Table 2 Results for the ML predicted EFA for 70 new compositions.

From: Discovery of high-entropy ceramics via machine learning

Composition EFAAttributes EFACALPHAD EFADFT Exp. Composition EFAAttributes EFACALPHAD EFADFT Exp.
CrNbTaVWC5 94 105    CrHfTiVZrC5 76 70   
CrMoNbTaVC5 107 105    CrMoTaVZrC5 70 70   
CrMoNbVWC5 100 104 116 S CrMoTiVZrC5 65 67   
CrMoNbTaWC5 97 104 105 S CrHfMoTiVC5 72 66   
CrMoTaVWC5 97 103 106 S CrMoNbTiZrC5 68 66   
CrMoNbTaTiC5 98 93    CrTaTiVWC5 69 66   
CrMoTaTiVC5 98 93    CrHfMoNbZrC5 63 62   
CrMoNbTiVC5 95 92    CrHfNbTaWC5 63 62   
CrHfNbTaVC5 97 91    CrHfMoVZrC5 69 62   
CrMoTiVWC5 82 88 76 S CrHfMoTaZrC5 61 60   
CrMoTaTiWC5 82 88    CrMoVWZrC5 65 59   
CrHfNbTaTiC5 93 88    CrMoNbWZrC5 64 59   
CrNbTaTiVC5 95 88    CrNbTaWZrC5 59 58   
CrHfTaTiVC5 91 87    CrHfMoVWC5 65 57   
CrHfMoNbVC5 75 84    CrHfMoTaWC5 61 56   
CrNbTaVZrC5 93 83    CrHfTaVWC5 54 56   
CrTaTiVZrC5 91 83    CrHfTaTiWC5 56 55   
CrMoNbTiWC5 74 81    CrHfMoNbWC5 52 54   
CrMoNbVZrC5 80 81    CrMoTaWZrC5 54 54   
CrNbTaTiZrC5 91 79    CrHfNbTiWC5 58 52   
CrHfMoNbTaC5 76 79    CrHfMoTiZrC5 65 51   
CrHfNbTiVC5 91 78    CrHfTaWZrC5 55 51 36 M
CrMoNbTaZrC5 70 78    CrHfNbVWC5 58 51   
CrHfTaVZrC5 77 78    CrTaTiWZrC5 54 50   
CrHfNbTaZrC5 70 77    CrNbVWZrC5 51 50   
CrNbTiVZrC5 94 76    CrMoTiWZrC5 51 49 52 M
CrNbTiVWC5 72 74    CrTaVWZrC5 52 48   
CrHfTaTiZrC5 82 74    CrTiVWZrC5 50 48   
CrHfMoTaVC5 73 73    CrNbTiWZrC5 51 48   
CrHfNbTiZrC5 76 72    CrHfVWZrC5 52 47   
CrHfMoNbTiC5 69 72    CrHfNbWZrC5 52 46   
CrHfNbVZrC5 88 71    CrHfTiWZrC5 51 46   
CrHfMoTaTiC5 73 71    CrHfTiVWC5 46 46   
CrMoTaTiZrC5 72 70    CrHfMoWZrC5 53 45   
CrNbTaTiWC5 67 70    CrHfMoTiWC5 53 45 42 M
  1. Results for both ML models are provided for each composition. For the selected compositions, a DFT-computed EFA value is listed in the next column. In the experimental result, “S” and “M” stand for single- and multi-phase, respectively. Units: EFA in (eV/atom)−1.