Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Tough and stretchable ionogels by in situ phase separation


Ionogels are compelling materials for technological devices due to their excellent ionic conductivity, thermal and electrochemical stability, and non-volatility. However, most existing ionogels suffer from low strength and toughness. Here, we report a simple one-step method to achieve ultra-tough and stretchable ionogels by randomly copolymerizing two common monomers with distinct solubility of the corresponding polymers in an ionic liquid. Copolymerization of acrylamide and acrylic acid in 1-ethyl-3-methylimidazolium ethyl sulfate results in a macroscopically homogeneous covalent network with in situ phase separation: a polymer-rich phase with hydrogen bonds that dissipate energy and toughen the ionogel; and an elastic solvent-rich phase that enables for large strain. These ionogels have high fracture strength (12.6 MPa), fracture energy (~24 kJ m−2) and Young’s modulus (46.5 MPa), while being highly stretchable (~600% strain) and having self-healing and shape-memory properties. This concept can be applied to other monomers and ionic liquids, offering a promising way to tune ionogel microstructure and properties in situ during one-step polymerization.

This is a preview of subscription content

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Schematics of three types of ionogels.
Fig. 2: Photographs, mechanical demonstration and SEM images of various ionogels.
Fig. 3: Mechanical characterization of various gels.
Fig. 4: Self-recovery, self-healing and shape-memory properties of P(AAm0.8125-co-AA0.1875) ionogel.

Data availability

Data generated or analysed during this study are provided as Source Data or included in the Supplementary Information. Further data are available from the corresponding authors on request. Further details on the methods are available in the Supplementary Information.


  1. Lodge, T. P. & Ueki, T. Mechanically tunable, readily processable ion gels by self-assembly of block copolymers in ionic liquids. Acc. Chem. Res. 49, 2107–2114 (2016).

    CAS  Google Scholar 

  2. Ding, Y. et al. Preparation of high‐performance ionogels with excellent transparency, good mechanical strength, and high conductivity. Adv. Mater. 29, 1704253 (2017).

    Google Scholar 

  3. Zhou, B. et al. Flexible, self-healing, and fire-resistant polymer electrolytes fabricated via photopolymerization for all-solid-state lithium metal batteries. ACS Macro Lett. 9, 525–532 (2020).

    CAS  Google Scholar 

  4. Shi, L. et al. Highly stretchable and transparent ionic conductor with novel hydrophobicity and extreme-temperature tolerance. Research 2020, 2505619 (2020).

    CAS  Google Scholar 

  5. Tamate, R. et al. Self‐healing micellar ion gels based on multiple hydrogen bonding. Adv. Mater. 30, 1802792 (2018).

    Google Scholar 

  6. Kim, Y. M. & Moon, H. C. Ionoskins: nonvolatile, highly transparent, ultrastretchable ionic sensory platforms for wearable electronics. Adv. Funct. Mater. 30, 1907290 (2020).

    CAS  Google Scholar 

  7. Ren, Y. et al. Ionic liquid–based click-ionogels. Sci. Adv. 5, eaax0648 (2019).

    CAS  Google Scholar 

  8. Lu, B. et al. Pure PEDOT: PSS hydrogels. Nat. Commun. 10, 1043 (2019).

    Google Scholar 

  9. Xu, J. et al. Multi-scale ordering in highly stretchable polymer semiconducting films. Nat. Mater. 18, 594–601 (2019).

    CAS  Google Scholar 

  10. Liu, Y. et al. Soft and elastic hydrogel-based microelectronics for localized low-voltage neuromodulation. Nat. Biomed. Eng. 3, 58–68 (2019).

    CAS  Google Scholar 

  11. Ma, Y. et al. Flexible hybrid electronics for digital healthcare. Adv. Mater. 32, 1902062 (2020).

    CAS  Google Scholar 

  12. Kim, H. J., Chen, B., Suo, Z. & Hayward, R. C. Ionoelastomer junctions between polymer networks of fixed anions and cations. Science 367, 773–776 (2020).

    CAS  Google Scholar 

  13. Osada, I., de Vries, H., Scrosati, B. & Passerini, S. Ionic‐liquid‐based polymer electrolytes for battery applications. Angew. Chem. Int. Ed. Engl. 55, 500–513 (2016).

    CAS  Google Scholar 

  14. Chen, N., Zhang, H., Li, L., Chen, R. & Guo, S. Ionogel electrolytes for high‐performance lithium batteries: a review. Adv. Energy Mater. 8, 1702675 (2018).

    Google Scholar 

  15. Chen, N. et al. Biomimetic ant-nest ionogel electrolyte boosts the performance of dendrite-free lithium batteries. Energy Environ. Sci. 10, 1660–1667 (2017).

    CAS  Google Scholar 

  16. Hyun, W. J., Thomas, C. M. & Hersam, M. C. Nanocomposite ionogel electrolytes for solid‐state rechargeable batteries. Adv. Energy Mater. 10, 2002135 (2020).

    CAS  Google Scholar 

  17. Shi, L. et al. Dielectric gels with ultra-high dielectric constant, low elastic modulus, and excellent transparency. NPG Asia Mater. 10, 821–826 (2018).

    CAS  Google Scholar 

  18. Liu, Y., He, K., Chen, G., Leow, W. R. & Chen, X. Nature-inspired structural materials for flexible electronic devices. Chem. Rev. 117, 12893–12941 (2017).

    CAS  Google Scholar 

  19. Shi, L. et al. Highly stretchable and transparent ionic conducting elastomers. Nat. Commun. 9, 2630 (2018).

    Google Scholar 

  20. Lei, Z. & Wu, P. A highly transparent and ultra-stretchable conductor with stable conductivity during large deformation. Nat. Commun. 10, 3429 (2019).

    Google Scholar 

  21. Cao, Z., Liu, H. & Jiang, L. Transparent, mechanically robust, and ultrastable ionogels enabled by hydrogen bonding between elastomers and ionic liquids. Mater. Horiz. 7, 912–918 (2020).

    CAS  Google Scholar 

  22. Zhang, L. M. et al. Self‐healing, adhesive, and highly stretchable ionogel as a strain sensor for extremely large deformation. Small 15, 1804651 (2019).

    Google Scholar 

  23. Li, T., Wang, Y., Li, S., Liu, X. & Sun, J. Mechanically robust, elastic, and healable ionogels for highly sensitive ultra‐durable ionic skins. Adv. Mater. 32, 2002706 (2020).

    Google Scholar 

  24. Correia, D. M. et al. Ionic liquid–polymer composites: a new platform for multifunctional applications. Adv. Funct. Mater. 30, 1909736 (2020).

    CAS  Google Scholar 

  25. Le Bideau, J., Viau, L. & Vioux, A. Ionogels, ionic liquid based hybrid materials. Chem. Soc. Rev. 40, 907–925 (2011).

    Google Scholar 

  26. Yu, L. et al. Highly tough, Li‐metal compatible organic–inorganic double‐network solvate ionogel. Adv. Energy Mater. 9, 1900257 (2019).

    Google Scholar 

  27. Zhao, X. Multi-scale multi-mechanism design of tough hydrogels: building dissipation into stretchy networks. Soft Matter 10, 672–687 (2014).

    CAS  Google Scholar 

  28. Gong, J. P., Katsuyama, Y., Kurokawa, T. & Osada, Y. Double‐network hydrogels with extremely high mechanical strength. Adv. Mater. 15, 1155–1158 (2003).

    CAS  Google Scholar 

  29. Sun, J.-Y. et al. Highly stretchable and tough hydrogels. Nature 489, 133–136 (2012).

    CAS  Google Scholar 

  30. Zhang, H. J. et al. Tough physical double‐network hydrogels based on amphiphilic triblock copolymers. Adv. Mater. 28, 4884–4890 (2016).

    CAS  Google Scholar 

  31. Sato, K. et al. Phase‐separation‐induced anomalous stiffening, toughening, and self‐healing of polyacrylamide gels. Adv. Mater. 27, 6990–6998 (2015).

    CAS  Google Scholar 

  32. Gong, J. P. Why are double network hydrogels so tough? Soft Matter 6, 2583–2590 (2010).

    CAS  Google Scholar 

  33. Corkhill, P., Trevett, A. & Tighe, B. The potential of hydrogels as synthetic articular cartilage. Proc. Inst. Mech. Eng. H 204, 147–155 (1990).

    CAS  Google Scholar 

  34. Zhang, H. et al. Polyelectrolyte microcapsules as ionic liquid reservoirs within ionomer membrane to confer high anhydrous proton conductivity. J. Power Sources 279, 667–677 (2015).

    CAS  Google Scholar 

  35. Ueki, T. & Watanabe, M. Polymers in ionic liquids: dawn of neoteric solvents and innovative materials. Bull. Chem. Soc. Jpn 85, 33–50 (2012).

    CAS  Google Scholar 

  36. Ueki, T., Watanabe, M. & Lodge, T. P. Doubly thermosensitive self-assembly of diblock copolymers in ionic liquids. Macromolecules 42, 1315–1320 (2009).

    CAS  Google Scholar 

  37. Weng, D. et al. Polymeric complex-based transparent and healable ionogels with high mechanical strength and ionic conductivity as reliable strain sensors. ACS Appl. Mater. Interfaces 12, 57477–57485 (2020).

    CAS  Google Scholar 

  38. Sun, T. L. et al. Physical hydrogels composed of polyampholytes demonstrate high toughness and viscoelasticity. Nat. Mater. 12, 932–937 (2013).

    CAS  Google Scholar 

  39. Hu, X., Vatankhah‐Varnoosfaderani, M., Zhou, J., Li, Q. & Sheiko, S. S. Weak hydrogen bonding enables hard, strong, tough, and elastic hydrogels. Adv. Mater. 27, 6899–6905 (2015).

    CAS  Google Scholar 

  40. Kong, W. et al. Muscle‐inspired highly anisotropic, strong, ion‐conductive hydrogels. Adv. Mater. 30, 1801934 (2018).

    Google Scholar 

  41. Mredha, M. T. I. et al. A facile method to fabricate anisotropic hydrogels with perfectly aligned hierarchical fibrous structures. Adv. Mater. 30, 1704937 (2018).

    Google Scholar 

  42. Asaletha, R., Kumaran, M. & Thomas, S. Thermoplastic elastomers from blends of polystyrene and natural rubber: morphology and mechanical properties. Eur. Polym. J. 35, 253–271 (1999).

    CAS  Google Scholar 

  43. Bai, R., Yang, J. & Suo, Z. Fatigue of hydrogels. Eur. J. Mech. A 74, 337–370 (2019).

    Google Scholar 

Download references


M.D. acknowledges support from the Coastal Studies Institute. J.H. acknowledges the support of the National Natural Science Foundation of China (11702207). We thank Prof. L. Cai for helpful discussion. We thank Mr M. Yang and Mr X. Chen for help with 3D printing. Nano-IR analysis was performed by W.Q. at the NanoEngineering Research Core Facility (NERCF), which is partially funded by the Nebraska Research Initiative.

Author information

Authors and Affiliations



M.W., J.H. and M.D.D. conceived the idea. J.H. and M.D.D. supervised the project. M.W. carried out most of the experiments. P.Z. participated in the fracture energy measurements. M.S. and V.K.T. participated in the SEM measurements. M.S. participated in the SAXS measurements. J.L.T. contributed to the SAXS data processing and analysis. W.Q. conducted the nano-IR measurements. J.M. contributed to the demonstration of the falling metal ball. M.W., J.H., and M.D.D. wrote the paper, and all authors reviewed the manuscript.

Corresponding authors

Correspondence to Jian Hu or Michael D. Dickey.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature Materials thanks Xuanhe Zhao and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–17, Notes 1–4, Tables 1 and 2, Videos 1–5 and refs. 1–7.

Supplementary Video 1

This movie shows that the P(AAm0.8125-co-AA0.1875) ionogel is strong enough to lift a 1 kg weight, while the pure PAA and PAAm ionogel and P(AAm0.8125-co-AA0.1875) hydrogel break. Cm = 6 M, CMBAA = 0.1 mol%.

Supplementary Video 2

This movie demonstrates the ultra-tough properties of the gel when a metal ball drops on a membrane of P(AAm0.8125-co-AA0.1875) ionogel stretched across a rigid frame. The membrane (thickness = 0.5 mm) was glued to two polyacrylate clamps with a circular opening (diameter = 7 cm). A stainless steel ball with a diameter of 2.54 cm and mass of 64 g was dropped from a height of 2 m. Upon hitting the membrane, the ball bounced back and the membrane remained intact with small deformation, while the P(AAm0.8125-co-AA0.1875) hydrogel was stretched to rupture after large deformation. Cm = 6 M, CMBAA = 0.1 mol%.

Supplementary Video 3

This movie shows the excellent self-healing property of the P(AAm0.8125-co-AA0.1875) ionogel. The dog-bone samples were cut into half pieces and then the pieces from two different samples were put together to heal. After storing the sample at 80 °C for 1 h, the self-healed sample could lift the 1 kg weight. The copolymer ionogel samples were stained with methylene blue and rhodamine B. Cm = 6 M, CMBAA = 0.1 mol%.

Supplementary Video 4

This movie shows the excellent shape-memory properties of P(AAm0.8125-co-AA0.1875) ionogel by demonstrating the fast programming and recovery process. The ionogel sample was stained with rhodamine B for visualization. Cm = 6 M, CMBAA = 0.1 mol%.

Supplementary Video 5

This movie exhibits superb shape-memory behaviour of P(AAm0.8125-co-AA0.1875) ionogel using a more complicated six-layer structure of a ‘blooming flower’. Six layers of the copolymer ionogel samples were glued together to mimic the flower bud blooming process and the ionogels could fully recover within 25 s. The ionogel samples were stained with methylene blue. Cm = 6 M, CMBAA = 0.1 mol%.

Source data

Source Data Fig. 3

Source data.

Source Data Fig. 4

Source data.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wang, M., Zhang, P., Shamsi, M. et al. Tough and stretchable ionogels by in situ phase separation. Nat. Mater. 21, 359–365 (2022).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing