Black P/graphene hybrid: A fast response humidity sensor with good reversibility and stability

Black phosphorus (BP) materials have attracted considerable attention owing to their ultra-sensitive humidity sensing characteristics because of the natural absorption of water (H2O) molecules on the BP surface caused by the specific 2D layer-crystalline structure. On the other hand, the BP-based humidity sensor is less repeatable due to the instability of BP with water molecules and the stability of the sensor is reduced. In this study, this limitation of the BP-based humidity sensor was overcome by preparing a BP/graphene hybrid as a novel humidity sensing nanostructure. The BP/graphene interface improved the stability of the humidity sensor after a few weeks with a linear response within the relative humidity (RH) range of 15–70%. The sensor’s response/recovery speed of the humidity sensor was extremely fast within few seconds. The response (S) of the humidity sensor based on the BP/graphene hybrid is 43.4% at RH = 70%. The estimated response and recovery time of the sensor is only 9 and 30 seconds at RH = 70% at room temperature. The experimental investigation reveals that the BP/graphene hybrid not only improves the reversibility and hysteresis factors but also enhances the stability of the humidity sensor.

control provides the latest advantages of 2D electronics, such as low electronic noise, low power consumption and excellent stability interfaces.
To date, exfoliated 2D layers, particularly BP, could only be transferred in small sizes onto substrates in basic and proof-of-concept studies 12,13 . However, to take advantage of unique characteristics of scalable technologies, it is essential to establish a mass production process for 2D materials synthesis and sensor device fabrication. This very exciting challenge will be addressed in the current work. In this study, a large quantity of BP materials was synthesized in powder form (several gram-scale) with a novel technique of high energy ball milling (HEBM). The BP powder was exfoliated by a mild ultrasonication process and BP/graphene heterojunction was formed on the graphene surface using an electrospray system for humidity sensor. The humidity sensing performances of the sensors prepared with a pure BP and BP-graphene heterojunction were investigated and compared in terms of the sensitivity, reversibility, and stability. The role of graphene and the interface between BP/graphene for humidity sensors was investigated in detail. Figure 1 presents the sequence of humidity sensor fabrication process using BP material on graphene. The fabrication process starts at transfering graphene onto SiO 2 /Si with wafer-level. Then, the platform of humidity sensor chip comprise patterned graphene between two gold (Au) electrode. The BP powder was synthesized by a HEBM method and deposited on the patterned graphene by electro-spray (see in Supplementary data for more detail). Figure 2a presents a SEM image of fabricated humidity sensor based on BP/graphene hybrid. The patterned graphene was located between two gold (Au) electrodes. The distance between two Au-electrodes was 100 µm. The BP particles were synthesized using a commercially available red P powder according to the HEBM technique (Fig. 2b). The size of BP particles was ca. 200 nm, which were well deposited on the patterned graphene area by an electrospray system, as shown in Fig. 2b.The well-developed crystalline structured BP with an interesting 2D puckered-layer crystalline structure was confirmed by HRTEM (Fig. 2c). HRTEM electron diffraction, as in Fig. 2d showed that the sample was corresponded well to the orthorhombic BP. Figure 3a shows the XRD pattern of BP powder. Major peaks in the pure BP sample were observed at 2θ = 16.44°, 34.8°, and 55.78°, which corresponds to the (020), (040), and (060) planes of BP, respectively, as denoted by the International Center for Diffraction Data (JCPDS # 74-1878). Figure 3b presents the Raman spectrum for the BP-graphene heterojunction, where the characteristic A g 1 , B 2g , and A g 2 peaks of BP are clearly visible at 359, 432, and 462 cm −1 , respectively 8,19 . The A g 1 and A g 2 peaks of the pure BP sample were observed at 356 and 459 cm −1 , respectively. The Raman spectrum of single layer graphene consisted of two major sharp peaks (G and 2D peaks) at 1584 and 2674 cm −1 . The major peaks (G and 2D peaks) originated from the doubly degenerate zone center E 2g mode and the second order zone boundary phonons, respectively 20 . The D peak at 1350 cm −1 is related to the defects present 20 . The features of those peaks are indicators of the quality of graphene, such as doping and strain. The G and 2D peaks in BP/graphene were 1590 and 2689 cm −1 , respectively. No obvious increase in the D peak in the Raman spectra before and after depositing BP powder on graphene was observed. The as-synthesized single layer graphene has Raman spectra with 2D/G ratio > 1. However, the 2D/G ratio value was reduced (2D/G < 1) after the sensor fabrication process (see detail in Fig. S4, Supplementary data). Figure 4 shows the transient response of the as-fabricated humidity sensor, which is based on a pure BP and BP-graphene heterojunction, and their response after 1 hour with a reproducible relative humidity (RH) of 70%. Figure 4a shows the response of humidity sensor using pure BP powder with non-repeatability and degradation after 1 hour. This degradation of the BP-based sensor in a high humidity environment was similar to other works 21,22 , and were reported in other published papers 21,22 . Compared to the pure BP sample, the humidity  sensor based on BP-graphene in Fig. 4b showed a much better response with the advantages of fast response/ recovery, good repeatability and non-degradation after 1 hour. For comparison, the response of as-fabricated humidity sensor using pure graphene can be found in Fig. S5 (Supplementary data). The initial resistance of the humidity sensor was 7.5 kΩ and 500 kΩ for the BP/graphene and pure BP sample, respectively. Owing to the good conductivity of single layer graphene (the initial resistance of humidity sensor using pure graphene was only 0.63 kΩ, see in Fig. S5, Supplementary data), the BP/graphene heterojunction sensor had a very low resistance compared to that of pure BP. Moreover, the signal-to-noise level in the BP/graphene heterojunction was higher than that of pure BP, leading to a clear signal of resistivity sensor in the BP/graphene sample.

Results and Discussion
The sensor relative response (S) is defined as the percentage resistance change of the resistivity sensor by exposure to humidity: where R a is the resistance of the sensors in the presence of dry N 2 gas only and R h is the resistance in the presence of humidity at the given concentrations. The response time is defined as the time required for the humidity sensor to reach 90% of the resistance change (ΔR) when the sensor is exposed to a given humidity. The recovery time is defined as the time needed to recover to 90% of the initial baseline after turning-off the humidity. The responses S (%) of the humidity sensor based on BP-graphene heterojunction calculating from Fig. 5a were 43.4, 35, 25.1, 13, and 3% with a RH of 70, 55, 40, 25, and 15%, respectively. The response/recovery time of humidity sensor was 9/30 seconds at a RH of 70%.Compared to other similar studies, the humidity sensor using the liquid exfoliation of pure BP has a response/recovery time of 255/10 seconds 21 and 5/5 seconds 12 . Meanwhile, the response/recovery time of our humidity sensor using pure BP was 24/72 seconds. The results showed that the humidity sensor using BP/graphene heterojunction is better than that using pure BP with a 2-fold faster response time. Moreover, the humidity sensor using pure BP without a passivation method showed large degradation after a few cycles (within 2 hours) 21 . Fig. 5b explains the sensing mechanism of the humidity sensors based on the BP/graphene heterojunction. The humidity (H 2 O) molecules withdraw a free electron from the BP flakes and increase the hole density in BP. The BP exhibits a p-type semiconductor behavior 8,9,15 . Therefore, the increasing hole density in p-type BP leads to decreasing resistance in the humidity sensor of the pure BP sample (as see in Fig. 4a). With BP-graphene heterojunction sample, this encourages the free electron to graphene transfer to BP via the BP/ graphene interface. Finally, the increasing holes in p-type graphene decrease the resistance of the BP/graphene sample (as see in Fig. 4b). Figure 5c shows the transient response of the humidity sensor based on the as-fabricated BP-graphene heterojunction and the response on the same sensor sample after 2 weeks. In general, there is little difference between these responses, except that the response/recovery is slower after 2 weeks. On the other hand, the sensor had a large reduction in response after 4 weeks, as shown in Fig. 5d (see also in the Supplementary data). Figure 5d confirmed the linearity of humidity sensor in the RH range of 15-70% and the stability of the sensor after 2 weeks. Compared to previous publications on humidity sensing using BP materials 12 , the BP-graphene heterojunction humidity sensor in this study has the advantageous features of a fast response/recovery time, linearity and mass production process of sensor. The degradation of the BP only sensor was caused by lower stability of the surface of the BP flake in moisture and humidity 14 . In this case, pure BP played a role both as a humidity sensing material and conducting patch between the Au electrodes in the sensor device, leading to higher noise and degradation during humidity absorption/desorption. The sensing mechanism of BP/graphene heterojunction involves charge transfer at the interface between BP/graphene and graphene playing a role as a stable conducting path. In addition, due to the good stability at the BP/graphene interface [15][16][17] , the humidity sensor could show better stability and reversibility, compared to the sensor using the BP only sample. Passivation of BP surface is essential for sensing applications 12,22 , and electronic devices 14, 15 based on BP materials. This is the greatest challenge for applying BP as a sensing material because the passivated BP process reduced the sensitivity of the BP surface, leading to the complicated fabrication of the sensor. However, the sensor based on passivated BP showed a long-term stability up to one month 22 or three months 12 . In this study, the BP/graphene heterojunction humidity sensor showed high sensitivity, fast/response recovery owing to BP without a passivation process and acceptable stability for up to two-weeks, which is better than that of the sensor using the pure exfoliated BP material with stability for only a few hours.

Conclusions
A humidity sensor based on BP/graphene heterojunction was developed using a large scale fabrication technique. The role of graphene in the heterojunction of the humidity sensor was investigated by comparing the sensor performance of the BP and BP/graphene sample. The BP-only samples showed good sensitivity to humidity with the advantages of a strong response and rapid response/recovery time, but were less stable, non-linear and reversible. On the other hand, the BP/graphene heterojunction-based humidity sensor overcomes these limitations and has excellent sensing properties with a response of 43.4% and a response/recovery time of 9/30 seconds with a RH of 70%. In addition, the humidity sensor has good repeatability, low hysteresis and long-term stability over two weeks by forming a BP-graphene heterojunction. Moreover, it solves the instability of the BP-only sensor.

Methods
The BP powder was synthesized using the HEBM technique at ambient temperature and pressure. The detail experimental conditions for the synthesis of BP powder by HEBM can be found elsewhere (see the Supplementary data) 23 . The wafer-scale of single layer graphene was synthesized by chemical vapor deposition (CVD) 20 . The sensor chip (graphene chip) with patterned graphene between the two gold (Au)-electrodes (distance of 100 µm) was fabricated in wafer-scale level by a dry-etching technique and conventional MEMS process (see the Supplementary data). The BP powder dispersed in dimethyl sulphonate (DMSO, Sigma-Aldrich) by an ultrasonic treatment was deposited on a graphene chip to fabricate a humidity sensor via an electrospray system. DMSO was used as the solvent for BP in the electrospray experiment, where BP was deposited on the patterned graphene surface. The water flow rate was controlled precisely by a syringe pump (KD 200; KD scientific). The electric potential was adjusted using a power supply (+ 0-30 kV; Korea switching) connected to the metal capillary. The metal capillary was used as an electrospray emitter with an inner diameter of 250 μm. The nozzle tip-to-substrate distance was fixed to 10 mm. For rapid evaporation of the solvent, the surface temperature of the substrate was adjusted using a hot plate (more details, see the Supplementary data). For comparison, the humidity sensor using pure BP powder was fabricated but without graphene between the Au electrodes. Humidity sensors using pure BP powder for comparison were fabricated under the same conditions but without graphene between the Au electrodes. In the wire-bonding process, the humidity sensor was mounted on the TO-39 chip to finish the sensor fabrication process.
The surfaces of the BP/graphene hybrid were characterized by field emission scanning electron microscope (FESEM, a JSM-6500F). Transmission electron microscopy (TEM) and high resolution TEM (HRTEM) images of the BP were captured using an ultra-high resolution field emission electron microscope (JEOL JEM-2100). The crystalline characteristics of the BP were investigated by X-ray diffraction (XRD, D/MAX 2500 Rigaku, Japan). Raman spectroscopy(Xplora Horiba, France) was performed in a back scattering configuration using a 532 nm laser source and holographic grating of 1200 grooves/mm. The sensors were mounted inside an enclosed environmental chamber and a multi-meter (Fluke 8846 A) connected to the computer was used to record the resistance of the sensors. The humidity in gas chamber was generated using a water bubble controller and introduced into the chamber by N 2 gas. A computerized mass flow controller (ATOVAC, GMC 1200) was used to change the humidity and concentration of N 2 gas. The relative humidity (RH%) was varied from 15 to 70%. N 2 gas with different humidity level was delivered to the chamber at a constant flow rate of 100 standard cubic centimeters per minute (sccm). The gas chamber was purged with N 2 gas between each humidity pulse, allowing the surfaces of the sensors to return to the standby state.