Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

A universal close-space annealing strategy towards high-quality perovskite absorbers enabling efficient all-perovskite tandem solar cells


The broad bandgap tunability of organic–inorganic metal halide perovskites enables the fabrication of multi-junction all-perovskite tandem solar cells with ultra-high power conversion efficiencies (PCEs). Controllable crystallization plays a crucial role in the formation of high-quality perovskites. Here we report a universal close-space annealing strategy that increases grain size, enhances crystallinity and prolongs carrier lifetimes in low-bandgap (low-Eg) and wide-bandgap (wide-Eg) perovskite films. By placing the intermediate-phase perovskite films with their faces towards solvent-permeable covers during the annealing process, high-quality perovskite absorber layers are obtained with a slowed solvent releasing process, enabling fabrication of efficient single-junction perovskite solar cells (PVSCs) and all-perovskite tandem solar cells. As a result, the best PCEs of 21.51% and 18.58% for single-junction low-Eg and wide-Eg PVSCs are achieved and thus ensure the fabrication of 25.15% efficiency 4-terminal and 25.05% efficiency 2-terminal all-perovskite tandem solar cells.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Scheme of different annealing processes and corresponding film morphology.
Fig. 2: Characterizations of low-Eg perovskite films and PVSCs based on normal annealing, solvent annealing and CSA processes.
Fig. 3: Film quality of wide-Eg perovskites and device performance with normal annealing, solvent annealing and CSA processes.
Fig. 4: Photovoltaic performance of 4-T and 2-T tandem solar cells.

Similar content being viewed by others

Data availability

The datasets analysed and generated during the current study are included in the paper and its Supplementary Information. Source data are provided with this paper.


  1. Lin, R. et al. All-perovskite tandem solar cells with improved grain surface passivation. Nature 603, 73–78 (2022).

    Article  Google Scholar 

  2. Zhao, D. & Ding, L. All-perovskite tandem structures shed light on thin-film photovoltaics. Sci. Bull. 65, 1144–1146 (2020).

    Article  Google Scholar 

  3. Eperon, G. E. et al. Perovskite–perovskite tandem photovoltaics with optimized band gaps. Science 354, 861–865 (2016).

    Article  Google Scholar 

  4. Zhao, D. et al. Four-terminal all-perovskite tandem solar cells achieving power conversion efficiencies exceeding 23%. ACS Energy Lett. 3, 305–306 (2018).

    Article  Google Scholar 

  5. Tong, J. et al. Carrier lifetimes of >1 μs in Sn–Pb perovskites enable efficient all-perovskite tandem solar cells. Science 364, 475–479 (2019).

    Article  Google Scholar 

  6. He, R. et al. Wide-bandgap organic–inorganic hybrid and all-inorganic perovskite solar cells and their application in all-perovskite tandem solar cells. Energy Environ. Sci. 14, 5723–5759 (2021).

    Article  Google Scholar 

  7. Wang, C., Song, Z., Li, C., Zhao, D. & Yan, Y. Low-bandgap mixed tin–lead perovskites and their applications in all-perovskite tandem solar cells. Adv. Funct. Mater. 29, 1808801 (2019).

    Article  Google Scholar 

  8. Wang, L. et al. A Eu3+-Eu2+ ion redox shuttle imparts operational durability to Pb–I perovskite solar cells. Science 363, 265–270 (2019).

    Article  Google Scholar 

  9. Tan, H. et al. Efficient and stable solution-processed planar perovskite solar cells via contact passivation. Science 355, 722–726 (2017).

    Article  Google Scholar 

  10. Zheng, X. et al. Defect passivation in hybrid perovskite solar cells using quaternary ammonium halide anions and cations. Nat. Energy 2, 17102 (2017).

    Article  Google Scholar 

  11. Liu, Y., Dong, B., Hagfeldt, A., Luo, J. & Graetzel, M. Chemically tailored molecular surface modifiers for efficient and stable perovskite photovoltaics. SmartMat 2, 33–37 (2021).

    Article  Google Scholar 

  12. Shi, T. et al. Effects of organic cations on the defect physics of tin halide perovskites. J. Mater. Chem. A 5, 15124–15129 (2017).

    Article  Google Scholar 

  13. Wang, J. et al. Controlling the crystallization kinetics of lead-free tin halide perovskites for high performance green photovoltaics. Adv. Energy Mater. 11, 2102131 (2021).

    Article  Google Scholar 

  14. Zhou, Y. et al. Manipulating crystallization of organolead mixed-halide thin films in antisolvent baths for wide-bandgap perovskite solar cells. ACS Appl. Mater. Interfaces 8, 2232–2237 (2016).

    Article  Google Scholar 

  15. Bu, T. et al. Lead halide-templated crystallization of methylamine-free perovskite for efficient photovoltaic modules. Science 372, 1327–1332 (2021).

    Article  Google Scholar 

  16. Li, N. et al. Liquid medium annealing for fabricating durable perovskite solar cells with improved reproducibility. Science 373, 561–567 (2021).

    Article  Google Scholar 

  17. Xiao, K. et al. All-perovskite tandem solar cells with 24.2% certified efficiency and area over 1 cm2 using surface-anchoring zwitterionic antioxidant. Nat. Energy 5, 870–880 (2020).

    Article  Google Scholar 

  18. Xiao, Z. et al. Solvent annealing of perovskite-induced crystal growth for photovoltaic-device efficiency enhancement. Adv. Mater. 26, 6503–6509 (2014).

    Article  Google Scholar 

  19. Zhu, W. et al. Facile face-down annealing triggered remarkable texture development in CH3NH3PbI3 films for high-performance perovskite solar cells. ACS Appl. Mater. Interfaces 9, 6104–6113 (2017).

    Article  Google Scholar 

  20. Liu, J. et al. Lead-free solar cells based on tin halide perovskite films with high coverage and improved aggregation. Angew. Chem. Int. Ed. 57, 13221–13225 (2018).

    Article  Google Scholar 

  21. Zhu, L. et al. Solvent-molecule-mediated manipulation of crystalline grains for efficient planar binary lead and tin triiodide perovskite solar cells. Nanoscale 8, 7621–7630 (2016).

    Article  Google Scholar 

  22. Chen, S. et al. Stabilizing perovskite-substrate interfaces for high-performance perovskite modules. Science 373, 902–907 (2021).

    Article  Google Scholar 

  23. Jiang, X. et al. One-step synthesis of SnI2·(DMSO)x adducts for high-performance tin perovskite solar cells. J. Am. Chem. Soc. 143, 10970–10976 (2021).

    Article  Google Scholar 

  24. Chen, S. et al. Crystallization in one-step solution deposition of perovskite films: upward or downward? Sci. Adv. 7, eabb2412 (2021).

    Article  Google Scholar 

  25. Zhao, D. et al. Efficient two-terminal all-perovskite tandem solar cells enabled by high-quality low-bandgap absorber layers. Nat. Energy 3, 1093–1100 (2018).

    Article  Google Scholar 

  26. Zhao, D. et al. Low-bandgap mixed tin–lead iodide perovskite absorbers with long carrier lifetimes for all-perovskite tandem solar cells. Nat. Energy 2, 17018 (2017).

    Article  Google Scholar 

  27. Chen, Q. et al. Unveiling roles of tin fluoride additives in high-efficiency low-bandgap mixed tin–lead perovskite solar cells. Adv. Energy Mater. 11, 2101045 (2021).

    Article  Google Scholar 

  28. Li, C. et al. Reducing saturation-current density to realize high-efficiency low-bandgap mixed tin–lead halide perovskite solar cells. Adv. Energy Mater. 9, 1803135 (2018).

    Article  Google Scholar 

  29. Liao, W. et al. Fabrication of efficient low-bandgap perovskite solar cells by combining formamidinium tin iodide with methylammonium lead iodide. J. Am. Chem. Soc. 138, 12360–12363 (2016).

    Article  Google Scholar 

  30. Yu, Y. et al. Synergistic effects of lead thiocyanate additive and solvent annealing on the performance of wide-bandgap perovskite solar cells. ACS Energy Lett. 2, 1177–1182 (2017).

    Article  Google Scholar 

  31. Boccard, M. & Ballif, C. Influence of the subcell properties on the fill factor of two-terminal perovskite–silicon tandem solar cells. ACS Energy Lett. 5, 1077–1082 (2020).

    Article  Google Scholar 

  32. Yang, M. et al. Facile fabrication of large-grain CH3NH3PbI3−xBrx films for high-efficiency solar cells via CH3NH3Br-selective Ostwald ripening. Nat. Commun. 7, 12305 (2016).

    Article  Google Scholar 

  33. Zhang, G. et al. Synthesis of polymeric fluorescent brightener based on coumarin and its performances on paper as light stabilizer, fluorescent brightener and surface sizing agent. Appl. Surf. Sci. 367, 167–173 (2016).

    Article  Google Scholar 

  34. Alsalloum, A. Y. et al. 22.8%-efficient single-crystal mixed-cation inverted perovskite solar cells with a near-optimal bandgap. Energy Environ. Sci. 14, 2263–2268 (2021).

    Article  Google Scholar 

  35. Lu, H. et al. Vapor-assisted deposition of highly efficient, stable black-phase FAPbI3 perovskite solar cells. Science 370, eabb8985 (2020).

    Article  Google Scholar 

  36. Li, D.-B. et al. Stable and efficient CdS/Sb2Se3 solar cells prepared by scalable close space sublimation. Nano Energy 49, 346–353 (2018).

    Article  Google Scholar 

  37. Chen, Y. et al. Self-elimination of intrinsic defects improves the low-temperature performance of perovskite photovoltaics. Joule 4, 1961–1976 (2020).

    Article  Google Scholar 

  38. Chen, C. et al. Optical properties of amorphous and polycrystalline Sb2Se3 thin films prepared by thermal evaporation. Appl. Phys. Lett. 107, 043905 (2015).

    Article  Google Scholar 

  39. Lin, R. et al. Monolithic all-perovskite tandem solar cells with 24.8% efficiency exploiting comproportionation to suppress Sn(II) oxidation in precursor ink. Nat. Energy 4, 864–873 (2019).

    Article  Google Scholar 

  40. Yu, Z. et al. Simplified interconnection structure based on C60/SnO2-x for all-perovskite tandem solar cells. Nat. Energy 5, 657–665 (2020).

    Article  Google Scholar 

  41. Li, C. et al. Low-bandgap mixed tin–lead iodide perovskites with reduced methylammonium for simultaneous enhancement of solar cell efficiency and stability. Nat. Energy 5, 768–776 (2020).

    Article  Google Scholar 

  42. Wang, C. et al. Compositional and morphological engineering of mixed cation perovskite films for highly efficient planar and flexible solar cells with reduced hysteresis. Nano Energy 35, 223–232 (2017).

    Article  Google Scholar 

  43. Wang, C. et al. Low-temperature plasma-enhanced atomic layer deposition of tin oxide electron selective layers for highly efficient planar perovskite solar cells. J. Mater. Chem. A 4, 12080–12087 (2016).

    Article  Google Scholar 

Download references


The work was financially supported by the National Key Research and Development Program of China (number 2019YFE0120000), National Natural Science Foundation of China (numbers 61875143, 62005188, 62174112, and 62120106001), Natural Science Foundation of Jiangsu Province (BK20190825), Fundamental Research Funds for the Central Universities (numbers YJ2021157, 2021SCU12057, and YJ201955), the Science and Technology Program of Sichuan Province (numbers 2020JDJQ0030), Engineering Featured Team Fund of Sichuan University (2020SCUNG102) and Engineering Research Center of Digital Imaging and Display, Ministry of Education, Soochow University. F.F. acknowledges funding from the Swiss Federal Office of Energy (SFOE)-BFE (project number SI/501805-01).

Author information

Authors and Affiliations



C.W. and D.Z. conceived the project. C.W. carried out single cell and tandem cell fabrication and characterization. Y.Z., Y.A. and R.H. helped with the fabrication of single-junction wide-Eg PVSCs in both regular and inverted structures. T.M. and J.Z. helped the device fabrication of single-junction low-Eg PVSCs. C.C. did the SEM, X-ray diffraction characterizations of single-junction PVSCs and helped the solvent annealing processes of both low-Eg and wide-Eg perovskite films. S.R. did the PL and TRPL measurements. C.W., F.F., D.Z. and X.L. analysed the data and wrote the manuscript. Y.Z., T.M., Y.A., R.H., J.Z., C.C., S.R. and F.F. helped with the manuscript preparation. All the authors discussed the results and commented on the manuscript. X.L. and D.Z. supervised the project.

Corresponding authors

Correspondence to Fan Fu, Dewei Zhao or Xiaofeng Li.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature Energy thanks Rohit Prasanna, Atsushi Wakamiya and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–31, Discussions 1–4, Tables 1–5 and References 1–4.

Reporting Summary.

Supplementary Data 1

Supplementary Figs. 1 and 13h and Tables 1 and 3–5.

Source data

Source Data Fig. 2

Source data for Fig. 2c.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Wang, C., Zhao, Y., Ma, T. et al. A universal close-space annealing strategy towards high-quality perovskite absorbers enabling efficient all-perovskite tandem solar cells. Nat Energy 7, 744–753 (2022).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing