Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Reply to: Perovskite decomposition and missing crystal planes in HRTEM

The Original Article was published on 09 June 2021

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.

from$8.99

All prices are NET prices.

Fig. 1: TEM analysis of quantum dots in perovskite.

Data availability

The data within this paper and findings of this study are available from the corresponding author upon reasonable request.

References

  1. 1.

    Ning, Z. et al. Quantum-dot-in-perovskite solids. Nature 523, 324–328 (2015).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Deng, Y.-H. Perovskite decomposition and missing crystal planes in HRTEM. Nature https://doi.org/10.1038/s41586-021-03423-4 (2021).

  3. 3.

    Chen, S. et al. Atomic scale insights into structure instability and decomposition pathway of methylammonium lead iodide perovskite. Nat. Commun. 9, 4807 (2018).

    ADS  Article  Google Scholar 

  4. 4.

    Zhu, H. et al. Lead halide perovskite nanowire lasers with low lasing thresholds and high quality factors. Nat. Mater. 14, 636–642 (2015).

    ADS  CAS  Article  Google Scholar 

  5. 5.

    Gao, L. et al. Passivated single-crystalline CH3NH3PbI3 nanowire photodetector with high detectivity and polarization sensitivity. Nano Lett. 16, 7446–7454 (2016).

    ADS  CAS  Article  Google Scholar 

  6. 6.

    Kollek, T. et al. Porous and shape-anisotropic single crystals of the semiconductor perovskite CH3NH3PbI3 from a single-source precursor. Angew. Chem. Int. Ed. 54, 1341–1346 (2015).

    CAS  Article  Google Scholar 

  7. 7.

    Son, D. Y. et al. Self-formed grain boundary healing layer for highly efficient CH3NH3PbI3 perovskite solar cells. Nat. Energy 1, 16081 (2016).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Long, M. et al. Textured CH3NH3PbI3 thin film with enhanced stability for high performance perovskite solar cells. Nano Energy 33, 485–496 (2017).

    CAS  Article  Google Scholar 

  9. 9.

    Zhu, F. et al. Shape evolution and single particle luminescence of organometal halide perovskite nanocrystals. ACS Nano 9, 2948–2959 (2015).

    CAS  Article  Google Scholar 

  10. 10.

    Fan, Z. et al. Layer-by-layer degradation of methylammonium lead tri-iodide perovskite microplates. Joule 1, 548–562 (2017).

    CAS  Article  Google Scholar 

  11. 11.

    Jung, Y. K., Butler, K. T. & Walsh, A. Halide perovskite heteroepitaxy: bond formation and carrier confinement at the PbS–CsPbBr3 interface. J. Phys. Chem. C 121, 27351–27356 (2017).

    CAS  Article  Google Scholar 

  12. 12.

    Sytnyk, M. et al. Quasi-epitaxial metal–halide perovskite ligand shells on PbS nanocrystals. ACS Nano 11, 1246–1256 (2017).

    CAS  Article  Google Scholar 

  13. 13.

    Zhang, X. et al. Inorganic CsPbI3 perovskite coating on PbS quantum dot for highly efficient and stable infrared light converting solar cells. Adv. Energy Mater. 8, 1702049 (2018).

    Article  Google Scholar 

  14. 14.

    Liu, M. et al. Lattice anchoring stabilizes solution-processed semiconductors. Nature 570, 96–101 (2019).

    ADS  CAS  Article  Google Scholar 

  15. 15.

    Masi, S. et al. Chemi-structural stabilization of formamidinium lead iodide perovskite by using embedded quantum dots. ACS Energy Lett. 5, 418–427 (2020).

    CAS  Article  Google Scholar 

  16. 16.

    Zhang, X. et al. PbS capped CsPbI3 nanocrystals for efficient and stable light-emitting devices using p-i-n structures. ACS Cent. Sci. 4, 1352–1359 (2018).

    CAS  Article  Google Scholar 

  17. 17.

    Peng, J., Chen, Y., Zhang, X., Dong, A. & Liang, Z. Solid-state ligand-exchange fabrication of CH3NH3PbI3 capped PbS quantum dot solar cells. Adv. Sci. 3, 1500432 (2015).

    Article  Google Scholar 

Download references

Acknowledgements

The TEM characterization was supported by the Center for High-resolution Electron Microscopy (ChEM) at ShanghaiTech University. We thank Y. Yu, B. Yuan and K. Xu at ShanghaiTech University for the TEM measurement. We thank Y. Li at Stanford University for discussions.

Author information

Affiliations

Authors

Contributions

X.G., Z.N., O.V. and E.H.S. designed and directed this study. Z.N. led the experimental work. X.G., Z.N., O.V. and E.H.S. wrote the manuscript. R.C., F.F., E.Y. and S.H. participated in discussions. All authors contributed to reviewing and commenting on the manuscript.

Corresponding author

Correspondence to Edward H. Sargent.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ning, Z., Gong, X., Comin, R. et al. Reply to: Perovskite decomposition and missing crystal planes in HRTEM. Nature 594, E8–E9 (2021). https://doi.org/10.1038/s41586-021-03424-3

Download citation

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing