Abstract
Gas hydrates provide alternative solutions for gas storage & transportation and gas separation. However, slow formation rate of clathrate hydrate has hindered their commercial development. Here we report a form of porous ice containing an unfrozen solution layer of sodium dodecyl sulfate, here named active ice, which can significantly accelerate gas hydrate formation while generating little heat. It can be readily produced via forming gas hydrates with water containing very low dosage (0.06 wt% or 600 ppm) of surfactant like sodium dodecyl sulfate and dissociating it below the ice point, or by simply mixing ice powder or natural snow with the surfactant. We prove that the active ice can rapidly store gas with high storage capacity up to 185 Vg Vw−1 with heat release of ~18 kJ mol−1 CH4 and the active ice can be easily regenerated by depressurization below the ice point. The active ice undergoes cyclic ice−hydrate−ice phase changes during gas uptake/release, thus removing most critical drawbacks of hydrate-based technologies. Our work provides a green and economic approach to gas storage and gas separation and paves the way to industrial application of hydrate-based technologies.
Similar content being viewed by others
Introduction
Gas hydrates have attracted much attention because not only natural gas hydrates are believed to be the largest natural gas resource on Earth, but also gas hydrates provide alternative and innovative solutions for industrial requirements, e.g., natural gas storage & transportation and gas mixture separation. Gas hydrate forms when water molecules and gas molecules contact at low temperatures and high pressures; as a result, gas molecules are enwrapped in lattices that consisted of hydrogen−bonded water molecules1. Ideally, each unit volume of hydrate can store 180 volumes of natural gas2; different gases have different equilibrium conditions in hydrate formation; in addition, gas hydrate can be preserved under atmospheric pressure at 268.15 K3. These features make it a promising medium for gas storage and separation. However, the feasibility of these hydrate−based technologies is heavily reliant on the formation rate of gas hydrate, which is naturally slow.
Gas hydrate formation is an interfacial process between gas and water. For the hydrate formation without human intervention, a solid hydrate film with low permeability would spread over and seal off the interface, which hinders the contact of gas and water for continued gas hydrate formation. Consequently, a spontaneous hydrate growth always stagnates at film thickness less than 100 μm4,5, leaving a large amount of unconverted water beneath the hydrate film. Besides that, the heat released during hydrate formation due to its exothermic nature also would retard hydrate formation in turn by rising the reactants’ temperature. Thus, the slow hydrate formation results from the retarded mass transfer and the heat generation.
Efforts have been dedicated to remove or minimize mass transfer resistance and to accelerate hydrate formation6,7,8,9,10,11,12,13,14,15. Among them, using kinetic promoters like surfactants, e.g., sodium dodecyl sulfate (SDS), is among the most effective ways known today to accelerate hydrate formation. Another class of kinetic promoters that have gained recent prominence are amino acids16. The fastest hydrate formation in the presence of kinetic promoters reported so far could be accomplished at 11 min with water conversion over 80%6. Despite the conspicuous performance of kinetic promoters accelerating hydrate formation, scaling-up the hydrate production via using kinetic promoters may encounter three major challenges.
The accelerated hydrate formation comes from an upward and wall-adhering growth pattern of gas hydrate induced by kinetic promoters, which is known as wall−climbing effect17. This effect accelerates hydrate formation by sucking the aqueous solution onto the reactor wall and providing larger contact area for hydrate formation. Due to such hydrate growth pattern, the hydrate formation rate is closely related to the solution load in reactors; with the same reactor configuration and under similar thermodynamic conditions, overall hydrate formation rate decreases with the increase of solution load18,19,20, which is unfavorable for scaling-up of the process. The second challenge hindering the scaling-up is the temperature increase due to the exothermic nature of the formation process; because of significant heat released during hydrate formation from water or aqueous solution (e.g., ~9.07 kJ mol−1 water or 54.44 kJ mol−1 for methane hydrate21), the temperature of the liquids could rise by 4 ~ 8 K in the 0.5 ~ 2.7 h of formation processes14,18,20; a faster hydrate formation process required by industrial hydrate production would further increase the temperature, and then hamper the hydrate formation in turn. The third challenge is the inadequate utilization of the reactor space; plenty of gas space is required for the upward growth to avoid the blockage of the gas inlet/outlet; for that reason, gas hydrate formation in the presence of surfactants is generally conducted with gas volume of 65% ~ 90% in the reactors. Besides the three major challenges, the hollow appearance of the hydrate22 formed with the wall−climbing effect could decrease the apparent gas storage density; meanwhile, the serious bubble and foam generation during hydrate dissociation is also detrimental to industrial gas hydrate production.
In order to break through the limits of mass and heat transfer on hydrate formation rate and reduce the subsequent problems, here, we report an active ice approach and demonstrate its excellence as a formation medium for gas hydrate. We first use a kind of active ice produced by decomposing primary gas hydrate that is formed from SDS solution to form methane hydrate, and the hydrate formation typically completes within 5 min with gas uptake over than 170 Vg Vw−1 at 272.65 K. Beside the rapid formation rate, the active ice exhibits multiple advantages, i.e., good repeatability, recyclability, compressibility, simple storage condition and low heat generation. Characterization results show that the active ice is porous and contains unfrozen SDS solution layer. Gas hydrate formation in this solution layer at temperature slightly lower than the ice point spawns a virtuous circle of ice melt—hydrate formation—ice melt, which hastens gas hydrate formation strikingly. The ice with unfrozen surfactant solution layer seems to be activated for gas hydrate, it is therefore an active ice. Inspired by this, we improve the preparation process of active ice without impairing its performance in gas hydrate formation. With the multiple advantages, the active ice approach is capable of overcoming the obstacles to scaling−up gas hydrate formation process for industrial purpose.
Results
Being attracted by the porous morphologies of gas hydrate formed from aqueous SDS solution (CH4–SDS hydrate), we wonder whether cage structures retain in the solid medium produced after hydrate dissociation below ice point and try to use it for reformation of gas hydrate. An active ice was made by decomposing a primary gas hydrate mass below the ice point, which was previously synthesized with methane and 600−ppm SDS solution (Fig. 1a–c. Supplementary Fig. 1), then methane hydrate was formed in it (Fig. 1d). When methane hydrate formed in 600–ppm SDS solution at 272.65 K and initial pressure of 6.0 MPa (Supplementary Fig. 2), the induction time for hydrate nucleation ranged from 5 to 82 min though stirring was adopted to accelerate it, and the time required to finish the hydrate formation after the induction period ranged from 18 to 32 min. In one of these formation experiments (Fig. 1e), the methane uptake of hydrate was 168.60 Vg Vw−1 (volume of STP gas per volume of water; the theoretical value without the effect of thermodynamic promoters is 216 Vg Vw−1 for structure I methane hydrate) after a 1 h formation process, including an induction time of 18 min. By contrast, the active ice gulps methane very rapidly without retard at 272.65 K (Fig. 1f). The equilibrium methane uptake reaches in 5 min and is encouragingly high as 185.70 Vg Vw−1 or so; meanwhile, the wall−climbing effect17, which always occurs when gas hydrate forms in surfactant solutions and potentially hinders the operation in hydrate production, could be eliminated in the active ice. This rapid hydrate formation implied that the major obstacle in hydrate formation, i.e., blocked mass transfer, could be overcome by the active ice approach.
Following PXRD measurements indicate this kind medium is normal ice still (Fig. 2a) although SEM images show that its porous characteristic is significant (Fig. 2b, c. Supplementary Fig. 3); the thermal property of the medium also support this inference (Supplementary Table 1). Considering pure ice powder does not exhibit such perfect gas uptake performance (Fig. 1f), we call this kind of medium active ice. The Raman spectrum measurements (Fig. 2d) suggest that the active ice and pure ice have the same Raman spectrum; after methane uptake in the active ice, phase transition of ice to clathrate hydrate has occurred, indicating that the gas uptake process in the active ice is actually a clathrate hydrate formation process, although little change in the morphology of the active ice could be observed by naked eye (refer to Fig. 1c, d). The characteristic that gas uptake occurs only when pressure is higher than equilibrium pressure of hydrate formation (Supplementary Fig. 4) also supports the formation of clathrate hydrate.
Figure 3 shows the mechanism of fast hydrate formation in the active ice. Adsorbed SDS molecules on the surface of ice particles work like salt to decrease the local melting point and result in the occurrence of aqueous solution layer (Supplementary Table 2) on the surface when the temperature is set to 272.65 K or so, which is very close to the melting point of pure ice. Because of the promotion effect of SDS, this liquid layer forms hydrate promptly when the active ice contact to gas like methane under enough high pressure. The difference between the hydrate formation heat from liquid water (~9.07 kJ mol−1 water21) and the ice melting heat (5.99 kJ mol−1 water, Supplementary Table 1) guarantees the continuous melt of ice and generation of new liquid layer between the hydrate shell and residual ice core; the liquid layer then adsorbs SDS molecules, which are excluded in the pre−hydrate formation, to its surface; porous morphology of hydrate shell formed in the presence of SDS helps gas molecules migrate to the surface of the newly generated liquid layer rapidly and cause new hydrate formation. By this way, a virtuous circle of ice melt—hydrate formation—ice melt is established, which results in the rapid hydrate formation from the surface to center of active ice particles. This kind of melt-catalytic mechanism as we see it is supported by two facts. The first one is that the temperature increases from 272.65 K to higher than 278.0 K, which is higher than the melting point of ice, during hydrate formation when initial temperature is set to 272.65 K (Supplementary Fig. 5); this indicates that ice melting is thermodynamically possible. The second one is that both the hydrate formation rate and the maximum gas uptake are very low when temperature is set far lower than the ice point, e.g., ≤270.65 K (Supplementary Fig. 6); this result could be attributed to the impossibility to form enough amount of liquid layer before and during hydrate formation under such lower temperature. Because of the porous or powdery characteristic of the active ice, gas could contact to all ice particles at the same time and forms hydrate uniformly, that is why we see a rapid gas uptake.
Since the surfactant played a critical role in the rapid gas hydrate formation in the active ice, we have further tested six different kinetic promoters to prepare the active ice to further extend the applicability to different surfactants, whose methane uptake profiles are shown in Supplementary Fig. 7. All these kinetic promoters display positive effects on accelerating hydrate formation while sodium dodecanoate and sodium dodecyl benzene sulfonate perform better than the rest. The comparison between Supplementary Figs. 7 and 8 indicate that the performance of a kinetic promoter in promoting gas hydrate formation in the active ice is closely related to its ability in promoting gas hydrate formation in aqueous solution; namely, if a promoter can significantly enhance gas hydrate formation in aqueous solution, it is also a potential additive for producing the active ice.
More tests have been performed to show the other feasibility and advantages for active ice to be used for gas storage or gas mixture separation. For example, active ice could be recycled (Fig. 4a, Supplementary Fig. 9) and be stored for long time (Fig. 4b), without losing its gas uptake performance; the optimized SDS dose in active ice is as low as 600 mg L−1 (Supplementary Fig. 10). Actually, the regeneration of the active ice does not refer to strictly reinstating the microstructure of the active ice, it only means recovering the ability of providing rapid gas uptake as evidenced in this work. In addition, high hydrate formation rate and gas uptake could be achieved under smaller driving force (the difference between actual hydrate formation pressure and equilibrium hydrate formation pressure). As shown in Fig. 4c, the cumulative gas uptake could reach 174.8 Vg Vw−1 within 5 min under 272.65 K and constant pressure of 3.0 ± 0.02 MPa, corresponding to a drive force of only 0.69 MPa, which is much smaller than that typically adopted in cases where aqueous SDS solution were used to form hydrate18,23. Surely, moderate operation pressure helps to reduce the operating cost of hydrate production. Moreover, another bottleneck besides the slow formation rate of the hydrate-based technologies, i.e., high formation heat, could be basically eliminated. Compared to the formation heat of higher than 50 kJ mol−1 gas for methane hydrate formed from water, the formation heat of methane in active ice is only 18.13 kJ mol−1 CH424. The smaller heat release could bring about lower increment in temperature peak when the mass of active ice is multiplied in fast methane uptake. When the mass of active ice was increased from 5.0 to 79.0 g, the temperature peak only increased from 278.76 to 281.53 K in the fast gas uptake period (<5 min); meanwhile, the gas uptakes (181.10 Vg Vw−1 and 173.21 Vg Vw−1) reached 91.19% and 90.97% of their final values, respectively (Supplementary Fig. 5c). In these experiments, methane hydrate formation in the active ice were accomplished within 5 min (gas uptake > 89% of its final value); this indicated that hydrate formation started simultaneously at multi points in the active ice, which is marginally affected by the amount of the active ice; all these results suggested an excellent potential of active ice in scaling-up the gas hydrate production. Apart from the formation heat, the effect of the packing bed’s size on the heat removal plays an important role in the inevitable increase in temperature peak when the amount of active ice was multiplied; however, this issue could be solved by optimizing the heat exchange in the packing bed of active ice.
Although the porous or powdery morphology of active ice brings high gas uptake rate, it makes the apparent specific volume of active ice packing bed much bigger than that of ice crystal and results in lower apparent storage capacity. For example, the apparent storage capacity is only 83.92 ± 2.6 Vg Vbed−1 (standard volume of gas per volume of active ice bed; free gas in the bed is included) if directly using the hollow active ice column produced by dissociating CH4 − SDS hydrate displaying in Fig. 1c. It is too low for industrial application. Hence compression is required to decrease the apparent volume and increase apparent gas storage capacity of active ice packing bed. Certainly, the compression will reduce both uptake rate and final gas uptake as shown in Fig. 4d. Fortunately, these negative effects are negligible under moderate compression, e.g., in cases when loosening coefficient α, the ratio of the specific volume of active ice packing bed to the specific volume of perfect ice crystal of the same mass, retains higher than 1.398. Therefore, decreasing the apparent volume of the active ice (or gas hydrate) by compression and good regeneration capacity can be realized at the same time. However, this only happens at moderate compression levels. The apparent methane storage capacity of active ice packing bed reached 126.36 Vg Vbed−1 under the optimized loosening coefficient α = 1.492 and 5.76 MPa (residual pressure after hydrate formation, Supplementary Fig. 11), which is 2.44 times higher than that of compressed natural gas under the same temperature and pressure. It is also much higher than that of dry ZIF-8 (a well-known metal-organic framework adsorbent) packing bed under similar thermodynamic conditions (105.37 Vg Vbed−1 at 269.15 K and 5.25 MPa)25.
Though the active ice has shown excellent performance in accelerating gas hydrate formation, the complicated preparation of it would restrict its practical application. We have further attempted to simplify its preparation process based on the mechanism of fast gas hydrate formation in active ice. Those experiments show that the active ice prepared via dissociating CO2–SDS hydrate below the ice point (active ice 2 in Fig. 4f) also works well, just like that originated from CH4–SDS hydrate. This finding is of significance because it makes the manufacture of the active ice safer and more economic since CO2 is incombustible and can form hydrate under milder conditions. It is more interesting to observe that the active ice prepared by grinding frozen aqueous SDS solution or by simply mixing natural snow with SDS also exhibits the same perfect gas uptake behavior (active ice 3 and 4, respectively, in Fig. 4f).
Finally, we demonstrate the use of active ice for the separation of several representative binary gas mixtures, CH4/CO2, CH4/H2, and CH4/C2H6, and compared its separation performance with that of aqueous SDS solution. The results show that, compared with SDS solution, the active ice not only eliminated the induction time and diminished the time required for separating the gas mixtures, it also remarkably increased the separation factor compared to SDS solution (Supplementary Fig. 12 and Supplementary Table 3). For CH4/H2, a separation factor of 355.66 and a methane recovery of 38.22% could be acquired within 11 min with the active ice, which was much faster and more effective than that with SDS solution under similar conditions. With an obvious improvement in separation kinetics and better separation results, the feasibility of hydrate-based gas separation could, therefore, be improved with the active ice.
We propose a conceptual process with respect to the potential application of the active ice in natural gas storage and transportation. The active ice could be prepared by decomposing gas-promoter hydrate below the ice point, or grinding the ice of suitable kinetic promoters’ aqueous solution, or just simply mixing ice powder or natural snow with kinetic promoters. As regards the most economical or feasible preparation method, it depends on specific situations. After being produced and shaped in a factory, the active ice could be loaded in a tank on vehicles, in which built-in heat exchangers should be installed. The on-board tanks will be used for gas storage in the gas fields. Natural gas is precooled and injected into the tank and is expected to form gas hydrate rapidly with the active ice. The formed hydrate then will be degassed to atmospheric pressure and transported to its destination and natural gas is recovered along with the active ice. This kind of charging–discharging mode based on the rapid hydrate formation is similar to compressed natural gas (CNG) method; however, it is superior in the economic benefits, safety benefits and environmental friendliness perspective according to the literature6. As for the application of the active ice in gas mixture separation, traditional pressure swing adsorption (PSA) mode could be adopted because of the smaller heat release26. Because the uncertainty of the scaling-up effect, the above methods are only suggestions for the potential use of the active ice in gas storage and transportation and gas separation, and they must be developed and analyzed in further studies.
Discussion
In summary, we have discovered a kind of active ice, which is of porous or powdery appearance and contains low-dose kinetic promoters. The promoters locally decrease the freezing point of water while keeping its effect on hydrate formation, thus create extensive active sites in the active ice at temperature slightly lower than the ice point of pure water. The spiral development of ice melting—hydrate formation—ice melting at the active sites enables minute-level and high-conversion gas hydrate formation even at very small driving force. The fast hydrate formation, in association with the small formation heat, the shapable packing bed of active ice, and the recyclability of the active ice, could overcome the main obstacles in realizing hydrate-based technologies. What’s more, the greenness and cheapness of the active ice, make it an excellent alternative sorbent for more extensive gas storage or separation.
Methods
Materials
Methane, carbon dioxide, hydrogen, and ethane with purity of 99.99% were purchased from Beijing AP BAIF Gas Industry CO., Ltd. Sodium dodecyl sulfate (SDS) with ACS reagent grade (>99%) was provided by Sigma-Aldrich. Sodium oleate with purity >97% and N-Carbobenzoxy-DL-leucine with purity >98% were purchased from Shanghai Aladdin Biochemical Technology Co., Ltd. Dodecylbenzenesulfonic acid (> 90%), Sodium dodecyl benzene sulfonate (>95%), Sodium laurylsulfonate (>98%) were provided by Shanghai Makclin Biochemical Co., Ltd. Deionized water was produced in our laboratory.
Experimental setup
Supplementary Fig. 13 shows the schematic of the apparatus employed to produce the active ice and to evaluate its performance in hydrate formation. Briefly, a high-pressure sapphire cell with internal diameter of 2.54 cm and internal volume of 61.90 cm3 was used as the reactor. A piston was mounted at the bottom of the reactor to compress the active ice. An iron ring reciprocates inside the reactor and acts as a stirrer before gas hydrate formation in aqueous solution, which was driven by a group of magnets beside the reactor. A stainless-steel gas reservoir with an internal volume of 130.23 cm3 was used to precool gas. The reactor and the gas reservoir were mounted in an air bath (temperature stability = ±0.1 K). Two pressure transducers (0 ~ 20 MPa, ±0.1%FS; 0 ~ 10 MPa, ±0.1%FS) were used to measure the pressures of the gas reservoir and the reactor, respectively. The pressure data were logged by a data acquisition system for every 1 min. A buffer tank was used to precool the pressurizing fluid of the pump, and the inner volume of the buffer tank is 80.10 cm3. A stainless-steel reactor with internal diameter of 5.07 cm and 220.00 cm3 was used to conduct the scale-up hydrate formation experiments in Supplementary Fig. 5c, d; meanwhile, another gas reservoir with internal volume of 750.09 cm3 was used to precool the gas.
Another reactor was used coupled with a Raman spectrometer for in situ characterization of the active ice. The schematic of the reactor is shown in Supplementary Fig. 14. Two opposite sapphire windows were designed on the reactor for optical observation and Raman spectroscopy determination. Between the sapphire windows, a chamber with internal volume of approximately 1.4 cm3 is surrounded by the windows and the stainless-steel wall, and the in situ hydrate formation and dissociation for Raman characterization were performed in the chamber. An annular passage surrounding the chamber was designed as the flow channel for coolant to regulate the temperature in the chamber. A pt100 temperature sensor with accuracy of 0.05 K was inserted into the chamber. A pressure transducer with accuracy of 0.02 MPa was used to measure the pressure in the reactor.
Preparation of the active ice
(1) methane hydrate formation-dissociation route. The active ice was prepared following a hydrate formation-dissociation method shown in Supplementary Fig. 1. A certain amount of SDS was dissolved in water first. Then, 10 g of the SDS solution was added into the sapphire reactor shown in Supplementary Fig. 13, and the reactor was sealed tight. The air in the reactor and the gas reservoir was purged by charging methane (primary gas) and vacuuming for three times. After that, the primary gas was charged into the gas reservoir to higher than 10 MPa. Subsequently, the temperature of the air bath was set to 277.15 K for hydrate formation. 3 h later, the temperature of the SDS solution and the primary gas reached 277.15 K after a long enough cooling. Then, the reactor was pressurized with the primary gas from the gas reservoir to 6.0 MPa, and the stirring device was switched on to accelerate hydrate nucleation. When hydrate crystals appeared in the reactor, the stirring device was switched off to let hydrate grow quiescently. This hybrid approach enables the control of stochasticity associated with the nucleation of hydrate formation27. About 3 h later, the pressure drop caused by hydrate formation decreased to less than 20 kPa h−1. Then, the formation of the hydrate (primary hydrate) is considered to be accomplished. The active ice was produced by dissociating the primary hydrate below the ice point. Before the hydrate dissociation, the temperature of the air bath was reset to 272.65 K. 3 h later, the primary hydrate was depressurized to atmospheric pressure within 20 s. Then, the primary hydrate dissociated at 272.65 K and under atmospheric pressure. The temperature and pressure change in the preparation of the active ice via dissociating methane hydrate are shown in Supplementary Fig. 15. The dissociation procedure lasted at least for 3 h to release most of the primary gas that stored in the primary hydrate. The ice-like substance left in the reactor after hydrate dissociation was exactly the active ice. (2) Carbon dioxide hydrate formation-dissociation route. The procedures of this route are almost the same with route (1), except that the methane was replaced by carbon dioxide. (3) ice powder or natural snow route. A certain amount of ice was ground into ice powder. Then, some ice powder or natural snow was mixed with surfactant evenly. The grinding and mixing are conducted under the protection of dry ice.
Compress the active ice
In the experiments shown in Fig. 4d, e, the active ice was compressed before being used in hydrate formation. The active ice was cooled to 268.15 K first. Then, a precooled PTFE disk with similar diameter to the internal diameter of the sapphire reactor was put into the reactor and placed on the active ice. Subsequently, the piston was pushed upward by the hand pump, and the active ice, therefore, was compressed between the piston and the PTFE disk. Before the compression, the pressurizing fluid was precooled in the buffer tank to avoid the dissociation of the active ice. After the compression, the PTFE disk was taken out from the reactor, and 0.2 MPa of methane was charged into the reactor to push the piston back to the bottom of the reactor. Then, the reactor was discharged to atmospheric pressure. All these operations were conducted at 268.15 K.
Methane hydrate formation in the active ice
The hydrate formation experiments in the active ice were mainly conducted in the sapphire reactor depicted in Supplementary Fig. 13; namely, the active ice was not taken out from the sapphire reactor after it was prepared. The temperature for hydrate formation was reset on the air bath. The gas reservoir was charged with methane to 10 MPa. 3 h later, the temperature of the active ice and methane gas reached the desired value. Then, the reactor was charged with methane to 6.0 MPa from the gas reservoir. The pressure drop in the reactor was used to calculate the gas uptake in the hydrate. In the control experiments that methane hydrate formation in SDS solution, the active ice was displaced by a certain amount of SDS solution; the following steps were the same with the hydrate formation in the active ice.
Gas separation with the active ice
The gas separation experiments were also conducted in the apparatus depicted in Supplementary Fig. 13. After the active ice was prepared in the reactor, the temperature for hydrate formation was reset on the air bath. Gas mixture was injected into the gas reservoir to a certain pressure. When the temperature of the active ice and the gas mixture reached the set value, the reactor was pressurized with the gas mixture from the gas reservoir. When the pressure in the reactor stopped decreasing, the gas remained in the reactor was analyzed with an Agilent 7890 A gas chromatography.
Data treatment
Both the gas storage and separation results were calculated based on the molar balance of gas in the gas and hydrate phase. The detailed treatment is shown in Supplementary Information.
Characterization
The methods of Raman, PXRD, SEM, and DSC characterization are shown in Supplementary Information.
Data availability
The data generated in this study are provided in the Supplementary Information and Source Data file. Source data are provided with this paper.
References
Sloan, E. D. Clathrate Hydrates of Natural Gases 3rd edn (CRC Press, 2007).
Sloan, E. D. Fundamental principles and applications of natural gas hydrates. Nature 426, 353–363 (2003).
Stern, L. A., Circone, S., Kirby, S. H. & Durham, W. B. Anomalous preservation of pure methane hydrate at 1 atm. J. Phys. Chem. B 105, 1756–1762 (2001).
Taylor, C. J., Miller, K. T., Koh, C. A. & Sloan, E. D. Macroscopic investigation of hydrate film growth at the hydrocarbon/water interface. Chem. Eng. Sci. 62, 6524–6533 (2007).
Ohmura, R., Kashiwazaki, S. & Mori, Y. H. Measurements of clathrate-hydrate film thickness using laser interferometry. J. Cryst. Growth 218, 372–380 (2000).
Bhattacharjee, G., Goh, M. N., Arumuganainar, S. E. K., Zhang, Y. & Linga, P. Ultra-rapid uptake and the highly stable storage of methane as combustible ice. Energ. Environ. Sci. 13, 4946–4961 (2020).
Stern, L. A., Kirby, S. H. & Durham, W. B. Peculiarities of methane clathrate hydrate formation and solid-state deformation, including possible superheating of water ice. Science 273, 1843–1848 (1996).
Zhong, Y. & Rogers, R. E. Surfactant effects on gas hydrate formation. Chem. Eng. Sci. 55, 4175–4187 (2000).
Fukumoto, K., Tobe, J., Ohmura, R. & Mori, Y. H. Hydrate formation using water spraying in a hydrophobic gas: a preliminary study. AlChE J. 47, 1899–1904 (2001).
Wang, W., Bray, C. L., Adams, D. J. & Cooper, A. I. Methane storage in dry water gas hydrates. J. Am. Chem. Soc. 130, 11608–11609 (2008).
Hao, W. F., Wang, J. Q., Fan, S. S. & Hao, W. B. Study on methane hydration process in a semi-continuous stirred tank reactor. Energy Convers. Manag. 48, 954–960 (2007).
Fujita, S., Watanabe, K. & Mori, Y. H. Clathrate-hydrate formation by water spraying onto a porous metal plate exuding a hydrophobic liquid coolant. AlChE J. 55, 1056–1064 (2009).
Luo, Y. T., Zhu, J. H., Fan, S. S. & Chen, G. J. Study on the kinetics of hydrate formation in a bubble column. Chem. Eng. Sci. 62, 1000–1009 (2007).
Fan, S. S., Yang, L., Lang, X. M., Wang, Y. H. & Xie, D. L. Kinetics and thermal analysis of methane hydrate formation in aluminum foam. Chem. Eng. Sci. 82, 185–193 (2012).
Yang, L., Fan, S. S., Wang, Y. H., Lang, X. M. & Xie, D. L. Accelerated formation of methane hydrate in aluminum foam. Ind. Eng. Chem. Res. 50, 11563–11569 (2011).
Bhattacharjee, G. & Linga, P. Amino acids as kinetic promoters for gas hydrate applications: a mini review. Energy Fuels 35, 7553–7571 (2021).
Gayet, P. et al. Experimental determination of methane hydrate dissociation curve up to 55 MPa by using a small amount of surfactant as hydrate promoter. Chem. Eng. Sci. 60, 5751–5758 (2005).
Zhang, J. S., Lee, S. & Lee, J. W. Kinetics of methane hydrate formation from SDS solution. Ind. Eng. Chem. Res. 46, 6353–6359 (2007).
Lin, W. et al. Effect of surfactant on the formation and dissociation kinetic behavior of methane hydrate. Chem. Eng. Sci. 59, 4449–4455 (2004).
Xiao, P. et al. Enhancing methane hydrate formation in bulk water using vertical reciprocating impact. Chem. Eng. J. 336, 649–658 (2018).
Gupta, A., Lachance, J., Sloan, E. D. & Koh, C. A. Measurements of methane hydrate heat of dissociation using high pressure differential scanning calorimetry. Chem. Eng. Sci. 63, 5848–5853 (2008).
Botimer, J. D., Dunn-Rankin, D. & Taborek, P. Evidence for immobile transitional state of water in methane clathrate hydrates grown from surfactant solutions. Chem. Eng. Sci. 142, 89–96 (2016).
Okutani, K., Kuwabara, Y. & Mori, Y. H. Surfactant effects on hydrate formation in an unstirred gas/liquid system: an experimental study using methane and sodium alkyl sulfates. Chem. Eng. Sci. 63, 183–194 (2008).
Handa, Y. P. Compositions, enthalpies of dissociation, and heat capacities in the range 85 to 270 K for clathrate hydrates of methane, ethane, and propane, and enthalpy of dissociation of isobutane hydrate, as determined by a heat-flow calorimeter. J. Chem. Thermodyn. 18, 915–921 (1986).
Mu, L. et al. A novel method to improve the gas storage capacity of ZIF-8. J. Mater. Chem. 22, 12246–12252 (2012).
Babu, P., Kumar, R. & Linga, P. A new porous material to enhance the kinetics of clathrate process: application to precombustion carbon dioxide capture. Environ. Sci. Technol. 47, 13191–13198 (2013).
Veluswamy, H. P., Kumar, A., Kumar, R. & Linga, P. An innovative approach to enhance methane hydrate formation kinetics with leucine for energy storage application. Appl. Energy 188, 190–199 (2017).
Bernal, J. D. & Fowler, R. H. A theory of water and ionic solution, with particular reference to hydrogen and hydroxyl ions. J. Chem. Phys. 1, 515–548 (1933).
Murshed, M. M. & Kuhs, W. F. Kinetic Studies of Methane–ethane mixed gas hydrates by neutron diffraction and Raman spectroscopy. J. Phys. Chem. B 113, 5172–5180 (2009).
Schicks, J. M., Erzinger, J. & Ziemann, M. A. Raman spectra of gas hydrates—differences and analogies to ice 1h and (gas saturated) water. Spectrochim. Acta A Mol. Biomol. Spectrosc. 61, 2399–2403 (2005).
Acknowledgements
The authors acknowledge fundings from the National Natural Science Foundation of China (Grant No. 22127812 to G.-J.C., 52004311 to P.X., U20B6005 to G.-J.C., and 22178379 to C.-Y.S.).
Author information
Authors and Affiliations
Contributions
G.-J.C., P.L., and B.L. designed the project; C.-Y.S. and P.X. designed the experiments. P.X. performed the active ice preparation and hydrate formation with the help of J.-J.L. and X.W.P.; P.X. carried out the analysis with the help of W.-X.P., X.-H.W., C.D., B.L., and Y.-L.P. Y.X. and Y.-J.Z. performed the Raman and DSC characterization. W.C. contributed to the gas separation experiments. P.X. drafted the manuscript. G.-J.C. and P.L. reviewed and edited the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Ju Dong Lee and the anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xiao, P., Li, JJ., Chen, W. et al. Enhanced formation of methane hydrate from active ice with high gas uptake. Nat Commun 14, 8068 (2023). https://doi.org/10.1038/s41467-023-43487-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-43487-6