Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

A weak topological insulator state in quasi-one-dimensional bismuth iodide

A Publisher Correction to this article was published on 21 July 2020

This article has been updated


The major breakthroughs in understanding of topological materials over the past decade were all triggered by the discovery of the Z2-type topological insulator—a type of material that is insulating in its interior but allows electron flow on its surface. In three dimensions, a topological insulator is classified as either ‘strong’ or ‘weak’1,2, and experimental confirmations of the strong topological insulator rapidly followed theoretical predictions3,4,5. By contrast, the weak topological insulator (WTI) has so far eluded experimental verification, because the topological surface states emerge only on particular side surfaces, which are typically undetectable in real three-dimensional crystals6,7,8,9,10. Here we provide experimental evidence for the WTI state in a bismuth iodide, β-Bi4I4. Notably, the crystal has naturally cleavable top and side planes—stacked via van der Waals forces—which have long been desirable for the experimental realization of the WTI state11,12. As a definitive signature of this state, we find a quasi-one-dimensional Dirac topological surface state at the side surface (the (100) plane), while the top surface (the (001) plane) is topologically dark with an absence of topological surface states. We also find that a crystal transition from the β-phase to the α-phase drives a topological phase transition from a nontrivial WTI to a normal insulator at roughly room temperature. The weak topological phase—viewed as quantum spin Hall insulators stacked three-dimensionally13,14—will lay a foundation for technology that benefits from highly directional, dense spin currents that are protected against backscattering.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Crystal structure, transport and band topology calculations for α- and β-Bi4I4.
Fig. 2: Two cleavage surfaces of β-Bi4I4.
Fig. 3: Experimental band structures of α- and β-Bi4I4 as measured by laser-ARPES.
Fig. 4: Surface-selective nano-ARPES of β-Bi4I4 at hv  = 85 eV.

Data availability

The data that support the findings of this study are available from the corresponding authors on reasonable request.

Change history

  • 21 July 2020

    An amendment to this paper has been published and can be accessed via a link at the top of the paper.


  1. Fu, L., Kane, C. L. & Mele, E. J. Topological insulators in three dimensions. Phys. Rev. Lett. 98, 106803 (2007).

    PubMed  ADS  Google Scholar 

  2. Fu, L. & Kane, C. L. Topological insulators with inversion symmetry. Phys. Rev. B 76, 045302 (2007).

    ADS  Google Scholar 

  3. Hasan, M. Z. & Kane, C. L. Topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).

    CAS  ADS  Google Scholar 

  4. Qi, X.-L. & Zhang, S.-C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).

    CAS  ADS  Google Scholar 

  5. Ando, Y. Topological insulator materials. J. Phys. Soc. Jpn 82, 102001 (2013).

    ADS  Google Scholar 

  6. Yan, B., Müchler, L. & Felser, C. Prediction of weak topological insulators in layered semiconductors. Phys. Rev. Lett. 109, 116406 (2012).

    PubMed  ADS  Google Scholar 

  7. Rasche, B. et al. Stacked topological insulator built from bismuth-based graphene sheet analogues. Nat. Mater. 12, 422–425 (2013).

    CAS  PubMed  ADS  Google Scholar 

  8. Tang, P. et al. Weak topological insulators induced by the inter-layer coupling: a first-principles study of stacked Bi2TeI. Phys. Rev. B 89, 041409 (2014).

    ADS  Google Scholar 

  9. Yang, G., Liu, J., Fu, L., Duan, W. & Liu, C. Weak topological insulators in PbTe/SnTe superlattices. Phys. Rev. B 89, 085312 (2014).

    ADS  Google Scholar 

  10. Pauly, C. et al. Subnanometre-wide electron channels protected by topology. Nat. Phys. 11, 338–343 (2015).

    CAS  Google Scholar 

  11. Liu, C.-C., Zhou, J.-J., Yao, Y. & Zhang, F. Weak topological insulators and composite weyl semimetals: β-Bi4X4 (X=Br, I). Phys. Rev. Lett. 116, 066801 (2016).

    PubMed  ADS  Google Scholar 

  12. Autès, G. et al. A novel quasi-one-dimensional topological insulator in bismuth iodide β-Bi4I4. Nat. Mater. 15, 154–158 (2016).

    PubMed  ADS  Google Scholar 

  13. Bernevig, B. A., Hughes, T. L. & Zhang, S.-C. Quantum spin Hall effect and topological phase transition in HgTe quantum wells. Science 314, 1757–1761 (2006).

    CAS  PubMed  ADS  Google Scholar 

  14. Konig, M. et al. Quantum spin Hall insulator state in HgTe quantum wells. Science 318, 766–770 (2007).

    PubMed  ADS  Google Scholar 

  15. von Schnering, H. G., von Benda, H. & Kalveram, C. Wismutmonojodid BiJ, eine Verbindung mit Bi(O) und Bi(II). Z. Anorg. Allg. Chem. 438, 37–52 (1978).

    Google Scholar 

  16. Tran, F. & Blaha, P. Accurate band gaps of semiconductors and insulators with a semilocal exchange-correlation potential. Phys. Rev. Lett. 102, 226401 (2009).

    PubMed  ADS  Google Scholar 

  17. Zhang, H. et al. Topological insulators in Bi2Se3, Bi2Te3 and Sb2Te3 with a single Dirac cone on the surface. Nat. Phys. 5, 438–442 (2009).

    CAS  Google Scholar 

  18. Xia, Y. et al. Observation of a large-gap topological-insulator class with a single Dirac cone on the surface. Nat. Phys. 5, 398–402 (2009).

    CAS  Google Scholar 

  19. Chen, Y. L. et al. Experimental realization of a three-dimensional topological insulator, Bi2Te3. Science 325, 178–181 (2009).

    CAS  PubMed  ADS  Google Scholar 

  20. Imura, K.-I., Takane, Y. & Tanaka, A. Weak topological insulator with protected gapless helical states. Phys. Rev. B 84, 035443 (2011).

    ADS  Google Scholar 

  21. Ringel, Z., Kraus, Y. E. & Stern, A. Strong side of weak topological insulators. Phys. Rev. B 86, 045102 (2012).

    ADS  Google Scholar 

  22. Mong, R. S. K., Bardarson, J. H. & Moore, J. E. Quantum transport and two-parameter scaling at the surface of a weak topological insulator. Phys. Rev. Lett. 108, 076804 (2012).

    PubMed  ADS  Google Scholar 

  23. Yoshimura, Y., Matsumoto, A., Takane, Y. & Imura, K.-I. Perfectly conducting channel on the dark surface of weak topological insulators. Phys. Rev. B 88, 045408 (2013).

    ADS  Google Scholar 

  24. Lau, A., Ortix, C. & van den Brink, J. One-dimensional Dirac electrons on the surface of weak topological insulators. Phys. Rev. B 91, 085106 (2015).

    ADS  Google Scholar 

  25. Sánchez-Barriga, J. et al. Photoemission of Bi2Se3 with circularly polarized light: probe of spin polarization or means for spin manipulation? Phys. Rev. X 4, 011046 (2014).

    Google Scholar 

  26. Ran, Y., Zhang, Y. & Vishwanath, A. One-dimensional topologically protected modes in topological insulators with lattice dislocations. Nat. Phys. 5, 298–303 (2009).

    CAS  Google Scholar 

  27. Liu, C.-X., Qi, X.-L. & Zhang, S.-C. Half quantum spin Hall effect on the surface of weak topological insulators. Physica E 44, 906–911 (2012).

    ADS  Google Scholar 

  28. Slager, R.-J., Mesaros, A., Juričić, V. & Zaanen, J. Interplay between electronic topology and crystal symmetry: dislocation-line modes in topological band insulators. Phys. Rev. B 90, 241403 (2014).

    CAS  ADS  Google Scholar 

  29. Mross, D. F., Essin, A., Alicea, J. & Stern, A. Anomalous quasiparticle symmetries and non-Abelian defects on symmetrically gapped surfaces of weak topological insulators. Phys. Rev. Lett. 116, 036803 (2016).

    PubMed  ADS  Google Scholar 

  30. Filatova, T. G. et al. Electronic structure, galvanomagnetic and magnetic properties of the bismuth subhalides Bi4I4 and Bi4Br4. J. Solid State Chem. 180, 1103 (2007).

    CAS  ADS  Google Scholar 

  31. Iwasa, A., Clay, W. A., Dahl, J. E., Carlson, R. M. K., Shen, Z.-X. & Sasagawa, T. Environmentally friendly refining of diamond-molecules via the growth of large single crystals. Cryst. Growth Des. 10, 870 (2010).

    CAS  Google Scholar 

  32. Blaha, P. et al. Full-potential, linearized augmented plane wave programs for crystalline systems. Comput. Phys. Commun. 59, 399–415 (1990).

    CAS  ADS  Google Scholar 

  33. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    CAS  PubMed  ADS  Google Scholar 

  34. Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).

    MathSciNet  ADS  Google Scholar 

  35. Kuneš, J. et al. Wien2wannier: from linearized augmented plane waves to maximally localized Wannier functions. Comput. Phys. Commun. 181, 1888 (2010).

    MATH  ADS  Google Scholar 

  36. Mostofi, A. A. et al. Wannier90: a tool for obtaining maximally-localised Wannier functions. Comput. Phys. Commun. 178, 685 (2008).

    CAS  MATH  ADS  Google Scholar 

  37. Sancho, M. P. L. et al. Highly convergent schemes for the calculation of bulk and surface Green functions. J. Phys. F  15, 851 (1985).

    ADS  Google Scholar 

  38. Yaji, K. et al. High-resolution three-dimensional spin- and angle-resolved photoelectron spectrometer using vacuum ultraviolet laser light. Rev. Sci. Instrum. 87, 053111 (2016).

    PubMed  ADS  Google Scholar 

  39. Shimojima, T., Okazaki, K. & Shin, S. Low-temperature and high-energy-resolution laser photoemission spectroscopy. J. Phys. Soc. Jpn 84, 072001 (2015).

    ADS  Google Scholar 

  40. Dudin, P. et al. Angle-resolved photoemission spectroscopy and imaging with a submicrometre probe at the SPECTROMICROSCOPY-3.2L beamline of Elettra. J. Synchrotron Radiat. 17, 445–450 (2010).

    CAS  PubMed  Google Scholar 

  41. Jozwiak, C. et al. Widespread spin polarization effects in photoemission from topological insulators. Phys. Rev. B 84, 165113 (2011).

    ADS  Google Scholar 

  42. Heinzmann, U. & Dil, J. H. Spin-orbit-induced photoelectron spin polarization in angle-resolved photoemission from both atomic and condensed matter targets. J. Phys. Condens. Matter 24, 173001 (2012).

    PubMed  ADS  Google Scholar 

  43. Okuda, T. et al. Experimental evidence of hidden topological surface states in PbBi4Te7. Phys. Rev. Lett. 111, 206803 (2013).

    PubMed  ADS  Google Scholar 

Download references


We thank Y. Okada, D. Hamane, M. Lippmaa, Y. Yoshida, T. Miyamachi, T. Hattori, Y. Hasegawa and F. Komori for scanning electron microscope (SEM)/atomic force microscope (AFM)/scanning tunnelling microscope (STM) characterization of the Bi4I4 surface and for fruitful discussions; and Y. Ishida for supporting analysis of data. We thank the Diamond Light Source for access to beamline I05 under proposals SI15095, SI16161 and SI17816, contributing to the results presented here. We also thank the Elettra Light Source for access to the spectromicroscopy beamline. The GISAXS experiments were performed under the approval of Public Finance–Public Accountability Collective (PF–PAC) no. 2016G548. The work done at the Tokyo Institute of Technology was supported by a JST Core Research for Evolutional Science and Technology (CREST) project (JPMJCR16F2) and a Japan Society for the Promotion of Science (JSPS) Grants-in-Aid for Scientific Research (B) (JP16H03847). R.N. acknowledges support from JSPS under KAKENHI grant JP18J21892, and by JSPS through the Program for Leading Graduate Schools (Advanced Leading Course for Photon Science). This work was also supported by the ‘Topological Materials Science’ (JP16H00979) KAKENHI on Innovative Areas from JSPS, and by JSPS KAKENHI grants JP16H06013, JP17K14319, JP16H02209, JP16K13829, and JP18H01165. R.A. acknowledges support from the Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan, under KAKENHI grant JP16H06345.

Reviewer information

Nature thanks J. Sanchez-Bárriga and the other anonymous reviewer(s) for their contribution to the peer review of this work.

Author information

Authors and Affiliations



T.K. and T.Sa. planned the experimental project. R.N. and K.K. conducted the ARPES experiment and analysed the data. M.S., C.B., M.N., M.D.W., K.Y., A.H., H.I., P.D., T.K.K., M.H., V.K, A.G, A.B, S.S. and T.K. supported the ARPES experiment. T.T. and T.Sa. made and characterized single crystals of α- and β-Bi4I4, measured laser-microscope images, and performed transport experiments. T.Sh. performed the GISAXS experiment. R.N. measured SEM images. T.Sa., M.O. and R.A. calculated the band structure and analysed the band topology. R.N., K.K., M.D.W., T.Sa., M.O., T.Sh. and T.K. wrote the paper. All authors discussed the results and commented on the manuscript.

Corresponding authors

Correspondence to T. Sasagawa or Takeshi Kondo.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 X-ray diffraction measurements for α- and β-Bi4I4.

a, b, X-ray diffraction measurements taken with CuKα radiation from the ab planes of α- and β-Bi4I4 crystals used in our experiments. These two crystals were obtained by the quenching procedure (see Methods). The lattice parameters obtained by structural analysis using single-crystal X-ray diffraction are: a = 14.345 Å, b = 4.443 Å, c = 20.112 Å and β = 92.974° for the α-phase; and a = 14.406 Å, b = 4.432 Å, c = 10.475 Å and β = 107.463° for the β-phase.

Extended Data Fig. 2 Theoretical study of the electronic structure of α-Bi4I4.

a, The first Brillouin zone of α-Bi4I4. b, Bulk band structures calculated by GGA without SOC (left), with SOC (middle) and by GGA plus mBJ with SOC (right). The red and blue circles label the parities (±) for the bulk bands at the M and L points. The band topology of the α-phase is estimated to be a normal insulator (NI). c, Projected bulk bands for the top surface (001) of α-Bi4I4. The colour of the lines denotes different kz values.

Extended Data Fig. 3 Theoretical study of the electronic structure of the (001) surface of β-Bi4I4.

ad, Calculated bulk band dispersions for the \(\bar{{\rm{M}}}\) and \(\bar{\Gamma }\) points of the (001) surface, depending on the topological phase. Colours denote different kz values. eh, Calculation of the band structures, including surface states (SS), for the \(\bar{{\rm{M}}}\) and \(\bar{\Gamma }\) points of the (001) surface depending on the topological phase.

Extended Data Fig. 4 Spin texture of the quasi-1D Dirac state in β-Bi4I4.

a, Experimental geometry used for the spin-resolved measurements. We used s-polarization (vertical polarization) of incident light and measured three-dimensional spin polarizations, Sx, Sy and Sz. b, Schematic illustration of the band structure for the spin-resolved measurements around \(\bar{{\rm{Z}}}\). The solid lines indicate the TSSs; the grey areas indicate the bulk valence band (BVB) and the bulk conduction band (BCB). The dotted lines denote the wavenumber (ky) corresponding to the measured angles. The red and blue arrows show the direction of the measured spin polarization along z-axis. c, Spin texture of the constant energy contour for the (100) surface of β-Bi4I4 obtained by first-principles calculations. The red arrows indicate the directions of the spin polarizations of the TSSs at each momentum point. The energy is set at 0.05 eV to duplicate the Fermi surface obtained in the ARPES experiment. df, Spin-resolved photoelectron intensities around \(\bar{{\rm{Z}}}\) (θ = 49°) for the x- (d), y- (e) and and z- (f) axes, where x is perpendicular to the (100) plane, while y and z are in-plane. gi, Corresponding spin polarizations for the x- (g), y- (h) and z- (i) axes. Red and blue areas indicate positive and negative spin polarizations, respectively, of photoelectrons.

Extended Data Fig. 5 Angle-resolved photoemssion spectra of α- and β-Bi4I4 measured at hv  = 85 eV and 6.994 eV.

a, Experimental geometry of synchrotron-based ARPES at  = 85 eV. b, c, Constant energy contours at EF for α- and β-Bi4I4. The ARPES intensities are integrated within an energy window of 30 meV about the chemical potential. The dashed lines denote the two-dimensional Brillouin zone of the projected (001) surface. d, e, Band dispersion along the high-symmetry direction \(\bar{\Gamma }\) – \(\bar{{\rm{M}}}{\prime} \). f, g, Magnified intensity maps around the \(\bar{\Gamma }\) point. h, MDCs at EF around the \(\bar{\Gamma }\) point. i, Energy-distribution curves (EDCs) at the \(\bar{\Gamma }\) point. j, k, ARPES images measured at  = 6.994 eV for the α-phase (j) and the β-phase (k) (these panels are duplicates of Fig. 3f, j (θ = 28°), respectively). l, EDCs along the red dotted lines in panels j, k. The black arrows indicate the peak positions of the bulk valence bands; the data clearly show the presence of bilayer splitting in the α-phase, consistent with our theoretical calculations (Extended Data Fig. 2c).

Extended Data Fig. 6 Polarization dependence of the quasi-1D TSS of β-Bi4I4 measured with a 6.994-eV laser.

a, Experimental geometry of laser-ARPES, showing the direction of s- and p-polarized light. b, Fermi surface mapping obtained with p-polarized light. c, d, ARPES band maps across the \(\bar{\Gamma }\) point of the (100) surface (red arrow in b) taken with p-polarized light (c) and s-polarized light (d). e, f, As for c, d, but with the momentum cut across the \(\bar{{\rm{Z}}}\) point of the (100) surface (yellow arrow in b). The quasi-1D TSSs are observed with both p- and s-polarized light, in agreement with the orbital characters obtained by first-principles calculations (Extended Data Fig. 7).

Extended Data Fig. 7 Orbital characters of the TSSs in β-Bi4I4.

a, Calculated constant energy contour for the (100) surface of β-Bi4I4. The energy is set at 0.05 eV to allow comparison with the Fermi surface obtained by ARPES experiment. b, Orbital separated spectra, calculated with the p-orbital model, of the surface electronic structure around the \(\bar{\Gamma }\) point of the (100) surface (red arrow in a). Each subpanel shows the contribution of the px, py and pz orbitals for Bi, I and all elements. The directions of the px,y,z orbitals are defined relative to the (100) surface, as illustrated in a. c, The same results as b, but for the momentum cut across the \(\bar{{\rm{Z}}}\) point (orange arrow in a).

Extended Data Fig. 8 A slight modulation of 1D Fermi surface along kz in the side surface of β-Bi4I4.

a, Calculated constant energy contour of the band for the (100) surface of β-Bi4I4. The energy is set at 0.05 eV to allow comparison with the Fermi surface obtained in the ARPES experiment. be, ARPES band maps and their MDCs at EF around the \(\bar{\Gamma }\) and \(\bar{{\rm{Z}}}\) points of the (100) surface. Double Lorentzian curves (black dotted curves) are fit to the MDCs with two-peak structure. The distances between these two peaks are indicated by the thin red arrows in b and d.

Extended Data Fig. 9 Periodicity of band dispersions obtained by surface-selective nano-ARPES at hv  = 74 eV.

a, b, Schematics of surface preparation for nano-ARPES measurements of the side (a) and top (b) planes. c, Real-space mapping of photoemission intensity for the cleavage surface of a (left), along with a magnified image (right). The white circle indicates the position at which we performed surface-selective ARPES measurements. d, Fermi surface mapping for the (100) surface. The intensities are integrated within 100 meV. The dashed lines indicate the Brillouin zone for the (100) surface. e, f, Similar results to c, d, respectively, but for the (001) surface. g, h, ARPES band dispersion along the chain direction extracted at ky = −0.4 Å−1 (blue arrow in d, f). The dashed red curves trace the band dispersions, with periodicities consistent with the sizes of the Brillouin zones for the (100) and (001) surfaces (red and black arrows in g and h, respectively). A high-flux nanometre-scale beam obtained using a Schwarzschild objective enabled clear mapping of kz/x dispersions. i, j, ARPES band maps cut across the \(\bar{\Gamma }\) and \(\bar{{\rm{Z}}}\) points of the (100) surface. k, l, ARPES band maps cut across the \(\bar{\Gamma }\) and \(\bar{{\rm{M}}}\) points of the (001) surface.

Extended Data Fig. 10 Demonstration of the switchable topological state in Bi4I4, using the same piece of crystal.

a, Schematic showing the experimental sequence used to demonstrate the topological phase transition from the β- to the α-phase with the same piece of crystal. b, c, ARPES images of the same piece of crystal measured at θ = 0° and 20 K after quenching (b) and after mild cooling (c). d, Schematic showing the experimental sequence used to demonstrate the topological phase transition from the α- to the β-phase for the same piece of crystal. e, f, ARPES images of the same piece of crystal measured at θ = 0° and 20 K after mild cooling (e) and after quenching (f).

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Noguchi, R., Takahashi, T., Kuroda, K. et al. A weak topological insulator state in quasi-one-dimensional bismuth iodide. Nature 566, 518–522 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing