Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Molecular heterogeneity drives reconfigurable nematic liquid crystal drops

An Author Correction to this article was published on 22 August 2020

This article has been updated


With few exceptions1,2,3, polydispersity or molecular heterogeneity in matter tends to impede self-assembly and state transformation. For example, shape transformations of liquid droplets with monodisperse ingredients have been reported in equilibrium4,5,6,7 and non-equilibrium studies8,9, and these transition phenomena were understood on the basis of homogeneous material responses. Here, by contrast, we study equilibrium suspensions of drops composed of polydisperse nematic liquid crystal oligomers (NLCOs). Surprisingly, molecular heterogeneity in the polydisperse drops promotes reversible shape transitions to a rich variety of non-spherical morphologies with unique internal structure. We find that variation of oligomer chain length distribution, temperature, and surfactant concentration alters the balance between NLCO elastic energy and interfacial energy, and drives formation of nematic structures that range from roughened spheres to ‘flower’ shapes to branched filamentous networks with controllable diameters. The branched structures with confined liquid crystal director fields can be produced reversibly over areas of at least one square centimetre and can be converted into liquid crystal elastomers by ultraviolet curing. Observations and modelling reveal that chain length polydispersity plays a crucial role in driving these morphogenic phenomena, via spatial segregation. This insight suggests new routes for encoding network structure and function in soft materials.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Spontaneous shape transition of NLCO drops.
Fig. 2: Equilibrium NLCO drop morphologies as a function of mean oligomer chain length and surfactant concentration.
Fig. 3: Director configurations within NLCO structures.
Fig. 4: SEM images of self-assembled NLCEs.

Data availability

The authors declare that the data supporting the findings of this study are available within the text, including the Methods section, and Extended Data files. Raw data are available from the corresponding author upon reasonable request.

Code availability

Custom computer codes associated with modelling in this study are available on GitHub (

Change history

  • 22 August 2020

    An amendment to this paper has been published and can be accessed via a link at the top of the paper.


  1. Fasolo, M. & Sollich, P. Equilibrium phase behavior of polydisperse hard spheres. Phys. Rev. Lett. 91, 068301 (2003).

    ADS  PubMed  Google Scholar 

  2. Zaccarelli, E. et al. Crystallization of hard-sphere glasses. Phys. Rev. Lett. 103, 135704 (2009).

    ADS  CAS  PubMed  Google Scholar 

  3. Liddle, S. M., Narayanan, T. & Poon, W. C. K. Polydispersity effects in colloid-polymer mixtures. J. Phys. Condens. Matter 23, 194116 (2011).

    ADS  CAS  PubMed  Google Scholar 

  4. Lavrentovich, O. D. et al. Helical smectic A. Europhys. Lett. 13, 313–318 (1990).

    ADS  CAS  Google Scholar 

  5. Gibaud, T. et al. Reconfigurable self-assembly through chiral control of interfacial tension. Nature 481, 348–351 (2012).

    ADS  CAS  PubMed  Google Scholar 

  6. Denkov, N., Tcholakova, S., Lesov, I., Cholakova, D. & Smoukov, S. K. Self-shaping of oil droplets via the formation of intermediate rotator phases upon cooling. Nature 528, 392–395 (2015).

    ADS  CAS  PubMed  Google Scholar 

  7. Guttman, S. et al. How faceted liquid droplets grow tails. Proc. Natl Acad. Sci. USA 113, 493–496 (2016).

    ADS  CAS  PubMed  Google Scholar 

  8. Toquer, G. et al. Colloidal shape controlled by molecular adsorption at liquid crystal interfaces. J. Phys. Chem. B 112, 4157–4160 (2008).

    CAS  PubMed  Google Scholar 

  9. Peddireddy, K., Kumar, P., Thutupalli, S., Herminghaus, S. & Bahr, C. Myelin structures formed by thermotropic smectic liquid crystals. Langmuir 29, 15682–15688 (2013).

    CAS  PubMed  Google Scholar 

  10. Ware, T. H., McConney, M. E., Wie, J. J., Tondiglia, V. P. & White, T. J. Voxelated liquid crystal elastomers. Science 347, 982–984 (2015).

    ADS  CAS  PubMed  Google Scholar 

  11. Gannon, M. G. J. & Faber, T. E. The surface tension of nematic liquid crystals. Phil. Mag. A 37, 117–135 (1978).

    ADS  CAS  Google Scholar 

  12. Butt, H. J., Graf, K. & Kappl, M. Physics and Chemistry of Interfaces Ch. 3 (Wiley & Sons, 2006).

  13. Schiele, K. & Trimper, S. On the elastic constants of a nematic liquid crystal. Phys. Status Solidi B 118, 267–274 (1983).

    ADS  CAS  Google Scholar 

  14. Kamien, R. D. & Toner, J. Anomalous elasticity of polymer cholesterics. Phys. Rev. Lett. 74, 3181–3184 (1995).

    ADS  CAS  PubMed  Google Scholar 

  15. Kasten, H. & Strobl, G. Nematic wetting at the free surface of 4-cyano-4′-n-alkyl-biphenyls. J. Chem. Phys. 103, 6768–6774 (1995).

    ADS  CAS  Google Scholar 

  16. Tintaru, M., Moldovan, R., Beica, T. & Frunza, S. Surface tension of some liquid crystals in the cyanobiphenyl series. Liq. Cryst. 28, 793–797 (2001).

    CAS  Google Scholar 

  17. Lubensky, T. C., Pettey, D., Currier, N. & Stark, H. Topological defects and interactions in nematic emulsions. Phys. Rev. E 57, 610–625 (1998).

    ADS  CAS  Google Scholar 

  18. Allender, D. W., Crawford, G. P. & Doane, J. W. Determination of the liquid-crystal surface elastic constant K24. Phys. Rev. Lett. 67, 1442–1445 (1991).

    ADS  CAS  PubMed  Google Scholar 

  19. Muševič, I. Liquid Crystal Colloids Ch. 7 (Springer, 2017).

  20. Cholakova, D., Valkova, Z., Tcholakova, S., Denkov, N. & Smoukov, S. K. “Self-shaping” of multicomponent drops. Langmuir 33, 5696–5706 (2017).

    CAS  PubMed  Google Scholar 

  21. Shimshick, E. J. & McConnell, H. M. Lateral phase separation in phospholipid membranes. Biochemistry 12, 2351–2360 (1973).

    CAS  PubMed  Google Scholar 

  22. Sidky, H. & Whitmer, J. K. Elastic response and phase behavior in binary liquid crystal mixtures. Soft Matter 12, 4489–4498 (2016).

    ADS  CAS  PubMed  Google Scholar 

  23. Elias, F., Clarke, S. M., Peck, R. & Terentjev, E. M. Nematic order drives phase separation in polydisperse liquid crystalline polymers. Macromolecules 33, 2060–2068 (2000).

    ADS  CAS  Google Scholar 

  24. Ahir, S. V., Tajbakhsh, A. R. & Terentjev, E. M. Self-assembled shape-memory fibers of triblock liquid-crystal polymers. Adv. Funct. Mater. 16, 556–560 (2006).

    CAS  Google Scholar 

  25. Ohm, C. et al. Preparation of actuating fibres of oriented main-chain liquid crystalline elastomers by a wetspinning process. Soft Matter 7, 3730–3734 (2011).

    ADS  CAS  Google Scholar 

  26. Xia, Y., Zhang, X. & Yang, S. Instant locking of molecular ordering in liquid crystal elastomers by oxygen-mediated thiol-acrylate click reactions. Angew. Chem. 130, 5767–5770 (2018).

    Google Scholar 

  27. Krause, S., Dersch, R., Wendorff, J. H. & Finkelmann, H. Photocrosslinkable liquid crystal main-chain polymers: thin films and electrospinning. Macromol. Rapid Commun. 28, 2062–2068 (2007).

    CAS  Google Scholar 

  28. Dufresne, E. R. et al. Self-assembly of amorphous biophotonic nanostructures by phase separation. Soft Matter 5, 1792–1795 (2009).

    ADS  CAS  Google Scholar 

  29. Saranathan, V. et al. Structure, function, and self-assembly of single network gyroid (I4132) photonic crystals in butterfly wing scales. Proc. Natl Acad. Sci. USA 107, 11676–11681 (2010).

    ADS  CAS  PubMed  Google Scholar 

  30. Radja, A., Horsley, E. M., Lavrentovich, M. O. & Sweeney, A. M. Pollen cell wall patterns form from modulated phases. Cell 176, 856–868 (2019).

    CAS  PubMed  Google Scholar 

  31. Adamson, A. W. & Gast, A. P. Physical Chemistry of Surfaces 6th edn, Ch. 2 (Wiley & Sons, 1997).

  32. Daerr, A. & Mogne, A. Pendent_drop: an imagej plugin to measure the surface tension from an image of a pendent drop. J. Open Res. Softw. 4, e3 (2016).

    Google Scholar 

  33. Terentjev, E. M. Density functional model of anchoring energy at a liquid crystalline polymer-solid interface. J. Phys. II France 5, 159–170 (1995).

    CAS  Google Scholar 

  34. Frank, F. C. I. Liquid crystals: on the theory of liquid crystals. Discuss. Faraday Soc. 25, 19–28 (1958).

    Google Scholar 

  35. Oseen, C. W. The theory of liquid crystals. Trans. Faraday Soc. 29, 883–899 (1933).

    CAS  MATH  Google Scholar 

  36. Nehring, J. & Saupe, A. On the elastic theory of uniaxial liquid crystals. J. Chem. Phys. 54, 337–343 (1971).

    ADS  CAS  Google Scholar 

  37. Barbero, G. & Oldano, C. Derivative-dependent surface-energy terms in nematic liquid crystals. Nuovo Cimento D 6, 479–493 (1985).

    ADS  Google Scholar 

  38. Sparavigna, A., Komitov, L. & Strigazzi, A. Hybrid aligned nematics and second order elasticity. Phys. Scr. 43, 210 (1991).

    ADS  Google Scholar 

  39. Crawford, G. P., Allender, D. W. & Doane, J. W. Surface elastic and molecular-anchoring properties of nematic liquid crystals confined to cylindrical cavities. Phys. Rev. A 45, 8693–8708 (1992).

    ADS  CAS  PubMed  Google Scholar 

  40. Rapini, A. & Papoular, M. Distorsion d’une lamelle nématique sous champ magnétique conditions d’ancrage aux parois. J. Phys. Colloques 30, 54–56 (1969).

    Google Scholar 

  41. Cladis, P. E. & Kléman, M. Non-singular disclinations of strength S = +1 in nematics. J. Phys. France 33, 591–598 (1972).

    CAS  Google Scholar 

  42. Meyer, R. B. On the existence of even indexed disclinations in nematic liquid crystals. Phil. Mag. 27, 405–424 (1973).

    ADS  CAS  Google Scholar 

  43. Burylov, S. V. Equilibrium configuration of a nematic liquid crystal confined to a cylindrical cavity. J. Exp. Theor. Phys. 85, 873–886 (1997).

    ADS  Google Scholar 

  44. Li, X. & Denn, M. M. Interface between a liquid crystalline polymer and a flexible polymer. Macromolecules 35, 6446–6454 (2002).

    ADS  CAS  Google Scholar 

  45. Wu, J. & Mather, P. T. Interfacial tension of a liquid crystalline polymer in an isotropic polymer matrix. Macromolecules 38, 7343–7351 (2005).

    ADS  CAS  Google Scholar 

  46. Bradshaw, M. J., Raynes, E. P., Bunning, J. D. & Faber, T. E. The Frank constants of some nematic liquid crystals. J. Phys. France 46, 1513–1520 (1985).

    CAS  Google Scholar 

  47. Zhou, S. et al. Elasticity, viscosity, and orientational fluctuations of a lyotropic chromonic nematic liquid crystal disodium cromoglycate. Soft Matter 10, 6571–6581 (2014).

    ADS  CAS  PubMed  Google Scholar 

  48. Xia, Y., Serra, F., Kamien, R. D., Stebe, K. J. & Yang, S. Direct mapping of local director field of nematic liquid crystals at the nanoscale. Proc. Natl Acad. Sci. USA 112, 15291–15296 (2015).

    ADS  CAS  PubMed  Google Scholar 

  49. Yokoyama, H. & van Sprang, H. A. A novel method for determining the anchoring energy function at a nematic liquid crystal-wall interface from director distortions at high fields. J. Appl. Phys. 57, 4520–4526 (1985).

    ADS  CAS  Google Scholar 

  50. Yang, F., Ruan, L. & Sambles, J. R. Homeotropic polar anchoring energy of a nematic liquid crystal using the fully leaky waveguide technique. J. Appl. Phys. 88, 6175–6182 (2000).

    ADS  CAS  Google Scholar 

  51. Škarabot, M., Osmanagič, E. & Muševič, I. Surface anchoring of nematic liquid crystal 8OCB on a DMOAP-silanated glass surface. Liq. Cryst. 33, 581–585 (2006).

    Google Scholar 

  52. Ciferri, A., Krigbaum, W. R. & Meyer, R. B. Polymer Liquid Crystals Ch. 6 (Academic, 1982).

Download references


We thank the following for discussions: K. B. Aptowicz, C.-C. Chang, P. J. Collings, A. de la Cotte, Z. S. Davidson, R. Dreyfus, P. Habdas, A. Hill, Y.-Y. Ho, R. D. Kamien, J. Jeong, T. C. Lubensky, X. Ma, A. Martinez, C. K. Mishra and P. Palffy-Muhoray. A. Soleymannezhad and J. Timmons (Tosoh Bioscience) assisted with SEC operation and analysis. We acknowledge financial support from the National Science Foundation (grant no. DMR16-07378), the Materials Research Science & Engineering Center (MRSEC) at University of Pennsylvania (grant no. DMR-1720530) including MRSEC’s Optical Microscopy and Electron Microscopy Shared Experimental Facility, and NASA (grant no. 80NSSC19K0348).

Author information

Authors and Affiliations



W.-S.W., Y.X., S.Y. and A.G.Y. conceived the idea and designed the experiments. W.-S.W., Y.X. and S.E. initiated and performed the experiments. W.-S.W., Y.X., S.E., S.Y. and A.G.Y. worked on different facets of the data analysis. W.-S.W. and A.G.Y. wrote the paper, and all authors contributed to the final manuscript.

Corresponding author

Correspondence to Wei-Shao Wei.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature thanks Kari Dalnoki-Veress, Stoyan Smoukov and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Distribution of chain length and molecular weight of NLCO samples measured by size exclusion chromatography.

a, The NLCO source samples are shown by size exclusion chromatography (SEC) to be a mixture of monomers, dimers, trimers, tetramers and other oligomers (blue solid line; peaks appearing at longer retention times represent shorter chain lengths). In step-polymerization processes, when the extent of reaction is less than 0.9, monomers dominate the overall molar fraction. For comparison, liquid crystal (LC) macromers (used in the supporting experiment in Methods) synthesized following the schemes of Ware et al.10 are also included in the plot; these show longer mean chain length and very few (if any) short-chain components (red dashed line). Furthermore, since our system is made in an aqueous solution, the polymerization rate is expected to be slower. For reference, the black dotted line shows the peak for pure RM82 monomer. b, Calculated from SEC data (example in a), the number-average molecular weight (\({\bar{M}}_{{\rm{n}}}\), blue solid squares) and polydispersity index (PDI, red filled circles) of the NLCOs are shown as function of oligomerization time. Both \({\bar{M}}_{{\rm{n}}}\) and PDI increase with oligomerization time. The dotted (for \({\bar{M}}_{{\rm{n}}}\)) and dashed (for PDI) curves are to guide the eye. (For comparison, the LC macromer synthesized following the schemes of Ware et al.10 and used in Methods section ‘Macromer–monomer mixing experiments’ has \({\bar{M}}_{{\rm{n}}}\approx \text{6,900}\,{\rm{D}}{\rm{a}}\) and PDI ≈ 1.3.) Bars indicate the spread in \({\bar{M}}_{{\rm{n}}}\), which mainly arises from our inability to detect the longer-chain components.

Extended Data Fig. 2 Bright-field optical microscopy images showing reversible shape transitions of NLCO drops during temperature cycling.

ac, When temperature is increased from room temperature (20 °C) to a higher value (here 90 °C), the NLCO filamentous structures reversibly evolve into spherical microdroplets. ce, When cooled from 90 °C to 20 °C, the spherical microdroplets reversibly evolve back into filamentous structures. The drop morphology can be transformed repeatedly, remaining quantitatively similar. Here, multiple small drops evolve in the field of view; data shown earlier (Fig. 1c–h) showed only one large evolving drop. Scale bar in a (for all panels), 20 μm.

Extended Data Fig. 3 Macroscopic interfacial tension of NLCO pendant drops as function of temperature and NLCO oligomerization time.

The NLCO drop has homeotropic anchoring at the interface in an aqueous solution consisting of 0.1 wt% SDS. The interfacial tension γ decreases with decreasing temperature and increasing NLCO mean oligomer chain length (consult Fig. 2f for the relation between oligomerization processing time and ). Inset, optical image of a NLCO pendant drop hanging from a flat-tip syringe needle (1.26 mm outer diameter) in a 0.1 wt% SDS aqueous solution. The dashed curves are to guide the eye.

Extended Data Fig. 4 Bright-field optical microscopy images of drop morphologies obtained from mixtures of macromers ( ≈ 9) and monomers (RM82) at different weight ratios in a 0.1 wt% SDS aqueous solution after cooling.

ae, Images for monomer:macromer weight ratios of 1:0.3, 1:0.5, 1:0.7, 1:0.9 and 1:1, respectively. With a fixed amount of RM82, increasing the concentration of macromers in the drop leads to longer , larger bulk elasticity and lower interfacial tension. The last two factors favour interfacial roughening and filament formation. Images are taken at room temperature after cooling. Scale bar in a (for all panels), 50 μm.

Extended Data Fig. 5 Bright-field optical microscopy images of NLCO structures in aqueous solutions of different surfactants as a function of the mean oligomer chain length, .

af, NLCO drops in aqueous solutions with different surfactants, that is, with either cationic (ac; hexadecyltrimethylammonium bromide, C16TAB) or nonionic (df, Polysorbate 20, Tween 20) surfactants. These systems exhibit a drop morphology evolution similar to that resulting from SDS, that is, with respect to cooling and an increase of . After cooling from 90 °C to 20 °C, a representative NLCO drop in a 0.5 mM C16TAB aqueous solution (below the CMC; ac) and a representative NLCO drop in a 0.03 mM Tween 20 aqueous solution (below the CMC; df). Both evolve with increasing (left to right; consult Fig. 2f for the relation between the oligomerization time (shown at bottom left in all panels) and ). For this behaviour to be shown, it is important that NLCOs should favour homeotropic anchoring at the drop interface. Images are taken at room temperature. Scale bars in af, 20 μm.

Extended Data Fig. 6 Bright-field optical microscopy image of aggregated NLCO filamentous structures for an SDS concentration above the CMC.

In a 1 wt% SDS aqueous solution (shown here), the NLCO drops exhibit a similar but more complicated shape transition behaviour than that which occurs below the CMC, after cooling from 90 °C to 20 °C. For example, aggregated filamentous structures form and sometimes stick to the substrate due, in part, to micelle-induced depletion. (For comparison, expanded filamentous structures form in aqueous solutions below the CMC, see example in Fig. 1h.) Scale bar, 20 μm.

Extended Data Fig. 7 Self-assembled NLCE fibrous mat.

NLCE fibres can be densely packed into centimetre-wide and few-micrometres-thick, non-woven, free-standing mats by sedimentation. Here we show an image of such a mat (mounted on a hollowed holder) with a diameter greater than 1 cm. Corresponding high-magnification SEM images of this mat are shown in Fig. 4e, f.

Extended Data Table 1 Parameter values that permit shape transitions of NLCO drops

Supplementary information

Supplementary Video 1 | Spontaneous shape transition of NLCO drop during cooling

At high temperature (~40 °C, 00:00:00), the suspended NLCO drop is spherical. Upon cooling, the drop destabilizes and spontaneously evolves from a sphere to a filamentous structure (01:00:00 roughening starts at ~37 °C; 11:00:00 short filaments form at ~30 °C; 26:00:00 long filaments form at ~26 °C). Images are taken between crossed-polarizers with a full-wave retardation plate. This scheme permits visualization of director fields (yellow indicates northwest–southeast alignment; cyan indicates northeast–southwest alignment). Scale bar is 15 μm. The video is sped up by 100×. The focal plane is occasionally adjusted to keep filaments in focus.

Supplementary Video 2 | Reversible shape transitions of small NLCO drops during temperature cycling

Multiple small NLCO drops are shown in the field-of-view in bright-field microscopy. At the beginning of the video, equilibrium NLCO filamentous structures are intertwined with their neighbors at low temperature (~25 °C). As the temperature increases to 60 °C, the NLCO filamentous structures reversibly evolve back into spherical micro-droplets. Then, during recooling, the micro-droplets evolve back into filamentous structures. The temperature cycling and corresponding morphology changes are repeatable. Scale bar is 20 μm. The video is sped up by 20×.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wei, WS., Xia, Y., Ettinger, S. et al. Molecular heterogeneity drives reconfigurable nematic liquid crystal drops. Nature 576, 433–436 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing