Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Synergistic interaction of Re complex and amine functionalized multiple ligands in metal-organic frameworks for conversion of carbon dioxide

Abstract

A metal-organic framework (MOF) is composed of secondary building units (SBUs) of metal ions and organic ligands to link each SBU. Moreover, the photosynthetic synthesis of a valuable CO chemical from carbon dioxide (CO2) represents an important class of appealing methods. Herein, we find that a molecular photocatalyst with high selectivity and activity can be designed via a fine balance in the proximity of Re complex (ReI(CO)3(BPYDC)(Cl), BPYDC = 2,2′-bipyridine-5,5′-dicarboxylate) and -NH2 functionalized multiple ligands composing a MOF photocatalyst, denoted as Re-MOF-NH2. These ligands in Re-MOF-NH2 has been confirmed by infrared, UV-visible, and 1H nuclear magnetic resonance spectra. Moreover, we show from extended X-ray absorption fine structure and in-situ infrared spectra that the bond corresponding to Re-CO upon introduction of -NH2 functional groups is divided into asymmetric bonds of 1.4 Å and 2.3 Å along with different CO2 vibrations, thus making the configuration of carbonyl groups in a Re metal complex become asymmetric in addition to aiding formation of CO2 intermediates within Re-MOF-NH2. Indeed, both of the uneven electron distribution in asymmetric carbonyl groups for Re-CO and the intermolecular stabilization of carbamate intermediates are proven to give the approximately 3-fold increase in photocatalytic activity for conversion of CO2 into CO.

Introduction

Artificial photosynthesis using molecular catalysts1,2,3,4,5 is an attractive method for converting solar energy into value-added chemicals such as CO6. Hydrogen (H2) has a specific energy density much higher than those of conventional energy carriers while its nature in a gas state stable at ambient conditions, thus resulting in the storage issues in high pressures or extremely low temperatures. Meanwhile, a variety of liquefied fuels in principle, which are safe for transportation at ambient conditions, could be produced from CO on combination with gaseous H2 molecules7. For example, CO could be used to generate a liquefied fuel of methanol that has a high-energy density of 5,400 Wh per kilogram. Subsequently, methanol can be also used to produce other chemical products such as Olefin via “Methanol-to-Olefin (MTO)” process and Gasoline via “Methanol-to-Gasoline (MTG)” process8. Our recent work9 suggested a new strategy for tuning molecular photoactive ligand centres within the interior of a metal-organic framework (MOF) having embedded plasmon nanoparticles. Meanwhile, development of a molecular catalyst on combination of cooperative molecular ligands that enable the manipulation of the activity and selectivity for its photocatalytic conversion of CO2 into a valuable CO chemical with 100% selectivity would give a breakthrough solution to conversion of solar energy into useful hydrocarbon fuels, thus paving a new route for many promising applications. As of today, a single molecular catalyst with one kind of photoactive molecular ligand centres often does not have functional group enabling cooperation conversion of carbon dioxide into CO with high selectivity and activity. Additionally, absorption of visible light on the main solar energy spectrum is still limited for even molecular catalysts with multiple ligands. Therefore, it is advantageous for a molecular catalyst to have conjugated ligands enabling synergistic conversion of carbon dioxide upon visible light absorption.

Herein, we report a new MOF with multiple functional ligands enabling structural conjugation for photocatalytic conversion of CO2, where a fine balance in the proximity of two functional groups inside the molecular MOF catalyst is proven to result in cooperative photocatalytic activity for carbon dioxide conversion under visible light. We chose the amine (-NH2) functional group as the chemical functionality for incorporation into Re-MOF9,10,11,12,13 with ReI(CO)3(BPYDC)(Cl), BPYDC = 2,2′-bipyridine-5,5′-dicarboxylate, hereafter referred to as ReTC, which is covalently attached within a zirconium MOF based on a UiO-67-type structure14. The -NH2 functionalized Re-MOF having a controlled amount of -NH2 groups in mol% of X to the total amount of organic linkers is also denoted as Re-MOF-NH2 (X%) and Fig. 1 shows that the -NH2 functional groups contribute to make the molecular structure of ReTC asymmetric while it helps to form the CO2 intermediate within Re-MOF-NH2 (33%). MOFs are doped with9,10,11,12,13, built by one kind15,16,17,18,19,20,21 of molecular ligands, and/or combined with inorganic nanomaterials9, 12, 13, 22 to give varying levels of photocatalytic activities. Our work has been concentrated on realizing the molecular photocatalysts capable of giving unique cooperative functionality through structural conjugation of two different ligand centres within MOFs. Moreover, the combined experimental methods using inductively coupled plasma atomic emission spectroscopy (ICP-AES) analysis, X-ray diffraction (XRD) patterns, extended X-ray absorption fine structure (EXAFS) spectra, ultraviolet-visible (UV-vis) and in-situ infrared (IR) spectra, X-ray photoelectron spectroscopy (XPS) scanning electron microscope (SEM) and tunnelling electron microscope (TEM) images, and gas chromatograph data have been also used to probe the cooperative photocatalytic conversion mechanism of carbon dioxide on Re-MOF-NH2 having the conjugated ReTC and amine functionalized ligand centres.

Figure 1
figure1

Schematic diagram for the ─NH2-functionalized Re-MOF that converts CO2 to CO under visible light. (a,b) Zr6O4(OH)4(–CO2)12 secondary building units (SBUs) are combined with H2BPDC, H2ReTC and H2BPDC-(NH2)2 linkers to form Re-MOF-(NH2)(X%). The structure of Re-MOF-NH2 (X%) is shown. Twelve-coordinated Zr-based metal clusters are interconnected by BPDC, ReTC and BPDC-(NH2)2 linkers in a face-centred cubic array. Atom labelling scheme: C, black; O, red; Zr, blue polyhedra; Re, yellow; Cl, green; H atoms are omitted for clarity. (c) A schematic diagram of the photocatalytic CO2 conversion within Re-MOF-NH2 (X%).

Results and Discussion

Sample preparation

The Re-MOF-NH2 (X%) samples were prepared by varying the ratio of 2,2′-diaminobiphenyl-4,4′-dicarboxylic acid [H2BPDC-(NH2)2, Fig. S1 in the Supplementary Information] in the range of 0 mol% (-NH2-free Re-MOF) to 80 mol% (-NH2 at the maximal loading), where the experiment was carried out by increasing the amount of H2BPDC-(NH2)2 by 20, 40, 60, and 80 mol% compared to the total amount of H2ReTC and 4,4′-biphenyldicarboxylic acid (H2BPDC). The optimal amount of H2ReTC was determined to be 20 mol% in the preparation solution of Re-MOF-NH2 (X%) for CO2 conversion. The amount of H2ReTC (Fig. 1a) depends on the ratio of H2BPDC-(NH2)2. The protonated combinations of these three linkers and ZrCl4 were dissolved in a mixed solution of DMF/acetic acid in a 20-mL screw-capped vial, which were then heated at 85 °C for 12 hours. The orange suspensions produced in these processes were collected and washed three times with DMF using a centrifuge (8000 rpm for 10 minutes) and sonication. Then, it has been sequentially immersed in methanol for three 24-hour periods. Finally, the samples were activated by removing the solvent under vacuum for 12 hours at room temperature. These processes were found to result in Re-MOF-NH2 (X%) with X = 0, 33, 52, 68, and 80, which were identified (Fig. 2a) by the combined experiments using the inductively coupled plasma atomic emission spectroscopy (ICP-AES) and the 1H NMR spectroscopy of a digested solution of these samples (Fig. S2 and Table S1 in the Supplementary Information).

Figure 2
figure2

Structural analysis of Re-MOF-NH2 (X%). (a) Percent incorporation of BPDC-(HN2)2 in Re-MOF-NH2 (X%). (b) PXRD patterns of Re-MOF, Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%) in comparison with the simulated pattern of Re-MOF. (c) SEM images of Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%). (d) N2 adsorption isotherms for Re-MOF, Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%) at 77 K with adsorption and desorption points represented by closed circles and open circles, respectively (P/P 0 , relative pressure). (e) IR spectra of Re-MOF, Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%).

Structural characterization of Re-MOF-NH2 (X%)

The crystallinity of Re-MOF-NH2 (X%) was determined by the PXRD analysis (Figs 2b and S3 in the Supplementary Information), which gave sharp diffraction lines matching with those of the simulated pattern obtained from the experimental X-ray crystal diffraction data of Re-MOF. This gives a clear evidence for the preservation of the Re-MOF structural arrangement upon introduction of -NH2 functional groups at varied ratios and it is notable that all the samples were synthesized as nanoparticle morphologies. The representative scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images (Figs 2c and S4 in the Supplementary Information) of Re-MOF-NH2 (X%) demonstrate further that the size of the particles is approximately 300 nm and particles in all the samples have octahedral geometries, regardless of the amount of -NH2 functional groups incorporated. The permanent porosity of all the samples was found to be preserved, as confirmed by measurement of the N2 adsorption isotherms (Figs 2d and S5 in the Supplementary Information). The results showed Type I isotherms similar to those of Re-MOFs and UiO-679, 14. The Langmuir surface areas for Re-MOF, Re-MOF-NH2 (33%), Re-MOF-NH2 (52%), Re-MOF-NH2 (68%), and Re-MOF-NH2 (80%) were 2049, 1900, 1845, 1641, and 1500 m2 g−1, respectively. This difference in the surface areas was attributed to the amount of the -NH2 functional groups and the cramped pore structure in the presence of mixed functional groups.

Chemical analysis of Re-MOF-NH2 (X%)

The presence of -NH2 groups and ReTC in Re-MOF-NH2 (X%) was confirmed through IR spectra (Figs 2e and S6 in the Supplementary Information). The peak at 1655 cm−1 was assigned to the N-H bending mode of the -NH2 functional group, while those at 2022, 1920, and 1910 cm−1 correspond to the C≡O stretching ones of ReTC9, 23. In addition, the UV-vis spectra and XPS results of Re-MOF-NH2 (X%) support the presence of ReTC, BPDC-(NH2)2, and BPDC (Figs S7 and S8 in the Supplementary Information). The results show that chemical groups of NH2 and C≡O remain unchanged during synthesis. The ratios of functional group, determined by the 1H NMR spectroscopy of a digested solution (Figs 2a and S2 in the Supplementary Information), were shown to result in Re-MOF, Zr6O4(OH)4(ReTC)1.62(BPDC)4.38; Re-MOF-NH2 (33%), Zr6O4(OH)4(ReTC)1.62(BPDC-(NH2)2)1.98(BPDC)2.43; Re-MOF-NH2 (52%), Zr6O4(OH)4(ReTC)1.62(BPDC-(NH2)2)3.12(BPDC)1.44; Re-MOF-NH2 (68%), Zr6O4(OH)4(ReTC)1.26(BPDC-(NH2)2)4.08(BPDC)0.63; Re-MOF-NH2 (80%), Zr6O4(OH)4(ReTC)1.20(BPDC-(NH2)2)4.8.

Photocatalytic activity and stability of Re-MOF-NH2 (X%)

All Re-MOF-NH2 (X%) samples were explored for photocatalytic CO2 conversion rate under visible light. The samples, which were kept in vacuum overnight, were placed in a stainless-steel reactor and purged with CO2 and the conversion was initiated in the presence of triethylamine (TEA) under visible light (400–700 nm) using a 300 W Xenon arc lamp. The products produced through the photocatalytic reaction were analysed and quantified using the gas chromatography (GC) equipped with a flame ionization detector (FID) and normalized to the mass of the sample. Figure 3a shows photocatalytic activities of the Re-MOF-NH2 (X%) samples. The results show that the photocatalytic conversion is the highest when 33 mol% of -NH2 functional groups, denoted as Re-MOF-NH2 (33%), is incorporated. Moreover, its activity is proven to be 3-folds higher than that of Re-MOF with no -NH2 groups (Fig. 3a). In the absence of CO2 under a He atmosphere or with no ReTC, no CO generation was observed. The high activity was maintained for at least 6 hours while the molecular catalyst of H2ReTC was found to be deactivated within 1 hour9, 24, attributed to both ReTC and -NH2 functional groups covalently bound to the Re-MOF-NH2 (X%) framework. This signals that it prevents the prevailing deactivation pathway of dimerization commonly observed in photoactive molecular complexes. The stability of the Re-MOF-NH2 (33%) sample was also tested after the photocatalytic reaction. The PXRD, SEM and TEM analyses (Figs 3c and S9 in the Supplementary Information) show that their crystallinity and morphology are well maintained after the photocatalytic reaction. In addition, the IR spectra of Re-MOF-NH2 (33%) before and after the reaction (Fig. 3d) demonstrate that conjugation of ReTC and -NH2 functional groups preserves their chemical configurations after photocatalysis. This is a clear evidence that Re-MOF-NH2 (33%) enables to give a high conversion rate with the 100% selectivity for conversion of CO2 into CO under visible light while maintaining its crystal structure, morphology and chemical functionality after the photocatalytic reaction.

Figure 3
figure3

Photocatalytic activity and stability of Re-MOF-NH2 (X%). (a) Photocatalytic CO2-to-CO conversion activity under visible light (400–700 nm). (b) Photocatalytic CO2 conversion rate under visible light. (c) PXRD of Re-MOF-NH2 (33%) before and after the reaction. (d) IR spectra of Re-MOF-NH2 before and after the reaction.

EXAFS analysis to determine the cooperative mechanism for photocatalytic conversion

The photocatalytic activity in Re-MOF-NH2 (33%) should be related to the interaction between the ReTC and its neighbouring -NH2 functional group. The EXAFS analysis, which was performed for Re-MOF, Re-MOF-NH2 (33%), and Re-MOF-NH2 (80%) at the Pohang Accelerator Laboratory (PAL, Republic of Korea) on the 7D beamline at 3 GeV energy and the Re L3-edge spectra (E0 = 10207 eV), were also performed in the transmission mode25, 26 to measure the bonding length between the Re metal complex centre and the neighbouring atoms (Fig. 4a). The spectra were obtained through the Athena software based on the IFEFFIT library. The results demonstrate that Re-MOF without any -NH2 functional group gives two bonding lengths of 1.8 Å and 2.3 Å, corresponding to the bonds for Re-C and Re-Cl in ReTC, respectively. When the -NH2 functional groups are introduced into Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%), we found that the bond corresponding to Re–C was divided into two bonding lengths of 1.4 Å and 2.3 Å. This is because the configuration of carbonyl groups in ReTC becomes asymmetric upon the interaction with the -NH2 functional groups. Figure 4b gives the clear evidence that the distance between the Re centre and each carbonyl group becomes different. This asymmetric configuration of the carbonyl groups leads to the uneven electron distribution in ReTC for Re-MOF-NH2 (X%), which would contribute to polarization of ReTC and thus increase the partial electron affinity to make better chance converting CO2 to CO when carbamate is formed upon interaction with the -NH2 functional groups.

Figure 4
figure4

Characterization of the photocatalytic conversion mechanism in Re-MOF-NH2 (33%). (a) EXAFS spectra for Re-MOF, Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%). (b) Electrostatic potential diagram for Re-MOF-NH2 (33%) where the ReTC inside is asymmetric. (c) IR spectra of Re-MOF-NH2 (33%) under vacuum and CO2 atmosphere. (d) Difference IR spectra of Re-MOF, Re-MOF-NH2 (33%) and Re-MOF-NH2 (80%) in the presence of CO2. (e) Electrostatic potential diagram of the intermolecular stabilization of carbamate by the -NH2 functional groups before making CO in Re-MOF-NH2 (33%).

IR spectroscopy of Re-MOF-NH2 (X%) in the presence of CO2

The results via the EXAFS analysis could not explain why Re-MOF-NH2 (33%) gives a higher activity than Re-MOF-NH2 (80%). In this reason, we have investigated further the interaction between the -NH2 functional group and CO2 using the in-situ IR spectroscopy, where each sample of Re-MOF, Re-MOF-NH2 (33%), and Re-MOF-NH2 (80%) was kept inside the chamber and the IR spectra were measured with the chamber under vacuum or filled with CO2. The IR spectra of Re-MOF-NH2 (33%) are shown in Fig. 4c and those of Re-MOF and Re-MOF-NH2 (80%) are shown in Fig. S10a,b in the Supplementary Information. Figure 4d also show the difference spectra of each sample in the presence of CO2. The results give that differences in the spectra are evident only in Re-MOF-NH2 (33%) and that the most pronounced peaks are at 1596 and 1420 cm−1 corresponding to the asymmetric and symmetric COO- stretching vibrations, respectively27. This shows that amine functional groups helped to result in the intermolecular stabilization of carbamate as shown in Fig. 4e.

Theoretical investigation for photocatalytic cooperative conversion mechanism of CO2 into CO

Figure 5a shows the stable CO2–to–CO photochemical reduction pathway determined by using density functional theory (DFT) calculations. The first reaction corresponding to step i occurs via formation of the carbamate complex that is initiated by adsorption of CO2 into the -NH2 ligand, where the OH of the carboxylic group forms a week hydrogen bonding interaction with the Cl attached in a neighboring ReTC ligand (Fig. S11a,b). Steps ii and iii in Fig. 5a give clear evidences that the electron uptake from TEA spontaneously occurs after the photo-excitation process. Due to the additional electron injected in the ReTC, the Re center attacks the electrophilic carbonyl carbon of a nearby –COOH accompanying with the protonation of amine group where the proton is from TEA+. This leads to the migration of the –COOH group to the ReTC ligand along with the regeneration of -NH2 group (step iv). It is notable that the Re center then forms a 7-coordinate system (Fig. S11c). Subsequently, upon the second photo-excitation process (step v) followed by the second electron and proton uptake from TEA (step vi and vii), the –COOH group is transformed to the final product of CO and the byproduct of H2O at the ReTC ligand. Consequently, these support that the formation of the carbamate intermediate in the presence of the -NH2 ligand is responsible to give efficient production of CO from CO2 in Re-MOF-NH2 via the synergistic interaction of two different ReTC and -NH2 ligands that is not available in Re-MOF having no adjacent amine moiety. Furthermore, the corresponding energy diagram from step i to viii (Fig. 5b) gives more clarifications that the production of CO upon absorption of two photons in visible light is energetically favorable in the presence of the -NH2 ligand and the ReTC ligand in the neighboring sites. It is also notable that the structural details involving in the photocatalytic reaction have been summarized in Fig. S12.

Figure 5
figure5

Proposed amine-assisted synergetic photocatalytic conversion mechanism of CO2 into CO based on DFT energetics. (a) The reaction paths for photocatalytic conversion of CO2 into CO; (i) the carbamate formation, (ii) the 1st photo-excitation, (iii) the 1st electron transfer from TEA, (iv) the nucleophilic attack of Re to COOH accompanied with the 1st proton transfer from TEA+, (v) the 2nd photo-excitation, (vi) the 2nd electron transfer from TEA, (vii) the H2O formation accompanied with the 2nd proton transfer from TEA+, and (viii) the CO formation. (b) The calculated energies from stage i to stage viii. The results demonstrate that the production of CO upon absorption of two photons in visible light is energetically favorable in the presence of the –NH2 ligand and the ReTC ligand in the neighboring sites.

On summary, we designed the chemical environment of a molecular photocatalyst covalently bound to the MOFs through incorporation of the -NH2 functionalized ligand resulting in a conjugated structure of the neighbouring Re metal complex ligand. The ratio of the -NH2 functional groups was varied from 0 to 80 mol% in Re-MOF, and the results showed that the photocatalytic CO2 to CO conversion reached the highest activity when 33 mol% of the -NH2 functional groups was incorporated. In addition, the EXAFS and IR spectra supported the cooperative reaction mechanism in Re-MOF-NH2 (33%). These results revealed that the -NH2 functional groups induced the different bond lengths for Re-CO in ReTC while they help to make the intermolecular stabilization of carbamate with CO2, thus increasing its photocatalytic activity.

Methods

Synthesis of Re-MOF-NH2 (X%)

We have prepared the ligand and metal units for the MOF separately. First, ZrCl4 (9.3 mg, 0.04 mmol) was dissolved in N,N’-dimethylformamide (DMF, 5 mL) with acetic acid (0.5 mL) in a 20 mL glass vial. The ligand was prepared using a solution of rhenium ligands (4.4 mg, 0.008 mmol), H2-BPDC-(NH2)2 (0, 20, 40, 60, and 80 mol% of H2ReTC), biphenyl-4,4′-dicarboxylic acid (adding up to a total amount of 0.040 mmol of organic linker) and DMF (5 mL). Then, the well-dispersed ligand solution was poured into the metal solution, and the sealed vial was placed in an 85 °C oven for 12 hours without light. Then, it was cooled to room temperature and the solid was separated with a centrifuge (8000 rpm for 10 minutes). Next, it was washed with DMF once and methanol three times. After washing, the product was dried in a vacuum oven.

Photocatalytic measurements

The photocatalytic CO2 conversion experiments were conducted using a stainless-steel reactor. To accomplish this, 5 mg of the sample was placed on a glass holder and the reactor was fastened with screws. To remove solvent and air, the reactor was kept under vacuum overnight. Then, the reactor was purged using CO2 gas (99.9%) for 30 minutes. Next, 0.1 mL of trimethylamine (TEA) was injected into the chamber, which was kept at 40 °C for approximately 15 minutes to vaporize the TEA. The sample was irradiated through the quartz glass using a 300 W Xenon arc lamp (ORIEL) equipped with an IR water filter and a UV filter to obtain visible light ranging from 400 to 700 nm. The evolved gas was sampled using an airtight sample-lock syringe (Hamilton, 81256) and was injected into a gas chromatography column (Shimadzu, GC-2014A) and passed through a HayeSep Q Porapak Q column with helium carrier gas. The gas was detected using a flame ionization detector (FID) and a methanizer.

EXAFS analysis

The extended X-ray absorption fine structure (EXAFS) analysis was conducted at the Pohang Accelerator Laboratory (PAL) on the 7D beamline at 3 GeV energy. A Si(111) double crystal monochromator was used to monochromatize the synchrotron radiation and the Re L3-edge spectra (E0 = 10207 eV) were obtained in transmission mode. To minimize contamination of higher harmonics, the incident beam was detuned by 10%. Also, the intensity of the beam was monitored by using a N2-filled IC SPEC ionization chamber. This experiment was conducted with 0.4 eV steps between 10515 and 10585 eV, 30 eV steps between 10585 and 11707 eV, and 50 eV steps between 11707 and 12007 eV with 2, 3, and 3 seconds per the point, respectively. Then, the spectra were obtained through the Athena software based on the IFEFFIT library.

In-situ IR Spectroscopy

The in-situ IR spectroscopy was measured by the FT-IR spectrometer equipped with a gas chamber. The Re-MOF-NH2 (X%) samples were diluted with the KBr powder and placed in the sample holder. Then, before measuring the IR spectrum in vacuum, the chamber was evacuated for 30 minutes. Next, the chamber was filled with CO2 gas for 30 minutes to measure the IR signal under CO2 atmosphere. Each sample was measured with a 4 cm−1 spectral resolution and a 4 mm/cm scanning speed.

Computational Details

DFT calculations were performed using the Jaguar 8.9 software28 for theoretical reaction energetics. We used the range-separated exchange-correlation functional of CAM-B3LYP29 the reliable description of band edge positions, and used the LACVP basis set30. Also, the ground electronic and geometric structures were fully optimized under constraints with the fixed coordinates of oxygen atoms in terminal carboxylic functional groups from experimentally observed atomic positions. For the steps involving electron/proton transfer, the electron transfer is determined on consideration of coupling with the oxidation of TEA corresponding to the reaction of TEA → TEA+ + −e while the proton is transferred from the alpha carbon of TEA+. The photo-excitation energy is calculated using the HOMO-LUMO gap.

References

  1. 1.

    Gade, L. H. & Hofmann, P. Molecular Catalysts: Structure and Functional Design (Wiley, 2014).

  2. 2.

    Okada, Tatsuhiro & Kaneko, Masao. Molecular Catalysts for Energy Conversion (Springer, 2009).

  3. 3.

    Blakemore, J. D., Crabtree, R. H. & Brudvig, G. W. Molecular Catalysts for Water Oxidation. Chem. Rev. 115, 12974–13005 (2015).

    CAS  Article  PubMed  Google Scholar 

  4. 4.

    White, J. L. et al. Light-Driven Heterogeneous Reduction of Carbon Dioxide: Photocatalysts and Photoelectrodes. Chem. Rev. 115, 12888–12935 (2015).

    CAS  Article  PubMed  Google Scholar 

  5. 5.

    Berardi, S. et al. Molecular Artificial Photosynthesis. Chem. Soc. Rev. 43, 7501–7519 (2014).

    CAS  Article  PubMed  Google Scholar 

  6. 6.

    Aresta, M., Dibenedetto, A. & Angelini, A. Catalysis for the Valorization of Exhaust Carbon: from CO2 to Chemicals, Materials, and Fuels. Technological Use of CO2. Chem Rev. 114, 1709–1742 (2013).

    Article  PubMed  Google Scholar 

  7. 7.

    Schulz, H. Short History and Present Trends of Fischer–Tropsch Synthesis. App Catal A: General. 186, 3–12 (1999).

    CAS  Article  Google Scholar 

  8. 8.

    Centi, G., Quadrelli, E. A. & Perathoner, S. Catalysis for CO2 Conversion: A Key Technology for Rapid Introduction of Renewable Energy in the Value Chain of Chemical Industries. Energy & Environ Sci. 6, pp. 1711–1731 (2013).

  9. 9.

    Choi, K. et al. Plasmon-Enhanced Photocatalytic CO2 Conversion within Metal-Organic Frameworks Under Visible Light. J. Am. Chem. Soc., doi:10.1021/jacs.6b11027.

  10. 10.

    Wang, C., Xie, Z., deKrafft, K. E. & Lin, W. Doping Metal-Organic Frameworks for Water Oxidation, Carbon Dioxide Reduction, and Organic Photocatalysis. J. Am. Chem. Soc. 133, 13445–13454 (2011).

    CAS  Article  PubMed  Google Scholar 

  11. 11.

    Blake, A. J. et al. Photoreactivity Examined through Incorporation in Metal-Organic Frameworks. Nat. Chem. 2, 688–694 (2010).

    CAS  Article  PubMed  Google Scholar 

  12. 12.

    Zhang, T. & Lin, W. Metal–Organic Frameworks for Artificial Photosynthesis and Photocatalysis. Chem. Soc. Rev. 43, 5982–5993 (2014).

    CAS  Article  PubMed  Google Scholar 

  13. 13.

    Wang, J., Wang, C. & Lin, W. Metal–Organic Frameworks for Light Harvesting and Photocatalysis. ACS Catalysis 2, 2630–2640 (2012).

    CAS  Article  Google Scholar 

  14. 14.

    Cavka, J. H. et al. A New Zirconium Inorganic Building Brick Forming Metal Organic Frameworks with Exceptional Stability. J. Am. Chem. Soc. 130, 13850–13851 (2008).

    Article  PubMed  Google Scholar 

  15. 15.

    Lee, Y., Kim, S., Kang, J. K. & Cohen, S. M. Photocatalytic CO2 Reduction by a Mixed Metal (Zr/Ti), Mixed Ligand Metal–Organic Framework under Visible Light Irradiation. Chem. Commun. 51, 5735–5738 (2015).

    CAS  Article  Google Scholar 

  16. 16.

    Fei, H., Sampson, M. D., Lee, Y., Kubiak, C. P. & Cohen, S. M. Photocatalytic CO2 Reduction to Formate Using a Mn(I) Molecular Catalyst in a Robust Metal-Organic Framework. Inorg. Chem. 54, 6821–6828 (2015).

    CAS  Article  PubMed  Google Scholar 

  17. 17.

    Fu, Y. et al. An Amine-Functionalized Titanium Metal-Organic Framework Photocatalyst with Visible-Light-Induced Activity for CO2 Reduction. Angew. Chem. Int. Ed. 51, 3364–3367 (2012).

    CAS  Article  Google Scholar 

  18. 18.

    Wang, D., Huang, R., Liu, W., Sun, D. & Li, Z. Fe-Based MOFs for Photocatalytic CO2 Reduction: Role of Coordination Unsaturated Sites and Dual Excitation Pathways. ACS Catal. 4, 4254–4260 (2014).

    CAS  Article  Google Scholar 

  19. 19.

    Wang, S., Yao, W., Lin, J., Ding, Z. & Wang, X. Cobalt Imidazolate Metal-Organic Frameworks Photosplit CO2 under Mild Reaction Conditions. Angew. Chem. Int. Ed. 53, 1034–1038 (2014).

    CAS  Article  Google Scholar 

  20. 20.

    Easun, T. L. et al. Photochemistry in a 3D Metal-Organic Framework (MOF): Monitoring Intermediates and Reactivity of the Fac-to-Mer Photoisomerization of Re(diimine)(CO)3Cl Incorporated in a MOF. Inorg. Chem. 53, 2606–2612 (2014).

    CAS  Article  PubMed  Google Scholar 

  21. 21.

    Hod, I. et al. Fe-Porphyrin Based MOF Films as High-Surface-Concentration, Heterogeneous Catalysts for Electrochemical Reduction of CO2. ACS Catal. 5, 6302–6309 (2015).

    CAS  Article  Google Scholar 

  22. 22.

    Wang, C., Krafft, K. E. & Lin, W. Pt Nanoparticles@Photoactive Metal–Organic Frameworks: Efficient Hydrogen Evolution via Synergistic Photoexcitation and Electron Injection. J. Am. Chem. Soc. 134, 7211–7214 (2012).

    CAS  Article  PubMed  Google Scholar 

  23. 23.

    Zhao, H. C. et al. Investigation of Monomeric versus Dimeric fac-Rhenium(I) Tricarbonyl Systems Containing the Noninnocent 8-Oxyquinolate Ligand. Organometallics 32, 1832–1841 (2013).

    CAS  Article  Google Scholar 

  24. 24.

    Benson, E. E. & Kubiak, C. P. Structural Investigations into the Deactivation Pathway of the CO2 Reduction Electrocatalyst Re(bpy)(CO)3Cl. Chem. Commun. 48, 7374–7376 (2012).

    CAS  Article  Google Scholar 

  25. 25.

    Surblé, S., Millange, F., Serre, C., Férey, G. & Walton, R. I. An EXAFS Study of the Formation of a Nanoporous Metal-Organic Framework: Evidence for the Retention of Secondary Building Units during Synthesis. Chem. Commun. 14, 1518–1520 (2006).

    Article  Google Scholar 

  26. 26.

    Macnaughtan, M. L., Soo, H. S. & Frei, H. Binuclear ZrOCo Metal-to-Metal Charge-Transfer Unit in Mesoporous Silica for Light-Driven CO2 Reduction to CO and Formate. J. Phys. Chem. C 118, 7874–7885 (2014).

    CAS  Article  Google Scholar 

  27. 27.

    Hahn, M. W., Jelic, J., Berger, E., Reuter, K., Jentys, A. & Lercher, J. A. Role of Amine Functionality for CO2 Chemisorption on Silica. J. Phys. Chem. B 120, 1988–1995 (2016).

    CAS  Article  PubMed  Google Scholar 

  28. 28.

    Bochevarov, A. D. et al. Jaguar: A High-Performance Quantum Chemistry Software Program with Strengths in Life and Materials Sciences. Int. J. Quantum Chem. 113, 2110–2142 (2013).

    CAS  Article  Google Scholar 

  29. 29.

    Yanai, T., Tew, D. P. & Handy, N. C. A New Hybrid Exchange–Correlation Functional Using the Coulomb-Attenuating Method (CAM-B3LYP). Chem. Phys. Lett. 393, 51–57 (2004).

    ADS  CAS  Article  Google Scholar 

  30. 30.

    Hay, P. J. & Wadt, W. R. Ab Initio Effective Core Potentials for Molecular Calculations: Potentials for K to Au Including the Outermost Core Orbitals. J. Chem. Phys. 82, 299–310 (1985).

    ADS  CAS  Article  Google Scholar 

Download references

Acknowledgements

This work was mainly supported by the Global Frontier R&D Program (2013M3A6B1078884) of the Center for Hybrid Interface Materials (HIM), the Korea Center of the Artificial Photosynthesis (2009-0093881), and by the National Research Foundation of Korea (2016R1A2B3012053) funded by the Ministry of Science, ICT & Future Planning. K.M.C. acknowledges support from the Basic Science Research Program through the National Research Foundation of Korea (2016R1C1B1010781).

Author information

Affiliations

Authors

Contributions

U.J.R., K.M.C. and J.K.K. designed the experiments. U.J.R. and S.J.K. carried out the experiments and analysis. H.K.L. and H.J.K. carried out the theoretical calculations. H.J.K., K.M.C. and J.K.K. wrote the manuscript on discussions with U.J.R., S.J.K., and H.K.L.

Corresponding authors

Correspondence to Hyungjun Kim or Kyung Min Choi or Jeung Ku Kang.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ryu, U.J., Kim, S.J., Lim, HK. et al. Synergistic interaction of Re complex and amine functionalized multiple ligands in metal-organic frameworks for conversion of carbon dioxide. Sci Rep 7, 612 (2017). https://doi.org/10.1038/s41598-017-00574-1

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing