Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Letter
  • Published:

Engineering stable electrocatalysts by synergistic stabilization between carbide cores and Pt shells


Core–shell particles with earth-abundant cores represent an effective design strategy for improving the performance of noble metal catalysts, while simultaneously reducing the content of expensive noble metals1,2,3,4. However, the structural and catalytic stabilities of these materials often suffer during the harsh conditions encountered in important reactions, such as the oxygen reduction reaction (ORR)3,4,5. Here, we demonstrate that atomically thin Pt shells stabilize titanium tungsten carbide cores, even at highly oxidizing potentials. In situ, time-resolved experiments showed how the Pt coating protects the normally labile core against oxidation and dissolution, and detailed microscopy studies revealed the dynamics of partially and fully coated core–shell nanoparticles during potential cycling. Particles with complete Pt coverage precisely maintained their core–shell structure and atomic composition during accelerated electrochemical ageing studies consisting of over 10,000 potential cycles. The exceptional durability of fully coated materials highlights the potential of core–shell architectures using earth-abundant transition metal carbide (TMC) and nitride (TMN) cores for future catalytic applications.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: SFC–ICP–MS single potential cycle and galvanostatic measurements.
Fig. 2: Structural stability during potential cycling.
Fig. 3: Long-term durability in O2-sat electrolyte and at elevated temperature.
Fig. 4: ORR catalytic stability.

Similar content being viewed by others

Data availability

Experimental data are available from the corresponding authors on reasonable request.


  1. Strasser, P. et al. Lattice-strain control of the activity in dealloyed core–shell fuel cell catalysts. Nat. Chem. 2, 454–460 (2010).

    Article  CAS  Google Scholar 

  2. Gasteiger, H. A. & Marković, N. M. Just a dream—or future reality? Science 324, 48–49 (2009).

    Article  CAS  Google Scholar 

  3. Stephens, I. E. L., Bondarenko, A. S., Grønbjerg, U., Rossmeisl, J. & Chorkendorff, I. Understanding the electrocatalysis of oxygen reduction on platinum and its alloys. Energy Environ. Sci. 5, 6744–6762 (2012).

    Article  CAS  Google Scholar 

  4. Oezaslan, M., Hasché, F. & Strasser, P. Pt-Based core–shell catalyst architectures for oxygen fuel cell electrodes. J. Phys. Chem. Lett. 4, 3273–3291 (2013).

    Article  CAS  Google Scholar 

  5. Wang, X. et al. Palladium-platinum core–shell icosahedra with substantially enhanced activity and durability towards oxygen reduction. Nat. Commun. 6, 7594 (2015).

    Article  Google Scholar 

  6. Schwammlein, J. N. et al. Origin of superior activity of Ru@Pt core–shell nanoparticles towards hydrogen oxidation in alkaline media. ECS Trans. 75, 971–982 (2016).

    Article  Google Scholar 

  7. Alayoglu, S., Nilekar, A. U., Mavrikakis, M. & Eichhorn, B. Ru-Pt core–shell nanoparticles for preferential oxidation of carbon monoxide in hydrogen. Nat. Mater. 7, 333–338 (2008).

    Article  CAS  Google Scholar 

  8. Sasaki, K. et al. Core-protected platinum monolayer shell high-stability electrocatalysts for fuel-cell cathodes. Angew. Chem. Int. Ed. 49, 8602–8607 (2010).

    Article  CAS  Google Scholar 

  9. Tedsree, K. et al. Hydrogen production from formic acid decomposition at room temperature using a Ag-Pd core–shell nanocatalyst. Nat. Nanotech 6, 302–307 (2011).

    Article  CAS  Google Scholar 

  10. Strickler, A. L., Jackson, A. & Jaramillo, T. F. Active and stable Ir@Pt core–shell catalysts for electrochemical oxygen reduction. ACS Energy Lett. 2, 244–249 (2016).

    Article  Google Scholar 

  11. Cui, C., Gan, L., Heggen, M., Rudi, S. & Strasser, P. Compositional segregation in shaped Pt alloy nanoparticles and their structural behaviour during electrocatalysis. Nat. Mater. 12, 765–771 (2013).

    Article  CAS  Google Scholar 

  12. Chen, S., Gasteiger, H. A., Hayakawa, K., Tada, T. & Shao-Horn, Y. Platinum-alloy cathode catalyst degradation in proton exchange membrane fuel cells: nanometer-scale compositional and morphological changes. J. Electrochem. Soc. 157, A82–A97 (2010).

    Article  CAS  Google Scholar 

  13. Perez-Alonso, F. J. et al. Identical locations transmission electron microscopy study of Pt/C electrocatalyst degradation during oxygen reduction reaction. J. Power Sources 196, 6085–6091 (2011).

    Article  CAS  Google Scholar 

  14. Knossalla, J. et al. Shape-controlled nanoparticles in pore-confined space. J. Am. Chem. Soc. 140, 15684–15689 (2018).

    Article  CAS  Google Scholar 

  15. Hunt, S. T. et al. Self-assembly of noble metal monolayers on transition metal carbide nanoparticle catalysts. Science 352, 974–978 (2016).

    Article  CAS  Google Scholar 

  16. Zhong, Y. et al. Transition metal carbides and nitrides in energy storage and conversion. Adv. Sci. 3, 1500286 (2016).

    Article  Google Scholar 

  17. Hunt, S. T., Nimmanwudipong, T. & Roman-Leshkov, Y. Engineering non-sintered, metal-terminated tungsten carbide nanoparticles for catalysis. Angew. Chem. 53, 5131–5136 (2014).

    CAS  Google Scholar 

  18. Kuttiyiel, K. A. et al. Enhancement of the oxygen reduction on nitride stabilized Pt-M (M=Fe, Co, and Ni) core–shell nanoparticle electrocatalysts. Nano Energy 13, 442–449 (2015).

    Article  CAS  Google Scholar 

  19. Tian, X. et al. Transition metal nitride coated with atomic layers of Pt as a low-cost, highly stable electrocatalyst for the oxygen reduction reaction. J. Am. Chem. Soc. 138, 1575–1583 (2016).

    Article  CAS  Google Scholar 

  20. Garg, A. et al. Transition‐Metal nitride Core@Noble‐Metal shell nanoparticles as highly CO tolerant catalysts. Angew. Chem. Int. Ed. 56, 8828–8833 (2017).

    Article  CAS  Google Scholar 

  21. Hunt, S. T., Milina, M., Wang, Z. & Roman-Leshkov, Y. Activating earth-abundant electrocatalysts for efficient, low-cost hydrogen evolution/oxidation: sub-monolayer platinum coatings on titanium tungsten carbide nanoparticles. Energy Environ. Sci. 9, 3290–3301 (2016).

    Article  CAS  Google Scholar 

  22. Garg, A. Transition Metal Carbide and Nitride Nanoparticles with Noble Metal Shells as Enhanced Catalysts (Massachusetts Institute of Technology, 2018).

  23. Topalov, A. A. et al. Dissolution of platinum: limits for the deployment of electrochemical energy conversion? Angew. Chem. 51, 12613–12615 (2012).

    Article  CAS  Google Scholar 

  24. Göhl, D. et al. Electrochemical stability of hexagonal tungsten carbide in the potential window of fuel cells and water electrolyzers investigated in a half-cell configuration. Electrochim. Acta 270, 70–76 (2018).

    Article  Google Scholar 

  25. Weidman, M. C., Esposito, D. V., Hsu, I. J. & Chen, J. G. Electrochemical stability of tungsten and tungsten monocarbide (WC) over wide ph and potential ranges. J. Electrochem. Soc. 157, F179–F188 (2010).

    Article  CAS  Google Scholar 

  26. Pourbaix, M. Atlas of Electrochemical Equilibria in Aqueous Solutions (National Association of Corrosion Engineers, 1974).

  27. Greeley, J. et al. Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat. Chem. 1, 552–556 (2009).

    Article  CAS  Google Scholar 

  28. Hendon, C. H. et al. Realistic surface descriptions of heterometallic interfaces: the case of TiWC coated in noble metals. J. Phys. Chem. Lett. 7, 4475–4482 (2016).

    Article  CAS  Google Scholar 

  29. Hasche, F., Oezaslan, M. & Strasser, P. Activity, stability and degradation of multi walled carbon nanotube (MWCNT) supported Pt fuel cell electrocatalysts. Phys. Chem. Chem. Phys. 12, 15251–15258 (2010).

    Article  CAS  Google Scholar 

  30. Meier, J. C. et al. Design criteria for stable Pt/C fuel cell catalysts. Beilstein J. Nanotechnol. 5, 44–67 (2014).

    Article  Google Scholar 

  31. Grote, J.-P., Zeradjanin, A. R., Cherevko, S. & Mayrhofer, K. J. J. Coupling of a scanning flow cell with online electrochemical mass spectrometry for screening of reaction selectivity. Rev. Sci. Instrum. 85, 104101 (2014).

    Article  Google Scholar 

  32. Mayrhofer, K. J. J. et al. Measurement of oxygen reduction activities via the rotating disc electrode method: from Pt model surfaces to carbon-supported high surface area catalysts. Electrochim. Acta 53, 3181–3188 (2008).

    Article  CAS  Google Scholar 

Download references


This research was funded by the Federal Ministry for Economic Affairs and Energy (BMWi) of Germany in the framework of PtTM@HGS (project number 03ET6080A) and by the Toyota Research Institute through the Accelerated Materials Design and Discovery program. We acknowledge Z. Wang for his help in synthesis of materials, A. Mingers for her help at the ICP–MS and G. Fortunato for the TEM images of Pt NPs/bulk WC.

Author information

Authors and Affiliations



D.G., A.G., Y.R.-L. and M.L. conceived this study. A.G. synthesized the materials and performed physicochemical characterization. D.G. conducted the electrochemical stability measurements via SFC–ICP–MS. P.P. carried out IL–STEM measurements accompanied with EDX elemental mapping. D.G. and A.G. conducted ORR activity measurements via RDE. The manuscript was written by A.G., Y.R.-L., D.G. and M.L. All authors discussed the manuscript and the results.

Corresponding authors

Correspondence to Yuriy Román-Leshkov or Marc Ledendecker.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–12, Table 1, discussion and ref. 1.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Göhl, D., Garg, A., Paciok, P. et al. Engineering stable electrocatalysts by synergistic stabilization between carbide cores and Pt shells. Nat. Mater. 19, 287–291 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing