Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

High-energy lithium metal pouch cells with limited anode swelling and long stable cycles


Lithium metal anodes have attracted much attention as candidates for high-energy batteries, but there have been few reports of long cycling behaviour, and the degradation mechanism of realistic high-energy Li metal cells remains unclear. Here, we develop a prototypical 300 Wh kg−1 (1.0 Ah) pouch cell by integrating a Li metal anode, a LiNi0.6Mn0.2Co0.2O2 cathode and a compatible electrolyte. Under small uniform external pressure, the cell undergoes 200 cycles with 86% capacity retention and 83% energy retention. In the initial 50 cycles, flat Li foil converts into large Li particles that are entangled in the solid-electrolyte interphase, which leads to rapid volume expansion of the anode (cell thickening of 48%). As cycling continues, the external pressure helps the Li anode maintain good contact between the Li particles, which ensures a conducting percolation pathway for both ions and electrons, and thus the electrochemical reactions continue to occur. Accordingly, the solid Li particles evolve into a porous structure, which manifests in substantially reduced cell swelling by 19% in the subsequent 150 cycles.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Rent or buy this article

Prices vary by article type



Prices may be subject to local taxes which are calculated during checkout

Fig. 1: 300 Wh kg−1 Li metal pouch cell at 1.0 Ah level.
Fig. 2: Characterization of 300 Wh kg−1 Li||NMC622 pouch cells with two different electrolytes.
Fig. 3: Cycling of the 300 Wh kg−1 Li||NMC622 pouch cell with uniform external pressure in a compatible electrolyte.
Fig. 4: Post-cycling characterization of Li metal anodes in the 300 Wh kg−1 Li||NMC622 pouch cell, with a compatible electrolyte and uniform external pressure.
Fig. 5: Structural evolution of the Li metal anode in high-energy Li metal pouch cells.

Data availability

The data that support the plots within this paper and other findings of this study are available from the corresponding author on reasonable request.


  1. Whittingham, M. S. Ultimate limits to intercalation reactions for lithium batteries. Chem. Rev. 114, 11414–11443 (2014).

    Article  Google Scholar 

  2. Thackeray, M. M., Wolverton, C. & Isaacs, E. D. Electrical energy storage for transportation—approaching the limits of, and going beyond, lithium-ion batteries. Energy Environ. Sci. 5, 7854–7863 (2012).

    Article  Google Scholar 

  3. Pang, Q., Liang, X., Kwok, C. Y. & Nazar, L. F. Advances in lithium–sulfur batteries based on multifunctional cathodes and electrolytes. Nat. Energy 1, 16132 (2016).

    Article  Google Scholar 

  4. Lv, D. et al. High performance Li-ion sulfur batteries enabled by intercalation chemistry. Chem. Commun. 51, 13454–13457 (2015).

    Article  Google Scholar 

  5. Zhang, J.-G., Xiao, J. & Xu, W. in The Lithium Air Battery: Primary Lithium Air Batteries 1st edn (eds Imanishi, N., Luntz, A. C. & Bruce, P.) Ch.10 (Springer, 2014).

  6. Lu, D. et al. Formation of reversible solid electrolyte interface on graphite surface from concentrated electrolytes. Nano Lett. 17, 1602–1609 (2017).

    Article  Google Scholar 

  7. Liang, X. et al. A facile surface chemistry route to a stabilized lithium metal anode. Nat. Energy 2, 17119 (2017).

    Article  Google Scholar 

  8. Wu, B. et al. Interfacial behaviours between lithium ion conductors and electrode materials in various battery systems. J. Mater. Chem. A 4, 15266–15280 (2016).

    Article  Google Scholar 

  9. Wang, H. et al. A reversible dendrite-free high-areal-capacity lithium metal electrode. Nat. Commun. 8, 15106 (2017).

    Article  Google Scholar 

  10. Pan, H. et al. Non-encapsulation approach for high-performance Li–S batteries through controlled nucleation and growth. Nat. Energy 2, 813–820 (2017).

    Article  Google Scholar 

  11. Wood, K. N., Noked, M. & Dasgupta, N. P. Lithium metal anodes: toward an improved understanding of coupled morphological, electrochemical, and mechanical behavior. ACS Energy Lett. 2, 664–672 (2017).

    Article  Google Scholar 

  12. Lu, D. et al. Failure mechanism for fast-charged lithium metal batteries with liquid electrolytes. Adv. Energy Mater. 5, 1400993 (2015).

    Article  Google Scholar 

  13. Xiao, J. et al. Interplay between two-phase and solid solution reactions in high voltage spinel cathode material for lithium ion batteries. J. Power Sources 242, 736–741 (2013).

    Article  Google Scholar 

  14. Li, X. et al. Mesoporous silicon sponge as an anti-pulverization structure for high-performance lithium-ion battery anodes. Nat. Commun. 5, 4105 (2014).

    Article  Google Scholar 

  15. Kim, M. S. et al. Langmuir–Blodgett artificial solid-electrolyte interphases for practical lithium metal batteries. Nat. Energy 3, 889–898 (2018).

    Article  Google Scholar 

  16. Madec, L. et al. Effect of sulfate electrolyte additives on LiNi1/3Mn1/3Co1/3O2/graphite pouch cell lifetime: correlation between XPS surface studies and electrochemical test results. J. Phys. Chem. C 118, 29608–29622 (2014).

    Article  Google Scholar 

  17. Self, J., Aiken, C. P., Petibon, R. & Dahn, J. R. Survey of gas expansion in Li-ion NMC pouch cells. J. Electrochem. Soc. 162, A796–A802 (2015).

    Article  Google Scholar 

  18. Samba, A. et al. Impact of tab location on large format lithium-ion pouch cell based on fully coupled tree-dimensional electrochemical-thermal modeling. Electrochim. Acta 147, 319–329 (2014).

    Article  Google Scholar 

  19. Kumar, A. et al. Communication—indentation of Li-ion pouch cell: effect of material homogenization on prediction of internal short circuit. J. Electrochem. Soc. 163, A2494–A2496 (2016).

    Article  Google Scholar 

  20. Bond, T., Zhou, J. & Cutler, J. Electrode stack geometry changes during gas evolution in pouch-cell-type lithium ion batteries. J. Electrochem. Soc. 164, A6158–A6162 (2017).

    Article  Google Scholar 

  21. Cheng, X.-B. et al. The gap between long lifespan Li–S coin and pouch cells: the importance of lithium metal anode protection. Energy Storage Mater. 6, 18–25 (2017).

    Article  Google Scholar 

  22. Dixon, B., Mason, A. & Sahraei, E. Effects of electrolyte, loading rate and location of indentation on mechanical integrity of Li-ion pouch cells. J. Power Sources 396, 412–420 (2018).

    Article  Google Scholar 

  23. Hagen, M. et al. Lithium–sulfur cells: the gap between the state-of-the-art and the requirements for high energy battery cells. Adv. Energy Mater. 5, 1401986 (2015).

    Article  Google Scholar 

  24. Nelson, K. J., Harlow, J. E. & Dahn, J. R. A comparison of NMC/graphite pouch cells and commercially available LiCoO2/graphite pouch cells tested to high potential. J. Electrochem. Soc. 165, A456–A462 (2018).

    Article  Google Scholar 

  25. Genovese, M. et al. Combinatorial methods for improving lithium metal cycling efficiency. J. Electrochem. Soc. 165, A3000–A3013 (2018).

    Article  Google Scholar 

  26. Muenzel, V. et al. A comparative testing study of commercial 18650-format lithium-ion battery cells. J. Electrochem. Soc. 162, A1592–A1600 (2015).

    Article  Google Scholar 

  27. Sahraei, E., Hill, R. & Wierzbicki, T. Calibration and finite element simulation of pouch lithium-ion batteries for mechanical integrity. J. Power Sources 201, 307–321 (2012).

    Article  Google Scholar 

  28. Bai, P., Li, J., Brushett, F. R. & Bazant, M. Z. Transition of lithium growth mechanisms in liquid electrolytes. Energy Environ. Sci. 9, 3221–3229 (2016).

    Article  Google Scholar 

  29. Zhang, S. S. Problem, status, and possible solutions for lithium metal anode of rechargeable batteries. ACS Appl. Energy Mater. 1, 910–920 (2018).

    Article  Google Scholar 

  30. Xu, W. et al. Lithium metal anodes for rechargeable batteries. Energy Environ. Sci. 7, 513–537 (2014).

    Article  Google Scholar 

  31. Jiao, S. et al. Behavior of lithium metal anodes under various capacity utilization and high current density in lithium metal batteries. Joule 2, 110–124 (2018).

    Article  Google Scholar 

  32. Wu, B. et al. The role of the solid electrolyte interphase layer in preventing Li dendrite growth in solid-state batteries. Energy Environ. Sci. 11, 1803–1810 (2018).

    Article  Google Scholar 

  33. Wu, B., Lochala, J., Taverne, T. & Xiao, J. The interplay between solid electrolyte interface (SEI) and dendritic lithium growth. Nano Energy 40, 34–41 (2017).

    Article  Google Scholar 

  34. Chen, S. et al. High-efficiency lithium metal batteries with fire-retardant electrolytes. Joule 2, 1548–1558 (2018).

    Article  Google Scholar 

  35. Chen, S. et al. High-voltage lithium-metal batteries enabled by localized high-concentration electrolytes. Adv. Mater. 30, 1706102 (2018).

    Article  Google Scholar 

  36. Mussa, A. S., Klett, M., Lindbergh, G. & Lindström, R. W. Effects of external pressure on the performance and ageing of single-layer lithium-ion pouch cells. J. Power Sources 385, 18–26 (2018).

    Article  Google Scholar 

  37. Barai, P., Higa, K. & Srinivasan, V. Impact of external pressure and electrolyte transport properties on lithium dendrite growth. J. Electrochem. Soc. 165, A2654–A2666 (2018).

    Article  Google Scholar 

  38. Yin, X. et al. Insights into morphological evolution and cycling behaviour of lithium metal anode under mechanical pressure. Nano Energy 50, 659–664 (2018).

    Article  Google Scholar 

  39. Cannarella, J. & Arnold, C. B. Stress evolution and capacity fade in constrained lithium-ion pouch cells. J. Power Sources 245, 745–751 (2014).

    Article  Google Scholar 

  40. Kingery, W. D., Bowen, H. K. & Uhlmann, D. R. Introduction of Ceramics 2nd edn (Wiley, 1976).

  41. Albertus, P., Babinec, S., Litzelman, S. & Newman, A. Status and challenges in enabling the lithium metal electrode for high-energy and low-cost rechargeable batteries. Nat. Energy 3, 16–21 (2018).

    Article  Google Scholar 

  42. Monroe, C. & Newman, J. The impact of elastic deformation on deposition kinetics at lithium/polymer interfaces. J. Electrochem. Soc. 152, A396–A404 (2005).

    Article  Google Scholar 

  43. Lu, Z. et al. Nonfilling carbon coating of porous silicon micrometer-sized particles for high-performance lithium battery anodes. ACS Nano 9, 2540–2547 (2015).

    Article  Google Scholar 

Download references


This research was supported by the Assistant Secretary for Energy Efficiency and Renewable Energy, Office of Vehicle Technologies of the US Department of Energy (DoE) through the Advanced Battery Materials Research Program (Battery500 Consortium). SEM and XRD analyses were conducted in the William R. Wiley Environmental Molecular Sciences Laboratory, a national scientific user facility sponsored by the DoE's Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory (PNNL). PNNL is operated by Battelle for the DoE under contract DE-AC05-76RLO1830. We thank L. Luo, Y. He and C. Wang of the PNNL for TEM characterizations.

Author information

Authors and Affiliations



J.X. and J.L. proposed the research. C.N. assembled the pouch cells, performed the electrochemical measurements and carried out the characterizations with assistance from H.L. The compatible electrolyte was developed by S.C., W.X. and J.-G.Z. Q.L. and J.D. helped with cell assembly. M.S.W. participated in data analyses and discussion. C.N., H.L., J.X. and J.L. co-wrote the manuscript with input from all authors.

Corresponding authors

Correspondence to Jie Xiao or Jun Liu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–9

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Niu, C., Lee, H., Chen, S. et al. High-energy lithium metal pouch cells with limited anode swelling and long stable cycles. Nat Energy 4, 551–559 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing