Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Electrical control of 2D magnetism in bilayer CrI3


Controlling magnetism via electric fields addresses fundamental questions of magnetic phenomena and phase transitions1,2,3, and enables the development of electrically coupled spintronic devices, such as voltage-controlled magnetic memories with low operation energy4,5,6. Previous studies on dilute magnetic semiconductors such as (Ga,Mn)As and (In,Mn)Sb have demonstrated large modulations of the Curie temperatures and coercive fields by altering the magnetic anisotropy and exchange interaction2,4,7,8,9. Owing to their unique magnetic properties10,11,12,13,14, the recently reported two-dimensional magnets provide a new system for studying these features15,16,17,18,19. For instance, a bilayer of chromium triiodide (CrI3) behaves as a layered antiferromagnet with a magnetic field-driven metamagnetic transition15,16. Here, we demonstrate electrostatic gate control of magnetism in CrI3 bilayers, probed by magneto-optical Kerr effect (MOKE) microscopy. At fixed magnetic fields near the metamagnetic transition, we realize voltage-controlled switching between antiferromagnetic and ferromagnetic states. At zero magnetic field, we demonstrate a time-reversal pair of layered antiferromagnetic states that exhibit spin-layer locking, leading to a linear dependence of their MOKE signals on gate voltage with opposite slopes. Our results allow for the exploration of new magnetoelectric phenomena and van der Waals spintronics based on 2D materials.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type



Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Bilayer CrI3 spin ordering, gated device structure, and RMCD without gating.
Fig. 2: MOKE signal versus gate voltage and applied magnetic field.
Fig. 3: Origin of voltage-controlled metamagnetism.
Fig. 4: Gate-voltage-induced MOKE of layered AFM states at zero magnetic field.


  1. Chiba, D. et al. Electrical control of the ferromagnetic phase transition in cobalt at room temperature. Nat. Mater. 10, 853–856 (2011).

    Article  Google Scholar 

  2. Chiba, D. et al. Magnetization vector manipulation by electric fields. Nature 455, 515–518 (2008).

    Article  Google Scholar 

  3. Eerenstein, W., Mathur, N. D. & Scott, J. F. Multiferroic and magnetoelectric materials. Nature 442, 759–765 (2006).

    Article  Google Scholar 

  4. Matsukura, F., Tokura, Y. & Ohno, H. Control of magnetism by electric fields. Nat. Nanotech. 10, 209–220 (2015).

    Article  Google Scholar 

  5. Prinz, G. A. Magnetoelectronics. Science 282, 1660–1663 (1998).

    Article  Google Scholar 

  6. Chu, Y. H. et al. Electric-field control of local ferromagnetism using a magnetoelectric multiferroic. Nat. Mater. 7, 478–482 (2008).

    Article  Google Scholar 

  7. Ohno, H. et al. Electric-field control of ferromagnetism. Nature 408, 944–947 (2000).

    Article  Google Scholar 

  8. Dietl, T., Ohno, H., Matsukura, F., Cibert, J. & Ferrand, D. Zener model description of ferromagnetism in zinc-blende magnetic semiconductors. Science 287, 1019–1022 (2000).

    Article  Google Scholar 

  9. MacDonald, A. H., Schiffer, P. & Samarth, N. Ferromagnetic semiconductors: moving beyond (Ga,Mn)As. Nat. Mater. 4, 195–202 (2005).

    Article  Google Scholar 

  10. Gong, C. et al. Discovery of intrinsic ferromagnetism in two-dimensional van der Waals crystals. Nature 546, 265–269 (2017).

    Article  Google Scholar 

  11. Tian, Y., Gray, M. J., Ji, H., Cava, R. J. & Burch, K. S. Magneto-elastic coupling in a potential ferromagnetic 2D atomic crystal. 2D Mater. 3, 25035 (2016).

    Article  Google Scholar 

  12. Zhou, B. et al. Possible structural transformation and enhanced magnetic fluctuations in exfoliated α-RuCl3. J. Phys. Chem. Solids (in the press).

  13. O’Hara, D. J. et al. Room temperature intrinsic ferromagnetism in epitaxial manganese selenide films in the monolayer limit. Preprint at (2018).

  14. Wang, X. et al. Raman spectroscopy of atomically thin two-dimensional magnetic iron phosphorus trisulfide (FePS3) crystals. 2D Mater. 3, 31009 (2016).

    Article  Google Scholar 

  15. Huang, B. et al. Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit. Nature 546, 270–273 (2017).

    Article  Google Scholar 

  16. Seyler, K. L. et al. Ligand-field helical luminescence in a 2D ferromagnetic insulator. Nat. Phys. 14, 277–281 (2018).

    Article  Google Scholar 

  17. Lee, J. U. et al. Ising-type magnetic ordering in atomically thin FePS3. Nano Lett. 16, 7433–7438 (2016).

    Article  Google Scholar 

  18. Xing, W. et al. Electric field effect in multilayer Cr2Ge2Te6: a ferromagnetic two-dimensional material. 2D Mater. 4, 24009 (2017).

    Article  Google Scholar 

  19. McGuire, M. A., Dixit, H., Cooper, V. R. & Sales, B. C. Coupling of crystal structure and magnetism in the layered, ferromagnetic insulator CrI3. Chem. Mater. 27, 612–620 (2015).

