Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Efficient radical-based light-emitting diodes with doublet emission


Organic light-emitting diodes (OLEDs)1,2,3,4,5, quantum-dot-based LEDs6,7,8,9,10, perovskite-based LEDs11,12,13 and micro-LEDs14,15 have been championed to fabricate lightweight and flexible units for next-generation displays and active lighting. Although there are already some high-end commercial products based on OLEDs, costs must decrease whilst maintaining high operational efficiencies for the technology to realise wider impact.  Here we demonstrate efficient action of radical-based OLEDs16, whose emission originates from a spin doublet, rather than a singlet or triplet exciton. While the emission process is still spin-allowed in these OLEDs, the efficiency limitations imposed by triplet excitons are circumvented for doublets. Using a luminescent radical emitter, we demonstrate an OLED with maximum external quantum efficiency of 27 per cent at a wavelength of 710 nanometres—the highest reported value for deep-red and infrared LEDs. For a standard closed-shell organic semiconductor, holes and electrons occupy the highest occupied and lowest unoccupied molecular orbitals (HOMOs and LUMOs), respectively, and recombine to form singlet or triplet excitons. Radical emitters have a singly occupied molecular orbital (SOMO) in the ground state, giving an overall spin-1/2 doublet. If—as expected on energetic grounds—both electrons and holes occupy this SOMO level, recombination returns the system to the ground state, giving no light emission. However, in our very efficient OLEDs, we achieve selective hole injection into the HOMO and electron injection to the SOMO to form the fluorescent doublet excited state with near-unity internal quantum efficiency.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: LEDs with doublet emission.
Fig. 2: Doublet photophysics.
Fig. 3: Electronic structure of doublets: from HOMO to SOMO.
Fig. 4: Doublet electroluminescence mechanism.

Similar content being viewed by others

Data availability

The datasets collected and analysed in this work are available at


  1. Tang, C. W. & VanSlyke, S. A. Organic electroluminescent diodes. Appl. Phys. Lett. 51, 913–915 (1987).

    Article  CAS  ADS  Google Scholar 

  2. Burroughes, J. H. et al. Light-emitting diodes based on conjugated polymers. Nature 347, 539–541 (1990); correction 348, 352 (1990).

    Article  CAS  ADS  Google Scholar 

  3. Baldo, M. A. et al. Highly efficient phosphorescent emission from organic electroluminescent devices. Nature 395, 151–154 (1998).

    Article  CAS  ADS  Google Scholar 

  4. Ma, Y., Zhang, H., Shen, J. & Che, C. Electroluminescence from triplet metal-ligand charge-transfer excited state of transition metal complexes. Synth. Met. 94, 245–248 (1998).

    Article  CAS  Google Scholar 

  5. Uoyama, H., Goushi, K., Shizu, K., Nomura, H. & Adachi, C. Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492, 234–238 (2012).

    Article  CAS  ADS  Google Scholar 

  6. Tessler, N., Medvedev, V., Kazes, M., Kan, S. & Banin, U. Efficient near-infrared polymer nanocrystal light-emitting diodes. Science 295, 1506–1508 (2002).

    Article  ADS  Google Scholar 

  7. Sun, Q. et al. Bright, multicoloured light-emitting diodes based on quantum dots. Nat. Photon. 1, 717–722 (2007).

    Article  CAS  ADS  Google Scholar 

  8. Dai, X. et al. Solution-processed, high-performance light-emitting diodes based on quantum dots. Nature 515, 96–99 (2014).

    Article  CAS  ADS  Google Scholar 

  9. Yang, Y. et al. High-efficiency light-emitting devices based on quantum dots with tailored nanostructures. Nat. Photon. 9, 259–266 (2015).

    Article  CAS  ADS  Google Scholar 

  10. Dai, X., Deng, Y., Peng, X. & Jin, Y. Quantum-dot light-emitting diodes for large-area displays: towards the dawn of commercialization. Adv. Mater. 29, 1607022 (2017).

    Article  Google Scholar 

  11. Tan, Z.-K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).

    Article  CAS  ADS  Google Scholar 

  12. Cho, H. et al. Overcoming the electroluminescence efficiency limitations of perovskite light-emitting diodes. Science 350, 1222–1225 (2015).

    Article  CAS  ADS  Google Scholar 

  13. Wang, N. et al. Perovskite light-emitting diodes based on solution-processed self-organized multiple quantum wells. Nat. Photon. 10, 699–704 (2016).

    Article  CAS  ADS  Google Scholar 

  14. Jin, S. X., Li, J., Li, J. Z., Lin, J. Y. & Jiang, H. X. GaN microdisk light emitting diodes. Appl. Phys. Lett. 76, 631–633 (2000).

    Article  CAS  ADS  Google Scholar 

  15. Zhang, K., Peng, D., Lau, K. M. & Liu, Z. Fully-integrated active matrix programmable UV and blue micro-LED display system-on-panel (SoP). J. Soc. Inf. Disp. 25, 240–248 (2017).

    Article  CAS  Google Scholar 

  16. Peng, Q., Obolda, A., Zhang, M. & Li, F. Organic light-emitting diodes using a neutral π radical as emitter: the emission from a doublet. Angew. Chem. Int. Ed. 54, 7091–7095 (2015).

    Article  CAS  Google Scholar 

  17. Ballester, M., Molinet, C. & Castañer, J. Preparation of highly strained aromatic chlorocarbons. I. A powerful nuclear chlorinating agent. Relevant reactivity phenomena traceable to molecular strain. J. Am. Chem. Soc. 82, 4254–4258 (1960).

    Article  CAS  Google Scholar 

  18. Armet, O. et al. Inert carbon free radicals. 8. Polychlorotriphenylmethyl radicals: synthesis, structure, and spin-density distribution. J. Phys. Chem. 91, 5608–5616 (1987).

    Article  CAS  Google Scholar 

  19. Heckmann, A., Lambert, C., Goebel, M. & Wortmann, R. Synthesis and photophysics of a neutral organic mixed-valence compound. Angew. Chem. Int. Ed. 43, 5851–5856 (2004).

    Article  CAS  Google Scholar 

  20. Velasco, D. et al. Red organic light-emitting radical adducts of carbazole and tris(2,4,6-trichlorotriphenyl)methyl radical that exhibit high thermal stability and electrochemical amphotericity. J. Org. Chem. 72, 7523–7532 (2007).

    Article  CAS  Google Scholar 

  21. Castellanos, S., Velasco, D., López-Calahorra, F., Brillas, E. & Julia, L. Taking advantage of the radical character of tris(2,4,6-trichlorophenyl)methyl to synthesize new paramagnetic glassy molecular materials. J. Org. Chem. 73, 3759–3767 (2008).

    Article  CAS  Google Scholar 

  22. Hattori, Y., Kusamoto, T. & Nishihara, H. Luminescence, stability, and proton response of an open-shell (3,5-dichloro-4-pyridyl)bis(2,4,6-trichlorophenyl)methyl radical. Angew. Chem. Int. Ed. 53, 11845–11848 (2014).

    Article  CAS  Google Scholar 

  23. Ai, X., Chen, Y., Feng, Y. & Li, F. A stable room-temperature luminescent biphenylmethyl radical. Angew. Chem. Int. Ed. 57, 2869–2873 (2018).

    Article  CAS  Google Scholar 

  24. Hung, W. Y. et al. The first tandem, all-exciplex-based WOLED. Sci. Rep. 4, 5161 (2014).

    Article  CAS  Google Scholar 

  25. Sasabe, H. et al. 2-Phenylpyrimidine skeleton-based electron-transport materials for extremely efficient green organic light-emitting devices. Chem. Commun. 5821–5823 (2008).

  26. Li, C. et al. Deep-red to near-infrared thermally activated delayed fluorescence in organic solid films and electroluminescent devices. Angew. Chem. Int. Ed. 56, 11525–11529 (2017).

    Article  CAS  Google Scholar 

  27. Kim, D.-H. et al. High-efficiency electroluminescence and amplified spontaneous emission from a thermally activated delayed fluorescent near-infrared emitter. Nat. Photon. 12, 98–104 (2018).

    Article  CAS  ADS  Google Scholar 

  28. Xue, J. et al. High-efficiency near-infrared fluorescent organic light-emitting diodes with small efficiency roll-off: a combined design from emitters to devices. Adv. Funct. Mater. 27, 1703283 (2017).

    Article  Google Scholar 

  29. Ipatov, A. et al. Excited-state spin-contamination in time-dependent density-functional theory for molecules with open-shell ground states. J. Mol. Struct. Theochem 914, 60–73 (2009).

    Article  CAS  Google Scholar 

  30. Neier, E. et al. Solution-processed organic light-emitting diodes with emission from a doublet exciton; using (2,4,6-trichlorophenyl)methyl as emitter. Org. Electron. 44, 126–131 (2017).

    Article  CAS  Google Scholar 

Download references


X.A., S.D., H.G., Y.C. and F.L. are grateful for the financial support received from the National Key R&D Program of China (grant number 2016YFB0401001), the National Natural Science Foundation of China (grant numbers 51673080 and 91233113) and the National Key Basic Research and Development Program of China (973 programme, grant number 2015CB655003). E.W.E., A.J.G. and R.H.F. thank the EPSRC for funding (EP/M01083X/1, EP/M005143/1). T.J.H.H. thanks Jesus College, Cambridge for a Research Fellowship. F.L. is an academic visitor at the Cavendish Laboratory, Cambridge and is supported by the China Scholarship Council (CSC) and the Talents Cultivation Program (Jilin University, China).

Reviewer information

Nature thanks T. Kusamoto and the other anonymous reviewer(s) for their contribution to the peer review of this work.

Author information

Authors and Affiliations



X.A., S.D. and H.G. designed and synthesized the luminescent radicals and performed the steady-state spectroscopy. E.W.E. performed the transient-photoluminescence measurements and the quantum chemical calculations. T.J.H.H devised the group theory treatment. A.J.G. conducted the transient-absorption spectroscopy measurements. X.A., Y.C. and F.L. optimized the devices. E.W.E., R.H.F. and F.L. initiated, designed and supervised the work. E.W.E., R.H.F. and F.L. wrote the manuscript, with input from all authors.

Corresponding authors

Correspondence to Richard H. Friend or Feng Li.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Thermal stability and electron paramagnetic resonance measurements of TTM-3NCz and TTM-3PCz.

a, Thermogravimetric analysis measurements show thermal decomposition temperatures of 362 °C (TTM-3NCz) and 367 °C (TTM-3PCz). b, EPR spectra for solid samples at room temperature. ESR, electron spin resonance; B, magnetic field.

Extended Data Fig. 2 Electrochemical properties and stability of TTM-3NCz and TTM-3PCz.

a, c, Cyclic voltammograms of TTM-3NCz (a) and TTM-3PCz (c) in CH2Cl2. For both TTM-3NCz and TTM-3PCz, the average of the cathodic and anodic potentials gives a reduction potential of −1.1 V, first oxidation potential of +0.4 V and second oxidation potential of +0.9 V. b, d, Multi-cycle (20 cycles) cyclic voltammetry measurements of TTM-3NCz (b) and TTM-3PCz in CH2Cl2 (d). A ferrocence cation/ferrocence (Fc+/Fc) reference redox couple was used for the measurements.

Extended Data Fig. 3 Photostability of TTM and TTM-3NCz.

Luminescence intensity (l) of TTM-3NCz and TTM solutions (10 µM, cyclohexane) as a function of time. A pulsed laser of 355 nm with an energy density of 315 kW cm−2 (pulse width, 8 ns; frequency, 10 Hz) was used under ambient conditions.

Extended Data Fig. 4 Device reproducibility for TTM-3NCz.

a, EQE–current density plots for five TTM-3NCz devices. The peak EQEmax values are: 25% (device 1), 27% (device 2), 20% (device 3), 24% (device 4) and 16% (device 5). The EQE at 1 mA cm−2 is: 8% (device 1), 10% (device 2), 7% (device 3), 9% (device 4) and 7% (device 5). b, Radiance–voltage plots for the same five TTM-3NCz devices. The radiance levels for EQEmax are indicated, which can be distinguished from the noise. c, Current density–voltage plots for the same five TTM-3NCz devices.

Extended Data Fig. 5 Device stability for TTM-3NCz.

Electroluminescence spectra for TTM-3NCz devices operated at current densities of 0.006–1.6 mA cm−2. There is no current dependence.

Supplementary information

Supplementary Information

This file contains further experimental details; Supplementary Text: including synthesis and MO diagram derivation; Supplementary Figures: 1–2) TA data, 3–4) MO diagrams and basis set, 5–6) DFT orbitals and difference density plots; and Supplementary Tables: 1) TDDFT orbital contributions, 2) red LED literature.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Ai, X., Evans, E.W., Dong, S. et al. Efficient radical-based light-emitting diodes with doublet emission. Nature 563, 536–540 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:


This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing