Abstract
This article presents the high temperature tensile and creep behaviors of a novel high entropy alloy (HEA). The microstructure of this HEA resembles that of advanced superalloys with a high entropy FCC matrix and L12 ordered precipitates, so it is also named as “high entropy superalloy (HESA)”. The tensile yield strengths of HESA surpass those of the reported HEAs from room temperature to elevated temperatures; furthermore, its creep resistance at 982 °C can be compared to those of some Ni-based superalloys. Analysis on experimental results indicate that HESA could be strengthened by the low stacking-fault energy of the matrix, high anti-phase boundary energy of the strengthening precipitate, and thermally stable microstructure. Positive misfit between FCC matrix and precipitate has yielded parallel raft microstructure during creep at 982 °C, and the creep curves of HESA were dominated by tertiary creep behavior. To the best of authors’ knowledge, this article is the first to present the elevated temperature tensile creep study on full scale specimens of a high entropy alloy, and the potential of HESA for high temperature structural application is discussed.
Similar content being viewed by others
Introduction
The concept of high entropy alloys (HEAs) has allowed the exploration of large composition space of alloys, and is currently one of the most intriguing research topics in the field of materials science1,2,3. Recent studies have shown attractive mechanical properties of HEAs at cryogenic temperature4 and room temperature5 with excellent combinations of high strength and toughness, indicating their potential as the structural materials. However, the strength of single phase type HEAs were reported to be insufficient at elevated temperatures6. Several HEAs, such as CoCrFeNiNbx 7 and CoCrFeNiMox 8 demonstrated that a moderate increase in tensile strength can be achieved by various precipitates. As a result, precipitation strengthening should be considered in developing HEAs for high temperature applications. The physical metallurgy of superalloys9 have been employed to design HEAs by utilization of significant volume fractions of stable and coherent L12 γ′ to provide high temperature strength, e.g., Al10Co25Cr8Fe15Ni36Ti6 HEA was designed to contain 46 vol% of γ′ precipitates10, and its tensile strength could surpass those of Inconel 617 and Alloy 800 H. Nevertheless, the γ′ solvus temperatures of the reported γ′-bearing HEAs still remained relatively low comparing to those of superalloys9. Furthermore, there were phase instability associated with the formation of L21 Ni2AlTi, B2, and Cu-rich FCC5,11,12. Therefore, the development for precipitation strengthened HEAs is only at the incipient stage, and more research efforts will be required.
In present study, the high temperature tensile and creep behaviors of a novel alloy named high entropy superalloy (HESA)13 have been investigated. HESA is strengthened by the coherent L12 γ′ precipitates, while the FCC matrix remains high entropy (ΔSmix > 1.5 R)14. For example, the composition of HESA in current study is Ni47.9Al10.2Co16.9Cr7.4Fe8.9Ti5.8Mo0.9Nb1.2W0.4C0.4 (at%), so the calculated ΔSmix is 1.60 R, which is higher than those of conventional superalloys such as CM247LC (ΔSmix = 1.29 R), Rene′ N5 (ΔSmix = 1.22 R), and CMSX-2 (ΔSmix = 1.14 R). Previous studies have shown that the γ - γ′ microstructure of HESAs can remain stable against topologically-close-packed (TCP) phase formation from 700 to 1100 °C for at least 500 h15, and with enhanced γ′ solvus temperatures above 1150 °C16. Furthermore, HESAs have shown good resistances against high temperature oxidation and corrosion by forming protective Al2O3 and Cr2O3, respectively17. However, the tensile and creep behaviors of HESA have not yet been reported. Therefore, these two properties are the main subject of focus in this article. To the best of authors’ knowledge, there is no reported creep studies on the full scale sample of HEAs at elevated temperature such as 982 °C. Although some studies utilized nano-indentation method to deduce creep mechanism of HEA18,19, these tests could not take the effect of long-term microstructure stability on creep into consideration. Therefore, this article presents the first tensile creep studies on full size specimen of a high entropy alloy, which can benefit the community of materials science and engineering whose interest is in the development of HEAs for elevated temperature applications.
Results
Figure 1(a) shows the SEM back-scattered electron image of the as-cast HESA, which consists of dendritic microstructure with some carbides. The morphology of carbide is shown in Fig. 1(b), and the average chemical composition measured by SEM-EDS suggests that these are (Nb, Ti)-rich MC carbides, Table 1. After the solution and aging heat-treatments, the microstructure consists of γ matrix and dispersed γ′ precipitates is shown in Fig. 2(a). The γ′ precipitates appears to be spherical with an average size of 290 nm and 69 vol% measured by image analysis. Figure 2(b) shows the XRD scan at room temperature, and the characteristic peaks confirm the FCC + L12 phases of HESA. The DTA curve during heating is shown in Fig. 2(c). It also indicates the two phases microstructure, and the γ′ solvus and solidus temperature are 1199 and 1276 °C, respectively. In addition, deconvolution of {200} reflection of XRD scan at 982 °C allows the measurement of lattice misfit at high temperature, Fig. 2(d); peak intensity ratio between γ and γ′ can be correlated with their relative volume fractions for determining lattice constants of γ and γ′ to be 3.625 and 3.628 Å, respectively. Therefore, by the calculation of \(\delta =2({a}_{{\rm{\gamma }}^{\prime} }-\,{a}_{\gamma })/({a}_{{\rm{\gamma }}^{\prime} }+{a}_{\gamma })\), where δ is the lattice misfit between γ and γ′, a γ and \({a}_{{\gamma }^{^{\prime} }}\) is the lattice constant of γ and γ′ phase, respectively, the lattice misfit of HESA at 982 °C is 0.08%.
The chemical composition of γ and γ′ phase has been determined by strain-aging method20 in this study. Figure 3(a) shows the cellular microstructure of γ and γ′ phase after strain-aging, and the average compositions of individual γ and γ′ measured by SEM-EDS are summarized in Table 1 along with those of a conventional superalloy CMSX-2 reported in literature21, which contains an average 68 vol% of cuboidal shape γ′ precipitates. By utilizing the chemical compositions, Fig. 3(b) can be plotted with \({{\rm{C}}}_{\gamma {\rm{^{\prime} }}}\) - Cγ vs. Cm - Cγ, where Cm is the nominal composition, \({{\rm{C}}}_{\gamma {\rm{^{\prime} }}}\) is the γ′ composition, and Cγ is the γ composition. The linear fitting slope in Fig. 3(b) is 0.62, which is close to the γ′ volume fractions measured experimentally, so the validity of the measured γ and γ′ compositions has been demonstrated. According to Table 1, there are relatively high Co and Ti concentrations in both γ and γ′ phases of HESA. Since Co and Ti additions can reduce the stacking fault energy (SFE) of a Ni matrix22, lower SFE of γ matrix in HESA can be expected, as the generally reported low SFEs of HEAs23,24. A functional model has been utilized to estimate the SFE of HESA25. The fractional change of γ SFE due to alloying can be described as: \({{\rm{\Delta }}}_{\Gamma }^{\gamma }(x)=\sum _{i}{x}_{i}\delta {\Gamma }_{i}\), where Γ is the stacking fault energy and \(\delta {\Gamma }_{i}\) is the optimized model parameter value for the effect of alloying element on SFE of pure Ni, Table 2 25. By applying the γ compositions in Table 1 into the above model, the value of \({{\rm{\Delta }}}_{\Gamma }^{\gamma }(x)\) are −1.0 and −0.67 for HESA and CMSX-2, respectively, indicating that the reduction of SFE in the Ni-based FCC matrix due to alloying in HESA can be 1.5 times greater than that of CMSX-2. According to references, the SFE of pure Ni is 1.3 J/m2 and that of CMSX-2 is 0.9 J/m2 26, so the reduction of SFE due to alloying for CMSX-2 is 0.4 J/m2, while that for HESA should be 0.6 J/m2. Therefore, the SFE of the HEA matrix can be estimated around 0.7 J/m2. Furthermore, high Ti content in γ′ phase can significantly increase the anti-phase boundary (APB) energy27. According to JMatPro calculations, the APB energies of γ′ phase in HESA and CMSX-2 are 0.22 and 0.19 J/m2, respectively. Consequently, higher APB energy of γ′ may contribute to some degree of strengthening in HESA28.
The tensile yield strength versus temperature plot of HESA comparing to those of the commercial Ni-based superalloys29,30,31 and reported high entropy alloys10,32,33,34 are shown in Fig. 4. The precipitation strengthening has allowed HESA to possess higher tensile yield strengths than those of CoCrFeMnNi throughout the temperatures. Furthermore, the tensile yield strengths of HESA are the highest among reported high entropy alloys. Although the strengths of HESA are lower than those of CMSX-4 and CMSX-10, its behavior above 800 °C can be close to those of CMSX-2.
Creep behaviors of HESA at 982, 850 and 750 °C under 159 MPa are shown in Fig. 5a,b,c. The creep rupture life of HESA at 982 °C is about 114 h, which is similar to those of several first-generation Ni-based superalloys under similar test conditions, e.g., the creep life of NX-188 DS under 982 °C/138 MPa test is 58 h35, and that of Rene′ 80 under 982 °C/145 MPa test is 118 h36. The 982 °C creep curve of HESA is clearly shown in Fig. 5(b), and there is no obvious primary creep with gradual increase in creep strain rate corresponding to an extensive tertiary creep behavior. Figure 5(c) enlarges the creep strain axis of 750 and 850 °C creep curves, and there are still no obvious primary creep regime. After 800 h interrupted tests, the creep strains only have accumulated to 0.04% and 0.25% at 750 °C and 850 °C, respectively. The creep strain rates versus strain curves are shown in Fig. 5(d), and by plotting the minimum creep strain rate versus T−1, where T is the temperature, the dependence of creep strain rate on the testing temperature can be shown in Fig. 6; the creep strain rates of CMSX-2 under 200 MPa load are also included in this figure (5.6 × 10−8 sec−1 at 875 °C and 2.6 × 10−7 sec−1 at 948 °C37). Dependence of the steady-state creep rate (\(\dot{{\rm{\varepsilon }}}\)) on the applied stress (σ) and temperature (T) can be expressed as: \(\dot{\varepsilon }={\rm{A}}{\sigma }^{n}\exp (-{\rm{Q}}/{\rm{RT}})\), where A is a constant, Q is the activation energy for creep and R is the gas constant9, thus the activation energy for creep (Q) can be further described as: \({\rm{Q}}=-{\rm{R}}(-\partial \,\mathrm{ln}\,\dot{\varepsilon }/\partial {T}^{-1})\) under constant loads. From the linear slope of \(\mathrm{ln}\,\dot{{\rm{\varepsilon }}}\) vs. T−1 curve, the creep activation energy of HESA can be estimated to be 290 kJ/mol, while that of CMSX-2 is 230 kJ/mol37.
Figure 7(a) shows the side view of the 982 °C crept rupture specimen of HESA. The diameter of the fractured gauge region has decreased from the original 6.35 mm to 4.75 mm, which demonstrates a ductile necking behavior before fracture. In addition, it appears to be no severe stress concentration occurred during creep deformation. The transverse fractograph are shown in Fig. 7b,c. According to Fig. 7(b), the fracture surface is rough and with the majority dimple feature corresponding to ductile behaviour; however, minor brittle fracture regions reflected by facet-like morphology can be observed associated with the presence of carbides, Fig. 7(c). Microstructure evolution during high temperature creep is known to influence creep behaviour, such as the directional coarsening of γ′ precipitates – “rafting”38. The plate-like γ′ morphology of the 982 °C crept HESA is shown in Fig. 8(a). The average diameter of γ′ perpendicular to the stress axis has coarsened from 0.29 μm to 0.5 μm, while the average length in parallel direction extended to 3 μm. Therefore, the rafting of γ′ in HESA has shown to coarsen along the direction of the applied stress, which can be related to the positive lattice misfit (δ) between γ and γ′39. Figure 8(b) shows the TEM analysis of crept HESA at 982 °C; dislocations have mainly piled-up within the γ matrix with no shearing the γ′ phase. Figure 9a,b show the microstructures of HESA after 800 h interrupted creep at 750 and 850 °C. The microstructure can be stable with high entropy γ matrix and L12 γ′, while the size of γ′ has increased from 0.3 μm to 0.4 and 0.6 μm after 750 and 850 °C creep tests, respectively. Moreover, the morphology of γ′ has remained spherical, indicating that no rafting of γ′ has occurred in both conditions. These stable γ′ morphologies can be beneficial to resist creep deformation, and further discussions is presented in the next section.
Discussion
The high temperature tensile and creep properties of a precipitation strengthened high entropy alloy, i.e., high entropy superalloy (HESA) have been investigated. Comparing to those of the reported high entropy alloys, HESA possesses outstanding tensile yield strength from ambient to elevated temperatures. Furthermore, the creep rupture life of HESA at 982 °C can be compared to those of Ni-based superalloys such as RENE′ 80 and NX-188 DS, so the potential of HESA for high temperature applications is demonstrated in this article.
The tensile strength of HESA can be attributed to the high volume fraction of strengthening precipitates γ′, while previous HEAs like Al10Co25Cr8Fe15Ni36Ti6 contains only 46 vol% of γ′ at room temperature10. As compared with the tensile yield strength of CMSX-2, the underlying reason of the slightly lower tensile yield strength can be elucidated by the following section. According to strong-pair and weak-pair coupling theories40,41, the critical resolved shear stress (τc) of the precipitation strengthened alloys can be determined by the factors of APB energy, volume fraction of γ′ and γ′ size as: \({\tau }_{c}=\frac{{\gamma }_{APB}}{2b}[{(\frac{6{\gamma }_{APB}fr}{\pi T})}^{1/2}-f]\) and \({\tau }_{c}=\sqrt{\frac{3}{2}}(\frac{Gb}{r})\,{f}^{1/2}\frac{w}{{\pi }^{3/2}}{(\frac{2\pi {\gamma }_{APB}r}{wG{b}^{2}}-1)}^{1/2}\), where γ APB is the APB energy, f is the volume fraction of γ′, r is the γ′ radius, T is the line tension, G is the shear modulus, b is the Burgers vector and w is a dimensionless constant. Since these theories have indicated that the peak strength would be yielded as the r increases to around \(\frac{2T}{{\gamma }_{APB}}\) 9, and with the similar volume fraction of γ′ between HESA (69 vol%) and CMSX-2 (68 vol%), the optimized size of γ′ for peak strength in HESA can be estimated from that of CMSX-2. According to JMatPro calculations, the APB energy of HESA and CMSX-2 is 0.22 and 0.19 J/m2, respectively. In addition, due to the tensile strength of CMSX-2 has been reported to be significantly improved with an increase in average γ′ size from 300 nm to 450 nm42, and with the inversely proportional relationship to APB energy, the optimized size of γ′ in HESA should be around 390 nm; however, the as heat-treated γ′ size is only 290 nm in this work. As the τc is proportional to r1/2, the strength of HESA may increase by 16% when its γ′ size increases from 290 to 390 nm, which would contribute to the room temperature tensile yield strength increment from 840 MPa to 960 MPa. Furthermore, by comparing the increase in tensile yield strength from room temperature to the peak strength (Δσy) of CMSX-2 (960 to 1150 MPa) and HESA (840 to 855 MPa), the magnitude of positive temperature dependence on yield strength of HESA appears to be less pronounced. For an alloy with coherent precipitates, the constrained lattice misfit (δ) can also affect the mechanical strength, i.e., higher degree of |δ| could lead to higher increase in yield strength due to the stress field around the precipitates interact with dislocations43,44. Since the δ of CMSX-2 was reported around −0.33%45, its higher degree of misfit value would contribute to the higher strength. From a designer point of view, the tensile yield strength of HESA appears to be very stable from room temperature to 800 °C, which could be more favorable than conventional superalloys for gas turbine engine application.
Regarding to creep behaviors, rafting can strongly affect the deformation at elevated temperatures. The coarsening of γ′ in CMSX-2 has been reported to be perpendicular to the stress axis (N-raft)37, so the N-rafted γ′ can provide interfaces with the formation of equilibrium interfacial dislocation network to hinder dislocation movements46. By contrast, the creep of HESA is dominated by parallel raft (P-raft) and without perpendicular γ/γ′ interfaces. Tetzlaff et al. have reported that tertiary creep may dominate the creep response of P-rafted superalloys47, and this is exactly the creep behavior observed for HESA at 982 °C. Therefore, higher creep rate of HESA compared to that of CMSX-2 could be a result of P-raft. According to a recent work on the thermal cycling creep of Ni-based superalloys, the P-raft of γ′ is proposed to be instead beneficial to the thermal cyclic creep resistance48. Consequently, the non-isothermal creep behavior of HESA may be worth studying in the future. On the other hand, HESA can exhibit the more comparable creep resistances to those of CMSX-2 at intermediate temperatures. According to the creep behaviors of HESA shown in Fig. 5, no obvious primary creep is observed, demonstrating that the dislocation shearing γ′ mechanism should not be applicable. Instead, thermally activated by-passing of dislocations around γ′ precipitates should be the deformation mechanism with such low applied stress;49,50 the inelastic deformation can essentially concentrate within the γ regions, where dislocations move by climb and glide processes to pass by γ′ particles51,52,53. Therefore, the possible sluggish diffusion of the higher entropy γ matrix and the un-rafted γ′ microstructure can contribute to lower creep rate. Furthermore, the lower stacking fault energy (SFE) of the γ matrix and higher activation energy of creep in HESA system would also be important strengthening factors. The correlation between SFE, creep activation energy and creep strain rate is described as: \(\dot{\varepsilon }=A{\rm{^{\prime} }}{({\gamma }_{SF}/Gb)}^{3}{(\sigma /G)}^{5}\exp (-{\rm{Q}}/{\rm{R}}{\rm{T}})\), where A′ is a constant, γ SF is the stacking fault energy, G is the shear modulus, b is the Burgers vector, Q is the activation energy of creep and σ is the applied stress29, so the lower SFE and higher Q of HESA can lead to lower creep rates. For materials possessing lower SFE, partial dislocations are more energetically favorable, and the spacing between partial dislocations can be increased. As a result, the dislocations bowing around γ′ particles would become more difficult, which effectively decreases the creep strain rate.
In summary, owing to higher volume fractions and higher APB energy of γ′ precipitates, HESA can show the superior tensile yield strength to those of the reported high entropy alloys from room to elevated temperatures. In addition, the high temperature strength of HESA can approach that of the Ni-based superalloy CMSX-2, and the optimizations in larger γ′ size, higher degree of misfit value may contribute to further strengthening. Regarding to creep resistances, HESA can be strengthened by the lower stacking fault energy, higher creep activation energy and stable γ′ phases; the sluggish diffusion of the high entropy γ matrix may have attributed to the higher creep activation energy. At higher temperature, although the P-raft γ′ at 982 °C has led to a more rapid increase in creep strain rate, the creep life of HESA can be compared to those of some conventional superalloys and with less refractory contents. Therefore, HESA can be a promising new type of high temperature alloy with improved cost-performance. For the future alloy designs, the minor addition of γ partitioning elements like Mo and Re would lead to the desirable negative lattice misfit for N-type rafting of γ′ and also provide solid-solution strengthening to the γ matrix54.
Methods
The nominal composition of the investigated HESA is listed in Table 1. The alloy is rich in Ni, Co, Fe with a mixing entropy of the alloy to 1.60 R, which can be categorized as a high entropy alloy14. The term of mixing entropy is calculated by: ΔSmix = −R(XAlnXA + XBlnXB + …), where R is the gas constant, XA means the molar fraction of constituent A in whole alloy, XB means the molar fraction of constituent B, and so on. Al, Ti and Nb are the γ′ forming elements for precipitation strengthening. Cr is added to provide oxidation and corrosion resistance. The slight carbon content is for grain-boundary pinning purpose, and minor amounts of Mo and W are added for solid-solution strengthening. The design of HESA was also assisted by CALPHAD-based simulation (JMatPro55, Ni-alloys database), and the aim is to contain more than 60 vol% of strengthening L12 γ′ as commercial Ni-based superalloys. Furthermore, since the addition of refractory elements can easily promote the formation of detrimental topological-close packed (TCP) phases, the fraction of TCP was designed to be less than 1 vol% while adjusting the refractory additions. The ingot of HESA was prepared by vacuum-arc-melting process followed by directional-solidification (DS) to produce columnar microstructure; the setup of DS casting furnace has been described in our previous work15. The solution-heat-treatment (SHT) was then conducted at 1210 °C for 10 h to homogenize chemical segregations, and followed by a primary aging at 1000 °C for 3 h and a secondary aging at 800 °C for 20 h to grow and refine the morphology of γ′ precipitates.
A Pyris Diamond TG/DTA was used to determine the γ′ solvus temperature of HESA; 30 mg sample was put in an Al2O3 crucible with a heating rate of 10 °C/min to 1350 °C and with 400 sccm of Ar flow. A scanning electron microscope (SEM, Hitachi SU-8010) equipped with energy dispersive X-ray spectrometer (EDS) and a transmission electron microscope (TEM, Tecnai F30) were used to observe the microstructures. TEM foils were prepared by a twin-jet polisher with a solution of 30 ml perchloric acid (HClO4) with 300 ml methanol (CH3OH) and 175 ml butanol (C4H9OH) at −10 °C. An X-ray diffractometer (Shimazu XRD-6000) with a heating stage and Cu-target radiation at 30 kV/20 mA was used to obtain the characteristic γ/γ′ peaks under a vacuum environment (1 × 10−4 atm). The XRD specimens were in a plate form with dimension of 1 cm х 1 cm х 3 mm, and scanned at 2θ angle from 20 to 100° by 2 degree/min at room temperature and 982 °C. MDI Jade software was used to deconvolute the {200} lattice reflection and determine the peak positions of γ and γ′ for calculating the lattice misfit (δ). A strain aging method was conducted to assist measuring the compositions of γ and γ′ phase; samples were subjected to indentation after the solution-heat-treatment process stated above, and then followed by an annealing at 900 °C for 50 h. Therefore, cellular growth of γ′ would occur20, and resulted in the coarsened γ/γ′ morphology. In addition, the measured compositions of γ and γ′ were verified with the lever rule analyses. The diagram of \({{\rm{C}}}_{\gamma {\rm{^{\prime} }}}\) - Cγ vs. Cm - Cγ would be plotted, where Cγ, \({{\rm{C}}}_{\gamma {\rm{^{\prime} }}}\) and Cm are the chemical compositions measured from γ, γ′ and bulk alloy, respectively; the linear fitting slope of \({{\rm{C}}}_{\gamma {\rm{^{\prime} }}}\) - Cγ vs. Cm - Cγ diagram should correlate with the volume fraction of γ′ phase.
Tensile tests were conducted by a MTS 810 testing machine; flat tensile specimens were prepared by electrical discharge machining. The total length of a specimen is 43 mm, while the gauge length, width, and thickness are 19 mm, 10 mm, and 1.5 mm, respectively. The specimens were tensile tested at a stain rate of 10−3 sec−1 from room temperature to 950 °C. Creep tests were performed at 750, 850 and 982 °C with a constant stress of 159 MPa using an ATS Series 2330 lever arm creep tester. The dimension of rod specimens was machined to a diameter of 6.35 mm with a gage length of 25.4 mm according to the Japanese Industrial Standard (JIS-Z-227156).
References
Yeh, J. W. et al. Nanostructured high-entropy alloys with multiple principal elements: Novel alloy design concepts and outcomes. Adv. Eng. Mater. 6, 299–303 (2004).
Lu, Y. P. et al. A Promising New Class of High-Temperature Alloys: Eutectic High-Entropy Alloys. Sci. Rep. 4, 6200 (2014).
Miracle, D. & O. Senkov, A. critical review of high entropy alloys and related concepts. Acta Mater. 122, 448–511 (2017).
Gludovatz, B. et al. A fracture-resistant high-entropy alloy for cryogenic applications. Science 345, 1153–1158 (2014).
He, J. Y. et al. A precipitation-hardened high-entropy alloy with outstanding tensile properties. Acta Mater. 102, 187–196 (2016).
Lu, Z. et al. An assessment on the future development of high-entropy alloys: summary from a recent workshop. Intermetallics 66, 67–76 (2015).
Liu, W. H. et al. Effects of Nb additions on the microstructure and mechanical property of CoCrFeNi high-entropy alloys. Intermetallics 60, 1–8 (2015).
Liu, W. H. et al. Ductile CoCrFeNiMox high entropy alloys strengthened by hard intermetallic phases. Acta Mater. 116, 332–342 (2016).
R. C. Reed The Superalloys: Fundamentals and Applications (Cambridge University Press, 2006).
Daoud, H., Manzoni, A., Wanderka, N. & Glatzel, U. High-Temperature Tensile Strength of Al10Co25Cr8Fe15Ni36Ti6 Compositionally Complex Alloy (High-Entropy Alloy). JOM 67, 2271–2277 (2015).
Gwalani, B. et al. Stability of ordered L12 and B2 precipitates in face centered cubic based high entropy alloys - Al0.3CoFeCrNi and Al0.3CuFeCrNi2. Scripta Mater. 123, 130–134 (2016).
Xu, X. D. et al. Nanoscale phase separation in a fcc-based CoCrCuFeNiAl0.5 high-entropy alloy. Acta Mater. 84, 145–152 (2015).
Yeh, A. C. et al. Developing new type of high temperature alloys – High Entropy Superalloys, Int. J. Met. Mater. Eng. 1 (2015).
Yeh, J. W. Alloy Design Strategies and Future Trends in High-Entropy Alloys. JOM 65, 1759–1771 (2013).
Tsao, T. K., Yeh, A. C., Kuo, C. M. & Murakami, H. On The Superior High Temperature Hardness of Precipitation Strengthened High Entropy Ni‐Based Alloys. Adv. Eng. Mater. 19, 1600475 (2017).
Tsao, T. K., Yeh, A. C. & Murakami, H. The Microstructure Stability of Precipitation Strengthened Medium to High Entropy Superalloys. Metall. Mater. Trans. A 48, 2435–2442 (2017).
Tsao, T. K., Yeh, A. C., Kuo, C. M. & Murakami, H. High Temperature Oxidation and Corrosion Properties of High Entropy Superalloys. Entropy 18, 62 (2016).
Zhang, L. et al. Nanoindentation Creep Behavior of an Al0.3CoCrFeNi High-Entropy Alloy. Metall. Mater. Trans. A 47, 5871–5875 (2016).
Cao, T. et al. The influence of Al elements on the structure and the creep behavior of AlxCoCrFeNi high entropy alloys. Mater. Lett. 164, 344–347 (2016).
Oblak, J. M. & Owczarsk, W. Cellular Recrystalization in Nickle-Base Superalloy. T. Metall. Soc. Aime. 242, 1563–1568 (1968).
Blavette, D. & Bostel, A. Phase composition and long range order in γ′ phase of a nickel base single crystal superalloy CMSX2: An atom probe study. Acta Metall. 32, 811–816 (1984).
Shang, S. L. et al. Effects of alloying element and temperature on the stacking fault energies of dilute Ni-base superalloys. J. Phys-Condens. Mat. 24, 505403 (2012).
Huang, S. et al. Temperature dependent stacking fault energy of FeCrCoNiMn highentropy alloy. Sripta Mater. 108, 44–47 (2015).
Zaddach, A. J., Scattergood, R. O. & Koch, C. C. Tensile properties of low-stacking fault energy high-entropy alloys. Mater. Sci. Eng. A 636, 373–378 (2015).
Kim, Y. K., Kim, D., Kim, H. K., Oh, C. S. & Lee, B. J. An intermediate temperature creep model for Ni-based superalloys. Int. J. Plasticity 79, 153–175 (2016).
Pollock, T. M. & Argon, A. S. Creep Resistance of CMSX-3 Nickel-Base Superalloy Single-Crystals. Acta Metall. Mater. 40, 1–30 (1992).
Chandran, M. & Sondhi, S. First-principle calculation of APB energy in Ni-based binary and ternary alloys. Model. Simul. Mater. Sc. 19, 025008 (2011).
Tsao, T. K. & Yeh, A. C. The thermal stability and strength of highly alloyed Ni3Al. Mater. Trans. 56, 1905–1910 (2015).
Nabarro, F. R. N. & de Villiers, F. L. Physics of creep and creep-resistant alloys (CRC press, 1995).
Sengupta, A. et al. Tensile behavior of a new single-crystal nickel-based superalloy (CMSX-4) at room and elevated temperatures. J. Mater. Eng. Perform. 3, 73–81 (1994).
Erickson, G. L. The development and application of CMSX@-10, Superalloys 35–44 (1996).
Otto, F. et al. The influences of temperature and microstructure on the tensile properties of a CoCrFeMnNi high-entropy alloy. Acta Mater. 61, 5743–5755 (2013).
Daoud, H. M., Manzoni, A., Volkl, R., Wanderka, N. & Glatzel, U. Microstructure and Tensile Behavior of Al8Co17Cr17Cu8Fe17Ni33 (at.%) High-Entropy Alloy. JOM 65, 1805–1814 (2013).
Kuznetsov, A. V., Shaysultnov, D. G., Stepanov, N. D., Salishchev, G. A. & Senkov, O. N. Tensile properties of an AlCrCuNiFeCo high-entropy alloy in as-cast and wrought conditions. Mater. Sci. Eng. A 533, 107–118 (2012).
Howes, M. A. Additional thermal fatigue data on nickel and cobalt-base superalloys (1973).
Nakagawa, Y., Ohtomo, A. & Saiga, Y. Directional solidification of Rene’ 80. T. Jpn. I. Met. 17, 323–329 (1976).
Rouault-Rogez, H., Dupeux, M. & Ignat, M. High temperature tensile creep of CMSX-2 nickel base superalloy single crystals. Acta Metall. Mater. 42, 3137–3148 (1994).
Veron, M., Brechet, Y. & Louchet, F. Directional coarsening of nickel based superalloys: Driving force and kinetics, Superalloys 181–190 (1996).
Ratel, N., Bruno, G., Bastie, P. & Mori, T. Plastic strain-induced rafting of γ′ precipitates in Ni superalloys: Elasticity analysis. Acta Mater. 54, 5087–5093 (2006).
Gabrisch, H. & Mukherji, D. Character of dislocations at the γ/γ′ interfaces and internal stresses in Nickel-base superalloys. Acta mater. 48, 3157–3167 (2000).
Brown, L. & Ham, R. Dislocation-Particle Interactions, in: Strengthening Methods in Crystals (Elsevier Publishing Corporation, 1971).
Caron, P. & Khan, T. Improvement of creep strength in a nickel-base single-crystal superalloy by heat treatment. Mater. Sci. Eng. 61, 173–184 (1983).
Ardell, A. J. Precipitation hardening. Metall. Trans. A 16, 2131–2165 (1985).
Wang, Q. et al. A cuboidal B2 nanoprecipitation-enhanced body-centered-cubic alloy Al0.7CoCrFe2Ni with prominent tensile properties. Scripta Mater. 120, 85–89 (2016).
Khan, T., Caron, P., Fournier, D. & Harris, K. Single Crystal Superalloys for Turbine Blades: Characterization and Optimization of CMSX-2 Alloy, The 11th Symposium on Steel and Special Alloys for Aerospace, Paris (1985).
Zhang, J. X., Murakumo, T., Koizumi, Y. & Harada, H. The influence of interfacial dislocation arrangements in a fourth generation single crystal TMS-138 superalloy on creep properties. J. Mater. Sci. 24, 4883–4888 (2003).
Tetzlaff, U. & Mughrabi, H. Enhancement of the high-temperature tensile creep strength of monocrystalline nickel-base superalloys by pre-rafting in compression, Superalloys 273–282 (2000).
Cormier, J. Thermal Cycling Creep Resistance of Ni-based single crystal superalloys, Superalloys 385–394 (2016).
Nathal, M. V., MacKay, R. A. & Miner, R. V. Influence of precipitate morphology on intermediate temperature creep properties of a nickel-base superalloy single crystal. Metall. Trans. A 20, 133–141 (1989).
Kuttner, T. & Wahi, R. P. Modelling of internal stress distribution and deformation behaviour in the precipitation hardened superalloy SC16. Mater. Sci. Eng. A 242, 259–267 (1998).
Stevens, R. A. & Flewitt, P. E. J. The dependence of creep rate on microstructure in a γ′ strengthened superalloy. Acta Metall. 29, 867–882 (1981).
Gabrisch, H., Mukherji, D. & Wahi, R. P. Deformation-induced dislocation networks at the γ - γ′ interfaces in the single-crystal superalloy SC16: a mechanism-based analysis. Philos. Mag. A 74, 229–249 (1996).
Mukherji, D. & Wahi, R. P. Some implications of the particle and climb geometry on the climb resistance in nickel-base superalloys. Acta Mater. 44, 1529–1539 (1996).
Murakami, H., Harada, H. & Bhadeshia, H. The Location of Atoms in Re-Containing and V-Containing Multicomponent Nickel-Base Single-Crystal Superalloys. Appl. Surf. Sci. 76, 177–183 (1994).
Saunders, N., Guo, U. K. Z., Li, X., Miodownik, A. P. & Schillé, J. P. Using JMatPro to model materials properties and behavior. JOM 55, 60–65 (2003).
JIS-Z-2271 Japanese Industrial Standard 678–691 (2004).
Acknowledgements
Authors would like to thank the financial support from Ministry of Science and Technology, Taiwan (R.O.C.), project grant number: 103-2221-E-214-035, 104-2221-E-214-033. Te-Kang Tsao would like to thank the support of DS casting and creep tests by Jian-An Huang of I-Shou University, Taiwan, and also ICGP scholarship organized by National Institute for Materials Science, Japan.
Author information
Authors and Affiliations
Contributions
T.K. Tsao contributed to all the experiments and analyses. Prof. A.C. Yeh, Dr. H. Murakami and Prof. J.W. Yeh contributed to the discussion on materials characterization. Prof. K. Kakehi, Prof. C.M. Kuo and Prof. S.R. Jian contributed to the creep tests and materials processing. All authors contributed to the preparation and revision of the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Tsao, TK., Yeh, AC., Kuo, CM. et al. The High Temperature Tensile and Creep Behaviors of High Entropy Superalloy. Sci Rep 7, 12658 (2017). https://doi.org/10.1038/s41598-017-13026-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-13026-7
This article is cited by
-
Advanced Polycrystalline γ′-Strengthened CoNiCr-Based Superalloys
Metallurgical and Materials Transactions A (2024)
-
On the Development of Equiaxed Microstructures in High-Entropy Superalloys and Their Impact on High-Temperature Oxidation Behavior
High Entropy Alloys & Materials (2024)
-
On the Phase Configurational Entropy of Dual-Phase γ/γ′ Multi-principal Element Alloys: A Case Study on the Al–Cu–Fe–Ni–Ti System
High Entropy Alloys & Materials (2024)
-
Design of Laves phase-reinforced compositionally complex alloy
Scientific Reports (2023)
-
Constitutive Behavior With Microstructure and Texture Evolution During the High-Temperature Deformation of Fe11.5Co20.6Ni40.7Cr12.2Al7.8Ti7.2 High-Entropy Alloy
Metallurgical and Materials Transactions A (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.