Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Improving cyclability of Li metal batteries at elevated temperatures and its origin revealed by cryo-electron microscopy


Operations of lithium-ion batteries have long been limited to a narrow temperature range close to room temperature. At elevated temperatures, cycling degradation speeds up due to enhanced side reactions, especially when high-reactivity lithium metal is used as the anode. Here, we demonstrate enhanced performance in lithium metal batteries operated at elevated temperatures. In an ether-based electrolyte at 60 °C, an average Coulombic efficiency of 99.3% is obtained and more than 300 stable cycles are realized, but, at 20 °C, the Coulombic efficiency drops dramatically within 75 cycles, corresponding to an average Coulombic efficiency of 90.2%. Cryo-electron microscopy reveals a drastically different solid electrolyte interface nanostructure emerging at 60 °C, which maintains mechanical stability, inhibits continuous side reactions and guarantees good cycling stability and low electrochemical impedance. Furthermore, larger lithium particles grown at the elevated temperature reduce the electrolyte/electrode interfacial area, which decreases the per-cycle lithium loss and enables higher Coulombic efficiencies.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: The conventional wisdom about the operating temperature of battery performance.
Fig. 2: Enhanced performance at elevated temperature demonstrated by Cu/Li cells.
Fig. 3: Cryo-EM reveals an emergent SEI nanostructure formed at elevated temperature.
Fig. 4: Elevated temperature nucleates larger Li particles and optimizes the electrode/electrolyte contact area.
Fig. 5: Elevated temperature results in small and stable impedance during cycling.
Fig. 6: Enhanced performance at elevated temperature demonstrated by LiFePO4/Li cells.

Similar content being viewed by others

Data availability

The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.


  1. Tarascon, J. M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001).

    Article  Google Scholar 

  2. Chu, S. & Majumdar, A. Opportunities and challenges for a sustainable energy future. Nature 488, 294–303 (2012).

    Article  Google Scholar 

  3. Leng, F., Tan, C. M. & Pecht, M. Effect of temperature on the aging rate of Li ion battery operating above room temperature. Sci. Rep. 5, 12967 (2015).

    Article  Google Scholar 

  4. Lithium Ion Rechargeable Batteries: Technical Handbook (Sony Corporation, 2009);

  5. Cho, H.-M., Choi, W.-S., Go, J.-Y., Bae, S.-E. & Shi, H.-C. A study on time-dependent low temperature power performance of a lithium-ion battery. J. Power Sources 198, 273–280 (2012).

    Article  Google Scholar 

  6. Zhang, S. S., Xu, K. & Jow, T. R. Electrochemical impedance study on the low temperature of Li-ion batteries. Electrochim. Acta 49, 1057–1061 (2004).

    Article  Google Scholar 

  7. Sides, C. R. & Martin, C. R. Nanostructured electrodes and the low-temperature performance of Li-ion batteries. Adv. Mater. 17, 125–128 (2005).

    Article  Google Scholar 

  8. Ishikawa, M., Kanemoto, M. & Morita, M. Control of lithium metal anode cycleability by electrolyte temperature. J. Power Sources 81–82, 217–220 (1999).

    Article  Google Scholar 

  9. Yang, X.-G., Zhang, G., Ge, S. & Wang, C.-Y. Fast charging of lithium-ion batteries at all temperatures. Proc. Natl Acad. Sci. USA 115, 7266–7271 (2018).

    Article  Google Scholar 

  10. Yan, P. et al. Tailoring grain boundary structures and chemistry of Ni-rich layered cathodes for enhanced cycle stability of lithium-ion batteries. Nat. Energy 3, 600–605 (2018).

    Article  Google Scholar 

  11. Ramadass, P., Haran, B., White, R. & Popov, B. N. Capacity fade of Sony 18650 cells cycled at elevated temperatures Part I. Cycling performance. J. Power Sources 112, 606–613 (2002).

    Article  Google Scholar 

  12. Liu, D.-Q., Liu, X.-Q. & He, Z.-Z. The elevated temperature performance of LiMn2O4 coated with Li4Ti5O12 for lithium ion battery. Mater. Chem. Phys. 105, 362–366 (2007).

    Article  Google Scholar 

  13. Shim, J., Kostecki, R., Richardson, T., Song, X. & Striebel, K. A. Electrochemical analysis for cycle performance and capacity fading of a lithium-ion battery cycled at elevated temperature. J. Power Sources 112, 222–230 (2002).

    Article  Google Scholar 

  14. Waldmann, T., Wilka, M., Kasper, M., Fleischhammer, M. & Wohlfahrt-Mehrens, M. Temperature dependent ageing mechanisms in lithium-ion batteries—a post-mortem study. J. Power Sources 262, 129–135 (2014).

    Article  Google Scholar 

  15. Jung, H.-G., Jang, M. W., Hassoun, J., Sun, Y.-K. & Scrosati, B. A high-rate long-life Li4Ti5O12/ Li[Ni0.45Co0.1Mn1.45]O4 lithium-ion battery. Nat. Commun. 2, 516 (2011).

    Article  Google Scholar 

  16. Schimpe, M. et al. Comprehensive modeling of temperature-dependent degradation mechanisms in lithium iron phosphate batteries. J. Electrochem. Soc. 165, A181–A193 (2018).

    Article  Google Scholar 

  17. Xu, W. et al. Lithium metal anodes for rechargeable batteries. Energy Environ. Sci. 7, 513–537 (2014).

    Article  Google Scholar 

  18. Tikekar, M. D., Choudhury, S., Tu, Z. & Archer, L. A. Design principles for electrolytes and interfaces for stable lithium-metal batteries. Nat. Energy 1, 16114 (2016).

    Article  Google Scholar 

  19. Lin, D., Liu, Y. & Cui, Y. Reviving the lithium metal anode for high-energy batteries. Nat. Nanotechnol. 12, 194–206 (2017).

    Article  Google Scholar 

  20. Xu, K. Nonaqueous liquid electrolytes for lithium-based rechargeable batteries. Chem. Rev. 104, 4303–4417 (2004).

    Article  Google Scholar 

  21. Xu, K. Electrolytes and interphases in Li-ion batteries and beyond. Chem. Rev. 114, 11503–11618 (2014).

    Article  Google Scholar 

  22. Li, L. et al. Self-heating-induced healing of lithium dendrites. Science 359, 1513–1516 (2018).

    Article  Google Scholar 

  23. Winter, M. The solid electrolyte interphase—the most important and the least understood solid electrolyte in rechargeable Li batteries. Z. Phys. Chem. 223, 1395–1406 (2009).

    Article  Google Scholar 

  24. Wang, A., Kadam, S., Li, H., Shi, S. & Qi, Y. Review on modeling of the anode solid electrolyte interphase (SEI) for lithium-ion batteries. npj Comput. Mater. 4, 15 (2018).

    Article  Google Scholar 

  25. Li, Y. et al. Atomic structure of sensitive battery materials and interfaces revealed by cryo-electron microscopy. Science 358, 506–510 (2017).

    Article  Google Scholar 

  26. Li, Y. et al. Correlating structure and function of battery interphases at atomic resolution using cryo-electron microscopy. Joule 2, 2167–2177 (2018).

    Article  Google Scholar 

  27. Zachman, M. J., Tu, Z., Choudhury, S., Archer, L. A. & Kourkoutis, L. F. Cryo-STEM mapping of solid–liquid interfaces and dendrites in lithium-metal batteries. Nature 560, 345–349 (2018).

    Article  Google Scholar 

  28. Aurbach, D., Ein‐Ely, Y. & Zaban, A. The surface chemistry of lithium electrodes in alkyl carbonate solutions. J. Electrochem. Soc. 141, L1–L3 (1994).

    Article  Google Scholar 

  29. Mogensen, R., Brandell, D. & Younesi, R. Solubility of the solid electrolyte interphase (SEI) in sodium ion batteries. ACS Energy Lett. 1, 1173–1178 (2016).

    Article  Google Scholar 

  30. Pan, H. et al. Addressing passivation in lithium–sulfur battery under lean electrolyte condition. Adv. Funct. Mater. 0, 1707234 (2018).

    Article  Google Scholar 

  31. Mikhaylik, Y. V. Electrolytes for lithium sulfur cells. US patent 7,354,680 B2 (2008).

  32. Pei, A., Zheng, G., Shi, F., Li, Y. & Cui, Y. Nanoscale nucleation and growth of electrodeposited lithium metal. Nano Lett. 17, 1132–1139 (2017).

    Article  Google Scholar 

  33. Ely, D. R. & Garcia, R. E. Heterogeneous nucleation and growth of lithium electrodeposits on negative electrodes. J. Electrochem. Soc. 160, A662–A668 (2013).

    Article  Google Scholar 

  34. Wang, F.-M. et al. Aging effects to solid electrolyte interface (SEI) membrane formation and the performance analysis of lithium ion batteries. Int. J. Electrochem. Sci. 6, 1014–1026 (2011).

    Google Scholar 

  35. Liu, Y. et al. An artifcial solid electrolyte interphase with high Li-ion conductivity, mechanical strength, and flexibility for stable lithium metal anodes. Adv. Mater. 29, 1605531 (2017).

    Article  Google Scholar 

  36. Tu, Z. et al. Nanoporous hybrid electrolytes for high-energy batteries based on reactive metal anodes. Adv. Energy Mater. 7, 1602367 (2017).

    Article  Google Scholar 

  37. Hu, Q. et al. Graft copolymer-based lithium-ion battery for high-temperature operation. J. Power Sources 196, 5604–5610 (2011).

    Article  Google Scholar 

Download references


Y.C. acknowledges support from the Assistant Secretary for Energy Efficiency and Renewable Energy, Office of Vehicle Technologies, Battery Materials Research (BMR) Program and Battery 500 Consortium of the US Department of Energy, Stanford Global Climate and Energy Projects (GCEP), the Office of Naval Research, the Joint Center for Energy Storage Research (JCESR) and a KAUST Investigator Award. A.P. acknowledges support from the National Defense Science and Engineering Graduate Fellowship and the Stanford Graduate Fellowship. Part of this work was performed at the Stanford Nano Shared Facilities (SNSF), supported by the National Science Foundation under award ECCS-1542152.

Author information

Authors and Affiliations



J.W., A.P. and Y.C. conceived and designed the experiments. J.W. and A.P. performed the experiments. W.H. and Y.L. conducted TEM characterization. J.W., A.P., W.H. and Y.C. co-wrote the paper. All authors discussed the results and commented on the manuscript.

Corresponding author

Correspondence to Yi Cui.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Information

Supplementary information

Supplementary Figs. 1–12

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Wang, J., Huang, W., Pei, A. et al. Improving cyclability of Li metal batteries at elevated temperatures and its origin revealed by cryo-electron microscopy. Nat Energy 4, 664–670 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing