Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Observation of two independent skyrmion phases in a chiral magnetic material


Magnetic materials can host skyrmions, which are topologically non-trivial spin textures. In chiral magnets with cubic lattice symmetry, all previously observed skyrmion phases require thermal fluctuations to become thermodynamically stable in bulk materials, and therefore exist only at relatively high temperature, close to the helimagnetic transition temperature. Other stabilization mechanisms require a lowering of the cubic crystal symmetry. Here, we report the identification of a second skyrmion phase in Cu2OSeO3 at low temperature and in the presence of an applied magnetic field. The new skyrmion phase is thermodynamically disconnected from the well-known, nearly isotropic, high-temperature phase, and exists, in contrast, when the external magnetic field is oriented along the 〈100〉 crystal axis only. Theoretical modelling provides evidence that the stabilization mechanism is given by well-known cubic anisotropy terms, and accounts for an additional observation of metastable helices tilted away from the applied field. The identification of two distinct skyrmion phases in the same material and the generic character of the underlying mechanism suggest a new avenue for the discovery, design and manipulation of topological spin textures.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Qualitative depiction of the intensity patterns in reciprocal space characterizing the modulated magnetic order in Cu2OSeO3 and magnetic phase diagrams for different temperature versus field histories.
Fig. 2: Typical small-angle neutron scattering patterns, intensity maps, and specific temperature dependences of the integrated intensity for HFC/FH.
Fig. 3: Signatures of increasing magnetic anisotropies under increasing magnetic field at approximately 3.6 K and the skyrmionic nature of the low-temperature phase.
Fig. 4: Key results of the theoretical calculations.

Similar content being viewed by others


  1. Skyrme, T. A unified field theory of mesons and baryons. Nucl. Phys. 31, 556–569 (1962).

    Article  MathSciNet  Google Scholar 

  2. Brown, G. E. & Rho, M. The Multifaceted Skyrmion (World Scientific, Singapore, 2010).

  3. Volovik, G. The Universe in a Helium Droplet (Clarendon Press, Oxford, 2003).

    MATH  Google Scholar 

  4. Al Khawaja, U. & Stoof, H. Skyrmions in a ferromagnetic Bose–Einstein condensate. Nature 411, 918–920 (2001).

    Article  ADS  Google Scholar 

  5. Mühlbauer, S. et al. Skyrmion lattice in a chiral magnet. Science 323, 915–919 (2009).

    Article  ADS  Google Scholar 

  6. Münzer, W. et al. Skyrmion lattice in the doped semiconductor Fe1−xCoxSi. Phys. Rev. B 81, 041203(R) (2010).

    Article  ADS  Google Scholar 

  7. Yu, X. Z. et al. Near room-temperature formation of a skyrmion crystal in thin-films of the helimagnet FeGe. Nat. Mater. 10, 106–109 (2011).

    Article  ADS  Google Scholar 

  8. Seki, S., Yu, X. Z., Ishiwata, S. & Tokura, Y. Observation of skyrmions in a multiferroic material. Science 336, 198–201 (2012).

    Article  ADS  Google Scholar 

  9. Nagaosa, N. & Tokura, Y. Topological properties and dynamics of magnetic skyrmions. Nat. Nanotech. 8, 899–911 (2013).

    Article  ADS  Google Scholar 

  10. Landau, L. D. & Lifshitz, E. M. Course of Theoretical Physics Vol. 8 (Pergamon Press, Oxford, 1980).

  11. Bogdanov, A. & Yablonskii, D. Thermodynamically stable “vortices” in magnetically ordered crystals. The mixed state of magnets. Zh. Eksp. Teo. Fiz. 95, 178–182 (1989).

    Google Scholar 

  12. Tokunaga, Y. et al. A new class of chiral materials hosting magnetic skyrmions beyond room temperature. Nat. Commun. 6, 7638 (2015).

    Article  Google Scholar 

  13. Buhrandt, S. & Fritz, L. Skyrmion lattice phase in three-dimensional chiral magnets from Monte Carlo simulations. Phys. Rev. B 88, 195137 (2013).

    Article  ADS  Google Scholar 

  14. Bauer, A. & Pfleiderer, C. in Generic Aspects of Skyrmion Lattices in Chiral Magnets in Topological Structures in Ferroic Materials (ed. Seidel, J.) 1–28 (Springer, Basel, 2016).

  15. Kezsmarki, I. et al. Néel-type skyrmion lattice with confined orientation in the polar magnetic semiconductor GaV4S8. Nat. Mater. 14, 1116–1122 (2015).

    Article  ADS  Google Scholar 

  16. Bordacs, S. et al. Equilibrium skyrmion lattice ground state in a polar easy-plane magnet. Sci. Rep. 7, 7584 (2017).

    Article  ADS  Google Scholar 

  17. Yu, X. et al. Magnetic stripes and skyrmions with helicity reversals. Proc. Natl Acad. Sci. 109, 8856–8860 (2012).

    Article  ADS  Google Scholar 

  18. Nayak, A. K. et al. Magnetic antiskyrmions above room temperature in tetragonal Heusler materials. Nature 548, 561–566 (2017).

    Article  ADS  Google Scholar 

  19. Wilson, M. N., Butenko, A. B., Bogdanov, A. N. & Monchesky, T. L. Chiral skyrmions in cubic helimagnet films: The role of uniaxial anisotropy. Phys. Rev. B 89, 094411 (2014).

    Article  ADS  Google Scholar 

  20. Kanazawa, N. et al. Critical phenomena of emergent magnetic monopoles in a chiral magnet. Nat. Commun. 7, 11622 (2016).

    Article  ADS  Google Scholar 

  21. Chacon, A. et al. Uniaxial pressure dependence of magnetic order in MnSi. Phys. Rev. Lett. 115, 267202 (2015).

    Article  ADS  Google Scholar 

  22. Okamura, Y., Kagawa, F., Seki, S. & Tokura, Y. Transition to and from the skyrmion lattice phase by electric fields in a magnetoelectric compound. Nat. Commun. 7, 12669 (2016).

    Article  ADS  Google Scholar 

  23. Oike, H. et al. Interplay between topological and thermodynamic stability in a metastable magnetic skyrmion lattice. Nat. Phys. 12, 62–66 (2016).

    Article  Google Scholar 

  24. Karube, K. et al. Robust metastable skyrmions and their triangular-square lattice structural transition in a high-temperature chiral magnet. Nat. Mater. 15, 1237–1242 (2016).

    Article  ADS  Google Scholar 

  25. Grigoriev, S. V., Sukhanov, A. S. & Maleyev, S. V. From spiral to ferromagnetic structure in B20 compounds: Role of cubic anisotropy. Phys. Rev. B 91, 224429 (2015).

    Article  ADS  Google Scholar 

  26. Belesi, M. et al. Magnetoelectric effects in single crystals of the cubic ferrimagnetic helimagnet Cu2OSeO3. Phys. Rev. B 85, 224413 (2012).

    Article  ADS  Google Scholar 

  27. Qian, F. et al. Phase diagram and magnetic relaxation phenomena in Cu2OSeO3. Phys. Rev. B 94, 064418 (2016).

    Article  ADS  Google Scholar 

  28. Qian, F. et al. New magnetic phase of the chiral skyrmion material Cu2OSeO3. Preprint at (2018).

  29. Milde, P. et al. Unwinding of a skyrmion lattice by magnetic monopoles. Science 340, 1076–1080 (2013).

    Article  ADS  Google Scholar 

  30. Wild, J. et al. Entropy-limited topological protection of skyrmions. Sci. Adv. 3, e1701704 (2017).

    Article  ADS  Google Scholar 

  31. Mühlbauer, S. et al. The new small-angle neutron scattering instrument SANS-1 at MLZ—characterization and first results. Nucl. Instr. Meth. Phys. Res. A 832, 297–305 (2016).

    Article  ADS  Google Scholar 

Download references


We wish to thank F. Haslbeck, S. Mayr, M. Meven and the team at FRM II for helpful discussions and support. A.C., M.H. and W.S. acknowledge financial support through the TUM Graduate School. L.H. and A.R. acknowledge financial support through DFG CRC1238 (project C02). M.G. acknowledges financial support from DFG CRC 1143 and DFG grant 1072/5. A.B., M.H., W.S. and C.P. acknowledge support through DFG TRR80 (projects E1, F2 and F7) as well as ERC-AdG (291079 TOPFIT).

Author information

Authors and Affiliations



A.C., M.H., A.B., W.S. and S.M. performed the experimental work; A.C. analysed the data; C.P. supervised the experimental work; H.B. grew the single crystals; L.H., M.G. and A.R. developed the theoretical analysis; A.C. and C.P. proposed this study and wrote the manuscript; all authors discussed the data and commented on the manuscript; correspondence may be addressed to A.C. and C.P.

Corresponding authors

Correspondence to A. Chacon or C. Pfleiderer.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supporting online material

Supplementary figures S1 to S23

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Chacon, A., Heinen, L., Halder, M. et al. Observation of two independent skyrmion phases in a chiral magnetic material. Nature Phys 14, 936–941 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing