Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Intrinsically stable organic solar cells under high-intensity illumination


Organic photovoltaic cells are now approaching commercially viable efficiencies, particularly for applications that make use of their unique potential for flexibility and semitransparency1,2,3. However, their reliability remains a major concern, as even the most stable devices reported so far degrade within only a few years4,5,6,7,8. This has led to the belief that short operational lifetimes are an intrinsic disadvantage of devices that are fabricated using weakly bonded organic materials—an idea that persists despite the rapid growth and acceptance of organic light-emitting devices, which can achieve lifetimes of several million hours9. Here we study an extremely stable class of thermally evaporated single-junction organic photovoltaic cells. We accelerated the ageing process by exposing the packaged cells to white-light illumination intensities of up to 37 Suns. The cells maintained more than 87 per cent of their starting efficiency after exposure for more than 68 days. The degradation rate increases superlinearly with intensity, leading to an extrapolated intrinsic lifetime, T80, of more than 4.9 × 107 hours, where T80 is the time taken for the power conversion efficiency to decrease to 80 per cent of its initial value. This is equivalent to 27,000 years outdoors. Additionally, we subjected a second group of organic photovoltaic cells to 20 Suns of ultraviolet illumination (centred at 365 nanometres) for 848 hours, a dose that would take 1.7 × 104 hours (9.3 years) to accumulate outdoors. No efficiency loss was observed over the duration of the test. Overall, we find that organic solar cells packaged in an inert atmosphere can be extremely stable, which is promising for their future use as a practical energy-generation technology.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Device structure, molecular structures, and OPV ageing data under illumination.
Fig. 2: Photocurrent and electroluminescence losses.
Fig. 3: Assessment of the stability of active-layer materials.
Fig. 4: Ageing acceleration factor and lifetime estimation.

Similar content being viewed by others

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.


  1. Che, X., Li, Y., Qu, Y. & Forrest, S. R. High fabrication yield organic tandem photovoltaics combining vacuum- and solution-processed subcells with 15% efficiency. Nat. Energy 3, 422–427 (2018).

    Article  CAS  ADS  Google Scholar 

  2. Li, Y. et al. High efficiency near-infrared and semitransparent non-fullerene acceptor organic photovoltaic cells. J. Am. Chem. Soc. 139, 17114–17119 (2017).

    Article  CAS  Google Scholar 

  3. Chang, S., Cheng, P., Li, G. & Yang, Y. Transparent polymer photovoltaics for solar energy harvesting and beyond. Joule 2, 1039–1054 (2018).

    Article  CAS  Google Scholar 

  4. Peters, C. H. et al. High efficiency polymer solar cells with long operating lifetimes. Adv. Energy Mater. 1, 491–494 (2011).

    Article  CAS  Google Scholar 

  5. Baran, D. et al. Reducing the efficiency-stability-cost gap of organic photovoltaics with highly efficient and stable small molecule acceptor ternary solar cells. Nat. Mater. 16, 363–369 (2017).

    Article  CAS  ADS  Google Scholar 

  6. Gasparini, N. et al. Burn-in free nonfullerene-based organic solar cells. Adv. Energy Mater. 7, 1700770 (2017).

    Article  Google Scholar 

  7. Burlingame, Q. et al. Reliability of small molecule organic photovoltaics with electron-filtering compound buffer layers. Adv. Energy Mater. 6, 1601094 (2016).

    Article  Google Scholar 

  8. Sapkota, S. B., Spies, A., Zimmermann, B., Dürr, I. & Würfel, U. Promising long-term stability of encapsulated ITO-free bulk-heterojunction organic solar cells under different aging conditions. Sol. Energy Mater. Sol. Cells 130, 144–150 (2014).

    Article  CAS  Google Scholar 

  9. Burrows, P. E. & Forrest, S. R. Operating lifetime of phosphorescent organic light emitting devices. Appl. Phys. Lett. 76, 2493 (2000).

    Article  CAS  ADS  Google Scholar 

  10. Zhang, H. et al. Photochemical transformations in fullerene and molybdenum oxide affect the stability of bilayer organic solar cells. Adv. Energy Mater. 5, 1–9 (2014).

    ADS  Google Scholar 

  11. Liu, X., Ding, K., Panda, A. & Forrest, S. R. Charge transfer states in dilute donor–acceptor blend organic heterojunctions. ACS Nano 10, 7619–7626 (2016).

    Article  CAS  Google Scholar 

  12. Haillant, O., Dumbleton, D. & Zielnik, A. An Arrhenius approach to estimating organic photovoltaic module weathering acceleration factors. Sol. Energy Mater. Sol. Cells 95, 1889–1895 (2011).

    Article  CAS  Google Scholar 

  13. F́ry, C., Racine, B., Vaufrey, D., Doyeux, H. & Ciǹ, S. Physical mechanism responsible for the stretched exponential decay behavior of aging organic light-emitting diodes. Appl. Phys. Lett. 87, 1–3 (2005).

    Google Scholar 

  14. Hermenau, M. et al. The effect of barrier performance on the lifetime of small-molecule organic solar cells. Sol. Energy Mater. Sol. Cells 97, 102–108 (2012).

    Article  CAS  Google Scholar 

  15. Scholz, S., Kondakov, D., Lüssem, B. & Leo, K. Degradation mechanisms and reactions in organic light-emitting devices. Chem. Rev. 115, 8449–8503 (2015).

    Article  CAS  Google Scholar 

  16. Zhang, Y., Lee, J. & Forrest, S. R. Tenfold increase in the lifetime of blue phosphorescent organic light-emitting diodes. Nat. Commun. 5, 5008 (2014).

    Article  CAS  ADS  Google Scholar 

  17. Habte, A., Sengupta, M. & Lopez, A. Evaluation of the National Solar Radiation Database (NSRDB): 1998–2015. Report No. NREL/TP-5D00-67722 (National Renewable Energy Laboratory, 2017).

  18. Garner, L. E. et al. Photobleaching dynamics in small molecule vs. polymer organic photovoltaic blends with 1,7-bis-trifluoromethylfullerene. J. Mater. Chem. A 6, 4623–4628 (2018).

    Article  CAS  Google Scholar 

  19. Lakhwani, G., Rao, A. & Friend, R. H. Bimolecular recombination in organic photovoltaics. Annu. Rev. Phys. Chem. 65, 557–581 (2014).

    Article  CAS  ADS  Google Scholar 

  20. Bartesaghi, D. et al. Competition between recombination and extraction of free charges determines the fill factor of organic solar cells. Nat. Commun. 6, 7083 (2015).

    Article  CAS  ADS  Google Scholar 

  21. Dibb, G. F. A., Jamieson, F. C., Maurano, A., Nelson, J. & Durrant, J. R. Limits on the fill factor in organic photovoltaics: distinguishing nongeminate and geminate recombination mechanisms. J. Phys. Chem. Lett. 4, 803–808 (2013).

    Article  CAS  Google Scholar 

  22. Vandewal, K., Tvingstedt, K., Gadisa, A., Inganäs, O. & Manca, J. V. On the origin of the open-circuit voltage of polymer–fullerene solar cells. Nat. Mater. 8, 904–909 (2009).

    Article  CAS  ADS  Google Scholar 

  23. Rau, U. Reciprocity relation between photovoltaic quantum efficiency and electroluminescent emission of solar cells. Phys. Rev. B 76, 085303 (2007).

    Article  ADS  Google Scholar 

  24. Franke, R., Maennig, B., Petrich, A. & Pfeiffer, M. Long-term stability of tandem solar cells containing small organic molecules. Sol. Energy Mater. Sol. Cells 92, 732–735 (2008).

    Article  CAS  Google Scholar 

  25. Pearson, A. J. et al. Critical light instability in CB/DIO processed PBDTTT-EFT:PC71BM organic photovoltaic devices. Org. Electron. 30, 225–236 (2016).

    Article  CAS  Google Scholar 

  26. Jeong, C. et al. Understanding molecular fragmentation in blue phosphorescent organic light-emitting devices. Org. Electron. 64, 15–21 (2019).

    Article  CAS  Google Scholar 

  27. Giebink, N. C. et al. Intrinsic luminance loss in phosphorescent small-molecule organic light emitting devices due to bimolecular annihilation reactions. J. Appl. Phys. 103, 044509 (2008).

    Article  ADS  Google Scholar 

  28. Lee, J. et al. Hot excited state management for long-lived blue phosphorescent organic light-emitting diodes. Nat. Commun. 8, 1–9 (2017).

    Article  ADS  Google Scholar 

  29. Burlingame, Q. et al. Photochemical origins of burn-in degradation in small molecular weight organic photovoltaic cells. Energy Environ. Sci. 8, 1005–1010 (2015).

    Article  CAS  Google Scholar 

  30. Wilson, P. F. & Ma, M. T. Fields radiated by electrostatic discharges. IEEE Trans. Electromagn. Compat. 33, 10–18 (1991).

    Article  ADS  Google Scholar 

  31. Wang, N. et al. Snow cleaning of substrates increases yield of large-area organic photovoltaics. Appl. Phys. Lett. 101, 133901 (2012).

    Article  ADS  Google Scholar 

  32. Burlingame, Q., Zanotti, G., Ciammaruchi, L., Katz, E. A. & Forrest, S. R. Outdoor operation of small-molecule organic photovoltaics. Org. Electron. 41, 274–279 (2017).

    Article  CAS  Google Scholar 

Download references


This work was supported by the United States Department of Energy SunShot Program under awards DE-EE0006708 and DE-EE0005310 and the Department of the Navy, Office of Naval Research under award N00014-17-1-2211.

Author information

Authors and Affiliations



Q.B. constructed the high-intensity LED ageing setup and designed experimental protocols. Q.B. and X.H. fabricated all samples, performed all measurements, and analysed and fitted the data. X.L. assisted with electroluminescence measurements and performed the transient photoluminescence spectroscopy. C.J. collected the mass spectra on organic films. C.C. and X.H. constructed the ultraviolet ageing system and C.C. performed the error analysis of the acceleration factor. S.R.F. supervised the project and analysed the data. The manuscript was written by Q.B., X.H. and S.R.F., and edited by all co-authors.

Corresponding author

Correspondence to Stephen R. Forrest.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Spectrum of an Xe-arc solar simulator lamp over time.

Spectrum (left axis) of the Xe-arc lamp used for 1-Sun ageing of the OPVs, both before (black) and after (red) operating continuously for 2,000 h. EQEs (right axis) of the Si reference cell (blue) used for calibrating the intensity of the Xe-arc lamp intensity, and the EQE of a DBP:C70 OPV cell (pink). Previously, we reported the operational stability of DBP:C70 OPV cells with an identical structure to those studied here, and found that JSC degraded linearly with time when measured in situ under continuous illumination from a Xe-arc lamp7. The spectrum of the Xe-arc lamp red-shifts with time as shown, leading to an underestimation of the lifetime of the OPV cells. In this study, the EQE and current–voltage characteristics were measured between solar-ageing periods to avoid this error.

Extended Data Fig. 2 Charge-extraction efficiency and wavelength-dependent EQE spectra.

a, Charge-extraction efficiency at V = 0 (extracted from the reverse-bias photocurrent data, as described in Methods) plotted against time. b, Wavelength-dependent EQE spectra after 47 days of ageing at 9.5, 20 and 37 Suns. The inset shows the change in EQE after 47 days; that is, ΔEQE = [EQE(t = 47 days) − EQEfresh]/EQEfresh.

Extended Data Fig. 3 High-intensity LED ageing system and performance characterization.

a, b, Side (a) and top (b) views of the water-cooled white-LED setup used to supply high-intensity illumination to the OPVs. Each of the four stations consists of a cool-white LED (colour temperature = 5,000 K) with a heat sink and active water cooling of an Al block attached to the substrate. Cylindrical Ag-coated light pipes are used to collimate the LED light onto the OPV, shown detail in c. Despite the reflectivity of the Ag coating being greater than 99%, the OPV and its reflections are visible through the pipe owing to the extreme light intensity within. d, The spectrum of the white LEDs, ultraviolet LED and Xe-arc lamp measured at the surface of the OPV, compared with the AM1.5G spectrum. e, Surface temperature of the OPV cells plotted against intensity, across the range of white LED output intensities. The three ageing conditions used for OPV cells and thin films are indicated on the plot.

Extended Data Fig. 4 Current–voltage characteristics of aged OPVs.

Dark current (Jdark, left axis) and current under 1-Sun illumination (J1-Sun, right axis) as a function of applied voltage for an OPV before and after ageing for 47 days under illumination at 37 Suns.

Extended Data Fig. 5 Correlation between degradation of VOC and decrease in electroluminescence intensity.

To quantify the effect of recombination on the performance of the device, we express the change in VOC as: \(\Delta {V}_{{\rm{OC}}}={V}_{{\rm{OC}}}\left(0\right)-{V}_{{\rm{OC}}}\left(t\right)=\frac{{k}_{{\rm{B}}}T}{q}{\rm{ln}}\left(\frac{{J}_{{\rm{SC}}}\left(0\right)}{{J}_{{\rm{SC}}}\left(t\right)}\frac{{{\rm{EQE}}}_{{\rm{EL}}}\left(t\right)}{{{\rm{EQE}}}_{{\rm{EL}}}\left(0\right)}\frac{\int {{\rm{EQE}}}_{{\rm{PV}}}\left(t\right){\Phi }_{{\rm{BB}}}{\rm{d}}E}{\int {{\rm{EQE}}}_{{\rm{PV}}}\left(0\right){\Phi }_{{\rm{BB}}}{\rm{d}}E}\right)\) where kB is Boltzmann’s constant, T is the cell temperature, q is the charge of an electron, EQEEL is the electroluminescence quantum efficiency of the charge-transfer states, EQEPV is the photovoltaic quantum efficiency, ΦBB is the black-body flux incident on the device, and E is the photon energy22. Predicted values of ΔVOC calculated using the above equation are plotted as a function of time along with the measured change in VOC. For the above equation to accurately predict the change in VOC, each of the parameters should be measured under an illumination intensity of 1 Sun. Because EQEEL was measured in the dark at a constant current density of 4 mA cm−2 rather than at JSC (that is, under 1-Sun illumination), the absolute value of the prediction from the above equation differs from the measured ΔVOC by approximately a factor of 2. Nevertheless, there is a qualitative match between the degradation time constants of the predicted and measured ΔVOC, which suggests that EQEEL measurements are a useful test of recombination and voltage loss in photovoltaic-degradation studies.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Burlingame, Q., Huang, X., Liu, X. et al. Intrinsically stable organic solar cells under high-intensity illumination. Nature 573, 394–397 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing