Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Rapid energy-efficient manufacturing of polymers and composites via frontal polymerization


Thermoset polymers and composite materials are integral to today’s aerospace, automotive, marine and energy industries and will be vital to the next generation of lightweight, energy-efficient structures in these enterprises, owing to their excellent specific stiffness and strength, thermal stability and chemical resistance1,2,3,4,5. The manufacture of high-performance thermoset components requires the monomer to be cured at high temperatures (around 180 °C) for several hours, under a combined external pressure and internal vacuum6. Curing is generally accomplished using large autoclaves or ovens that scale in size with the component. Hence this traditional curing approach is slow, requires a large amount of energy and involves substantial capital investment6,7. Frontal polymerization is a promising alternative curing strategy, in which a self-propagating exothermic reaction wave transforms liquid monomers to fully cured polymers. We report here the frontal polymerization of a high-performance thermoset polymer that allows the rapid fabrication of parts with microscale features, three-dimensional printed structures and carbon-fibre-reinforced polymer composites. Precise control of the polymerization kinetics at both ambient and elevated temperatures allows stable monomer solutions to transform into fully cured polymers within seconds, reducing energy requirements and cure times by several orders of magnitude compared with conventional oven or autoclave curing approaches. The resulting polymer and composite parts possess similar mechanical properties to those cured conventionally. This curing strategy greatly improves the efficiency of manufacturing of high-performance polymers and composites, and is widely applicable to many industries.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Overview of the frontal-polymerization concept.
Fig. 2: Advanced manufacturing with FROMP.
Fig. 3: Composite fabrication and modelling.
Fig. 4: Characterization of the FROMP curing approach.

Similar content being viewed by others


  1. Pascault, J.-P., Sautereau, H., Verdu, J. & Williams, R. J. J. Thermosetting Polymers (CRC Press, New York, 2002).

    Book  Google Scholar 

  2. Daniel, I. M. & Ishai, O. Engineering Mechanics of Composite Materials (Oxford Univ. Press, Oxford, 2005).

    Google Scholar 

  3. Brøndsted, P., Lilholt, H. & Lystrup, A. Composite materials for wind power turbine blades. Annu. Rev. Mater. Res. 35, 505–538 (2005).

    Article  ADS  Google Scholar 

  4. Friedrich, K. & Almajid, A. A. Manufacturing aspects of advanced polymer composites for automotive applications. Appl. Compos. Mater. 20, 107–128 (2013).

    Article  ADS  CAS  Google Scholar 

  5. Karbhari, V. M. & Seible, F. Fiber reinforced composites—advanced materials for the renewal of civil infrastructure. Appl. Compos. Mater. 7, 95–124 (2000).

    Article  ADS  CAS  Google Scholar 

  6. Abliz, D. et al. Curing methods for advanced polymer composites—a review. Polym. Polymer Compos. 21, 341–348 (2013).

    CAS  Google Scholar 

  7. Timmis, A. J. et al. Environmental impact assessment of aviation emission reduction through the implementation of composite materials. Int. J. Life Cycle Assess. 20, 233–243 (2015).

    Article  CAS  Google Scholar 

  8. Taynton, P. et al. Repairable woven carbon fiber composites with full recyclability enabled by malleable polyimine networks. Adv. Mater. 28, 2904–2909 (2016).

    Article  CAS  PubMed  Google Scholar 

  9. Lee, J., Stein, I. Y., Kessler, S. S. & Wardle, B. L. Aligned carbon nanotube film enables thermally induced state transformations in layered polymeric materials. ACS Appl. Mater. Interfaces 7, 8900–8905 (2015).

    Article  CAS  PubMed  Google Scholar 

  10. Li, N., Li, Y., Hang, X. & Gao, J. Analysis and optimization of temperature distribution in carbon fiber reinforced composite materials during microwave curing process. J. Mater. Process. Technol. 214, 544–550 (2014).

    Article  CAS  Google Scholar 

  11. Witik, R. A. et al. Economic and environmental assessment of alternative production methods for composite aircraft components. J. Clean. Prod. 29–30, 91–102 (2012).

    Article  Google Scholar 

  12. Pojman, J. A. in Polymer Science: A Comprehensive Reference Vol. 4 (eds. Matyjaszewski, K. & Möller, M.) 957–980 (Elsevier, Amsterdam, 2012).

  13. Chekanov, Y. A. & Pojman, J. A. Preparation of functionally gradient materials via frontal polymerization. J. Appl. Polym. Sci. 78, 2398–2404 (2000).

    Article  CAS  Google Scholar 

  14. Nuvoli, D. et al. Synthesis and characterization of functionally gradient materials obtained by frontal polymerization. ACS Appl. Mater. Interfaces 7, 3600–3606 (2015).

    Article  CAS  PubMed  Google Scholar 

  15. Chen, S., Sui, J., Chen, L. & Pojman, J. A. Polyurethane–nanosilica hybrid nanocomposites synthesized by frontal polymerization. J. Polym. Sci. A 43, 1670–1680 (2005).

    Article  CAS  Google Scholar 

  16. Yan, Q.-Z., Zhang, W.-F., Lu, G.-D., Su, X.-T. & Ge, C.-C. Frontal polymerization synthesis of starch-grafted hydrogels: effect of temperature and tube size on propagating front and properties of hydrogels. Chem. Eur. J. 12, 3303–3309 (2006).

    Article  CAS  PubMed  Google Scholar 

  17. Guo, X., Wang, C.-F., Fang, Y., Chen, L. & Chen, S. Fast synthesis of versatile nanocrystal-embedded hydrogels toward the sensing of heavy metal ions and organoamines. J. Mater. Chem. 21, 1124–1129 (2011).

    Article  CAS  Google Scholar 

  18. Sanna, R. et al. Polymer hydrogels of 2-hydroxyethyl acrylate and acrylic acid obtained by frontal polymerization. J. Polym. Sci. A 50, 1515–1520 (2012).

    Article  CAS  Google Scholar 

  19. Nagy, I. P., Sike, L. & Pojman, J. A. Thermochromic composite prepared via a propagating polymerization front. J. Am. Chem. Soc. 117, 3611–3612 (1995).

    Article  CAS  Google Scholar 

  20. White, S. R. & Kim, C. A simultaneous lay-up and in situ cure process for thick composites. J. Reinf. Plast. Compos. 12, 520–535 (1993).

    Article  ADS  Google Scholar 

  21. Kim, C., Teng, H., Tucker, C. L. & White, S. R. The continuous cuing process for thermoset polymer composites. Part 1: modeling and demonstration. J. Compos. Mater. 29, 1222–1253 (1995).

    Article  ADS  CAS  Google Scholar 

  22. Scognamillo, S., Bounds, C., Luger, M., Mariani, A. & Pojman, J. A. Frontal cationic curing of epoxy resins. J. Polym. Sci. A 48, 2000–2005 (2010).

    Article  CAS  Google Scholar 

  23. Robertson, I. D., Lopez Hernandez, H., White, S. R. & Moore, S. Rapid stiffening of a microfluidic endoskeleton via frontal polymerization. ACS Appl. Mater. Interfaces 6, 18469–18474 (2014).

    Article  CAS  PubMed  Google Scholar 

  24. Datta, P., Efimenko, K. & Genzer, J. The effect of confinement on thermal frontal polymerization. Polym. Chem. 3, 3243–3246 (2012).

    Article  CAS  Google Scholar 

  25. Delaude, L. & Noels, A. F. in Kirk-Othmer Encyclopedia of Chemical Technology Vol. 26 (ed. Seidel, A.) 920–958 (John Wiley & Sons, Inc., Malden, 2007).

  26. Woodson, C. S. Jr & Grubbs, R. H. Polymeric composites including dicyclopentadiene and related monomers. US patent 6,310,121 B1 (2001).

  27. Vallons, K. A. M., Drozdzak, R., Charret, M., Lomov, S. V. & Verpoest, I. Assessment of the mechanical behaviour of glass fibre composites with a tough polydicyclopentadiene (PDCPD) matrix. Compos. Part A Appl. Sci. Manuf. 78, 191–200 (2015).

    Article  CAS  Google Scholar 

  28. Mariani, A., Fiori, S., Chekanov, Y. & Pojman, J. A. Frontal ring-opening metathesis polymerization of dicyclopentadiene. Macromolecules 34, 6539–6541 (2001).

    Article  ADS  CAS  Google Scholar 

  29. Ruiu, A., Sanna, D., Alzari, V., Nuvoli, D. & Mariani, A. Advances in the frontal ring opening metathesis polymerization of dicyclopentadiene. J. Polym. Sci. A 52, 2776–2780 (2014).

    Article  CAS  Google Scholar 

  30. Robertson, I. D. et al. Alkyl phosphite inhibitors for frontal ring-opening metathesis polymerization greatly increase pot life. ACS Macro Lett. 6, 609–612 (2017).

    Article  CAS  Google Scholar 

  31. Yang, G. & Lee, J. K. Curing kinetics and mechanical properties of endo-dicyclopentadiene synthesized using different Grubbs’ catalysts. Ind. Eng. Chem. Res. 53, 3001–3011 (2014).

    Article  CAS  Google Scholar 

  32. Gaston, D., Newman, C., Hansen, G. & Lebrun-Grandié, D. MOOSE: a parallel computational framework for coupled systems of nonlinear equations. Nucl. Eng. Des. 239, 1768–1778 (2009).

    Article  CAS  Google Scholar 

  33. Knoll, D. A. & Keyes, D. E. Jacobian-free Newton–Krylov methods: a survey of approaches and applications. J. Comput. Phys. 193, 357–397 (2004).

    Article  ADS  MathSciNet  MATH  Google Scholar 

  34. Pernice, M. & Walker, H. NITSOL: a Newton iterative solver for nonlinear systems. SIAM J. Sci. Comput. 19, 302–318 (1998).

    Article  MathSciNet  MATH  Google Scholar 

Download references


This research was conducted as part of the Center for Excellence for Self-Healing, Regeneration and Structural Remodeling, supported by the United States Air Force Office of Scientific Research through award FA9550-16-1-0017. We thank J. Sung for preparing the micropatterned silicon substrates, T. Ross for sample photography, D. Loudermilk for graphics assistance, and the Beckman Institute for Advanced Science and Technology for use of their facilities and equipment. I.D.R. thanks the US Department of Defense for a National Defense Science and Engineering Graduate Fellowship. L.M.D. thanks the National Science Foundation for a Graduate Research Fellowship.

Reviewer information

Nature thanks J. Pojman and the other anonymous reviewer(s) for their contribution to the peer review of this work.

Author information

Authors and Affiliations



S.R.W., J.S.M., N.R.S. and P.H.G. directed the research. J.S.M., S.R.W., N.R.S. and I.D.R. conceived the idea. I.D.R., M.Y., P.J.C., J.E.A., D.G.I., E.M.L. and L.M.D. performed the experiments. E.G. conducted the computational studies. All authors participated in writing the manuscript.

Corresponding author

Correspondence to Scott R. White.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 Characterization of DCPD gel and pDCPD products.

a, Heat of reaction, measured by DSC, for the formulation presented in Fig. 4b after ageing the resin at 23 °C for the indicated times. As the curing proceeds, the exothermic peak shifts slightly to lower temperatures and broadens. b, Heat of reaction of pDCPD specimens produced by liquid FROMP, gel FROMP and conventional (oven) cure approaches, indicating fully cured products with a degree of cure of 99.6%, 99.6% and 99.7%, respectively. c, Heat of reaction of the gel before 3D printing and of a cured part after printing, measured by DSC. There is minimal heat of reaction in the printed polymer, indicating a 99.2% degree of cure. d, Rheological profile of the 3D printable gel, showing shear thinning behaviour.

Extended Data Fig. 2 Simulation of FROMP reaction.

a, Schematic representation of the axisymmetric model of FROMP in a glass tube. b, c, Propagation of the reaction front in neat resin. d, Schematic representation of the axisymmetric model of FROMP in the presence of a carbon-fibre tow placed at the centre of the glass tube. e, f, Evolution of the location and profile of the polymerization front in the presence of a carbon-fibre tow.

Extended Data Table 1 Inhibitor concentration and resin incubation time for different manufacturing techniques and the corresponding front temperature and velocity
Extended Data Table 2 Comparison of FRPC panels made with different manufacturing techniques
Extended Data Table 3 Physical and thermal properties of the various components used in computational modelling

Supplementary information

Video 1: Frontal polymerization of an elastic pDCPD gel rolled into a cylinder.

An elastic pDCPD gel is manually shaped into a cylinder and frontally polymerized with a point heat source. The front propagates radially and solidifies the gel into a rigid cylinder within about  3 minutes. The video is presented at 5× speed. The scale bar is 1 cm.

Video 2: Continuous 3D printing and frontal polymerization of a pDCPD helix.

A DCPD gel is printed and simultaneously frontally polymerized. The front initiates where the gel contacts with the heated print bed (70 °C). The front follows behind the nozzle and cures the filament as it is being extruded, forming a freeform helix. The printing takes about 2 minutes. The video is presented at 3× speed. The scale bar is 5 mm.

Video 3: In-plane frontal curing of a 12-ply carbon fibre composite initiated by one resistive heating wire.

FROMP of a 12-ply composite is initiated by powering a single embedded resistive heating wire for 20 seconds. The front propagates from left to right and the part fully cures in about 2 minutes. The video is recorded using a thermal infrared camera and is presented at 4× speed. The scale bar is 5 cm.

Video 4: In-plane frontal curing of a 12-ply carbon fibre composite initiated by two resistive heating wires.

FROMP of a 12-ply composite is initiated by powering two embedded resistive heating wires for 20 seconds. The front propagates from both left and right ends and the part fully cures in about 1 minute. The video is recorded using a thermal infrared camera and is presented at 4× speed. The scale bar is 5 cm.

Video 5: Through-thickness frontal curing of a 12-ply carbon fibre composite initiated by a surface heater.

FROMP of a 12-ply composite is initiated by powering a surface heater from below the layup. The front propagates through the thickness and the cure is complete in about 30 seconds. The video is recorded using a thermal infrared camera and is presented at 4× speed. The scale bar is 5 cm.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Robertson, I.D., Yourdkhani, M., Centellas, P.J. et al. Rapid energy-efficient manufacturing of polymers and composites via frontal polymerization. Nature 557, 223–227 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing