Abstract
Organic ultralong room-temperature phosphorescence (RTP) usually emerges instantly and immediately decays after excitation removal. Here we report a new delayed RTP that is postponed by dozens of milliseconds after excitation removal and decays in two steps including an initial increase in intensity followed by subsequent decrease in intensity. The delayed RTP is achieved through introduction of phosphines into carbazole emitters. In contrast to the rapid energy transfer from single-molecular triplet states (T1) to stabilized triplet states (Tn*) of instant RTP systems, phosphine groups insert their intermediate states (TM) between carbazole-originated T1 and Tn* of carbazole-phosphine hybrids. In addition to markedly increasing emission lifetimes by ten folds, since TM → Tn* transition require >30 milliseconds, RTP is thereby postponed by dozens of milliseconds. The emission character of carbazole-phosphine hybrids can be used to reveal information through combining instant and delayed RTP, realizing multi-level time resolution for advanced information, biological and optoelectronic applications.
Similar content being viewed by others
Introduction
Organic ultralong room temperature phosphorescence (RTP) is a kind of afterglow from organic systems after excitation removal, which can persist several seconds and even hours1. With the merits of low cost and large-scale production, diverse applications of organic RTP materials were demonstrated, e.g. information encryption2,3, anti-counterfeiting4,5, biological imaging6,7, sensing8,9, and optoelectronic devices10,11. The rapid emergence of organic RTP materials in recent years is owing to the development of several approaches effectively overcoming the limitations of spin-forbidden triplet radiation and collision-induced triplet nonradiation by environmental factors (moisture, oxygen and temperature, etc)12,13,14, including crystallization15,16,17, self-assembly18,19, H-aggregation20,21,22,23, polymerization24,25,26 and doping27,28,29,30,31,32,33. As a consequence, efficient and long-persist organic RTP in whole visible-light range were already demonstrated34,35,36,37. On the one hand, non-covalent interactions (e.g. π-π stacking20 and intermolecular hydrogen bond) and rigid matrixes can prevent air infiltration and phonon vibration, therefore stabilize triplet excitons and suppress triplet nonradiation. On the other hand, besides incorporating heavy-atom effects of Br and I, aromatic heterocycles containing N, O, P and/or S atoms are also introduced to break through the El-Sayed rule14 for increasing triplet population, because their 1(n, π*)-dominant singlet excited states can markedly enhance spin-orbital coupling and intersystem crossing to 3(π, π*)-featured triplet states, in contrast to 1(π, π*) states38,39. These structural designs were commonly combined to elongate lifetimes and improve quantum efficiencies.
It is noteworthy that all reported organic RTP phenomena are unidirectionally time correlated: after excitation, molecules transit to the first triplet states (T1) from the first singlet excited states (S1) through intersystem crossing, and then the excited energy is trapped by stabilized triplet states (Tn*) for afterglow (Fig. 1a). The same 3(π, π*) characters of T1 and Tn* leads to microsecond-level transition between them. So, for the human eye, this kind of RTP is instantaneous, and concurrent with fluorescence and phosphorescence, respectively, from the S1 and T1 states. In this case, after excitation removal, fluorescence and phosphorescence disappear, and RTP can be immediately observed by the human eye without any postponement. This kind of RTP phenomena can be defined as “instant” RTP, which has the intrinsic limitation in time resolution for naked eyes, regarding information hierarchy. Obviously, “delayed” RTP is “ideal” for realizing in-turn information display along timeline, which remains a big challenge in accurately modulating excited-state transitions. One feasible approach is inserting 3(n, π*)-featured triplet state as intermediate state (TM) between 3(π, π*)-featured T1 and Tn* state. In addition to the elongate energy transfer process, the different triplet characteristics could largely postpone transitions between, leading to delayed RTP. Nevertheless, despite incorporating 3(n, π*) state, instant RTP channel still exists, therefore competes with delayed RTP. In this sense, 3(n, π*)-featured mediate groups in the molecules are crucial.
The phosphorus atom has sufficient n electrons to enhance intersystem crossing40,41. Meanwhile, sp3 configuration of phosphine groups would modify intermolecular interactions, therefore modulate exited-state contributions of 3(n, π*) and 3(π, π*) components41,42,43,44,45. More importantly, we recently found that in p-carbazolylphenyl-diphenylphosphine, diphenylphosphine group provide 3(n, π*) energy level below 3(π, π*) energy level of carbazole group, rendering twofold increased RTP lifetime46. It can be expected that energy level relationship of carbazole-phosphine hybrids can be further accurately optimized to postpone Tn* population by dozens of milliseconds, reaching the time limit can be recognized by the human eyes.
As a proof of concept, we construct two carbazole and bromine-substituted phosphine derivatives named DCzSBrSP and DCzSBrSPO (Fig. 1b and Supplementary Note 1, Supplementary Fig. 1). Compared to brominated bicarbazole analogs DCzSBr and DCzDBr with instant RTP, whose two carbazoles at ortho position enhance the stability of 3(π, π*) states, diphenylphosphine and diphenylphosphine oxide of DCzSBrSP and DCzSBrSPO are introduced as 3(n, π*)-featured mediate groups. The heavy atom effect of bromines is utilized to further improve intersystem crossing and triplet radiation. Under UV excitation at 365 nm, the emissions from the powders are white and yellow for DCzSBr and DCzDBr, and greenish blue for DCzSBrSP and DCzSBrSPO (Fig. 1c). After excitation removal, DCzSBr and DCzDBr immediately exhibit orange RTP with durations of ~2 s. In contrast, yellow RTP from DCzSBrSP can still be recognized at ~8 s. More importantly, RTP intensity of DCzSBrSP gradually increase during the initial 200 ms and then decrease, indicating the desired “delayed” RTP. DCzSBrSPO also reveals a similar delayed RTP phenomenon with doubled postponement time (400 ms). Notably, instant RTP of DCzSBrSP and DCzSBrSPO can also be recognized, but largely weaker than their delayed RTP and instant RTP of DCzSBr and DCzDBr. It indicates competition between instant and delayed RTP and the predominance of 3(n, π*) states in triplet transitions of DCzSBrSP and DCzSBrSPO.
Results
Steady-state photoluminescence spectra of DCzSBr powder consist of two bands respectively centered at 420 and 600 nm, in which the yellow band is nearly the same with its time-resolved RTP spectra; while photoluminescence and RTP spectra of DCzDBr are nearly overlapped, since its triplet radiation is facilitated by doubled atom effect of its two bromine atoms (Fig. 2a and Supplementary Table 1). In contrast, RTP components in steady-state photoluminescence spectra of DCzSBrSP and DCzSBrSPO are markedly weaker, giving rise to their emission peaks at 465 and 502 nm, respectively. Nonetheless, their time-resolve RTP spectra correspond to yellow emissions with main and shoulder peaks at ~540 and ~590 nm, respectively. RTP spectra of DCzSBrSP and DCzSBrSPO are the same when excited at 350 and 390 nm, but DCzSBr and DCzDBr excited with 350 nm reveal two additional RTP peaks at ~570 and ~620 nm. Excitation-emission spectral mapping further demonstrates that when excitation wavelength <390 nm, RTP spectra of DCzSBr and DCzDBr are unchanged, but which are different to their RTP spectra excited with 390 nm (Fig. 2b). Furthermore, all these four materials display nearly identical RTP spectra excited by 390 nm, corresponding to the same transition processes of their carbazole-originated Tn* states. In opposite to DCzSBr and DCzDBr, RTP spectra of DCzSBrSP and DCzSBrSPO are independent on excitation wavelengths, despite their electronic spectra identical to those of DCzSBr and DCzDBr (Supplementary Note 2, Supplementary Fig. 2). It means phosphine groups of DCzSBrSP and DCzSBrSPO indeed provide TM energy levels to facilitate energy transfer to low-lying Tn* states.
For RTP peaks at 540 nm excited by 390 nm, compared to DCzSBr and DCzDBr with RTP lifetimes of 116 and 80 ms, DCzSBrSP exhibits the longest RTP lifetime at 540 nm reaching 742 ms, which is elongated by more than 6 and 9 folds, respectively (Fig. 2c). Despite shorter than that of DCzSBrSP, RTP lifetime of DCzSBrSPO also increases to 503 ms. Furthermore, RTP lifetimes at 590 nm are nearly equal to those at 540 nm for all these four materials, indicating consistent photophysical procedures. However, sulfide of DCzSBrSP does not exhibit long-persistence room temperature phosphorescence, since the lifetimes of its powder are less than 20 ms (Supplementary Figs. 3 and 4). The comparable lifetimes of DCzSBrSP and DCzSBrSPO imply their similar RTP mechanism, which is undoubtedly different to that for DCzSBr and DCzDBr. Obviously, this mechanism difference also renders the unique delayed RTP for DCzSBrSP and DCzSBrSPO.
Carbazole is the chromophore of all these four materials, which makes the main contributions to single-molecular excited-state characteristics, therefore, their electronic absorption, photoluminescence and phosphorescence spectra in dilute solutions (10−5 mol L−1 in dichloromethane) are nearly identical (Supplementary Fig. 5 and Supplementary Table 2). The lifetimes of the solutions are similar to the fluorescence lifetimes of the powders, indicating the initial states of emissions from the powders are their single-molecular S1 states (Supplementary Figs. 6, 7). The details of transition processes for RTP from these four materials are investigated with time-resolved emission spectra (TRES) of DCzSBr, DCzDBr, DCzSBrSP and DCzSBrSPO powders, which indicate the step-by-step evolution from the T1 states to Tn* states (Fig. 3a and Supplementary Fig. 8). It is shown that in the time range from microsecond to millisecond, all these four materials firstly revealed the microsecond-scaled emissions centered at ~420 nm, which are nearly identical to single-molecular phosphorescence spectra originated from the T1 states (insets of Supplementary Figs. 5, 9, 10). Without any intermediate processes, T1 states of DCzSBr and DCzDBr transit to the Tn* states within 60 and 20 μs, respectively. Such short time gaps can not be recognized by human eyes, giving rise to instant RTP. On the contrary, only a small proportion of the T1 states for DCzSBrSP and DCzSBrSPO immediately transit to their Tn* states after dozens of microseconds, rendering negligible instant RTP. But, the majority of their T1 states evolve to the TM states, which are embodied as the additional triplet bands at ~490 nm between single-molecular phosphorescence and RTP, and finally transit to the Tn* states of DCzSBrSP and DCzSBrSPO after 30 and 50 ms, respectively, resulting in delayed RTP at 540 nm. Consequently, “dark time” of dozens of milliseconds from excitation removal to delayed RTP is long enough to be recognizable by naked eyes.
Single-crystal X-ray diffraction data indicate that π-π stackings between carbazole groups of adjacent DCzSBrSP and DCzSBrSPO molecules are similar to those of DCzSBr and DCzDBr, but DCzSBrSP and DCzSBrSPO reveal additional intermolecular p-π interactions between adjacent carbazole and phosphine groups (Supplementary Note 3, Supplementary Figs. 11–15). Quantum chemical calculation shows that at triplet excited state, the frontier molecular orbital distributions and energy levels of π-π stacked DCzSBrSP and DCzSBrSPO dimers are similar to those of DCzSBr and DCzDBr dimers; while, DCzSBrSP and DCzSBrSPO dimers with p-π interactions reveal the increased contributions of diphenylphosphine groups to triplet excited states, rendering the higher triplet energy levels than the π-π stacked dimers (Supplementary Note 4, Supplementary Figs. 16–20).
DCzSBrSP is considered as the combination of DCzSBr and (2-bromophenyl)-diphenylphosphine (TPPBr) as RTP and delay units, respectively (Fig. 3b). The sliced time-resolved emission spectra of DCzSBrSP illustrate the excited-state evolution of DCzSBrSP after excitation removal: (i) during <7.5 μs, phosphorescence spectrum centered at ~420 nm corresponds to carbazole-originated 3(π, π*) states identical to that of DCzSBr at 10–20 μs; (ii) during 7.5–150 μs, along with 420-nm phosphorescence decreases, a new phosphorescence band centered at ~490 nm increases, which is consistent with 3(n, π*)-featured phosphorescence spectrum of TPPBr; (iii) during 400–500 μs, carbazole-based 420-nm phosphorescence disappears, but accompanied by 490-nm band, another new band peaked at 540 and 590 nm arises, which is identical to RTP spectrum of DCzSBr from the Tn* state; (iv) at >5 ms, only RTP band remains.
Therefore, it is rational that the transition process of DCzSBrSP and DCzSBrSPO is 3(π, π*) state of carbazole group → 3(n, π*) state of phosphine group → 3(π, π*) featured Tn* state of carbazole group → RTP. The transition from 3(n, π*) state to Tn* state is the slowest step at millisecond scale, resulting in the special delayed RTP. In this case, phosphine moieties play the key role as mediate groups, which provide intermediate 3(n, π*) states as TM states to trap triplet energy for dozens of milliseconds.
DCzSBrSP with delayed RTP and DCzSBr and DCzDBr with instant RTP were adopted to realize incremental information display by utilizing their different occurrence and decay times (Fig. 4). The ground powders of DCzDBr, DCzSBrSP and DCzSBr were used as solid inks for screen-printing three elements of main-building pattern, Chinese and English characters and numbers in a logo for 80th anniversary of Heilongjiang University, respectively (Fig. 4a). After UV turn-off, afterglows of main-building pattern and numbers firstly appeared, and then the characters as information increment became visible and the brightest at 30 and 500 ms, respectively (Movie S1). Subsequently, in accordance with the RTP lifetimes of DCzDBr, DCzSBr and DCzSBrSP, main-building pattern, numbers and characters successively disappeared within 2 s.
This combination of instant and delayed RTP can easily realize multi-level and time-resolved anti-counterfeiting and information encryption. A set of numbers “8987898aa1” as a triplet-encryption password was also prepared with DCzSBr, DCzDBr and DCzSBrSP inks (Fig. 4b and Supplementary Note 5, Supplementary Fig. 21). Bis[4-(9,9-dimethyl-9,10-dihydroacridine)phenyl]sulfone (DMAC-DPS) with bright blue fluorescence was used as background to cover the different emissions of the inks and form initial numbers of “8888888888” under UV excitation. At 30 ms after UV off, since DCzSBrSP based bars were non-emissive, instant RTP of DCzSBr and DCzDBr-based bars generated an instant information of “0987654321” (Movie S2). Then, at 150 ms, RTP of DCzSBrSP-based bars became comparable, giving rise to the first delayed information same as the correct password. And then, DCzDBr based bars with the shorted lifetime disappeared at 500 ms to generate the second delayed information of “”4567890231”. Obviously, this triple encryption was mainly dependent on delayed RTP, which added new information at the initial stage of emission decay, thereby doubled information depth. Furthermore, time windows for recognizing encrypted information, e.g. instant information herein, is only dozens of milliseconds, which is delicately balanced for purposeful recognition, but makes unintentional cracking far more difficult.
Discussion
In conclusion, we have demonstrated delayed RTP in carbazole-phosphine hybrid organic molecules featuring mixed π-π and p-π intermolecular interactions in solid states. Different to common instant RTP immediately occurred after excitation removal, delayed RTP can only be recognized with a postponement of dozens of milliseconds, and then gradually enhanced in the next hundreds of milliseconds. Therefore, delayed RTP can realize incremental information display, rather than common unidirectional decay. Photophysical results suggest that phosphine groups provide the 3(n, π*)-featured intermediate state (TM) between 3(π, π*)-featured T1 and Tn* states to form a step-by-step transition process. The different excited-state characteristics postpone TM → Tn* transition by dozens of milliseconds, resulting in delayed RTP. This work not only presents a fundamental for controllably modulating transition process in delayed RTP systems containing π-π and p-π segments, but also supports a flexible and unique platform for multiple time-resolution optical applications in bio-imaging, passive programmable display, multi-level anti-counterfeiting, and so on.
Methods
General information
The crystals suitable for single-crystal XRD analysis were obtained through vapor-phase diffusing n-hexane to dichloromethane solution (5 ml) of the materials (10 mg). All diffraction data were collected at 295 K on a Rigaku Xcalibur E diffractometer with graphite monochromatized Mo Kα (λ = 0.71073 Å) radiation in ω scan mode. All structures were solved by direct method and difference Fourier syntheses. Non-hydrogen atoms were refined by full-matrix least-squares techniques on F2 with anisotropic thermal parameters. The hydrogen atoms attached to carbons were placed in calculated positions with C−H = 0.93 Å and U(H) = 1.2Ueq(C) in the riding model approximation. All calculations were carried out with the SHELXL97 program. Absorption spectra were measured using a SHIMADZU UV-3150 spectrophotometer. Photoluminescence spectra were measured with an Edinburgh FPLS 1000 fluorescence spectrophotometer. The time decay spectra was measured using Time-Correlated Single Photon Counting (TCSPC) method with a picosecond hydrogen lamp for 100 ps–10 μs and a microsecond pulsed Xenon light source for 1 μs-10 s lifetime measurement, the synchronization photomultiplier for signal collection and the Multi-Channel Scaling Mode of the PCS900 fast counter PC plug-in card for data processing. Lifetime values were simulated by a single exponential fitting function in Fluoracle software. For anti-counterfeiting and encryption applications, a circular ultraviolet flashlight (GET-104) was used as the excitation source with a power of 3 W and the peak wavelength at 365 nm, whose spot diameter is about 2 cm at the distance of 10 cm above the samples.
General procedure for pattern preparation
(i) Platemaking: screens used for printing were customized according to the separated elements of the patterns (Fig. 4a and Supplementary Note 5, Supplementary Fig. 21).
(ii) Ink preparation: all the materials were ground and then sieved. The inks were prepared through uniformly dispersing the powders in aloe vera gel. Inks of DCzDBr, DCzSBrSP and DCzSBr were directly used to print the patterns in Fig. 4a; while, for Supplementary Fig. 21 and Fig. 4b, Inks of DCzDBr, DCzSBrSP and DCzSBr were mixed with DMAC-DPS based ink, so that under UV excitation, RTP can be covered by blue fluorescence from DMAC-DPS.
(iii) Printing: The separated elements of the patterns were sequentially printed with the corresponding inks through screens prepared in step (1). For the pattern in Fig. 4a, DCzDBr-based ink was firstly used to print the “main building of Heilongjiang University” on filter paper. After this pattern dried, DCzSBrSP based ink was used to print the university name in Chinese and English. Finally, DCzSBr-based ink was used to print the year numbers. The Chinese characters of “周年” were used to calibrate the positions of all the elements. For the patterns in Fig. 4b, as shown in Supplementary Fig. 21, four screens were used to the patterns on the filter paper through four steps and the corresponding inks.
Sample preparation
Synthesis of 9,9’-(4-Bromo-1,2-phenylene)bis(9H-carbazole) (DCzSBr)
A mixture of carbazole (4.01 g, 24 mmol), 4-bromo-1,2-difluorobenzene (1.93 g, 10 mmol) and KOH (1.35 g, 24 mmol) in dimethyl sulfoxide (DMSO) (45 mL) was stirred at 140 °C for 1.5 h under argon atmosphere. After cooling to room temperature, the mixture was poured into water and then filtered. The crude product was dried and then purified by column chromatography and recrystallization from methanol and ethyl acetate, affording white solid with a yield of 72% (3.51 g). 1H NMR (TMS, CDCl3, 400 MHz): δ = 7.983 (d, J = 2.0 Hz, 1H), 7.766–7.833 (m, 5H), 7.702 (d, J = 8.4 Hz, 1H), 7.109–7.175 (m, 4H), 7.029–7.082 ppm (m, 8H); 13C NMR (TMS, CDCl3, 101 MHz): δ = 139.645, 139.617, 135.774, 133.668, 133.450, 132.059, 131.807, 125.666, 125.617, 123.674, 123.640, 121.660, 120.376, 120.249, 120.112, 109.638, 109.585 ppm; LDI-TOF: m/z (%): 487.0792 (100) [M+].
Synthesis of 9,9’-(4,5-Dibromo-1,2-phenylene)bis(9H-carbazole) (DCzDBr)
A mixture of carbazole (3.60 g, 21.5 mmol), 1,2-dibromo-4,5-difluorobenzene (2.72 g, 10 mmol), and K2CO3 (3.34 g, 24 mmol) in dimethyl sulfoxide (DMSO) (30 mL) was stirred at 150 °C for 12 h under argon atmosphere. After cooling to room temperature, the mixture was poured into water and then filtered. The crude product was dried and then purified by column chromatography and recrystallization from ethyl acetate to afford white solid with a yield of 75% (4.25 g). 1H NMR (TMS, CDCl3, 400 MHz): δ = 8.090 (s, 2H), 7.773-7.795 (m, 4H), 7.126-7.149 (m, 4H), 7.045-7.089 ppm (m, 8H); 13C NMR (TMS, CDCl3, 101 MHz): δ = 139.401, 134.897, 134.550, 125.773, 124.427, 123.735, 120.560, 120.170, 109.468 ppm; LDI-TOF: m/z (%): 565.9821 (100) [M+].
Synthesis of 9,9’-(4-Bromo-5-(diphenylphosphaneyl)-1,2-phenylene)bis(9H-carbazole) (DCzSBrSP)
To a solution of 9,9’-(4,5-dibromo-1,2-phenylene)bis(9H-carbazole) (5.66 g, 10 mmol) in mixed Et2O (25 mL) and tetrahydrofuran (THF, 60 mL) was added with n-BuLi (2.5 M in hexane, 4 mL, 10 mmol) at -120 °C. Then, the mixture was stirred for 30 min at the same temperature. The mixture was added with Ph2PCl (1.8 mL, 10 mmol) during 30 min, and then the solution naturally returned to room temperature. The mixture was treated with aqueous NH4Cl and extracted with CH2Cl2. The organic phase was separated and dried over anhydrous Na2SO4. After removal of the solvents, the residue was purified by column chromatography and recrystallization with ethyl acetate to give white solid with a yield of 64% (4.30 g). 1H NMR (TMS, CDCl3, 400 MHz): δ = 8.078 (d, J = 3.2 Hz, 1H), 7.758-7.779 (m, 2H), 7.700 (d, J = 7.6 Hz, 2H), 7.336–7.462 (m, 10H), 7.232 (d, J = 1.6 Hz, 1H), 7.113–7.135 (m, 2H), 6.893–7.065 ppm (m, 10H); 13C NMR (TMS, CDCl3, 101 MHz): δ = 140.369, 140.208, 139.248, 139.060, 135.916, 135.061, 135.019, 134.959, 134.131, 134.106, 134.060, 133.857, 133.085, 129.586, 129.093, 129.021, 125.618, 125.383, 123.687, 123.469, 120.389, 120.167, 120.003, 119.824, 109.566, 109.375 ppm; 31P NMR (TMS, CDCl3, 162 MHz): δ = −4.629 ppm; LDI-TOF: m/z (%): 673.1232 (100) [M+].
Synthesis of (2-bromo-4,5-di(9H-carbazol-9-yl)phenyl)diphenylphosphine oxide (DCzSBrSPO)
To a solution of DCzSBrSP (1.34 g, 2 mmol) in dichloromethane (DCM, 10 mL) was added with 30% H2O2 at 0 °C. The mixture was further stirred for 4 h at the room temperature. The mixture was washed with aq. NaHSO3, and then extracted with CH2Cl2. The extracts were dried over anhydrous Na2SO4. After removing DCM, the residue was purified with column chromatography to give white solid with a yield of ~100% (1.37 g). 1H NMR (TMS, CDCl3, 400 MHz): δ = 8.184 (d, J = 2.8 Hz, 1H), 7.855–7.901 (m, 4H), 7.699–7.782 (m, 5H), 7.540–7.555 (m, 6H), 6.948–7.121 ppm (m, 12H); 13C NMR (TMS, CDCl3, 101 MHz): δ = 137.812, 137.778, 136.861, 136.832, 136.418, 136.304, 135.125, 135.041, 133.133, 132.116, 131.641, 131.572, 131.508, 131.475, 131.449, 130.995, 130.940, 130.897, 130.374, 129.295, 127.935, 127.810, 124.733, 124.536, 124.164, 124.114, 122.810, 122.550, 119.732, 119.430, 119.031, 118.926, 108.365, 108.025 ppm; 31P NMR (TMS, CDCl3, 162 MHz): δ = 30.184 ppm; LDI-TOF: m/z (%): 689.1196 (100) [M+].
The original NMR, high-resolution MS (HRMS) and high-performance liquid chromography (HPLC) spectra were provided in Supplementary Note 6 (Supplementary Figs. 22–36).
Gaussian simulation
Theoretical computations were carried out on the basis of the restricted and unrestricted formalism of Beck’s three-parameter hybrid exchange functional47 and Lee, and Yang and Parr correlation functional48 (B3LYP). The optimization was also performed at the level of 6-31 G(d,p), respectively, on the basis of single-crystal data. The fully optimized stationary points were further characterized by harmonic vibrational frequency analysis to ensure that real local minima had been found without imaginary vibrational frequency. The total energies were also corrected by zero-point energy both for the ground and excited states. Natural transition orbital (NTO) analysis was performed on the basis of optimized ground-state geometries at the same level49.
Data availability
The authors declare that the data generated in this study are provided in Supplementary Information. Crystallographic data for the structures reported in this Article have been deposited at the Cambridge Crystallographic Data Centre, under deposition numbers 2309045 (DCzSBr) [https://doi.org/10.5517/ccdc.csd.cc2hhrb3], 2309044 (DCzDBr) [https://doi.org/10.5517/ccdc.csd.cc2hhr92], 2309047 (DCzSBrSP) [https://doi.org/10.5517/ccdc.csd.cc2hhrd5] and 2309046 (DCzSBrSPO) [https://doi.org/10.5517/ccdc.csd.cc2hhrc4], respectively. Copies of the data can be obtained free of charge via https://www.ccdc.cam.ac.uk/structures/.
References
Zhao, W., He, Z. & Tang, B. Z. Room-temperature phosphorescence from organic aggregates. Nat. Rev. Mater. 5, 869–885 (2020).
Zhang, Y. et al. Ultraviolet irradiation-responsive dynamic ultralong organic phosphorescence in polymeric systems. Nat. Commun. 12, 2297 (2021).
Ye, W. et al. Confining isolated chromophores for highly efficient blue phosphorescence. Nat. Mater. 20, 1539–1544 (2021).
Yao, X. et al. Ultralong organic phosphorescence from isolated molecules with repulsive interactions for multifunctional applications. Nat. Commun. 13, 4890 (2022).
Yang, Y. et al. Efficient and color-tunable dual-mode afterglow from large-area and flexible polymer-based transparent films for anti-counterfeiting and information encryption. Angew. Chem. Int. Ed. 61, e202201820 (2022).
Zhen, X. et al. Ultralong phosphorescence of water-soluble organic nanoparticles for in vivo afterglow imaging. Adv. Mater. 29, 1606665 (2017).
You, Y. et al. Hydrophilic ultralong organic nanophosphors. Small 16, 1906733 (2020).
Zhou, Y. et al. Long-lived room-temperature phosphorescence for visual and quantitative detection of oxygen. Angew. Chem. Int. Ed. 58, 12102–12106 (2019).
Hamzehpoor, E. et al. Efficient room-temperature phosphorescence of covalent organic frameworks through covalent halogen doping. Nat. Chem. 15, 83–90 (2023).
Zhang, Y. et al. Large-area, flexible, transparent, and long-lived polymer-based phosphorescence films. J. Am. Chem. Soc. 143, 13675–13685 (2021).
Feng, H.-T. et al. Tuning molecular emission of organic emitters from fluorescence to phosphorescence through push-pull electronic effects. Nat. Commun. 11, 2617 (2020).
Kenry, Chen, C. & Liu, B. Enhancing the performance of pure organic room-temperature phosphorescent luminophores. Nat. Commun. 10, 2111 (2019).
Li, D. et al. Completely aqueous processable stimulus responsive organic room temperature phosphorescence materials with tunable afterglow color. Nat. Commun. 13, 347 (2022).
Lower, S. K. & El-Sayed, M. A. The triplet state and molecular electronic processes in organic molecules. Chem. Rev. 66, 199–241 (1966).
Gu, L. et al. Colour-tunable ultra-long organic phosphorescence of a single-component molecular crystal. Nat. Photon. 13, 406–411 (2019).
Gong, Y. et al. Crystallization-induced dual emission from metal- and heavy atom-free aromatic acids and esters. Chem. Sci. 6, 4438–4444 (2015).
Gan, N. et al. Manipulating the stacking of triplet chromophores in the crystal form for ultralong organic phosphorescence. Angew. Chem. Int. Ed. 58, 14140–14145 (2019).
Bian, L. et al. Simultaneously enhancing efficiency and lifetime of ultralong organic phosphorescence materials by molecular self-assembly. J. Am. Chem. Soc. 140, 10734–10739 (2018).
Nidhankar, A. D. et al. Self-assembled helical arrays for the stabilization of the triplet state. Angew. Chem. Int. Ed. 59, 13079–13085 (2020).
An, Z. et al. Stabilizing triplet excited states for ultralong organic phosphorescence. Nat. Mater. 14, 685–690 (2015).
Jin, J. et al. Modulating tri-mode emission for single-component white organic afterglow. Angew. Chem. Int. Ed. 60, 24984–24990 (2021).
Lucenti, E. et al. Cyclic triimidazole derivatives: intriguing examples of multiple emissions and ultralong phosphorescence at room temperature. Angew. Chem. Int. Ed. 56, 16302–16307 (2017).
Tu, L. et al. How temperature and hydrostatic pressure impact organic room temperature phosphorescence from H-aggregation of planar triarylboranes and the application in bioimaging. Sci. China Chem. 66, 816–825 (2023).
Tao, S. et al. Design of metal-free polymer carbon dots: a new class of room-temperature phosphorescent materials. Angew. Chem. Int. Ed. 57, 2393–2398 (2018).
Gu, L. et al. Color-tunable ultralong organic room temperature phosphorescence from a multicomponent copolymer. Nat. Commun. 11, 944 (2020).
Zhang, T. et al. Molecular engineering for metal-free amorphous materials with room-temperature phosphorescence. Angew. Chem. Int. Ed. 59, 11206–11216 (2020).
Lei, Y. et al. Wide-range color-tunable organic phosphorescence materials for printable and writable security inks. Angew. Chem. Int. Ed. 59, 16054–16060 (2020).
Li, D. et al. Amorphous metal-free room-temperature phosphorescent small molecules with multicolor photoluminescence via a host–guest and dual-emission strategy. J. Am. Chem. Soc. 140, 1916–1923 (2018).
Zhang, Z.-Y., Chen, Y. & Liu, Y. Efficient room-temperature phosphorescence of a solid-state supramolecule enhanced by Cucurbit[6]uril. Angew. Chem. Int. Ed. 58, 6028–6032 (2019).
Su, Y. et al. Ultralong room temperature phosphorescence from amorphous organic materials toward confidential information encryption and decryption. Sci. Adv. 4, eaas9732 (2018).
Li, Q. et al. Induction of long-lived room temperature phosphorescence of carbon dots by water in hydrogen-bonded matrices. Nat. Commun. 9, 734 (2018).
Tian, R., Xu, S.-M., Xu, Q. & Lu, C. Large-scale preparation for efficient polymer-based room-temperature phosphorescence via click chemistry. Sci. Adv. 6, eaaz6107 (2020).
Li, J.-A. et al. Switchable and highly robust ultralong room-temperature phosphorescence from polymer-based transparent films with three-dimensional covalent networks for erasable light printing. Angew. Chem. Int. Ed. 62, e202217284 (2023).
Su, Y. et al. Excitation-dependent long-life luminescent polymeric systems under ambient conditions. Angew. Chem. Int. Ed. 59, 9967–9971 (2020).
Wang, J.-X. et al. Time-dependent afterglow color in a single-component organic molecular crystal. Angew. Chem. Int. Ed. 59, 10032–10036 (2020).
Wang, H. et al. Amorphous ionic polymers with color-tunable ultralong organic phosphorescence. Angew. Chem. Int. Ed. 58, 18776–18782 (2019).
Wang, Y. et al. Nonconventional luminophores with unprecedented efficiencies and color-tunable afterglows. Mater. Horiz. 7, 2105–2112 (2020).
Zhao, W. et al. Rational molecular design for achieving persistent and efficient pure organic room-temperature phosphorescence. Chem 1, 592–602 (2016).
Wang, Z. et al. Recent advances in organic room-temperature phosphorescence of heteroatom (B/S/P)-containing chromophores. CCS Chem 5, 292–309 (2023).
She, P. et al. Controllable photoactivated organic persistent room-temperature phosphorescence for information encryption and visual temperature detection. Cell Rep. Phys. Sci. 2, 100505 (2021).
Gao, W. et al. Propeller ultralong room temperature phosphorescence: new aspect of triphenylphosphine derivatives. Adv. Opt. Mater. 11, 2202904 (2023).
She, P. et al. Single-component molecular dual persistent room temperature phosphorescence from low- and high-lying triplet states. Adv. Opt. Mater. 10, 2102706 (2022).
Xue, P., Wang, P., Chen, P., Ding, J. & Lu, R. Enhanced room-temperature phosphorescence of triphenylphosphine derivatives without metal and heavy atoms in their crystal phase. RSC Adv 6, 51683–51686 (2016).
Wu, X. et al. Exploiting racemism enhanced organic room-temperature phosphorescence to demonstrate Wallach’s rule in the lighting chiral chromophores. Nat. Commun. 11, 2145 (2020).
Zhou, Y. et al. Dual promotion of phosphorus groups for ultralong room temperature phosphorescence with high efficiency. Adv. Opt. Mater. 11, 2201904 (2023).
Song, X. et al. Phosphine-manipulated p-π and π-π synergy enables efficient ultralong organic room-temperature phosphorescence. Angew. Chem. Int. Ed. 62, e202300980 (2023).
Becke, A. D. Density-functional thermochemistry. III. The role of exact exchange. J. Chem. Phys. 98, 5648–5652 (1993).
Lee, C., Yang, W. & Parr, R. G. Development of the Colle-Salvetti correlation-energy formula into a functional of the electron density. Phys. Rev. B 37, 785–789 (1988).
Martin, R. L. Natural transition orbitals. J. Chem. Phys. 118, 4775–4777 (2003).
Acknowledgements
H.X. thanks Prof. Runfeng Chen for his constructive suggestions on DRTP mechanism. The authors thank the support by the National Natural Science Foundation of China (22325502, 92061205, 62175060, 52273173, 22005088).
Author information
Authors and Affiliations
Contributions
H.X. conceived the projects. G.L., J.T., H.W., Y.M., and C.D. performed the experiments. H.X., G.L., Y.M., S.C., J.Z., and C.H. analyzed the data and wrote the paper. All authors commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lu, G., Tan, J., Wang, H. et al. Delayed room temperature phosphorescence enabled by phosphines. Nat Commun 15, 3705 (2024). https://doi.org/10.1038/s41467-024-47888-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-47888-z
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.