Over the past few decades, several molecular cages, hosts and nanoporous materials enclosing nanometre-sized cavities have been reported1,2,3,4,5, including coordination-driven nanocages6. Such nanocages have found widespread use in molecular recognition, separation, stabilization and the promotion of unusual chemical reactions, among other applications3,4,5,6,7,8,9,10. Most of the reported nanospaces within molecular hosts are confined by aromatic walls, the properties of which help to determine the host–guest behaviour. However, cages with nanospaces surrounded by antiaromatic walls have not yet been developed, owing to the instability of antiaromatic compounds; as such, the effect of antiaromatic walls on the properties of nanospaces remains unknown. Here we demonstrate the construction of an antiaromatic-walled nanospace within a self-assembled cage composed of four metal ions with six identical antiaromatic walls. Calculations indicate that the magnetic effects of the antiaromatic moieties surrounding this nanospace reinforce each other. This prediction is confirmed by 1H nuclear magnetic resonance (NMR) signals of bound guest molecules, which are observed at chemical shift values of up to 24 parts per million (ppm), owing to the combined antiaromatic deshielding effect of the surrounding rings. This value, shifted 15 ppm from that of the free guest, is the largest 1H NMR chemical shift displacement resulting from an antiaromatic environment observed so far. This cage may thus be considered as a type of NMR shift reagent, moving guest signals well beyond the usual NMR frequency range and opening the way to further probing the effects of an antiaromatic environment on a nanospace.
This is a preview of subscription content
Subscribe to Nature+
Get immediate online access to the entire Nature family of 50+ journals
Subscribe to Journal
Get full journal access for 1 year
only $3.90 per issue
All prices are NET prices.
VAT will be added later in the checkout.
Tax calculation will be finalised during checkout.
Get time limited or full article access on ReadCube.
All prices are NET prices.
All data needed to evaluate the conclusions given in the paper are present in the paper and Supplementary Information. Any additional data related to this paper may be requested from the authors. Crystallographic data for the structure reported in this paper has been deposited at the Cambridge Crystallographic Data Centre (deposition number 1893553) and can be obtained free of charge via www.ccdc.cam.ac.uk/data_request/cif.
Corma, A. State of the art and future challenges of zeolites as catalysts. J. Catal. 216, 298–312 (2003).
Kitagawa, S., Kitaura, R. & Noro, S. Functional porous coordination polymers. Angew. Chem. Int. Ed. 43, 2334–2375 (2004).
Hooley, R. J. & Rebek, J. Jr Chemistry and catalysis in functional cavitands. Chem. Biol. 16, 255–264 (2009).
Zhang, G. & Mastalerz, M. Organic cage compounds – from shape-persistency to function. Chem. Soc. Rev. 43, 1934–1947 (2014).
Cook, T. R., Zheng, Y.-R. & Stang, P. J. Metal-organic frameworks and self-assembled supramolecular coordination complexes: comparing and contrasting the design, synthesis, and functionality of metal-organic materials. Chem. Rev. 113, 734–777 (2013).
Fujita, M. et al. Self-assembly of ten molecules into nanometre-sized organic host frameworks. Nature 378, 469–471 (1995).
Ariga, K., Ito, H., Hill, J. P. & Tsukube, H. Molecular recognition: from solution science to nano/materials technology. Chem. Soc. Rev. 41, 5800–5835 (2012).
Galan, A. & Ballester, P. Stabilization of reactive species by supramolecular encapsulation. Chem. Soc. Rev. 45, 1720–1737 (2016).
Yoshizawa, M., Klosterman, J. K. & Fujita, M. Functional molecular flasks: new properties and reactions within discrete, self-assembled hosts. Angew. Chem. Int. Ed. 48, 3418–3438 (2009).
Yoshizawa, M. & Yamashina, M. Coordination-driven nanostructures with polyaromatic shells. Chem. Lett. 46, 163–171 (2017).
Mugridge, J. S., Bergman, R. G. & Raymond, K. N. 1H NMR chemical shift calculations as a probe of supramolecular host–guest geometry. J. Am. Chem. Soc. 133, 11205–11212 (2011).
Garcia-Borràs, M., Osuna, S., Luis, J. M., Swart, M. & Solà, M. The role of aromaticity in determining the molecular structure and reactivity of (endohedral metallo)fullerenes. Chem. Soc. Rev. 43, 5089–5105 (2014).
Nakamura, Y. et al. A directly fused tetrameric porphyrin sheet and its anomalous electronic properties that arise from the planar cyclooctatetraene core. J. Am. Chem. Soc. 128, 4119–4127 (2006).
Peeks, M. D., Claridge, T. D. W. & Anderson, H. L. Aromatic and antiaromatic ring currents in a molecular nanoring. Nature 541, 200–203 (2017).
Breslow, R. Antiaromaticity. Acc. Chem. Res. 6, 393–398 (1973).
Nishinaga, T., Ohmae, T. & Iyoda, M. Recent studies on the aromaticity and antiaromaticity of planar cyclooctatetraene. Symmetry (Basel) 2, 76–97 (2010).
Zeng, Z. et al. Pro-aromatic and anti-aromatic π-conjugated molecules: an irresistible wish to be diradicals. Chem. Soc. Rev. 44, 6578–6596 (2015).
Hensel, T., Anderson, N. N., Plesner, M. & Pittelkow, M. Synthesis of heterocyclic circulenes and related structures. Synlett 27, 498–525 (2016).
Reddy, B. K., Basavarajappa, A., Ambhore, M. D. & Anand, V. G. Isophlorinoids: the antiaromatic congeners of porphyrinoids. Chem. Rev. 117, 3420–3443 (2017).
Szyszko, B., Białek, M. J., Pacholska-Dudziak, E. & Latos-Grażyński, L. Flexible porphyrinoids. Chem. Rev. 117, 2839–2909 (2017).
Ito, T., Hayashi, Y., Shimizu, S., Shin, J.-Y., Kobayashi, N. & Shinokubo, H. Gram-scale synthesis of nickel(ii) norcorrole: the smallest antiaromatic porphyrinoid. Angew. Chem. Int. Ed. 51, 8542–8545 (2012).
Deng, Z., Li, X., Stępień, M. & Chmielewski, P. J. Nitration of norcorrolatonickel(ii): first observation of a diatropic current in a system comprising a norcorrole ring. Chem. Eur. J. 22, 4231–4246 (2016).
Nozawa, R. et al. Stacked antiaromatic porphyrins. Nat. Commun. 7, 13620 (2016).
Yoshida, T. & Shinokubo, H. Direct amination of antiaromatic Niii norcorrole. Mater. Chem. Front. 1, 1853–1857 (2017).
Li, X., Meng, Y., Yi, P., Stępień, M. & Chmielewski, P. J. Pyridine-fused bis(norcorrole) through Hantzsch-type cyclization: enhancement of antiaromaticity by an aromatic bridge. Angew. Chem. Int. Ed. 56, 10810–10814 (2017).
Kawashima, H., Hiroto, S. & Shinokubo, H. Acid-mediated migration of bromide in an antiaromatic porphyrinoid: preparation of two regioisomeric Ni(ii) bromonorcorroles. J. Org. Chem. 82, 10425–10432 (2017).
Zhang, D., Ronson, T. K. & Nitschke, J. R. Functional capsules via subcomponent self-assembly. Acc. Chem. Res. 51, 2423–2436 (2018).
Rizzuto, F. J., Wood, D. M., Ronson, T. K. & Nitschke, J. R. Tuning the redox properties of fullerene clusters within a metal−organic capsule. J. Am. Chem. Soc. 139, 11008–11011 (2017).
Povie, G., Segawa, Y., Nishihara, T., Miyauchi, Y. & Itami, K. Synthesis of a carbon nanobelt. Science 356, 172–175 (2017).
Brock-Nannestad, T. et al. Tetra-tert-butyltetraoxacirculene and its unusual aggregation behaviour. Eur. J. Org. Chem., 6320–6325 (2011).
This study was supported by the European Research Council (695009) and the UK Engineering and Physical Sciences Research Council (EPSRC, EP/P027067/1). M.Y. acknowledges the Japan Society for the Promotion of Science (JSPS) for an Overseas Research Fellowship. R.L. was funded by a Fondation Wiener-Anspach postdoctoral fellowship. M.P. acknowledges support from the Danish Council for Independent Research (DFF 4181-00206). We thank the NMR service of the University of Cambridge Chemistry Department for NMR experiments. We thank Diamond Light Source for providing time on Beamline I19 (MT15768), and D. Allan and L. Saunders for assistance. The computations were performed at the Research Center for Computational Science, Okazaki, Japan. We appreciate discussions with H. Shinokubo (Nagoya University), M. Yoshizawa (Tokyo Institute of Technology) and T. Soya (Kyoto University).
The authors declare no competing interests.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
When 1 was treated with 1,3-dibromo-5,5-dimethylhydantoin, inseparable mono-, di- and tribrominated products were obtained. As bromination randomly occurred at positions 3, 7, 12 and 16 (that is, adjacent to the mesityl moieties), the 3,12- and 3,16-substituted dibromonorcorroles trans-1a and cis-1a were obtained as the main products (Supplementary Figs. 1, 2). Subsequently, disubstituted trans-1b and cis-1b were obtained by Suzuki–Miyaura cross-coupling at 43% yield as a mixture of two regioisomers (Supplementary Figs. 3, 4). Finally, 3,12-substituted subcomponent 2 could be isolated as a single regioisomer at 46% yield following reduction of the NO2 groups and chromatography (Supplementary Figs. 5–9). Reagents and conditions: (i) 1,3-dibromo-5,5-dimethylhydantoin, CH2Cl2, −78 °C, 1 h, 94% (mixture of trans-1a, cis-1a and other brominated species). (ii) 4-Nitrophenylboronic acid pinacol ester, Pd(PPh3)4, K3PO4, dry THF, 70 °C, 1 h, 43% (mixture of trans-1b and cis-1b). (iii) SnCl2·H2O, dry THF, 70 °C, overnight, 46% (isolated 2).
This file contains detailed additional synthetic procedures, host–guest studies, extended methods, full characterisation data, Supplementary Figures 1–74, Supplementary Tables 1–7 and additional references – see content page for details.
This file contains the crystallographic data for compound 3.
Three-dimensional NICSiso grid within the antiaromatic-walled nanospace. Yellow, orange and red dots represent medium to strong magnetic deshielding regions (NICSiso = 3–6 for yellow, 6–9 for orange and >9 for red). Regions outside the walls and for NICSiso<3 are not shown for clarity. Calculation details are provided in the Supplementary Information.
About this article
Cite this article
Yamashina, M., Tanaka, Y., Lavendomme, R. et al. An antiaromatic-walled nanospace. Nature 574, 511–515 (2019). https://doi.org/10.1038/s41586-019-1661-x
Self-assembly of a photoluminescent metal-organic cage and its spontaneous aggregation in dilute solutions enabling time-dependent emission enhancement
Science China Chemistry (2022)
Nature Reviews Materials (2021)
A host–guest semibiological photosynthesis system coupling artificial and natural enzymes for solar alcohol splitting
Nature Communications (2021)
Photoacoustic imaging-guided chemo-photothermal combinational therapy based on emissive Pt(II) metallacycle-loaded biomimic melanin dots
Science China Chemistry (2021)