Abstract
Chern insulators, which are the lattice analogues of the quantum Hall states, can potentially manifest high-temperature topological orders at zero magnetic field to enable next-generation topological quantum devices1,2,3. Until now, integer Chern insulators have been experimentally demonstrated in several systems at zero magnetic field3,4,5,6,7,8, whereas fractional Chern insulators have been reported in only graphene-based systems under a finite magnetic field9,10. The emergence of semiconductor moiré materials11, which support tunable topological flat bands12,13, provides an opportunity to realize fractional Chern insulators13,14,15,16. Here we report thermodynamic evidence of both integer and fractional Chern insulators at zero magnetic field in small-angle twisted bilayer MoTe2 by combining the local electronic compressibility and magneto-optical measurements. At hole filling factor ν = 1 and 2/3, the system is incompressible and spontaneously breaks time-reversal symmetry. We show that they are integer and fractional Chern insulators, respectively, from the dispersion of the state in the filling factor with an applied magnetic field. We further demonstrate electric-field-tuned topological phase transitions involving the Chern insulators. Our findings pave the way for the demonstration of quantized fractional Hall conductance and anyonic excitation and braiding17 in semiconductor moiré materials.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on SpringerLink
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
Source data are provided with this paper. All other data are available from the corresponding authors upon reasonable request.
References
Haldane, F. D. M. Model for a quantum Hall effect without Landau levels: condensed-matter realization of the “parity anomaly”. Phys. Rev. Lett. 61, 2015–2018 (1988).
Hasan, M. Z. & Kane, C. L. Colloquium: topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).
Liu, C.-X., Zhang, S.-C. & Qi, X.-L. The quantum anomalous Hall effect: theory and experiment. Annu. Rev. Condens. Matter Phys. 7, 301–321 (2016).
Chang, C.-Z. et al. Experimental observation of the quantum anomalous Hall effect in a magnetic topological insulator. Science 340, 167–170 (2013).
Serlin, M. et al. Intrinsic quantized anomalous Hall effect in a moiré heterostructure. Science 367, 900–903 (2020).
Chen, G. et al. Tunable correlated Chern insulator and ferromagnetism in a moiré superlattice. Nature 579, 56–61 (2020).
Deng, Y. et al. Quantum anomalous Hall effect in intrinsic magnetic topological insulator MnBi2Te4. Science 367, 895–900 (2020).
Li, T. et al. Quantum anomalous Hall effect from intertwined moiré bands. Nature 600, 641–646 (2021).
Spanton, E. M. et al. Observation of fractional Chern insulators in a van der Waals heterostructure. Science 360, 62–66 (2018).
Xie, Y. et al. Fractional Chern insulators in magic-angle twisted bilayer graphene. Nature 600, 439–443 (2021).
Mak, K. F. & Shan, J. Semiconductor moiré materials. Nat. Nanotechnol. 17, 686–695 (2022).
Wu, F., Lovorn, T., Tutuc, E., Martin, I. & MacDonald, A. H. Topological insulators in twisted transition metal dichalcogenide homobilayers. Phys. Rev. Lett. 122, 086402 (2019).
Devakul, T., Crépel, V., Zhang, Y. & Fu, L. Magic in twisted transition metal dichalcogenide bilayers. Nat. Commun. 12, 6730 (2021).
Li, H., Kumar, U., Sun, K. & Lin, S.-Z. Spontaneous fractional Chern insulators in transition metal dichalcogenide moiré superlattices. Phys. Rev. Res. 3, L032070 (2021).
Crépel, V. & Fu, L. Anomalous Hall metal and fractional Chern insulator in twisted transition metal dichalcogenides. Phys. Rev. B 107, L201109 (2022).
Morales-Durán, N. et al. Pressure-enhanced fractional Chern insulators in moiré transition metal dichalcogenides along a magic line. Preprint at https://arxiv.org/abs/2304.06669 (2023).
Nayak, C., Simon, S. H., Stern, A., Freedman, M. & Sarma, S. D. Non-Abelian anyons and topological quantum computation. Rev. Mod. Phys. 80, 1083–1159 (2008).
Sheng, D. N., Gu, Z.-C., Sun, K. & Sheng, L. Fractional quantum Hall effect in the absence of Landau levels. Nat. Commun. 2, 389 (2011).
Neupert, T., Santos, L., Chamon, C. & Mudry, C. Fractional quantum Hall states at zero magnetic field. Phys. Rev. Lett. 106, 236804 (2011).
Tang, E., Mei, J.-W. & Wen, X.-G. High-temperature fractional quantum Hall states. Phys. Rev. Lett. 106, 236802 (2011).
Regnault, N. & Bernevig, B. A. Fractional Chern insulator. Phys. Rev. X 1, 021014 (2011).
Qi, X.-L. Generic wave-function description of fractional quantum anomalous Hall states and fractional topological insulators. Phys. Rev. Lett. 107, 126803 (2011).
Wu, Y.-L., Bernevig, B. A. & Regnault, N. Zoology of fractional Chern insulators. Phys. Rev. B 85, 075116 (2012).
Parameswaran, S. A., Roy, R. & Sondhi, S. L. Fractional quantum Hall physics in topological flat bands. C. R. Phys. 14, 816–839 (2013).
Zhang, Y.-H., Mao, D., Cao, Y., Jarillo-Herrero, P. & Senthil, T. Nearly flat Chern bands in moiré superlattices. Phys. Rev. B 99, 075127 (2019).
Abouelkomsan, A., Liu, Z. & Bergholtz, E. J. Particle-hole duality, emergent Fermi liquids, and fractional Chern insulators in moiré flatbands. Phys. Rev. Lett. 124, 106803 (2020).
Ledwith, P. J., Tarnopolsky, G., Khalaf, E. & Vishwanath, A. Fractional Chern insulator states in twisted bilayer graphene: an analytical approach. Phys. Rev. Res. 2, 023237 (2020).
Repellin, C. & Senthil, T. Chern bands of twisted bilayer graphene: fractional Chern insulators and spin phase transition. Phys. Rev. Res. 2, 023238 (2020).
Wilhelm, P., Lang, T. C. & Läuchli, A. M. Interplay of fractional Chern insulator and charge density wave phases in twisted bilayer graphene. Phys. Rev. B 103, 125406 (2021).
Mai, P., Feldman, B. E. & Phillips, P. W. Topological Mott insulator at quarter filling in the interacting Haldane model. Phys. Rev. Res. 5, 013162 (2023).
Anderson, E. et al. Programming correlated magnetic states via gate controlled moiré geometry. Science 81, 6655 (2023)
Xia, Z. et al. Optical readout of the chemical potential of two-dimensional electrons. Preprint at https://arxiv.org/abs/2304.09514 (2023).
Zhu, J., Su, J.-J. & MacDonald, A. H. Voltage-controlled magnetic reversal in orbital Chern insulators. Phys. Rev. Lett. 125, 227702 (2020).
Reddy, A. P., Allsallom, F. F., Zhang. Y., Devakul, T. & Fu, L. Fractional quantum anomalous Hall states in twisted bilayer MoTe2 and WSe2. Preprint at https://arxiv.org/abs/2304.12261 (2023).
Wang, C. et al. Fractional Chern insulator in twisted bilayer MoTe2. Preprint at https://arxiv.org/abs/2304.11864 (2023).
Xu, Y. et al. A tunable bilayer Hubbard model in twisted WSe2. Nat. Nanotechnol. 17, 934–939 (2022).
Devakul, T. & Fu, L. Quantum anomalous Hall effect from inverted charge transfer gap. Phys. Rev. X 12, 021031 (2022).
Xie, Y.-M., Zhang, C.-P., Hu, J.-X., Mak, K. F. & Law, K. T. Valley-polarized quantum anomalous Hall state in moiré MoTe2/WSe2 heterobilayers. Phys. Rev. Lett. 128, 026402 (2022).
Pan, H., Xie, M., Wu, F. & Das Sarma, S. Topological phases in AB-stacked MoTe2/WSe2: \({{\mathbb{Z}}}^{2}\) topological insulators, Chern insulators, and topological charge density waves. Phys. Rev. Lett. 129, 056804 (2022).
Cai, J. et al. Signatures of fractional quantum anomalous Hall states in twisted MoTe2. Nature https://doi.org/10.1038/s41586-023-06289-w (2023).
Foutty, B. A. et al. Mapping twist-tuned multi-band topology in bilayer WSe2. Preprint at https://arxiv.org/abs/2304.09808 (2023).
Park, H. et al. Observation of fractionally quantized anomalous Hall effect. Nature https://doi.org/10.1038/s41586-023-06536-0 (2023).
Acknowledgements
We thank L. Fu for the discussions. This work was supported by the US Department of Energy, Office of Science, Basic Energy Sciences, under award no. DE-SC0019481 (thermodynamic studies), the Air Force Office of Scientific Research under award no. FA9550-20-1-0219 (magneto-optical studies), and the Cornell University Materials Research Science and Engineering Center under award no. DMR-1719875 (device fabrication). This work was also funded in part by the Gordon and Betty Moore Foundation (grant doi: https://doi.org/10.37807/GBMF11563) and performed in part at the Cornell NanoScale Facility, an NNCI member supported by the NSF grant NNCI-2025233. The growth of the hBN crystals was supported by the Elemental Strategy Initiative of MEXT, Japan, and CREST (JPMJCR15F3), JST. We also acknowledge support from the David and Lucille Packard Fellowship (K.F.M.) and the Swiss National Science Foundation (P.K.).
Author information
Authors and Affiliations
Contributions
Y.Z. and Z.X. fabricated the devices, performed the measurements and analysed the data. K.K., P.K., J.Z. and C.V. provided data from additional devices. K.W. and T.T. grew the bulk hBN crystals. Y.Z., Z.X., K.F.M. and J.S. designed the scientific objectives. K.F.M. and J.S. oversaw the project. All authors discussed the results and commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Calibration of the moiré density.
a, Dependence of the optical reflectance spectrum of the sensor on the sample-sensor bias voltage Vsample (sensor grounded); the top and bottom gate voltages are kept constant; the sample is heavily hole-doped; the magnetic field is fixed at 8.8 T. Clear quantum oscillations in the attractive polaron resonance energy and amplitude are observed with hole doping due to the formation of spin-valley-polarized Landau levels at high magnetic fields. b, Dependence of the integrated attractive polaron amplitude (over the spectral window bound by the dashed lines in a) on Vs (blue curve). The orange curve represents the smooth background. We show data between −0.6 and −1 V, for which the sensor is heavily hole-doped and the Landau levels are two-fold degenerate. c, Oscillation amplitude (after removal of the smooth background) as a function of Vs. The average distance between adjacent amplitude peaks at high hole doping densities is 82.5 mV; this corresponds to a change in the sensor doping density of 4.26 × 1011 cm−2 based on the known Landau level degeneracy (= 2) in this density range. The data allow us to accurately determine the sample-to-sensor geometrical capacitance Cs ≈ 8.3 ± 0.3 μFcm−2. d, Centre-of-mass filling factor for the ν = 1 state as a function of the bottom gate voltage (Vbg) and the sample-sensor bias voltage (Vs). The slope determines the capacitance ratio \(\frac{{C}_{s}}{{C}_{{bg}}}=2.17\pm 0.01\). Combined with the calibration of Cs, the moiré density can be determined nM = (3.2 ± 0.2) × 1012 cm−2 (see Methods for details).
Extended Data Fig. 2 Determination of the chemical potential jump and incompressibility peak in filling factors.
a, Filling-factor dependent incompressibility at 1.6 K, zero electric field and B = 1 T. The incompressibility peak above the baseline (blue dashed lines) is integrated to obtain the chemical potential jump at ν = 2/3 and 1. This procedure effectively removes the negative incompressibility background in the chemical potential measurements. The same incompressibility peak (above the background) is used to calculate the centre-of-mass filling factor for the ν = 2/3 and 1 states (green arrows). Gaussian fit to the data (red dashed lines) near the local incompressibility peak at ν = 2/3 and 1 yields nearly identical peak fillings (red arrows). The vertical dashed lines denote the filling range for both analyses, the centre of which is chosen at the local incompressibility maximum (black arrows). b, Peak position of the incompressible states extracted from the Gaussian fit as a function of magnetic field (the analysis used the same data set as that in Fig. 2). The error bars are the fit uncertainty. Similar quantum numbers are obtained from the linear fits as in the main text.
Extended Data Fig. 3 Determination of the quantum numbers at small magnetic fields.
a–c, Electronic incompressibility versus the filling factor and magnetic field (0–3 T) near ν = 1 (a) and ν = 2/3 (b) at zero interlayer potential difference, and near ν = 1 at large interlayer potential difference (c). Data were obtained from the same location of the sample as in the main text. d–f, Incompressibility peak position versus magnetic field extracted from the centre-of-mass analysis. Linear fits in d and e yield a slope of 0.67 ± 0.08 for ν = 2/3 and 1.1 ± 0.1 for ν = 1, consistent with the emergence of fractional and integer CIs, respectively, in the zero-magnetic-field limit. The red line in f marks a non-topological Mott insulator that does not disperse with applied magnetic field. Error bars denote the combined systematic and random uncertainties of the measurements.
Extended Data Fig. 4 Thermodynamic equation of state at varying magnetic fields.
The filling factor dependent chemical potential near zero electric field is shown. The curves are vertically displaced for clarity. We subtract the B = 0 T curve from the B = 3 T curve to obtain the plot in Fig. 2d.
Extended Data Fig. 5 Electric-field dependent optical reflectance and spontaneous MCD spectra of tMoTe2 at ν = 1.
a, Optical reflectance spectrum (unpolarized) as a function of vertical electric field. The bonding (about 1.12 eV) and anti-bonding (about 1.14 eV) features in the layer-hybridized region evolve into the neutral exciton feature (about 1.13 eV) of one layer in the layer-polarized region. The red dashed lines denote the critical electric fields that separate the layer-hybridized and layer-polarized regions. We trace the highest reflectance amplitude to obtain the 2D map in Fig. 3c. b, Strong spontaneous MCD is observed only in the layer-hybridized region. The MCD spectrum between the black dashed lines is integrated to obtain the 2D map in Fig. 3b.
Extended Data Fig. 6 Dual-gated tMoTe2 devices for chemical potential measurements.
a, Schematic structure of dual-gated devices with a monolayer WSe2 sensor inserted between the top gate and the twisted bilayer MoTe2 sample. In addition to the structure shown in Fig. 1b, the device has contact gates to both the metal-sample and metal-sensor contacts. In this experiment, a large negative voltage is applied to the contact gates to heavily hole-dope the contact regions in order to achieve good electrical contacts for the chemical potential measurements. b, Optical micrograph of the device studied in the main text. The red and blue lines outline the boundaries of the twisted bilayer MoTe2 sample and the WSe2 sensor, respectively. The results presented in the main text and in Extended Data Fig. 5 were obtained at the black spot. Results obtained at the red and blue locations are shown in Extended Data Fig. 7.
Extended Data Fig. 7 Integer and fractional CIs at other sample locations.
a,b, Electronic incompressibility versus the filling factor and the out-of-plane electric field at zero magnetic field for the red (a) and blue (b) spots in Extended Data Fig. 6b. Similar to the black spot, incompressible states at ν = 1 and 2/3 are observed in the layer-hybridized region. The gate capacitances were measured locally using the sensor’s quantum oscillations as described in Methods and Extended Data Fig. 1, allowing accurate determination of the local twist angle. c–f, Linear fits of the magnetic-field dependence of the incompressibility peak filling factor at the red spot yield a slope of 0.63 ± 0.08 for ν = 2/3 and 1.08 ± 0.09 for ν ± 1, consistent with the emergence of FCI and CI.
Extended Data Fig. 8 Spontaneous MCD in samples with different twist angles.
Integrated MCD as a function of filling factor and electric field in 3 different samples with twist angles of 2.1 degrees (a), 2.7 degrees (b) and 4.6 degrees (c). All data were acquired at T = 1.6 K and B = 20 mT. The incident light was kept below 20 nW on the sample. Ferromagnetism is observed over a wide range of twist angles.
Extended Data Fig. 9 Integer and fractional CIs in other samples.
a,b, Incompressibility as a function of ν and B in samples with twist angles of 2.1 degrees (a) and 2.7 degrees (b). The nearly horizontal stripes in b are the quantum oscillations of the graphite gate electrodes. c,d, Linear fits of the extracted centre-of-mass fillings for the CIs in a,b. Integer CIs at ν = 1 are observed in all samples while FCIs at ν = 2/3 are observed only in samples with twist angles of 2.7 and 3.4 degrees.
Extended Data Fig. 10 Independent calibration of the ν = 1 state quantum numbers.
Electric-field and filling-factor dependent incompressibility at 8.8 T and 4 K. A clear upshift in the filling factor for the ν = 1 incompressible state is observed only in the layer-hybridized region (red dashed lines denoting the boundaries between the layer-hybridized and layer-polarized regions). The upshift reflects the emergence of the CI (the correlated insulator in the layer-polarized region is non-topological). The average centre-of-mass filling shift from the non-topological state (marked by the black dashed lines) is 0.070 ± 0.006 at 8.8 T. This corresponds to \(t=\frac{h}{e}\frac{dv}{dB}{n}_{M}=\frac{h}{e}\frac{0.070\pm 0.006}{8.8}{n}_{M}=1.1\,\pm \,0.1\) (see Methods). No non-topological insulating state at ν = 2/3 can be identified.
Supplementary information
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Zeng, Y., Xia, Z., Kang, K. et al. Thermodynamic evidence of fractional Chern insulator in moiré MoTe2. Nature 622, 69–73 (2023). https://doi.org/10.1038/s41586-023-06452-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-023-06452-3
This article is cited by
-
Nonlinear physics of moiré superlattices
Nature Materials (2024)
-
All-electric writing of a chiral quantum memory
Nature Materials (2024)
-
Charge-transfer contacts for the measurement of correlated states in high-mobility WSe2
Nature Nanotechnology (2024)
-
Fractional quantum anomalous Hall effect in multilayer graphene
Nature (2024)
-
The fractional quantum anomalous Hall effect
Nature Reviews Materials (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.