Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Robust graphene-based molecular devices

Abstract

One of the main challenges to upscale the fabrication of molecular devices is to achieve a mechanically stable device with reproducible and controllable electronic features that operates at room temperature1,2. This is crucial because structural and electronic fluctuations can lead to significant changes in the transport characteristics at the electrode–molecule interface3,4. In this study, we report on the realization of a mechanically and electronically robust graphene-based molecular junction. Robustness was achieved by separating the requirements for mechanical and electronic stability at the molecular level. Mechanical stability was obtained by anchoring molecules directly to the substrate, rather than to graphene electrodes, using a silanization reaction. Electronic stability was achieved by adjusting the ππ orbitals overlap of the conjugated head groups between neighbouring molecules. The molecular devices exhibited stable current–voltage (IV) characteristics up to bias voltages of 2.0 V with reproducible transport features in the temperature range from 20 to 300 K.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Junction geometry, molecular design and electrical characterization.
Fig. 2: Electrical characterization of devices A (left), B (middle) and C (right) at 20 K exposed to the molecule BPC.
Fig. 3: Transport measurements through a BPC molecular junction (device A) at different temperatures.
Fig. 4: Transport through graphene–molecule–graphene junctions that containing the M and BPC molecule.

Similar content being viewed by others

Data availability

The data that support the plots within this paper and other findings of this study are available from the corresponding authors upon reasonable request. Measurements and analysis were performed in Origin and Matlab. All codes are available from the authors upon reasonable request.

References

  1. van der Molen, S. J. et al. Visions for a molecular future. Nat. Nanotechnol. 8, 385–389 (2013).

    Article  Google Scholar 

  2. Aradhya, S. V. & Venkataraman, L. Single-molecule junctions beyond electronic transport. Nat. Nanotechnol. 8, 399–410 (2013).

    Article  CAS  Google Scholar 

  3. Sadeghi, H., Sangtarash, S. & Lambert, C. Robust molecular anchoring to graphene electrodes. Nano Lett. 17, 4611–4618 (2017).

    Article  CAS  Google Scholar 

  4. Tao, N. Electron transport in molecular junctions. Nat. Nanotechnol. 1, 173–181 (2006).

    Article  CAS  Google Scholar 

  5. Lau, C. S. et al. Redox-dependent Franck–Condon blockade and avalanche transport in a graphene–fullerene single-molecule transistor. Nano Lett. 16, 170–176 (2015).

    Article  Google Scholar 

  6. Barreiro, A., van der Zant, H. S. & Vandersypen, L. M. Quantum dots at room temperature carved out from few-layer graphene. Nano Lett. 12, 6096–6100 (2012).

    Article  CAS  Google Scholar 

  7. Sadeghi, H. et al. Conductance enlargement in picoscale electroburnt graphene nanojunctions. Proc. Natl Acad. Sci. USA 112, 2658–2663 (2015).

    Article  CAS  Google Scholar 

  8. Gehring, P. et al. Quantum interference in graphene nanoconstrictions. Nano Lett. 16, 4210–4216 (2016).

    Article  CAS  Google Scholar 

  9. Prins, F. et al. Room-temperature gating of molecular junctions using few-layer graphene nanogap electrodes. Nano Lett. 11, 4607–4611 (2011).

    Article  CAS  Google Scholar 

  10. Jia, C. et al. Covalently bonded single-molecule junctions with stable and reversible photoswitched conductivity. Science 352, 1443–1445 (2016).

    Article  CAS  Google Scholar 

  11. Su, T. A., Neupane, M., Steigerwald, M. L., Venkataraman, L. & Nuckolls, C. Chemical principles of single-molecule electronics. Nat. Rev. Mater. 1, 16002 (2016).

    Article  CAS  Google Scholar 

  12. Li, S. et al. The evolving quality of frictional contact with graphene. Nature 539, 541–545 (2016).

    Article  CAS  Google Scholar 

  13. Mol, J. A. et al. Graphene–porphyrin single-molecule transistors. Nanoscale 7, 13181–13185 (2015).

    Article  CAS  Google Scholar 

  14. Xu, Q. et al. Single electron transistor with single aromatic ring molecule covalently connected to graphene nanogaps. Nano Lett. 17, 5335–5341 (2017).

    Article  CAS  Google Scholar 

  15. Yao, J., Zhong, L., Natelson, D. & Tour, J. M. Silicon oxide: a non-innocent surface for molecular electronics and nanoelectronics studies. J. Am. Chem. Soc. 133, 941–948 (2011).

    Article  CAS  Google Scholar 

  16. Pósa, L. et al. Multiple physical time scales and dead time rule in few-nanometers sized graphene–SiOx–graphene memristors. Nano Lett. 17, 6783–6789 (2017).

    Article  Google Scholar 

  17. Aswal, D., Lenfant, S., Guerin, D., Yakhmi, J. & Vuillaume, D. Self-assembled monolayers on silicon for molecular electronics. Anal. Chem. Acta 568, 84–108 (2006).

    Article  CAS  Google Scholar 

  18. DiBenedetto, S. A., Facchetti, A., Ratner, M. A. & Marks, T. J. Molecular self-assembled monolayers and multilayers for organic and unconventional inorganic thin-film transistor applications. Adv. Mater. 21, 1407–1433 (2009).

    Article  CAS  Google Scholar 

  19. Krasnoslobodtsev, A. V. & Smirnov, S. N. Effect of water on silanization of silica by trimethoxysilanes. Langmuir 18, 3181–3184 (2002).

    Article  CAS  Google Scholar 

  20. Hines, T. et al. Transition from tunneling to hopping in single molecular junctions by measuring length and temperature dependence. J. Am. Chem. Soc. 132, 11658–11664 (2010).

    Article  CAS  Google Scholar 

  21. Segal, D., Nitzan, A., Davis, W. B., Wasielewski, M. R. & Ratner, M. A. Electron transfer rates in bridged molecular systems 2. A steady-state analysis of coherent tunneling and thermal transitions. J. Phys. Chem. B 104, 3817–3829 (2000).

    Article  CAS  Google Scholar 

  22. Kim, H. & Segal, D. Controlling charge transport mechanisms in molecular junctions: distilling thermally induced hopping from coherent-resonant conduction. J. Chem. Phys. 146, 164702 (2017).

    Article  Google Scholar 

  23. Hihath, J. Charge transport in the inverted Marcus region. Nat. Nanotechnol. 13, 276–277 (2018).

    Article  CAS  Google Scholar 

  24. Yuan, L. et al. Transition from direct to inverted charge transport Marcus regions in molecular junctions via molecular orbital gating. Nat. Nanotechnol. 13, 322–329 (2018).

    Article  CAS  Google Scholar 

  25. Selzer, Y., Cabassi, M. A., Mayer, T. S. & Allara, D. L. Thermally activated conduction in molecular junctions. J. Am. Chem. Soc. 126, 4052–4053 (2004).

    Article  CAS  Google Scholar 

  26. Soler, J. M. et al. The SIESTA method for ab initio order-N materials simulation. J. Phys. Condens. Matter 14, 2745 (2002).

    Article  CAS  Google Scholar 

  27. Ferrer, J. et al. Gollum: a next-generation simulation tool for electron, thermal and spin transport. New J. Phys. 16, 093029 (2014).

    Article  Google Scholar 

  28. Nef, C. et al. High-yield fabrication of nm-size gaps in monolayer CVD graphene. Nanoscale 6, 7249–7254 (2014).

    Article  CAS  Google Scholar 

  29. El Abbassi, M. et al. From electroburning to sublimation: substrate and environmental effects in the electrical breakdown process of monolayer graphene. Nanoscale 9, 17312–17317 (2017).

    Article  CAS  Google Scholar 

  30. Chenoweth, K., van Duin, A. C. T. & Goddard, W. A. Reaxff reactive force field for molecular dynamics simulations of hydrocarbon oxidation. J. Phys. Chem. A 112, 1040–1053 (2008).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

We thank C. Schönenberger for fruitful discussions. This work was partially supported by the European Commission FP7-ITN Molecular-scale Electronics: Concepts, Contacts and Stability (MOLESCO) grant (no. 606728) and the FET open project QuIET (no. 767187). This work was supported by UK Engineering and Physical Sciences Research Council Grant EP/M014452/1 and EP/N017188/1 and the European Research Council Advanced Grant (Mols@Mols). H.S. acknowledges the UK Research and Innovation for Future Leaders Fellowship no. MR/S015329/1 and the Leverhulme Trust for Leverhulme Early Career Fellowship no. ECF-2017-186. S.S. acknowledges the Leverhulme Trust for Early Career Fellowship no. ECF-2018-375. M.L.P. acknowledges the funding by the EMPAPOSTDOCS-II programme, which has received funding from the European Union’s Horizon 2020 research and innovation programme under the Marie Skłodowska–Curie Grant Agreement no. 754364. O.B. acknowledges technical support from the Binning and Rohrer Nanotechnology Center (BRNC).

Author information

Authors and Affiliations

Authors

Contributions

M.E.A. conducted the measurements and performed the data analysis. O.B. and M.E.A. fabricated the devices. X.L, S.-X.L., S.D. and S.Y. provided the molecules. S.S. and H.S. provided the theory and performed the DFT calculations. M.E.A., M.L.P., H.S., H.S.J.vdZ., C.L. and M.C. designed and supervised the study. M.E.A., M.L.P., S.S. and H.S. wrote the paper. M.E.A., M.L.P., S.S., H.S. and M.C. participated in the discussion of the data. All the authors discussed the results and commented on the manuscript.

Corresponding authors

Correspondence to Shi-Xia Liu, Hatef Sadeghi or Michel Calame.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Nanotechnology thanks Dirk Mayer and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–9 and refs. 1–3.

Supplementary Movie 1

MD movie molecule C.

Supplementary Movie 2

MD movie molecule BPC.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

El Abbassi, M., Sangtarash, S., Liu, X. et al. Robust graphene-based molecular devices. Nat. Nanotechnol. 14, 957–961 (2019). https://doi.org/10.1038/s41565-019-0533-8

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41565-019-0533-8

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing