Biodegradable and biocompatible elastic materials for soft robotics, tissue engineering or stretchable electronics with good mechanical properties, tunability, modifiability or healing properties drive technological advance, and yet they are not durable under ambient conditions and do not combine all the attributes in a single platform. We have developed a versatile gelatin-based biogel, which is highly resilient with outstanding elastic characteristics, yet degrades fully when disposed. It self-adheres, is rapidly healable and derived entirely from natural and food-safe constituents. We merge all the favourable attributes in one material that is easy to reproduce and scalable, and has a low-cost production under ambient conditions. This biogel is a step towards durable, life-like soft robotic and electronic systems that are sustainable and closely mimic their natural antetypes.
This is a preview of subscription content, access via your institution
Open Access articles citing this article.
npj Flexible Electronics Open Access 23 October 2023
Scientific Reports Open Access 31 May 2023
Nature Communications Open Access 20 April 2023
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Rent or buy this article
Prices vary by article type
Prices may be subject to local taxes which are calculated during checkout
Hoornweg, D., Bhada-Tata, P. & Kennedy, C. Environment: waste production must peak this century. Nature 502, 615–617 (2013).
Leung, A., Luksemburg, W., Wong, A. & Wong, M. Spatial distribution of polybrominated diphenyl ethers and polychlorinated dibenzo-p-dioxins and dibenzofurans in soil and combusted residue at Guiyu, an electronic waste recycling site in southeast China. Environ. Sci. Technol. 41, 2730–2737 (2007).
Baumgartner, M. et al. in Green Materials for Electronics (eds Irimia‐Vladu, M., Glowacki, E. D., Sariciftci, N. S. & Bauer, S.) 1–53 (Wiley, 2017)
Irimia-Vladu, M. et al. Biocompatible and biodegradable materials for organic field-effect transistors. Adv. Funct. Mater. 20, 4069–4076 (2010).
Boutry, C. et al. A stretchable and biodegradable strain and pressure sensor for orthopaedic application. Nat. Electron. 1, 314–321 (2018).
Walker, S. et al. Using an environmentally benign and degradable elastomer in soft robotics. Int. J. Intell. Robotics Appl. 1, 124–142 (2017).
Hwang, S. et al. A physically transient form of silicon electronics. Science 337, 1640–1644 (2012).
Yang, C. & Suo, Z. Hydrogel ionotronics. Nat. Rev. Mater. 3, 125–142 (2018).
Acome, E. et al. Hydraulically amplified self-healing electrostatic actuators with muscle-like performance. Science 359, 61–65 (2018).
Someya, T. & Amagai, M. Toward a new generation of smart skins. Nat. Biotechnol. 37, 382–388 (2019).
Li, C. H. et al. A highly stretchable autonomous self-healing elastomer. Nat. Chem. 6, 618–624 (2016).
Cao, Y. et al. Self-healing electronic skins for aquatic environments. Nat. Electron. 2, 75–82 (2019).
Wang, S. et al. Skin electronics from scalable fabrication of an intrinsically stretchable transistor array. Nature 555, 83–88 (2018).
Wirthl, D. et al. Instant tough bonding of hydrogels for soft machines and electronics. Sci. Adv. 3, e1700053 (2017).
Wang, X. et al. Food-materials-based edible supercapacitors. Adv. Mater. Technol. 1, 1600059 (2016).
Bauer, S. & Kaltenbrunner, M. Built to disappear. ACS Nano 8, 5380–5382 (2014).
Yang, J., Webb, A. R. & Ameer, G. A. Novel citric acid-based biodegradable elastomers for tissue engineering. Adv. Mater. 16, 511–516 (2004).
Webb, A. R., Yang, J. & Ameer, G. A. Biodegradable polyester elastomers in tissue engineering. Expert Opin. Biol. Ther. 4, 801–812 (2004).
Wang, Y., Ameer, G. A., Sheppard, B. J. & Langer, R. A tough biodegradable elastomer. Nat. Biotechnol. 20, 602–606 (2002).
Cohn, D. & Salomon, A. H. Designing biodegradable multiblock PCL/PLA thermoplastic elastomers. Biomaterials 26, 2297–2305 (2005).
Skarja, G. A. & Woodhouse, K. A. In vitro degradation and erosion of degradable, segmented polyurethanes containing an amino acid-based chain extender. J. Biomater. Sci. Polym. Ed. 12, 851–873 (2001).
Averous, L., Moro, L., Dole, P. & Fringant, C. Properties of thermoplastic blends: starch–polycaprolactone. Polymer 41, 4157–4167 (2000).
Zhu, C. et al. Highly stretchable HA/SA hydrogels for tissue engineering. J. Biomater. Sci. Polym. Ed. 29, 543–561 (2018).
Shintake, J., Sonar, H., Piskarev, E., Paik, J. & Floreano, D. Soft pneumatic gelatin actuator for edible robotics. In 2017 IEEE/RSJ International Conference on Intelligent Robots and Systems (IROS) 6221–6226 (IEEE, 2017).
Van Den Bulcke, A. I. et al. Structural and rheological properties of methacrylamide modified gelatin hydrogels. Biomacromolecules 1, 31–38 (2000).
Wu, T. et al. A pH-responsive biodegradable high-strength hydrogel as potential gastric resident filler. Macromol. Mater. Eng. 303, 1800290 (2018).
Ceseracciu, L., Heredia-Guerrero, J. A., Dante, S., Athanassiou, A. & Bayer, I. S. Robust and biodegradable elastomers based on corn starch and polydimethylsiloxane (PDMS). ACS Appl. Mater. Interfaces 7, 3742–3753 (2015).
He, Q., Huang, Y. & Wang, S. Hofmeister effect-assisted one step fabrication of ductile and strong gelatin hydrogels. Adv. Funct. Mater. 28, 1705069 (2018).
Qin, Z. et al. Freezing-tolerant supramolecular organohydrogel with high toughness, thermoplasticity, and healable and adhesive properties. ACS Appl. Mater. Interfaces 11, 21184–21193 (2019).
Schrieber, R. & Gareis, H. Gelatine Handbook (Wiley, 2007).
Luo, Z. et al. Biodegradable gelatin methacryloyl microneedles for transdermal drug delivery. Adv. Healthcare Mater. 8, 1801054 (2018).
Echave, M. et al. Enzymatic crosslinked gelatin 3D scaffolds for bone tissue engineering. Int. J. Pharm. 562, 151–161 (2019).
Mandrycky, C. et al. 3D bioprinting for engineering complex tissues. Biotechnol. Adv. 34, 422–434 (2016).
Kim, D., Lee, H., Kwon, S., Choi, H. & Park, S. Magnetic nano-particles retrievable biodegradable hydrogel microrobot. Sens. Actuators B 289, 65–77 (2019).
Chambers, L., Winfield, J., Ieropoulos, I. & Rossiter, J. Biodegradable and edible gelatine actuators for use as artificial muscles. In Proc. SPIE 9056, Electroactive Polymer Actuators and Devices 90560B (SPIE, 2014).
Sardesai, A. et al. Design and characterization of edible soft robotic candy actuators. MRS Adv. 3, 3003–3009 (2018).
Deng, Y., Zhang, Y., Lemos, B. & Ren, H. Tissue accumulation of microplastics in mice and biomarker responses suggest widespread health risks of exposure. Sci. Rep. 7, 46687 (2017).
Feig, V., Tran, H. & Bao, Z. Biodegradable polymeric materials in degradable electronic devices. ACS Centr. Sci. 4, 337–348 (2018).
Shimizu, S. & Matubayasi, N. Gelation: the role of sugars and polyols on gelatin and agarose. J. Phys. Chem. B 118, 13210–13216 (2014).
Polygerinos, P. et al. Soft robotics: review of fluid‐driven intrinsically soft devices; manufacturing, sensing, control, and applications in human–robot interaction. Adv. Engin. Mater. 19, 1700016 (2017).
Amjadi, M., Kyung, K.-U., Park, I. & Sitti, M. Stretchable, skin-mountable, and wearable strain sensors and their potential applications: a review. Adv. Funct. Mater. 26, 1678–1698 (2016).
Krause, J., Winfield, A. & Deneubourg, J. Interactive robots in experimental biology. Trends Ecol. Evol. 26, 369–375 (2011).
Bogue, R. Fruit picking robots: has their time come?. Ind. Robot 47, 141–145 (2010).
Hohimer, C. J. et al. Design and field evaluation of a robotic apple harvesting system with a 3D-printed soft-robotic end-effector. Trans. ASABE 62, 405–415 (2019).
Hartmann, F., Drack, M. & Kaltenbrunner, M. Meant to merge: fabrication of stretchy electronics for robotics. Sci. Robotics 3, eaat9091 (2018).
Luangtana-anan, M., Nunthanid, J. & Limmatvapirat, S. Effect of molecular weight and concentration of polyethylene glycol on physicochemical properties and stability of shellac film. J. Agric. Food Chem. 58, 12934–12940 (2010).
This work was supported by the European Research Council Starting Grant ‘GEL-SYS’ under grant agreement no. 757931, the Austrian Research Promotion Agency GmbH (FFG) within the COMET-project TextileUX under grant agreement no. 865791 and through start-up funding of the Linz Institute of Technology (LIT) ‘Soft Electronics Laboratory’ under grant no. LIT013144001SEL. M.B. received support from Borealis and the Borealis Social Scholarship, VDI and the Dr Maria Schaumayer Foundation. G.B. acknowledges financial support from the European Commission within the ‘LiNaBioFluid’ project within the scope of H2020-FETOPEN-2014-2015-RIA. We thank Ewald-Gelatine, especially T. Hilt, for material support and fruitful discussions. We dedicate this work to S. Bauer.
The authors declare no competing interests.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
a, A bioinspired soft actuator consisting of wood, cotton-yarn, and gelatin-based biogel. b, Degradation reaction and end product of cellulose. c, Degradation and end product of gelatin. Single polypeptide strands are split by microorganisms found in waste water, gut, or soils.
a, The manually actuated elephant trunk in its relaxed state and b, actuated u-shaped state. c, U-shaped movement allows grabbing of various objects. Scale bar, 2 cm.
Assembly process of the sensor skin consisting of degradable e-skin and reusable PCB. 1, Gels of different mechanical properties are joined by laser assisted rapid healing (LARH). 2–3, A zinc metal sheet is then applied to the gel and structured by a fiber laser. 4, After the structuring process the zinc residues are peeled off. 5, A flexible reusable PCB is mounted on the gel and soldered to the zinc foil of the e-skin. In the last fabrication step a temperature sensitive paste is placed on the gel to finalize the temperature sensor.
a, Stretchable meanders of zinc foil serve as conductors on biogels (G1730). b, Repeated stretching and increase of the maximum strain does not affect the conductivity of the zinc meanders. Mean resistance changes (solid line) during stretch-release cycles (data envelope) are shown. c, Those are durable for over 1000 stretching cycles, when stretched to a maximum strain of 20 %. d, Humidity sensors are realized with structured zinc foil on biogels (G2430). e, The magnitude of the impedance Z is measured as function of frequency at different climatic conditions, showing a change of two orders of magnitude. f, The sensor response is below 1 % when stretched repeatedly to a maximum strain of 10 %. g, Temperature sensors are realized with a conductive paste between two stretchable conductors on a biogel (G3030). h, The conductive pastes, fabricated on glass substrates, show a change larger than a factor of 2 over a range of 30 °C. Error bars, standard deviation for a measurement period >10 min. i, Strain sensors are designed with 5 fingers total to allow displacement of the electrodes. j, The sensor signals follow the applied strain profile linearly. Repeated cycles are tested between 20 % and 40 % strain, to account for irreversible mechanical deformation of the substrate during the first stretch-release cycle. Scale bars, 5 mm.
a, Schematic of the 90° peel-test used to measure the debond energy between a biogel slightly pressed against diverse substrates. A 6 µm thick PET foil serves as stiff backing to prevent elongation of the peel arm, whereas a linear guiding ensures a constant angle of 90°. b, Measured debond energy for aluminum (blue), paper (purple), porcine skin (turquoise), PDMS (orange) and Ecoflex (red). c, Photographs of a biogel-porcine skin peel-sample taken during a peel-test showing the propagation of the peel-front between biogel and substrate. Mean values (solid line) and standard deviation (shadow) for n > 4 samples each. Scale bar, 1 cm.
a, Two gel discs (G1730) with a thickness of 1 mm and 2 mm and a diameter of 2 cm were applied on the skin of the upper arm with little pressure. Scale bar, 2 cm. b, The test started at 9am, c, and showed no signs of gel disintegration during 4 h of wearing. Scale bars, 1 cm. d, Even after sports activities (13 pm to 14 pm) that involved higher mechanical load and sweating, there are no signs of detachment. Scale bar, 1 cm. e, After 7 h the biogel still adheres to the skin, even at the edges of the gel. Scale bar, 1 cm. f, The gel can be removed with no visible irritations after removal. Scale bar, 2 cm. g, Rectangular stripes were applied on the skin for up to 4 days (5–12 h each day) and compared to reference samples of the same batch. Mean values (solid line) and data envelope (gray shadow) for n > 3 samples each are shown. The biogel mechanics do not change upon wearing, even after 38 h wear-time on skin, resulting in constant h, Young’s modulus (ref. A: 170 kPa ± 4 kPa, ref. B: 207 kPa ± 5 kPa), i, ultimate stress (ref. A: 830 kPa ± 60 kPa, ref. B: 1070 kPa ± 26 kPa), j, and ultimate strain (ref. A: 373 % ± 26 %, ref. B: 423 % ± 22 %). Error bars, standard deviation for a n > 3 measurements.
a–d, A weight of 20 g is applied to single pixels of the pressure skin sensor matrix. The measurement shows an impedance increase of 7–15 % compared to the initial value. Scale bar, 2 cm.
Supplementary Discussion, Methods, Tables 1–3, Figs. 1–24 and Video captions 1–13.
Dissolution of biogel. The video shows dissolution of a disk of G1620 biogel in DI-water.
Dissolution of biogel foam. The video shows dissolution of a disk of G1215f biogel foam in DI-water.
Biodegradable encapsulation. The video shows dissolution of a disk of a G2430 biogel in DI-water in comparison to an equal disk with a biodegradable encapsulation. The initial color change of the coating is typical for shellac immersed in water. The biodegradable encapsulation significantly delays biogel dissolution also in acidic solutions (citric acid, pH 2.1). Degradation is triggered by basic solutions (Tris buffer, pH 8.1).
Inflation of biogels. The video shows inflation of three different biogels (G2820, G2420, and G1620). The comparison of the biogels shows that G2820 biogel allows for the largest strains.
Motion of the biogel actuators. The video shows u-shaped and s-shaped motion of the biogel actuators. An actuator tube made from fluorescent biogel is barely visible in relaxed state, but fully visible when actuated due to increased surface area of the biogel.
Biogel actuators operating underwater. Pneumatic actuators are dip-coated in cooking oil and operate in 20 °C DI-water. Actuator reaches 900 actuation cycles after 45 min of operation. Action continues over 1.5 h with more than 1500 actuation cycles before failure.
Lifting of objects with the s-shaped actuator. The video shows an actuator tube with a suction cup on its tip lifting objects. Vacuum is applied when an object is in contact with the suction cup and turned off when the lifting movement is over. Different sizes of objects can be lifted. Even objects that are smaller than the suction cup itself. Small dolls are equally lifted despite different weights ranging from 5.5 g to 30 g. The actuator (actuator weight ~35 g) lifts objects up to 119 g.
Interaction between two soft biodegradable robots. 1, In this video two biodegradable robots perform a manually actuated ball transfer. At the beginning the smaller degradable robot “Percy the Gellyfant” with inflated u-shaped trunk holds a sphere shaped object. The s-shaped actuator of the larger plywood soft robot has a suction cup attached to its front end and is also in its inflated state. 2, While Percy is still holding the table tennis ball the plywood elephant slowly deflates and approaches the round object until the suction cup completely touches it. 3, Vacuum is manually applied to the suction cup while the actuator of Percy is deflated. 4, As the actuator of Percy is deflated the plywood elephant actuator is inflated and lifts the table tennis ball. 5, The plywood elephant is then deflated and approaches the now inflated trunk of Percy. 6, When the biogel-actuator of Percy is bent to a curve, the lowered suction cup of the plywood elephant actuator places the table tennis ball back in Percys trunk. “Percy the Gellyfant” is holding an object. 1, The manually actuated u-shaped trunk is holding a cylindrical rigid object. 2, When the trunk is deflated the object is released 3, until it is dropped.
Pressure sensor enhanced smart soft actuator. 1, The video shows the movement of an u-shaped biogel actuator against a rigid object. On the tip of the soft actuator a pressure sensor is mounted, which is triggered when the sensor is compressed by contact to an object. The inflation and deflation is automated by a program. 2, At first the actuator passes by a screwdriver after inflation 3, until it reaches its maximum bending angle. At this point the deflation is actuated by the program and not by the sensor. 4, In the second case the biogel-actuator is again inflated by the program with the screwdriver in its trajectory. 5, The actuator approaches the object. After contact the foam sensor is compressed and initiates the deflation. 6, The soft actuator retreats from the screwdriver until it is completely deflated. 7, Via automated inflation of the actuator the pressure sensor at top of the actuator tip approaches a sharp rose thorn. 8, Contact with the sharp thorn compresses the pressure sensor without harming it and triggers retracting from the pointed obstacle. 9, The actuator retreats fully from the obstacle.
Autonomous soft electronic sensor skin. The video shows an electronic skin that intrinsically adheres to the human body. The e-skin sticks to the skin under shaking and twisting of the arm. Wireless communication and signal processing is placed on a flexible PCB, whereas the rest of the e-skin is biodegradable and stretchable. The impedance change is monitored during aspiration of the e-skin. Temperature sensors monitor hot objects like a cup with hot water. The e-skin is peeled off from the body after use.
Powder coating for reduced adhesion. The video shows biogels covered with talcum powder. 1, Powder covered biogels loose their stickiness. 2, The powder is removed from the surface by wiping it away with water. 3, With the powder removed, the biogel’s adhesion to arbitrary surfaces is restored.
Biogel thin film. 1, The video shows a biogel thin film (G1730) of 0.58 mm thickness, prepared with doctor blading. 2, The film is coated with talcum powder to make handling easier. 3, The thin film is reversibly highly stretchable and 4, deformable.
Soft pressure sensor array. The video shows a 4 ×4 pressure sensor array monitoring different loads. Weights (10 g, 20 g, 50 g) are placed on a single sensor to demonstrate its response. A 20 g weight is placed on different sensors. The position of the weight is detected throughout the whole skin.
About this article
Cite this article
Baumgartner, M., Hartmann, F., Drack, M. et al. Resilient yet entirely degradable gelatin-based biogels for soft robots and electronics. Nat. Mater. 19, 1102–1109 (2020). https://doi.org/10.1038/s41563-020-0699-3
This article is cited by
Scientific Reports (2023)
Nature Sustainability (2023)
npj Flexible Electronics (2023)
Nature Communications (2023)