Abstract
Supramolecular soft crystals are periodic structures that are formed by the hierarchical assembly of complex constituents, and occur in a broad variety of ‘soft-matter’ systems1. Such soft crystals exhibit many of the basic features (such as three-dimensional lattices and space groups) and properties (such as band structure and wave propagation) of their ‘hard-matter’ atomic solid counterparts, owing to the generic symmetry-based principles that underlie both2,3. ‘Mesoatomic’ building blocks of soft-matter crystals consist of groups of molecules, whose sub-unit-cell configurations couple strongly to supra-unit-scale symmetry. As yet, high-fidelity experimental techniques for characterizing the detailed local structure of soft matter and, in particular, for quantifying the effects of multiscale reconfigurability are quite limited. Here, by applying slice-and-view microscopy to reconstruct the micrometre-scale domain morphology of a solution-cast block copolymer double gyroid over large specimen volumes, we unambiguously characterize its supra-unit and sub-unit cell morphology. Our multiscale analysis reveals a qualitative and underappreciated distinction between this double-gyroid soft crystal and hard crystals in terms of their structural relaxations in response to forces—namely a non-affine mode of sub-unit-cell symmetry breaking that is coherently maintained over large multicell dimensions. Subject to inevitable stresses during crystal growth, the relatively soft strut lengths and diameters of the double-gyroid network can easily accommodate deformation, while the angular geometry is stiff, maintaining local correlations even under strong symmetry-breaking distortions. These features contrast sharply with the rigid lengths and bendable angles of hard crystals.
This is a preview of subscription content, access via your institution
Relevant articles
Open Access articles citing this article.
-
Medial packing and elastic asymmetry stabilize the double-gyroid in block copolymers
Nature Communications Open Access 12 May 2022
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Rent or buy this article
Prices vary by article type
from$1.95
to$39.95
Prices may be subject to local taxes which are calculated during checkout
Data availability
SVSEM and SCF modelling data are available at https://doi.org/10.7275/wv24-3j62.
Code availability
Supporting software codes are available at https://doi.org/10.7275/wv24-3j62.
References
Hyde, S. et al. The Language of Shape 141–197 (Elsevier Science, 1997).
Urbas, A. M., Maldovan, M., DeRege, P. & Thomas, E. L. Bicontinuous cubic block copolymer photonic crystals. Adv. Mater. 14, 1850–1853 (2002).
Lee, J. H. et al. 25th anniversary article: ordered polymer structures for the engineering of photons and phonons. Adv. Mater. 26, 532–569 (2014).
Laurer, J. H. et al. Microstructural analysis of a cubic bicontinuous morphology in a neat SIS triblock copolymer. Macromolecules 30, 3938–3941 (1997).
Jinnai, H. et al. Direct measurement of interfacial curvature distributions in a bicontinuous block copolymer morphology. Phys. Rev. Lett. 84, 518–521 (2000).
Li, Z. H. et al. Linking experiment and theory for three-dimensional networked binary metal nanoparticle-triblock terpolymer superstructures. Nat. Commun. 5, 3247 (2014).
Ercius, P., Alaidi, O., Rames, M. J. & Ren, G. Electron tomography: a three-dimensional analytic tool for hard and soft materials research. Adv. Mater. 27, 5638–5663 (2015).
Feng, X. Y., Guo, H. & Thomas, E. L. Topological defects in tubular network block copolymers. Polymer 168, 44–52 (2019).
Hayworth, K. J. et al. Ultrastructurally smooth thick partitioning and volume stitching for large-scale connectomics. Nat. Methods 12, 319–322 (2015).
Narayan, K. & Subramaniam, S. Focused ion beams in biology. Nat. Methods 12, 1021–1031 (2015).
Schick, M. Avatars of the gyroid. Physica A 251, 1–11 (1998).
Schroeder-Turk, G. E., Fogden, A. & Hyde, S. T. Bicontinuous geometries and molecular self-assembly: comparison of local curvature and global packing variations in genus-three cubic, tetragonal and rhombohedral surfaces. Eur. Phys. J. B 54, 509–524 (2006).
Hajduk, D. A. et al. The gyroid—a new equilibrium morphology in weakly segregated diblock copolymers. Macromolecules 27, 4063–4075 (1994).
Matsen, M. W. The standard Gaussian model for block copolymer melts. J. Phys. Condens. Matter 14, R21–R47 (2002).
Cochran, E. W., Garcia-Cervera, C. J. & Fredrickson, G. H. Stability of the gyroid phase in diblock copolymers at strong segregation. Macromolecules 39, 2449–2451 (2006).
Lo, T. Y. et al. Phase transitions of polystyrene-b-poly(dimethylsiloxane) in solvents of varying selectivity. Macromolecules 46, 7513–7524 (2013).
Toombes, G. E. S. et al. A re-evaluation of the morphology of a bicontinuous block copolymer-ceramic material. Macromolecules 40, 8974–8982 (2007).
Faber, M., Hofman, A. H., Loos, K. & ten Brinke, G. Highly ordered structure formation in RAFT-synthesized PtBOS-b-P4VP diblock copolymers. Macromol. Rapid Commun. 37, 911–919 (2016).
Chavis, M. A., Smilgies, D. M., Wiesner, U. B. & Ober, C. K. Widely tunable morphologies in block copolymer thin films through solvent vapor annealing using mixtures of selective solvents. Adv. Funct. Mater. 25, 3057–3065 (2015).
Dolan, J. A. et al. Controlling self-assembly in gyroid terpolymer films by solvent vapor annealing. Small 14, 1802401 (2018).
Henderson, R., Baldwin, J. M., Downing, K. H., Lepault, J. & Zemlin, F. Structure of purple membrane from halobacterium halobium: recording, measurement and evaluation of electron micrographs at 3.5 Å resolution. Ultramicroscopy 19, 147–178 (1986).
Große-Brauckmann, K. Gyroids of constant mean curvature. Exp. Math. 6, 33–50 (1997).
Thomas, E. L., Anderson, D. M., Henkee, C. S. & Hoffman, D. Periodic area-minimizing surfaces in block copolymers. Nature 334, 598–601 (1988).
Matsen, M. W. & Bates, F. S. Origins of complex self-assembly in block copolymers. Macromolecules 29, 7641–7644 (1996).
Schroeder, G. E., Ramsden, S. J., Christy, A. G. & Hyde, S. T. Medial surfaces of hyperbolic structures. Eur. Phys. J. B 35, 551–564 (2003).
Prasad, I., Jinnai, H., Ho, R. M., Thomas, E. L. & Grason, G. M. Anatomy of triply-periodic network assemblies: characterizing skeletal and inter-domain surface geometry of block copolymer gyroids. Soft Matter 14, 3612–3623 (2018).
Olmsted, P. D. & Milner, S. T. Strong segregation theory of bicontinuous phases in block copolymers. Macromolecules 31, 4011–4022 (1998).
Grason, G. M. The packing of soft materials: molecular asymmetry, geometric frustration and optimal lattices in block copolymer melts. Phys. Rep. 433, 1–64 (2006).
Ivanov, A. O. & Tuzhilin, A. A. Minimal Networks: The Steiner Problem and Its Generalizations (CRC Press, 1994).
Alex, J. & Grosse-Braukmann, K. Periodic Steiner networks minimizing length. Preprint at http://arxiv.org/abs/1705.02471 (2017).
Fruchart, M. et al. Soft self-assembly of Weyl materials for light and sound. Proc. Natl Acad. Sci. USA 115, E3655–E3664 (2018).
Cantoni, M. & Holzer, L. Advances in 3D focused ion beam tomography. MRS Bull. 39, 354–360 (2014).
Kotula, P. G., Rohrer, G. S. & Marsh, M. P. Focused ion beam and scanning electron microscopy for 3D materials characterization. MRS Bull. 39, 361–365 (2014).
Wilson, J. R. et al. Three-dimensional reconstruction of a solid-oxide fuel-cell anode. Nat. Mater. 5, 541–544 (2006).
Kim, S., Park, M. J., Balsara, N. P., Liu, G. & Minor, A. M. Minimization of focused ion beam damage in nanostructured polymer thin films. Ultramicroscopy 111, 191–199 (2011).
Arora, A. et al. Broadly accessible self-consistent field theory for block polymer materials discovery. Macromolecules 49, 4675–4690 (2016).
Brakke, K. A. The surface evolver. Exp. Math. 1, 141–165 (1992).
Beucher, S. & Meyer, F. in Mathematical Morphology in Image Processing (ed. Dougherty, E. R.) 433–481 (CRC Press, 1993).
Oppenheim, A. V. & Schafer, R. W. Discrete-Time Signal Processing (Prentice-Hall, 1999).
Lee, T. C., Kashyap, R. L. & Chu, C. N. Building skeleton models via 3-D medial surface axis thinning algorithms. CVGIP Graph. Models Image Proc. 56, 462–478 (1994).
Acknowledgements
Primary support for this research was provided through the US Department of Energy (DOE), Office of Basic Energy Sciences, Division of Materials Sciences and Engineering under award DE-SC0014599 to G.M.G. and E.L.T. Use of the Advanced Photon Source at the Argonne National Laboratory was supported by the US DOE, Office of Science, and Office of Basic Energy Sciences. A grant from the National Science Foundation to E.L.T. under award DMR 1742864 supported the development of SVSEM techniques. A grant from the Ministry of Science and Technology supported the R.-M.H. group. SCF calculations were performed on the UMass Cluster at the Massachusetts Green High Performance Computing Center. We thank B. van Leer, T. Lacon and T. Santisteban from Thermo Fisher for insights into the hardware and software underlying SVSEM tomography.
Author information
Authors and Affiliations
Contributions
The research was designed and supervised by E.L.T. and G.M.G. The BCP was synthesized by A.A., and R.-M.H. was responsible for processing samples. The SVSEM technique was developed by H.G., M. Z. and X.F., and carried out by X.F. and H.G. K.Y. provided modifications to the SVSEM software. Numerical algorithms for morphology analysis were developed by C.J.B. with I.P., and applied by C.J.B., X.F. and A.R. SCF computations were carried out and analysed by A.R. The manuscript was written by E.L.T, G.M.G., X.F., C.J.B. and A.R.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Variation in the unit-cell parameters of triclinic unit cells within one grain.
Unit-cell parameters at five different places (1–5) within one grain are measured in real space. The result indicates that the structure is coherent but non-cubic, with unit-cell parameters exhibiting only small deviations throughout the many-cubic micrometre grain.
Extended Data Fig. 2 Strain eigenvector mapping from a cDG lattice to a vtDG lattice within the slicing coordinate frame of reference.
Directions and magnitudes of deviations from cubic symmetry in different grains of the sample are not correlated with the ion-milling (slicing) direction (Z).
Extended Data Fig. 3 Mean (H) and Gaussian (K) distribution of IMDS curvature in theoretical models.
a, b, Distributions are shown for a constant mean curvature (CMC) surface (a) and for a constant matrix thickness (CMT) surface (b). c–f, Distributions obtained from SCF theoretical calculations of cDG as a function of segregation strength: χN = 12.5 (c), χN = 15 (d), χN = 25 (e) and χN = 35 (f). As in the main text, D is the cubic unit cell repeat length.
Extended Data Fig. 4
Histogram showing the internode angles of experimental vtDG (from SVSEM) and non-affine triclinic SCF models.
Extended Data Fig. 5 SAXS pattern from a region of the bulk polygranular PS-PDMS sample.
The structure can be nominally associated with a double-gyroid morphology, with an average cubic lattice parameter of D = 130 nm. Diffraction from the {110}tDG and {200}tDG families, which are forbidden for the cubic \(Ia\bar{3}d\) space group, are observed, indicating the non-affine deformation of the cubic double-gyroid lattice.
Extended Data Fig. 6
The workflow for collection and analysis of SVSEM tomography data. See Methods for more details.
Extended Data Fig. 7 Acquisition and processing of SVSEM images.
a, Illustration of the SVSEM reconstruction method. In step 1, low-energy incident electrons (1 KeV) are used to image the near-surface region of a bulk sample. In step 2, a Ga+ beam is used to slice a roughly 3-nm-thick section from the sample surface. In step 3, electrons are again used to image the ion-beam-milled sample surface. The process is repeated. With a large enough number of images (more than 200), the 3D morphology can be constructed via alignment of the stack of slices. b, Different sample stage positions are used for undistorted imaging during slice-and-view. i, For ion milling during slicing, the sample observing surface is parallel to the ion beam. ii, For electron imaging, the sample observing surface is perpendicular to the electron beam.
Extended Data Fig. 8 Secondary-electron images acquired with different electron-accelerating voltages.
Corresponding raw greyscale pixel-intensity distributions are presented blow the electron images. With a lower accelerating voltage, there is a clear binary separation of the pixels into a dark peak (left) and a bright peak (right). Each image is from a freshly sliced region.
Extended Data Fig. 9 Alignment fiducials and monitoring of slice thickness during experiments.
a, An X-shaped fiducial (within the red square) in ion-beam view is used for the registration of FIB slicing. b, An X-shaped fiducial (within the yellow square) in electron-beam view is used for registration of electron imaging. The round cross-section of the perpendicularly drilled hole (within the orange square) is used for the fine registration of secondary-electron images. c, A secondary-electron image used for data acquisition, showing an ion-milled hole (within the orange square) used for fine registration. d, Monitoring of slice thickness: we measured the distance between the milling surface of the nth slice and the milling surface of the first slice (total slice thickness d) from FIB images, and then plotted d versus (n − 1). This reveals a linear relationship with a slope of 2.96 ± 0.01, which is the averaged slice thickness (in nm).
Extended Data Fig. 10 Monitoring of potential SEM image rotation during FIB-SEM image collection.
a, SEM raw data image of the region of interest, with two holes drilled normal to the slice surface by the FIB. b, c, Side-view snapshots of 3D reconstructed holes 1 and 2 (the corresponding rotational videos are in Supporting Video 3). The image stack (80 slices) was aligned using hole 1. The reconstruction of hole 2 is still symmetric, indicating no image rotation.
Extended Data Fig. 11 Important Fourier components of the experimental double-gyroid structure.
The overall intensity of each diffraction family was normalized by the strongest {211}tDG family from the 3D FFT of the region containing approximately 160 unit cells (the same region as in Fig. 4f, which shows the intensity of each individual peak). The overall normalized intensity data are plotted against their associated cubic q value for those planes. For our reconstructions, we use a Bragg filter that selects peaks above an intensity threshold of 10−7 (Imin) for associated q values smaller than 0.2 nm−1.
Supplementary information
Supplementary Video 1
Comparison video of slicing along c direction of the 2 × 2 × 2 unit cell volume box (Fig. 1b) and slicing of corresponding SCF tDG.
Supplementary Video 2
Rotational view of a rendering of 3D FFT analysis from a region containing approximately 160 unit cells (same region as Fig. 1c) before Bragg filtering.
Supplementary Video 3
Rotational view of 3D reconstructions of hole 1 and hole 2, which are presented in Extended Data Fig. 10.
Rights and permissions
About this article
Cite this article
Feng, X., Burke, C.J., Zhuo, M. et al. Seeing mesoatomic distortions in soft-matter crystals of a double-gyroid block copolymer. Nature 575, 175–179 (2019). https://doi.org/10.1038/s41586-019-1706-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-019-1706-1
This article is cited by
-
Medial packing and elastic asymmetry stabilize the double-gyroid in block copolymers
Nature Communications (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.