Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Additive engineering for robust interphases to stabilize high-Ni layered structures at ultra-high voltage of 4.8 V

Abstract

Nickel-rich layered cathode materials promise high energy density for next-generation batteries when coupled with lithium metal anodes. However, the practical capacities accessible are far less than the theoretical values due to their structural instability during cycling, especially when charged at high voltages. Here we demonstrate that stable cycling with an ultra-high cut-off voltage of 4.8 V can be realized by using an appropriate amount of lithium difluorophosphate in a common commercial electrolyte. The Li||LiNi0.76Mn0.14Co0.10O2 cell retains 97% of the initial capacity (235 mAh g–1) after 200 cycles. The cycling stability is ascribed to the robust interphase on the cathode. It is formed by lithium difluorophosphate decomposition, which is facilitated by the catalytic effect of transition metals. The decomposition products (Li3PO4 and LiF) form a protective interphase. This suppresses transition metal dissolution and cathode surface reconstruction. It also facilitates uniform Li distribution within the cathode, effectively mitigating the strain and crack formation.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Electrochemical performance of Li || NMC76 cells using different electrolytes at ultra-high voltage.
Fig. 2: CEI XPS characterization and LiDFP additive decomposition mechanism.
Fig. 3: HAADF-STEM and soft XAS characterizations for cycled NMC76 cathode.
Fig. 4: Electrode-level quantification of the deposited TM on lithium anode.
Fig. 5: Electrode-level characterization of the chemo-mechanical interaction when using the electrolytes with and without the LiDFP additive.
Fig. 6: X-ray diffraction and tomography analysis of cycled NMC76 cathode.

Similar content being viewed by others

Data availability

The datasets analysed and generated during the current study are included in the paper and its Supplementary Information file.

Code availability

The source code of the analysis of synchrotron phase contrast nano-tomography cathode data is available at our GitHub repository: https://github.com/YijinLiu-Lab/LIBNet.

References

  1. Wu, L. et al. Structural origin of overcharge-induced thermal instability of Ni-containing layered-cathodes for high-energy-density lithium batteries. Chem. Mater. 23, 3953–3960 (2011).

    Article  Google Scholar 

  2. Nam, K.-W. et al. Combining in situ synchrotron X-ray diffraction and absorption techniques with transmission electron microscopy to study the origin of thermal instability in overcharged cathode materials for lithium-ion batteries. Adv. Funct. Mater. 23, 1047–1063 (2013).

    Article  Google Scholar 

  3. Lin, F. et al. Surface reconstruction and chemical evolution of stoichiometric layered cathode materials for lithium-ion batteries. Nat. Commun. 5, 3529 (2014).

    Article  Google Scholar 

  4. Mao, Y. et al. High‐voltage charging‐induced strain, heterogeneity, and micro‐cracks in secondary particles of a nickel‐rich layered cathode material. Adv. Funct. Mater. 29, 1900247 (2019).

    Article  Google Scholar 

  5. Tornheim, A. et al. Effect of electrolyte composition on rock salt surface degradation in NMC cathodes during high-voltage potentiostatic holds. Nano Energy 55, 216–225 (2019).

    Article  Google Scholar 

  6. Zhang, S., Ma, J., Hu, Z., Cui, G. & Chen, L. Identifying and addressing critical challenges of high-voltage layered ternary oxide cathode materials. Chem. Mater. 31, 6033–6065 (2019).

    Article  Google Scholar 

  7. Gent, W. E. et al. Persistent state-of-charge heterogeneity in relaxed, partially charged Li1–xNi1/3Co1/3Mn1/3O2 secondary particles. Adv. Mater. 28, 6631–6638 (2016).

    Article  Google Scholar 

  8. Wei, C. et al. Mesoscale battery science: the behavior of electrode particles caught on a multispectral X-ray camera. Acc. Chem. Res. 51, 2484–2492 (2018).

    Article  Google Scholar 

  9. Shangguan, X. et al. Additive-assisted novel dual-salt electrolyte addresses wide temperature operation of lithium–metal batteries. Small 15, 1900269 (2019).

    Article  Google Scholar 

  10. Yang, H. et al. Simultaneously dual modification of Ni‐rich layered oxide cathode for high‐energy lithium‐ion batteries. Adv. Funct. Mater. 29, 1808825 (2019).

    Article  Google Scholar 

  11. Park, K.-J. et al. Improved cycling stability of Li[Ni0.90Co0.05Mn0.05]O2 through microstructure modification by boron doping for Li-ion batteries. Adv. Energy Mater. 8, 1801202 (2018).

    Article  Google Scholar 

  12. Yan, P. et al. Tailoring grain boundary structures and chemistry of Ni-rich layered cathodes for enhanced cycle stability of lithium-ion batteries. Nat. Energy 3, 600–605 (2018).

    Article  Google Scholar 

  13. Bi, Y. et al. Reversible planar gliding and microcracking in a single-crystalline Ni-rich cathode. Science 370, 1313–1317 (2020).

    Article  Google Scholar 

  14. Wang, W. et al. Stable cycling of high-voltage lithium-metal batteries enabled by high-concentration FEC-based electrolyte. ACS Appl. Mater. Interfaces 12, 22901–22909 (2020).

    Article  Google Scholar 

  15. Kim, K.-E. et al. A combination of lithium difluorophosphate and vinylene carbonate as reducible additives to improve cycling performance of graphite electrodes at high rates. Electrochem. Commun. 61, 121–124 (2015).

    Article  Google Scholar 

  16. Yang, B., Zhang, H., Yu, L., Fan, W. & Huang, D. Lithium difluorophosphate as an additive to improve the low temperature performance of LiNi0.5Co0.2Mn0.3O2/graphite cells. Electrochim. Acta 221, 107–114 (2016).

    Article  Google Scholar 

  17. Zhao, W. et al. Toward a stable solid-electrolyte-interfaces on nickel-rich cathodes: LiPO2F2 salt-type additive and its working mechanism for LiNi0.5Mn0.25Co0.25O2 cathodes. J. Power Sources 380, 149–157 (2018).

    Article  Google Scholar 

  18. Ma, L. et al. LiPO2F2 as an electrolyte additive in Li[Ni0.5Mn0.3Co0.2]O2/graphite pouch cells. J. Electrochem. Soc. 165, A891–A899 (2018).

    Article  Google Scholar 

  19. Liu, Y., Harlow, J. & Dahn, J. Microstructural observations of “single crystal” positive electrode materials before and after long term cycling by cross-section scanning electron microscopy. J. Electrochem. Soc. 167, 020512 (2020).

    Article  Google Scholar 

  20. Zhao, D. et al. New insight into the mechanism of LiPO2F2 on the interface of high-voltage cathode LiNi0.5Mn1.5O4 with truncated octahedral structure. Appl. Surf. Sci. 491, 595–606 (2019).

    Article  Google Scholar 

  21. Fan, X. & Wang, C. High-voltage liquid electrolytes for Li batteries: progress and perspectives. Chem. Soc. Rev 50, 10486–10566 (2021).

    Article  Google Scholar 

  22. Suo, L. et al. Fluorine-donating electrolytes enable highly reversible 5-V-class Li metal batteries. Proc. Natl Acad. Sci. USA 115, 1156–1161 (2018).

    Article  Google Scholar 

  23. Wang, C., Meng, Y. S. & Xu, K. Perspective—fluorinating interphases. J. Electrochem. Soc. 166, A5184–A5186 (2019).

    Article  Google Scholar 

  24. Zhan, C., Wu, T., Lu, J. & Amine, K. Dissolution, migration, and deposition of transition metal ions in Li-ion batteries exemplified by Mn-based cathodes – a critical review. Energy Environ. Sci. 11, 243–257 (2018).

    Article  Google Scholar 

  25. Xu, G.-L. et al. Building ultraconformal protective layers on both secondary and primary particles of layered lithium transition metal oxide cathodes. Nat. Energy 4, 484–494 (2019).

    Article  Google Scholar 

  26. Li, S. et al. Targeted research on the single role of lithium bis(oxalate)borate in the film-forming process through a novel lithium salt-free electrolyte system. J. Power Sources 471, 228426 (2020).

    Article  Google Scholar 

  27. Cui, X. et al. Antioxidation mechanism of highly concentrated electrolytes at high voltage. ACS Appl. Mater. Interfaces 13, 59580–59590 (2021).

    Article  Google Scholar 

  28. Li, N. W., Yin, Y. X., Yang, C. P. & Guo, Y. G. An artificial solid electrolyte interphase layer for stable lithium metal anodes. Adv. Mater. 28, 1853–1858 (2016).

    Article  Google Scholar 

  29. Hall, D. S., Self, J. & Dahn, J. R. Dielectric constants for quantum chemistry and Li-ion batteries: solvent blends of ethylene carbonate and ethyl methyl carbonate. J. Phys. Chem. C 119, 22322–22330 (2015).

    Article  Google Scholar 

  30. Zhao, W. et al. Toward a stable solid-electrolyte-interfaces on nickel-rich cathodes: LiPO2F2 salt-type additive and its working mechanism for LiNi0.5Mn0.25Co0.25O2 cathodes. J. Power Sources 380, 149–157 (2018).

    Article  Google Scholar 

  31. Wang, J. et al. Analyzing the mechanism of functional groups in phosphate additives on the interface of LiNi0.8Co0.15Al0.05O2 cathode materials. ACS Appl. Mater. Interfaces 13, 16939–16951 (2021).

    Article  Google Scholar 

  32. Wang, C. et al. Lithium difluorophosphate as a promising electrolyte lithium additive for high-voltage lithium-ion batteries. ACS Appl. Energy Mater. 1, 2647–2656 (2018).

    Article  Google Scholar 

  33. Eldesoky, A., Logan, E. R., Johnson, M. B., McFarlane, C. R. M. & Dahn, J. R. Scanning micro X-ray fluorescence (μXRF) as an effective tool in quantifying Fe dissolution in LiFePO4 cells: towards a mechanistic understanding of Fe dissolution. J. Electrochem. Soc. 167, 130539 (2020).

    Article  Google Scholar 

  34. Müller, V. et al. Effects of mechanical compression on the aging and the expansion behavior of Si/C-composite|NMC811 in different lithium-ion battery cell formats. J. Electrochem. Soc. 166, A3796–A3805 (2019).

    Article  Google Scholar 

  35. Harte, P. et al. Adaptation and improvement of an elemental mapping method for lithium ion battery electrodes and separators by means of laser ablation-inductively coupled plasma-mass spectrometry. Anal. Bioanal. Chem. 411, 581–589 (2019).

    Article  Google Scholar 

  36. Yang, S.-J. et al. Plating current density distribution of lithium metal anodes in pouch cells. J. Energy Chem. 69, 70–75 (2022).

    Article  Google Scholar 

  37. Wandt, J. et al. Transition metal dissolution and deposition in Li-ion batteries investigated by operando X-ray absorption spectroscopy. J. Mater. Chem. A 4, 18300–18305 (2016).

    Article  Google Scholar 

  38. Giordano, L. et al. Chemical reactivity descriptor for the oxide-electrolyte interface in Li-ion batteries. J. Phys. Chem. Lett. 8, 3881–3887 (2017).

    Article  Google Scholar 

  39. Østergaard, T. M. et al. Oxidation of ethylene carbonate on Li metal oxide surfaces. J. Phys. Chem. C 122, 10442–10449 (2018).

    Article  Google Scholar 

  40. Jiang, Z. et al. Machine-learning-revealed statistics of the particle-carbon/binder detachment in lithium-ion battery cathodes. Nat. Commun. 11, 2310 (2020).

    Article  Google Scholar 

  41. Li, J. et al. The impact of electrolyte additives and upper cut-off voltage on the formation of a rocksalt surface layer in LiNi0.8Mn0.1Co0.1O2 electrodes. J. Electrochem. Soc. 164, A655–A665 (2017).

    Article  Google Scholar 

  42. Li, S. et al. Synergistic dual-additive electrolyte enables practical lithium-metal batteries. Angew. Chem. Int. Ed. 59, 14935–14941 (2020).

    Article  Google Scholar 

  43. Hu, J. et al. Fundamental linkage between structure, electrochemical properties, and chemical compositions of LiNi1–xyMnxCoyO2 cathode materials. ACS Appl. Mater. Interfaces 13, 2622–2629 (2021).

    Article  Google Scholar 

  44. Hu, J. et al. Mesoscale-architecture-based crack evolution dictating cycling stability of advanced lithium ion batteries. Nano Energy 79, 105420 (2021).

    Article  Google Scholar 

  45. Solé, V. A., Papillon, E., Cotte, M., Walter, P. & Susini, J. A multiplatform code for the analysis of energy-dispersive X-ray fluorescence spectra. Spectrochim. Acta B Spectrosc. 62, 63–68 (2007).

    Article  Google Scholar 

  46. Cesar da Silva, J. et al. Efficient concentration of high-energy X-rays for diffraction-limited imaging resolution. Optica 4, 492–495 (2017).

    Article  Google Scholar 

  47. Cloetens, P. et al. Holotomography: quantitative phase tomography with micrometer resolution using hard synchrotron radiation X rays. Appl. Phys. Lett. 75, 2912–2914 (1999).

    Article  Google Scholar 

  48. Mirone, A., Brun, E., Gouillart, E., Tafforeau, P. & Kieffer, J. The PyHST2 hybrid distributed code for high speed tomographic reconstruction with iterative reconstruction and a priori knowledge capabilities. Nucl. Instrum. Methods Phys. Res. B 324, 41–48 (2014).

    Article  Google Scholar 

Download references

Acknowledgements

S.T., Z.S., X.-Q.Y. and E.H. are supported by the Assistant Secretary for Energy Efficiency and Renewable Energy, Vehicle Technology Office of the US Department of Energy (DOE) through the Advanced Battery Materials Research Program, including the Battery500 Consortium under contract no. DE-SC0012704. S.T., Z.S., X.-Q.Y. and E.H. also acknowledge the support from the Assistant Secretary for Energy Efficiency and Renewable Energy, Vehicle Technology Office of the US DOE through the Applied Battery Research for Transportation programme under contract no. DE-SC0012704. HAADF-STEM measurements and DFT computational work used the resources of the Center for Functional Nanomaterials, a US DOE Office of Science User Facility at Brookhaven National Laboratory, under contract no. DE-SC0012704. This research used beamlines 5-ID, 7-BM, 23-ID-2 and 28-ID-2 of the NSLS II, a US DOE Office of Science user facility operated for the DOE Office of Science by Brookhaven National Laboratory under contract no. DE-SC0012704. The hard X-ray phase contrast tomography was conducted at the nano-imaging beamline ID16A-NI at the European Synchrotron Radiation Facility, Grenoble, France. A.C. and K.X. thank the Joint Center of Energy Storage Research, an energy hub funded by the US DOE Office of Science, for support. Y.L. and J.L. acknowledge the support from the US DOE Laboratory Directed Research and Development programme at SLAC National Accelerator Laboratory under contract DE-AC02-76SF00515.

Author information

Authors and Affiliations

Authors

Contributions

E.H., K.X. and S.T. conceived the idea and designed the experiments. S.T. and Z.S. carried out the electrochemical measurements. S.T., Z.S., E.H., Y.Y., A.H., I.W. and L.M. conducted the synchrotron soft and hard XAS, X-ray diffraction and XRF mapping experiments. J.L., Y.L., F.M. and P.C. carried out the synchrotron tomography experiments and machine-learning-assisted data analysis. X.W. performed the DFT calculation. R.L. carried out the HAADF-STEM experiments. J.H. and J.X. synthesized the cathode materials. A.C. and K.X. carried out the XPS measurement. S.T., Z.S., J.L., Y.L., X.-Q.Y., K.X. and E.H. wrote the manuscript with input from all the authors.

Corresponding authors

Correspondence to Yijin Liu, Xiao-Qing Yang, Kang Xu or Enyuan Hu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature Energy thanks Mérièm Anouti, Shiyou Li and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–22, Tables 1 and 2, notes and references.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Tan, S., Shadike, Z., Li, J. et al. Additive engineering for robust interphases to stabilize high-Ni layered structures at ultra-high voltage of 4.8 V. Nat Energy 7, 484–494 (2022). https://doi.org/10.1038/s41560-022-01020-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41560-022-01020-x

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing