Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Ballistic molecular transport through two-dimensional channels


Gas permeation through nanoscale pores is ubiquitous in nature and has an important role in many technologies1,2. Because the pore size is typically smaller than the mean free path of gas molecules, the flow of the gas molecules is conventionally described by Knudsen theory, which assumes diffuse reflection (random-angle scattering) at confining walls3,4,5,6,7. This assumption holds surprisingly well in experiments, with only a few cases of partially specular (mirror-like) reflection known5,8,9,10,11. Here we report gas transport through ångström-scale channels with atomically flat walls12,13 and show that surface scattering can be either diffuse or specular, depending on the fine details of the atomic landscape of the surface, and that quantum effects contribute to the specularity at room temperature. The channels, made from graphene or boron nitride, allow helium gas flow that is orders of magnitude faster than expected from theory. This is explained by specular surface scattering, which leads to ballistic transport and frictionless gas flow. Similar channels, but with molybdenum disulfide walls, exhibit much slower permeation that remains well described by Knudsen diffusion. We attribute the difference to the larger atomic corrugations at molybdenum disulfide surfaces, which are similar in height to the size of the atoms being transported and their de Broglie wavelength. The importance of this matter-wave contribution is corroborated by the observation of a reversed isotope effect, whereby the mass flow of hydrogen is notably higher than that of deuterium, in contrast to the relation expected for classical flows. Our results provide insights into the atomistic details of molecular permeation, which previously could be accessed only in simulations10,14, and demonstrate the possibility of studying gas transport under controlled confinement comparable in size to the quantum-mechanical size of atoms.

Your institute does not have access to this article

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Helium gas transport through ångström-scale slits.
Fig. 2: Enhanced gas flow through 2D channels.


  1. Baker, R. W. Membrane Technology and Applications 2nd edn (John Wiley & Sons, Chichester, 2004).

    Book  Google Scholar 

  2. Lu, G. Q. & Zhao, X. S. Nanoporous Materials: Science and Engineering (Imperial College Press, London, 2004).

    Book  Google Scholar 

  3. Knudsen, M. Die Gesetze der Molekularströmung und der inneren Reibungsströmung der Gase durch Röhren. Ann. Phys. 333, 75–130 (1909).

    Article  MATH  Google Scholar 

  4. v. Smoluchowski, M. Zur kinetischen Theorie der Transpiration und Diffusion verdünnter Gase. Ann. Phys. 338, 1559–1570 (1910).

    Article  MATH  Google Scholar 

  5. Steckelmacher, W. A review of the molecular flow conductance for systems of tubes and components and the measurement of pumping speed. Vacuum 16, 561–584 (1966).

    ADS  Article  CAS  Google Scholar 

  6. Livesey, R. G. in Foundations of Vacuum Science and Technology (ed. Lafferty, J. M.) Ch. 2 (John Wiley & Sons, New York, 1998).

  7. Lei, W., Rigozzi, M. K. & McKenzie, D. R. The physics of confined flow and its application to water leaks, water permeation and water nanoflows: a review. Rep. Prog. Phys. 79, 025901 (2016).

    ADS  Article  PubMed  CAS  Google Scholar 

  8. Holt, J. K. et al. Fast mass transport through sub-2-nanometer carbon nanotubes. Science 312, 1034–1037 (2006).

    ADS  Article  PubMed  CAS  Google Scholar 

  9. Agrawal, A. & Prabhu, S. V. Survey on measurement of tangential momentum accommodation coefficient. J. Vac. Sci. Technol. A 26, 634–645 (2008).

    Article  CAS  Google Scholar 

  10. Bhatia, S. K., Bonilla, M. R. & Nicholson, D. Molecular transport in nanopores: a theoretical perspective. Phys. Chem. Chem. Phys. 13, 15350–15383 (2011).

    Article  PubMed  CAS  Google Scholar 

  11. Majumder, M., Chopra, N. & Hinds, B. J. Mass transport through carbon nanotube membranes in three different regimes: ionic diffusion and gas and liquid flow. ACS Nano 5, 3867–3877 (2011).

    Article  PubMed  CAS  Google Scholar 

  12. Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).

    Article  PubMed  CAS  Google Scholar 

  13. Radha, B. et al. Molecular transport through capillaries made with atomic-scale precision. Nature 538, 222–225 (2016).

    ADS  Article  PubMed  CAS  Google Scholar 

  14. Zhang, W.-M., Meng, G. & Wei, X. A review on slip models for gas microflows. Microfluid. Nanofluidics 13, 845–882 (2012).

    Article  CAS  Google Scholar 

  15. Koenig, S. P., Wang, L., Pellegrino, J. & Bunch, J. S. Selective molecular sieving through porous graphene. Nat. Nanotechnol. 7, 728–732 (2012).

    ADS  Article  PubMed  CAS  Google Scholar 

  16. Berry, V. Impermeability of graphene and its applications. Carbon 62, 1–10 (2013).

    Article  CAS  Google Scholar 

  17. Celebi, K. et al. Ultimate permeation across atomically thin porous graphene. Science 344, 289–292 (2014).

    ADS  Article  PubMed  CAS  Google Scholar 

  18. Wang, L. et al. Molecular valves for controlling gas phase transport made from discrete ångström-sized pores in graphene. Nat. Nanotechnol. 10, 785–790 (2015).

    ADS  Article  PubMed  CAS  Google Scholar 

  19. Kim, H. W. et al. Selective gas transport through few-layered graphene and graphene oxide membranes. Science 342, 91–95 (2013).

    ADS  Article  PubMed  CAS  Google Scholar 

  20. Li, H. et al. Ultrathin, molecular-sieving graphene oxide membranes for selective hydrogen separation. Science 342, 95–98 (2013).

    ADS  Article  PubMed  CAS  Google Scholar 

  21. Liu, G., Jin, W. & Xu, N. Two-dimensional-material membranes: a new family of high-performance separation membranes. Angew. Chem. Int. Ed. 55, 13384–13397 (2016).

    Article  CAS  Google Scholar 

  22. Wang, L. et al. Fundamental transport mechanisms, fabrication and potential applications of nanoporous atomically thin membranes. Nat. Nanotechnol. 12, 509–522 (2017).

    ADS  Article  PubMed  CAS  Google Scholar 

  23. Falk, K. et al. Molecular origin of fast water transport in carbon nanotube membranes: superlubricity versus curvature dependent friction. Nano Lett. 10, 4067–4073 (2010).

    ADS  Article  PubMed  CAS  Google Scholar 

  24. Gass, M. H. et al. Free-standing graphene at atomic resolution. Nat. Nanotechnol. 3, 676–681 (2008).

    ADS  Article  PubMed  CAS  Google Scholar 

  25. Haigh, S. J. et al. Cross-sectional imaging of individual layers and buried interfaces of graphene-based heterostructures and superlattices. Nat. Mater. 11, 764–767 (2012).

    ADS  Article  PubMed  CAS  Google Scholar 

  26. Li, Z. et al. Effect of airborne contaminants on the wettability of supported graphene and graphite. Nat. Mater. 12, 925–931 (2013).

    ADS  Article  PubMed  CAS  Google Scholar 

  27. Arya, G., Chang, H.-C. & Maginn, E. J. Knudsen diffusivity of a hard sphere in a rough slit pore. Phys. Rev. Lett. 91, 026102 (2003).

    ADS  Article  PubMed  CAS  Google Scholar 

  28. You, H. X., Brown, N. M. D. & Al-Assadi, K. F. Radio-frequency plasma etching of graphite with oxygen: a scanning tunnelling microscope study. Surf. Sci. 284, 263–272 (1993).

    ADS  Article  CAS  Google Scholar 

  29. Addou, R., Colombo, L. & Wallace, R. M. Surface defects on natural MoS2. ACS Appl. Mater. Interfaces 7, 11921–11929 (2015).

    Article  PubMed  CAS  Google Scholar 

  30. Mehio, N., Dai, S. & Jiang, D. Quantum mechanical basis for kinetic diameters of small gaseous molecules. J. Phys. Chem. A 118, 1150–1154 (2014).

    Article  PubMed  CAS  Google Scholar 

  31. Sharvin, Y. V. A possible method for studying Fermi surfaces. Sov. Phys. JETP 21, 655–656 (1965).

    ADS  Google Scholar 

  32. Giannuzzi, L. A. & Stevie, F. A. (eds) Introduction to Focused Ion Beams: Instrumentation, Theory, Techniques and Practice (Springer, New York, 2005).

    Google Scholar 

  33. Esfandiar, A. et al. Size effect in ion transport through angstrom-scale slits. Science 358, 511–513 (2017).

    ADS  Article  PubMed  CAS  Google Scholar 

  34. Schaffer, M., Schaffer, B. & Ramasse, Q. Sample preparation for atomic-resolution STEM at low voltages by FIB. Ultramicroscopy 114, 62–71 (2012).

    Article  PubMed  CAS  Google Scholar 

  35. Bentley, J. Electron density as a descriptor of thermal molecular size. J. Phys. Chem. A 104, 9630–9635 (2000).

    Article  CAS  Google Scholar 

  36. VandeVondele, J. et al. Quickstep: fast and accurate density functional calculations using a mixed Gaussian and plane waves approach. Comput. Phys. Commun. 167, 103–128 (2005).

    ADS  Article  CAS  Google Scholar 

  37. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  Article  PubMed  CAS  Google Scholar 

  38. VandeVondele, J. & Hutter, J. Gaussian basis sets for accurate calculations on mole-cular systems in gas and condensed phases. J. Chem. Phys. 127, 114105 (2007).

    ADS  Article  PubMed  CAS  Google Scholar 

  39. Goedecker, S., Teter, M. & Hutter, J. Separable dual-space Gaussian pseudopotentials. Phys. Rev. B 54, 1703–1710 (1996).

    ADS  Article  CAS  Google Scholar 

  40. Lu, T. & Chen, F. Multiwfn: a multifunctional wavefunction analyzer. J. Comput. Chem. 33, 580–592 (2012).

    Article  PubMed  CAS  Google Scholar 

  41. Jorgensen, W. L., Maxwell, D. S. & Tirado-Rives, J. Development and testing of the OPLS all-atom force field on conformational energetics and properties of organic liquids. J. Am. Chem. Soc. 118, 11225–11236 (1996).

    Article  CAS  Google Scholar 

  42. Laio, A. & Parrinello, M. Escaping free-energy minima. Proc. Natl Acad. Sci. USA 99, 12562–12566 (2002).

    ADS  Article  PubMed  PubMed Central  CAS  Google Scholar 

  43. Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 117, 1–19 (1995).

    ADS  Article  MATH  CAS  Google Scholar 

  44. Rubinstein, M. & Colby, R. H. Polymer Physics Ch. 2, 3 (Oxford Univ. Press, Oxford, 2003).

    Google Scholar 

Download references


This work was supported by the European Research Council, Lloyd’s Register Foundation, the EU Graphene Flagship and the Royal Society. B.R. acknowledges a Leverhulme Early Career Fellowship, a L’Oréal Fellowship for Women in Science and EPSRC grant EP/R013063/1. F.C.W. acknowledges support from the National Natural Science Foundation of China (11772319 and 11572307) and the Shanghai Supercomputer Center. S.J.H. and A.P.R. were funded by the European Research Council under the European Union’s Horizon 2020 research and innovation programme (grant agreements ERC-2016-STG-EvoluTEM-715502 and DISCOVERER-2017 737183), the US Defence Threat Reduction Agency (HDTRA1-12-1-0013) and the EPSRC (EP/P009050/1 and EP/K016946/1).

Reviewer information

Nature thanks L. Bocquet and the other anonymous reviewer(s) for their contribution to the peer review of this work.

Author information

Authors and Affiliations



A.K.G. and B.R. designed and directed the project. A.K., B.R., A.J., S.H., A.E and S.A.D. fabricated the devices. A.K., B.R. and A.J. performed the measurements and their analysis. F.C.W. provided theoretical support. A.P.R. and S.J.H. carried out TEM imaging. A.K.G., B.R., F.C.W., A.K. and I.V.G. wrote the manuscript. All authors contributed to discussions.

Corresponding authors

Correspondence to A. K. Geim or B. Radha.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Fabrication procedures.

a, Thin crystal was transferred to cover an opening in a SiN x membrane. b, The opening is extended through the bottom crystal. c, Spacer stripes were deposited on top of the bottom layer and etched from the back side. The top crystal is then transferred on top to fully cover the rectangular opening. d, Left, optical image of a single-channel capillary device made entirely from graphite; N = 5. The SiN x /Si wafer is seen in dark green; the SiN x membrane appears as a light-green square; the top graphite layer shows up in bright yellow; and the rectangular opening (lighter green) is indicated by the black arrow. Centre, atomic force micrograph near the channel entry, where the top graphite does not cover the spacer layer (the scan area is shown by the red contour). The height profile taken along the dotted white line is shown on the right, indicating h ≈ 1.7 ± 0.1 nm. The side cavities perpendicular to the 2D channel were made to prevent contamination bubbles25 across the main channel. e, A gold mask is placed on top of the trilayer assembly for final etching, to define L and to unblock the channel entry. f, Optical image of the final capillary device in the transmission mode. The SiN x membrane is fully transparent (bright). The Au mask is partially transparent, and both the top graphite and the rectangular hole in SiN x can be seen underneath the Au, as indicated by the arrows.

Extended Data Fig. 2 Visualization of 2D channels.

a, Array of 2D slits made entirely from MoS2, as imaged in bright-field STEM. For guidance, the edges of one of the channels are indicated by red marks. The vertical stripes are from the curtaining effect caused by ion milling32. b, High-magnification STEM image of a 2D channel with the top and bottom walls made from MoS2 and bilayer graphene as the spacer (right panel). The channel is white in the bright-field image, and atomic layers of MoS2 can be seen as dark lines running parallel to the channel. The left panel shows a contrast profile across the region indicated by the red rectangle. Cross-sectional images of 2D slits made entirely from graphite crystals can be found in ref. 13.

Extended Data Fig. 3 Helium permeation measurements.

a, Schematic of our experimental set-up. b, Helium flow through round apertures of various diameters as measured by our He-leak detector (symbols). Red line, expected Knudsen flow through these apertures (no fitting parameters). Inset, optical image of one of the apertures. The error bars are from measurements using different devices.

Extended Data Fig. 4 Intrinsic roughness of atomically flat surfaces.

Electron-density profiles near graphite, h-BN and MoS2 surfaces are shown. Schematics of the atomic structures are shown on top. The red curves indicate the thermal exclusion surfaces.

Extended Data Fig. 5 MD simulations for a heavy polymer molecule inside ångström-scale channels.

a, Sketch of our simulation set-up. b, c, Energy of a PMMA molecule (M = 40,000) for slits with N = 4 (b) and N = 12 (c). The axes show the position of the centre of mass with respect to the entrance edge. The origin of the axes is shown in a. The colour scales to the right show the relative free energy (potential of mean force, PMF).

Extended Data Fig. 6 Height of absorbed PMMA.

MD results are shown for the apparent (circles) and gyration (squares) heights of PMMA on graphene. The shaded areas indicate the standard errors using the data for M ≥ 40,000. Error bars show the standard error from our simulation runs lasting 10 ns.

Extended Data Fig. 7 Finite-size entry effect.

If an incident atom of diameter d hits one of the edges of the channel, it can be reflected. To avoid this, the centre trajectory should be d/(2cosθ) away from the edge, effectively reducing the entry aperture to h*(θ) = h − d/cosθ.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Keerthi, A., Geim, A.K., Janardanan, A. et al. Ballistic molecular transport through two-dimensional channels. Nature 558, 420–424 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing