Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Superconductivity with broken time-reversal symmetry inside a superconducting s-wave state


In general, magnetism and superconductivity are antagonistic to each other. However, there are several families of superconductors in which superconductivity coexists with magnetism, and a few examples are known where the superconductivity itself induces spontaneous magnetism. The best known of these compounds are Sr2RuO4 and some non-centrosymmetric superconductors. Here, we report the finding of a narrow dome of an \(s+is^{\prime}\) superconducting phase with apparent broken time-reversal symmetry (BTRS) inside the broad s-wave superconducting region of the centrosymmetric multiband superconductor Ba1 − xKxFe2As2 (0.7 x 0.85). We observe spontaneous magnetic fields inside this dome using the muon spin relaxation (μSR) technique. Furthermore, our detailed specific heat study reveals that the BTRS dome appears very close to a change in the topology of the Fermi surface. With this, we experimentally demonstrate the likely emergence of a novel quantum state due to topological changes of the electronic system.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Multiband superconductivity.
Fig. 2: Thermodynamic properties.
Fig. 3: Zero-field μSR.
Fig. 4: Anisotropy of the muon spin depolarization rate.
Fig. 5: Phase diagram.

Similar content being viewed by others

Data availability

The data represented in Figs. 25 are available as Source Data. All other data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.

Code availability

The code for calculating spontaneous fields within the Ginsburg–Landau model is available with the Supplementary Information files attached to this paper.


  1. Lee, W.-C., Zhang, S.-C. & Wu, C. Pairing state with a time-reversal symmetry breaking in FeAs-based superconductors. Phys. Rev. Lett. 102, 217002 (2009).

    ADS  Google Scholar 

  2. Ng, T. K. & Nagaosa, N. Broken time-reversal symmetry in Josephson junction involving two-band superconductors. Europhys. Lett. 87, 17003 (2009).

    ADS  Google Scholar 

  3. Tanaka, Y. & Yanagisawa, T. Chiral ground state in three-band superconductors. J. Phys. Soc. Jpn 79, 114706 (2010).

    ADS  Google Scholar 

  4. Stanev, V. & Tesanovic, Z. Three-band superconductivity and the order parameter that breaks time-reversal symmetry. Phys. Rev. B 81, 134522 (2010).

    ADS  Google Scholar 

  5. Carlstrom, J., Garaud, J. & Babaev, E. Length scales, collective modes, and type-1.5 regimes in three-band superconductors. Phys. Rev. B 84, 134518 (2011).

    ADS  Google Scholar 

  6. Hu, X. & Wang, Z. Stability and Josephson effect of time-reversal-symmetry-broken multicomponent superconductivity induced by frustrated intercomponent coupling. Phys. Rev. B 85, 064516 (2012).

    ADS  Google Scholar 

  7. Khodas, M. & Chubukov, A. V. Interpocket pairing and gap symmetry in Fe-based superconductors with only electron pockets. Phys. Rev. Lett. 108, 247003 (2012).

    ADS  Google Scholar 

  8. Maiti, S. & Chubukov, A. V. s + is state with broken time-reversal symmetry in Fe-based superconductors. Phys. Rev. B 87, 144511 (2013).

    ADS  Google Scholar 

  9. Garaud, J. & Babaev, E. Domain walls and their experimental signatures in s + is superconductors. Phys. Rev. Lett. 112, 017003 (2014).

    ADS  Google Scholar 

  10. Platt, C., Thomale, R., Honerkamp, C., Zhang, S.-C. & Hanke, W. Mechanism for a pairing state with time-reversal symmetry breaking in iron-based superconductors. Phys. Rev. B 85, 180502(R) (2015).

    Google Scholar 

  11. Maiti, S., Sigrist, M. & Chubukov, A. Spontaneous currents in a superconductor with s + is symmetry. Phys. Rev. B 91, 161102 (2015).

    ADS  Google Scholar 

  12. Garaud, J., Silaev, M. & Babaev, E. Thermoelectric signatures of time-reversal symmetry breaking states in multiband superconductors. Phys. Rev. Lett. 116, 097002 (2016).

    ADS  Google Scholar 

  13. Lin, S.-Z., Maiti, S. & Chubukov, A. Distinguishing between s + id and s + is pairing symmetries in multiband superconductors through spontaneous magnetization pattern induced by a defect. Phys. Rev. B 94, 064519 (2016).

    ADS  Google Scholar 

  14. Böker, J., Volkov, P. A., Efetov, K. B. & Eremin, I. s + is superconductivity with incipient bands: doping dependence and STM signatures. Phys. Rev. B 96, 014517 (2017).

    ADS  Google Scholar 

  15. Yerin, Y., Omelyanchouk, A., Drechsler, S.-L., Efremov, D. V. & van den Brink, J. Anomalous diamagnetic response in multiband superconductors with broken time-reversal symmetry. Phys. Rev. B 96, 144513 (2017).

    ADS  Google Scholar 

  16. Vadimov, V. L. & Silaev, M. A. Polarization of spontaneous magnetic field and magnetic fluctuations in s + is anisotropic multiband superconductors. Phys. Rev. B 98, 104504 (2018).

    ADS  Google Scholar 

  17. Chubukov, A. Itinerant electron scenario for Fe-based superconductors. Springer Series Mater. Sci. 211, 255–329 (2015).

    Google Scholar 

  18. Luke, G. M. et al. Time-reversal symmetry-breaking superconductivity in Sr2RuO4. Nature 394, 558–561 (1998).

    ADS  Google Scholar 

  19. Biswas, P. K. et al. Evidence for superconductivity with broken time-reversal symmetry in locally noncentrosymmetric SrPtAs. Phys. Rev. B 87, 180503(R) (2013).

    ADS  Google Scholar 

  20. Hillier, A. D., Quintanilla, J., Mazidian, B., Annett, J. F. & Cywinski, R. Nonunitary triplet pairing in the centrosymmetric superconductor LaNiGa2. Phys. Rev. Lett. 109, 097001 (2012).

    ADS  Google Scholar 

  21. Mazin, I. I. Superconductivity gets an iron boost. Nature 464, 183–186 (2010).

    ADS  Google Scholar 

  22. Kuroki, K. et al. Unconventional pairing originating from the disconnected Fermi surfaces of superconducting LaFeAsO1 − xFx. Phys. Rev. Lett. 101, 087004 (2008).

    ADS  Google Scholar 

  23. Ahn, F. et al. Superconductivity from repulsion in LiFeAs: novel s-wave symmetry and potential time-reversal symmetry breaking. Phys. Rev. B 89, 144513 (2014).

    ADS  Google Scholar 

  24. Ding, H. et al. Observation of Fermi-surface-dependent nodeless superconducting gaps in Ba0.6K0.4Fe2As2. Europhys. Lett. 83, 47001 (2008).

    ADS  Google Scholar 

  25. Kordyuk, A. A. ARPES experiment in fermiology of quasi-2D metals. Low Temp. Phys. 40, 286–296 (2014).

    ADS  Google Scholar 

  26. Xu, N. et al. Possible nodal superconducting gap and Lifshitz transition in heavily hole-doped Ba0.1K0.9Fe2As2. Phys. Rev. B 88, 220508(R) (2013).

    ADS  Google Scholar 

  27. Malaeb, W. et al. Abrupt change in the energy gap of superconducting Ba1 − xKxFe2As2 single crystals with hole doping. Phys. Rev. B 86, 165117 (2012).

    ADS  Google Scholar 

  28. Grinenko, V. et al. Superconductivity with broken time-reversal symmetry in ion-irradiated Ba0.27K0.73Fe2As2 single crystals. Phys. Rev. B 95, 214511 (2017).

    ADS  Google Scholar 

  29. Bobkov, A. M. & Bobkova, I. V. Time-reversal symmetry breaking state near the surface of s ±-superconductor. Phys. Rev. B 84, 134527 (2011).

    ADS  Google Scholar 

  30. Liu, Y. & Lograsso, T. A. Crossover in the magnetic response of single-crystalline Ba1 − xKxFe2As2 and Lifshitz critical point evidenced by Hall effect measurements. Phys. Rev. B 90, 224508 (2014).

    ADS  Google Scholar 

  31. Hirano, M. et al. Potential antiferromagnetic fluctuations in hole-doped iron-pnictide superconductor Ba1 − xKxFe2As2 studied by 75As nuclear magnetic resonance measurement. J. Phys. Soc. Jpn 81, 054704 (2012).

    ADS  Google Scholar 

  32. Eilers, F. et al. Strain-driven approach to quantum criticality in AFe2As2 with A = K, Rb and Cs. Phys. Rev. Lett. 116, 237003 (2016).

    ADS  Google Scholar 

  33. Drechsler, S.-L., Johnston, S., Grinenko, V., Tomczak, J. M. & Rosner, H. Constraints on the total coupling strength to bosons in the iron based superconductors. Phys. Status Solidi B 254, 1700006 (2017).

    ADS  Google Scholar 

  34. Drechsler, S.-L. et al. Mass enhancements and band shifts in strongly hole-overdoped Fe-based pnictide superconductors: KFe2As2 and CsFe2As2. J. Supercond. Novel Magn. 31, 777–783 (2018).

    Google Scholar 

  35. Bud’ko, S. L., Ni, N. & Canfield, P. C. Jump in specific heat at the superconducting transition temperature in Ba(Fe1 − xCox)2As2 and Ba(Fe1 − xNix)2As2 single crystals. Phys. Rev. B 79, 220516(R) (2009).

    ADS  Google Scholar 

  36. Bang, Y. & Stewart, G. R. Superconducting properties of the s ±-wave state: Fe-based superconductors. J. Phys. Condens. Matter 29, 123003 (2017).

    ADS  Google Scholar 

  37. Ota, Y. et al. Evidence for excluding the possibility of d-wave superconducting-gap symmetry in Ba-doped KFe2As2. Phys. Rev. B 89, 081103(R) (2014).

    ADS  Google Scholar 

  38. Watanabe, D. et al. Doping evolution of the quasiparticle excitations in heavily hole-doped Ba1 − xKxFe2As2: a possible superconducting gap with sign-reversal between hole pockets. Phys. Rev. B 89, 115112 (2014).

    ADS  Google Scholar 

  39. Cho, K., Konczykowski, M., Teknowijoyo, S., Tanatar, M. A. & Prozorov, R. Using electron irradiation to probe iron-based superconductors. Supercond. Sci. Technol. 31, 064002 (2018).

    ADS  Google Scholar 

  40. Yoshida, T. et al. Orbital character and electron correlation effects on two- and three-dimensional Fermi surfaces in KFe2As2 revealed by angle-resolved photoemission spectroscopy. Front. Phys. 2, 17 (2014).

    Google Scholar 

  41. Blanter, Y. M., Kaganov, M. I., Pantsulaya, A. V. & Varlamova, A. A. The theory of electronic topological transitions. Phys. Rep. 245, 159–257 (1994).

    ADS  Google Scholar 

  42. Hodovanets, H. et al. Fermi surface reconstruction in Ba1−xKxFe2As2 (0.44 ≤ x ≤ 1) probed by thermoelectric power measurements. Phys. Rev. B 89, 224517 (2014).

    ADS  Google Scholar 

  43. Grinenko, V. et al. Superconducting specific-heat jump \({C}_{{\rm{el}}}\propto {T}_{{\rm{c}}}^{\beta }\)(β≈ 2) for K1−xNaxFe2As2. Phys. Rev. B 89, 060504(R) (2014).

    Google Scholar 

  44. Hardy, F. et al. Strong correlations, strong coupling and s-wave superconductivity in hole-doped BaFe2As2 single crystals. Phys. Rev. B 94, 205113 (2016).

    ADS  Google Scholar 

  45. Hatlo, M. et al. Developments of mathematical software libraries for the LHC experiments. IEEE Trans. Nucl. Sci. 52, 2818–2822 (2005).

    ADS  Google Scholar 

  46. Grinenko, V. et al. Superconducting properties of K1−xNaxFe2As2 under pressure. Phys. Rev. B 90, 094511 (2014).

    ADS  Google Scholar 

  47. Kihou, K. et al. Single-crystal growth of Ba1 − xKxFe2As2 by KAs self-flux method. J. Phys. Soc. Jpn 85, 034718 (2016).

    ADS  Google Scholar 

  48. Amato, A. et al. The new versatile general purpose surface-muon instrument (GPS) based on silicon photomultipliers for μSR measurements on a continuous-wave beam. Rev. Sci. Instrum. 88, 093301 (2017).

    ADS  Google Scholar 

  49. Suter, A. & Wojek, B. M. Musrfit: A free platform-independent framework for μSR data analysis. Phys. Procedia 30, 69–73 (2012).

    Google Scholar 

  50. Koepernik, K. & Eschrig, H. Full-potential nonorthogonal local-orbital minimum-basis bandstructure scheme. Phys. Rev. B 59, 1743–1757 (1990).

    ADS  Google Scholar 

  51. Garaud, J., Silaev, M. & Babaev, E. Microscopically derived multi-component Ginzburg–Landau theories for s + is superconducting state. Proc. Ninth International Conference on Vortex Matter in Nanostructured Superconductors 533, 63–73 (2017).

    Google Scholar 

  52. Virtanen, P. et al. SciPy 1.0: fundamental algorithms for scientific computing in Python. Nat. Methods 17, 261–272 (2020).

    Google Scholar 

Download references


This work was supported by DFG (GR 4667/1, GRK 1621 and SFB 1143 project C02). The work of M. A. Silaev was supported by the Academy of Finland (project no. 297439). The work of I.E. was carried out with support from the Ministry of Science and Higher Education of the Russian Federation in the framework of Increase Competitiveness Program of NUST MISiS grant no. К2-2020-001. This work was partly performed at the Swiss Muon Source (SμS), PSI, Villigen. We acknowledge fruitful discussions with A. Amato, S. Borisenko, E. Babaev, A. Charnukha, O. Dolgov, C. Hicks, C. Meingast and A. de Visser. We especially acknowledge D. Efremov for support with DFT calculations. We are grateful for technical assistance from C. Baines.

Author information

Authors and Affiliations



V.G. designed the study, initiated and supervised the project and wrote the paper, performed the μSR, specific heat, magnetic susceptibility and X-ray diffraction measurements. R.S. performed the μSR experiments. K.K. and C.H.L. prepared Ba1 − xKxFe2As2 single crystals in the doping range 0.65 x 0.85. I.M. and S.A. prepared Ba1 − xKxFe2As2 single crystals with x ≈ 0.98. P.C. performed and W.S. supervised TEM measurements. K. Nenkov performed specific heat and magnetization measurements. B.B, R.H. and K. Nielsch supervised the research at IFW. S.-L.D. provided interpretation of the experimental data. V.L.V. and M.A.S. performed calculation of the spontaneous magnetic fields in the BTRS state. P.A.V. and I.E. analysed specific heat in the BTRS state. H.L. performed μSR experiments and supervised the research at PSI. H.-H.K. initiated the project and supervised the research. All authors discussed the results and implications and commented on the manuscript.

Corresponding authors

Correspondence to V. Grinenko, M. A. Silaev or H.-H. Klauss.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Physics thanks Thomas A. Maier and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data

Extended Data Fig. 1 Normal state depolarization rate.

(Left axis) Doping dependence of the normal state depolarization rate Λ0 extrapolated to zero temperature as shown in Fig. 3 of the main text obtained assuming temperature independent σ. The error-bars in the absolute value of the depolarization rate is caused by uncertainty in the background contribution. (Right axis) Doping dependence of the static susceptibility measured at T = 20 K given in Fig. 2a of the main text. Dashed lines are guides to the eyes. Inset: Doping dependence of the temperature independent depolarization rate σ.

Extended Data Fig. 2 The structure of the spontaneous fields and currents in an s + is superconductor.

The structure of the spontaneous magnetic field (left panels) and spontaneous currents (right panels) produced by the spherically-symmetric inhomogeneity in anisotropic s + is and sis states. In the left panels the red/blue arrows show clockwise/counter-clockwise parts of the magnetic field distribution. The clockwise and counter-clockwise field is generated by the supercurrents with jz > 0 (red arrows) and jz < 0 (blue arrows) shown in the right panels. Notice that the magnetic field and current directions are opposite in s + is and sis states. The length-scale in the axes is given in units of the zero-temperature coherence length ħvF/Tc. The x, y and z axes are chosen along the a, b and c crystallographic directions, respectively.

Extended Data Fig. 3 Anisotropy of the internal fields in an s + is superconductor.

Two orthogonal components of the normalized internal spontaneous fields Bint/Bc2 depending on a strength of the variation of the SC coupling constant Δη2 due to an inhomogeneity. Inset: Δη2 dependence of the anisotropy ratio of the internal fields γint. In the main text ΔλaΔη2 with a ~ 1 (see section 6 in the Supplementary information for details).

Extended Data Fig. 4 Electrical resistivity.

(a) Temperature dependence of the resistivity of the Ba1−xKxFe2As2 single crystals with different doping levels. Inset: Zoom into the temperature range close Tc. (b) The resistivity versus squared temperature. Dashed curves are the fits using ρ(T) = ρ0 + AFLT2. Inset: Doping dependence of the AFL coefficient. The data for x = 1 are taken from Ref. 46.

Extended Data Fig. 5 Impurity effect on the phase diagram.

Doping dependence of the residual resistivity ρ0 of the Ba1−xKxFe2As2 single crystals (green triangles, right axis) on top of the phase diagram with the region close to the BTRS dome.

Supplementary information

Supplementary Information

Supplementary Figs. 1–12 and discussion.

Supplementary Software 1

The code for calculating spontaneous fields within the Ginsburg–Landau model. Software_1 file contains the code implementing relaxation minimization of the free energy functional defined on the triangular grid which is constructed in Software_2 file. The parameters of the Ginzburg–Landau model like temperature, pairing constants and effective masses are passed to the constructor of the main class SPlusIS_XZ. Parameter ‘kappa’ defines the ratio between the London penetration depth and the coherence length (the default value None corresponds to the infinite penetration depth), parameter ‘spis’ distinguishes between the s + is and s + id cases. The method ‘solve’ of this class minimizes the free energy functional.

Supplementary Software 2

The code for calculating spontaneous fields within the Ginsburg–Landau model. Software_2 file contains a class that describes a triangular grid and vector operations like gradient, divergence and curl.

Source data

Source Data Fig. 2

Susceptibility data and raw SQUID data from Fig. 2a Electronic specific heat from Fig. 2b Tc, Electronic specific heat/T, Sommerfeld coefficient versus K-doping from Fig. 2c and 2d.

Source Data Fig. 3

Zero-field muSR time spectra from Fig. 3a, 3b, and 3c muon spin depolarization rate at different temperatures and magnetic susceptibility at Bab = 0.5 mT from Figs. 3d, Fig. 3e, Fig. 3f, Fig. 3g and Fig. 3h.

Source Data Fig. 4

Muon spin depolarization rate at different temperatures for Pμc, and for Pμa from Fig. 4a and Fig. 4b.

Source Data Fig. 5

Tc defined from specific heat and magnetization data, TBTRS temperature, electronic specific heat, experimental Sommerfeld coefficient, calculated DOS, calculated Sommerfeld coefficient \({\gamma }_{{\rm{DFT}}}/{\gamma }_{{\rm{DFT}},\min }\) and calculated mean field \({T}_{{\rm{c}}}/{T}_{{\rm{c}},\min }\) versus K-doping.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Grinenko, V., Sarkar, R., Kihou, K. et al. Superconductivity with broken time-reversal symmetry inside a superconducting s-wave state. Nat. Phys. 16, 789–794 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing