Lanthanum hexaboride for solar energy applications


We investigate the optical properties of LaB6 – based materials, as possible candidates for solid absorbers in Concentrating Solar Power (CSP) systems. Bulk LaB6 materials were thermally consolidated by hot pressing starting from commercial powders. To assess the solar absorbance and spectral selectivity properties, room-temperature hemispherical reflectance spectra were measured from the ultraviolet to the mid-infrared, considering different compositions, porosities and surface roughnesses. Thermal emittance at around 1100 K has been measured. Experimental results showed that LaB6 can have a solar absorbance comparable to that of the most advanced solar absorber material in actual plants such as Silicon Carbide, with a higher spectral selectivity. Moreover, LaB6 has also the appealing characteristics to be a thermionic material, so that it could act at the same time both as direct high-temperature solar absorber and as electron source, significantly reducing system complexity in future concentrating solar thermionic systems and bringing a real innovation in this field.


Lanthanum hexaboride (LaB6) is a well known thermionic material (see for instance refs 1,2,3,4,5 among the many available). Its ability to emit electrons has been widely exploited in last 60 years since the pioneering work of Lafferty on sintered hexaboride ceramics6. It has been used to build hot cathodes for a large variety of applications, including electron guns in cathode tubes7, cathodes for plasma production8, 9 and electron microscopes10, 11. While at present, mainly single crystalline emitters are used, sintered ceramics show thermionic properties as well, and historically they have been the first to be studied6, 7, 12. It has been shown that, if surface impurities are removed, sintered LaB6 can show a work function value of 2.36 eV, which is fully comparable to that of single crystals (2.28 ÷ 2.47 eV)13. In addition, photo-induced electron emission is documented in the literature both by single crystals and by polycristalline specimens14, 15, as well as simultaneous thermionic emission and photoemission under excitation of a polycrystalline film at 442 nm wavelength (2.8 eV)16.

In the field of material processing, LaB6 is also used as additive to other diboride ultra-high temperature ceramics (UHTCs) for improving their oxidation resistance at extreme temperatures17, 18. Because of its well-defined plasma reflection edge making it a textbook case, optical properties of bulk and thin film LaB6 have been investigated and theoretically modeled in the past19,20,21. Recently, the attention on optical properties of LaB6 has been renewed, but to the best of our knowledge, it is mainly restricted to the use of this material in form of nanoparticles22,23,24.

Renewable energies, and in particular solar energy exploitation issues, are a key topic for the future. At present, the main technologies for concentrating solar systems are solar thermal power and concentrating photovoltaics. However, very recently a novel approach has been proposed for the direct generation of power from concentrated sunlight exploiting both thermionic and thermoelectric effects25. In the cited paper, the solar absorber and the thermionic emitter were different materials, with the thermionic emitter (a thin diamond film) deposed on the back surface of the sunlight absorber (an UHTC carbide with a special treatment to increase solar absorbance).

From our previous studies on UHTC carbides and borides26,27,28,29,30,31,32,33,34, we have assessed strength and weakness points for the use of this class of novel materials as innovative high-temperature solar absorbers in thermodynamic solar plants. In fact, the ideal solar absorber should withstand very high temperatures while maintaining, with no damage, good mechanical strength and stability, high thermal conductivity, high solar absorbance to efficiently collect sunlight, and low emittance at operating temperatures, to minimize unwanted energy losses by thermal re-radiation35,36,37. From point of view of optical properties, strength points of UHTC materials we have investigated so far are the intrinsic low thermal emittance and good spectral selectivity, while solar absorbance typically is to be improved, e.g. by proper surface treatments38, 39. In this work we report on the microstructural and optical characterization of LaB6 ceramics. For thermodynamic solar applications, the knowledge of optical properties of LaB6 is of interest because, as recalled above, it is used as additive for UHTC borides.

However, we point out that the innovation potential of LaB6 is much higher. In fact, compared to previously investigated UHTCs, LaB6 has the appealing characteristics to be a thermionic material, so that it could act at the same time both as direct high-temperature solar absorber and as electron source, significantly reducing system complexity in future concentrating solar thermionic systems and bringing a real innovation in this field. Moreover, if surface impurities will be carefully controlled, e.g. with a proper control of production processes and with operation in vacuum, so that the work function is maintained below 4.13 eV (corresponding to light wavelengths longer than 300 nm), direct electron emission (photoemission) from LaB6 induced by absorption of the UV-blue spectral portion of concentrated sunlight could be additionally and simultaneously exploited (Fig. 1). Thus, to assess the potential of LaB6 for this radically new concept of solar absorber we carried out our study as a function of the sample porosity and surface finishing.

Figure 1

Concept of the thermionic/thermodynamic solar absorber.

Results and Discussion

Microstructural features

Table 1 lists investigated samples, while Fig. 2 shows microstructures and EDS spectra. As expected, the monolithic material (LaB6_p), Fig. 2a,b contains a significant fraction of open porosity, in agreement with density measurements. The grain size ranges from 3 to 10 µm. Traces of La-B-O spurious phases were recognized along the grain boundaries by SEM-EDS analysis. (see inset of Fig. 2b and corresponding EDS spectra). These impurities are typical contaminants of the boride powders and hindered the material densification during hot pressing40.

Table 1 List of materials, compositions, densities and surface roughness.
Figure 2

(a) Rough surface of porous LaB6 in SE imaging, (b) polished surface of porous LaB6 in SE imaging, Inset: high magnification of porous LaB6 microstructure showing oxide phases (La2O3) wetting the grain boundaries and relative EDS spectra, (c) polished surface of dense LaB6 in SE imaging, (d) higher magnification details showing B4C pockets in BSE imaging; (e) ZrB2 inclusion in LaB6 matrix in-lens imaging (d) and corresponding EDS spectra.

From both Fig. 2a,b and Table 1 the difference of surface roughness between as sintered and polished surface can be appreciated (Ra decreased from 0.58 to 0.09 µm for unpolished and polished surfaces, respectively).

As for the LaB6 _d sample, addition of ZrB2 and B4C notably improved the densification. The final material was completely dense and the microstructure can be observed in Fig. 2c–e. According to XRD (not shown) no extra phases formed. Dark spots in Fig. 2c,d belong to B4C, while the in secondary electron imaging LaB6 and ZrB2 display similar contrast. By in-lens signal, see Fig. 2e, dark contrasting grains belong to LaB6, whilst light contrasting grains belong to ZrB2. The improvement in the densification was mainly attributed to the addition of B4C, via cleaning of surface oxides such as LaxOy, BxOy from the boride particles, as observed for similar ceramics40. Increase in the final density also affected the quality of surface polishing and consequently the final roughness decreased to Ra 0.03 µm, see Table 1.

Optical characterization

Figure 3 shows the reflectance spectra of LaB6 samples, compared to previously analyzed dense hafnium and zirconium borides41. The inset of Fig. 3 shows the reflectance in the sunlight spectral region, the sunlight spectrum is also superimposed for reference.

Figure 3

Reflectance spectra of samples, compared to dense samples of hafnium and zirconium borides from ref. 41.

LaB6 reflectance directly increased with decreasing of the surface roughness. This is particularly evident comparing LaB6_p rough and LaB6_p polished. For the dense composite material, the reflectance was further improved due to the almost complete elimination of porosity. The spectrum shape presents very similar features in pure LaB6 and the LaB6 –based composite containing ZrB2 and B4C, except for a local minimum at round 3 μm wavelength and a couple of secondary small minima between 7 and 10 µm, present in both spectra of porous samples. These features could be ascribed to oxide phase impurities in porous LaB6 ceramics, like La-O phases, B-O, or mixed La-B-O phases (as those observed in Fig. 2b). In contrast, these spurious phases were not observed in the optical spectra of LaB6 _d owing to their removal by B4C, as previously mentioned. No specific features in the spectrum that could be attributed to B4C inclusions were recognized in LaB6_d.

Compared to hafnium and zirconium borides, LaB6 has a considerable lower reflectance (i.e. a higher absorbance) near the peak of sunlight spectral distribution. However, thanks to peculiar spectral features of LaB6, the rough porous sample, LaB6_p rough remains more absorptive up to about 1 μm wavelength. Towards longer wavelengths, the reflectance of porous pellets is about 20% lower than that of other borides, while the dense sample shows a similar reflectance at the infrared plateau region.

From the experimental room-temperature hemispherical reflectance ρ(λ) we calculated the total solar absorbance, α:

$$\alpha =\frac{{\int }_{{\lambda }_{\min }}^{{\lambda }_{\max }}(1-{\rho }^{\cap }(\lambda ))\cdot S(\lambda )d\lambda }{{\int }_{{\lambda }_{\min }}^{{\lambda }_{\max }}S(\lambda )d\lambda }$$

where S(λ) is the Sun emission spectrum42 and the integration is carried out between λmin = 0.3 µm and λmax = 3.0 µm; and an estimated hemispherical emittance, ε, at 1100 K:

$$\varepsilon =\frac{{\int }_{\lambda 1}^{\lambda 2}(1-{\rho }^{\cap }(\lambda ))\cdot B(\lambda ,1100K)d\lambda }{{\int }_{\lambda 1}^{\lambda 2}B(\lambda ,1100K)d\lambda }$$

where B(λ, 1100 K) is the blackbody spectral radiance at 1100 K temperature and λ1 = 0.3 µm and λ2 = 16.0 µm. The α/ε ratio (sometimes called spectral selectivity) is a parameter assessing the material potential for solar receiver applications, and ideally should be taken as high as possible. Figure 4 shows absorbance and spectral selectivity for the investigated LaB6 samples, together with the two reference borides.

Figure 4

Calculated solar absorbance α and solar selectivity α/ε for LaB6 samples and comparison with HfB2, ZrB2 and SiC.

From Fig. 4 we can immediately appreciate the high potential of LaB6 as solar absorber material: both solar absorbance and spectral selectivity are comparable or higher than those of comparison materials ZrB2 and HfB2 41. Even more, the rough porous sample (LaB6_p rough) shows a remarkable solar absorbance of 0.7, which is only slightly lower than that of the most advanced solar absorber material to date in actual plants, namely silicon carbide (SiC, α ≈ 0.841) (see ref. 43 and references therein). As for spectral selectivity, for all samples it remains higher than that of SiC (α/ε ≈ 141) and for most of them it is comparable to that of the two reference borides, with the LaB6 dense polished sample showing a remarkable value of α/ε = 6.4. If we compare LaB6 pellets each other, we can say that a high solar absorbance is obtained at the expense of spectral selectivity. However, even in its less absorptive form (dense polished), LaB6 results promising, as said before, with respect to previously investigated borides, as it shows a comparable absorbance and a remarkably higher spectral selectivity.

For a more reliable assessment of LaB6 potential for solar absorber applications, we measured the thermal emittance at high temperature. In fact it is known that emittance calculated from room-temperature reflectance spectra are a very useful tool for a preliminary material evaluation, but underestimate the value at high temperature44.

Figure 5 compares the experimental spectral normal emittances (solid lines) with the values calculated from room-temperature reflectance data εcalc(λ) = 1 − ρ(λ) (dashed values). As previously mentioned, the measured emittance is higher than the calculated one. Samples maintain the hierarchy among them, as expected, with the dense pellet showing the lowest emittance (spectrally integrated value of 0.2), the polished porous LaB6 the intermediate value (0.4) and the rough porous the highest value (0.6). As a term of comparison, it should be noticed that LaB6 favourably compares to SiC also if experimental emittances are considered, because the obtained values are significantly lower than those experimentally obtained for SiC pellets (0.9 at 1100 K).

Figure 5

Calculated (dashed lines) and experimental emittance (solid lines) of LaB6 samples. The measurement temperature for each sample is indicated in legend. The features at around 3.4 µm, 4.2 µm, between 4.8 and 7.7 µm and around 15 µm are instrumental artifacts due to unbalanced molecular absorption by ambient air in the optical path of the beams outside the furnace.

If the spectral shape of emittance curves is concerned, we can observe that for the dense sample, calculated and experimental curves are very similar, while porous samples show some differences. In particular, for porous pellets, we cannot find in experimental emittances the wide bands of local maxima peaked at around 3, 7 and 9 µm wavelengths, that can be seen, on the contrary, in the curves calculated from room temperature spectra. Even if a quantitative evaluation requires additional microstructural measurements after high temperature experiments, which are beyond the scope of this work and will be the subject of a further study, we can explain the obtained results in terms of degassing of impurities still present in porous samples. For instance, according to studies carried out on the boron oxide vapor pressure45, 1100 K and ~10−6 mbar cause boron oxide species vaporization in boride samples, which could be the case of the LaB6_p sample subjected to high vacuum/high temperature during the emissivity measurement.

In summary, the study we cave carried out both at room and high temperature show that LaB6 not only is comparable or better than other boride UHTCs, but in its porous rough form is even better than SiC showing a similar solar absorbance and twice the spectral selectivity, as inferred from room temperature measurements, and a lower measured emittance at 1100 K temperature (0.6 versus 0.9). As already mentioned, SiC is the most advanced solar absorber actually used in plants to date.


This work is devoted to the study of the spectral reflectance and thermal emittance of pure LaB6 and LaB6-ZrB2-SiC composites in order to evaluate their potential as novel solar absorbers. Pure LaB6 materials contained a porosity of about 20%, which resulted in a lower reflectance compared to composite materials. In dense composites containing ZrB2 as secondary phase, LaB6 has an intrinsic solar radiation selectivity with high reflectance plateau at wavelengths longer than 1 µm and a remarkable α/ε ratio approaching 6.4. Moreover, the porous sample with rough surface favorably compares even to SiC from all points of view, as it shows a similar solar absorbance and a doubled spectral selectivity. Finally, if we consider the thermal emittance at 1000–1100 K temperature, even the most emissive LaB6 porous rough sample has a significantly lower emittance than SiC.

However we emphasize that, in our opinion, the innovation potential of LaB6 is much higher because, in addition to the promising characteristics listed above, it is also a widely documented thermionic material, and with one of the highest known electron emissivities. Thanks to these properties it could successfully act, at the same time, both as direct high-temperature solar absorber and as electron source, significantly reducing system complexity in future concentrating solar thermionic systems. This could make it a really revolutionary material in solar technology.


Commercial powders were used to produce the discs: LaB6, (H.C. Starck Grade C), ZrB2 (H.C. Starck, grade B), B4C (H.C. Starck, grade HS). The monolithic LaB6 was produced by hot pressing at 1930 °C, 40 MPa and holding time 15 min. The composite material was obtained by wet ball milling, drying of the starting powders with the following composition:

$$-{{\rm{LaB}}}_{6}+15\,{\rm{vol}} \% \,{{\rm{ZrB}}}_{2}+3\,{\rm{vol}} \% \,{{\rm{B}}}_{4}{\rm{C}}$$

The powder mixture was then densified by hot pressing at 1900 °C, 40 MPa and holding time 15 min. After sintering, the density of the ceramics was experimentally determined by the Archimede method. The sintered pellets were polished using diamond paste up to 1 µm. The samples’ surface were analysed by SEM-EDS (FE-SEM, Carl Zeiss Sigma NTS Gmbh, Oberkochen, DE) and energy dispersive X-ray spectroscopy (EDS, INCA Energy 300, Oxford instruments, UK). The mean surface roughness (R a) and the distance between the highest asperity, peak or summit, and the lowest valley (R t) was measured according to the European standard CEN 624-4 using a commercial contact stylus instrument (Taylor Hobson mod. Talysurf Plus) fitted with a 2 µm-radius conical diamond tip over a track length of 8 mm and with a cut-off length of 0.8 mm.

The hemispherical reflectance spectra were acquired using two instruments: a double-beam spectrophotometer (Lambda900 by Perkin Elmer) equipped with a Spectralon®-coated integration sphere for the 0.25–2.5 µm wavelength region and a Fourier Transform spectrophotometer (FT-IR “Excalibur” by Bio-Rad) equipped with a gold-coated integrating sphere and a liquid nitrogen-cooled detector for the range 2.5–16.5 μm.

Thermal emittance has been measured using the setup described in detail in ref. 44 and here briefly recalled for convenience. The apparatus consists of a high-vacuum furnace interfaced either to a Fourier-transform infrared spectrophotometer (Bio-Rad Excalibur) and to a reference blackbody (C.I. Systems SR-2) by means of a splitting optical system. The ultimate pressure limit is few 10−6 mbar. The temperature is read on the sample upper surface by means of three thermocouples. The uncertainties are ±20 K on the temperature and ±5% on the spectral emittance. As for the temperature, it should be observed that the furnace heater is able to reach up to 1200 K, but the temperature obtained on the measurement surface of each sample is lower because of losses at thermal contact.


  1. 1.

    Oshima, C. et al. Thermionic emission from single‐crystal LaB6 tips with [100],[110],[111], and [210] orientations. Journal of Applied Physics 51, 1201–1206 (1980).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Futamoto, M. et al. Thermionic emission properties of a single‐crystal LaB6 cathode. Journal of Applied Physics 51, 3869–3876 (1980).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Storms, E. K. & Mueller, B. A. A study of surface stoichiometry and thermionic emission using LaB6. Journal of Applied Physics 50, 3691–3698 (1979).

    ADS  CAS  Article  Google Scholar 

  4. 4.

    Futamoto, M., Nakazawa, M. & Kawabe, U. Thermionic emission properties of hexaborides. Surface Science 100, 470–480 (1980).

    ADS  CAS  Article  Google Scholar 

  5. 5.

    Futamoto, M., Nakazawa, M. & Kawabe, U. High temperature surface composition of hexaboride thermionic electron emitters. Vacuum 33, 727–732 (1983).

    CAS  Article  Google Scholar 

  6. 6.

    Lafferty, J. M. Boride Cathodes. Journal of Applied Physics 22, 299–309 (1951).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Broers, A. N. Some experimental and estimated characteristics of the lanthanum hexaboride rod cathode electron gun. Journal of Physics E: Scientific Instruments 2, 273 (1969).

    ADS  Article  Google Scholar 

  8. 8.

    Goebel, D. M., Crow, J. T. & Forrester, A. T. Lanthanum hexaboride hollow cathode for dense plasma production. Review of Scientific Instruments 49, 469 (1978).

    ADS  CAS  Article  PubMed  Google Scholar 

  9. 9.

    Akhmetov, T. D. et al. Studies of plasma production in a linear device with plane LaB6 cathode and hollow anode. AIP Conference Proceedings 1771, 070003 (2016).

    Article  Google Scholar 

  10. 10.

    Broers, A. N. High‐resolution thermionic cathode scanning transmission electron microscope. Applied Physics Letters 22, 610–612 (1973).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Zhang, H. et al. An ultrabright and monochromatic electron point source made of a LaB6 nanowire. Nature Nanotechnology 11, 273–279 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  12. 12.

    Furukawa, Y., Yamabe, M., Ishizuka, T. & Inagaki, T. Current stability of single‐crystal and sintered LaB6 cathodes. Journal of Applied Physics 52, 533–534 (1981).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Pelletier, J. & Pomot, C. Work function of sintered lanthanum hexaboride. Applied Physics Letters 34, 249–251 (1979).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Mogren, S. & Reifenberger, R. Thermionic and threshold photoemission energy distributions from LaB6 (110). Surface science 186, 232–246 (1987).

    ADS  CAS  Article  Google Scholar 

  15. 15.

    Zimmer, C. M. et al. Nanoscale photoelectron ionisation detector based on lanthanum hexaboride. Physica status solidi (A) 208, 1241–1245 (2011).

    ADS  CAS  Article  Google Scholar 

  16. 16.

    May, P. G., Petkie, R. R., Harper, J. M. E. & Yee, D. S. Photoemission from thin‐film lanthanum hexaboride. Applied Physics Letters 57, 1584–1585 (1990).

    ADS  CAS  Article  Google Scholar 

  17. 17.

    Eakins, E., Jayaseelan, D. D. & Lee, W. E. Toward Oxidation-Resistant ZrB2-SiC Ultra High Temperature Ceramics. Metallurgical and Materials Transactions A 42, 878–887 (2011).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Zhang, X. H., Hu, P., Han, J. C., Xu, L. & Meng, S. H. The addition of lanthanum hexaboride to zirconium diboride for improved oxidation resistance. Scripta Materialia 57, 1036–1039 (2007).

    CAS  Article  Google Scholar 

  19. 19.

    Kauer, E. Optical and electrical properties of LaB6. Physics Letters 7, 171 (1963).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Kimura, S., Nanba, T., Tomikawa, M., Kunii, S. & Kasuya, T. Electronic structure of rare-earth hexaborides. Physical Reviews B 46, 12196–12204 (1992).

    ADS  CAS  Article  Google Scholar 

  21. 21.

    Peschmann, K. R., Calow, J. T. & Knauff, K. G. Diagnosis of the optical properties and structure of lanthanum hexaboride thin films. Journal Applied Physics 44, 2252–2256 (1973).

    ADS  CAS  Article  Google Scholar 

  22. 22.

    Yuan, H. O. N. G. et al. Size dependent optical properties of LaB6 nanoparticles enhanced by localized surface plasmon resonance. Journal of Rare Earths 31, 1096–1101 (2013).

    Article  Google Scholar 

  23. 23.

    Yuan, Y., Zhang, L., Hu, L., Wang, W. & Min, G. Size effect of added LaB6 particles on optical properties of LaB6/polymer composites. Journal of Solid State Chemistry 184, 3364–3367 (2011).

    ADS  CAS  Article  Google Scholar 

  24. 24.

    Chen, C. J. & Chen, D. H. Preparation of LaB6 nanoparticles as a novel and effective near-infrared photothermal conversion material. Chemical Engineering Journal 180, 337–342 (2012).

    CAS  Article  Google Scholar 

  25. 25.

    Bellucci, A. et al. Preliminary characterization of ST2G: Solar thermionic-thermoelectric generator for concentrating systems. AIP Conference Proceedings 1667, 020007 (2015).

    Article  Google Scholar 

  26. 26.

    Sani, E., Mercatelli, L., Francini, F., Sans, J.-L. & Sciti, D. Ultra-refractory ceramics for high-temperature solar absorbers. Scripta Materialia 65, 775–778 (2011).

    CAS  Article  Google Scholar 

  27. 27.

    Sani, E., Mercatelli, L., Fontani, D., Sans, J.-L. & Sciti, D. Hafnium and Tantalum Carbides for high temperature solar receivers. Journal of Renewable and Sustainable Energy 3, 063107 (2011).

    Article  Google Scholar 

  28. 28.

    Sani, E., Mercatelli, L., Sansoni, P., Silvestroni, L. & Sciti, D. Spectrally selective ultra-high temperature ceramic absorbers for high-temperature solar plants. Journal of Renewable and Sustainable Energy 4, 033104 (2012).

    Article  Google Scholar 

  29. 29.

    Sani, E., Mercatelli, L., Sans, J.-L., Silvestroni, L. & Sciti, D. Porous and dense Hafnium and Zirconium Ultra-High Temperature Ceramics for solar receivers. Optical Materials 36, 163–168 (2013).

    ADS  CAS  Article  Google Scholar 

  30. 30.

    Sciti, D. et al. Tantalum diboride-based ceramics for bulk solar absorbers. Solar Energy Materials and Solar Cells 130, 208–216 (2014).

    CAS  Article  Google Scholar 

  31. 31.

    Sani, E., Landi, E., Sciti, D. & Medri, V. Optical properties of ZrB2 porous architectures. Solar Energy Materials and Solar Cells 144, 608–615 (2016).

    CAS  Article  Google Scholar 

  32. 32.

    Sani, E. et al. Optical properties of dense zirconium and tantalum diborides for solar thermal absorbers. Renewable Energy 91, 340–346 (2016).

    CAS  Article  Google Scholar 

  33. 33.

    Sani, E. et al. Compositional dependence of optical properties of zirconium, hafnium and tantalum carbides for solar absorber applications. Solar Energy 131, 199–207 (2016).

    ADS  CAS  Article  Google Scholar 

  34. 34.

    Sani, E. et al. Process and composition dependence of optical properties of zirconium, hafnium and tantalum borides for solar receiver applications. Solar Energy Materials and Solar Cells 155, 368–377 (2016).

    CAS  Article  Google Scholar 

  35. 35.

    Bogaerts, W. F. & Lampert, C. M. Materials for photothermal solar energy conversion. Journal of Materials Science 18, 2847–75 (1983).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Lampert, C. M. Advanced optical materials for energy efficiency and solar conversion. Sol. Wind Techn 4, 347–79 (1987).

    Article  Google Scholar 

  37. 37.

    Kennedy C. E. Review of mid- to high-temperature solar selective absorber materials. National Renewable Energy Laboratory report no. NREL/TP-520-31267 (2002).

  38. 38.

    Sciti, D. et al. Femtosecond laser treatments to tailor the optical properties of Hafnium carbide for solar applications. Solar Energy Materials and Solar Cells 132, 460–466 (2015).

    CAS  Article  Google Scholar 

  39. 39.

    Sciti, D., Trucchi, D. M., Bellucci, A., Orlando, S., Zoli, L. & Sani, E. Effect of surface texturing by femtosecond laser on tantalum carbide ceramics for solar receiver applications. Solar Energy Materials and Solar Cells 161, 1–6 (2017).

    CAS  Article  Google Scholar 

  40. 40.

    Sciti D., Silvestroni L., Medri V., Monteverde F. Sintering and densification of ultra-high temperature ceramics, In: Ultra-High Temperature Ceramics: Materials for Extreme Environment Applications, eds Fahrenholtz W., Wuchina E., Lee W., and Zhou Y., ISBN 0-471-9781118700785 Copyright © Wiley, Inc. 2014.

  41. 41.

    Sciti, D., Silvestroni, L., Mercatelli, L., Sans, J.-L. & Sani, E. Suitability of ultra-refractory diboride ceramics as absorbers for solar energy applications. Solar Energy Materials and Solar Cells 109, 8–16 (2013).

    CAS  Article  Google Scholar 

  42. 42.

    Standard Tables for Reference Solar Spectral Irradiances: Direct Normal and Hemispherical on 37° Tilted Surface, Active Standard ASTM G173. ASTM G173 – 03 (2012).

  43. 43.

    Capuano, R. et al. Numerical models of advanced ceramic absorbers for volumetric solar receivers. Renewable and Sustainable Energy Reviews 58, 656–665 (2016).

    Article  Google Scholar 

  44. 44.

    Mercatelli, L., Meucci, M. & Sani, E. Facility for assessing spectral normal emittance of solid materials at high temperature. Applied Optics 54, 8700–8705 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  45. 45.

    Zhang, S. C., Hilmas, G. E. & Fahrenholtz, W. G. Pressureless densification of zirconium diboride with boron carbide additions. J. Am. Ceram. Soc. 89, 1544–1550 (2006).

    CAS  Article  Google Scholar 

Download references


Part of this activity has been carried out in the framework of the FIRB2012-SUPERSOLAR project RBFR12TIT1 funded by the Italian Ministry of University and Research. E.S. gratefully acknowledges the Italian bank foundation “Fondazione Ente Cassa di Risparmio di Firenze” for supporting this activity within the framework of “SOLE NANO” project (pratica no. 2015.0861). Thanks are due to Mr. M. D’Uva, Mr. M. Pucci (CNR-INO) and C. Melandri (CNR-ISTEC) for technical assistance. Dr. N. Azzali (CNR-INO) is gratefully acknowledged for his help in thermal emittance measurements.

Author information




D.S. and L.Z. prepared the samples and carried out microstructural analysis. E.S., L.M. and M.M. carried out optical characterization. E.S. and D.S. wrote the manuscript, which has been then reviewed by all authors.

Corresponding author

Correspondence to Elisa Sani.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Sani, E., Mercatelli, L., Meucci, M. et al. Lanthanum hexaboride for solar energy applications. Sci Rep 7, 718 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing