Abstract
A series of electrochemical tests combined with the techniques of scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and X-ray photoelectron spectroscopy (XPS) were used to study the effect of nitrogen content on the composition, structure and protectiveness of passive films, which were formed on the surfaces of high-nitrogen austenitic stainless steels (HNSS) in 0.5 mol/L NaCl solution. The results showed that the HNSS with higher nitrogen content had a larger proportion of low-angle grain boundaries, and it also had a lower corrosion current density in 0.5 mol/L NaCl solution and thus a lower corrosion rate. The existence of a larger proportion of stable oxides (e.g., Cr2O3) in the passive films facilitates the passivation/repassivation process and contributes to the high corrosion resistance of HNSS.
Similar content being viewed by others
Introduction
Generally, austenitic stainless steel (ASS) has good corrosion resistance in service environments1,2,3,4 and mechanical properties5,6. Due to its stable and uniform austenitic structure, it has been widely used in pipeline transportation, construction and chemical industries, and other fields7. Without the sacrifice of the corrosion performance and mechanical properties of the ASS, the replacement of Ni with other alloying elements (e.g., nitrogen (N) and manganese (Mn)) has been considered to lower the cost. On the other hand, the minimum usage of Ni can also be beneficial to the saving of global natural resources. Recent work showed that austenitic stabilizing elements like N and Mn can be used as substitutes8,9,10. This facilitates the design and development of ASS possessing a high content of Mn, N, or Cr element and having a low cost11,12,13,14, which is considered to be one of the important candidates to replace ASS with a high Ni content (i.e., 8–10 wt.%)15. Previous work16 showed that the addition of alloying element N into ASSs would decrease a tendency of pitting corrosion in chloride solutions. This is attributed to the improvement in the protective ability of the passive film formed on the surface of ASS17.
Many studies showed that the corrosion performance of the ASS is closely related to the N content and the existence status of nitrogen (i.e., whether N is bonding with other elements (i.e., Cr) to form intermetallic nitride). When the N content is low (i.e., less than 0.3 wt.%), the corrosion resistance of ASSs is relatively inferior. Because of the low N content, the number of the CxN phase in ASS is reduced, triggering that a dense nitride film could barely be formed on the surface18. When the N content is higher than 0.4 wt.%, the corrosion properties of ASS will be significantly improved19. For ASSs with high N content, a dense nitride layer could form on the surface. It prevents the oxide film from peeling and has higher corrosion resistance. Therefore, the addition of N in ASSs with high corrosion resistance and low cost has attracted widespread attention and gained great favor20.
As a trace element, N can significantly improve the corrosion resistance of ASS. The N atoms are much smaller in size than the Cr atoms; thus, they can penetrate into the lattice more easily, forming stable nitrides (Cr2N). The presence of nitrides can deteriorate the corrosion of stainless steel in corrosive media, thereby improving its corrosion resistance. It is reported that the addition of N in the Mn-containing ASS promotes the formation of austenite, expands the composition or temperature range of the austenitic phase and thus inhibits the formation of ferrite21,22,23. Moreover, N is beneficial to the refinement of the austenitic grains24,25,26 and the mechanical properties of ASS. On the other hand, the N-alloying can improve the resistance to localized corrosion, especially the pitting and intergranular corrosion. The results obtained by Mudali et al.27 showed that increasing the N content in austenitic stainless steel decreased the passive current density, expanded the passive potential range and increased the resistance to intergranular corrosion. The addition of Mn in ASS can strengthen the austenitic lattice, inhibit the formation of residual austenite and increase the stability of ASS. But the study of Toor et al.28 showed that the addition of Mn can deteriorate the corrosion resistance of ASS by lowering the pitting potential and triggering metastable pitting events. It suggests that the addition of a certain content of Mn into austenitic stainless steel has an adverse effect on its corrosion performance. Adding a certain content of Mn into austenitic stainless steel promotes the formation of MnS inclusions, which were preferentially attacked or/and dissolved in the corrosive media, leading to the occurrence of localized corrosion29. Adding an appropriate content of N (i.e., larger than 0.5 wt.%) can not only reduce the grain size and increase the density of Σ3 grain boundaries but also enhance the passivation/repassivation ability and hence promote the resistance to intergranular corrosion and stress cracking corrosion30. Even if severe pitting corrosion with “lace cover” features occurred, the increase of N content to stainless steel could evoke the passivation/repassivation process and increase the pitting corrosion resistance31,32. Therefore, further investigation needs to be conducted to address the effect of N (with the content exceeding 0.5 wt.%) on the passive behaviors of the modified stainless steels, with Ni completely replaced with Mn and N, and the evolution of the composition and structure of the passive films. These studies will help to better understand how Mn and N synergistically function to the formation of a protective layer on the surface of austenitic stainless steel, which can effectively suppress the occurrence of localized corrosion (e.g., intergranular corrosion and stress cracking corrosion33). These would eventually be beneficial to obtain the optimizing contents of Mn and N in ASS with promising mechanical properties and good corrosion resistance.
In this study, the corrosion behaviors of the HNSS containing ~20 wt.% Mn and various N contents in 0.5 mol/L NaCl solution were investigated by electrochemical impedance spectroscopy, potentiodynamic polarization, scanning electron microscopy and electron backscatter diffraction. In order to evaluate the protective ability of the passive films and characterize the compositions, potentiostatic polarization, Mott-Schottky curve and X-ray photoelectron spectroscopy (XPS) were performed. The aim of the present work was to investigate the effect of N content on the composition and structure of the passive films formed on the surface of the HNSS containing a high Mn content (i.e., 20 wt.%) and influenced its passivation/repassivation process, and to provide guidance on the design of the HNSS with higher corrosion resistance and low cost.
Results and discussion
Microstructural features
Figure 1 shows the XRD patterns of the two HNSSs and 316 stainless steel (SS). As seen in Fig. 1a, the diffraction peaks correspond to the γ phase with an FCC structure (standard card number 52-0512), mainly including γ(111), γ(200), γ(220) and γ(311). However, a difference exists in peak position and peak intensity, as shown in Fig. 1b. Compared with the result of the 316 SS, the γ(111) diffraction peaks of the HNSS1 and HNSS2 slightly shift to a lower angle. It might be relevant to the differences in the contents of alloying elements in these alloys since the incorporation of the alloying element having a smaller or larger atomic radius would result in the atomic arrangement, leading to lattice distortion34. Fujii et al.35 reported that only a small amount of Mn addition increased the f.c.c. lattice constant of CoCrCuFeMnxNi because Mn has a large atomic radius. The slightly higher Mn content in the HNSS2 would lead to the shift of the characteristic peak to a lower angle.
Figure 2 presents the microstructure of the two HNSSs. Both of them exhibited a single austenitic phase with twins located inside the austenitic grains. It is clear that the grain size of the HNSS1 (~23.3 μm) is larger than that of the HNSS2 (~8.8 μm). Plenty of voids can be observed inside and at the grain boundaries in the HNSS2, with white inclusions remaining in the voids, as shown in Fig. 2c, d. The inclusions were analyzed using EDS, and the results are shown in Fig. 2e. These inclusions mainly consist of Cr, Fe, Mn, Mo, O and C. It can be inferred that these inclusions are carbides and oxides, which may be produced during the smelting process17. It is consistent with the results reported by Qin et al.36 that ASS with an N content higher than 0.3 wt.% is prone to produce carbide and oxide inclusions during the smelting process37,38,39. These inclusions are unable to be detected by XRD because of their low contents. The precipitation of carbide and oxide inclusions on the corrosion properties of the HNSS2 will be detailed discussed in the latter.
The microstructure of 316 SS was characterized and presented in Fig. 3. In Fig. 3a, 316 SS has a granular structure composed of equiaxed austenitic grains with twins distributing inside austenitic grains38,39. Compared to the HNSS1 and HNSS2, these austenitic grains are smaller (Fig. 3b), with an average grain size of 6.1 μm.
EBSD analysis
Figure 4a, b shows the IPF diagrams of the two HNSSs. It can be clearly seen that the HNSS1 is mostly composed of regular polygonal austenitic grains, but the HNSS2 consists of irregular austenitic grains. The grain size distribution results of these two HNSSs are quite different from each other. As shown in Fig. 4c, over 90% of the grains in the HNSS1 possess a grain size smaller than 15 μm, while the grains in the HNSS2 are generally coarse, with the grain size ranges from 5 to 70 μm, as shown in Fig. 4d. The larger proportion of smaller grains with the size smaller than 15 μm is correlated with the increase in content of N, which facilitates the occurrence of partial recrystallization40. The grain size difference might lead to the difference in corrosion performance for these two HNSSs.
Figure 4e, f provides Kernel average misorientation diagrams of the two HNSSs. It is clear that there are almost no residual strains in the HNSS1, but there are some residual strains distributing along the grain boundaries, especially at the places where recrystallization occurred. Although the austenitic grains are much less uniform in the HNSS2 than in the HNSS1, but the proportion of small angle grain boundary (<10°) in the HNSS2 is much higher, as shown in Fig. 4g, h. The dislocation density of the HNSS1 is smaller than that of the HNSS2 due to the presence of a larger angle grain boundary which can absorb dislocation energy and reduce dislocation density. An41 reported that the large-angle grain boundary is easy to absorb lattice defects. In addition, the small angle boundary will inhibit the low energy segment connected by the large-angle grain boundary network and prevent the corrosion crack from expanding with the high-angle grain boundary42, and thus decrease the corrosion tendency.
Electrochemical tests
Figure 5a shows the potentiodynamic polarization of the two HNSSs in 0.5 mol/L NaCl solution. The two HNSSs exhibited a spontaneous passivation behavior, but the passive potential range of the HNSS1 was narrower than that of the HNSS2. A sudden increase of current density was observed at 0.05 VSCE for the HNSS1, indicating the breakdown of passive film and the occurrence of pitting corrosion. The enlarged view of Fig. 5a, as shown in Fig. 5b, presents current density fluctuations, indicating the initiation and repassivation of metastable pitting. This corrosion feature is frequently observed in potentiodynamic polarization curves of N-containing stainless steels in NaCl solutions43. In contrast, the HNSS2 had a higher pitting corrosion resistance with a wide passive region ranging from about −0.1 to 1.05 VSCE. Different from HNSS1, HNSS2 has a broader passive potential range up to ~1.05 VSCE. No current fluctuations can be observed in the potentiodynamic polarization curve of the HNSS2. The electrochemical parameters derived from polarization curves, including the corrosion potential (Ecorr), corrosion current density (icorr) and pitting potential (Ep), are shown in Table 1. It can be seen that the Ecorr of the HNSS2 was 70 mV higher than that of the HNSS1. The icorr of HNSS1 was 5.77 × 10−8 A cm−2, and the icorr of HNSS2 was 4.77 × 10−8 A cm−2. It suggests that the increase of N content improved the pitting resistance of HNSS and is consistent with the results reported by the available literature21,44.
The surface morphologies of the two HNSSs after the potentiodynamic polarization measurements are shown in Fig. 6. From Fig. 6a, a1, c, and c1, the corrosion pits appeared on the surface of both two materials. The number of corrosion pits is much larger for the HNSS1. It can be seen that the HNSS2 has a higher resistance to pitting corrosion. Figure 6b shows that pitting occurring on the surface of HNSS1 has a feature of lacy cover because the oxide inclusions at the surface provide initiation sites for the pits, and the detachment of the inclusions provides positions for the stagnation of the chloride solution, leading to the growth of the pits and the appearance of the lace covers45. Similarly, plenty of dense pits were also observed on the surface of HNSS2 in Fig. 6d. There are some minor defects on the surface of HNSS, including casting defects, which can promote the formation of corrosion pits.
Electrochemical impedance spectroscopy (EIS) measurements of HNSS1 and HNSS2 were performed and shown in Fig. 7. From Fig. 7a, the semi-capacitive arcs of the two steels appear in the Nyquist plots, suggesting the domination of a similar corrosion mechanism46,47. This characteristic was similar to the results of Fe-18Cr-15Mn-0.66 N48 and Fe-18Cr-15Mn-2Mo-0.66 N49 in a 3.5% NaCl solution. The capacitive arc radius of HNSS1 was smaller than that of HNSS2, suggesting the better corrosion resistance of the HNSS250. These results were in accordance with the corrosion behavior results of Fe-20Cr-20Mn-2.2Mo42 alloy in NaCl solution, which showed that increasing the nitrogen content enhanced the protectiveness of the passive film effectively.
In Bode plots (Fig. 7b), phase angles were close to 0° at the frequency of 104 Hz for both HNSSs, indicating that the impedance was solution resistance51. At the frequency region between 0.1 to 100 Hz, phase angles were close to 80°, suggesting the formation of stable and dense passive films52. At the lowest frequency limit (namely 10−2 Hz), the impedance resistance of HNSS2 was larger than that of HNSS1, indicating that HNSS2 had a higher corrosion resistance. It is in accordance with the potentiodynamic polarization results.
The equivalent circuit used to fitting the EIS spectra in Fig. 7 is shown in Fig. 8. In which Rs is solution resistance, Rf is the resistance of passive film, and CPE is constant phase element representing the capacitance of passive film53. CPE can be described using two parameters: Q and n, where Q is a constant, and n is a variable parameter ranging from 0 to 1 (n = 1 means the CPE is a pure capacitor, while n = 0 means it is a pure resistance54). EIS fitting results were presented in Table 2, yielding that the values of polarization resistance (Rp) were the values of film resistance (Rf). The reciprocal of Rp is proportional to the corrosion rate. At a higher N content, the Rp value was larger, indicating a higher protective ability of passive film and a lower corrosion rate55. It is in accordance with the results conducted by Wu et al.56 that the addition of N improved the stability of passive film and thus enhanced the passivation of austenitic steel.
The thickness of passive film can be calculated using the equations written below:
in which C0 is the capacitance of passive film, Rp is polarization resistance and ε the dielectric constant (15.6 for stainless steel57), ε0 is the dielectric constant of vacuum (8.85 × 10−14 F cm−1), A is the area of the sample, and dox is the thickness of passive film. Although HNSS2 had higher corrosion resistance than HNSS1, the thickness of the passive film was close to each other. The thickness of passive film on the surface of HNSS1 and HNSS2 was 12.7 nm and 13.5 nm, respectively.
Potentiostatic polarization tests
On the basis of the potentiodynamic polarization measurements in Fig. 5, both austenitic steels will be passive at an applied potential of −50 mVSCE. To form a layer of passive film on the surfaces of two HNSSs and to investigate their passivation behavior, potentiostatic polarization tests were performed at this potential for 1 h in 0.5 mol/L NaCl solution. The response of current density (i) with time (t) was plotted in Fig. 9a. It is clear that rapid nucleation and growth of passive films led to the dramatic decrease of the current densities at the initial stage (i.e., ≤300 s). As the duration of exposure time increased, the current densities gradually decreased and tended to stabilize at ~10−7 A cm−2, indicating the formation of stable passive films. From Fig. 9a, it can be seen that the steady-state current density value of HNSS1 is 1.11 × 10−7A cm−2, and the steady-state current density value of HNSS2 is 1.52 × 10−7A cm−2. Lu et al.58 found that the lower the current density, the more stable the passive film is. Therefore, the passive film formed on the surface of HNSS2 is more stable and has a higher protective ability on the substrate than HNSS1.
The relationship between i and t can be described as below:
where A is a constant. k represents the growth rate of the passive film46. Figure 9b shows the log i-log t plots of two steels. According to the ref. 59, the growth of the passive film is controlled by electric field. As shown in Fig. 8b, the k values of HNSS1 and HNSS2 were −0.15 and −0.12 at the initial stage (less than 40 s), suggesting that the films formed on these two HNSSs were similar to each other. With the increase of the exposure time, both k values decreased to −0.87 (for the HNSS1) and −0.90 (for the HNSS2). It indicates that passive films formed under these conditions were compact and dense. A lower k value for HNSS2 suggests that the passive film was denser and more compact than the HNSS1 and also had a faster formation rate. The current transient during potentiostatic polarization reflects the initiation and annihilation of the metastable pitting corrosion. There are two types of current transient for the HNSS1, as shown in Fig. 10. The first one showed that the current density increased quickly in 3 s and then decayed rapidly due to the repassivation process (Fig. 10a), while the other was that the current density surged owing to initially to nucleate the metastable pit, then partially decayed since the initiated metastable pit attempted to re-passive60, rose again due to the incomplete repassivation and the propagation of the metastable pit61, and finally decreased as a consequence of repassivation of the metastable pitting (Fig. 10b). As for the HNSS2, the current density exhibits a transient surge suggesting the event of occurrence metastable pitting, then symmetrically subside to the background due to the repassivation of passive film62, as shown in Fig. 10c.
Nucleation mechanism of the passive film
For passive films with semiconducting properties, such as Fe, Ni, etc., the nucleation and growth processes determined the permeation speed of point defects through the film, which affects the properties of the passive film63. Figure 11a shows potentiostatic polarization curves of two HNSSs at −0.05 VSCE. The current rises in the initial stage of the curve owing to the electrode system to the voltage and then gradually decreases in the response of the nucleation of passive film. Compared with HNSS1, the current transient of HNSS2 drops faster, implying that the passive film of HNSS2 is better than that of HNSS164. The transient current-time curves obtained from the experiment are transformed accordingly and then compared with the two standard nucleation theory model curves.
where jm and tm were the current density and time corresponding to the peak position of the curve obtained from the experiment, respectively.
As shown in Fig. 11b, c, the nucleation mechanisms of passive films of HNSS1 and HNSS2 are consistent with the theoretical curves of continuous nucleation. This suggested that the nucleation mechanism of the two HNSSs complies with the continuous nucleation mechanism. In Fig. 11, HNSS2 is closer to transient nucleation as compared to HNSS1, showing that the active sites on the surface of HNSS2 are rapidly activated during potentiostatic polarization process65, which is conducive to the accelerated formation of passive films.
Mott-Schottky analysis
The density of defect or carrier present in passive film is one of the important factors influencing the corrosion performance of passive materials in environments. It can be characterized by the measurement of capacitance (CSC) of the space charge layer as a function of applied potential (E).
Mott-Schottky equations are usually used to describe the correlation of capacitance of the space charge layer with applied potential, which is given for n-type/p-type semiconductor as follows66:
where ɛ is the dielectric constant of passive film, ɛ0 is vacuum permissivity constant (8.854 × 10−14 F·cm−1), e is electron charge (1.6021 × 10−19 C), ND and NA are donor and acceptor density, respectively, Efb is flat-band potential, k is Boltzmann constant (1.38 × 10−23 J·K−1), and T is temperature (K).
Figure 12 shows Mott-Schottky curves of two HNSSs in 0.5 mol/L NaCl solution. It can be said that the Mott-Schottky curves had the feature of an n-p type semiconductor. The slopes of the linear parts in region I and region II were fitted to calculate the donor and acceptor densities in passive film. As is seen in Table 3, the donor density in passive film in region I for HNSS1 and HNSS2 was 1.09 × 1021 cm−3 and 0.85 × 1021 cm−3, respectively. The acceptor density in region II was 2.55 × 1021 cm−3 and 2.24 × 1021 cm−3, respectively. The lower donor/acceptor density in passive film formed on the surface of HNSS2 suggests higher corrosion resistance.
Passive film characterization
Figure 13 shows the XPS spectra of passive films formed on the surfaces of the two HNSSs. The results showed that passive films were composed of Fe, Mn, Cr, O, N and C elements. Although nitrogen contents were different in these two HNSSs, the similar peak intensities of these elements showed that the contents of these elements present in passive films were similar. Figure 14a, b shows Fe 2p3/2 high-resolution XPS for passive films formed on the surfaces of the two HNSSs. Both of the two spectra are comprised of peaks of metallic Fe0 (707.8 eV), Fe3O4 (708.9 eV), Fe2O3 (710.4 eV) and FeOOH (712.3 eV)67. The fraction of these substances can be obtained by XPS fitting, as shown in Fig. 15a. It is shown that the fraction of metallic Fe0 in HNSS2 is less than that in HNSS1, while the fraction of Fe3O4, Fe2O3 and FeOOH in HNSS2 is higher. It seemed that higher N may induce the formation of a higher proportion of FexOy in passive film, which enhances the protective ability of passive film and increases corrosion resistance. Feng68 found that with the increase of N content, the fraction of Fe3O4 and Fe2O3 gradually increased, the fraction of metallic Fe0 decreased, the defect concentration of passive film was low, and the protection performance was better.
Figure 14c and d are Cr 2p3/2 spectra for passive films formed on the surfaces of the two HNSSs. The peaks can be identified as metallic Cr0 (574.2 eV), Cr2O3 (576.1 eV) and Cr(OH)3 (578.1 eV). The content of metallic Cr0 and Cr(OH)3 in HNSS1 is low, while the fraction of Cr2O3 in HNSS2 is high, as shown in Fig. 15b. The Cr2O3/Cr(OH)3 value of HNSS1 is 0.81, while that of HNSS2 surface increased to 0.99. Compared with Cr(OH)3, the Cr2O3 has lower point defect density and higher thermodynamic stability. Li et al.69 reported that the higher the fraction of Cr2O3 in passive film, the stronger the protective ability. Therefore, the higher the Cr2O3/Cr(OH)3 value of HNSS2, the passive film on the surface of HNSS2 (with higher N) exhibited higher stability and good protection ability.
Figure 14e, f are N 1s spectra for passive films formed on the surfaces of the two HNSSs. There are three forms of N element in the passive film, free nitrogen N0 (398.6 eV), NH3 (399.8 eV) and NH4+ (400.8 eV). Sun et al.70 reported that the adsorption of NH3 on the surface of ASS can improve the stability of the passive film. The findings of Wang et al.71 also showed that the presence of NH4+ and NH3 originate from the dissolving of N, the formation of NH4+ and NH3 can consume the H+, which could promote the repassivation of metastable pits. As shown in Fig. 15c, the NH4+ content of HNSS2 is higher than that of HNSS1, which suggests that the higher N may effectively inhibit the breakdown of passive film and the occurrence of pitting corrosion.
Figure 14g, h are O 1s spectra for passive films formed on HNSS1 and HNSS2. The results showed that the O element in the passive film is composed of O2− (530.2 eV), OH− (532 eV) and H2O (533.6 eV). The existence of O2− and OH− in the passive film corresponded to metallic oxide and metallic hydroxide, respectively. Figure 15d shows the ratio of O2−/OH− in of the XPS fitting result for HNSS2 is 0.64, and for HNSS1 is 0.49. Accordingly, the higher ratio of HNSS2 corresponds to the less serious risk of pitting corrosion. Vignal et al.72 found that with a significant increase in the O2−/OH− ratio, oxide on the surface of passive film formed on the austenite increased, and the passivity of metal was strengthened, which hindered the corrosion rate.
Corrosion mechanism
The corrosion resistance of stainless steel depends on the Cr, which is in the form of Cr2O3 on its surface, to ensure that the protective oxide film is self-healing. When the passive film is destroyed by corrosive ions such as Cl−, there is enough Cr3+ to reform the film. Based on the results obtained, the corrosion mechanism of HNSS in 0.5 mol/L NaCl solution is proposed and is shown in Fig. 16. As shown in Fig. 16, in the Cl− containing environment, the preferential adsorption of Cl− on the surface of HNSS passive film could extruding oxygen atoms, and combining with Fe2+ in the passive film to form soluble chloride, resulting in small corrosion pits. In serious cases, there will be a “lace cover”. The presence of Cl− directly destroys the passive state of stainless steel. Pitting refers to the localized occurrence of small pits with a certain depth on the surface of HNSS in corrosive environments, which are prone to occur in areas such as oxygen carbide inclusions, secondary phases, grain boundaries, and defects. The published works indicated that the N in metallic material can promote the pitting resistance of HNSS16,17. The preferential enrichment of N due to the anodic segregation could inhibit the dissolution of the matrix and improve the passivity of HNSSs. During the corrosion reaction process, N dissolution easily forms NH3 or \({{\rm{NH}}}_{4}^{+}\), reducing acidity and promoting passive performance in areas such as pitting and crevice corrosion. Grabke et al.73 reported that N is beneficial to enhance the repassivation ability of HNSS, rapidly promoting the repassivation of the material and inhibiting the growth of pitting corrosion.
The corrosion mechanism of nitrogen on the pitting corrosion process of HNSS is as follows74:
The dissolution of N also forms a dense and protective nitrogen oxide layer while forming NO3− or NO2−, which serves as a corrosion inhibitor and can effectively suppress local corrosion.
Methods
Materials
The materials used in this work were Fe-20Cr-20Mn-0.64N (HNSS1) and Fe-20Cr-20Mn-0.75N (HNSS2) ASS, provided by Northeastern University, China. The compositions of these two ASSs are shown in Table 4. The two HNSSs were cut into coupons with dimensions of 10 × 10 × 2 mm, ground with sandpaper to 1500 #, then polished using 2.5 μm diamond paste, ultrasonically cleaned in ethanol and water, and finally etched using FeCl3 solution (10 g FeCl3, 30 mL HCl and 120 mL H2O) for 15 s. The 316 SS was etched using 10% oxalic acid electrolysis for etching. When preparing the working electrode, connect the copper wire with conductive adhesive on the back of the sample working surface and seal the sample with epoxy resin.
Surface characterization
After etching, the microstructure of the tested steels was observed using a scanning electron microscope (SEM, XL30-FEG ESEM, FEI, Hillsboro, OR., USA). To identify texture, grain size and grain orientation, they were subsequently characterized using back electron scattering diffraction (EBSD). The phases of the HNSSs were identified using a D/Max 2400 X-ray diffractometer (Rigaku Corporation, Tokyo, Japan) with the Kα radiation of Cu at 10 kV and 40 mA. The scan rate of XRD was 6°/min. The surface morphologies of the two HNSSs after the potentiodynamic polarization test were observed using SEM. The samples were potentiostatically polarized at an applied potential of −0.05 VSCE for 1 h and were then analyzed using X-ray photoelectron spectroscopy (ESCALAB 250Xi T) using an Al Kα radiation source, and the results were fitted with CasaXPS peak fitting software.
Electrochemical tests
Electrochemical tests were carried out in a traditional three-electrode system which consisted of the auxiliary electrode of Pt sheet with an exposed area of 40 cm2, a reference electrode of saturated calomel electrode (SCE). The electrochemical tests were conducted using Gamry Reference 1010E (Gamry Instruments, Inc. USA) electrochemical workstation.
Prior to potentiodynamic polarization measurements, the samples were monitored at open circuit potentials (OCP) for 3600 s to achieve steady state. The potentiodynamic polarization measured with the scanning potential ranged from −0.5 to 1 VSCE of the (HNSS1) and −0.5 to 1.5 VSCE (HNSS2), with a scanning rate of 20 mV/min. Electrochemical impedance spectroscopy was performed at OCP with the frequency range of 104 ~ 1−2 Hz, and the amplitude is 10 mV. Potentiostatic polarization tests were conducted at a potential of −0.05 VSCE for 3600 s, and then Mott-Schottky tests were performed immediately from −0.6 to 1.2 VSCE at a fixed frequency of 103 Hz and a scanning rate of 30 mV/s. All electrochemical tests were carried out in 0.5 mol/L NaCl solution at room temperature (25 ± 1 °C). Each experiment was repeated three times to ensure the repeatability.
Data availability
The data that support the findings of this study are available from Dr. Yanxin Qiao (Email: yxqiao@just.edu.cn) upon reasonable request.
References
Wang, T. H. et al. Effect of boron on dissolution and repairing behavior of passive film on S31254 super-austenitic stainless steel immersed in H2SO4 solution. J. Iron Steel Res. Int. 29, 1012–1025 (2022).
Pujar, M. G., Kamachi, M. U. & Singh, S. S. Electrochemical noise studies of the effect of nitrogen on pitting corrosion resistance of high nitrogen austenitic stainless steels. Corros. Sci. 53, 4178–4186 (2011).
Olsson, C. O. A. & Landolt, D. Passive films on stainless steels—chemistry, structure and growth. Electrochim. Acta 48, 1093–1104 (2003).
Wang, S. et al. Titanium microalloying of steel: a review of its effects on processing, microstructure and mechanical properties. Int. J. Miner. Metall. Mater. 29, 645–661 (2022).
Qiao, Y. X. et al. Recent progress in microstructural evolution, mechanical and corrosion properties of medium-Mn steel. J. Iron Steel Res. Int. 30, 1463–1476 (2023).
Talha, M. C., Behera, K. & Sinha, O. P. In-vitro long term and electrochemical corrosion resistance of cold deformed nitrogen containing austenitic stainless steels in simulated body fluid. Mater. Sci. Eng. C 40, 455–466 (2014).
Poonguzhali, A. M., Pujar, G. & Kamachi, M. U. Effect of nitrogen and sensitization on the microstructure and pitting corrosion behavior of AISI type 316LN stainless steels. J. Mater. Eng. Perform. 22, 1170–1178 (2012).
Ha, H. Y., Jang, H. J. & Kwon, H. S. Effects of nitrogen on the passivity of Fe-20Cr alloy. Corros. Sci. 51, 48–53 (2009).
Dalipi, R. et al. Study of metal release from stainless steels in simulated food contact by means of total reflection X-ray fluorescence. J. Food Eng. 173, 85–91 (2016).
Taiwade, R. V. et al. Effect of grain size on degree of sensitization of chrome-manganese stainless steel. ISIJ Int. 53, 2206–2212 (2013).
Zambon, A., Ferro, P. & Bonollo, F. Microstructural, compositional and residual stress evaluation of CO2 laser welded superaustenitic AISI 904L stainless steel. Mater. Sci. Eng. A 424, 117–127 (2006).
Zhou, Z. L. & Johan, L. Dissimilar welding of super-duplex and super-austenitic stainless steels. Weld. World 61, 21–33 (2016).
Momeni, A., Dehghani, K. & Keshmiri, H. Hot deformation behavior and microstructural evolution of a superaustenitic stainless steel. Mater. Sci. Eng. A 527, 1605–1611 (2010).
Lee, C. M., Lee, Y. C. & Lee, C. H. Possibility of Mn substitution of Ni through evaluation of mechanical properties and corrosion resistance in superaustenitic stainless steel weld metal. Mater. Sci. Eng. A 733, 16–23 (2018).
Cui, B., Zhang, H. & Liu, F. D. Effects of shielding gas composition on the welding stability, microstructure and mechanical properties in laser-arc hybrid welding of high nitrogen steel. Mater. Res. Express 5, 1–17 (2018).
Ningshen, S., Kamachi, U. M., Mittal, V. K. & Khatak, H. S. Semiconducting and passive film properties of nitrogen-containing type 316LN stainless steels. Corros. Sci. 49, 481–496 (2007).
Ha, H. Y., Lee, T. H. & Oh, C. S. Effects of combined addition of carbon and nitrogen on pitting corrosion behavior of Fe-18Cr-10Mn alloys. Scr. Mater. 61, 121–124 (2009).
Diana, L. et al. Effect of nitrogen on the corrosion–erosion synergism in an austenitic stainless steel. Tribol. Int. 44, 610–616 (2011).
Hanninen, H. E. Applications and performance of high nitrogen steels. Steel Grips 2, 371–380 (2004).
Lokeswar, P., Saikat, R. M. & Sunil, K. Status of nickel free stainless steel in biomedical field: a review of last 10 years and what else can be done. Mater. Today. Proc. 26, 638–643 (2020).
Ningshen, S. et al. Hydrogen effects on the passive film formation and pitting susceptibility of nitrogen containing type 316L stainless steels. Corros. Sci. 48, 1106–1121 (2006).
Wu, X. Q. et al. Investigation on pitting corrosion of nickel-free and manganese-alloyed high-nitrogen stainless steels. J. Mater. Eng. Perform. 18, 287–298 (2009).
Olefjord, I. & Wegrelius, L. The influence of nitrogen on the passivation of stainless steels. Corros. Sci. 38, 1203–1220 (1996).
Yang, K. & Ren, Y. Nickel-free austenitic stainless steels for medical applications. Sci. Technol. Adv. Mater. 11, 014105 (2010).
Chen, S. S. et al. High nitrogen stainless steel drug-eluting stent—assessment of pharmacokinetics and preclinical safety in vivo. Bioact. Mater. 5, 779–786 (2020).
Hukovic, M. M. et al. High corrosion resistance of austenitic stainless steel alloyed with nitrogen in an acid solution. Corros. Sci. 53, 2176–2183 (2011).
Mudali, U., Ningshen, K. S. & Tyagi, A. K. Influence of metallurgical and chemical variables on the pitting corrosion behaviour of nitrogen-bearing austenitic stainless steels. Mater. Sci. Forum 318–320, 495–502 (1999).
Toor, I. H. Evaluation of corrosion performance of two Mn-containing stainless steel alloys. Int. J. Mater. Res. 105, 386–391 (2014).
Liang, C. H. & Zhang, J. D. Effect of phosphorus, silicon, manganese and copper on the pitting corrosion resistance of high purity 18Cr-14Ni stainless steel in chloride solution. Corros. Sci. Prot. Technol. 7, 336–340 (1995).
Tao, X. et al. Evaluation of the sliding wear and corrosion performance of triode-plasma nitrided Fe-17Cr-20Mn-0.5N high-manganese and Fe-19Cr-35Ni-1.2Si high-nickel austenitic stainless steels. Surf. Coat. Tech. 409, 126890 (2021).
Qiao, Y. X. et al. Corrosion behavior of a nickel-free high-nitrogen stainless steel with hydrogen charging. JOM 73, 1165–1172 (2021).
Fu, Y. et al. Effects of nitrogen on the passivation of nickel-free high nitrogen and manganese stainless steels in acidic chloride solutions. Electrochem. Acta 54, 4005–4014 (2009).
Li, J. G. et al. Effects of heat input and cooling rate during welding on intergranular corrosion behavior of high nitrogen austenitic stainless steel welded joints. Corros. Sci. 166, 108445 (2020).
Liu, H. F. et al. XRD and EBSD studies of severe shot peening induced martensite transformation and grain refinements in austenitic stainless steel. Mater. Charact. 168, 110574 (2020).
Fujii, T., Yamakawa, R. & Tohgo, K. Analysis of the early stage of stress corrosion cracking in austenitic stainless steel by EBSD and XRD. Mater. Character 172, 110882 (2021).
Qin, F. M. et al. Effect of nitrogen content on precipitation behavior and mechanical properties of Mn18Cr18N austenitic stainless steel. Acta Metall. Sin. 54, 55–64 (2018).
Taylor, C. D. et al. Integrated computational materials engineering of corrosion resistant alloys. NPJ Mater. Degrad. 2, 1–10 (2018).
Li, L. et al. Effect of cavitation erosion induced surface damage on the corrosion behavior of TA31 titanium alloy. Ultrason. Sonochem. 98, 106498 (2023).
Luo, H., Su, H. Z. & Dong, C. F. Passivation and electrochemical behavior of 316L stainless steel in chlorinated simulated concrete pore solution. Appl. Surf. Sci. 400, 38–48 (2017).
Feng, W., Yang, S. & Yan, Y. B. Dependence of grain boundary character distribution on the initial grain size of 304 austenitic stainless steel. Philos. Mag. 97, 1057–1070 (2017).
An, S. Y. et al. Effect of grain boundary engineering treatment on corrosion resistance and mechanical properties of 304 stainless steel. Nonferr. Met. Mater. Eng. 43, 19–26 (2021).
Shi, F. et al. Application of grain boundary engineering to improve intergranular corrosion resistance in a Fe-Cr-Mn-Mo-N high-nitrogen and nickel-free austenitic stainless steel. Acta Metal. Sin. (Engl. Lett.) 33, 789–798 (2020).
Qi, X., Mao, H. H. & Yang, Y. T. Corrosion behavior of nitrogen alloyed martensitic stainless steel in chloride containing solutions. Corros. Sci. 120, 90–98 (2017).
Xu, L. W. et al. Effects of nitrogen content on pitting corrosion resistance of non-magnetic drill collar steel. J. Iron Steel Res. Int. 27, 1466–1475 (2020).
Kamachi Mudali, U. et al. Pitting corrosion studies on nitrogen bearing austenitic stainless steels. Mater. Trans. 37, 1568–1573 (1996).
Liu, L., Li, Y. & Wang, F. H. Influence of nanocrystallization on passive behavior of Ni-based superalloy in acidic solutions. Electrochim. Acta 52, 2392–2400 (2007).
Luo, H. et al. Characterization of electrochemical and passive behaviour of Alloy 59 in acid solution. Electrochim. Acta 135, 412–419 (2014).
Qiao, Y. X. et al. Effect of aging treatment on microstructure and corrosion behavior of a Fe-18Cr-15Mn-0.66N stainless steel. J. Mater. Sci. Technol. 107, 197–206 (2022).
Zhang, H. et al. Microstructural evolution and pitting corrosion behavior of friction stir welded joint of high nitrogen stainless steel. Mater. Des. 110, 802–810 (2016).
Qiao, Y. X. et al. Cavitation erosion behaviors of a nickel-free high-nitrogen stainless steel. Tribol. Lett. 67, 1 (2019).
Shukla, A. K., Balasubramaniam, R. & Bhargava, S. Properties of passive film formed on CP titanium, Ti-6Al-4V and Ti-13.4Al-29Nb alloys in simulated human body conditions. Intermetallics 13, 631–637 (2005).
Wang, Z. B., Hu, H. X. & Liu, C. B. The effect of fluoride ions on the corrosion behavior of pure titanium in 0.05M sulfuric acid. Electrochim. Acta 135, 526–535 (2014).
Sotniczuk, A. et al. Corrosion behaviour of biomedical Ti under simulated inflammation: exploring the relevance of grain refinement and crystallographic texture. Corros. Sci. 200, 110238 (2022).
Orazem, M. E. et al. Invited interpretation of dielectric properties for materials showing constant phase element CPE impedance response. J. Electrochem. Soc. 45, 15–35 (2013).
Feng, H. et al. Sn microalloying enhances corrosion resistance of stainless steel by accelerating heterogeneous nucleation of passive film. Corros. Sci. 201, 110279 (2022).
Wu, X. Q. et al. Effects of nitrogen on passivity of nickel-free stainless steels by electrochemical impedance spectroscopy analysis. J. Mater. Eng. Perform. 24, 3607–3614 (2015).
Shi, J. J., Zou, Y. Q. & Ming, J. Effect of DC stray current on electrochemical behavior of low-carbon steel and 10%Cr steel in saturated Ca(OH)2 solution. Corros. Sci. 169, 108610 (2020).
Li, L. et al. Effect of cavitation erosion induced surface damage on pitting and passive behaviors of 304L stainless steel. Int. J. Miner. Metall. Mater. 30, 1338–1352 (2023).
Gui, Y., Zheng, Z. J. & Gao, Y. The bi-layer structure and the higher compactness of a passive film on nanocrystalline 304 stainless steel. Thin Solid Films 599, 64–71 (2016).
Burstein, G. T., Liu, C. & Souto, R. M. The effect of temperature on the nucleation of corrosion pits on titanium in Ringer’s physiological solution. Biomaterials 26, 245–256 (2005).
Cui, Y. W. et al. Metastable pitting corrosion behavior of laser powder bed fusion produced Ti-6Al-4V in Hank’s solution. Corros. Sci. 203, 110333 (2022).
Souto, R. M. & Burstein, G. T. A preliminary investigation into the microscopic depassivation of passive titanium implant materials in vitro. J. Mater. Sci. Technol. 7, 337–343 (1996).
Gai, X. et al. Electrochemical behaviour of passive film formed on the surface of Ti-6Al-4V alloys fabricated by electron beam melting. Corros. Sci. 145, 80–89 (2018).
Tang, Y. M., Zuo, Y. & Zhao, X. H. The metastable pitting behaviors of mild steel in bicarbonate and nitrite solutions containing Cl−. Corros. Sci. 50, 989–994 (2008).
Zhang, L. J. et al. Study on the anodic film formation process of AZ91D magnesium alloy. Electrochim. Acta 52, 5325–5333 (2007).
Gao, S. J. et al. Electrochemical behavior and nonlinear Mott-Schottky characterization of a stainless steel passive film. Anal. Lett. 47, 1162–1181 (2014).
Zhu, M., Zhang, Q. & Yuan, Y. F. Passivation behavior of 2507 super duplex stainless steel in simulated concrete pore solution. J. Mater. Eng. Perform. 29, 3141–3151 (2020).
Feng, H. et al. Influence of nitrogen on corrosion behaviour of high nitrogen martensitic stainless steels manufactured by pressurized metallurgy. Corros. Sci. 144, 288–300 (2018).
Li, J., Wang, Q. C. & Yang, Y. X. Enhancing pitting corrosion resistance of severely cold-worked high nitrogen austenitic stainless steel by nitric acid passivation. J. Electrochem. Soc. 166, 365–374 (2019).
Sun, S. C. et al. The synthesis and electrochemical behavior of high-nitrogen nickel-free austenitic stainless steel. J. Mater. Eng. Perform. 23, 3957–3962 (2014).
Wang, G. H., Jiang, Y. Q. & Guo, C. A. Effect of nitrogen content on the corrosion resistance of high- nitrogen austenitic stainless steel for nonmagnetic drill collar in a harsh service environment. Int. J. Electrochem. Sci. 17, 220656 (2022).
Vignal, V., Krawiec, H. & Heintz, O. Passive properties of lean duplex stainless steels after long-term ageing in air studied using EBSD, AES, XPS and local electrochemical impedance spectroscopy. Corros. Sci. 67, 109–117 (2013).
Grabke, H. J. The role of nitrogen in the corrosion of lron and steels. ISIJ Int. 36, 777–786 (1996).
Yu, C. Y. Analysis of the effect of nitrogen on the spot corrosion resistance of stainless steel. Corros. Prot. Petrochem. Ind. 29, 23–27 (2012).
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China (Nos. 52001142, 52005228, 51801218, and 51911530211), Science Foundation of Jiangsu Province (No. BK 20180984), GDAS’ Project of Science and Technology Development (2022GDASZH-2022010103).
Author information
Authors and Affiliations
Contributions
F.G. and L.Y.: Investigation, formal analysis, and writing—review and editing. F.G. and J.C.: Conceptualization, writing—review and editing. H.Z. and Z.Z.: Formal analysis and investigation. L.Z.: Sample preparation. Y.Q. and J.C.: Conceptualization, supervision.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gao, F., Qiao, Y., Chen, J. et al. Effect of nitrogen content on corrosion behavior of high-nitrogen austenitic stainless steel. npj Mater Degrad 7, 75 (2023). https://doi.org/10.1038/s41529-023-00394-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41529-023-00394-x