All-Materials-Inclusive Flash Spark Plasma Sintering

Scientific Reportsvolume 7, Article number: 15071 (2017) | Download Citation

Abstract

A new flash (ultra-rapid) spark plasma sintering method applicable to various materials systems, regardless of their electrical resistivity, is developed. A number of powders ranging from metals to electrically insulative ceramics have been successfully densified resulting in homogeneous microstructures within sintering times of 8–35 s. A finite element simulation reveals that the developed method, providing an extraordinary fast and homogeneous heating concentrated in the sample’s volume and punches, is applicable to all the different samples tested. The utilized uniquely controllable flash phenomenon is enabled by the combination of the electric current concentration around the sample and the confinement of the heat generated in this area by the lateral thermal contact resistance. The presented new method allows: extending flash sintering to nearly all materials, controlling sample shape by an added graphite die, and an energy efficient mass production of small and intermediate size objects. This approach represents also a potential venue for future investigations of flash sintering of complex shapes.

Introduction

The quest for a stable sintering process able to gather high material performance, high energy efficiency and short operating time lends impetus to the discovery of new unconventional sintering techniques. The pressure assisted sintering techniques such as hot pressing or hot isostatic pressing enable 200–400 K lower processing temperatures than in conventional sintering and reductions of sintering time by few hours, which results in finer microstructures1,2,3. Significant improvements of sintering kinetics are also observed when the process is assisted by electric current4 or electromagnetic field5,6,7,8. These powder consolidation technologies are predominantly represented in the modern studies by the electric current activated/assisted sintering (ECAS) techniques9 which encompass resistive sintering (RS), where the sample is Joule heated by an externally applied voltage or AC/DC/pulsed electric current, and electrical discharge sintering (EDS), where high voltage electric discharge pulses are generated by a capacitor bank10. The spark plasma sintering (SPS) process is an ECAS technique that combines the benefits of highly pulsed electric current (1000–8000 A), high pressure (up to 100 MPa), high temperatures (up to 2400 °C), and high heating rates (up to 1,000 K/min)3,11,12,13. With these characteristics, a wide range of materials can be fully compacted, from the polymers to ultra-high temperature ceramics14, such as TaC15, ZrB2 16, etc. With more than 6,000 archival publications (as indicated by Web of Science®), the SPS process is now a well-established and stable technology allowing the fabrication of small and large size samples for sintering times between 5 and 60 min depending on the material and the targeted application17. Despite its advantages, the SPS technique is low productive because of its commonly utilized batch processing schematics. To improve its productivity two main approaches can be employed. One is based on the simultaneous sintering of multiple parts specimens3. The other solution, proposed in the present study, is the reduction of the sintering time to few seconds, combining SPS and flash sintering (FS) approaches.

Flash sintering is an energy efficient sintering process involving very short sintering times between 1 and 60 s18. The first flash sintering phenomenon has been discovered during the field assisted sintering studies of yttria stabilized zirconia19. The heating of zirconia under applied electric potential indicates the existence of the two main process stages. During the first incubation stage (which follows the preliminary stage of the external heating of the powder specimen by a conventional sintering furnace), the specimen is self-heated (in addition to the external heating) by an increasing amount of electric current passing through it. At an onset temperature related to the material resistivity behavior with temperature, the specimen becomes sufficiently conductive to allow a high electric current passage, and during this second stage a significant acceleration of the specimen’s heating is accompanied by a very fast sintering in few seconds. This thermal runaway profile20,21,22 enables heating rates of the order of 500–10,000 K/min and sintering times of few seconds23,24. This fast-resistive sintering method is easily applicable to many materials exhibiting a negative temperature coefficient (NTC) behavior of their electric resistivity like zirconia25, silicon carbide26, most of the thermistor materials like oxide spinel27, perovskites28, alumina (with MgO doping29 or special electric field conditions30) and other materials31,32.

The flash sintering may involve the following mechanisms. Joule heating24,33 generates fast sample heating rates which may result in a thermal runaway34 leading to accelerated sintering35 as in experiments reported in ref.36. The grain boundary melting or softening have been reported for microwave flash sintering37 or for a traditional flash sintering process38,39. The nucleation of defects40,41,42, local overheating of the grain boundaries19 or the acceleration of sintering resulting from the dielectric breakdown when high electric fields are employed43 are also possible mechanisms of flash sintering.

Similar FS approaches based on the microwave sintering, EDS, and SPS have been developed. The microwave sintering naturally demonstrates a tendency for high thermal44 and sintering37 runaway of ceramics that also stems from the NTC behavior of the specimens and/or tooling materials45. The EDS techniques use discharge times of the order of hundreds of microseconds and thus can be categorized as ultrafast sintering methods which are predominantly applied to conductive powders10. A similar ultrafast and contactless sintering method with discharge time between 2–10 s using plasma electrode46 resulted in a nearly full densification of carbides (SiC, B4C). A promising approach utilizing SPS in the sinter-forging configuration with graphite felt preheating element to initiate the flash phenomenon allowed the full densification of zirconia47 and of high temperature materials such as SiC48 or ZrB2 49 in about 10–20 s. A similar flash spark plasma sintering process can be achieved starting directly from a cold pressed powder with the noticeable improvement of the sample homogeneity50. An even faster approach using the sinter-forging SPS configuration51 and SPS sacrificial tooling components succeeded to compact a powdered SiC sample in about 1 s.

Despite a strong potential, numerous technological issues of FS remain unsolved. The intrinsic instabilities responsible for the thermal runaway also generate local hot spots phenomena resulting in non-homogeneous microstructure developments44,52,53. FS employs dog bone shape specimens with platinum electrodes which reduces the commercial attractiveness of the method. Another issue is the increase of the overall operating time due to the preheating needed to activate the electric conductivity which is too low at room temperature for most of the NTC systems. But the greatest limitation of all the FS approaches is the lack of the applicability of FS to a wide range of materials. Contrary to NTC materials, metals and alloys have a very high conductivity that decreases with temperature preventing the appearance of a natural “intrinsic” thermal runaway under a constant applied voltage. In contrast, a high electric insulator, such as high purity alumina or boron nitride, does not allow the electric current to activate the Joule heating phenomena. A recent flash sintering review54 estimates the fractions of FS sintering papers of 50% published on zirconia, 37% on NTC materials and only 10% and 3% on highly insulative and conductive materials, respectively.

In this work, the applicability of the net shape flash spark plasma sintering (NSFSPS) technique to a wide range of materials from metals to electric insulators is presented. Contrary to the previously used sinter-forging flash SPS method49,51, the NSFSPS approach uses a graphite die electrically insulated by a sprayed boron nitride layer55 to concentrate the electric current into the sample, if electrically conductive, or in the nearby graphite foil, if electrically insulative. The graphite die allows an easy control of the final shape of the specimen and makes the overall pressure assisted process more stable. The NSFSPS approach uses graphite tools for high temperature applications and good thermal shock resistance. This method is related to the electric current concentration approaches introduced by Zapata-Solvas et al.56 for ceramic powders (ZrB2, MoSi2, Al2O3) in flash conditions and by Román-Manso et al.57 for the densification of SiC. However, in contrast with the above-mentioned techniques, the different current patterns employed in this paper demonstrate that an unordinary thermal runaway can be instigated by the electric current assistance for all kinds of the tested materials. The present study includes a numerical simulation to determine the efficiency of the flash heating phenomena for the different materials tested. This study demonstrates the possibility of a flash, homogeneous, energy efficient and near net shape sample sintering applicable to every material regardless of its electric conductivity.

Results

The current and displacement curves obtained for the Ni, 3Y-ZrO2, and Al2O3 samples under “constant current mode” and fast electric current ramping conditions (see “forced mode” in section Methods) are reported in Fig. 1. For each of the displacement curves, the pre-sintering heating generates a thermal dilatation of all the powder volumes responsible for a small negative displacement (indicated by the blue to red arrows). The densification stage (indicated by gray arrows) results in a positive displacement of about 1 mm with duration between 8 and 35 s. In both the “constant current mode” and the “forced mode”, the sintering time is smaller than 60 s thereby falling under the flash sintering category54. When the displacement plateau appears, the electric current decreases down to zero, and the cooling stage starts. During the cooling stage, a thermal contraction of the whole NSFSPS setup is characterized by a positive displacement (red to blue arrows). The SEM images of the center and the edge and at half the height of all the samples are shown in Fig. 2. The final relative density and average grain size obtained for all the experiments are given in Table 1. Each sample is nearly dense with a residual porosity between 1 and 3% for the ceramics and 5% for nickel powder. For zirconia and alumina, the grain size increased form an initial 37–100 nm range to about 20 µm in roughly 10 s. This suggests that the fast densification is accompanied by unusually fast grain growth kinetics. The comparison of the transgranular and fractured areas indicates that the residual porosity is present both at the grain boundary and inside the grain volume. The intragranular porosity is particularly pronounced in the metal sample. The comparison of the center/edge SEM images reveals no obvious microstructural differences indicating a very homogeneous process. Nevertheless, a noticeable microstructure difference is observed between the “constant current mode” and the “forced mode” for zirconia. The zirconia sample, that becomes electrically conductive at high temperature, seems to generate some heating instabilities (internal sample temperature runaway and overheating in the sample’s area) which cause high grain growth under the “constant current mode” despite both experiments were stopped when the densification reached the plateau. In comparison, the alumina sample, that possesses a low electrical conductivity at low and high temperatures, exhibits nearly no microstructure differences between the two modes. This suggests that the thermal runaway of zirconia enabling the resistive flash sintering process is a source of the unstable grain growth58 under NSFSPS conditions in contrast with alumina or nickel whose average grain size is nearly unchanged. The non-NTC materials, which are normally impossible to flash sinter using conventional flash methods, appear to be the most stable materials using the NSFSPS method.

Figure 1
Figure 1

Experimental electric current (a,c) and displacement (b,d) curves under constant current mode (a,b) and forced mode (c,d).

Figure 2
Figure 2

SEM images in the centers and edges of nickel, zirconia and alumina samples for constant and forced current modes.

Table 1 Average grain size and relative density and their standard deviation for all the samples.

The NSFSPS configuration seems to allow a universal fast densification of every material no matter what the material conductivity is. To understand the Joule heating behavior during NSFSPS for each of the different materials employed, a finite element simulation study has been carried out. The materials properties and boundary conditions are described in ref.59. The electric and thermal contact resistances (ECR and TCR) on each interface of the NSFSPS setup are very important parameters influencing the overall temperature distribution60,61,62,63,64. Both ECR and TCR are decreased with pressure and temperature and evolve differently depending on the location of the interface and the type of the contact inside the NSFSPS setup65,66. The complete determination of each ECR and TCR has been conducted in ref.67, those data are used in the present simulations. The temperature, electric current density field, and electric current isolines are reported in Fig. 3 for each material at the end of the sintering. For nickel powder, the current isolines are concentrated all inside the central column including the sample where the higher temperature is located also in the center. For alumina powder, all the current lines are concentrated in the graphite foil avoiding the electrically insulative sample where the higher temperatures are located at the edge. The electric current distribution is similar for the zirconia powder sample with a small portion of the current that goes through the sample, which becomes conductive at high temperatures but with the values of the electric conductivity still far below the electric conductivity of graphite (103 S/m for zirconia and 1.1E5 S/m for graphite at 1300 °C). The zirconia sample starts the self-heating at high temperatures which balances the sample temperature distribution. The TCR, that decreases the heat flowing into the lateral punch/die interface, is the main factor explaining the high temperature concentration inside the NSFSPS setup’s central column independently of the sample material nature. The heat generated by the central column is then more easily contained in the sample, which helps the gradients’ reduction. The higher the TCR is, the more homogeneous are the sample temperatures and, consequently, the more homogeneous are the respective microstructures. The temperature difference between the sample center and the edge is 140 K for nickel, 93 K for zirconia, and 138 K for alumina, which are the reasonable differences considering the high sample heating rates which can reach 10,000 K/min. It should be noted that the BN coating and bigger punch/die gap can drastically increase the lateral TCR and provide an even higher thermal confinement than the one predicted by the model. As suggested by the homogeneity of the observed microstructures, the real TCR should lead to even more optimistic temperature profiles. The thermal confinement and the short sintering time are favorable conditions to ensure the microstructure homogeneity observed experimentally. The thermal confinement results also from the lateral graphite foil heating. For ceramics sintering cases, a significant amount of the electric current is constrained in the sample/die graphite foil (see Fig. 3b,c), therefore the amount of the thermal energy dissipated in graphite foil is high. Under these conditions, the lateral graphite foil can be compared to a susceptor that heats the sample from the edge and considerably stabilizes the sample temperature homogeneity. Concerning the nickel sintering case, the electric current concentration in the lateral graphite foil does not happen because the sample is highly conductive (see the electric current isolines in Fig. 3a). Thus, the nickel sample does not have this lateral heating and is cooled from the edge leading to a temperature difference of 140 K, which is more intense than the temperature difference in ceramics considering the lower sintering temperatures of metals. The forced thermal runaway generates the sample heating rates of 1700 K/min for nickel and 4300 K/min for alumina. For zirconia, a transition regime occurs at the sample onset temperature of 1250 °C where the heating rate passes from 3400 K/min to 12000 K/min. This transition stems from the NTC properties of zirconia generating an intrinsic thermal runaway that is added on top of the imposed electric current amplification. This result explains the difference in the average grain sizes obtained for the two modes in the case of zirconia NSFSPS. This zirconia intrinsic runaway may dramatically influence the grain growth and needs to be controlled by shutting down the process cycle immediately after the full densification of the sample is achieved.

Figure 3
Figure 3

Simulated temperature, electric current density field, and electric current for nickel, zirconia, and alumina samples.

To conclude, the extraordinary possibility to homogeneously flash sinter various kinds of materials, no matter what their electrical conductivity is, with a near net shape capability, has been demonstrated experimentally and theoretically. The applicability of a homogeneous flash heating to any material originates from the two main factors. The first factor is the concentration of the electric current inside the powder sample and its adjacent area. The second factor is the confinement of the heat generated in the sample area by the lateral thermal contact resistance that heightens the sample heating rate and helps homogenize the specimen’s temperature spatial distribution. It has been shown that, imposing a variable current pattern, equivalent thermal runaways for metals and insulative samples are easily achievable. The zirconia sample demonstrates a high sensibility to the grain growth at the end of the processing cycle due to the intrinsic thermal runaway phenomenon whose onset temperature is around 1250 °C in NSFSPS configuration. Nearly fully dense specimens with homogeneous grain sizes have been obtained using the developed NSFSPS technique.

The new NSFSPS method represents an efficient way for the mass production of small objects with optimal production time and high material performance. The fabrication of large size objects is possible too but will require a specific design of the electric current path in the NSFSPS tooling to balance the amplified thermal gradients. Thus, contrary to the regular flash sintering approaches, the presence of the graphite die opens the prospect of the one-step production of complex shapes similarly to conventional powder metallurgy approaches.

Methods

Materials and preparation

All the experiments were performed using a Spark Plasma Sintering machine (SPSS DR.SINTER Fuji Electronics model 5015). The NSFSPS configuration is reported in Fig. 4. The main difference of the traditional SPS and NSFSPS configurations is in the inner die interfaces (punch/die and sample/die). In the traditional SPS configuration, a 0.15 mm thick graphite foil is inserted in the vicinity of the punch/die interface (0.2 mm gap). For the NSFSPS configuration two graphite foils are inserted in a 0.4 mm punch/die gap. In order to concentrate the electric current on the sample area, the inner die surface is coated by an electrically insulative boron nitride (BN) spray. The sample can then be hybrid-heated both internally and/or by the nearby graphite foil. Three different powders with different electric conductivities have been selected to test the NSFSPS method. A pure nickel powder (Cerac, Ni 99.9% pure, 5 µm) was selected to represent metals, Al2O3 (Cerac, Al2O3 99.99% pure, 37 nm) to represent electrically insulative materials, and 3Y-ZrO2 (Tosoh- zirconia TZ- 3YS, 100 nm) - as an intermediate electric conductivity material with an NTC behavior. The amount of each used powder introduced has been calculated aiming to obtain 2 mm dense pellets.

Figure 4
Figure 4

Net shape flash spark plasma sintering configuration, the lateral graphite foil is coated with a boron nitride spray to electrically insulate the die and concentrate the electric current on the sample.


Configuration and current patterns

The current cycle has been imposed manually in two patterns. A constant pressure of 90 MPa was applied from the start until the end of each experiment. For the ceramics powders, a constant applied current (named “the constant current mode”) has been imposed in order to reveal a potential intrinsic thermal runaway during the ceramic sample heating. For the nickel powder, a material without NTC behavior, an electric current cycle with a forced runaway was employed. The electric current was manually increased at 70 A/min up to the beginning of the densification, then the current was quickly increased at about 2500 A/min up to reaching the displacement plateau indicating the end of the densification. We named this electric current pattern “the forced mode” and it was applied also to all the three considered materials. The “forced mode” is a very flexible solution that allows an easy regulation of the electric current value so that the sintering happens under control of the overheating and melting problems with the possibility of stopping the experiment when sintering is finished.


Main differences compared to the traditional flash sintering

The first difference is the applied pressure that accelerates and stabilizes the overall sintering process. A die is employed for a better control of the final sample shape (here - cylindrical). For nickel and alumina, the thermal runaway that appears in traditional flash sintering approaches (for NTC materials) is artificially imposed (being not “intrinsic”) by an electric current pattern (in the forced mode) that reproduces a similar sample’s thermal response corresponding to the material’s electric conductivity.


Data availability

The authors declare that the data supporting the findings of this study are available from the corresponding author upon a reasonable request.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  1. 1.

    German, R. M. Sintering Theory and Practice (Wiley, 1996).

  2. 2.

    Thomas, A. G. & Jones, H. J. Hot pressing of ceramic powders. Powder Metall. 3, 160–169 (1960).

  3. 3.

    Guillon, O. et al. Field-Assisted Sintering Technology/Spark Plasma Sintering: Mechanisms, Materials, and Technology Developments. Adv. Eng. Mater. 16, 830–849 (2014).

  4. 4.

    Kelly, J. P. & Graeve, O. A. Spark Plasma Sintering as an Approach to Manufacture Bulk Materials: Feasibility and Cost Savings. JOM 67, 29–33 (2015).

  5. 5.

    Wroe, R. & Rowley, A. T. Evidence for a non-thermal microwave effect in the sintering of partially stabilized zirconia. J. Mater. Sci. 31, 2019–2026 (1996).

  6. 6.

    Brosnan, K. H., Messing, G. L. & Agrawal, D. K. Microwave Sintering of Alumina at 2.45 GHz. J. Am. Ceram. Soc. 86, 1307–1312 (2003).

  7. 7.

    Charmond, S., Carry, C. P. & Bouvard, D. Densification and microstructure evolution of Y-Tetragonal Zirconia Polycrystal powder during direct and hybrid microwave sintering in a single-mode cavity. J. Eur. Ceram. Soc. 30, 1211–1221 (2010).

  8. 8.

    Rybakov, K. I., Olevsky, E. A. & Krikun, E. V. Microwave Sintering: Fundamentals and Modeling. J. Am. Ceram. Soc. 96, 1003–1020 (2013).

  9. 9.

    Grasso, S., Sakka, Y. & Maizza, G. Electric current activated/assisted sintering (ECAS): a review of patents 1906–2008. Sci. Technol. Adv. Mater. 10, 53001 (2009).

  10. 10.

    Lee, G. et al. Densification of zirconium nitride by spark plasma sintering and high voltage electric discharge consolidation: A comparative analysis. Ceram. Int. 41, 14973–14987 (2015).

  11. 11.

    Munir, Z. A., Anselmi-Tamburini, U. & Ohyanagi, M. The effect of electric field and pressure on the synthesis and consolidation of materials: A review of the spark plasma sintering method. J. Mater. Sci. 41, 763–777 (2006).

  12. 12.

    Orrù, R., Licheri, R., Locci, A. M., Cincotti, A. & Cao, G. Consolidation/synthesis of materials by electric current activated/assisted sintering. Mater. Sci. Eng. R Reports 63, 127–287 (2009).

  13. 13.

    Risbud, S. H. & Han, Y.-H. Preface and historical perspective on spark plasma sintering. Scr. Mater. 69, 105–106 (2013).

  14. 14.

    Orrù, R. & Cao, G. Comparison of Reactive and Non-Reactive Spark Plasma Sintering Routes for the Fabrication of Monolithic and Composite Ultra High Temperature Ceramics (UHTC) Materials. Materials (Basel) 6, 1566–1583 (2013).

  15. 15.

    Kelly, J. P. & Graeve, O. A. Mechanisms of pore formation in high-temperature carbides: Case study of TaC prepared by spark plasma sintering. Acta Mater. 84, 472–483 (2015).

  16. 16.

    Guo, S.-Q. Densification of ZrB2-based composites and their mechanical and physical properties: A review. J. Eur. Ceram. Soc. 29, 995–1011 (2009).

  17. 17.

    Suarez, M. et al. In Sintering Applications 319–342, https://doi.org/10.5772/53706 (InTech, 2013)

  18. 18.

    Raj, R., Cologna, M., Prette, A. L. G. & Sglavo, V. Methods of flash sintering. (2013).

  19. 19.

    Cologna, M., Rashkova, B. & Raj, R. Flash Sintering of Nanograin Zirconia in <5 s at 850 °C. J. Am. Ceram. Soc. 93, 3556–3559 (2010).

  20. 20.

    Dong, Y. & Chen, I.-W. Thermal Runaway in Mold-Assisted Flash Sintering. J. Am. Ceram. Soc. 99, 2889–2894 (2016).

  21. 21.

    Du, Y., Stevenson, A. J., Vernat, D., Diaz, M. & Marinha, D. Estimating Joule heating and ionic conductivity during flash sintering of 8YSZ. J. Eur. Ceram. Soc. 36, 749–759 (2016).

  22. 22.

    Grasso, S. et al. Modeling of the temperature distribution of flash sintered zirconia. J. Ceram. Soc. Japan 119, 144–146 (2011).

  23. 23.

    Zapata-Solvas, E., Bonilla, S., Wilshaw, P. R. & Todd, R. I. Preliminary investigation of flash sintering of SiC. J. Eur. Ceram. Soc. 33, 2811–2816 (2013).

  24. 24.

    Todd, R. I., Zapata-Solvas, E., Bonilla, R. S., Sneddon, T. & Wilshaw, P. R. Electrical characteristics of flash sintering: thermal runaway of Joule heating. J. Eur. Ceram. Soc. 35, 1865–1877 (2015).

  25. 25.

    Yamamoto, O. Electrical conductivity of stabilized zirconia with ytterbia and scandia. Solid State Ionics 79, 137–142 (1995).

  26. 26.

    Racette, J. H. Intrinsic Electrical Conductivity in Silicon Carbide. Phys. Rev. 107, 1542–1544 (1957).

  27. 27.

    Prette, A. L. G., Cologna, M., Sglavo, V. & Raj, R. Flash-sintering of Co2MnO4 spinel for solid oxide fuel cell applications. J. Power Sources 196, 2061–2065 (2011).

  28. 28.

    Rousset, A. et al. Electrical Properties of Mn 3– x Co x O 4 (0 ≤ x ≤ 3) Ceramics: An Interesting System for Negative Temperature Coefficient Thermistors. Int. J. Appl. Ceram. Technol. 10, 175–185 (2013).

  29. 29.

    Cologna, M., Francis, J. S. C. & Raj, R. Field assisted and flash sintering of alumina and its relationship to conductivity and MgO-doping. J. Eur. Ceram. Soc. 31, 2827–2837 (2011).

  30. 30.

    Biesuz, M. & Sglavo, V. M. Flash sintering of alumina: Effect of different operating conditions on densification. J. Eur. Ceram. Soc. 36, 2535–2542 (2016).

  31. 31.

    Muccillo, R., Muccillo, E. N. S. & Kleitz, M. Densification and enhancement of the grain boundary conductivity of gadolinium-doped barium cerate by ultra fast flash grain welding. J. Eur. Ceram. Soc. 32, 2311–2316 (2012).

  32. 32.

    McLaren, C., Heffner, W., Tessarollo, R., Raj, R. & Jain, H. Electric field-induced softening of alkali silicate glasses. Appl. Phys. Lett. 107, 184101 (2015).

  33. 33.

    Biesuz, M., Luchi, P., Quaranta, A., Martucci, A. & Sglavo, V. M. Photoemission during flash sintering: An interpretation based on thermal radiation. J. Eur. Ceram. Soc. 37, 3125–3130 (2017).

  34. 34.

    Zhang, Y., Jung, J.-I. & Luo, J. Thermal runaway, flash sintering and asymmetrical microstructural development of ZnO and ZnO–Bi2O3 under direct currents. Acta Mater. 94, 87–100 (2015).

  35. 35.

    Olevsky, E. A., Kandukuri, S. & Froyen, L. Consolidation enhancement in spark-plasma sintering: Impact of high heating rates. J. Appl. Phys. 102, 114913 (2007).

  36. 36.

    Ji, W. et al. Ultra-fast firing: Effect of heating rate on sintering of 3YSZ, with and without an electric field. J. Eur. Ceram. Soc. 37, 2547–2551 (2017).

  37. 37.

    Bykov, Y. et al. On the Mechanism of Microwave Flash Sintering of Ceramics. Materials (Basel) 9, 684 (2016).

  38. 38.

    Chaim, R. Liquid Film Capillary Mechanism for Densification of Ceramic Powders during Flash Sintering. Materials (Basel) 9, 280 (2016).

  39. 39.

    Chaim, R. Particle Surface Softening as Universal Behaviour during Flash Sintering of Oxide Nano-Powders. Materials (Basel) 10, 179 (2017).

  40. 40.

    Naik, K. S., Sglavo, V. M. & Raj, R. Flash sintering as a nucleation phenomenon and a model thereof. J. Eur. Ceram. Soc. 34, 4063–4067 (2014).

  41. 41.

    Francis, J. S. C., Cologna, M., Montinaro, D. & Raj, R. Flash Sintering of Anode-Electrolyte Multilayers for SOFC Applications. J. Am. Ceram. Soc. 96, 1352–1354 (2013).

  42. 42.

    Raj, R., Cologna, M. & Francis, J. S. C. Influence of Externally Imposed and Internally Generated Electrical Fields on Grain Growth, Diffusional Creep, Sintering and Related Phenomena in Ceramics. J. Am. Ceram. Soc. 94, 1941–1965 (2011).

  43. 43.

    Biesuz, M., Luchi, P., Quaranta, A. & Sglavo, V. M. Theoretical and phenomenological analogies between flash sintering and dielectric breakdown in α-alumina. J. Appl. Phys. 120, 145107 (2016).

  44. 44.

    Manière, C., Zahrah, T. & Olevsky, E. A. Inherent heating instability of direct microwave sintering process: Sample analysis for porous 3Y-ZrO2. Scr. Mater. 128, 49–52 (2017).

  45. 45.

    Manière, C., Zahrah, T. & Olevsky, E. A. Fully coupled electromagnetic-thermal-mechanical comparative simulation of direct vs hybrid microwave sintering of 3Y-ZrO2. J. Am. Ceram. Soc. 100, 2439–2450 (2017).

  46. 46.

    Saunders, T., Grasso, S. & Reece, M. J. Ultrafast-Contactless Flash Sintering using Plasma Electrodes. Sci. Rep. 6, 27222 (2016).

  47. 47.

    Vasylkiv, O., Borodianska, H., Sakka, Y. & Demirskyi, D. Flash spark plasma sintering of ultrafine yttria-stabilized zirconia ceramics. Scr. Mater. 121, 32–36 (2016).

  48. 48.

    Grasso, S. et al. Flash Spark Plasma Sintering (FSPS) of α and β SiC. J. Am. Ceram. Soc. 99, 1534–1543 (2016).

  49. 49.

    Grasso, S. et al. Flash Spark Plasma Sintering (FSPS) of Pure ZrB2. J. Am. Ceram. Soc. 97, 2405–2408 (2014).

  50. 50.

    McKinnon, R., Grasso, S., Tudball, A. & Reece, M. J. Flash spark plasma sintering of cold-Pressed TiB 2 - h BN. J. Eur. Ceram. Soc. 37, 2787–2794 (2017).

  51. 51.

    Olevsky, E. A., Rolfing, S. M. & Maximenko, A. L. Flash (Ultra-Rapid) Spark-Plasma Sintering of Silicon Carbide. Sci. Rep. 6, 33408 (2016).

  52. 52.

    Qin, W., Majidi, H., Yun, J. & van Benthem, K. Electrode Effects on Microstructure Formation During FLASH Sintering of Yttrium-Stabilized Zirconia. J. Am. Ceram. Soc. 99, 2253–2259 (2016).

  53. 53.

    Steil, M. C., Marinha, D., Aman, Y., Gomes, J. R. C. & Kleitz, M. From conventional ac flash-sintering of YSZ to hyper-flash and double flash. J. Eur. Ceram. Soc. 33, 2093–2101 (2013).

  54. 54.

    Yu, M., Grasso, S., Mckinnon, R., Saunders, T. & Reece, M. J. Review of flash sintering: materials, mechanisms and modelling. Adv. Appl. Ceram. 116, 24–60 (2017).

  55. 55.

    Weintraub, G. & Rush, H. Process and apparatus for sintering refractory materials (1913).

  56. 56.

    Zapata-Solvas, E., Gómez-García, D., Domínguez-Rodríguez, A. & Todd, R. I. Ultra-fast and energy-efficient sintering of ceramics by electric current concentration. Sci. Rep. 5, 8513 (2015).

  57. 57.

    Román-Manso, B., Belmonte, M., Osendi, M. I. & Miranzo, P. Effects of Current Confinement on the Spark Plasma Sintering of Silicon Carbide Ceramics. J. Am. Ceram. Soc. 98, 2745–2753 (2015).

  58. 58.

    Qin, W., Yun, J., Thron, A. M. & van Benthem, K. Temperature gradient and microstructure evolution in AC flash sintering of 3 mol% yttria-stabilized zirconia. Mater. Manuf. Process. 32, 1–8 (2017).

  59. 59.

    Manière, C., Lee, G. & Olevsky, E. A. Proportional integral derivative, modeling and ways of stabilization for the spark plasma sintering process. Results Phys. 7, 1494–1497 (2017).

  60. 60.

    Zavaliangos, A., Zhang, J., Krammer, M. & Groza, J. R. Temperature evolution during field activated sintering. Mater. Sci. Eng. A 379, 218–228 (2004).

  61. 61.

    Vanmeensel, K., Laptev, A., Hennicke, J., Vleugels, J. & Vanderbiest, O. Modelling of the temperature distribution during field assisted sintering. Acta Mater. 53, 4379–4388 (2005).

  62. 62.

    Cincotti, A., Locci, A. M., Orrù, R. & Cao, G. Modeling of SPS apparatus: Temperature, current and strain distribution with no powders. AIChE J. 53, 703–719 (2007).

  63. 63.

    Wei, X., Giuntini, D., Maximenko, A. L., Haines, C. D. & Olevsky, E. A. Experimental Investigation of Electric Contact Resistance in Spark Plasma Sintering Tooling Setup. J. Am. Ceram. Soc. 98, 3553–3560 (2015).

  64. 64.

    Arnaud, C. et al. Dog-bone copper specimens prepared by one-step spark plasma sintering. J. Mater. Sci. 50, 7364–7373 (2015).

  65. 65.

    Maniere, C. et al. Pulse analysis and electric contact measurements in spark plasma sintering. Electr. Power Syst. Res. 127, 307–313 (2015).

  66. 66.

    Manière, C. et al. Finite-element modeling of the electro-thermal contacts in the spark plasma sintering process. J. Eur. Ceram. Soc. 36, 741–748 (2016).

  67. 67.

    Manière, C. et al. Contact resistances in spark plasma sintering: From in-situ and ex-situ determinations to an extended model for the scale up of the process. J. Eur. Ceram. Soc. 37, 1593–1605 (2017).

Download references

Acknowledgements

The support of the US Department of Energy, Materials Sciences Division, under Award No. DE-SC0008581 is gratefully acknowledged.

Author information

Affiliations

  1. Powder Technology Laboratory, San Diego State University, San Diego, USA

    • Charles Manière
    • , Geuntak Lee
    •  & Eugene A. Olevsky

Authors

  1. Search for Charles Manière in:

  2. Search for Geuntak Lee in:

  3. Search for Eugene A. Olevsky in:

Contributions

E.O. managed the overall project. C.M. and G.L. conducted the S.P.S. experiments. G.L conducted all the S.E.M. characterizations. C.M. performed the finite element simulations. C.M. wrote the paper with input from G.L. and E.O. E.O. refined the paper. All authors contributed to the interpretation of the results.

Competing Interests

The authors declare that they have no competing interests.

Corresponding author

Correspondence to Eugene A. Olevsky.

About this article

Publication history

Received

Accepted

Published

DOI

https://doi.org/10.1038/s41598-017-15365-x