Introduction

Electrochemical lithium extraction with intercalation hosts from dilute water sources shows great potential as an alternative method to secure Li supply and has received tremendous attention lately1,2,3,4,5,6,7,8,9,10,11. One-dimensional (1D) olivine iron phosphate (FePO4) is a promising host material owing to its appropriate working potentials, framework stability, thermodynamic Li intercalation preference, and lower Li migration barrier1,4,7,12,13. Specifically, the calculated lithiation voltage of olivine FePO4 host is around 3.45 V vs. Li/Li+ (=0.213 V vs. Ag/AgCl), which is higher than the sodiation voltage (3.08 V vs. Na/Na+ = 0.173 V vs. Ag/AgCl)13. The migration barrier of Li ion is only 0.17 eV, smaller than that of Na ion (0.29 eV)13. Even with the intrinsic material favorability to Li, during electrochemical Li extraction at low Li to Na ratio, co-intercalation occurs with Na as the main competitor7,9,13,14. Despite intriguing proof of concept, the FePO4 host structure response upon Li and Na competitive co-intercalation remains unknown1,3,4,9. The intercalation pathways and storage sites are critical in determining the energy barriers for both Li and Na intercalation (including formation enthalpy, migration barrier, nucleation barrier, and interfacial energy), affecting selectivity.

The intercalation behavior of single-component Li or Na in FePO4 hosts has been well studied13,15,16,17,18,19,20,21,22,23,24,25,26,27,28,29. During pure Li intercalation, the pathway depends on the kinetics21,23,25,28,30,31,32,33. Both theoretical and experimental evidence has shown that at slow (de)lithiation rates, Li-ion intercalation follows the domino-cascade intercalation model20,32,34,35. At high (de)lithiation rates, phase transformations in nanoparticles can proceed via a continuous change in structure without a distinct moving phase boundary, known as non-equilibrium solid solution (SS) model25,28,30,36. Besides the (de)lithiation rates, the impact of particle characteristics (including size32,37,38,39, morphology40, and defect level21,41) on the phase transformation of LiFePO4 has also been studied intensively. For Na, high (de)sodiation rates were seldom studied due to the sluggish kinetics13,26,27. At slow (de)sodiation rates, according to the phase diagram at room temperature, olivine NayFePO4 phase separates into FePO4 and Na2/3FePO4 for y < 2/3 and remains a solid-solution single phase for y > 2/326. With both Li and Na, there is competition for the storage sites, making the phase behavior more complex. As a result, accounting for the interaction between Na and Li during co-intercalation is crucial for manipulating the intercalation energy landscape for each ion and controlling the Li competitiveness.

In this study, we demonstrate, via density functional theory (DFT) calculation and direct structural characterization, that Li and Na tend to phase separate in 1D FePO4 hosts. X-ray diffraction (XRD), scanning electron nanodiffraction (SEND), and energy dispersive X-ray spectroscopy (EDS) characterization all showed distinctive Li and Na phases at both the single-particle level and for particle ensembles. Guided by the Li and Na phase separation behavior, we produce Li SS phases with partially filled 1D Li channels via seeding to change the relative intercalation barriers between Na and Li to repel Na. Compared to empty hosts, the Li-seeded hosts showed selectivity increases of ~1.6-fold and ~3.8-fold with 20% and 40% Li-seeding, respectively. With 40% Li-seeding, the total Li fraction (Li/(Li+Na)total) in the host is ~94%. The selectivity enhancement strongly correlates with the phase fraction of high-Li SS phases (LixFePO4, 0.5 ≤ x < 1), but weakly correlates with the phase fraction of low-Li SS phases (LixFePO4, 0 < x < 0.5). The high-Li SS phases are effective in preventing the intercalation of Na ions at different specific currents and persist even upon pure Na-ion intercalation. Moreover, we investigate the effects of FePO4 particle forms on the solid solution formation during the Li-seeding step and the consequential Li extraction performance. The defect levels, sizes, and morphologies play critical and complex roles in determining the formations of solid solutions under the same global specific current, which further affects the co-intercalation behavior and Li competitiveness. This work demonstrates the importance of manipulating intercalation kinetic pathways to control ion selectivity and points out that guiding the host phase evolution to undergo Li solid solution formation is an effective strategy to enhance the Li to Na selectivity.

Results

FePO4 host phase behavior upon Li and Na co-intercalation

We first used DFT to calculate the formation enthalpies of different structures with Li and Na co-existence. Figure 1a shows the calculated ternary phase diagram of FePO4-LiFePO4-NaFePO4. FePO4, LiFePO4, Na2/3FePO4, and NaFePO4 are the ground state structures. Among the 506 structures we calculated with a maximum super cell size of 86, there is no ground state configuration with a mixture of Li and Na, indicating that Li and Na do not prefer to co-exist in the same [010] channel during co-intercalation (See Supplementary Note 1 for computation details). Intermediate compositions are expected to decompose into these four ground state phases depending on the composition.

Fig. 1: Li and Na phase separation in FePO4 host.
figure 1

a Ternary phase diagram of FePO4-LiFePO4-NaFePO4. The stable phases (green dots) are FePO4, LiFePO4, Na2/3FePO4, and NaFePO4. The red squares denote the calculated intermediate compositions in the LixNayFePO4 (0 ≤ x+y ≤ 1) system. b Schematic illustrating the setup of scanning electron nanodiffraction. The blue and black arrows denote the scanning motion of the electron beam. c Absolute a, c-lattice constant maps of the LN(0.7)0.1C particle with their estimated errors (arrows are a guide-to-the-eye for the phase identification). d STEM image and its corresponding EDS elemental mapping (Na, O, Fe) of the LN(0.7)0.1C particle.

To verify the calculation results experimentally, we first used scanning electron nanodiffraction (SEND) (Fig. 1b, c and Supplementary Fig. 1) to identify existing phases at a single-particle level. The particles were prepared by directly intercalating FePO4 hosts in a 1 mM LiCl and 1 M NaCl (molar ratio Li: Na = 1: 1000) mixed solution under 0.1 C (14.7 mA/g) using 70% of the total capacity (The total capacity is 147 mAh/g, measured by cycling the electrodes in 60 mL 1 M LiCl aqueous solutions between −0.6 V and 0.6 V (vs. Ag/AgCl/KCl (4.0 M)) at room temperature (20~25 °C) under 0.1 C), labeled as LN(0.7)0.1C. The ratio of 1: 1000 Li: Na is selected based on the compositions of brines and geothermal fluids7,9,42,43,44,45,46,47. The platelet particles are observed along [010] channel direction. We constructed the lattice constant maps with the estimated errors as shown in Fig. 1c. Lattice constants for potentially related Li or Na phases are summarized in Supplementary Table 1. The lattice constant range points to the co-existence of olivine LiFePO4 (a, b, c-lattice constants = 10.329, 6.009, 4.695 Å) and olivine Na2/3FePO4 (a, b, c-lattice constants = 10.289, 6.082, 4.937 Å) phases and ruled out the existence of olivine FePO4 (a-lattice constant = 9.821 Å), olivine NaFePO4 (a = 10.406 Å; c = 4.947 Å) and maricite NaFePO4 (a = 9.001 Å; c = 5.052 Å) phases, since their lattice constants are out of the range. As shown in the SEND mapping, LiFePO4 phase mainly exists in the center of the particle (yellow areas in Fig. 1c, a-lattice constant map), and Na2/3FePO4 phase is mainly at the edges (yellow areas in Fig. 1c, c-lattice constant map) as guided by the arrows. The matching of lattice constants to pure Li and Na phases supports the Li and Na phase separation behavior. Meanwhile, lattice strains were calculated and shown in Supplementary Fig. 1. The contraction and expansion of c-lattice parameter in the [001] direction clearly show the results of Li and Na ions intercalating separately. It is also worth noting that from c-lattice constant map (Fig. 1c), we observed Na SS phases with intermediate c-lattice constants (0.482 nm~0.486 nm). The formation of metastable Na SS phases at 0.1 C was confirmed with pure Na-ion intercalation. XRD shows that the Na SS phase separated into Na2/3FePO4 and FePO4 after one month of storage (Supplementary Fig. 2). Therefore, 0.1 C (14.7 mA/g) is already a high current rate to drive a solid solution pathway between FePO4 and Na2/3FePO4 phases. Secondly, scanning transmission electron microscopy (STEM) with energy-dispersive X-ray spectroscopy (EDS) was used to map the elemental distribution (Fig. 1d). Na mapping showed nonuniform signal across the particle with higher intensity near the edges. The EDS mapping matches well with the SEND phase analysis and reveals the existence of Na2/3FePO4 near the edge of the particle (yellow areas in Fig. 1c, c-lattice constant mapping). At the electrode level for particle ensembles, the XRD pattern of the LN(0.7)0.1C electrode also showed a co-existence of LiFePO4 and Na0.71FePO4 phases (Supplementary Fig. 3).

Pre-seeding Li and quantification of SS phase fractions

Guided by the results that Li and Na tend to phase separate during co-intercalation, we propose to enhance the Li competitiveness in FePO4 hosts by creating partially filled Li 1D channels to raise the Na phase formation energy barrier. The typical electrochemical (de)intercalation pathway of Li in LixFePO4 particles with a sub-micrometer diameter at low specific currents (≤0.1 C) undergo phase separation during the vast majority of the process (0.05 ≤ x ≤ 0.95)28,35,48. To create partially filled Li 1D channels at room temperature (20~25 °C), we seed Li via the SS phase change pathway at high C rates (>1 C). The proposed seeding process is illustrated in Fig. 2a. We first extract Li from the host by chemical deintercalation of LiFePO4 (See Methods for chemical extraction details). It is worth noting that depending on the defect level of the synthesized FePO4 particles, some Li can be trapped in the 1D channels as remnant Li. The host was then seeded a target amount of Li in 1 M LiCl(aq) solution under high C rates (>1 C) and labeled as “L(X)nC”, where X is the percentage of Li filled in LixFePO4 and n is the C rate used in the seeding process. Specifically, the total capacity is 147 mAh/g and 1 C is equivalent to 147 mA/g (See Methods for more details). An ideal case would be for most of the channels to have some Li to repel Na.

Fig. 2: Seeding and quantification of Li SS phases.
figure 2

a Schematic of the Li seeding and Li/Na ions co-intercalation processes happening at high seeding C rates (>1 C). The inset illustrates the possible intercalation pathways at the electrode-electrolyte solution (E/S) interface. The initial host was prepared by chemical extraction. x’ denotes the remnant quantity of Li in the structure. See “Pre-seeding Li and quantification of SS phase fractions” in the main text for more information. b Normalized XRD (dotted line: raw data; solid line: fit) patterns of FePO4 electrodes before (L(0)) and after seeding with different amounts of Li (10%, 20%, 30% and 40% of the 147 mAh/g total capacity) under 4 C (588 mA/g), labeled as L(0.1/0.2/0.3/0.4)4C. The normalization is based on the intensity of (020) peak for FePO4 at 30.9°. The (020) peak of LiFePO4 is centered at 29.8°. The intensity bands between the two end-up phases are the intermediate SS phases. c An example of deconvoluted XRD pattern for the quantification of SS phases and corresponding R-squared value (R2). The obtained pattern (black dots) of L(0.3)4C is fitted with nine different phases of LixFePO4 with x = 0/0.125/0.250/0.375/0.500/0.625/0.750/0.875/1, as calculated based on Vegard’s law for the (211) and (020) of the LiFePO4 (Green) and FePO4 (Purple) end phases. See Supplementary Note 2 for more fitting details. d Averaged accumulative SS phase fractions of L(0/0.1/0.2/0.3/0.4)4C. (Error bars representing the standard deviation of three replicate measurements).

The Li SS phases and their fractions were quantified by XRD characterization after seeding. Figure 2b shows the normalized XRD patterns of FePO4 electrodes after seeding different amounts of Li (0, 10%, 20%, 30%, and 40% of the 147 mAh/g total capacity) under 4 C (588 mA/g), labeled as L(0/0.1/0.2/0.3/0.4)4C respectively (See Methods for sample preparation details). The strong intensity band between the characteristic (020) peaks for FePO4 and LiFePO4 indicates the formation of SS phases with a continuous structural change18,21,31,49. With more lithium seeded, the peak intensity ratios of SS phases to FePO4 and LiFePO4 to FePO4 increase. Following previous work48,49, we fit a sum of Gaussians to the diffraction patterns, deconvolving seven intermediate phases LixFePO4, x = 0.125/0.250/0.375/0.500/0.625/0.750/0.875, from FePO4 and LiFePO4 end phases (See Supplementary Tables 2,  3,  4, and Supplementary Note 2 for deconvolution details). We fixed (within a pre-defined window) the center location of each Gaussian based on linear combinations of the refined phases for LiFePO4 and FePO4 (Supplementary Fig. 4). Figure 2c shows an example of a deconvoluted XRD pattern. The high R2 value confirms the validity of our deconvolution method. The fitted accumulative phase fractions for samples representing the starting and four seeding ranges are summarized in Fig. 2d. The calculated weighted sum of Li from XRD fittings shows a good linear relationship with the electrochemical seeded Li amount (Supplementary Figs. 5,  6, and Supplementary Table 5). However, Li amounts showed deviations at the low seeding percentage. For example, before Li seeding (L(0)), the weighted sum of Li is ~0.17 (Supplementary Table 5). This deviation could be from the remnant Li trapped in the hosts after chemical extraction or the contributions from the system substrate effect when the background intensity is unignorable. The deviations caused by porous structures of carbon cloth can be decreased by using flat glassy carbon as the substrate. It is worth mentioning that flexible carbon cloth is a better choice considering manufacturing and practical use. As shown in Supplementary Figs. 7,  8 and Supplementary Table 6, a better quantitative agreement between the calculated weighted sum of Li and the seeding amount is achieved. By eliminating the background intensity contributions, we can see from Supplementary Table 6 that ~0.07 Li per formula was left in the host after the chemical extraction step before the seeding process which could be from defect-induced Li trapping (See Supplementary Note 3 for more discussions of the deviations).

Correlation of high-Li SS phases to Li selectivity

The effect of seeded Li SS phases on Li selectivity was investigated using 1: 1000 Li to Na molar ratio solution (1 mM LiCl and 1 M NaCl mixed solution). It should be noted that two different Li/(Li+Na) ratios are reported. One is Li/(Li+Na)total, which denotes the ratio of the total amount of Li detected in the recovery solution after emptying the host, and another one is Li/(Li+Na)net, which subtracts the initially seeded Li (See Methods for more details about the calculation of recovered Li ratios). First, we seeded different amounts of Li (10%, 20%, 30% and 40% of the 147 mAh/g total capacity) under 4 C (588 mA/g). The total SS fraction increased monotonically with the seeding amount (Supplementary Fig. 9a). After seeding, we conducted Li extraction in 1: 1000 Li to Na molar ratio solution under 0.1 C (14.7 mA/g) until 70% of capacity (102.9 mAh/g) was used, which we label as L(0.1/0.2/0.3/0.4)4C-LN(0.7)0.1C. Both Li/(Li+Na)total and Li/(Li+Na)net showed a monotonic increase (Supplementary Fig. 9a), indicating the effectiveness of pre-seeding strategy in promoting Li competitiveness. Specifically, the Li/(Li+Na)net ratio increased from 0.61 ± 0.01 to 0.86 ± 0.01 from 10% to 40% seeding. With 40% seeding, we achieved ~3.8 fold increase of Li selectivity to 6.0 × 103, comparing to the empty host without seeding. However, we inevitably need more cycle repetition to obtain the same amount of lithium transferred with a Li pre-seeded host. Further improvement of the structrual response of the FePO4 electrode could improve the capacity usage.

We then go on to examine whether all the seven intermediate SS phases are equivalently effective in enhancing the Li selectivity. First, we analyzed the Li selectivity trend to each SS phase (Supplementary Fig. 9b). None of the phases alone can explain the selectivity trend. We then divided the SS phases into two groups, the low-Li SS phases (LixFePO4, x = 0.125/0.250/0.375) and the high-Li SS phases (LixFePO4, x = 0.500/0.625/0.750/0.875) (Fig. 3a). The Li content in the SS phases should affect the energy barrier for Na-ion intercalation, since Li and Na intercalation into the FePO4 cause contraction and expansion in the [001] direction, respectively. After grouping, we observe a clear trend that the selectivity increase follows the high-Li SS phase fraction increase for fitting data on both carbon cloth and glassy carbon substrates (Fig. 3a, b and Supplementary Fig. 8). However, the low-Li SS phases did not show monotonic trend. The correlation shows that high-Li SS phases contribute the most to the improvement of Li selectivity. Interestingly, when the seeding range was small at 10%, L(0.1)4C-LN(0.7)0.1C, the Li/(Li+Na)net was comparable with the empty host (L(0)-LN(0.7)0.1C) (Fig. 3b). To explain this, we tested the capacity range dependent selectivity of the empty FePO4 host (Fig. 3c). The Li/(Li+Na) ratio is 0.92 ± 0.02 for the first 10% capacity and the Li/(Li+Na) ratio decreases with the increase of capacity usage (all 0.1 C, equivalent to 14.7 mA/g). The intrinsic solubility of Li in FePO4 hosts (as SS phase) is around 5%50. If the first 5% of the FePO4 undergoes SS phase change, with >90% selectivity, this is equivalent to the 4.5% Li seeding process, which can promote the Li selectivity. The effect of seeding C rate on SS phase fractions and Li selectivity was also examined at 20% and 40% seeding conditions. In Supplementary Fig. 10a, at a slow seeding rate of 0.1 C (14.7 mA/g), the Li/(Li+Na)net of L(0.2)0.1C-LN(0.7)0.1C was 0.66 ± 0.03, similar to that of empty FePO4 hosts (0.63 ± 0.01), showing that, for the slow-rate Li pre-seeded hosts, the domino-cascade model starts to play a role, which opens more free channels for later Na-ion intercalation in the mixed solution (Supplementary Fig. 11). With increasing seeding C rates, from 2 C (294 mA/g) to 8 C (1176 mA/g), the Li/(Li+Na)net witnessed a monotonous increase (Supplementary Fig. 10a) with a 20% of seeding range, which is consistent with the corresponding high-Li SS fraction in each case (Supplementary Fig. 10b). We also tested the electrodes with 40% of seeding under different seeding C rates. As shown in Supplementary Fig. 10c, comparing to 20% seeding, we see a clearer trend that increasing the seeding C rate would lead to better Li selectivity. For the L(0.4)8C-LN(0.7)0.1C case, we achieved the highest Li selectivity (Liselectivity = 1.48 × 104) in this work (Supplementary Table 7). The applied high seeding specific current induces concurrent, non-mosaic intercalation in the porous electrode48.

Fig. 3: Correlation between SS phase fractions and lithium extraction performance.
figure 3

a High-Li SS fractions (LixFePO4, x = 0.500/0.625/0.750/0.875) and low-Li SS fractions (LixFePO4, x = 0.125/0.250/0.375) under the same seeding rate 4 C (588 mA/g) with different seeding ranges L(0/0.1/0.2/0.3/0.4)4C. b Li/(Li+Na)total (including the contributions from seeded-Li) and Li/(Li+Na)net (subtracting the contributions from seeded-Li) of the same hosts from a after 0.1 C (14.7 mA/g) co-intercalation L(X)4C-LN(0.7)0.1C. c Li/(Li+Na) ratio of the empty hosts with different intercalation range L(0)-LN(X)0.1C. d Li/(Li+Na)net of the electrodes with the same seeding process L(0.2)4C but different intercalation rates L(0.2)4C-LN(0.7)0.1/0.2/0.5C, and Li/(Li+Na) ratio of the empty hosts L(0)-LN(0.7)0.01/0.1/0.2/0.5C. e Li/(Li+Na)net vs. low-Li/high-Li/total-Li SS fractions and corresponding COD. f Li/(Li+Na)total and Li/(Li+Na)net for the multi-intercalation stability test using L(0.2)4C-LN(0.7)0.1C. (Error bars representing the standard deviation of three replicate measurements).

We further investigated the effectiveness of high-Li SS phases in restricting Na-ion intercalation at different overpotentials. Higher overpotentials at larger currents can provide additional energy for Na to overcome its intercalation barrier and decrease the Li selectivity. At an slow current of 0.01 C (1.47 mA/g), the Li/(Li+Na)net molar ratio of L(0)-LN(0.7)0.01C was 0.93 ± 0.02 (Fig. 3d). This selectivity benefits from the higher Li-ion intercalation potential and lower Li migration barrier. The thermodynamic preference of Li-ion intercalation could compensate for more than three order of magnitudes molar concentration difference between Li and Na7. Without Li seeding, with increased intercalation C rates from 0.1 C (14.7 mA/g) to 0.5 C (73.5 mA/g), Li/(Li+Na) of empty host decreased drastically from 0.63 ± 0.01 to 0.32 ± 0.01, as a result of higher intercalation overpotentials ~0.22 V (final potential difference, Supplementary Fig. 12a). The increased co-intercalation C rates may also cause local depletion of Li on the cathode surface6,9. With Li seeding, as shown in Fig. 3d, at 0.2 C (29.4 mA/g) intercalation rate, the hosts could still maintain decent selectivities of Li/(Li+Na)net = 0.62 ± 0.02, compared to the case without seeding (Li/(Li+Na)net = 0.53 ± 0.03). From 0.1 C (14.7 mA/g) to 0.5 C (73.5 mA/g) intercalation rate, the seeding process was consistently promoting the Li competitiveness. This indicates that the high-Li SS phases are effective in preventing Na-ion intercalation even at fast kinetics and can tolerate a higher overpotential of at least ~0.21 V (Supplementary Fig. 12b).

To illustrate the relationships between Li competitiveness and Li SS fractions, without the differentiation of seeding conditions, we plot Li/(Li+Na)net (Fig. 3e) and Li/(Li+Na)total (Supplementary Fig. 13) versus high-Li, low-Li, and total SS phase fractions for all the Li-seeded samples, with co-intercalation step run at 0.1 C (14.7 mA/g). Coefficients of determination (COD) were calculated to quantify the correlations. The fraction of high-Li SS phases is strongly correlated to Li ratios (e.g., COD (Li/(Li+Na)net vs. high-Li SS) = 0.97). In contrast, the fraction of low-Li SS phases is uncorrelated with the Li ratios (e.g., COD (Li/(Li+Na)net vs. low-Li SS) = 0.01). Meanwhile, the L(0.2)4C seeding condition was tested for multiple cycles on one electrode. Each cycle has Li seeding, Li extraction, and Li recovery steps. We measured the Li selectivity for each cycle. As shown in Fig. 3f, the Li/(Li+Na)net is maintained at ~0.73, proving the effect of seeding to improve Li selectivity as well as cycle stability. Additionally, we conducted two more cycling tests. Shown in Supplementary Fig. 14, we skip the Li seeding step from the 2nd cycle and use either 70% or 50% of capacity for further Li extraction. A decrease of the recovered Li/(Li+Na) was observed without seeding from the 2nd cycle, indicating that the seeding effect can only work for one cycle.

High-Li fraction SS phases promoting Li competitiveness

To further investigate the role of Li SS phases to Na-ion intercalation, we directly intercalated pure Na ions (1 M NaCl) in Li-seeded L(0.2)4C host to L(0.2)4C-N(0.5)0.1C (XRD shown in Fig. 4a and Supplementary Fig. 15). Besides the expected increase of the Na2/3FePO4 phase and the decrease of empty FePO4 phase, we saw a pronounced increase of the relative peak intensity at the LiFePO4 position and a shift of the SS band to high-Li positions (Fig. 4a). To confirm the phases are LiFePO4 and high-Li SS phases, we prepared N(0.5)0.1C, N(0.7)0.1C and N(0.5)0.1C-L(0.2)0.1C (first intercalating 50% Na and then intercalating 20% Li; 0.1 C is equivalent to 14.7 mA/g) for comparison (Fig. 4b). Both N(0.5)0.1C and N(0.7)0.1C showed a broad band between Na2/3FePO4 (020) and FePO4 (020), indicating a SS phase transition pathway for Na-ion intercalation at 0.1 C. However, the SS bands of N(0.5)0.1C and N(0.7)0.1C do not overlap at the position of LiFePO4. The onset of peak around the LiFePO4 and high-Li SS positions only occurs with Li-ion intercalation (also see N(0.5)0.1C-L(0.2)0.1C). This proves the formation of LiFePO4 phase after pure Na-ion intercalation into pre-seeded L(0.2)4C. We further confirmed using ICP-MS that the total amount of Li before and after Na-ion intercalation did not change. Therefore, the formation of LiFePO4 and the increase of high-Li SS phases are caused by the rearrangement of original Li ions responding to Na-ion intercalation. Since the total Li amount does not change, the Li has to come from the low-Li SS phases. One possible pathway for the rearrangement is through Li ions moving out of the low-Li SS phases and adding to the high-Li SS phases48. These results support that high-Li SS phases are more stable than low-Li SS phases upon Na-ion intercalation. Meanwhile, without Na-ion intercalation, simply soaking the electrode in the NaCl(aq) solution for the same amount of time as Na-ion intercalation, the low-Li and high-Li SS phase fractions only showed a slight decrease (Fig. 4c and Supplementary Fig. 16), which could be attributed to the solvent assisted surface-ion diffusion at FePO448. The extent of Li rearrangement is much less than that in the case of Na-ion intercalation. Therefore, the significant Li rearrangement is mainly a response of Li phases upon Na competition. With the persistence of high-Li SS phases and diminish of low-Li phases, it reveals that the pre-seed Li SS phases are not equally effective in expelling Na ions during co-intercalation. The high-Li SS phases are more effective than the low-Li SS phases.

Fig. 4: Effect of high-Li SS phases in promoting Li competitiveness.
figure 4

a XRD of L(0.2)4C electrode before (light green dots: raw data; solid light green line: fit) and after (orange: obtained pattern) 50% Na insertion. Dark green and purple peaks are fitted LFP and FP (020) peaks for L(0.2)4C to guide the peak positions. Bottom bars are the positions of (020) and (211) peaks of nine LixFePO4, x = 0/0.125/0.250/0.375/0.500/0.625/0.750/0.875/1. b Raw XRD patterns of N(0.7)0.1C electrode (dark red), as well as N(0.5)0.1C electrode before (light red) and after (orange) 20% Li insertion. c XRD of L(0.2)4C electrode before (light green) and after (dark green) 5 h soaking in 1 M NaCl(aq) (Dotted lines: raw data; Solid lines: fit). d DFT calculation of Li and Na ions intercalation energy difference for each intermediate phase LixFePO4 with respect to empty FePO4 host.

Moreover, we use DFT to calculate the energy barrier differences between Li and Na ions intercalation in each intermediate SS phase (See Supplementary Note 4 for calculation details) to prove the effect of high-Li SS phases in promoting Li competitiveness. First, we established low energy supercell configurations for the seven intermediate phases, as shown in Supplementary Fig. 17. The channel filling information was summarized in Supplementary Table 8. From the calculation results, all seven Li SS phases, as well as the empty FePO4 host, showed negative ΔGLi-Na (Supplementary Table 9), which means that thermodynamically Li-ion intercalation is always preferred in all the structures of the 1D olivine host. The Li and Na intercalation energy difference clearly showed that all Li SS phases have enhanced Li preference, compared to the empty FePO4 phase, as \((\triangle {G}_{{Li}-{Na}}^{{{Li}}_{x}{{FePO}}_{4}}-\triangle {G}_{{Li}-{Na}}^{{{FePO}}_{4}})\) are negative (Fig. 4d). Between low-Li SS phases and high-Li SS phases, high-Li SS phases have more negative \((\triangle {G}_{{Li}-{Na}}^{{{Li}}_{x}{{FePO}}_{4}}-\triangle {G}_{{Li}-{Na}}^{{{FePO}}_{4}})\), supporting the conclusion that high-Li SS phases being more effective in promoting Li-ion intercalation competitiveness. We also compared the Li and Na intercalation potential difference of both the empty host and the 50% Li pre-seeded host under 4 C (588 mA/g). As shown in Supplementary Fig. 18, the potential difference (ΔV1) is 0.23 V for empty host and is 0.27 V (ΔV2) for L(0.5)4C host. The exhibited Li preference is stronger for L(0.5)4C, than the empty host (ΔV2 > ΔV1). Therefore, both experimental and computational results show the same trend of Li preference for Li pre-seeded hosts.

Effects of particle characteristics on solid solution seeding and Li selectivity

The ion insertion reaction of LixFePO4 with different particle characteristics has been studied intensively. The formation of solid solution in olivine FePO4 is a complicated process that is affected by many factors, such as the temperature18,26, particle size/morphology32,38,39,40, applied current25,28,29,30,51, and defects21,41. The earliest reports have shown that the (de)intercalation of Li+ goes through a phase separation reaction into Li-rich and Li-poor phases at room temperature (20~25 °C)15,52. At elevated temperature (>400 °C), single-phase reaction was observed in the whole composition range (0 < x < 1 in LixFePO4)26. In addition, the miscibility gap has been found to reduce with the reduction of particle size, even vanish when the particles reach the critical nano-size region (dc ≤ 22 nm)32,38,39. Moreover, both computational25,30 and experimental28,29 results have demonstrated that, at elevated (de)lithiation rates, phase separation is suppressed and replaced with a solid solution pathway. Particles with different morphologies may also have various response to the same applied current, even with similar particle size. It is demonstrated that platelet particles have a much lower exchange current than ellipsoidal particles, which would increase the active particle population and promote uniform solid-solution domains29,51. Importantly, defects play a significant role in controlling the intercalation phase transformation pathway. It is found that particle size can be considered as a good but not sufficient condition to anticipate single phase solid solution formation21. Different amounts of non-stoichiometry and cationic mixing could lead to different phase transformation, even with the same particle size. With considerable Li/Fe disorder, solid solution formation in the whole composition range can be realized21.

We then investigate the effect of particle characteristics on the formation of solid solutions and Li competitiveness. We studied two other particles with various forms. One is commercial LiFePO4 particles (Comm-LiFePO4), which were bought from MTI Corporation (Item Number: Lib-LFPOS21). As shown in Supplementary Fig. 19, the average dimension of the primary ellipsoidal shape particles is ~430 nm. Additionally, the dimension of the secondary particles is ~2.93 μm. As a comparison, Supplementary Fig. 20 shows the original particles (Synthesized-LiFePO4) which we used for all the experiments unless mentioned. The lateral dimension along the long axis is ~1.93 μm, with the [010] channel length ~270 nm. Besides, we synthesized another platelet-like particle (EG-LiFePO4) as shown in Supplementary Fig. 21 with smaller lateral (~97 nm) and thickness dimensions (~0.50 μm). All the particles have dimensions for the migration direction below 1 µm. Both Comm-LiFePO4 particles and EG-LiFePO4 particles follow the same chemical Li extraction process to prepare empty FePO4 hosts (See Methods for more details).

Comm-FePO4, Synthesized-FePO4, and EG-FePO4 showed capacity of 135 mAh/g, 147 mAh/g, and 125 mAh/g under 0.1 C, using 13.5 mA/g, 14.7 mA/g, and 12.5 mA/g respectively (The total capacity is measured by cycling the electrodes in 60 mL 1 M LiCl aqueous solutions between −0.6 V and 0.6 V (vs. Ag/AgCl/KCl (4.0 M)) at room temperature (20~25 °C)). It is worth mentioning that not all particles are good battery quality particles, especially EG-FePO4. Their low delivered capacity can be correlated to the presence of the high level of defects. Supplementary Fig. 22 shows example XRD patterns collected on flat glassy carbon for Comm-FePO4, Synthesized-FePO4, and EG-FePO4 electrodes with 20% Li seeding under 4 C (540 mA/g for Comm-FePO4, 588 mA/g for Synthesized-FePO4, and 500 mA/g for EG-FePO4). We seeded 20% Li for each type of particles and summarized the solid solution fractions in Supplementary Fig. 23a. In the case of Comm-FePO4 ellipsoidal shape particles, the total SS fraction generated is the least (Total SS = 0.234 ± 0.002) with the intercalated Li ions mainly formed fully occupied LiFePO4 phase, as indicated by the pronounced LiFePO4 (020) peak in Supplementary Fig. 22a. And the calculated weighted sum of Li is around 17% from the XRD pattern, close to the 20% Li seeding. The ellipsoidal shape and low defect level of Comm-FePO4 particles could increase the miscibility gap, which can suppress solid solution formation29,32,38,39,51. Meanwhile, we achieved the lowest selectivity with Comm-FePO4 particles (Li/(Li+Na)net = 0.26 ± 0.01, in Supplementary Fig. 23b).

For the platelet-like EG-LiFePO4 particles, we noticed that there is ~23.5% Li remained in the host after chemical Li-extraction process (Supplementary Table 10). The chemical route initially used cannot remove Li+ completely, suggesting the presence of defects in the EG-FePO4 particles which is consistent with their lower capacity. It is worth noting that these trapped Li species are in the form of solid solution phases, as evidenced by the strong solid solution intensity band in Supplementary Fig. 24a. Furthermore, the XRD patterns and the fitted phase fractions didn’t change after Li recovery deintercalation (Supplementary Fig. 24 and Supplementary Table 11), suggesting a lack of mobility of these defect-induced trapped Li ions during (de)intercalation. The EG-FePO4 particle shows a slightly higher Li selectivity (Supplementary Fig. 23b) after 20% seeding and without Li seeding (Li/(Li+Na)net = 0.81 ± 0.01 for L(0.2)4C-LN(0.7)0.1C and Li/(Li+Na)net = 0.74 ± 0.01 for L(0)-LN(0.7)0.1C), compared with Li pre-seeded Synthesized-FePO4 particle (Li/(Li+Na)net = 0.72 ± 0.03 for L(0.2)4C-LN(0.7)0.1C).

For the comparison among the three types of particles, the Li selectivity shows the same trend as the high-Li solid solution fractions for 20% seeded samples (Supplementary Fig. 23). However, the high-Li solid solution fraction to Li selectivity correlation across different particles might not follow the same linear relationship. Therefore, when comparing different particles, morphologies, sizes, and defect levels have to be taken into consideration since they can act together and play a complex role in determining the intercalation pathway and phase formation. Besides solid solution formation, some other aspects may also affect Li/Na selectivity. For example, coherency strain energy has different anisotropies and magnitude when changing from FePO4 to LixFePO4 or NaxFePO4, dependent on the particle size and the particle morphology, which may also be a significant factor for Li competitiveness40. Here, we demonstrated that production of Li solid solution phases is an effective strategy to improve the Li selectivity beyond the intrinsic thermodynamic and kinetic material preference to Li. More systematic studies on other structural factors could bring new opportunities in the future to facilitate the Li extraction process.

Discussion

In summary, both DFT calculation and structural characterization reveal that our model 1D FePO4 host tends to phase separate upon Li and Na ions co-intercalation. Benefiting from the phase separation, we improve the Li ions co-intercalation competitiveness by creating Li SS phases. Li SS phases restrict Na-ion intercalation and enhance Li-ion intercalation preference. We show both experimentally and theoretically that high-Li and low-Li SS phases are not equivalently effective in repelling Na. High-Li SS phases exhibit a strong correlation with Li selectivity enhancement and are more effective in promoting Li competitiveness. Moreover, particle characteristic is a critical factor in determining the solid solution formation, which affects co-intercalation behavior and Li selectivity. In our study, with a similar level of seeding, the solid solution fractions are higher in the platelet particles synthesized but lower for commercial ellipsoidal-shaped particles. Additionally, as the defect level in the particles increases, the trapped remnant Li amount increases in the host. These trapped Li exists as solid solution phases and leads to a higher Li selectivity. However, the influence of material characteristics (including morphologies, sizes, and defects) can be complex and requires future work to reveal their interplays. These insights highlight the importance of manipulating the co-intercalation kinetic pathways for controlling the Li selectivity.

Methods

Synthesis of FePO4 microplatelets

To synthesize pristine LiFePO4 microplatelets, a solvothermal method with a mixed water and polyethylene glycol solvent was used, modified slightly from the previous report48. All the operations were done in an N2/H2O glovebox (<1 ppm O2) to ensure that all precursors are not exposed to oxygen. 6 mL of 0.2 M H3PO4(aq) was mixed with 24 ml of polyethylene glycol 400. Afterward, 18 mL of 0.2 M LiOH(aq) was added to produce the creamy-white Li3PO4 precipitate. This mixture was stirred in an N2 glovebox overnight to remove dissolved oxygen. 1.2 mmol of FeSO4·7H2O was dried under vacuum in a Schlenk line overnight, while 12 mL of H2O was stored in the N2 glove box for 24 h to deoxygenate. Next, the deoxygenated H2O was transferred to the dried FeSO4 powder and stirred for about 10 min, creating a lime-green solution. The FeSO4 solution was transferred to the Li3PO4 suspension without oxygen exposure, and the entire mixture was transferred to a 100 mL Teflon-lined autoclave. The autoclave was heated to 140 °C for 1 h, then to 210 °C for 17 h and cooled.

After the synthesis was completed, the white LiFePO4 particles were centrifuged three times with deionized water and dried. Carbon coating was conducted by mixing the LiFePO4 with sucrose at a mass ratio of 5:1 (LiFePO4:sucrose) without breaking the primary particles. This sample was heated to 600 °C for 5 h in a tube furnace under flowing Ar to yield the carbon-coated LiFePO4. Surface carbon coating is used to increase the electronic conductivity of LiFePO4 and has proven to be an effective strategy53,54.

For chemical extraction of Li from carbon-coated LiFePO4, an oxidizing solution was prepared by dissolving 1.36 g of nitronium tetrafluoroborate (NO2BF4) in 80 mL of acetonitrile. 0.8 g of carbon-coated LiFePO4 powder was immersed into the solution and stirred for 24 h at room temperature (20~25 °C). The powder was then washed several times by acetonitrile and finally dried in a vacuum oven for 12 h. Finally, we will have micro-sized FePO4 platelet particles (Supplementary Fig. 20).

Commercial LiFePO4 particles (Comm-LiFePO4) were bought from MTI Corporation (Item Number: Lib-LFPOS21; Supplementary Fig. 19). We also synthesized a smaller platelet-like LiFePO4 particle by replacing 24 ml polyethylene glycol 400 with 24 ml ethylene glycol in the synthetic process, keeping all the other steps the same. The new formulation gives us smaller LiFePO4 platelet-like particles shown in Supplementary Fig. 21, which are labeled as EG-LiFePO4 particles. See Supplementary Fig. 25 and Supplementary Table 12 for the structure verification (Lebail refinements) of bought Comm-FePO4/LiFePO4 and EG-FePO4/LiFePO4 particles.

Preparation of electrodes

All FePO4 electrodes were prepared by casting a slurry of FePO4, Super P carbon black (MTI Corporation; Item Number: Lib-SP; average particle size ~40 nm; purity ≥99.5%), and polyvinylidene fluoride (MTI Corporation; Item Number: Lib-PVDF; purity ≥99.5%) with a mass ratio of 80:10:10, in N-methyl-2-pyrrolidone. The electrode slurry was drop cast on a 0.5 × 1 cm2 geometrical surface of a porous carbon cloth (ELAT-H, FuelCellEtc, 406 μm in thickness, 80% porosity) current collector of 5 × 1 cm2 or a flat glassy carbon disk electrode (5 mm in diameter, 4 mm in thickness) and dried on a hotplate at 100 °C overnight. 3 nm TiO2 was coated onto the FePO4 electrodes to increase the wettability and decrease the contact impedance (See Supplementary Figs. 2627,  28, Supplementary Tables 1314, and Supplementary Note 5 for more discussions of surface carbon and TiO2 coatings), using atomic layer deposition (ALD) at 100 °C, 0.645 Å/cycle with tetrakis(dimethylamido)titanium (IV) and H2O as precursors (Savannah G2 Thermal ALD). During tests, the other end of the carbon cloth was connected to a Pt clamp. The active material mass loadings ranged between 7 and 14 mg cm−2. To measure the accessible capacity, the electrodes were cycled in 1 M LiCl aqueous solutions at 14.7 mA/g (Supplementary Fig. 29a) between −0.6 V and 0.6 V (vs. Ag|AgCl|KCl (4.0 M)), which delivered a 147 mAh/g capacity. See Supplementary Fig. 29 for detailed aqueous electrochemical energy storage performance evaluation. FePO4 counter electrodes were made with the same slurry depositing on carbon felt (Alfa Aesar) disks (0.9525 cm diameter × 3.18 mm thickness, around 240 g/m2 in areal weight) by galvanostatically sodiating FePO4 in 1 M NaCl(aq) at a C/20 (7.35 mA/g) rate until reaching a −0.6 V versus Ag/AgCl voltage cutoff. C/N describes the current to (de)intercalate the electrode in Nh. The active material mass loading on the counter electrodes ranged between 60 and 70 mg cm−2. The larger mass loading of the counter electrode ensures we have enough ion stock in the counter electrode to avoid side reactions from water splitting and pH fluctuations.

We also evaluated the aqueous electrochemical energy storage performance of Comm-FePO4 and EG-FePO4 samples (Supplementary Figs. 30 and 31). Specifically, Comm-FePO4 and EG-FePO4 were cycled in 1 M LiCl aqueous solutions at 13.5 mA/g and 12.5 mA/g respectively, between −0.6 V and 0.6 V (vs. Ag|AgCl|KCl (4.0 M)), which delivered 135 mAh/g and 125 mAh/g capacity, respectively.

Electrochemical methods

All electrochemical operations were performed on a Bio-Logic VMP3 workstation using a three-neck round-bottomed flask at room temperature (20~25 °C). N2 (purity > 99.998%) was continuously bubbled into the solution to avoid side reactions caused from dissolved O27. Ag|AgCl|KCl (4.0 M) was used as the reference electrode.

During seeding process, FePO4 working electrodes were paired with LiFePO4 counter electrodes for galvanostatic Li-ion intercalation in 60 mL 1 M pure LiCl(aq) with different C rates (0.1 C, 2 C, 4 C, 6 C and 8 C; 1 C is equivalent to 147 mA/g specific current) and capacity range (10%, 20%, 30% and 40%; capacity range always relative to the measured capacity in 1 M LiCl aqueous solutions under 0.1 C, which is 147 mAh/g). For example, L(0.2)4C means seeding 20% of Li (29.4 mAh/g) into FePO4 hosts under 4 C (588 mA/g). After the seeding process, electrodes were rinsed with 1 L of DI water with a flow rate of ~0.3 L/min to remove adsorbed Li+ and ready for the intercalation process. Specifically, L(0) means no seeding process.

During co-intercalation process, with or without seeding, all the working electrodes, paired with NaFePO4 counter electrodes, would undergo intercalation in 500 mL of synthetic brine solutions (1 mM LiCl and 1 M NaCl mixed solution) until 70% of the total capacity using different intercalation C rates (0.1 C, 0.2 C, and 0.5 C; 0.1 C equals to 14.7 mA/g). For example, L(0.2)4C-LN(0.7)0.1C means, after 4C-20% seeding process (588 mA/g−29.4 mAh/g), the intercalation was carried out under 0.1 C (14.7 mA/g) until 70% of capacity (102.9 mAh/g) was used.

During recovery process, after finishing the Li extraction in Na-dominated solutions, the electrode was first rinsed in three different 60 mL DI water for 30 min with continuous N2 bubbling to remove excess adsorbed cations. The electrode was then de-intercalated in 30 mM NH4HCO3 solution with a constant current of C/30 (4.9 mA/g), using a graphite rod (Sigma-Aldrich, 99.995%, 10 cm length × 6 mm diameter) as the counter electrode and Ag|AgCl|KCl (4.0 M) as the reference electrode. The solution before and after the deintercalation process was collected for ICP-MS for Li and Na concentration measurement. We measure Li and Na concentration in the recovery solution and make sure the total ion amount measured matches the electrochemical deintercalation capacity with ~5% error tolerance.

See Supplementary Fig. 32 for the example electrochemical extraction cycle curves, including Li extraction and recovery steps. See Supplementary Fig. 33 for the detailed images of the cells used in the seeding, co-intercalation, and recovery processes. All the electrochemical operations were performed at room temperature (20~25 °C) with N2 (purity > 99.998%) continuously bubbled into the solution from the inlet. Specifically, no climatic/environmental chamber is used.

Electrochemical impedance spectroscopy (EIS) was conducted in 60 mL 1 M LiCl aqueous solution under open air at room temperature (20~25 °C), with a graphite rod as the counter electrode and Ag|AgCl|KCl (4.0 M) as the reference electrode. The applied signal was potentiostatic, with working potential set at open circuit voltage. The frequency ranged from 200 kHz to 100 mHz with 6 data points per decade of frequency at a 10 mV amplitude. Before each frequency, the measurement would wait for a 0.1 period.

Indicators for Li extraction performance

Two different Li/(Li+Na) ratios are reported here. One is Li/(Li+Na)total, which denotes the ratio of total Li+ in the recovery solution, and another one is Li/(Li+Na)net, which subtracts the contributions from the seeded-Li. For example, the tested Li/(Li+Na)total from ICP-MS results for L(0.2)4C-LN(0.7)0.1C is 0.802. Therefore, the calculated Li/(Li+Na)net should be:

$${{{{{{\rm{Li}}}}}}}/({{{{{\rm{Li}}}}}}+{{{{{\rm{Na}}}}}})_{{{{{{\rm{net}}}}}}}= \frac{{{{{{\rm{Li}}}}}}/({{{{{\rm{Li}}}}}}+{{{{{\rm{Na}}}}}})_{{{{{{\rm{total}}}}}}}\cdot {\mbox{Total used capacity}}-{\mbox{Seeded Li capacity}}}{{{{{{\rm{Co}}}}}}-{{{{{\rm{intercalated}}}}}}\,{{{{{\rm{capacity}}}}}}} \\= \frac{0.802\times 0.7-0.2}{(0.7-0.2)}=0.723$$

Another indicator is the Li selectivity, which is defined by the following equation:

$${{{{{{\rm{Li}}}}}}}_{{{{{{\rm{selectivity}}}}}}}=\frac{{(\left[{{{{{\rm{Li}}}}}}\right]/\left[{{{{{\rm{Na}}}}}}\right])}_{{{{{{\rm{final}}}}}}}}{{(\left[{{{{{\rm{Li}}}}}}\right]/\left[{{{{{\rm{Na}}}}}}\right])}_{{{{{{\rm{initial}}}}}}}}$$

XRD characterization

To prepare the seeded electrodes with SS maintained in the structure, we quickly disassembled the electrodes from the beaker cells in air, rinsed them with excess DI water to remove the adsorbed ions, dried the electrodes under vacuum for 20 min, and then sent for XRD measurements. The disassembly process was completed within 2 min of stopping the current. By rapidly disassembling the electrode and removing the electrolyte, we minimize inter-particle Li transport. XRD was carried out on Rigaku MiniFlex 600 diffractometer, using Cu Kα radiation (Kα 1: 1.54059 Å; Kα 2: 1.54441 Å; Kα 12 ratio: 0.4970). The tube voltage and the current used were 40 kV and 15 mA. Diffractograms were recorded with a 0.01° step width and a 5°/min speed. Rietveld refinement was executed on synthesized pristine LiFePO4 and FePO4 microplatelets using GSAS-II software (Supplementary Fig. 4).

ICP-MS characterization

3% HNO3(aq) was used as the diluting matrix for all the Li recovery solutions. Besides, the chemically Li-extracted EG-FePO4 hosts were first washed with distilled water 3–5 times, then digested with aqua regia solution for three days to ensure complete dissolution. The resulting supernatant was diluted with 3% HNO3 for later ICP-MS measurement. All the measurements used either Thermo iCAP Q ICP-MS or Thermo iCAP RQ ICP-MS.

SEM characterization

Scanning electron microscopy (SEM, Zeiss Merlin) was performed at the accelerating voltage of 10 kV.

STEM-EDS characterization

STEM images were acquired using JEOL ARM 200F equipped with a cold field emission source operated at 200 kV. STEM EDS mapping was acquired using an Oxford X-Max 100TLE windowless SDD detector equipped with JEOL ARM 200F.

SEND characterization

Scanning electron nanodiffraction patterns were acquired using a Themis Z S/TEM (Thermo Scientific, Waltham, USA). The microscope was operated in the μProbe STEM mode with an acceleration voltage of 300 kV. The electron probe focused on the sample had a semi-convergence angle of 0.46 mrad, and a probe size of 1.8 nm in FWHM. For strain mapping, camera length was set at 360 mm so that in each diffraction pattern, the positions of about 40 diffraction peaks can be measured using circular Hough transform method to fit a 2D reciprocal lattice. Diffraction patterns were recorded using a CMOS camera (Ceta, Thermo Scientific) at the resolution of 1024 × 1024 pixels and 0.1 s exposure time per diffraction pattern. The scan was over an area of 600 × 400 nm2 with a step size of 10 nm. The lattice parameters and measurement error are converted from diffraction peaks and uncertainty of peak detection, respectively, following our previous works55,56.

Reporting summary

Further information on research design is available in the Nature Research Reporting Summary linked to this article.