Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Near-complete depolymerization of polyesters with nano-dispersed enzymes


Successfully interfacing enzymes and biomachinery with polymers affords on-demand modification and/or programmable degradation during the manufacture, utilization and disposal of plastics, but requires controlled biocatalysis in solid matrices with macromolecular substrates1,2,3,4,5,6,7. Embedding enzyme microparticles speeds up polyester degradation, but compromises host properties and unintentionally accelerates the formation of microplastics with partial polymer degradation6,8,9. Here we show that by nanoscopically dispersing enzymes with deep active sites, semi-crystalline polyesters can be degraded primarily via chain-end-mediated processive depolymerization with programmable latency and material integrity, akin to polyadenylation-induced messenger RNA decay10. It is also feasible to achieve processivity with enzymes that have surface-exposed active sites by engineering enzyme–protectant–polymer complexes. Poly(caprolactone) and poly(lactic acid) containing less than 2 weight per cent enzymes are depolymerized in days, with up to 98 per cent polymer-to-small-molecule conversion in standard soil composts and household tap water, completely eliminating current needs to separate and landfill their products in compost facilities. Furthermore, oxidases embedded in polyolefins retain their activities. However, hydrocarbon polymers do not closely associate with enzymes, as their polyester counterparts do, and the reactive radicals that are generated cannot chemically modify the macromolecular host. This study provides molecular guidance towards enzyme–polymer pairing and the selection of enzyme protectants to modulate substrate selectivity and optimize biocatalytic pathways. The results also highlight the need for in-depth research in solid-state enzymology, especially in multi-step enzymatic cascades, to tackle chemically dormant substrates without creating secondary environmental contamination and/or biosafety concerns.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Biocatalysis with embedded enzyme for polymer degradation.
Fig. 2: Characterization and degradation of PCL-RHP-BC-lipase.
Fig. 3: Embedded BC–lipase depolymerizes polyesters via chain end-mediated processive degradation.
Fig. 4: Enzyme protectants (RHPs) associate with the embedded enzyme to retain activity during melt processing and thermal treatment to program degradation.

Similar content being viewed by others

Data availability

All data are available in the main text or the Supplementary Information. Additional requests can be made to the corresponding author.


  1. Tokiwa, Y. & Suzuki, T. Hydrolysis of polyesters by lipases. Nature 270, 76–78 (1977).

    Article  ADS  CAS  PubMed  Google Scholar 

  2. Tournier, V. et al. An engineered PET depolymerase to break down and recycle plastic bottles. Nature 580, 216–219 (2020).

    Article  ADS  CAS  PubMed  Google Scholar 

  3. Kuchler, A., Yoshimoto, M., Luginbuhl, S., Mavelli, F. & Walde, P. Enzymatic reactions in confined environments. Nat. Nanotechnol. 11, 409–420 (2016).

    Article  ADS  CAS  PubMed  Google Scholar 

  4. Yang, Z. et al. Activity and stability of enzymes incorporated into acrylic polymers. J. Am. Chem. Soc. 117, 4843–4850 (1995).

    Article  CAS  Google Scholar 

  5. Panganiban, B. et al. Random heteropolymers preserve protein function in foreign environments. Science 359, 1239–1243 (2018).

    Article  ADS  CAS  PubMed  Google Scholar 

  6. Ganesh, M., Dave, R. N., L’Amoreaux, W. & Gross, R. A. Embedded enzymatic biomaterial degradation. Macromolecules 42, 6836–6839 (2009).

    Article  ADS  CAS  Google Scholar 

  7. DelRe, C. et al. Reusable enzymatic fiber mats for neurotoxin remediation in water. ACS Appl. Mater. Inter. 10, 44216–44220 (2018).

    Article  CAS  Google Scholar 

  8. Khan, I., Nagarjuna, R., Dutta, J. R. & Ganesan, R. Enzyme-embedded degradation of poly(epsilon-caprolactone) using lipase-derived from probiotic Lactobacillus plantarum. ACS Omega 4, 2844–2852 (2019).

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  9. Huang, Q. Y., Hiyama, M., Kabe, T., Kimura, S. & Iwata, T. Enzymatic self-biodegradation of poly(l-lactic acid) films by embedded heat-treated and immobilized proteinase K. Biomacromolecules 21, 3301–3307 (2020).

    Article  CAS  PubMed  Google Scholar 

  10. Xu, F. F. & Cohen, S. N. RNA degradation in Escherichia coli regulated by 3′ adenylation and 5′ phosphorylatian. Nature 374, 180–183 (1995).

    Article  ADS  CAS  PubMed  Google Scholar 

  11. Wei, R. et al. Possibilities and limitations of biotechnological plastic degradation and recycling. Nat. Catal. 3, 867–871 (2020).

    Article  CAS  Google Scholar 

  12. Ivleva, N. P., Wiesheu, A. C. & Niessner, R. Microplastic in aquatic ecosystems. Angew. Chem. Int. Ed. 56, 1720–1739 (2017).

    Article  CAS  Google Scholar 

  13. Jambeck, J. R. et al. Plastic waste inputs from land into the ocean. Science 347, 768–771 (2015).

    Article  ADS  CAS  PubMed  Google Scholar 

  14. Haider, T. P., Volker, C., Kramm, J., Landfester, K. & Wurm, F. R. Plastics of the future? The impact of biodegradable polymers on the environment and on society. Angew. Chem. Int. Ed. 58, 50–62 (2019).

    Article  CAS  Google Scholar 

  15. Roohi, et al. Microbial enzymatic degradation of biodegradable plastics. Curr. Pharm. Biotechnol. 18, 429–440 (2017).

    Article  CAS  PubMed  Google Scholar 

  16. Breyer, W. A. & Matthews, B. W. Structure of Escherichia coli exonuclease I suggests how processivity is achieved. Nat. Struct. Biol. 7, 1125–1128 (2000).

    Article  CAS  PubMed  Google Scholar 

  17. Pleiss, J., Fischer, M. & Schmid, R. D. Anatomy of lipase binding sites: the scissile fatty acid binding site. Chem. Phys. Lipids 93, 67–80 (1998).

    Article  CAS  PubMed  Google Scholar 

  18. Li, S. M. & McCarthy, S. Influence of crystallinity and stereochemistry on the enzymatic degradation of poly(lactide)s. Macromolecules 32, 4454–4456 (1999).

    Article  ADS  CAS  Google Scholar 

  19. Flory, P. J. & Yoon, D. Y. Molecular morphology in semi-crystalline polymers. Nature 272, 226–229 (1978).

    Article  ADS  CAS  Google Scholar 

  20. Tokiwa, Y., Calabia, B. P., Ugwu, C. U. & Aiba, S. Biodegradability of plastics. Int. J. Mol. Sci. 10, 3722–3742 (2009).

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  21. Ru, J. K., Huo, Y. X. & Yang, Y. Microbial degradation and valorization of plastic wastes. Front Microbiol 11, 442, (2020).

    Article  PubMed  PubMed Central  Google Scholar 

  22. Tennakoon, A. et al. Catalytic upcycling of high-density polyethylene via a processive mechanism. Nat. Catal. 3, 893–901 (2020).

    Article  CAS  Google Scholar 

  23. Horn, S. J. et al. Costs and benefits of processivity in enzymatic degradation of recalcitrant polysaccharides. Proc. Natl Acad. Sci. USA 103, 18089–18094 (2006).

    Article  ADS  CAS  PubMed  Google Scholar 

  24. Beckham, G. T. et al. Molecular-level origins of biomass recalcitrance: decrystallization free energies for four common cellulose polymorphs. J. Phys. Chem. B 115, 4118–4127 (2011).

    Article  CAS  PubMed  Google Scholar 

  25. Payne, C. M., Himmel, M. E., Crowley, M. F. & Beckham, G. T. Decrystallization of oligosaccharides from the cellulose Iβ surface with molecular simulation. J. Phys. Chem. Lett. 2, 1546–1550 (2011).

    Article  CAS  Google Scholar 

  26. Klibanov, A. M. Improving enzymes by using them in organic solvents. Nature 409, 241–246 (2001).

    Article  ADS  CAS  PubMed  Google Scholar 

  27. Christensen, P. R., Scheuermann, A. M., Loeffler, K. E. & Helms, B. A. Closed-loop recycling of plastics enabled by dynamic covalent diketoenamine bonds. Nat. Chem. 11, 442–448 (2019).

    Article  CAS  PubMed  Google Scholar 

  28. Satchwell, A. J. et al. Accelerating the deployment of anaerobic digestion to meet zero waste goals. Environ. Sci. Technol. 52, 13663–13669 (2018).

    Article  ADS  CAS  PubMed  Google Scholar 

  29. Hobbs, S. R., Parameswaran, P., Astmann, B., Devkota, J. P. & Landis, A. E. Anaerobic codigestion of food waste and polylactic acid: effect of pretreatment on methane yield and solid reduction. Adv. Mater. Sci. Eng. 2019, 4715904 (2019).

    Article  CAS  Google Scholar 

  30. Nordahl, S. L. et al. Life-Cycle Greenhouse Gas Emissions and Human Health Trade-Offs of Organic Waste Management Strategies. Environ. Sci. Technol. 54, 9200–9209 (2020).

    Article  ADS  CAS  PubMed  Google Scholar 

  31. Radi, R. Oxygen radicals, nitric oxide, and peroxynitrite: redox pathways in molecular medicine. Proc. Natl Acad. Sci. USA 115, 5839–5848 (2018).

    Article  CAS  PubMed  Google Scholar 

  32. Iiyoshi, Y., Tsutsumi, Y. & Nishida, T. Polyethylene degradation by lignin-degrading fungi and malaganese peroxidase. J. Wood Sci. 44, 222–229 (1998).

    Article  CAS  Google Scholar 

  33. Yang, J., Yang, Y., Wu, W. M., Zhao, J. & Jiang, L. Evidence of polyethylene biodegradation by bacterial strains from the guts of plastic-eating waxworms. Environ. Sci. Technol. 48, 13776–13784 (2014).

    Article  ADS  CAS  PubMed  Google Scholar 

  34. Schneiderman, D. K. & Hillmyer, M. A. There is a great future in sustainable polymers. Macromolecules 50, 3733–3749 (2017).

    Article  ADS  CAS  Google Scholar 

  35. Liu, L. J., Li, S. M., Garreau, H. & Vert, M. Selective enzymatic degradations of poly(l-lactide) and poly(epsilon-caprolactone) blend films. Biomacromolecules 1, 350–359 (2000).

    Article  CAS  PubMed  Google Scholar 

  36. Varma-Nair, M., Pan, R. & Wunderlich, B. Heat capacities and entropies of linear, aliphatic polyesters. J. Polym. Sci. Pol. Phys. 29, 1107–1115 (1991).

    Article  ADS  CAS  Google Scholar 

  37. Hall, M., Bansal, P., Lee, J. H., Realff, M. J. & Bommarius, A. S. Cellulose crystallinity – a key predictor of the enzymatic hydrolysis rate. FEBS J. 277, 1571–1582 (2010).

    Article  CAS  PubMed  Google Scholar 

  38. Jiang, T. et al. Single-chain heteropolymers transport protons selectively and rapidly. Nature 577, 216–220 (2020).

    Article  ADS  CAS  PubMed  Google Scholar 

  39. Arnold, F. H. Directed evolution: bringing new chemistry to life. Angew. Chem. Int. Ed. 57, 4143–4148 (2018).

    Article  CAS  Google Scholar 

  40. Bornscheuer, U. et al. Lipase of pseudomonas-cepacia for biotechnological purposes – purification, crystallization and characterization. Biochim. Biophys. Acta Gen. Subj. 1201, 55–60 (1994).

    Article  CAS  Google Scholar 

  41. Wurm, A. et al. Crystallization and homogeneous nucleation kinetics of poly(epsilon-caprolactone) (PCL) with different molar masses. Macromolecules 45, 3816–3828 (2012).

    Article  ADS  CAS  Google Scholar 

  42. Ajioka, M., Suizu, H., Higuchi, C. & Kashima, T. Aliphatic polyesters and their copolymers synthesized through direct condensation polymerization. Polym. Degrad. Stabil. 59, 137–143 (1998).

    Article  CAS  Google Scholar 

  43. Smith, A. A. A., Hall, A., Wu, V. & Xu, T. Practical prediction of heteropolymer composition and drift. ACS Macro Lett. 8, 36–40 (2019).

    Article  ADS  CAS  Google Scholar 

Download references


This work was primarily supported by the US Department of Energy, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division (DOE-BES-MSE) under contract DE-AC02-05-CH11231, through the Organic−Inorganic Nanocomposites KC3104 programme (enzyme–plastic composite design and degradation mechanism; C.D., L.M., A.H., I.J., R.O.R., T.X.). Y.J. and T.P.R. acknowledge support from DOE-BES-MSE under the same contract number, through the Adaptive Interfacial Assemblies Towards Structuring Liquids KCTR16 programme (tensiometry studies on RHP/enzyme/polymer complexation). C.D.S. acknowledges Laboratory Directed Research and Development funding from Berkeley Lab (integration with organic waste infrastructure). The US Department of Defense, Army Research Office supported Z.R. (lipase stabilization) under contract W911NF-13-1-0232. C.D. was partially supported by a National Defense Science and Engineering Graduate (NDSEG) Fellowship (Bioremediation). T.X. also acknowledges support from a Bakar Fellowship at University of California Berkeley (compost tests). Scattering studies at the Advanced Light Source were supported by the US Department of Energy, Office of Science, Office of Basic Energy Science under contract DE-AC02-05CH11231.

Author information

Authors and Affiliations



T.X. conceived the idea and guided the project. C.D. and T.X. analysed degradation rate and by-product experiments, material characterization experiments, and determined the different enzyme mechanisms. C.D., Y.J., T.P.R. and T.X. analysed interfacial-tension data. C.D., P.K. and T.X. analysed the diblock degradation experiments. J.K. and R.O.R. analysed mechanical properties. P.K., Z.R. and A.H. synthesized and characterized the RHPs. I.J. analysed RHPs and enzyme surfaces and repeated the analysis of the degradation results. L.M. performed electron microscopy experiments. A.H. carried out repolymerization experiments. K.Z. and T.L. assisted with degradation-rate quantification and enzyme active-site analysis. C.D.S. provided insights on integration with organic-waste infrastructure.

Corresponding author

Correspondence to Ting Xu.

Ethics declarations

Competing interests

T.X., C.D. and J.K. have filed a PCT patent application. A.H. is the founder and CEO of Intropic Materials.

Additional information

Peer review information Nature thanks Jayati Ray Dutta, Mattheos Koffas and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Characterization of enzyme-embedded PCL.

a, DLS results for RHP and purified BC–lipase in toluene (the solvent used to cast PCL) with an average hydrodynamic diameter of 285 nm ± 35 nm (n = 5) (the error indicates standard deviation). b, DSC results for PCL and PCL–RHP–BC-lipase as-cast films. c, SAXS curves of PCL and PCL–RHP–BC–lipase as-cast films.

Extended Data Fig. 2 PCL–RHP–BC–lipase by-product analysis.

Liquid chromatogram of the degradation by-products for degradation by confined and dissolved (surface erosion) BC–lipase.

Extended Data Fig. 3 Degradation by confined CA–lipase with shallow active site.

a, GPC curve of the degradation of PCL–RHP–CA–lipase, showing a shift and broadening of the main peak, indicative of random chain scission. b, Zoomed-in version of a illustrating the peak shift and broadening.

Extended Data Fig. 4 Enzyme environment dictates biocatalytic reaction kinetics.

a, PCL degradation by BC–lipase dissolved in solution (surface), nanoscopically embedded in PCL with RHP, and embedded with Tween 80, a small-molecule surfactant, as microparticles. b, Hydrolysis of 4-nitrophenyl butyrate, a small-molecule ester, by BC–lipase in solution or confined in PCL (error bars represent one standard deviation; n ≥ 3).

Extended Data Fig. 5 Model interfacial-tension experiment to explain intermolecular interactions among enzyme, protectant and matrix.

ac, When all three components are initially mixed in toluene (a, left) and then a water interface is introduced (a, right), RHP–lipase complexes immediately interact with PCL at the interface, as shown by the fluorescence microscopy image taken ~20 s after shaking the vial to produce an emulsion (b) and the long delay time in interfacial-tension reduction that is seen only for PCL–RHP–lipase (c).

Extended Data Fig. 6 Characterization of semi-crystalline properties of melt-processed PCL–RHP–BC–lipase.

a, DSC curves of PCL–RHP–BC–lipase with different recrystallization conditions (the film with recrystallization temperature Tc = 49 °C has a crystallinity of 41% ± 1.2% compared to 39% ± 1.8% for the as-cast film). The increase in melting temperature from ~58 °C to ~64 °C indicates a substantial thickening in crystalline lamellae for Tc = 49 °C films, which was confirmed by SAXS. b, SAXS profiles of as-cast and Tc = 49 °C films of PCL–RHP–BC–lipase. The increase of long periods (shift to lower q), combined with the negligible difference in the bulk per cent crystallinity according to DSC data, confirms a thickening in crystalline lamellae after crystallizing at Tc = 49 °C.

Extended Data Fig. 7 Confirming enzyme does not denature at high temperatures.

Small-molecule ester hydrolysis by embedded BC–lipase as a function of temperature (red), overlaid with the PCL–RHP–BC–lipase degradation rate. The small-molecule activity remained high at 60 °C but was not quantified because the film shrivelled owing to melting, and thus was much thicker than films at lower temperatures, making quantification incomparable to all other temperatures.

Extended Data Fig. 8 Quantifying segmental hydrophobicity of different RHPs.

a, Hydropathy plots for RHPs with 60:10 MMA:EHMA composition. b, Hydropathy plots for RHPs with 50:20 MMA:EHMA composition. c, Hydropathy plots for RHPs with 20:50 MMA:EHMA composition. d, Average segmental HLB value for each RHP composition. Error bars indicate standard deviation, n ≥ 3.

Extended Data Fig. 9 Characterizing embedded enzymes for more commercially relevant plastics.

a, Crystal structure of proteinase K with the same colour-coding scheme as that used for lipases in the main text (Fig. 3). b, GPC curve of PLA–RHP–proteinase K (‘ProK”) as cast and after depolymerizing in buffer; c, Interfacial-tensiometry experiment results for a DCM–water interface with PLA, RHP and proteinase K in the DCM phase. d, Photograph of ABTS small-molecule assay in malonate buffer after ~10 min, demonstrating that laccase embedded in polystyrene (PS) retains the ability to oxidize a small molecule. Similar results were found for manganese peroxidase and for both enzymes embedded in polyethylene. e, Interfacial-tensiometry experiment results for a toluene–water interface with PS, RHP and either laccase or manganese peroxidase (‘MnP’) in the toluene phase.

Extended Data Table 1 Summary of all polymer–enzyme blends employed in the study

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

DelRe, C., Jiang, Y., Kang, P. et al. Near-complete depolymerization of polyesters with nano-dispersed enzymes. Nature 592, 558–563 (2021).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing