Abstract
The reconstruction of Cu catalysts during electrochemical reduction of CO2 is a widely known but poorly understood phenomenon. Herein, we examine the structural evolution of Cu nanocubes under CO2 reduction reaction and its relevant reaction conditions using identical location transmission electron microscopy, cyclic voltammetry, in situ X-ray absorption fine structure spectroscopy and ab initio molecular dynamics simulation. Our results suggest that Cu catalysts reconstruct via a hitherto unexplored yet critical pathway - alkali cation-induced cathodic corrosion, when the electrode potential is more negative than an onset value (e.g., −0.4 VRHE when using 0.1 M KHCO3). Having alkali cations in the electrolyte is critical for such a process. Consequently, Cu catalysts will inevitably undergo surface reconstructions during a typical process of CO2 reduction reaction, resulting in dynamic catalyst morphologies. While having these reconstructions does not necessarily preclude stable electrocatalytic reactions, they will indeed prohibit long-term selectivity and activity enhancement by controlling the morphology of Cu pre-catalysts. Alternatively, by operating Cu catalysts at less negative potentials in the CO electrochemical reduction, we show that Cu nanocubes can provide a much more stable selectivity advantage over spherical Cu nanoparticles.
Similar content being viewed by others
Introduction
The electrochemical reduction reaction of CO2 (CO2RR) to higher-value chemicals holds great promise for mitigating climate change and transitioning the chemical industry towards sustainability1,2. Among various heterogeneous electrocatalysts, copper (Cu) was found uniquely capable of producing multicarbon products, such as ethylene, ethanol, and propanol, at significant rates3,4. While previous research5,6,7,8 mainly aimed at improving the activity and selectivity of Cu catalysts, their stability under reaction conditions is at least equally important and has drawn increasing research attention9,10. Some studies demonstrate the stable operation of Cu catalysts for tens or hundreds of hours11,12,13. In contrast, others show substantial performance fluctuations within an hour or less14,15. The existence of such a discrepancy in literature is puzzling since essentially the same material, copper, was being tested. In addition to the possible causes associated with electrochemical reactors (e.g., flooding)16, it is widely acknowledged that Cu catalysts undergo significant reconstructions during the electrocatalytic reactions that may also affect its stability17,18,19. Buonsanti and colleagues20, as well as other researchers21,22,23 showed that this potential-induced reconstruction is the primary deactivation mechanism for shape-controlled Cu catalysts. However, in contrast, other studies by Jung et al. 24, by Choi et al. 25, and more recently by Yang et al. 26 suggested that the reconstruction can create active sites in Cu catalysts.
Experimentally studying the reconstruction of Cu under CO2RR conditions has been challenging at least partially due to the susceptibility of Cu to be oxidized27. Recently, many in situ characterization methods, such as in situ electron microscopy23,26,28,29, in situ scanning probe microscopy17,18,30, in situ X-ray scattering31 were developed and applied to study the reconstruction of Cu catalysts. However, the underlying causes and the impact of such a phenomenon on catalyst stability remain still elusive. For instance, some researchers13,24 attributed it to the reduction of copper oxides, while others showed that CO32,33 or H234,35 played important roles. The limited understanding of this reconstruction behavior of Cu catalysts in the cathode made it difficult to clarify the structural-property relationship, possibly also fueling debates regarding issues such as the identity of the active sites in Cu catalysts36 and whether oxide-derived Cu is intrinsically better than just Cu8,37,38.
In this work, we track the structural evolution of Cu nanocubes under relevant CO2RR reaction conditions using a combination of identical location TEM (IL-TEM), cyclic voltammetry (CV), in situ X-ray Absorption Fine Structure Spectroscopy (XAFS), Scanning Transmission Electron Microscopy (STEM), Density Functional Theory (DFT) and grand-potential Ab Initial Molecular Dynamics (AIMD) simulations. Our results suggest that Cu catalysts reconstruct via a hitherto unexplored yet critical pathway - alkali cation-induced cathodic corrosion39, when the electrode potential is more negative than an onset value (e.g., −0.4 VRHE when using 0.1 M KHCO3). Having alkali cations in the electrolyte is found critical for this phenomenon to take place. Our experiments and modeling suggest that Cu can be etched out by possibly forming intermediate ternary hydride40,41 with alkali cations, which can then be redeposited as metallic Cu under cathodic conditions, leading to experimentally observed reconstruction of the Cu catalyst and the formation of smaller Cu particles during the CO2RR reaction.
Since CO2RR usually requires highly cathodic conditions and having alkali cations in the electrolyte42,43,44,45, Cu catalysts will inevitably undergo surface reconstructions that lead to dynamic morphologies. We will argue that having this dynamic morphologies does not necessarily preclude stable operation using Cu catalysts as the catalyst morphology may potentially reach an equilibrium. However, because of the alkali cation-induced cathodic corrosion, many approaches towards engineering the morphology of Cu pre-catalyst may unlikely bring long-term selectivity/activity benefits46,47,48. Alternatively, this observation suggests that strategies can be designed to mitigate selectivity changes by reducing the extent to which the cathodic corrosion of Cu can occur. To this end, by operating Cu catalysts at less negative potentials than the threshold (e.g., −0.4 VRHE) in the CO electrochemical reduction reaction (CORR)49,50,51, we demonstrate that the cathodic corrosion can be switched off, allowing Cu nanocubes to maintain a stable selectivity advantage over spherical Cu nanoparticles.
Results
A hitherto unexplored yet critical reconstruction pathway for Cu catalysts
We use Cu nanocubes (NCs) as our model catalysts due to their well-defined initial structure, enabling us to closely track the structural evolution of the catalysts. Cu nanocubes were prepared following a previously reported protocol (see “Methods” section)7. As shown in Fig. 1a, the as-synthesized NCs are largely uniform with an average size of approximately 40 nm, although occasionally NCs of different sizes and spherical Cu particles can also be found. The metallic nature of the NCs is confirmed by electron diffraction (inset of Fig. 1a and Fig. S1). Despite our efforts to limit air exposure (see “Methods” section), we still anticipate the presence of thin surface oxide shells on the Cu NCs. Through scanning transmission electron microscopy (STEM) imaging and electron energy loss spectroscopy (EELS), we show that the surface oxide layers on Cu NCs that were subjected to our typical sample handling procedures are about 2 nm in thickness (Fig. S2). As part of our control experiments, we have also considered extreme cases wherein Cu catalysts were deliberately stored or exposed to air for extended periods (Figs. S3 and S4), where the Cu oxide layers were found no thicker than 5 nm. Based on these observations, it is reasonable to assume that the oxide layer on the Cu NCs that will be discussed in this manuscript will typically be around 2 nm and unlikely to exceed around 5 nm.
As-synthesized Cu NCs were tested for CO2RR at −1.1 VRHE using a typical H-cell setup and a CO2-saturated 0.1 M KHCO3 electrolyte for 10 h (Table S1, entry 1). Significant changes in reaction selectivity among gas-phase products were observed (Fig. S5), as were the morphological changes of the Cu catalysts and the formation of smaller Cu nanoparticles (Figs. S5 and S6). Identical location TEM (IL-TEM) was applied (Fig. 1b) to follow individual NCs before and after treating the catalysts at desired electrode potentials, using a method modified from the work by Mayrhofer et al.52 (see “Methods” section). A pair of representative IL-TEM bright field images of the catalyst before and after treating the catalysts at −1.1 VRHE in a CO2-saturated 0.1 M KHCO3 electrolyte (Table S1, entry 2) for 20 min were shown in Fig. 1c. Evidently, almost all Cu particles within this view exhibit clear signs of morphological changes after the treatment, irrespective of their size and shape. Moreover, as shown in Fig. 1d–f, it is apparent that the morphological changes of the Cu NCs extended deep into the core of the particle, significantly surpassing the estimated thickness of the earlier discussed oxide crusts. This suggests that the reduction or dissolution of surface oxides is unlikely the sole contributor to the morphological changes of the Cu catalysts.
Intriguingly, when we removed CO2 gas from the reaction and repeated the IL-TEM experiments at −1.1 VRHE using Ar-saturated 0.1 M KHCO3 electrolyte (Table S1, entry 3), a very similar catalyst reconstruction was observed (Fig. 2a, b). In contrast, the morphological changes observed on nanocubes subjected to electrochemical treatment under 0 VRHE (Table S1, entry 4) or slightly more negative potential of −0.36 VRHE (Table S1, entry 25) in Ar-saturated 0.1 M KHCO3 electrolyte, are primarily confined to less than 5–6 nm (Figs. S8–S10), which matches the estimated thickness of oxide layers. When we replace the electrolyte with Ar-saturated 0.1 M K2SO4 (Table S1, entry 5) or 0.1 M K2CO3 (Table S1, entry 6) and applied −1.1 VRHE, significant catalyst reconstruction will again be observed (Fig. S11). These results suggested that CO-related mechanisms32 are likely not the only possible mechanism responsible for observed morphological changes in Cu catalysts.
To address the limited sampling capacity of TEM, we implemented cyclic voltammetry (CV) as a complementary technique to provide an overall assessment of the structural evolution of Cu NCs53. CV is done in an electrochemical cell with a three-electrode configuration as in the IL-TEM setup, except that more catalysts were used to enhance OH- adsorption signals (see “Methods” section). Figure 2e show two voltammograms, recorded in 0.1 M NaOH after the catalysts were treated at about −1.05 VRHE in Ar-saturated 0.1 M KHCO3 (Table S1, entry 3) for 20 min and 65 min, respectively. This two-stage comparison helps to exclude the influence of surface oxide crusts, which should be reduced quickly (e.g., within 10 min for 40 nm thick Cu2O11) under such a highly cathodic condition. It is therefore reasonable to assume the surface oxides are completely reduced within 20 min under our experimental conditions. The voltammogram of the 65-min treated catalyst differs notably from its 20-min treated analogs in two main aspects: it exhibits a reduced feature associated with the {100}-specific OH-adsorption at around −0.1 V, and an enhanced feature related to surface defects Cu at above +0.3 V. These disparities observed are notably more substantial than those arising from the experimental uncertainties inherent between individual CV experiments (Fig. S12). This reinforces the suggestion that the reduction of surface oxides cannot be the sole reason for the reconstruction of Cu catalysts. It is also important to highlight that morphological changes occur on {100} facets and not just on the particle corners. As shown in Fig. 1c, we also observe significant morphological transformations occurring on spherical particles. These findings suggest that the shape of the particles and the potential field concentration are at least not the determining factors influencing the reconstruction process.
Considering the potential contribution of the hydrogen evolution reaction (HER) to the reconstruction of Cu under CO2RR relevant conditions34,35, we carried out additional CV experiments to study the catalysts being treated at about −1.05 VRHE using 0.05 M H2SO4 as the electrolyte (Table S1, entry 7). In this case, we observed only minor changes between voltammograms (Fig. 2f) associated with catalysts treated by 20 min and by 65 min. This suggests that in scenarios where only the HER occurs without the presence of alkali cations, the catalyst reconstruction is considerably less pronounced. Interestingly, changes in the voltammogram that correspond to significant reconstructions of NCs could be observed again once 0.3 M K2SO4 was added into the electrolyte, indicating that the presence of alkali cations in the electrolyte may promote the catalyst reconstruction. IL-TEM results of the catalysts being treated at about −1.1 VRHE in acidic electrolyte without (Table S1, entry 7) and with K+ (Table S1, entry 8) are shown in Figs. S13a and S12b, respectively, which are consistent with the CV observations. It’s important to emphasize that in our experiments, the electrolyte was thoroughly de-aerated to eliminate oxygen, which, if present, could lead to further dissolution of Cu, as reported in previous studies54. To experimentally demonstrate this, we intentionally reintroduced oxygen into the H2SO4 electrolyte by blowing air (Table S1, entry 9), which then resulted in significant copper dissolution observable through both IL-TEM and CV methods (Figs. S13c and S12d). These findings indicate that the further reconstruction of Cu catalysts, occurring after the initial surface oxides are removed, is unlikely due to additional reduction or dissolution of oxides. Increasing the K+ concentrations to 0.5 M and 1.5 M (Table S1, entries 10–11) led to apparently more obvious structural changes (Fig. S14). Significant reconstruction was observed when the catalysts were treated in electrolyte with other alkali cations including Li+, Na+, and Cs+ (Table S1, entries 12–19) both at constant voltage (Fig. S15) and at constant current (Fig. S16). This observation is consistent with the cathodic corrosion behavior reported for noble metals40.
These experimental findings indicate the existence of a previously unexplored yet critical pathway of reconstruction for Cu catalysts under CO2RR-related reaction conditions. The promoting effect of alkali cations makes the process closely resembling to the phenomenon of alkali cation-induced cathodic corrosion, which is known to cause the reconstructions of many metal electrodes, such as platinum, rhodium, and gold39. Koper and colleagues40,55 proposed that the presence of alkali cations can lead to the formation of intermediate ternary hydride with the cathode metal. Such species leave the electrode but are unstable and will be quickly redeposited onto the cathode, leading to a reconstruction. Although the detailed mechanism of cathodic corrosion is still not fully understood, likely due to the difficulties of identifying these transient species, researchers have already harnessed this phenomenon for applications, such as nanoparticle synthesis56. It is important to note that, to the best of our knowledge, alkali cation-induced cathodic corrosion has not been previously reported for Cu catalysts under CO2RR reaction conditions27.
Identifying an onset potential for the cathodic corrosion of Cu catalysts
Another important characteristic of cathodic corrosion is that it occurs only when the electrode potential is more negative than a certain onset potential55. This was found to also be the case for Cu catalysts. Figure S17 shows that the changes in CV features associated with {100} facets and defects become suppressed as the electrode potential was adjusted to more positive values of −0.82 VRHE, −0.62 VRHE, and −0.42 VRHE (Table S1, entries 21–23). We then repeated the experiment to ensure that the total charge transferred is approximately equivalent while varying the electrode potentials. As shown in Fig. 3a, a brief 3-min treatment at about −1.02 VRHE caused much more significant changes in the voltammogram compared to a 120 min additional treatment at a more positive potential of −0.36 VRHE (Table S1, entries 25–26). This indicates a more significant reconstruction in the case of −1.02 VRHE treated catalysts compared to the −0.36 VRHE treated, notwithstanding that the total amount of charge transferred in both cases was nearly identical (i.e., about 0.4 C, Fig. S18). The repeated CV experiments show consistent results as shown in Fig. S20. These results from the CV experiment also agree well with the ex-situ TEM (Fig. S19) and the IL−TEM results (Fig. 3b and Fig. S21) which show that the Cu NCs morphology remains largely intact after 150 min at −0.36 VRHE. Note that the images of the Cu nanocubes before the reaction shown in Fig. 3b have thin layers of surface oxides, making them differ slightly from those generating the signal of reference CV (30 min) in Fig. 3a since the 30 min of treatment under −0.36 VRHE or more will remove the surface oxides. We then repeated the experiment, this time comparing the CV of Cu nanocubes experienced a 60-min treatment at −0.36 V and the CV of Cu nanocubes with a 25-min treatment at −0.36 VRHE plus a 30-s treatment at about −1 VRHE using 1 M KOH as the electrolyte (Table S1, entries 23–24), and a similar trend was observed (Fig. S22). In sum, we found that there exists an onset potential of cathodic corrosion for Cu catalysts of approximately −0.4 VRHE under our experimental conditions.
In situ X-ray absorption fine structure (XAFS) spectroscopy studies were carried out in order to monitor the oxidation states of Cu during the CO2RR process. To eliminate the possible self-absorption effect in fluorescence mode57,58,59 and thus to have proper comparisons with a Cu foil standard, the transmission mode was adopted for the study. A schematic view of the in situ XAFS cell is shown in Fig. 4a. The electrochemical cell has a three-electrode configuration, with a total electrolyte thickness of 1.5 mm on one side of the electrode. This design ensures adequate transmission of X-ray photons. (see “Methods” section) To ensure that XAS captures the maximum amount of information about the sample surface, we employed the smallest attainable particle size of 7 nm7. This size represents the lower limit of controllable synthesis in our laboratory while maintaining a sufficiently large specific surface area. Figures 4b, c show Cu K-edge X-ray absorption near edge fine structures (XANES) recorded in 0.1 M KHCO3 as the Cu nanoparticles being treated at about −1.05 VRHE and −0.4 VRHE, respectively (Table S1, entries 29–30). At open circuit potential (OCP), Cu was found in a partially-oxidized state. After 15 min of cathodization at −1.05 VRHE, the spectra from the catalyst largely resembled the Cu foil reference, indicating oxide reduction to metallic Cu. Intriguingly, further cathodization at −1.05 VRHE led to a redshift for the shoulder feature relative to the Cu foil reference (Fig. 4b). Similar redshifts on the Pt L edge60 or Pd K-edge61 have been previously reported in alloys where the precious metals become electron-rich. Since this trend was not observed when catalysts were cathodized only at −0.4 VRHE for 72 min (Fig. 4c), we suspect that this feature could be related to the electron-rich form of Cu in the corrosion intermediates. More work is certainly needed to further identify the nature of such intermediates. The XAFS results align with our IL-TEM and CV observations shown in Fig. 3, suggesting an onset potential for alkali cation-induced cathodic corrosion exists for Cu at around −0.4 VRHE under our experimental conditions.
The computational investigation provides detailed thermodynamic information and theoretical insights into the corrosion-reaction kinetics at the atomic scale, which is important to understand the copper cathodic corrosion phenomena observed in our experiments. Inspired by a previous work of Pt cathodic corrosion by Alexandrov and colleagues41, our goal is to calculate the trend of free energy and its gradient during a hypothetical cathodic corrosion reaction. The trend at different potentials indicates whether the reaction is energetically favored. We performed AIMD simulations of copper dissolution at an interface between a protonated copper (001) surface and a solvated potassium ion. As shown in Fig. S24, the interface model contains a three-layer copper slab with 24 copper atoms (gray), and one potassium ion (blue) is equilibrated to be 3.4 Å from the copper surface. Water molecules (red and white) form an interface with copper, and an implicit water region extending up to 25 Å along the c direction - along which the reaction of copper dissolution is simulated. The bottom plot in Fig. S24 shows the electrostatic potential of the model along the c-axis (black curve), and the solvent potential VSol = 2.02 eV is calculated from the implicit water region. With the constant VSol, the electrode potential versus standard hydrogen electrode (SHE) can be calculated by USHE = VSol-EFermi-μe, where μe = 4.4 V is the absolute potential of SHE, and EFermi (blue line in the bottom of Fig. S24) is a variable determined by the number of electrons injected into the system.
We performed a temperature ramping followed by a period of the equilibration (see “Methods” section) of the interface model at two different potentials, namely −0.35 VRHE and −1.31 VRHE. These potentials are achieved by adding into the system ~0.2 and ~3.0 electrons, thereby simulating a grand-canonical ensemble where the system can exchange electrons with a reservoir. Due to limitations in our modeling that prevent the precise adjustment of potential to align with the original experimental conditions at −1.1 VRHE, we also conducted additional cyclovoltammetry (CV) experiments at approximately −1.3 VRHE (Table S1, entries 24) to better match with the simulation parameters. The results, presented in Fig. S17d, reveal that the catalyst undergoes significant reconstruction at −1.3 VRHE, mirroring the behavior observed at −1.1 VRHE. This consistency validates the choice of parameters used in our modeling. We then conducted constant-potential Blue-Moon AIMD41,62,63,64,65,66 on snapshots at 300 K taken from a copper dissolution trajectory generated by slow-growth AIMD (see “Methods” section). Here, the Blue-Moon AIMD simulation samples microstates of each window along the dissolution-reaction trajectory. Figures 5a, b show the statistical free energy gradient (purple) and numerically integrated free energy (green) as functions of the reaction coordinate of the copper dissolution. The reaction coordinate represents an approximate distance along with the copper atom gets away (in other words, dissolves) from the metal surface.
At −0.35 VRHE (Fig. 5a), the free energy gradient shows a monotonic increase up to a distance 1.5 Å far from the basal plane of the copper surface reaching a gradient ~1.3 eV/Å, and the gradients stay over 1 eV/Å at 2.0 Å. This trend leads to an increase in free energy, which reaches ~1.2 eV (115.8 kJ/mol) at 2.0 Å. The increasing gradient and high energy indicate that copper dissolution is energetically unfavored and inhibited. Notably, the structure at 2.5 Å from prior slow-growth AIMD (shown in the inset of Fig. 5a on the right) becomes unstable and cannot be converged by the constrained constant-potential AIMD. This is an indication that the copper atom leaving the surface is unstable at positions far away from the surface (deep into the solvent) and at more positive potentials, e.g., −0.35 VRHE. On the other hand, at more negative potentials −1.31 VRHE (Fig. 5b), the free energy gradient does not show an increasing trend, and multiple local minima below 0 eV/Å are observed. The trend results in a rather flat free energy curve around 0 eV and indicates energetically favored copper dissolution. The inset in Fig. 5b shows atomic structures along the dissolution trajectory (at 0 Å, 1.5 Å, and 2.5 Å Cu distance from the surface) generated by slow-growth AIMD. At 0 Å, the potassium cation appears partially desolvated to three water molecules and adsorbed at the copper surface. The potassium and copper species remain coordinated during the dissolution process. It is observed that copper species forms hydride with two protons (Cu-H bond lengths of ~1.64 and ~1.57 Å) when it dissolves at a distance of ~2.5 Å from the surface (right-most inset structure in Fig. 5b).
These modeling results show that the potential is indeed an important factor for the dissolution of copper. From these results, we can infer a plausible mechanism41 of the cathodic corrosion of Cu: at an electrode potential more negative than the onset potential (i.e., about −0.4 VRHE at our conditions) and with the presence of alkali cations in the solution, Cu forms soluble intermediate ternary hydride species. They may react quickly with adsorbed hydrogen species or water from the solution and get deposited back onto the electrode, leading to the observed reconstruction of the Cu catalyst and the formation of smaller Cu particles, and the reconstruction of Cu catalysts.
The impact of cathodic corrosion of Cu on its catalytic performance
Previous studies have highlighted the critical roles alkali cations played in CO2RR, as they can stabilize key reaction intermediates43,67 and suppress the hydrogen evolution reaction (HER)42,45,68. In addition, Cu catalysts are commonly operated at about −1 VRHE or more cathodic conditions to enhance selectivity towards multicarbon products4. Therefore, if the alkali cation-induced cathodic corrosion is in play, Cu catalysts will inevitably undergo reconstructions under a typical CO2RR condition and the selectivity advantages brought by morphology control in the pre-catalyst stage will unlikely to be stable. This is exactly what we found. As shown in Figs. S5, 6a, and Fig. S25, although Cu NCs initially offer high selectivity towards C2H4, the catalyst morphology and catalytic performance evolve over time, producing a lot more CH4 after 10 h (Table S1, entries 1). We then conducted another 10-h CO2RR experiment, this time employing 25 nm spherical Cu nanoparticles (Table S1, entries 31). These spherical Cu nanoparticles generate comparable amounts of C2 products (mainly C2H4) towards the end of the 10 h reaction, mirroring the performance of aged Cu nanocubes.
Given that controlling catalyst morphology is a major method to adjust the intrinsic activities of electrocatalysts5,6,69,70, we hope to see if we can switch off the alkali cation-induced cathodic corrosion so that we maintain the morphology and selectivity advantages of Cu NCs over spherical Cu nanoparticles. We choose to do the electrochemical reduction of CO (CORR) since it can give a range of more useful products at more positive electrode potentials compared to CO2RR50. CORR experiments were carried out using an electrolyzer flow cell and a gas diffusion electrode (GDE) (see “Methods” section), with 1 M KOH being used as the electrolyte. Figure S26a–d shows the cell current as a function of time on a Cu nanocube-containing electrode at various CORR potentials. The electrode was treated sequentially for 10 min each at −0.27 VRHE, −0.36 VRHE, −0.42 VRHE, and then −0.46 VRHE (Table S1, entries 32–35). We initially observed stable or decreasing currents at potentials more positive than −0.4 VRHE, but then noted a significant current increase at more negative potentials, indicating Cu surface roughening and Cu nanoparticle formation. Since the catalyst has already been treated with negative potentials close to −0.4 VRHE for 20 min, there should be no oxides left in the catalysts. Further experiments, including a 10-h test at −0.37 VRHE and a separate 80-min test at −0.58 VRHE (Figs. S26e, f, Table S1, entries 36–37), show consistent results. These findings strongly suggest that the cathodic corrosion is in play when the electrode potential is more negative than an onset potential around −0.4 VRHE under our experimental conditions. This explanation is supported by the ex-situ TEM results, via which we observed significant reconstruction of Cu NCs that underwent CORR at more negative potential than −0.4 VRHE (i.e., −0.7 VRHE, −0.9 VRHE) (Fig. S27, Table S1, entries 38–39). The results of these preliminary experiments indicate that the corrosion behavior of Cu catalysts during the CORR closely aligns with our earlier observations in CO2RR. More importantly, they suggest that this corrosion can be switched off by operating the CORR at a potential more positive than approximately −0.4 VRHE under our experimental conditions.
We subsequently conducted 10-h CORR experiments at −0.37 VRHE using 25 nm spherical Cu nanoparticles (Table S1, entries 40) and compared the results with that of a similar experiment conducted using 40 nm Cu nanocubes (Table S1, entries 36). The Faraday Efficiencies (FE) of products from these reactions, at both the start and end of the 10-h period, are illustrated in Fig. 6b. Ethylene (C2H4) was the sole gas-phase product detected via gas chromatography, with FE remaining relatively stable for both Cu NCs (28%–29%) and spherical Cu nanoparticles (26%–25%). An observed increase in hydrogen evolution reaction (HER) for both catalysts is attributed to gradual electrode flooding rather than to changes in catalyst morphology, as confirmed by TEM images before and after the reaction (insets in Fig. 6c, d). Liquid products were quantified by extracting about 0.6 ml of electrolyte every hour from the initial 15 ml catholyte and analyzing it via NMR (refer to Methods). A progressive decrease in total FE was noted (Fig. S28), likely due to some liquid products crossing over through the ion exchange membrane71. The low current and extended duration of the CORR experiments make them prone to such systematic errors. However, the total FE remained acceptably around or above 90%. Importantly, when focusing on the fractions of different liquid products, which were accurately determined via NMR, a consistent distribution was observed for both catalysts. Notably, Cu NCs produced a significantly higher fraction of propanol (about 60%) among all liquid products during the 10-h test (Fig. 6c), a result not replicated when spherical Cu nanoparticles were used (Fig. 6d). Thus, Cu NCs maintained a morphology-induced selectivity advantage in the CORR experiment at −0.37 VRHE, in contrast to the earlier CO2RR results at −1.1 VRHE. The CORR experiments were also carried out with 7 nm Cu spheres and the findings are basically identical (Fig. S29, Table S1, entries 41–42). This suggests that the corrosion behavior could indeed be switched off at relatively positive potentials, corroborating our hypothesis and indicating a solid understanding of such behaviors.
Given these observations, a legitimate question arises: If the morphology of Cu catalysts is going to be disrupted by the alkali cation-induced cathodic corrosion under typical reaction conditions, why stable operations of CO2RR using Cu can still be observed? We propose that the dissolution and redeposition of Cu species may reach an equilibrium state, allowing a stable performance to be observed. Rather than a uniform process, we posit that the alkali cation cathodic corrosion may preferentially remove Cu atoms with high surface energies (such as those with low coordination numbers)55,72. Similarly, vacancy sites with a high number of neighbors could be preferentially filled during the redeposition process. To visualize this process, we conducted a conceptual simulation using a two-dimensional square lattice model. As shown in Fig. S30, an equilibrium state can indeed be achieved through continuous dissolution and redeposition processes, provided an appropriate bias exists among surface sites and vacancies based on their coordination numbers. This simulation suggests that the initial morphology of Cu catalysts and their operating conditions would influence how quickly a catalyst could reach this “steady” state. This proposal agrees well with our observation that Cu NCs and spherical Cu nanoparticles eventually yield a similar selectivity profile in CO2RR, as depicted in Fig. 6a.
Discussion
In this work, we examined the structural evolution of Cu NCs under CO2 electrochemical reduction (CO2RR) and its relevant reaction conditions using a combined approach of identical location TEM (IL-TEM), cyclic voltammetry (CV), and additional experimental and theoretical approaches. Our experimental evidence strongly suggested the existence of a previously unexplored yet critical pathway reconstruction pathway for Cu catalysts – alkali cation-induced cathodic corrosion. Because of that, during a typical CO2RR process, Cu catalysts will undergo surface reconstructions, resulting in dynamic catalyst morphologies. As schematically summarized in Fig. 7, we illustrate that this corrosion behavior in Cu does not necessarily preclude stable operation of CO2RR, but will limit long-term selectivity and activity enhancement from morphology-controlled Cu pre-catalysts. Alternatively, by operating Cu catalysts at less negative potentials than the onset potential (around −0.4 VRHE in our conditions), we show that Cu NCs can maintain their morphology and provide a much more stable selectivity advantage towards propanol over spherical Cu nanoparticles.
Since the alkali cation-induced cathodic corrosion was found in many other metals39, it should not be too surprising that it also takes place in Cu. Our in situ XAFS results provided some hints on the existence of an electron-rich form of Cu in the corrosion intermediates, which are in line with earlier proposals about the possible involvement of intermediate ternary hydride40,41 in the cathodic corrosion of other metals. The pursuit to experimentally identify such transient species is still on. Notably, the continuous dissolution of Cu has indeed been observed in a recent ongoing work by Buonsanti and colleagues73. As such, cathodic corrosion is likely to be a missing puzzle piece for a mechanistic understanding of the performance of Cu catalysts in CO2RR. For instance, this or other types of possible intermediates need to be taken into consideration when constructing the reaction mechanisms for CO2RR on Cu.
It was predicted74 that multivalent cations can have a significant effect on CO2RR performance and some experimental exploration was reported75. Hence we went on to investigate whether multivalent cations (i.e., Mg2+ and Al3+) (Table S1, entries 43–45) can also lead to cathodic corrosion of Cu. The results (Fig. S31a) show that, despite we deliberately using an acidic environment (adding H2SO4 until the pH reaches 3), the local basic environment near the Cu electrode likely still result in the precipitation of hydroxides76,77 which contaminated the Cu electrode. As a result, the CV results cannot be used to detect Cu surface reconstruction or to judge whether the cathodic corrosion occurs. No significant structural changes were observed using TEM (Fig. S31b) after the reaction with multivalent cations. Hence it remains unclear whether multivalent cations can lead to or help to prevent cathodic corrosion.
The occurrence of alkali cation-induced cathodic corrosion in Cu does not negate the possibility of other mechanisms contributing to catalyst reconstruction. During the preparation and peer review of our paper, Magnussen and colleagues33 reported strong experimental evidence towards a CO-induced mechanism. Buonsanti and colleagues73 argued that CO-mediated corrosion involves a cationic Cu intermediate. To understand the role of CO in our proposed mechanism of alkali cation-induced cathodic corrosion, we conducted additional AIMD and structural optimization calculations. These examined the process of Cu extraction at the Cu-water interface with both K+ and CO present. Figure S32 reveals that CO tends to outcompete K+ for adsorption sites, and therefore likely inhibiting the corrosion mechanism outlined in Fig. 5. Nevertheless, our simulations also suggest that when CO molecules are distant, K+ can approach the surface to initiate the corrosion process. Given the significant difference in solubilities of K+ and CO in water, the impeding effect of CO should be limited. Recent works by Xu and colleagues78,79 indicate that CO coverage during CORR reactions is quite low and will decrease further as the electrode potential becomes more negative (e.g., approximately 0.05 monolayer at −0.6 V and 0.005 monolayer at −0.9 V). Moreover, our observations that the threshold potential for the alkali cation-induced cathodic corrosion to take place sit consistently at around −0.4 VRHE with (Fig. 6) or without CO present in the reaction suggest that variations in CO concentration or coverage do not significantly influence the process. Meanwhile, the H2-induced34,35 mechanisms for changing Cu morphologies could also be in play during a typical CO2RR or CORR experiment. Our findings, as depicted in Fig. 2f, demonstrate that under identical conditions at −1.1 VRHE, the morphological changes in Cu caused solely by the presence of H2SO4 in the electrolyte (pH = 1.16, Table S1, entry 7) were notably less pronounced than those observed when alkali cations were present in the electrolyte (pH = 1.28, Table S1, entry 8). An additional experiment conducted with K2SO4, wherein we adjusted the pH to 0.98 using H2SO4 (Table S1, entry 46), yielded significant morphological alterations again (Fig. S33). These findings underscore the pivotal role of alkali cations over the electrolyte’s pH in influencing the morphology of Cu. Consequently, it is reasonable to infer that several corrosion mechanisms might coexist, with alkali cation-cathodic corrosion possibly being the dominating process, especially considering the relatively low coverage of CO on the Cu catalyst in the reaction.
The identification of the alkali cation-induced cathodic corrosion in Cu catalysts marks a crucial first step toward devising effective mitigation strategies. In this study, we focused on identifying the occurrence of alkali cation-induced cathodic corrosion. However, our current methodologies, such as IL-TEM and CV, lack the temporal resolution necessary to analyze the kinetics of this corrosion process or to pinpoint its initiation time. It is reasonable to speculate that this type of corrosion will start as soon as the metallic copper is exposed to the electrolyte following the removal of surface oxides, though the oxide thickness and hence the timing may vary slightly from particle to particle. Our in situ XAFS results (Fig. 4) suggested that oxide layers should be removed within 15 min under typical reaction conditions, consistent with literature11 that reports completion of reduction within 10 min for a 40 nm Cu2O. Furthermore, Núria López and colleagues recently reported80 that, at weak reduction potentials (i.e., 0 VSHE), it takes approximately 208 s for an oxygen atom to diffuse through a 5 nm copper oxide layer. This simulation result largely agrees with our experimental observations.
It is possible that we have not seen the full potential of nanostructured Cu catalysts because of this corrosion behavior. In this work, we show that under conditions that do not prompt the alkali cation-induced cathodic corrosion, Cu nanocubes could provide stable selectivity advantages over Cu nanoparticles. It could be worthwhile to examine a broader range of nanostructured catalysts under conditions without the disruption of cathodic corrosion, which might get overlooked as they do not necessarily offer optimum performance in the beginning. Future research should also address many remaining questions about cathodic corrosion in Cu, including: Can the onset potential be tuned via changing reaction conditions? Is there any other way to control or even take advantage of the cathodic corrosion in Cu?
Methods
Chemicals
Copper (II) acetylacetonate (Cu(acac)2, 99.9%), copper bromide (CuBr, 99.999% trace metals basis), Oleylamine (OAm, 70%), Trioctylphosphine oxide (TOPO, 99%), sodium hydroxide (NaOH, reagent grade, ≥98%), Potassium bicarbonate (ACS reagent, 99.7%), Potassium bicarbonate (Aladdin, 99.99% trace metals basis), Potassium sulfate (Sigma, 99.99% trace metals basis), Lithium sulfate (Sigma, 99.99% trace metals basis), Cesium sulfate (Sigma, 99.99% trace metals basis), Sodium sulfate (ACS reagent, ≥99.0%, anhydrous), Magnesium sulfate (anhydrous, ReagentPlus®, ≥99.5%), Aluminum sulfate hydrate (99.99% trace metals basis). Sulfuric acid (H2SO4) was purchased from Sigma–Aldrich. Hexane and ethanol were technical grades and used without further purification.
Synthesis of Cu spherical nanoparticles Cu spheres (∼7 nm)
The nanoparticles were synthesized according to a modified procedure7. 1.5 mmol of Cu(acac)2, 5.7 mmol TOPO, and 35 mL OAm were loaded into a 100 mL three-necked flask under stirring. The mixture was heated at 80 °C for 30 min under Ar atmosphere. Then the mixture was further heated to 220 °C and reacted for 60 min, generating a reddish solution. The precipitate was cooled down to room temperature, washed five times with excessive ethanol, and dispersed in hexane. 25 nm commercial Cu spherical nanoparticles were purchased from Sigma–Aldrich, 774081, nanopowder, 25 nm particle size.
Synthesis of Cu nanocubes (∼40 nm)
Cu nanocubes were synthesized by adding 0.4 mmol of CuBr, 2 mmol TOPO, and 20 mL OAm into a 100 mL three-necked flask under stirring. The mixture was heated at 80 °C for 30 min under Ar atmosphere. Then, the mixture was further heated to 250 °C and reacted for 60 min, generating a reddish solution. The precipitate was cooled down to room temperature, washed five times with excessive ethanol, and dispersed in hexane.
Sample storage and transfer to limit air exposure
After being taken out from the inert synthesis environment, the as-synthesized Cu NCs is normally washed for five times, during which the sample might be exposed to air for less than 5 min. The particles were then stored in hexane overnight for the next day’s experiments. In the next day’s experiment, Cu NCs were dropped onto the electrode or TEM grid and sent to electrochemical reaction within 5 min; otherwise, the electrodes were put into a glovebox and waited for use.
Despite our efforts to limit air exposure (see “Methods” section), we still anticipate a thin surface oxide shell on the Cu NC. Through scanning transmission electron microscopy (STEM) imaging and electron energy loss spectroscopy (EELS), we show that the surface oxide layers on Cu NCs that were subjected to our typical sample handling procedures are approximately 2 nm in thickness (Fig. S2). We have also considered extreme cases wherein Cu catalysts were deliberately stored or exposed to air for extended periods (Figs. S3 and S4) as part of our control experiments, where the Cu oxide layer was found no thicker than 5 nm. Based on these findings, it is reasonable to assume that the oxide layer on the Cu NCs that will be discussed in detail in this manuscript will typically be around 2 nm and unlikely to exceed 5 nm.”
Cyclic voltammetry
Copper surface was treated under cathodic potential before voltammetric characterization. For the cathodization, the working electrode was prepared by dropping cast ethanol dispersion of 20–50 ug copper nanocubes onto the 0.2 cm2 glassy carbon on the rotation disk electrode. The catalyst loadings were kept identical across the samples in the batch used for any individual set of cyclic voltammetry (CV) comparisons. Before the electrochemical test, working electrode was treated by Ar plasma at 30 W for 60 s to remove surface ligands on the copper surface. TEM experiments confirmed that the morphology of the Cu nanocubes remain largely unchanged after the plasma treatment (Fig. S34). A PTFE electrochemical cell with a three-electrode configuration was employed, using a carbon rod through a Luggin capillary as the counter electrode to isolate the oxygen gas bubbles. For cathodization in acid, Hg/HgSO4 was used as a reference electrode. Hg/HgO was used as a reference electrode in alkaline electrolytes. Before cathodization, electrodes were connected to a potentiostat, and potentiostatic was run so that protective cathodic potential was applied to the copper surface immediately when it contacts with the electrolyte to avoid significant oxidation/dissolution of the copper surface at OCP. After cathodic treatment, copper surfaces were transferred and electrochemically characterized at room temperature by cyclic voltammetry in argon-saturated 0.1 M NaOH solutions at a sweep rate of 50 mVs−1. Transfer process takes several seconds from the cathodization cell to the characterization cell, during which the copper surface was mostly kept within the cell flowed with Ar to decrease the air exposure. For voltammetric, a PTFE electrochemical cell with a three-electrode configuration was employed, using a carbon rod as the counter electrode and an Hg/HgO electrode as the reference electrode. The voltammetries were normalized to yield identical double-layer (DL) thicknesses within a potential region where the voltammetries exhibited capacitive behavior (+0.2 V < E < +0.28 V, +0.02 V < E < +0.08 V)81. All electrolytes were pre-electrolyzed for 3–5 h on the clean carbon paper to remove electrolyte impurities. All electrolytes were bubbled with Argon for 1 h before measurement and kept being bubbled during measurement. In this work, all potentials are referred to RHE. The electrode potential was controlled using a CHI760E potentiostat.
Identical location transmission electron microscopy (IL-TEM)
Identical location TEM was achieved by positioning copper particles on an electrically conductive and corrosion-resistant Au grid that can be used both as a working electrode in an electrochemical cell and as a sample holder during TEM (Fig. 1b). A custom-made PTFE cap with a hole in the center was used to fix the TEM grid onto the surface of glassy carbon on rotation disk electrode. Both sides of the gold grid were covered by carbon deposition to block gold surface from electrochemical reaction and copper particles supported on the carbon film were observed under TEM. By taking overview images at progressively increasing magnification and using tracking markers, locations of interest in the untreated particles are selected and recorded. This step was repeated after an ex-situ electrochemical test, allowing the evaluation of the identical particles. After the electrochemical test, the grid was taken out and dried on a blotting paper for seconds before it was put into a glovebox and wait for the characterization. The electrochemical reaction was performed in the electrochemical cell with a three-electrode configuration, with a carbon rod through a Luggin capillary as the counter electrode and Hg/HgSO4 for the acidic electrolyte, and Hg/HgO for the alkaline electrolyte as reference electrode. The electrolyte was bubbled with Argon or CO2 for 1 h before measurement. Before immersion of the working electrode into the electrolyte, electrodes were connected to potentiostat, and potentiostatic was run so that protective cathodic potential was applied to the copper surface immediately when it contacts with the electrolyte to avoid further oxidation/dissolution of copper surface in the electrolyte at OCP. After electrolysis for the targeted time, the copper surface was extracted from the electrolyte with holding potential. For Ex-situ TEM imaging, a TEM grid was pressed onto the glassy carbon with a drop of hexane atop to collect the reacted nanoparticles after electrolysis.
Electron microscopy characterization
Scanning Transmission Electron Microscopy High angle annular dark field (HAADF) imaging, X-ray Energy Dispersive Spectroscopy (X-EDS), and Electron Energy Loss Spectroscopy (EELS) studies were conducted on a JEOL JEM ARM 200CF in the National University of Singapore, equipped with an Oxford Instrument X-ray Energy Dispersive Spectrometer and a Gatan Image Filter (GIF) system. In a typical STEM-EELS measurement, a probe current of around 100pA was utilized, with a dwell time of approximately 20 ms per pixel. The convergence half angle is about 29 mrad and the collection half angle is about 36 mrad for the STEM-EELS measurement. To generate the elemental map, background removal, signal integration, and multiple linear least square fitting were performed using Gatan Digitalmicrograph software.
X-ray absorption fine structure spectroscopy
XAFS spectra around the Cu K-edge (8979 eV) were collected at the XAFCA beamline of Singapore Synchrotron Light Source (SSLS) in transmission mode82. The double-crystal Si (111) monochromator was used for measurements. The size of the beam at the sample position was ca. 2 mm (h) × 1 mm. All XAFS data analyses were performed with the Athena software package to extract XANES83. The electrochemical setup with three electrodes and a Polyetheretherketone electrochemical cell was used for the reaction. The electrochemical setup consisted of an Ag/AgCl reference electrode, a carbon counter electrode, and a catalyst-modified carbon cloth (ca. 10 mm × 10 mm geometric area) working electrode. The catalyst ink was dropping cast onto carbon cloth. The electrolyte was first bubbled with CO2 gas for 30 min and then a constant potential was applied. The XAFS measurements were recorded simultaneously while performing the chronoamperometric measurements.
CO2RR measurements
The experiments were implemented at an electrochemical workstation (CHI760E) under ambient pressure and temperature. A gas-tight two-compartment cell configuration was employed with a counter electrode of Pt mesh and reference electrode of Ag/AgCl electrode and electrolyte of 0.1 M KHCO3. The electrolyte was prepared by dissolving KHCO3 in DI water and stored in a plastic volumetric flask. A piece of anion-exchange membrane with 2.5*2.5 cm2 area and 70um thickness was served to separate the counter and working electrodes in the two compartments. Working electrodes were prepared by evaporating hexane solution containing around 50ug Cu NCs within a squared area of 1cm2 on the glassy carbon substrates. The loading was calculated by multiplying the Cu concentration of the ink with the volume of the ink dropped onto the substrate. Here, the loading amounts were chosen to yield a decent Faradaic efficiency towards multicarbon products. The working electrodes were then held at a constant bias of −1.1 V vs. RHE using chronoamperometry for a set time of up to 10 h. During electrolysis, CO2 was constantly bubbled through the electrolyte at a flow rate of 20 sccm. The flow rate of CO2 was controlled with a mass flow controller. All potentials were corrected for iR-loss compensation by electrochemical impedance spectroscopy (EIS) and converted to potentials versus the reversible hydrogen electrode (RHE) using the following equation (1): \(E\left({vs}.{RHE}\right)=E\left({vs}.{Ag}/{AgCl}\right)-{iR}+ 0.197V+ 0.0591V\times {pH}\). The gaseous products were monitored by an online gas chromatograph, equipped with a thermal conductivity detector (TCD) detector for H2 and a flame ionization detector (FID) detector for hydrocarbon quantification. High-purity He gas (99.999%) was used as the carrier gas for all compartments of the GC. A GC run repeats every 29.5 minutes. The GC was calibrated using calibration curves of analytical gas standards. The calculation of Faradaic efficiency (FE) for gaseous products based on the following equation (2): \({{FE}}_{i}\left(\%\right)={j}_{i}/{j}_{{total}}\times 100={zF}\times \left(Q{P}_{0}{V}_{i}/{RT}\right)/{j}_{{total}}\). Here, the total current was measured by the potentiostat, and the partial currents were obtained from the areas of GC chromatogram peaks where Vi is the volume concentration of gas product i based on the calibration of GC. Q is the flow rate of CO2, z is the number of electrons transferred for reduction to product i, F is the Faradaic constant, P0 is atmosphere pressure, T is room temperature, and R is the ideal gas constant, 8.314 J·mol/K. 1 ml electrolyte was collected from both cathode and anode chamber at 1 h and 10 h of reaction and the containing liquid products were analyzed by 1H Nuclear Magnetic Resonance (NMR) spectrum (Bruker 400 MHZ system). The Faradic Efficiency (FE) of each product was calculated by following equation (3): \({{{{{\rm{FE}}}}}}\left(\%\right)={amount\; of\; the\; product}\times n\times F/C\times 100\), where n represents the number of electrons transferred, F represents the Faradaic constant, and C represents the total Coulomb number.
CORR measurements
The measurements were conducted in a flow cell, which was assembled from the sequential stacking of a gas chamber, a catalyst-loaded GDE cathode, a catholyte chamber (where an Ag/AgCl reference electrode was located), an anion-exchange membrane, an anolyte chamber, and an IrO2-loaded Ti plate anode. The working electrodes of Cu cube and Cu sphere were prepared as follows: 1 mg Cu cube/Cu sphere power was dispersed in a mixed solution with 1 mL of ethanol and 4 μL of 5 wt% Nafion solution to form a catalyst ink. The ink was dispersed in an ultrasonic machine for more than 10 minutes. And then the ink was sprayed onto carbon fiber (YSL-30T) paper with 1 mg cm−2 to form a smooth catalyst film.
During COR measurements, 21 sccm of CO was continuously fed to the working electrode through the mass flow controller. And the electrolyte (1 M KOH) was pumped to circulate through the flow cell at the rate of 15 mL min−1 by a peristaltic pump. The electrolyte was prepared by dissolving KOH in DI water and stored in a plastic bottle. The Bio-Logic VMP3 multichannel potentiostat/galvanostat was applied for the electrochemical measurements. The reference electrode was Ag/AgCl and the potential was converted to RHE with necessary iR compensation by equation (1). The ohmic-drop correction of the potentials applied was carried out manually using the resistance measured by the electrochemical impedance spectroscopy under open circuit potentials.
Gaseous reduction products were injected into an online gas chromatograph (GC, Shimadzu 2014) to analyze the concentration of each gas product. And liquid products were collected in the centrifuge tube and were identified by 1H Nuclear Magnetic Resonance (NMR) spectrum (Bruker 400 MHZ system). 0.6 ml electrolyte was taken every 1 h during the 10 h CORR from the initial 15 ml circulated catholyte. The Faradic Efficiency (FE) of each product was calculated by equation (3).
Computational investigation
All calculations were performed using Kohn-Sham DFT as implemented in VASP84. The unknown exchange and correlation functional was approximated by the revised Perdew−Burke−Erznzerhof (RPBE)85. Van der Waals (vdW) interactions were treated with the D3 method with zero damping86. The wavefunctions of the valence electrons were expanded as plane waves up to a cut-off of 400 eV87,88. Projector-augmented wave (PAW) potentials were used for core electrons89. A smearing width of 0.3 eV together with a second-order Methfessel−Paxton scheme90.
To model the dissolution reaction, a three-layer copper slab containing 24 atoms modeling the Cu(001)/water interface was put in direct contact with 26 explicit water molecules followed by a region where the effect of water is described by an implicit electrostatic model. The 26 water molecules fill a 15 Å-long region to maintain the water density ~1 g/cm3. A K ion was initially added 2.14 Å from the Cu(001) surface and then equilibrated. The Cu surface was pre-relaxed with DFT and 26 water molecules were pre-organized with classic molecular dynamics using LAMMPs. The implicit water was applied using VASPsol91,92.
Ab initio molecular dynamics (AIMD) simulations were performed at the Γ point with a time step of 1.0 fs and hydrogen mass of 3 amu. Simulation of a negative voltage to match the experimental electrode potential is realized by adding extra electrons into the cell and determined from the electrostatic potential of implicit water and the system’s Fermi level. Two different voltages were simulated, namely −1.31 VRHE by adding 3 electrons and −0.35 VRHE by adding 0.2 electrons. Temperature was ramped to 300 K during the first 3 ps using the Nose−Hoover thermostat93,94, and then the system was equilibrated at 300 K for 5 ps. The slow-growth method95 was employed to generate Cu extraction trajectory by controlling the distance between the Cu atom and bottom Cu layer, between the K atom and bottom Cu layer, and between the K and Cu atom. A trajectory of 2.5 Å in a period of 5 ps was generated for each system of different voltages. Five windows were taken from the trajectory and their free energy gradient was calculated using constrained constant-Fermi-level Blue-Moon AIMD41,62,63,64,65,66. The reaction coordinate - the Cu distance from the surface - was fixed for each window, and the Fermi level was kept within ±0.05 eV of the target value from the 5 ps equilibration by adding/removing electrons when it gets out of range.
Data availability
The computational data associated with this study is available on zenodo https://doi.org/10.5281/zenodo.8059745. The experiment-related source data were also uploaded to zenodo. https://doi.org/10.5281/zenodo.10259206. Source data are provided with this paper.
Change history
19 July 2024
A Correction to this paper has been published: https://doi.org/10.1038/s41467-024-50241-z
References
Jensen, S. H., Larsen, P. H. & Mogensen, M. Hydrogen and synthetic fuel production from renewable energy sources. Int. J. Hydrog. Energy 32, 3253–3257 (2007).
Whipple, D. T. & Kenis, P. J. A. Prospects of CO2 utilization via direct heterogeneous electrochemical reduction. J. Phys. Chem. Lett. 1, 3451–3458 (2010).
Hori, Y. Electrochemical CO2 reduction on metal electrodes. In Modern Aspects of Electrochemistry (eds Vayenas, C. G., White, R. E. & Gamboa-Aldeco, M. E.) 89–189 (Springer New York, New York, NY, 2008).
Nitopi, S. et al. Progress and perspectives of electrochemical CO2 reduction on copper in aqueous electrolyte. Chem. Rev. 119, 7610–7672 (2019).
Hori, Y., Takahashi, I., Koga, O. & Hoshi, N. Electrochemical reduction of carbon dioxide at various series of copper single crystal electrodes. J. Mol. Catal. A Chem. 199, 39–47 (2003).
Bagger, A., Ju, W., Varela, A. S., Strasser, P. & Rossmeisl, J. Electrochemical CO2 reduction: classifying Cu facets. ACS Catal. 9, 7894–7899 (2019).
Loiudice, A. et al. Tailoring copper nanocrystals towards C2 products in electrochemical CO2 reduction. Angew. Chem. Int Ed. Engl. 55, 5789–5792 (2016).
Cheng, D. et al. The nature of active sites for carbon dioxide electroreduction over oxide-derived copper catalysts. Nat. Commun. 12, 395 (2021).
Popovic, S. et al. Stability and degradation mechanisms of copper-based catalysts for electrochemical CO2 reduction. Angew. Chem. Int Ed. Engl. 59, 14736–14746 (2020).
Okatenko, V. et al. Alloying as a strategy to boost the stability of copper nanocatalysts during the electrochemical CO2 reduction reaction. J. Am. Chem. Soc. 145, 5370–5383 (2023).
Zhu, P. et al. Direct and continuous generation of pure acetic acid solutions via electrocatalytic carbon monoxide reduction. Proc. Natl Acad. Sci. USA 118, e2010868118 (2021).
Liu, W. et al. Electrochemical CO2 reduction to ethylene by ultrathin CuO nanoplate arrays. Nat. Commun. 13, 1877 (2022).
Moller, T. et al. Electrocatalytic CO2 reduction on CuOx nanocubes: tracking the evolution of chemical state, geometric structure, and catalytic selectivity using operando spectroscopy. Angew. Chem. Int Ed. Engl. 132, 17974–17983 (2020).
Wang, X. et al. Morphology and mechanism of highly selective Cu(II) oxide nanosheet catalysts for carbon dioxide electroreduction. Nat. Commun. 12, 794 (2021).
Ren, D., Wong, N. T., Handoko, A. D., Huang, Y. & Yeo, B. S. Mechanistic insights into the enhanced activity and stability of agglomerated Cu nanocrystals for the electrochemical reduction of carbon dioxide to n-propanol. J. Phys. Chem. Lett. 7, 20–24 (2016).
Ma, W. et al. Electrocatalytic reduction of CO2 and CO to multi-carbon compounds over Cu-based catalysts. Chem. Soc. Rev. 50, 12897–12914 (2021).
Simon, G. H., Kley, C. S. & Roldan Cuenya, B. Potential-dependent morphology of copper catalysts during CO2 electroreduction revealed by in situ atomic force microscopy. Angew. Chem. Int Ed. Engl. 60, 2561–2568 (2021).
Phan, T. H. et al. Emergence of potential-controlled Cu-nanocuboids and graphene-covered Cu-nanocuboids under operando CO2 electroreduction. Nano Lett. 21, 2059–2065 (2021).
Speck, F. D. & Cherevko, S. Electrochemical copper dissolution: a benchmark for stable CO2 reduction on copper electrocatalysts. Electrochem. Commun. 115, 106739 (2020).
Huang, J. et al. Potential-induced nanoclustering of metallic catalysts during electrochemical CO2 reduction. Nat. Commun. 9, 3117 (2018).
Grosse, P. et al. Dynamic changes in the structure, chemical state and catalytic selectivity of Cu nanocubes during CO2 electroreduction: size and support effects. Angew. Chem. Int Ed. Engl. 57, 6192–6197 (2018).
Kim, J. et al. Branched copper oxide nanoparticles induce highly selective ethylene production by electrochemical carbon dioxide reduction. J. Am. Chem. Soc. 141, 6986–6994 (2019).
Grosse, P. et al. Dynamic transformation of cubic copper catalysts during CO2 electroreduction and its impact on catalytic selectivity. Nat. Commun. 12, 6736 (2021).
Jung, H. et al. Electrochemical fragmentation of Cu2O nanoparticles enhancing selective C-C coupling from CO2 reduction reaction. J. Am. Chem. Soc. 141, 4624–4633 (2019).
Choi, C. et al. Highly active and stable stepped Cu surface for enhanced electrochemical CO2 reduction to C2H4. Nat. Catal. 3, 804–812 (2020).
Yang, Y. et al. Operando studies reveal active Cu nanograins for CO2 electroreduction. Nature 614, 262–269 (2023).
Raaijman, S. J., Arulmozhi, N. & Koper, M. T. M. Morphological stability of copper surfaces under reducing conditions. ACS Appl Mater. Interfaces 13, 48730–48744 (2021).
Aran-Ais, R. M. et al. Imaging electrochemically synthesized Cu2O cubes and their morphological evolution under conditions relevant to CO(2) electroreduction. Nat. Commun. 11, 3489 (2020).
Li, Y. et al. Electrochemically scrambled nanocrystals are catalytically active for CO2-to-multicarbons. Proc. Natl Acad. Sci. USA 117, 9194–9201 (2020).
Kim, Y.-G. et al. Surface reconstruction of pure-Cu single-crystal electrodes under CO-reduction potentials in alkaline solutions: a study by seriatim ECSTM-DEMS. J. Electroanal. Chem. 780, 290–295 (2016).
Lee, S. H. et al. Oxidation state and surface reconstruction of Cu under CO2 reduction conditions from in situ X-ray characterization. J. Am. Chem. Soc. 143, 588–592 (2021).
Wilde, P. et al. Is Cu instability during the CO(2) reduction reaction governed by the applied potential or the local CO concentration? Chem. Sci. 12, 4028–4033 (2021).
Amirbeigiarab, R. et al. Atomic-scale surface restructuring of copper electrodes under CO2 electroreduction conditions. Nat. Catal. 6, 837–846 (2023).
Matsushima, H., Taranovskyy, A., Haak, C., Grunder, Y. & Magnussen, O. M. Reconstruction of Cu(100) electrode surfaces during hydrogen evolution. J. Am. Chem. Soc. 131, 10362–10363 (2009).
Tackett, B. M., Raciti, D., Hight Walker, A. R. & Moffat, T. P. Surface hydride formation on Cu(111) and its decomposition to form H2 in acid electrolytes. J. Phys. Chem. Lett. 12, 10936–10941 (2021).
Scholten, F., Nguyen, K. C., Bruce, J. P., Heyde, M. & Roldan Cuenya, B. Identifying structure-selectivity correlations in the electrochemical reduction of CO2: a comparison of well-ordered atomically clean and chemically etched copper single-crystal surfaces. Angew. Chem. Int Ed. Engl. 60, 19169–19175 (2021).
Arán-Ais, R. M., Scholten, F., Kunze, S., Rizo, R. & Roldan Cuenya, B. The role of in situ generated morphological motifs and Cu(i) species in C2+ product selectivity during CO2 pulsed electroreduction. Nat. Energy 5, 317–325 (2020).
Malkani, A. S., Dunwell, M. & Xu, B. Operando spectroscopic investigations of copper and oxide-derived copper catalysts for electrochemical CO reduction. ACS Catal. 9, 474–478 (2018).
Hersbach, T. J. P. & Koper, M. T. M. Cathodic corrosion: 21st century insights into a 19th century phenomenon. Curr. Opin. Electrochem. 26, 100653 (2021).
Hersbach, T. J. P. et al. Alkali metal cation effects in structuring Pt, Rh, and Au surfaces through cathodic corrosion. ACS Appl. Mater. Interfaces 10, 39363–39379 (2018).
Evazzade, I., Zagalskaya, A. & Alexandrov, V. Revealing elusive intermediates of platinum cathodic corrosion through DFT simulations. J. Phys. Chem. Lett. 13, 3047–3052 (2022).
Gu, J. et al. Modulating electric field distribution by alkali cations for CO2 electroreduction in strongly acidic medium. Nat. Catal. 5, 268–276 (2022).
Monteiro, M. C. O. et al. Absence of CO2 electroreduction on copper, gold and silver electrodes without metal cations in solution. Nat. Catal. 4, 654–662 (2021).
Garcia de Arquer, F. P. et al. CO2 electrolysis to multicarbon products at activities greater than 1 A cm-2. Science 367, 661–666 (2020).
Zhang, Z. et al. Molecular understanding of the critical role of alkali metal cations in initiating CO2 electroreduction on Cu(100) surface. Nat. Commun. 15, 612 (2024).
Tang, W. et al. The importance of surface morphology in controlling the selectivity of polycrystalline copper for CO2 electroreduction. Phys. Chem. Chem. Phys. 14, 76–81 (2012).
Schouten, K. J. P., Pérez Gallent, E. & Koper, M. T. M. Structure sensitivity of the electrochemical reduction of carbon monoxide on copper single crystals. ACS Catal. 3, 1292–1295 (2013).
Garza, A. J., Bell, A. T. & Head-Gordon, M. Mechanism of CO2 reduction at copper surfaces: pathways to C2 products. ACS Catal. 8, 1490–1499 (2018).
Li, C. W., Ciston, J. & Kanan, M. W. Electroreduction of carbon monoxide to liquid fuel on oxide-derived nanocrystalline copper. Nature 508, 504–507 (2014).
Wang, L. et al. Electrochemically converting carbon monoxide to liquid fuels by directing selectivity with electrode surface area. Nat. Catal. 2, 702–708 (2019).
Wang, X. et al. Mechanistic reaction pathways of enhanced ethylene yields during electroreduction of CO2-CO co-feeds on Cu and Cu-tandem electrocatalysts. Nat. Nanotechnol. 14, 1063–1070 (2019).
Mayrhofer, K. J. J. et al. Fuel cell catalyst degradation on the nanoscale. Electrochem. Commun. 10, 1144–1147 (2008).
Schouten, K. J. P., Gallent, E. P. & Koper, M. T. M. The electrochemical characterization of copper single-crystal electrodes in alkaline media. J. Electroanal. Chem. 699, 6–9 (2013).
Kreizer, I. V., Marshakov, I. K., Tutukina, N. M. & Zartsyn, I. D. Partial reactions of copper dissolution under cathodic polarization in acidic media. Prot. Met. 40, 23–25 (2004).
Hersbach, T. J., Yanson, A. I. & Koper, M. T. Anisotropic etching of platinum electrodes at the onset of cathodic corrosion. Nat. Commun. 7, 12653 (2016).
Yanson, A. I. et al. Cathodic corrosion: a quick, clean, and versatile method for the synthesis of metallic nanoparticles. Angew. Chem. Int Ed. Engl. 50, 6346–6350 (2011).
Tröger, L. et al. Full correction of the self-absorption in soft-fluorescence extended x-ray-absorption fine structure. Phys. Rev. B Condens. Matter 46, 3283–3289 (1992).
Pfalzer, P. et al. Elimination of self-absorption in fluorescence hard-x-ray absorption spectra. Phys. Rev. B Condens. Matter 60, 9335–9339 (1999).
Booth, C. H. & Bridges, F. Improved self-absorption correction for fluorescence measurements of extended x-ray absorption fine-structure. Phys. Scr. 2005, 202 (2005).
Han, A. et al. Isolating contiguous Pt atoms and forming Pt-Zn intermetallic nanoparticles to regulate selectivity in 4-nitrophenylacetylene hydrogenation. Nat. Commun. 10, 3787 (2019).
Xie, M. et al. Intermetallic single-atom alloy In–Pd bimetallene for neutral electrosynthesis of ammonia from nitrate. J. Am. Chem. Soc. 145, 13957–13967 (2023).
Carter, E. A., Ciccotti, G., Hynes, J. T. & Kapral, R. Constrained reaction coordinate dynamics for the simulation of rare events. Chem. Phys. Lett. 156, 472–477 (1989).
Bonnet, N., Morishita, T., Sugino, O. & Otani, M. First-principles molecular dynamics at a constant electrode potential. Phys. Rev. Lett. 109, 266101 (2012).
Bouzid, A. & Pasquarello, A. Atomic-scale simulation of electrochemical processes at electrode/water interfaces under referenced bias potential. J. Phys. Chem. Lett. 9, 1880–1884 (2018).
Bouzid, A. & Pasquarello, A. Redox levels through constant fermi-level ab initio molecular dynamics. J. Chem. Theory Comput. 13, 1769–1777 (2017).
Sprik, M. & Ciccotti, G. Free energy from constrained molecular dynamics. J. Chem. Phys. 109, 7737–7744 (1998).
Resasco, J. et al. Promoter effects of alkali metal cations on the electrochemical reduction of carbon dioxide. J. Am. Chem. Soc. 139, 11277–11287 (2017).
Huang, J. E. et al. CO(2) electrolysis to multicarbon products in strong acid. Science 372, 1074–1078 (2021).
Christensen, O. et al. Can the CO2 reduction reaction be improved on Cu: selectivity and intrinsic activity of functionalized Cu surfaces. ACS Catal. 12, 15737–15749 (2022).
Ruditskiy, A., Peng, H. C. & Xia, Y. Shape-controlled metal nanocrystals for heterogeneous catalysis. Annu Rev. Chem. Biomol. Eng. 7, 327–348 (2016).
Wang, N. et al. Suppressing the liquid product crossover in electrochemical CO2 reduction. SmartMat 2, 12–16 (2021).
Vavra, J., Shen, T. H., Stoian, D., Tileli, V. & Buonsanti, R. Real-time monitoring reveals dissolution/redeposition mechanism in copper nanocatalysts during the initial stages of the CO2 reduction reaction. Angew. Chem. Int Ed. Engl. 60, 1347–1354 (2021).
Vavra, J. et al. Solution-based Cu+ transient species mediate the reconstruction of copper electrocatalysts for CO2 reduction. Nat. Catal. 7, 89–97 (2024).
Ringe, S. et al. Understanding cation effects in electrochemical CO2 reduction. Energy Environ. Sci. 12, 3001–3014 (2019).
Monteiro, M. C. O., Dattila, F., López, N. & Koper, M. T. M. The role of cation acidity on the competition between hydrogen evolution and CO2 reduction on gold electrodes. J. Am. Chem. Soc. 144, 1589–1602 (2022).
Monteiro, M. C. O. & Koper, M. T. M. Alumina contamination through polishing and its effect on hydrogen evolution on gold electrodes. Electrochim. Acta 325, 134915 (2019).
Bhargava, S. S. et al. Exploring multivalent cations-based electrolytes for CO2 electroreduction. Electrochim. Acta 394, 139055 (2021).
Hou, J., Chang, X., Li, J., Xu, B. & Lu, Q. Correlating CO coverage and CO electroreduction on Cu via high-pressure in situ spectroscopic and reactivity investigations. J. Am. Chem. Soc. 144, 22202–22211 (2022).
Chang, X. et al. C-C coupling is unlikely to be the rate-determining step in the formation of C2+ products in the copper-catalyzed electrochemical reduction of CO. Angew. Chem. Int. Ed. Engl. 61, e202111167 (2022).
Lian, Z., Dattila, F. & López, N. Stability and lifetime of diffusion-trapped oxygen in oxide-derived copper CO2 reduction electrocatalysts. Nat. Catal. 7, 401–411 (2024).
Raaijman, S. J., Arulmozhi, N., da Silva, A. H. M. & Koper, M. T. M. Clean and reproducible voltammetry of copper single crystals with prominent facet-specific features using induction annealing. J. Electrochem. Soc. 168, 096510 (2021).
Du, Y. et al. XAFCA: a new XAFS beamline for catalysis research. J. Synchrotron Radiat. 22, 839–843 (2015).
Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2005).
Kohn, W. & Sham, L. J. Self-consistent equations including exchange and correlation effects. Phys. Rev. 140, A1133–A1138 (1965).
Hammer, B., Hansen, L. B. & Nørskov, J. K. Improved adsorption energetics within density-functional theory using revised Perdew-Burke-Ernzerhof functionals. Phys. Rev. B 59, 7413–7421 (1999).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B Condens. Matter 54, 11169–11186 (1996).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B Condens. Matter 59, 1758–1775 (1999).
Methfessel, M. & Paxton, A. T. High-precision sampling for Brillouin-zone integration in metals. Phys. Rev. B Condens Matter 40, 3616–3621 (1989).
Mathew, K., Sundararaman, R., Letchworth-Weaver, K., Arias, T. A. & Hennig, R. G. Implicit solvation model for density-functional study of nanocrystal surfaces and reaction pathways. J. Chem. Phys. 140, 084106 (2014).
Mathew, K., Kolluru, V. S. C., Mula, S., Steinmann, S. N. & Hennig, R. G. Implicit self-consistent electrolyte model in plane-wave density-functional theory. J. Chem. Phys. 151, 234101 (2019).
Nose, S. A unified formulation of the constant temperature molecular dynamics methods. J. Chem. Phys. 81, 511–519 (1984).
Hoover, W. G. Canonical dynamics: equilibrium phase-space distributions. Phys. Rev. A Gen. Phys. 31, 1695–1697 (1985).
Woo, T. K., Margl, P. M., Blöchl, P. E. & Ziegler, T. A combined Car−Parrinello QM/MM implementation for ab initio molecular dynamics simulations of extended systems: application to transition metal catalysis. J. Phys. Chem. B 101, 7877–7880 (1997).
Acknowledgements
We acknowledge the funding support by the National Research Foundation (NRF) Singapore, under its NRF Fellowship (NRF-NRFF11-2019-0002). S.L. would like to acknowledge the support of the Chinese Scholarship Council. A.B.W. would like to acknowledge support via the Presidential Young Professorship (PYP) start-up funds at the National University of Singapore (A-0009245-05-00). L.W. acknowledges financial support from A*STAR (Agency for Science, Technology and Research) under its LCERF1 program (Award No U2102d2002), Centre for Hydrogen Innovations at NUS (CHI-P2022-06), and NRF Fellowship (NRF-NRFF13-2021-0007). P.C. and Y.L. acknowledge funding from the National Research Foundation under the NRF Fellowship NRF-NRFF12-2020-0012. J.L. acknowledges the support from the Agency for Science, Technology, and Research (A*STAR) under its AME IRG Grant (Project No. M22K2c0082). K.Y., A.C.N., and T.F.J. acknowledge support for evaluating Cu corrosion using mass spectrometry from the Liquid Sunlight Alliance, which is supported by the Basic Energy Sciences program of the US Department of Energy Office of Science through the Fuels from Sunlight Hub under award number DE-SC0021266. We want to express our special thanks to Dr Qiang Gao and Prof. Huiyuan Zhu from the University of Virginia for preparing some Cu NCs for online mass spectroscopy analysis. We also wish to thank Mr Han Xu and Mr Yukun Zhao from Professor Jiong Lu’s group at NUS, Singapore for their kind and timely help on getting the NMR results during the paper-revision process.
Author information
Authors and Affiliations
Contributions
S. Liu and Q. He conceived the idea and led the project. S. Liu carried out the sample preparation, IL-TEM experiments, CO2RR, and CV measurement under the supervision of Q. He and J. Lu, with many advices from L. Wang and A. Wong, and the technical help from H. Xu, X. Li, and W. Zang. M. Su and W. Liu also helped with Cu NCs synthesis and some TEM screening. Y. Li implemented the grand-potential AMID methodology carried out the simulation part of the study under the guidance of P. Canepa. D. Wang, S. Liu carried CORR measurement under the guidance of L. Wang, helped by Y.L. Wang; S. Liu and S. Xi carried out the in situ XAFS study. K. Yan, A. Nielander carried out preliminary online mass spectroscopy study under the guidance of T. Jaramillo. S. Liu, Y. Li, and Q. He drafted the paper and all authors participated in the manuscript discussion and polishing.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Federico Dattila, and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, S., Li, Y., Wang, D. et al. Alkali cation-induced cathodic corrosion in Cu electrocatalysts. Nat Commun 15, 5080 (2024). https://doi.org/10.1038/s41467-024-49492-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-49492-7