    Article  Google Scholar 

  20. Song, T. et al. Giant tunneling magnetoresistance in spin-filter van der Waals heterostructures. Preprint at (2018).

  21. Klein, D. R. et al. Probing magnetism in 2D van der Waals crystalline insulators via electron tunneling. Preprint at (2018).

  22. Wang, L. et al. One-dimensional electrical contact to a two-dimensional material. Science 342, 614–617 (2013).

    Article  Google Scholar 

  23. Sato, K. Measurement of magneto-optical Kerr effect using piezo-birefringent modulator. Jpn J. Appl. Phys. 20, 2403–2409 (1981).

    Article  Google Scholar 

  24. Zhang, Y. et al. Direct observation of a widely tunable bandgap in bilayer graphene. Nature 459, 820–823 (2009).

    Article  Google Scholar 

  25. Taychatanapat, T., Watanabe, K., Taniguchi, T. & Jarillo-Herrero, P. Quantum Hall effect and Landau-level crossing of Dirac fermions in trilayer graphene. Nat. Phys. 7, 621–625 (2011).

    Article  Google Scholar 

  26. Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nat. Nanotech. 5, 722–726 (2010).

    Article  Google Scholar 

  27. Wang, Z. et al. Very large tunneling magnetoresistance in layered magnetic semiconductor CrI3. Preprint at (2018).

  28. Weisheit, M. et al. Electric field-induced modification of magnetism in thin-film ferromagnets. Science 315, 349–351 (2007).

    Article  Google Scholar 

  29. Duan, C. G. et al. Surface magnetoelectric effect in ferromagnetic metal films. Phys. Rev. Lett. 101, 137201 (2008).

    Article  Google Scholar 

  30. Nakamura, K. et al. Giant modification of the magnetocrystalline anisotropy in transition-metal monolayers by an external electric field. Phys. Rev. Lett. 102, 187201 (2009).

    Article  Google Scholar 

  31. Schmehl, A. et al. Epitaxial integration of the highly spin-polarized ferromagnetic semiconductor EuO with silicon and GaN. Nat. Mater. 6, 882–887 (2007).

    Article  Google Scholar 

  32. Mairoser, T. et al. Is there an intrinsic limit to the charge-carrier-induced increase of the Curie temperature of EuO? Phys. Rev. Lett. 105, 257206 (2010).

    Article  Google Scholar 

  33. Sivadas, N., Okamoto, S. & Xiao, D. Gate-controllable magneto-optic Kerr effect in layered collinear antiferromagnets. Phys. Rev. Lett. 117, 267203 (2016).

    Article  Google Scholar 

  34. Gong, Z. et al. Magnetoelectric effects and valley-controlled spin quantum gates in transition metal dichalcogenide bilayers. Nat. Commun. 4, 2053 (2013).

    Article  Google Scholar 

  35. Jones, A. M. et al. Spin-layer locking effects in optical orientation of exciton spin in bilayer WSe2. Nat. Phys. 10, 130–134 (2014).

    Article  Google Scholar 

Download references


Work at the University of Washington was mainly supported by the Department of Energy, Basic Energy Sciences (DOE BES), Materials Sciences and Engineering Division (DE-SC0012509) and a University of Washington Innovation Award. Work at MIT was supported by the Center for Integrated Quantum Materials under National Science Foundation (NSF) grant DMR-1231319 as well as the Gordon and Betty Moore Foundation’s EPiQS Initiative through grant GBMF4541 to P.J.-H. D.R.K. was funded in part by a QuantEmX grant from ICAM and the Gordon and Betty Moore Foundation through grant GBMF5305 and from the NSF Graduate Research Fellowship Program (GRFP) under grant 1122374. Device fabrication has been partly supported by the Center for Excitonics, an Energy Frontier Research Center funded by the DOE BES under award DE-SC0001088. D.H.C.’s contribution was supported by DE-SC0002197. Work at CMU was also supported by DOE BES DE-SC0012509. W.Y. was supported by the Croucher Foundation (Croucher Innovation Award) and the HKU ORA. Work at ORNL (M.A.M.) was supported by the DOE BES Materials Sciences and Engineering Division. D.X. acknowledges the support of a Cottrell Scholar Award. X.X. acknowledges the support from the State of Washington funded Clean Energy Institute and from the Boeing Distinguished Professorship in Physics.

Author information

Authors and Affiliations



X.X. and P.J.-H. supervised the project. E.N.-M. and M.A.M. synthesized and characterized the bulk CrI3 crystals. D.R.K. fabricated the devices, assisted by D.M., G.C. and B.H. G.C. built the set-up with help from B.H. and N.W. B.H. and G.C. performed the MOKE measurements, assisted by K.L.S. and D.R.K. W.Y. and D.X. provided the theoretical support. All authors contributed to writing the paper and discussed the results.

Corresponding authors

Correspondence to Pablo Jarillo-Herrero or Xiaodong Xu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figures 1–5

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Huang, B., Clark, G., Klein, D.R. et al. Electrical control of 2D magnetism in bilayer CrI3. Nature Nanotech 13, 544–548 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing