Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Chemical control of structure and guest uptake by a conformationally mobile porous material


Metal–organic frameworks (MOFs) are crystalline synthetic porous materials formed by binding organic linkers to metal nodes: they can be either rigid1,2 or flexible3. Zeolites and rigid MOFs have widespread applications in sorption, separation and catalysis that arise from their ability to control the arrangement and chemistry of guest molecules in their pores via the shape and functionality of their internal surface, defined by their chemistry and structure4,5. Their structures correspond to an energy landscape with a single, albeit highly functional, energy minimum. By contrast, proteins function by navigating between multiple metastable structures using bond rotations of the polypeptide6,7, where each structure lies in one of the minima of a conformational energy landscape and can be selected according to the chemistry of the molecules that interact with the protein. These structural changes are realized through the mechanisms of conformational selection (where a higher-energy minimum characteristic of the protein is stabilized by small-molecule binding) and induced fit (where a small molecule imposes a structure on the protein that is not a minimum in the absence of that molecule)8. Here we show that rotation about covalent bonds in a peptide linker can change a flexible MOF to afford nine distinct crystal structures, revealing a conformational energy landscape that is characterized by multiple structural minima. The uptake of small-molecule guests by the MOF can be chemically triggered by inducing peptide conformational change. This change transforms the material from a minimum on the landscape that is inactive for guest sorption to an active one. Chemical control of the conformation of a flexible organic linker offers a route to modifying the pore geometry and internal surface chemistry and thus the function of open-framework materials.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Rent or buy this article

Prices vary by article type



Prices may be subject to local taxes which are calculated during checkout

Fig. 1: The structural flexibility of ZnGGH in the context of a conformational energy landscape.
Fig. 2: Chemical triggering of guest adsorption.
Fig. 3: Linker conformation directs pore shape and internal surface chemistry.
Fig. 4: Conformational energy landscape and selection of an active minimum in ZnGGH.

Data availability

The datasets supporting the findings of this study are available from the University of Liverpool, and can be found at


  1. Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, 1230444 (2013).

    Article  Google Scholar 

  2. Howarth, A. J. et al. Chemical, thermal and mechanical stabilities of metal–organic frameworks. Nat. Rev. Mater. 1, 15018 (2016).

    Article  ADS  CAS  Google Scholar 

  3. Kitagawa, S., Kitaura, R. & Noro, S. Functional porous coordination polymers. Angew. Chem. Int. Ed. 43, 2334–2375 (2004).

    Article  CAS  Google Scholar 

  4. Moliner, M., Martínez, C. & Corma, A. Multipore zeolites: synthesis and catalytic applications. Angew. Chem. Int. Ed. 54, 3560–3579 (2015).

    Article  CAS  Google Scholar 

  5. Kaskel, S. in The Chemistry of Metal–Organic Frameworks 1–3 (Wiley-VCH, Weinheim, Germany, 2016).

  6. Beck, D. A. C., Alonso, D. O. V., Inoyama, D. & Daggett, V. The intrinsic conformational propensities of the 20 naturally occurring amino acids and reflection of these propensities in proteins. Proc. Natl Acad. Sci. USA 105, 12259–12264 (2008).

    Article  ADS  CAS  Google Scholar 

  7. Swain, J. F. & Gierasch, L. M. The changing landscape of protein allostery. Curr. Opin. Struct. Biol. 16, 102–108 (2006).

    Article  CAS  Google Scholar 

  8. Csermely, P., Palotai, R. & Nussinov, R. Induced fit, conformational selection and independent dynamic segments: an extended view of binding events. Trends Biochem. Sci. 35, 539–546 (2010).

    Article  CAS  Google Scholar 

  9. Schneemann, A. et al. Flexible metal-organic frameworks. Chem. Soc. Rev. 43, 6062–6096 (2014).

    Article  CAS  Google Scholar 

  10. Horike, S., Shimomura, S. & Kitagawa, S. Soft porous crystals. Nat. Chem. 1, 695–704 (2009).

    Article  CAS  Google Scholar 

  11. Loiseau, T. et al. A rationale for the large breathing of the porous aluminum terephthalate (MIL-53) upon hydration. Chem. Eur. J. 10, 1373–1382 (2004).

    Article  CAS  Google Scholar 

  12. Nouar, F. et al. Tuning the breathing behaviour of MIL-53 by cation mixing. Chem. Commun. 48, 10237–10239 (2012).

    Article  CAS  Google Scholar 

  13. Serre, C. et al. Role of solvent-host interactions that lead to very large swelling of hybrid frameworks. Science 315, 1828–1831 (2007).

    Article  ADS  CAS  Google Scholar 

  14. Maji, T. K., Matsuda, R. & Kitagawa, S. A flexible interpenetrating coordination framework with a bimodal porous functionality. Nat. Mater. 6, 142–148 (2007).

    Article  ADS  CAS  Google Scholar 

  15. Mason, J. A. et al. Methane storage in flexible metal-organic frameworks with intrinsic thermal management. Nature 527, 357–361 (2015).

    Article  ADS  CAS  Google Scholar 

  16. Freye, S. et al. Allosteric binding of halide anions by a new dimeric interpenetrated coordination cage. Angew. Chem. Int. Ed. 51, 2191–2194 (2012).

    Article  CAS  Google Scholar 

  17. Freye, S. et al. Template control over dimerization and guest selectivity of interpenetrated coordination cages. J. Am. Chem. Soc. 135, 8476–8479 (2013).

    Article  CAS  Google Scholar 

  18. Löffler, S. et al. Triggered exchange of anionic for neutral guests inside a cationic coordination cage. J. Am. Chem. Soc. 137, 1060–1063 (2015).

    Article  Google Scholar 

  19. Lin, Z.-J., Lü, J., Hong, M. & Cao, R. Metal-organic frameworks based on flexible ligands (FL-MOFs): structures and applications. Chem. Soc. Rev. 43, 5867–5895 (2014).

    Article  CAS  Google Scholar 

  20. Colodrero, R. M. P. et al. Multifunctional lanthanum tetraphosphonates: flexible, ultramicroporous and proton-conducting hybrid frameworks. Dalton Trans. 41, 4045–4051 (2012).

    Article  CAS  Google Scholar 

  21. Rouschmeyer, P. et al. A flexible fluorescent Zr carboxylate metal-organic framework for the detection of electron-rich molecules in solution. Inorg. Chem. 56, 8423–8429 (2017).

    Article  CAS  Google Scholar 

  22. Yeung, H.-M. H., Kosa, M., Parrinello, M. & Cheetham, A. K. Chiral, racemic, and meso-lithium tartrate framework polymorphs: a detailed structural analysis. Cryst. Growth Des. 13, 3705–3715 (2013).

    Article  CAS  Google Scholar 

  23. Motkuri, R. K. et al. Role of hydrocarbons in pore expansion and contraction of a flexible metal-organic framework. Chem. Commun. 47, 7077–7079 (2011).

    Article  CAS  Google Scholar 

  24. Murdock, C. R., Lu, Z. & Jenkins, D. M. Effects of solvation on the framework of a breathing copper MOF employing a semirigid linker. Inorg. Chem. 52, 2182–2187 (2013).

    Article  CAS  Google Scholar 

  25. Haddad, J., Whitehead, G. F. S., Katsoulidis, A. P. & Rosseinsky, M. J. In-MOFs based on amide functionalised flexible linkers. Faraday Discuss. 201, 327–335 (2017).

    Article  ADS  CAS  Google Scholar 

  26. Rabone, J. et al. An adaptable peptide-based porous material. Science 329, 1053–1057 (2010).

    Article  ADS  CAS  Google Scholar 

  27. Martí-Gastaldo, C. et al. Side-chain control of porosity closure in single- and multiple-peptide-based porous materials by cooperative folding. Nat. Chem. 6, 343–351 (2014).

    Article  Google Scholar 

  28. Katsoulidis, A. P. et al. Guest-adaptable and water-stable peptide-based porous materials by imidazolate side chain control. Angew. Chem. Int. Ed. 53, 193–198 (2014).

    Article  CAS  Google Scholar 

  29. Mu, Y., Nguyen, P. H. & Stock, G. Energy landscape of a small peptide revealed by dihedral angle principal component analysis. Proteins 58, 45–52 (2005).

    Article  CAS  Google Scholar 

  30. Naganathan, A. N., Sanchez-Ruiz, J. M. & Muñoz, V. Direct measurement of barrier heights in protein folding. J. Am. Chem. Soc. 127, 17970–17971 (2005).

    Article  CAS  Google Scholar 

  31. Sheppard, D., Terrell, R. & Henkelman, G. Optimization methods for finding minimum energy paths. J. Chem. Phys. 128, 134106 (2008).

    Article  ADS  Google Scholar 

  32. Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).

    Article  ADS  Google Scholar 

  33. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    Article  ADS  CAS  Google Scholar 

  34. Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).

    Article  ADS  CAS  Google Scholar 

  35. Dion, M., Rydberg, H., Schröder, E., Langreth, D. C. & Lundqvist, B. I. van der Waals density functional for general geometries. Phys. Rev. Lett. 92, 246401 (2004).

    Article  ADS  CAS  Google Scholar 

Download references


This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation programme (grant agreement number 692685) and from the Engineering and Physical Sciences Research Council (EPSRC; grant EP/J008834). We acknowledge the High Performance Computing (HPC) Materials Chemistry Consortium for providing access to UK’s national supercomputer ARCHER under EPSRC grant EP/L000202. We thank the Diamond Light Source for provision of beamtime on the I11 and I19 beamlines, and the X-ray crystallography facility of the School of Chemistry at the University of Manchester for the use of their Rigaku Oxford diffraction FR-X instrument to collect two of the single-crystal diffraction datasets.

Author information

Authors and Affiliations



A.P.K., D.A. and M.J.R. conceived the research and wrote the first draft of the paper. A.P.K. and M.J.R. designed the experimental approach. A.P.K. synthesized the materials and carried out the adsorption experiments. D.J.A. provided input on materials synthesis and characterization. D.A., M.S.D., G.R.D. and N.G.B. designed the computational approach. D.A. performed the theoretical simulations. G.F.S.W. and E.J.C. performed the structural analyses. All the authors discussed the results and contributed to writing the manuscript. M.J.R. directed the research.

Corresponding author

Correspondence to Matthew J. Rosseinsky.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Synthesis and crystal structure of ZnGGH-1(DMF-H2O).

a, Schematic representation of ZnGGH-1(DMF-H2O) synthesis from glycine–glycine–l-histidine and Zn(OAc)2. The tripeptide is deprotonated at the C-terminal acid and the imidazole side chain. The resulting anion acts as a tetratopic linker and coordinates to four Zn2+ cations, thus forming a three-dimensional (4,4)-connected net. b, Top, structural representation of ZnGGH-1(DMF-H2O) viewed along the b axis reveals the parallelogram-shaped one-dimensional pores. Centre, the rigid layers of the framework are composed of the histidine residue. Each histidine links three Zn2+ cations; two of them are bridged by the imidazolate side chain, and the third is bound to the carboxylate group. Bottom, ZnGGH-1(DMF-H2O) viewed along the a axis shows the undulating shape of the rigid layers, which are interconnected by the flexible glycine–glycine chains.

Extended Data Fig. 2 The structural transformations of ZnGGH and the experimental workflow for triggered guest adsorption.

a, Eight distinct crystal structures are produced by exchanging the molecules that occupy the pores of as-made ZnGGH-1(DMF-H2O). b, Experimental procedure for the adsorption of dioxane by ZnGGH-2 with (left) and without (right) triggering by DMF. Adding DMF during the dioxane-adsorption experiment produces a structural transformation and allows dioxane to access the ZnGGH framework. In the absence of DMF, dioxane does not access the pores of ZnGGH-2. PXRD and 1H-NMR data are shown in Fig. 2. The small amount of dioxane measured in the non-triggered adsorption is assigned to surface species that are not removed during the required work-up procedure.

Extended Data Fig. 3 Structure and linker conformation of ZnGGH-2(DMSO).

ZnGGH-2(DMSO) is produced by treating ZnGGH-1(DMF-H2O) with pure DMSO. This reaction is reversible: ZnGGH-2(DMSO) is transformed to ZnGGH-1(DMF-H2O) after treatment with a DMF/H2O 3/1 (v/v) mixture. The linker in ZnGGH-2 adopts a twisted conformation, distinct from the straight conformation adopted in ZnGGH-1, which causes the pore window to shrink from 4.9 Å to 4.5 Å. The twisted conformation directs the glycine–glycine amide group inside the pore, where it forms a hydrogen bond with DMSO via the NH group of the central glycine. By contrast, the glycine–glycine amide group in ZnGGH-1(DMF-H2O) is directed along the pore direction and does not form a hydrogen bond with the DMF molecule. From top to bottom are shown parts of the structures at increasing magnification.

Extended Data Fig. 4 Structure, linker conformation and DMF orientation in ZnGGH-3(DMF) and ZnGGH-1(DMF-H2O).

ZnGGH-3(DMF) is produced by treating ZnGGH-1(DMF-H2O) with pure DMF. This reaction is reversible: ZnGGH-3(DMF) is transformed back to ZnGGH-1(DMF-H2O) after treatment with a DMF/H2O 3/1 (v/v) mixture. In both structures, the DMF molecule is hydrogen-bonded to the same proton of the terminal NH2, but its orientation changes by about 90° between structures 1 and 3. This change in DMF orientation is associated with repositioning of the terminal glycine between the two structures through conformational change of the tripeptide.

Extended Data Fig. 5 Structure and linker conformation of collapsed ZnGGH-9.

The collapsed structure ZnGGH-9 is produced by removing the solvents from ZnGGH-1(DMF-H2O). In ZnGGH-9, the linker adopts two very similar folded conformations. These conformational changes are realized by the torsions φ2 of histidine and ψ of the central glycine.

Extended Data Fig. 6 Three clusters of conformations—straight, twisted and folded—are observed in ZnGGH structures, with the ‘straight’ cluster divided into four subgroups.

a, We applied dPCA to the linker conformations of the nine experimentally observed ZnGGH structures, grouping them into three clusters: straight, twisted and folded (Fig. 4a). As identified by dPCA, the main variance in linker conformation comes from the torsions φ2 of histidine and ω of Gly–His (contributing to the first principal component, PC1) as well as torsions φ1 and ψ of the central glycine (contributing to the second principal component, PC2). b, The straight cluster is the most populated, containing six different conformations. dPCA applied to these six conformations shows that they further separate into four subgroups (Fig. 4b). The main contribution to the principal components is from the torsions φ1 and ψ of the central glycine.

Extended Data Fig. 7 Comparison of the structures of ZnGGH-5(H2O-DMF), ZnGGH-1(DMF-H2O) and ZnGGH-3(DMF).

ZnGGH-5(H2O-DMF) (centre) is produced by treating ZnGGH-1(DMF-H2O) with H2O/DMF = 5/3 (v/v). This structure combines the hydrogen bonding seen in ZnGGH-3(DMF) (left) and ZnGGH-1(DMF-H2O) (right). Although the linker conformations in these three structures belong to the same cluster (straight), the diversity between them (Extended Data Fig. 7b) is enough to produce different sets of hydrogen bonds, demonstrating the variety of structural subgroups shown by the second dPCA in Fig. 4b. ZnGGH-5(H2O-DMF) has the maximum number of three possible intraframework hydrogen bonds (see Supplementary Table 4). There are two hydrogen bonds between the flexible glycine–glycine chain of the linker: one between glycine–glycine amide groups (green shading) is characteristic of ZnGGH-3, and another between the terminal NH2 and the glycine–histidine amide group (yellow shading) is characteristic of ZnGGH-1. The hydrogen bond between the histidine carboxylate and glycine–histidine amide (pink shading), in the rigid part of the framework, is present in every ZnGGH structure.

Extended Data Fig. 8 Comparison of hydrogen-bond patterns between ZnGGH-6(F) and ZnGGH-7(FA).

The furfural (F) and furfuryl alcohol (FA) guests produce two distinct structures, ZnGGH-6(F) and ZnGGH-7(FA) respectively. Although these structures feature peptide conformations that place them in the ‘straight linker’ cluster (Fig. 4a), they present different hydrogen-bond patterns, placing them in distinct subgroups in Fig. 4b. ZnGGH-6(F) exhibits the same three intraframework hydrogen bonds as ZnGGH-5(H2O-DMF), and the carbonyl group of furfural forms a hydrogen bond with the terminal NH2. By contrast, in ZnGGH-7(FA), the hydroxyl of furfuryl alcohol is hydrogen-bonded to the glycine–glycine amide group and to the terminal NH2, while the flexible Gly–Gly chain of the linker has been rotated towards the guest to form these interactions, thereby disrupting two of the three intraframework hydrogen bonds observed in ZnGGH-6(F): one between the Gly–Gly amide groups (green circle) and one between the terminal NH2 and the Gly–His amide group (purple circle). The only intraframework hydrogen bond that is present in ZnGGH-7(FA) is between the histidine carboxylate and the Gly–His amide (black circle).

Extended Data Fig. 9 Structure and linker conformations of ZnGGH-4(H2O).

ZnGGH-4(H2O) is produced by treating ZnGGH-1(DMF-H2O) with H2O. In ZnGGH-4(H2O), the linker adopts two conformations. Conformation I (pink) is a straight conformation similar to that found in ZnGGH-1(DMF-H2O), and conformation II (green) is a twisted conformation similar to that found in ZnGGH-2(DMSO).

Extended Data Table 1 Characteristic dimensions of ZnGGH structures

Supplementary information

Supplementary information

This file contains Supplementary Notes 1-7, Supplementary Figures S1-S60 and Supplementary Tables S1-S20.

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Katsoulidis, A.P., Antypov, D., Whitehead, G.F.S. et al. Chemical control of structure and guest uptake by a conformationally mobile porous material. Nature 565, 213–217 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing