Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Large-scale fabrication of structurally coloured cellulose nanocrystal films and effect pigments


Cellulose nanocrystals are renewable plant-based colloidal particles capable of forming photonic films by solvent-evaporation-driven self-assembly. So far, the cellulose nanocrystal self-assembly process has been studied only at a small scale, neglecting the limitations and challenges posed by the continuous deposition processes that are required to exploit this sustainable material in an industrial context. Here, we addressed these limitations by using roll-to-roll deposition to produce large-area photonic films, which required optimization of the formulation of the cellulose nanocrystal suspension and the deposition and drying conditions. Furthermore, we showed how metre-long structurally coloured films can be processed into effect pigments and glitters that are dispersible, even in water-based formulations. These promising effect pigments are an industrially relevant cellulose-based alternative to current products that are either micro-polluting (for example, non-biodegradable microplastic glitters) or based on carcinogenic, unsustainable or unethically sourced compounds (for example, titania or mica).

Your institute does not have access to this article

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Overview of the R2R processing of a CNC suspension into photonic films and microparticles.
Fig. 2: Film thickness and optical properties versus coating parameters.
Fig. 3: Effect of sonication and drying conditions on the visual appearance of blade-cast CNC films.
Fig. 4: Optical properties of CNC films cast by R2R and dried either statically or with stepwise continuous translation through an in-line hot air dryer.
Fig. 5: Photonic CNC microparticles.

Data availability

Additional data relating to this publication are available from the University of Cambridge data repository (


  1. Green, D. S., Jefferson, M., Boots, B. & Stone, L. All that glitters is litter? Ecological impacts of conventional versus biodegradable glitter in a freshwater habitat. J. Hazard. Mater. 402, 124070 (2021).

    CAS  Google Scholar 

  2. Pfaff, G. & Reynders, P. Angle-dependent optical effects deriving from submicron structures of films and pigments. Chem. Rev. 99, 1963–1981 (1999).

    CAS  Google Scholar 

  3. European Commission. Environmental and Health Risks of Microplastic Pollution (European Union Publications, 2019).

  4. ten Kate, A., Schipper, I., Kiezebrink, V. & Remmers, M. Beauty and a Beast: Child Labour in India for Sparkling Cars and Cosmetics (Centre for Research on Multinational Corporations, 2016).

  5. Proposal for Harmonised Classification and Labelling: Titanium Dioxide CLH Report (French Agency for Food, Environmental and Occupational Health & Safety, 2008).

  6. Younes, M. et al. Safety assessment of titanium dioxide (E171) as a food additive. Eur. Food Saf. Auth. J. 19, e06585 (2021).

    CAS  Google Scholar 

  7. Frka-Petesic, B. & Vignolini, S. So much more than paper. Nat. Photon. 13, 365–367 (2019).

    CAS  Google Scholar 

  8. Klockars, K. W. et al. Asymmetrical coffee rings from cellulose nanocrystals and prospects in art and design. Cellulose 26, 491–506 (2019).

    CAS  Google Scholar 

  9. Lagerwall, J. P. F. et al. Cellulose nanocrystal-based materials: from liquid crystal self-assembly and glass formation to multifunctional thin films. NPG Asia Mater. 6, e80 (2014).

    CAS  Google Scholar 

  10. Zhang, Y. P., Chodavarapu, V. P., Kirk, A. G. & Andrews, M. P. Nanocrystalline cellulose for covert optical encryption. J. Nanophoton. 6, 063516 (2012).

    Google Scholar 

  11. Zhao, T. H. et al. Printing of responsive photonic cellulose nanocrystal microfilm arrays. Adv. Funct. Mater. 29, 1804531 (2019).

    Google Scholar 

  12. Giese, M., Blusch, L. K., Khan, M. K., Hamad, W. Y. & Maclachlan, M. J. Responsive mesoporous photonic cellulose films by supramolecular cotemplating. Angew. Chem. Int. Ed. 53, 8880–8884 (2014).

    CAS  Google Scholar 

  13. Reid, M. S., Villalobos, M. & Cranston, E. D. Benchmarking cellulose nanocrystals: from the laboratory to industrial production. Langmuir 33, 1583–1598 (2017).

    CAS  Google Scholar 

  14. Reiner, R. S. & Rudie, A. W. in Production and Applications of Cellulose Nanomaterials (eds Postek, M. T. et al.) 21–24 (TAPPI Press, 2013).

  15. Vanderfleet, O. M. & Cranston, E. D. Production routes to tailor the performance of cellulose nanocrystals. Nat. Rev. Mater. 6, 124–144 (2021).

    CAS  Google Scholar 

  16. Chowdhury, R. A., Clarkson, C. & Youngblood, J. Continuous roll-to-roll fabrication of transparent cellulose nanocrystal (CNC) coatings with controlled anisotropy. Cellulose 25, 1769–1781 (2018).

    CAS  Google Scholar 

  17. Koppolu, R. et al. Continuous roll-to-roll coating of cellulose nanocrystals onto paperboard. Cellulose 25, 6055–6069 (2018).

    CAS  Google Scholar 

  18. Parker, R. M. et al. Hierarchical self-assembly of cellulose nanocrystals in a confined geometry. ACS Nano 10, 8443–8449 (2016).

    CAS  Google Scholar 

  19. Gray, D. G. Recent advances in chiral nematic structure and iridescent color of cellulose nanocrystal films. Nanomaterials 6, 213 (2016).

    Google Scholar 

  20. Revol, J.-F., Godbout, L. & Gray, D. G. Solid self-assembled films of cellulose with chiral nematic order and optically variable properties. J. Pulp Pap. Sci. 24, 146–149 (1998).

    CAS  Google Scholar 

  21. Gicquel, E., Bras, J., Rey, C. & Jean, B. Impact of sonication on the rheological and colloidal properties of highly concentrated cellulose nanocrystal suspensions. Cellulose 7, 7619–7634 (2019).

    Google Scholar 

  22. Shafiei-Sabet, S., Hamad, W. Y. & Hatzikiriakos, S. G. Rheology of nanocrystalline cellulose aqueous suspensions. Langmuir 28, 17124–17133 (2012).

    CAS  Google Scholar 

  23. Haywood, A. D. & Davis, V. A. Effects of liquid crystalline and shear alignment on the optical properties of cellulose nanocrystal films. Cellulose 24, 705–716 (2017).

    CAS  Google Scholar 

  24. Diaz, J. A., Wu, X., Martini, A., Youngblood, J. P. & Moon, R. J. Thermal expansion of self-organized and shear-oriented cellulose nanocrystal films. Biomacromolecules 14, 2900–2908 (2013).

    CAS  Google Scholar 

  25. Parker, R. M. et al. The self-assembly of cellulose nanocrystals: hierarchical design of visual appearance. Adv. Mater. 30, 1704477 (2018).

    Google Scholar 

  26. Zhu, B. et al. Hyperspectral imaging of photonic cellulose and implications for self-assembly pathways. ACS Nano 14, 15361–15373 (2020).

    CAS  Google Scholar 

  27. Berreman, D. W. Optics in stratified and anisotropic media: 4×4-matrix formulation. J. Opt. Soc. Am. 62, 502–510 (1972).

    CAS  Google Scholar 

  28. de Vries, H. Rotatory power and other optical properties of certain liquid crystals. Acta Crystallogr. 4, 219–226 (1951).

    Google Scholar 

  29. Beck, S., Bouchard, J. & Berry, R. Controlling the reflection wavelength of iridescent solid films of nanocrystalline cellulose. Biomacromolecules 12, 167–172 (2011).

    CAS  Google Scholar 

  30. Dong, X. M., Revol, J.-F. & Gray, D. G. Effect of microcrystallite preparation conditions on the formation of colloid crystals of cellulose. Cellulose 5, 19–32 (1998).

    CAS  Google Scholar 

  31. Foster, E. J. et al. Current characterization methods for cellulose nanomaterials. Chem. Soc. Rev. 47, 2609–2679 (2018).

    CAS  Google Scholar 

  32. Walters, C. M., Boott, C. E., Nguyen, T. D., Hamad, W. Y. & Maclachlan, M. J. Iridescent cellulose nanocrystal films modified with hydroxypropyl cellulose. Biomacromolecules 21, 1295–1302 (2020).

    CAS  Google Scholar 

  33. Bardet, R., Roussel, F., Coindeau, S., Belgacem, N. & Bras, J. Engineered pigments based on iridescent cellulose nanocrystal films. Carbohydr. Polym. 122, 367–375 (2015).

    CAS  Google Scholar 

  34. Wang, P. X., Hamad, W. Y. & MacLachlan, M. J. Structure and transformation of tactoids in cellulose nanocrystal suspensions. Nat. Commun. 7, 11515 (2016).

    Google Scholar 

  35. Beck, S. & Bouchard, J. Auto-catalyzed acidic desulfation of cellulose nanocrystals. Nord. Pulp Pap. Res. J. 29, 6–14 (2014).

    CAS  Google Scholar 

  36. Lin, N. & Dufresne, A. Surface chemistry, morphological analysis and properties of cellulose nanocrystals with gradiented sulfation degrees. Nanoscale 6, 5384–5393 (2014).

    CAS  Google Scholar 

  37. Dong, X. M. & Gray, D. G. Effect of counterions on ordered phase formation in suspensions of charged rodlike cellulose crystallites. Langmuir 13, 2404–2409 (1997).

    CAS  Google Scholar 

  38. Chauve, G., Mauran, D., Fraschini, C. & Bouchard, J. Critical discussion on the thermal behavior of sulfated cellulose nanocrystals. TAPPI J. 15, 383–391 (2016).

    CAS  Google Scholar 

  39. D’Acierno, F., Hamad, W. Y., Michal, C. A. & Maclachlan, M. J. Thermal degradation of cellulose filaments and nanocrystals. Biomacromolecules 21, 3374–3386 (2020).

    Google Scholar 

  40. D’Acierno, F., Ohashi, R., Hamad, W. Y., Michal, C. A. & MacLachlan, M. J. Thermal annealing of iridescent cellulose nanocrystal films. Carbohydr. Polym. 272, 118468 (2021).

    Google Scholar 

  41. Gençer, A., Van Rie, J., Lombardo, S., Kang, K. & Thielemans, W. Effect of gelation on the colloidal deposition of cellulose nanocrystal films. Biomacromolecules 19, 3233–3243 (2018).

    Google Scholar 

  42. Mu, X. & Gray, D. G. Droplets of cellulose nanocrystal suspensions on drying give iridescent 3-D “coffee-stain” rings. Cellulose 22, 1103–1107 (2015).

    CAS  Google Scholar 

  43. Dufresne, A. Nanocellulose: from Nature to High Performance Tailored Materials (De Gruyter, 2012).

  44. Frka-Petesic, B., Kamita, G., Guidetti, G. & Vignolini, S. Angular optical response of cellulose nanocrystal films explained by the distortion of the arrested suspension upon drying. Phys. Rev. Mater. 3, 045601 (2019).

    CAS  Google Scholar 

  45. Klockars, K. W. et al. Effect of anisotropy of cellulose nanocrystal suspensions on stratification, domain structure formation and structural colors. Biomacromolecules 19, 2931–2943 (2018).

    CAS  Google Scholar 

  46. Honorato-Rios, C. et al. Fractionation of cellulose nanocrystals: enhancing liquid crystal ordering without promoting gelation. NPG Asia Mater. 10, 455–465 (2018).

    CAS  Google Scholar 

  47. Tardy, B. L. et al. Tessellation of chiral-nematic cellulose nanocrystal films by microtemplating. Adv. Funct. Mater. 29, 1808518 (2019).

    Google Scholar 

  48. Kamita, G. et al. Biocompatible and sustainable optical strain sensors for large-area applications. Adv. Opt. Mater. 4, 1950–1954 (2016).

    CAS  Google Scholar 

Download references


This work was supported by the Engineering and Physical Sciences Research Council (EP/R511675/1 for S.V.; EP/N016920/1 for H.-L.L, J.J.B., M.D.V. and S.V.), by the European Union’s Horizon 2020 Marie Skłodowska-Curie research and innovation programme (H2020-MSCA-ITN-2016 722842 for B.E.D and S.V.) and the European Research Council (ERC-2014-STG H2020 639088 for B.F.-P., R.M.P. and S.V.; ERC-2017-POC 790518 for S.V.). We thank F. Firth for performing the thermogravimetric analysis characterization.

Author information

Authors and Affiliations



The concept of R2R-manufactured photonics was conceived by J.J.B., M.D.V. and S.V.; CNC suspensions, films and particles were prepared and characterized by B.E.D.; R2R experiments were realized by B.E.D. and H.-L.L.; B.F.-P and R.M.P. provided critical feedback on results. The manuscript was written by B.E.D., R.M.P., B.F.-P. and S.V. with input from all authors.

Corresponding author

Correspondence to Silvia Vignolini.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Materials thanks Jay Guo and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–24 and Tables 1 and 2.

Supplementary Video 1

This time-lapse video shows a CNC film drying on a thin R2R web (75 µm), where the stress-induced web warping is clearly visible.

Supplementary Video 2

This time-lapse video shows a CNC film drying on a thick R2R web (500 + 75 µm), where no stress-induced web warping occurs.

Supplementary Video 3

This video shows the drying of a R2R-coated CNC suspension into a structurally coloured film, with the help of a hot air dryer placed in-line and blowing hot air at ~60 °C. The continuous deposition is performed stepwise, with the web being moved every 15 min by ~20 cm at a speed of vc = 0.1 m min–1.

Supplementary Video 4

This time-lapse video shows the in-line peeling of a thick CNC film.

Supplementary Video 5

This video shows a CNC particle initially observed in air being placed in a 1:1 mixture of ethanol and water. The redshift is progressive as ethanol preferentially evaporates and moisture condensation occurs. When no solvent is left, the particle dries and returns to its original colour in air. The video was accelerated six times compared to the original.

Supplementary Video 6

This video shows the samples of Fig. 1j in motion after turning the vials upside-down.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Droguet, B.E., Liang, HL., Frka-Petesic, B. et al. Large-scale fabrication of structurally coloured cellulose nanocrystal films and effect pigments. Nat. Mater. 21, 352–358 (2022).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing