerous phase transition materials could be discovered inside a computer.

## Methods

### Flowchart of the strategy for theoretical prediction

The formation enthalpies at zero kelvin of the α- and β-phases, H F,α and H F,β, are obtained by first-principles periodic structure calculations of the electronic structures (Fig. 1, upper). The temperature dependence of the enthalpies due to the lattice vibrations can be obtained by first-principles phonon mode calculations, H vib,α(T) and H vib,β(T). The sum of H F,α and H vib,α(T) shows the temperature dependence of enthalpy, H α(T). In a similar manner, H β(T) is obtained. The phonon mode calculations also provide the vibrational entropies of the α- and β-phases, S vib,α(T) and S vib,β(T), respectively. Additionally, the degeneracy of the orbitals and the multiplicity of the spins contribute to the entropy as orbital-and-spin entropy, S os. The S os value is obtained by RlnW, where R is the gas constant and W = (orbital degeneracy) × (spin multiplicity) = (2l + 1)(2s + 1). Therefore, S(T) is expressed as the sum of S vib(T) and S os (i.e., S α(T) = S vib,α(T) + S os,α and S β(T) = S vib,β(T) + S os,β). Based on the aforementioned thermodynamic parameters, the Gibbs energies for the α- and β-phases, G α(T) and G β(T), are evaluated. The crossover temperature between G α(T) and G β(T) corresponding to the phase transition temperature, T p, is predicted.

To determine whether a system has a thermal hysteresis, the SD model was adopted (Fig. 1, lower). In the SD model, the excess enthalpy ΔH E is expressed by γx(1 − x), where γ is the interaction parameter due to the interaction between the A–B and A+–B units, and x is the fraction of the A+–B unit. To evaluate γ, we need to consider the virtual transient phase (tr-phase), such as the –A–B–A+–B phase. The enthalpy of this virtual transient phase H tr(T) was calculated by first-principles electronic structure calculations and phonon mode calculations.

The ΔH E(T) value corresponds to the difference between H tr(T) and the average formation enthalpy of the α- and β-phases (i.e., ΔH E(T) = H tr(T)−{H α(T) + H β(T)}/2). From the relation of ΔH E(T) = γx(1 − x), γ is obtained. Then the x vs. T plots can be evaluated by the SD model. The Gibbs energy in the SD model, G SD(T), is described by G SD(T) = x(H β(T) − H α(T)) + γx(1 − x) + T{R[xlnx + (1 − x)ln(1 − x) − x(S β(T) − S α(T))]}. From the results of the SD model calculations, whether a thermal hysteresis loop appears or not can be determined.

### First-principles calculations of formation enthalpies

The formation enthalpies of the FeII–MnIII and FeIII–MnII phases and the virtual transient phase were calculated by first-principles calculations using VASP, which is a plane-wave projector augmented wave (PAW) method program57,58. To obtain accurate values, HSE06 hybrid functional was used for the exchange-correlation energy59,60,61,62. The range separation parameter of 0.2 Å−1 was adopted for HSE06. The plane-wave cutoff energy was set to 500 eV, and the electronic iterations convergence were 1 × 10−6 eV. Calculations were performed with k-mesh of 3 × 3 × 3 for all phases.

### First-principles calculations of phonon modes

First-principles phonon mode calculations based on density functional theory were conducted for rubidium manganese hexacyanoferrate, RbMn[Fe(CN)6], using the Phonon code by GGA + U/PBE. Wave functions based on the plane waves and the potentials of the core orbitals were represented by the projector-augmented wave of Blöchl. The exchange-correlation term was evaluated by the generalized gradient approximation by Perdew, Burke, and Ernzerhof. The reported tetragonal and cubic lattice parameters for the FeII–MnIII and FeIII–MnII phases of rubidium manganese hexacyanoferrate were used as the initial structures in the computed models41. The lattice parameters and atomic positions were optimized with an energy cutoff of 500 eV and a 3 × 3 × 3 k-mesh until satisfying a 10−5 eV pm−1 force tolerance. √2 × √2 × 1 supercells of the optimized structures were used to calculate the phonon modes of RbMn[Fe(CN)6], which were calculated by the direct method implemented in Phonon code with 2-pm displacements using the optimized atomic positions. U − J value was set to 4.0 eV for Fe and Mn (Supplementary Information).

### Measurements

Elemental analyses for Rb, Mn, and Fe were performed by HP4500 inductively coupled plasma mass spectroscopy, while those for C and N were performed by standard microanalytical methods. X-ray powder diffraction measurements were performed with a Rigaku Ultima IV diffractometer with Cu K α radiation (λ = 1.5418 Å). The PDXL program (Rigaku) was used for the Rietveld analyses. For the spectroscopic measurements, a JASCO 6100 spectrometer was used in the energy region of 100–650 cm−1, and a Shimadzu FT-IR 8200PC spectrometer was used in the energy region of 1950–2300 cm−1. Raman spectra were measured with a Raman microspectrometer (JASCO NRS-5100).

## References

1. 1.

Kolobov, A. V. et al. Understanding the phase-change mechanism of rewritable optical media. Nature Mater. 3, 703–708 (2004).

2. 2.

Wuttig, M. & Yamada, N. Phase-change materials for rewriteable data storage. Nature Mater. 6, 824–832 (2007).

3. 3.

Gütlich, P., Hauser, A. & Spiering, H. Thermal and optical switching of iron(II) complexes. Angew. Chem., Int. Ed. Engl. 33, 2024–2054 (1994).

4. 4.

Kahn, O. & Martinez, C. J. Spin-transition polymers: From molecular materials toward memory devices. Science 279, 44–48 (1998).

5. 5.

Renz, F. et al. Strong field iron (II) complex converted by light into a long-lived high-spin state. Angew. Chem., Int. Ed. 39, 3699–3700 (2000).

6. 6.

Létard, J. F. et al. Light induced excited pair spin state in an iron(II) binuclear spin-crossover compound. J. Am. Chem. Soc. 121, 10630–10631 (1999).

7. 7.

Real, J. A. et al. Spin crossover in a catenane supramolecular system. Science 268, 265–267 (1995).

8. 8.

Ohkoshi, S., Imoto, K., Tsunobuchi, Y., Takano, S. & Tokoro, H. Light-induced spin-crossover magnet. Nature Chem. 3, 564–569 (2011).

9. 9.

van der Veen, R. M., Kwon, O. H., Tissot, A., Hauser, A. & Zewail, A. H. Single-nanoparticle phase transitions visualized by four-dimensional electron microscopy. Nature Chem. 5, 395–402 (2013).

10. 10.

Bleuzen, A. et al. Photoinduced ferrimagnetic systems in Prussian blue analogues CI x Co4[Fe(CN)6] y (CI = alkali cation). 1. Conditions to observe the phenomenon. J. Am. Chem. Soc. 122, 6648–6652 (2000).

11. 11.

Ohkoshi, S., Hamada, Y., Matsuda, T., Tsunobuchi, Y. & Tokoro, H. Crystal structure, charge-transfer-induced spin transition, and photoreversible magnetism in a cyano-bridged cobalt–tungstate bimetallic assembly. Chem. Mater. 20, 3048–3054 (2008).

12. 12.

Avendano, C. et al. Temperature and light induced bistability in a Co3[Os(CN)6]2 6H2O Prussian blue analog. J. Am. Chem. Soc. 132, 13123–13125 (2010).

13. 13.

Miyano, K., Tanaka, T., Tomioka, Y. & Tokura, Y. Photoinduced insulator-to-metal transition in a perovskite manganite. Phys. Rev. Lett. 78, 4257–4260 (1997).

14. 14.

Fiebig, M., Miyano, K., Tomioka, Y. & Tokura, Y. Visualization of the local insulator–metal transition in Pr0.7Ca0.3MnO3. Science 280, 1925–1928 (1998).

15. 15.

Coey, J. M. D., Viret, M. & von Molnár, S. Mixed-valence manganites. Adv. Phys. 48, 167–293 (1999).

16. 16.

Decurtins, S., Gütlich, P., Köhler, C. P., Spiering, H. & Hauser, A. Light-induced excited spin state trapping in a transition-metal complex: The hexa-1-propyltetrazole-iron(II) tetrafluoroborate spin-crossover system. Chem. Phys. Lett. 105, 1–4 (1984).

17. 17.

Cobo, S. et al. Single-laser-shot-induced complete bidirectional spin transition at room temperature in single crystals of [FeII(pyrazine)(Pt(CN)4)]. J. Am. Chem. Soc. 130, 9019–9024 (2008).

18. 18.

Ohkoshi, S. et al. 90-degree optical switching of output second-harmonic light in chiral photomagnet. Nature Photon. 8, 65–71 (2014).

19. 19.

Auböck, G. & Chergui, M. Sub-50-fs photoinduced spin crossover in [Fe(bpy)3]2+. Nature Chem. 7, 629–633 (2015).

20. 20.

Bertoni, R. et al. Elastically driven cooperative response of a molecular material impacted by a laser pulse. Nature Mater. 15, 606–610 (2016).

21. 21.

Bleuzen, A., Marvaud, V., Mathonière, C., Sieklucka, B. & Verdaguer, M. Photomagnetism in clusters and extended molecule-based magnets. Inorg. Chem. 48, 3453–3466 (2009).

22. 22.

Ohkoshi, S. et al. Photoinduced magnetization in copper octacyanomolybdate. J. Am. Chem. Soc. 128, 270–277 (2006).

23. 23.

Li, D. et al. Magnetic and optical bistability driven by thermally and photoinduced intramolecular electron transfer in a molecular cobalt–iron Prussian blue analogue. J. Am. Chem. Soc. 130, 252–258 (2008).

24. 24.

Pajerowski, D. M. et al. Persistent photoinduced magnetism in heterostructures of Prussian blue analogues. J. Am. Chem. Soc. 132, 4058–4059 (2010).

25. 25.

Ohkoshi, S. & Tokoro, H. Photomagnetism in cyano-bridged bimetal assemblies. Acc. Chem. Res. 45, 1749–1758 (2012).

26. 26.

Koshihara, S., Tokura, Y., Mitani, T., Saito, G. & Koda, T. Photoinduced valence instability in the organic molecular compound tetrathiafulvalene-p-chloranil (TTF-CA). Phys. Rev. B 42, 6853–6856 (1990).

27. 27.

Collet, E. et al. Laser-induced ferroelectric structural order in an organic charge-transfer crystal. Science 300, 612–615 (2003).

28. 28.

Ohkoshi, S. et al. Synthesis of a metal oxide with a room-temperature photoreversible phase transition. Nature Chem. 2, 539–545 (2010).

29. 29.

Gütlich, P., Gaspar, A. B., Ksenofontov, V. & Garcia, Y. Pressure effect studies in molecular magnetism. J. Phys.: Condens. Matter. 16, S1087–S1108 (2004).

30. 30.

Coronado, E. et al. Pressure-tuning of magnetism and linkage isomerism in iron(II) hexacyanochromate. J. Am.Chem. Soc. 127, 4580–4581 (2005).

31. 31.

Egan, L., Kamenev, K., Papanikolaou, D., Takabayashi, Y. & Margadonna, S. Pressure-induced sequential magnetic pole inversion and antiferromagnetic–ferromagnetic crossover in a trimetallic Prussian blue analogue. J. Am. Chem. Soc. 128, 6034–6035 (2006).

32. 32.

Avdeev, M. et al. Pressure-induced ferroelectric to antiferroelectric phase transition in Pb0.99(Zr0.95Ti0.05)0.98Nb0.02O3. Phys. Rev. B 73, 064105/1–14 (2006).

33. 33.

Takabayashi, Y. et al. The disorder-free non-BCS superconductor Cs3C60 emerges from an antiferromagnetic insulator parent state. Science 323, 1585–1590 (2009).

34. 34.

Nayak, A. P. et al. Pressure-induced semiconducting to metallic transition in multilayered molybdenum disulphide. Nature Commun. 5, 3731 (2014).

35. 35.

Tokoro, H. et al. External stimulation-controllable heat-storage ceramics. Nature Commun. 6, 7037 (2015).

36. 36.

Asamitsu, A., Tomioka, Y., Kuwahara, H. & Tokura, Y. Current switching of resistive states in magnetoresistive manganites. Nature 388, 50–52 (1997).

37. 37.

Yamanouchi, M., Chiba, D., Matsukura, F. & Ohno, H. Current-induced domain-wall switching in a ferromagnetic semiconductor structure. Nature 428, 539–542 (2004).

38. 38.

Ikeda, S. et al. A perpendicular-anisotropy CoFeB–MgO magnetic tunnel junction. Nature Mater. 9, 721–724 (2010).

39. 39.

Mahfoud, T. et al. Electric-field-induced charge-transfer phase transition: A promising approach toward electrically switchable devices. J. Am. Chem. Soc. 131, 15049–15054 (2009).

40. 40.

Tokoro, H., Ohkoshi, S. & Hashimoto, K. One-shot-laser-pulse-induced demagnetization in rubidium manganese hexacyanoferrate. Appl. Phys. Lett. 82, 1245–1247 (2003).

41. 41.

Tokoro, H., Ohkoshi, S., Matsuda, T. & Hashimoto, K. A large thermal hysteresis loop produced by a charge-transfer phase transition in a rubidium manganese hexacyanoferrate. Inorg. Chem. 43, 5231–5236 (2004).

42. 42.

Ohkoshi, S. et al. Coexistence of ferroelectricity and ferromagnetism in a rubidium manganese hexacyanoferrate. Angew. Chem., Int. Ed. 46, 3238–3241 (2007).

43. 43.

Vertelman, E. J. M. et al. Light- and temperature-induced electron transfer in single crystals of RbMn[Fe(CN)6]·H2O. Chem. Mater. 20, 1236–1238 (2008).

44. 44.

Tokoro, H. et al. Visible-light-induced reversible photomagnetism in rubidium manganese hexacyanoferrate. Chem. Mater. 20, 423–428 (2008).

45. 45.

Slichter, C. P. & Drickamer, H. G. Pressure-induced electronic changes in compounds of iron. J. Chem. Phys. 56, 2142–2160 (1972).

46. 46.

Tokoro, H., Nakagawa, K., Imoto, K., Hakoe, F. & Ohkoshi, S. Zero thermal expansion fluid and oriented film based on a bistable metal-cyanide polymer. Chem. Mater. 24, 1324–1330 (2012).

47. 47.

Kahn, O. Molecular Magnetism. VCH-Verlag, Weinheim, New York 1993.

48. 48.

Kepenekian, M., Guennic, B. L. & Robert, V. Primary role of the electrostatic contributions in a rational growth of hysteresis loop in spin-crossover Fe(II) complexes. J. Am. Chem. Soc. 131, 11498–11502 (2009).

49. 49.

Kambara, T. The effect of iron concentration on the high-spin ↔ low spin transitions in iron compounds. J. Phys. Soc. Jpn. 49, 1806–1811 (1980).

50. 50.

Sasaki, N. & Kambara, T. Theory of cooperative high-spin ↔ low spin transitions in iron (III) compounds induced by the molecular distortions. J. Chem. Phys. 74, 3472–3481 (1981).

51. 51.

Kambara, T. Theory of high-spin ↔ low spin transitions in transition metal compounds induced by cooperative molecular distortions and lattice strains. J. Chem. Phys. 74, 4557–4565 (1981).

52. 52.

Ohnishi, T. & Sugano, S. Strain interaction effects on the high-spin–low spin transition of transition metal compounds. J. Phys. C: Solid State Phys. 14, 39–55 (1981).

53. 53.

Spiering, H., Meissner, E., Köppen, H., Müller, E. W. & Gütlich, P. The effect of the lattice expansion on high spin ↔ low spin transitions. Chem. Phys. 68, 65–71 (1982).

54. 54.

Adler, P. et al. The influence of the lattice on the spin transition in solids. Investigations of the high spin ↔ low spin transition in mixed crystals of [Fe x M1−x (2-pic)3]Cl2∙MeOH. J. Phys. Chem. Solids 48, 517–525 (1987).

55. 55.

Zimmermann, R. A model for high-spin/low-spin transitions with an interpretation of thermal hysteresis effects. J. Phys. Chem. Solids 44, 151–158 (1983).

56. 56.

Slimani, A. et al. Visualization and quantitative analysis of spatiotemporal behavior in a first-order thermal spin transition: A stress-driven multiscale process. Phys. Rev. B 84, 094442/1–8 (2011).

57. 57.

Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

58. 58.

Xie, Y. & Kent, P. R. C. Hybrid density functional study of structural and electronic properties of functionalized Tin+1Xn (X = C, N) monolayers. Phys Rev. B 87, 235441/1–10 (2013).

59. 59.

Heyd, J., Scuseria, G. E. & Ernzerhof, M. Hybrid functionals based on a screened Coulomb potential. J. Chem. Phys. 118, 8207–8215 (2003).

60. 60.

Paier, J. et al. Screened hybrid density functionals applied to solids. J. Chem. Phys. 124, 154709/1–13 (2006).

61. 61.

Heyd, J., Scuseria, G. E. & Ernzerhof, M. Hybrid functionals based on a screened Coulomb potential [vol 118, pg 8207, (2003)]. J. Chem. Phys. 124, 219906/1 (2006).

62. 62.

Eyert, V. VO2: A novel view from band theory. Phys. Rev. Lett. 107, 016401/1–4 (2011).

## Acknowledgements

The present research was supported in part by a JSPS Grant-in-Aid for specially promoted Research Grant Number 15H05697, JSPS KAKENHI Grant Number JP16H06521 Coordination Asymmetry, a JSPS Grant-in-Aid for Young Scientists (A), and the Shitagau Noguchi Foundation. We also recognize the Cryogenic Research Center, The University of Tokyo, and Nanotechnology Platform, which are supported by MEXT. We are grateful to Dr. K. Nakagawa and Dr. Y. Umeta for the technical support.

## Author information

Authors

### Contributions

H.T. performed samples synthesis, characterization, thermodynamic calculations, and contributed to all measurements and calculations. A.N. contributed to writing the manuscript, the analysis of the thermodynamic calculations and preparation of the figures. M.Y. contributed to analysing the first-principles calculations and thermodynamic calculations. R.F. performed the far-infrared and mid-infrared measurements. K.C. conducted the first-principles phonon mode calculations. S.O. designed and coordinated this study, wrote the paper, contributed to all measurements and calculations. All authors commented on the manuscript.

### Corresponding authors

Correspondence to Hiroko Tokoro or Shin-ichi Ohkoshi.

## Ethics declarations

### Competing Interests

The authors declare that they have no competing interests.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

Reprints and Permissions

Tokoro, H., Namai, A., Yoshikiyo, M. et al. Theoretical prediction of a charge-transfer phase transition. Sci Rep 8, 63 (2018). https://doi.org/10.1038/s41598-017-18213-0

• Accepted:

• Published:

• ### Synthesis of nanosize tetratitanium heptoxide and its anomalous phase transition

• Hiroko Tokoro
• , Yusuke Araki
• , Iori Nagata
• , Takahiro Kondo
• , Kenta Imoto
•  & Shin-ichi Ohkoshi

Materials Research Letters (2020)

• ### Long-term heat-storage ceramics absorbing thermal energy from hot water

• Yoshitaka Nakamura
• , Yuki Sakai
• , Masaki Azuma
•  & Shin-ichi Ohkoshi

• ### Synthesis of Two-Dimensional Photomagnetic K4{[CuII(ida)]2[MIV(CN)8]}·4H2O (MIV = Mo, W) Materials

• Olaf Stefańczyk
•  & Shin-ichi Ohkoshi

Inorganic Chemistry (2020)

• ### Supramolecular copolymerization driven by integrative self-sorting of hydrogen-bonded rosettes

• Keisuke Aratsu
• , Rika Takeya
• , Brian R. Pauw
• , Martin J. Hollamby
• , Yuichi Kitamoto
• , Nobutaka Shimizu
• , Hideaki Takagi
• , Rie Haruki
•  & Shiki Yagai

Nature Communications (2020)

• ### Multi-colour uranyl emission efficiently tuned by hexacyanidometallates within hybrid coordination frameworks

• Szymon Chorazy
• , Jakub J. Zakrzewski
• , Mateusz Reczyński
•  & Barbara Sieklucka

Chemical Communications (2019)