Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Recyclable and malleable thermosets enabled by activating dormant dynamic linkages


Chemical recycling of polymers is critical for improving the circular economy of plastics and environmental sustainability. Traditional thermoset polymers have generally been considered permanently crosslinked materials that are difficult or impossible to recycle. Herein, we demonstrate that by activating ‘dormant’ covalent bonds, traditional polycyanurate thermosets can be recycled into the original monomers, which can be circularly reused for their original purpose. Through retrosynthetic analysis, we redirected the synthetic route from forming conventional C–N bonds via irreversible cyanate trimerization to forming the C–O bonds through reversible nucleophilic aromatic substitution of alkoxy-substituted triazine derivatives by alcohol nucleophiles. The new reversible synthetic route enabled the synthesis of previously inaccessible alkyl-polycyanurate thermosets, which exhibit excellent film properties with high chemical resistance, closed-loop recyclability and reprocessing capability. These results show that ‘apparently dormant’ dynamic linkages can be activated and utilized to construct fully recyclable thermoset polymers with a broader monomer scope and increased sustainability.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Synthetic strategies of polymers.
Fig. 2: SNAr in cyanurate exchange reactions.
Fig. 3: Preparation and characterization of PCNs.
Fig. 4: Chemical recycling of PCNs.

Similar content being viewed by others

Data availability

Data supporting the findings of this study are included in the Article and its Supplementary Information. Data are also available upon request. Source data are provided with this paper.


  1. Geyer, R., Jambeck, J. R. & Law, K. L. Production, use, and fate of all plastics ever made. Sci. Adv. 3, e1700782 (2017).

    Article  Google Scholar 

  2. MacLeod, M., Arp, H. P. H., Tekman, M. B. & Jahnke, A. The global threat from plastic pollution. Science 373, 61–65 (2021).

    Article  CAS  Google Scholar 

  3. Garcia, J. M. & Robertson, M. L. The future of plastics recycling. Science 358, 870–872 (2017).

    Article  CAS  Google Scholar 

  4. Ragaert, K., Delva, L. & Van Geem, K. Mechanical and chemical recycling of solid plastic waste. Waste Manage. 69, 24–58 (2017).

    Article  CAS  Google Scholar 

  5. Eagan, J. M. et al. Combining polyethylene and polypropylene: enhanced performance with PE/iPP multiblock polymers. Science 355, 814–816 (2017).

    Article  CAS  Google Scholar 

  6. Coates, G. W. & Getzler, Y. D. Y. L. Chemical recycling to monomer for an ideal, circular polymer economy. Nat. Rev. Mater. 5, 501–516 (2020).

    Article  CAS  Google Scholar 

  7. Vollmer, I. et al. Beyond mechanical recycling: giving new life to plastic waste. Angew. Chem. Int. Ed. 59, 15402–15423 (2020).

    Article  CAS  Google Scholar 

  8. Korley, L. T. J., Epps, T. H. III, Helms, B. A. & Ryan, A. J. Toward polymer upcycling—adding value and tackling circularity. Science 373, 66–69 (2021).

    Article  CAS  Google Scholar 

  9. Zhu, J.-B., Watson, E. M., Tang, J. & Chen, E. Y.-X. A synthetic polymer system with repeatable chemical recyclability. Science 360, 398–403 (2018).

    Article  CAS  Google Scholar 

  10. Christensen, P. R., Scheuermann, A. M., Loeffler, K. E. & Helms, B. A. Closed-loop recycling of plastics enabled by dynamic covalent diketoenamine bonds. Nat. Chem. 11, 442–448 (2019).

    Article  CAS  Google Scholar 

  11. Abel, B. A., Snyder, R. L. & Coates, G. W. Chemically recyclable thermoplastics from reversible-deactivation polymerization of cyclic acetals. Science 373, 783–789 (2021).

    Article  CAS  Google Scholar 

  12. Haussler, M., Eck, M., Rothauer, D. & Mecking, S. Closed-loop recycling of polyethylene-like materials. Nature 590, 423–427 (2021).

    Article  Google Scholar 

  13. Mohadjer Beromi, M. et al. Iron-catalysed synthesis and chemical recycling of telechelic 1,3-enchained oligocyclobutanes. Nat. Chem. 13, 156–162 (2021).

    Article  CAS  Google Scholar 

  14. Sathe, D. et al. Olefin metathesis-based chemically recyclable polymers enabled by fused-ring monomers. Nat. Chem. 13, 743–750 (2021).

    Article  CAS  Google Scholar 

  15. Shieh, P. et al. Cleavable comonomers enable degradable, recyclable thermoset plastics. Nature 583, 542–547 (2020).

    Article  CAS  Google Scholar 

  16. Jin, Y., Yu, C., Denman, R. J. & Zhang, W. Recent advances in dynamic covalent chemistry. Chem. Soc. Rev. 42, 6634–6654 (2013).

    Article  CAS  Google Scholar 

  17. Kloxin, C. J. & Bowman, C. N. Covalent adaptable networks: smart, reconfigurable and responsive network systems. Chem. Soc. Rev. 42, 7161–7173 (2013).

    Article  CAS  Google Scholar 

  18. Denissen, W., Winne, J. M. & Du Prez, F. E. Vitrimers: permanent organic networks with glass-like fluidity. Chem. Sci. 7, 30–38 (2016).

    Article  CAS  Google Scholar 

  19. Fortman, D. J. et al. Approaches to sustainable and continually recyclable cross-linked polymers. ACS Sustain. Chem. Eng. 6, 11145–11159 (2018).

    Article  CAS  Google Scholar 

  20. Jin, Y., Lei, Z., Taynton, P., Huang, S. & Zhang, W. Malleable and recyclable thermosets: the next generation of plastics. Matter 1, 1456–1493 (2019).

    Article  Google Scholar 

  21. Garcia, J. M. et al. Recyclable, strong thermosets and organogels via paraformaldehyde condensation with diamines. Science 344, 732–735 (2014).

    Article  CAS  Google Scholar 

  22. Taynton, P. et al. Heat- or water-driven malleability in a highly recyclable covalent network polymer. Adv. Mater. 26, 3938–3942 (2014).

    Article  CAS  Google Scholar 

  23. Montarnal, D., Capelot, M., Tournilhac, F. & Leibler, L. Silica-like malleable materials from permanent organic networks. Science 334, 965–968 (2011).

    Article  CAS  Google Scholar 

  24. Röttger, M. et al. High-performance vitrimers from commodity thermoplastics through dioxaborolane metathesis. Science 356, 62–65 (2017).

    Article  Google Scholar 

  25. Cash, J. J., Kubo, T., Bapat, A. P. & Sumerlin, B. S. Room-temperature self-healing polymers based on dynamic-covalent boronic esters. Macromolecules 48, 2098–2106 (2015).

    Article  CAS  Google Scholar 

  26. Denissen, W. et al. Vinylogous urethane vitrimers. Adv. Funct. Mater. 25, 2451–2457 (2015).

    Article  CAS  Google Scholar 

  27. Fortman, D. J., Brutman, J. P., Cramer, C. J., Hillmyer, M. A. & Dichtel, W. R. Mechanically activated, catalyst-free polyhydroxyurethane vitrimers. J. Am. Chem. Soc. 137, 14019–14022 (2015).

    Article  CAS  Google Scholar 

  28. Nishimura, Y., Chung, J., Muradyan, H. & Guan, Z. Silyl ether as a robust and thermally stable dynamic covalent motif for malleable polymer design. J. Am. Chem. Soc. 139, 14881–14884 (2017).

    Article  CAS  Google Scholar 

  29. Yue, L., Amirkhosravi, M., Gong, X., Gray, T. G. & Manas-Zloczower, I. Recycling epoxy by vitrimerization: influence of an initial thermoset chemical structure. ACS Sustain. Chem. Eng. 8, 12706–12712 (2020).

    Article  CAS  Google Scholar 

  30. Yang, H., Jin, Y., Du, Y. & Zhang, W. Application of alkyne metathesis in polymer synthesis. J. Mater. Chem. A 2, 5986–5993 (2014).

    Article  CAS  Google Scholar 

  31. Gross, D. E., Discekici, E. & Moore, J. S. Macrocyclic depolymerization of arylene-ethynylene copolymers: a dynamic combinatorial method. Chem. Commun. 48, 4426–4428 (2012).

    Article  CAS  Google Scholar 

  32. Ramdani, N., Zaimeche, H. & Derradji, M. Biobased thermally-stable aromatic cyanate ester thermosets: a review. React. Funct. Polym. 168, 105037 (2021).

    Article  CAS  Google Scholar 

  33. Kandelbauer, A. in Handbook of Thermoset Plastics 3rd edn (eds Dodiuk, H. & Goodman, S. H.) 425–457 (William Andrew Publishing, 2014).

  34. Hamerton, I. Chemistry and Technology of Cyanate Ester Resins (Springer, 1994).

  35. Söthje, D., Dreyer, C. & Bauer, M. Advanced Possibilities in Thermoset Recycling in Thermosets 2013 From Monomers to Components Proceedings of the 3rd International Conference on Thermosets, 18–20 September 2013, Berlin, Germany (Fraunhofer Research Institution for Polymeric Materials and Composites PYCO, 2013).

  36. Söthje, D., Bauer, M. & Dreyer, C. Process for reutilization of recycled polycyanurate-containing materials in new polymeric materials. International patent, EP2885338A1 (2014).

  37. Dreyer, C. & Dominik, S. Progress in recycling of composites with polycyanurate matrix. Adv. Chem. Eng. Sci. 4, 167–183 (2014).

  38. Fainleib, A. M., Hourston, D. J., Grigoryeva, O. P., Shantalii, T. A. & Sergeeva, L. M. Structure development in aromatic polycyanurate networks modified with hydroxyl-terminated polyethers. Polymer 42, 8361–8372 (2001).

    Article  CAS  Google Scholar 

  39. Rohrbach, S. et al. Concerted nucleophilic aromatic substitution reactions. Angew. Chem. Int. Ed. 58, 16368–16388 (2019).

    Article  CAS  Google Scholar 

  40. Ong, W. J. & Swager, T. M. Dynamic self-correcting nucleophilic aromatic substitution. Nat. Chem. 10, 1023–1030 (2018).

    Article  CAS  Google Scholar 

  41. Jin, Y. & Zhang, W. SNAr stands corrected. Nat. Chem. 10, 996–998 (2018).

    Article  CAS  Google Scholar 

  42. Armarego, W. L. F. Purification of Laboratory Chemicals 148 (Elsevier Science, 2017).

Download references


We thank D. Walba for the help with differential scanning calorimetry characterization. We acknowledge Colorado State University Analytical Resources Core (RRID SCR_021758) for gas chromatography–mass spectrometry and thermogravimetric analysis characterizations. K.Y. acknowledges the support from the National Science Foundation (grant CMMI-1901807). W.Z. acknowledges the support from University of Colorado Boulder.

Author information

Authors and Affiliations



Z.L. and W.Z. conceived the concept and led the project. Z.L., H.C. and Y.R. performed the small-molecule model study, polymer synthesis, characterization and recycling. C.L. performed the dynamic mechanical analysis. Y.H. performed the differential scanning calorimetry tests. Z.L., Y.J. and W.Z. wrote the manuscript. All authors discussed and revised the manuscript.

Corresponding author

Correspondence to Wei Zhang.

Ethics declarations

Competing interests

Z.L. and W.Z. are coinventors on a provisional US patent covering the methods of polymerization and composition of matter presented in this work, filed through the University of Colorado Boulder (application no. 63/354,754). The other authors declare no competing interests.

Peer review

Peer review information

Nature Chemistry thanks the anonymous reviewers for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data

Extended Data Fig. 1 Small molecule study of cyanurate exchange.

a, No reaction between TETA and methanol was observed without TBD catalyst. b, The first step of exchange reaction between TETA and deuterated methanol can be considered as an irreversible pseudo first-order reaction when the deuterated methanol is used as solvent.

Extended Data Fig. 2 FTIR comparison.

a, FTIR spectra of PCN-A4 film and its corresponding monomers. b, FTIR spectra of PCN-A6 film and its corresponding monomers. c, FTIR spectra of PCN-A12 film and its corresponding monomers.

Extended Data Fig. 3 Chemical resistance test of PCN films.

a, Chemical resistance test for PCN-A4 film. b, Chemical resistance test for PCN-A6 film. c, Chemical resistance test for PCN-A12 film. The PCN films were cut into the rectangular shape and submerged in different solutions (1 M HCl, 1 M NaOH, 30% H2O2 and 1 M NaBH4); the top, middle and bottom photos were taken before submerging, after 48-hour submerging, and after drying, respectively. No change in appearance was observed for all the PCN films.

Extended Data Fig. 4 Chemical recycling of PCN-A12.

a, 1H-NMR spectra show that the film degradation in ethanol is clean (TMB, 1,3,5-trimethoxybenzene, used as internal standard) and the recycled DO-12 and TETA are in high purity. b, Nearly identical loss factors for the original and recycled PCN-A12 samples. c, Nearly identical FTIR spectra of the original and recycled PCN-A12 samples.

Extended Data Fig. 5 Chemical recycling of PCN-A4.

a, 1H-NMR spectra show that the film degradation in ethanol is clean (TMB used as internal standard). and the recycled TETA is in high purity. b, Nearly identical loss factors for the original and recycled PCN-A4 samples. c, Nearly identical FTIR spectra of the original and recycled PCN-A4 samples.

Extended Data Fig. 6 Chemical recycling of PCN-A6.

a, 1H-NMR spectra show that the film degradation in ethanol is clean (TMB used as internal standard) and the recycled TETA is in high purity. b, Neary identical loss factor for the original and recycled PCN-A6 samples. c, Nearly identical FTIR spectra of the original and recycled PCN-A6 samples.

Extended Data Fig. 7 Kinetic study of cyanurate exchange in polymer.

a, Bond exchange reaction can be triggered under heat in the presence of 23 mol% excess of diol monomers and 10 mol% of TBD. b, Stress relaxation test of PCN-A6-m at various temperatures. c, Arrhenius plot and its linear fitting. The activation energy was calculated to be 76.7 kJ/mol.

Supplementary information

Supplementary Information

Supplementary Figs. 1–26, Tables 1–5 and Discussion.

Source data

Source Data Fig. 2

Concentration data points.

Rights and permissions

Springer Nature or its licensor holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Lei, Z., Chen, H., Luo, C. et al. Recyclable and malleable thermosets enabled by activating dormant dynamic linkages. Nat. Chem. 14, 1399–1404 (2022).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing