Polyethylene terephthalate is one of the most abundantly used polymers, but also a significant pollutant in oceans. Due to growing environmental concerns, polyethylene terephthalate alternatives are highly sought after. Here we present readily recyclable polyethylene terephthalate analogues, made entirely from woody biomass. Central to the concept is a two-step noble metal free catalytic sequence (Cu20-PMO catalyzed reductive catalytic fractionation and Raney Ni mediated catalytic funneling) that allows for obtaining a single aliphatic diol 4-(3-hydroxypropyl) cyclohexan-1-ol in high isolated yield (11.7 wt% on lignin basis), as well as other product streams that are converted to fuels, achieving a total carbon yield of 29.5%. The diol 4-(3-hydroxypropyl) cyclohexan-1-ol is co-polymerized with methyl esters of terephthalic acid and furan dicarboxylic acid, both of which can be derived from the cellulose residues, to obtain polyesters with competitive Mw and thermal properties (Tg of 70–90 °C). The polymers show excellent chemical recyclability in methanol and are thus promising candidates for the circular economy.
With an annual production of 70 million tons globally, polyethylene terephthalate (PET) is one of the most widely used polymers worldwide, indispensable for the manufacturing of packaging material, clothing, fibers, and single-use beverage bottles1,2. However, its accumulation in landfills and oceans has been estimated to reach up to 530 million tons to date2, which accounts for near-catastrophic environmental pollution2,3,4. Moreover, most of the PET is still, typically, produced from fossil resources by copolymerization of ethylene glycol (EG) and terephthalic acid (TPA)5.
Thus, there is a tremendous incentive to obtain readily recyclable6,7 or upcyclable8, fully bio-based PET alternatives9,10 in order to implement circular economy approaches11,12,13,14,15. This will require the development of robust catalytic methods and comprehensive biorefinery strategies16,17,18,19.
A well-known emerging industrial approach is the replacement of petrol-based TPA with furan dicarboxylic acid (FDCA) from sugar-derived 5-hydroxymethylfurfural (5-HMF)20,21. Other laboratory-scale examples focus on pathways to source EG22,23 and TPA from biomass24,25,26,27. Lignin-derived monomers, such as ferulic or syringic acids, have been investigated for the preparation of PET, PET mimics and PET reinforced plastics8,9,28,29 (Fig. 1A). Beckham and coworkers developed a smart upcycling route where PET was modified by EG and muconic acid to give an unsaturated polyester, which was subjected to cross-linking to produce fiberglass-reinforced plastics8.
Reductive catalytic fractionation (RCF)30,31,32,33 has shown a powerful strategy for obtaining high yields of aromatic monomers from lignocellulose that can be converted to a variety of polymer building blocks including TPA24 but also others such as 4-propylcyclohexanol34,35, bisphenol 5,5-methylenebis(4-n-propylguaiacol)36 and 3,3′-ethylenebis(4-n-propylsyringol)37 for making diverse types of polymers. Epp’s group synthesized high-performance adhesives from 4-n-propylsyringol and RCF mixtures38.
Here we present a comprehensive biorefinery strategy for constructing PET analogues, as well as gasoline range and jet-range fuels, based entirely on woody biomass (Fig. 1B). In our unique approach, lignin gives the aliphatic diol building block, while cellulose may provide the necessary aromatic diacid components (FDCA or TPA) in the developed polyesters. Central to the method is the catalytic funneling24,39,40,41,42 of native lignin by a non-noble metal two-step catalytic sequence, which results in 4-(3-hydroxypropyl) cyclohexan-1-ol (PC), obtained as a single compound in an excellent isolated yield of 11.7 wt% (on lignin basis), and other product streams are convertible to gasoline range cyclohexane derivatives and high energy density fuel range bicyclic alkane, achieving a total carbon yield of 29.5%. Notably, this funneling strategy allows overcoming tedious and expensive product isolation and purification protocols, providing a single polymer building block PC from complex biomass feed as well as other usable product streams. This leads to overall excellent lignocellulose utilization and the synthesis of fully wood-based polyesters. The polyesters poly (PC/TPA) and poly (PC/FDCA) display excellent thermal properties (Tg = between 75–90 °C) that compare favorably to commercially available PET and are readily recyclable in methanol. Preliminary techno-economic analysis shows the feasibility of the developed process, thus overall these fully bio-based polyesters are promising candidates for the circular economy.
Catalytic defunctionalization of lignin-derived platform chemicals
We have previously reported on the RCF of various lignocellulose species with excellent selectivity to 4-n-propanolguaiacol (1 G) using pine and to a mixture of 4-n-propanolguaiacol (1 G) and 4-n-propanolsyringol (1 S) using poplar/beech lignocellulose, with Cu20-PMO as a catalyst43. The advantage of this method is that 1 G and 1 S feature an aliphatic alcohol moiety. Thus, first, we envisioned the catalytic funneling of these aromatic platform chemicals to the aliphatic diol PC to test its suitability for making PET analogues. This should be achieved by highly selective demethoxylation/hydrogenation, while maintaining this primary alcohol functionality; a challenging reaction, since the γ-alcohol may participate in direct hydrogenolysis or undergo a dehydrogenation/decarbonylation cascade, especially at higher temperatures43. In fact, such reactions have been typically investigated using simpler substrates or lignin-derived bio-oils, resulting in a higher degree of defunctionalization44,45.
To circumvent the above-mentioned pathways, we first evaluated a range of commercially available heterogeneous catalysts (Fig. 2A and Supplementary Table 1) that may exhibit good reactivity in demethoxylation/hydrogenation under relatively mild conditions (100 °C, for 2 h, using 10 bar H2) in isopropanol as a solvent, using 1 G as a substrate (Supplementary Note 2.1). Both Ni/γ-Al2O3 and Ni/C were inactive, and only moderate success was achieved with Ni/SiO2-Al2O3. Noble metal catalysts demonstrated high 1 G conversions (83.4%, Pd/C and 100%, Ru/C), but low selectivity for the desired diol PC (11.5%, Pd/C and 29.9%, Ru/C), while displaying higher selectivity to 4-(3-hydroxypropyl)-2- methoxycyclohexanol (1) (51.6%, Ru/C, 30.5%, Pd/C) and other side products such as 4-ethylcyclohexanol (2), 4-propylcyclohexanol (3), 4-propylphenol (2H) and 4-(3-hydroxypropyl)phenol (1H).
Gratifyingly, using Raney Ni led to 84.8% 1 G conversion and 84.4% PC selectivity. Diol PC was obtained as a 1:2 mixture of cis: trans isomers (determined by GC-FID (Supplementary Fig. 28b) and 1H-NMR (Supplementary Fig. 32). The addition of H2 gas appeared necessary to suppress the dehydrogenation/decarbonylation cascade otherwise leading to loss of selectivity (Fig. 2B and Supplementary Table 2). The reaction mixture obtained under optimized conditions consisted of compounds PC, 1, and 2.
Further evaluating a range of solvents using Raney Ni (10 bar H2, at 100 °C), it was confirmed that isopropanol is a superior reaction medium (Fig. 2C and Supplementary Table 3), in line with excellent previous work of Rinaldi and coworkers44 using this solvent/catalyst combination for transfer hydrogenation purposes. Thus, we attribute this higher rate of catalytic funneling towards PC to the high transfer hydrogenation activity of Raney Ni as well as its lower tendency for aromatic ring hydrogenation compared to noble metal catalysts46 (Supplementary Note 5). Optimization led to an 84.8% yield of PC at 120 °C for 2 h, applying 10 bar H2 (Fig. 2D and Supplementary Table 4).
Based on the product distribution, PC could have formed through demethoxylation, followed by hydrogenation or vice versa. To gain more insight into plausible reaction pathways from 1 G leading to PC, further kinetic studies were undertaken (Supplementary Notes 2.3, 2.4). Reaction intermediates 1H and 1 showed a significant difference in reactivity when subjected to optimized reaction conditions (Supplementary Tables 7, 8 and Fig. 2E). While 1 displayed very low conversion, 1H was readily hydrogenated to the desired product PC. As a comparison, the aromatic ring hydrogenation rate of 1H (k2 = 0.4400 min−1) was much higher than demethoxylation of 1 (k4 = 10−10 min−1). Furthermore, the rate of hydrogenation of 1 G to 1 (k3 = 0.0017 min−1) and the rate of demethoxylation of 1 G to 1H (k1 = 0.0082 min−1) were comparable. Summing up these observations, the following order was observed: k2 > k1 > k3 > k4, where demethoxylation of 1 G to 1H is the rate-limiting step (Fig. 2E). Therefore, we assume that the catalytic conversion of 1 G proceeds through demethoxylation to give compound 1H, followed by its hydrogenation to PC, while hydrogenation of 1 G to intermediate 1 is considered a parallel side reaction, and other side reactions are relatively slow (Fig. 2F and Supplementary Fig. 27).
Next, 1 S comprising extra functionality was evaluated as substrate (Supplementary Table 5), using Raney Ni catalyst under previously optimized reaction conditions (140 °C, 20 bar, 2 h, isopropanol). Gratifyingly, PC was obtained in an 84.6% yield (Table 1). Moreover, in order to establish a catalytic funneling strategy, model mixtures of 1 G/1 S and 1 G/1 S/1H that are the main components of bio-oils derived by RCF of hardwood or switchgrasses, were successfully converted into PC with an excellent yield of 84.8 and 86.3% respectively.
Catalytic funneling of crude RCF mixtures
Next, we applied the developed Ni-based method for the chemo-catalytic funneling of the bio-oil obtained through RCF of beech lignocellulose (Supplementary Note 2.5). Treating 2 g of beech wood over Cu20-PMO using 40 bar H2 at 180 °C gave crude aromatic bio-oil (Fig. 3) rich in the desired phenolic monomers 1 G (31.3 mg) and 1 S (65.2 mg). Further in-depth analysis by 2D-HSQC (Supplementary Fig. 30), GC-FID (Supplementary Fig. 28b), and GPC (Supplementary Fig. 29) revealed the presence of additional monomers 2 S (21.8 mg), 2 G (5.2 mg), 3 S (4.6 mg) as well as lignin dimers (Supplementary Fig. 28a), oligomers and sugar residues (Supplementary Figs. 29,30). For comparison, we also performed the RCF step using Pd/C and achieved a high 1 G/1 S selectivity (Supplementary Table 10).
Initial attempts to directly subject crude aromatic bio-oil from Cu20-PMO treatment, to further catalytic processing was unsuccessful, likely due to catalyst deactivation. Therefore, a simple fractionation protocol with EtOAc was implemented to get rid of residual lignin oligomers, sugars, and small amounts of organic acids, that may be detrimental to the catalysis, as earlier reported47. Gratifyingly, after this treatment, the—still multicomponent—EtOAc extracts were smoothly converted to a mixture of aliphatic alcohols rich in PC (52.4 mg, 74.2%) and 1 (16.3 mg) (Fig. 3), originating from 1 G and 1 S, which represents 13.9 wt% yield based on lignin, an efficiency of 56.3% given that theoretical maximum yield is 24.7 wt% (Supplementary Note 1). Furthermore, compounds 2 S, 2 G, 3 S, and 3 G also contained in EtOAc extracts in smaller amounts, were converted to alcohols 2 (5.7 mg) and 3 (11 mg), while aliphatic dimers and oligomers (totally approximately 40 mg) were also formed, and these accounted for less than 28.3 wt% of the defunctionalized and hydrogenated product mixture (Supplementary Fig. 28a). PC was obtained by column chromatography from the aliphatic product mixture in an excellent 11.7 wt% isolated yield.
To evaluate the generality of the method, pine and poplar lignocellulose (2 g each) were also subjected to RCF to give crude aromatic bio-oil, resulting in 1 G from pine wood in 7.5 wt% yield (88.0% selectivity), as well as a mixture of 1 G (30% selectivity) and 1 S (46.1% selectivity) from poplar wood in 28.2 wt% combined yield as summarized in Supplementary Table 9. After applying the developed fractionation protocol, catalytic funneling of these RCF oils gave 4.6 wt% yield to PC (76.5% selectivity) for pine and 15.5 wt% yield to PC (75.1% selectivity) for poplar lignocellulose (Table 1 - Entry 6, 7 and Fig. 3).
Synthesis of PET analogues from lignin-derived PC
Considering our strategy, where PC is obtained from lignin through RCF and catalytic funneling, a portion of the residual cellulose may be utilized for the production of FDCA or TPA by applying methods that are already established (Supplementary Note 1), thereby giving fully wood-based PET analogues. Therefore, we have selected methyl esters of aromatic diacids TPA and FDCA for copolymerization with PC (For details on polymer synthesis see Supplementary Note 3). Thus, the methyl ester of TPA was copolymerized with PC using Zn(OAc)248 as a catalyst to result in poly (PC/TPA) in up to 75.0% yield (Table 2, Entry 1), while copolymerization of PC with the methyl ester of FDCA using Titanium (IV) butoxide (TBT)49 as catalyst gave poly (PC/FDCA) in excellent, up to 92.3% yield (Table 2, Entry 5). Overall, the yields of the obtained polyesters, ranging from 50–95% (Table 2, Entries 1-11) largely depended on the type of catalysts, polymerization conditions, and the comonomer partners used. In addition, Sb2O3 was also tested and compared for the synthesis of poly (PC/TPA) but lower reactivity was found (Supplementary Table 11). All prepared polymers displayed a molecular weight range of 20–50 kg mol−1 (Table 2). Selected samples of poly (PC/TPA) and poly (PC/FDCA) were also subjected to a purification protocol48, which further enhanced their Mw to 50 kg mol−1 (Table 2, Entries 3, 6, and Supplementary Figs. 56, 66).
The obtained PET analogues were structurally characterized by 1H, 13C NMR, 2D NMR (Supplementary Figs. 36–46), and FT-IR (Supplementary Fig. 68) as extensively discussed in Supplementary Note 3.1 briefly below. Featuring both an aliphatic primary and secondary alcohol moiety, diol PC is asymmetric in nature and this leads to different reactivity and unit connectivity when forming an ester linkage with diacids at each end of the molecule, hence forming three distinct dyads, namely head-to-tail (H-T), head-to-head (H-H), and tail-to-tail (T-T) (Fig. 4A). We have first assigned the main-chain sequence of poly (PC/TPA), where PC is a mixture of cis and trans isomers (ratio of 1: 2), by 1H, 13C NMR, and 2D-HSQC spectroscopy (Fig. 4C) (for 2D HMBC see Supplementary Fig. 46). The polymer dyad structure was established by 13C NMR (Fig. 4B and Supplementary Fig. 45) analysis that displayed three distinguishable groups of carbonyl signals (C8). Based on related literature data, the high field signals of C8 at 165.24 ppm (C8 cis) and 165.42 ppm (C8 trans) were assigned to H-H type50 and the low field C8 signals (cis and trans overlapped) at 166.05 ppm to T-T type structure51, and the signals in-between (165.28, 165.48, and 165.97 ppm) to mixed (H-T, T-H) type connectivity units. The signal assignment was further confirmed by 2D 1H-13C HMBC (Supplementary Fig. 46), where protons H1, correlating with C8 at 165.2–165.5 ppm and at 165.95–166.05 ppm, respectively displayed an H type bonding, while proton H7 correlating with C8 at 165.9–166.1 ppm was assigned to a T type bonding. The proposed structural assignment was further supported by comparing the spectral data of poly (PC/TPA) with poly (PCtrans/TPA) and poly (PCcis/TPA), separately made from pure trans or cis PC (Supplementary Fig. 47), discussed in detail in the Supplementary Note 3.1. The signals of C8 were assigned according to T-T, T-H, and H-H types of dyads, which displayed a random distribution: [H-H] = [T-T] = 0.25 and [H-T] = 0.50, as quantified by integration of quantitative 13C NMR spectrum (Supplementary Fig. 45). The structural analysis of the polymer poly (PC/FDCA) is discussed in detail in Supplementary Note 3.2, similarly to the poly (PC/TPA), it is a random type polymer.
Overall, the favorable thermal properties of poly (PC/TPA) and poly (PC/FDCA) indicate the potential for the use of these polymers in applications similar to those of PET or as a replacement. Gratifyingly, with glass transition temperatures (Tg) between 70–90 °C, both poly (PC/TPA) and poly (PC/FDCA) (Table 2, Entries 1–6) showed a thermal behavior comparable or better to that of commercial PET (Tg = 67–80 °C)52. Furthermore, these polymers also showed good thermal stability with decomposition temperature T5% = 329 °C and T5% = 319 °C under N2, albeit lower than that of commercial PET (410 °C).
The physical and thermal properties of poly (PCcis/TPA) (Table 2, Entry 7) and poly (PCtrans/TPA) (Table 2, Entry 8) were also compared with that of the synthesized poly (PC/TPA) (Table 2, Entry 1). While poly (PCcis/TPA) was obtained in 84% yield, only 53% yield was reached for poly (PCtrans/TPA) indicating somewhat higher reactivity of the cis PC isomer in the polycondensation reaction. Interestingly, the molecular weight distribution of poly (PC/TPA) was higher than either of the polymers obtained from the pure isomers PCcis or PCtrans. A better heat resistance (Tg value of 76 °C) was obtained for poly (PC/TPA) synthesized from a mixture of cis and trans PC isomers, while different Tg values (72 °C versus 51 °C) were observed for the pure PCcis and PCtrans analogues. The lower value of Tg for poly (PCtrans/TPA), compared to poly (PCtrans/TPA) could be attributed to its lower Mw value (21.2 kg mol−1 versus 16.8 kg mol−1). The T5% values were in the range of 310–320 °C for all poly (PC/TPA) variants. Gratifyingly, the obtained thermal characteristics demonstrate that there is no need for the separation of the mixture of cis and trans isomers of PC obtained by catalytic funneling prior to polymerization.
Next, polyesters from the aliphatic alcohol mixture of PC and 1 (PC, 82 and 1, 13%) obtained from catalytic funneling of a standard equimolar mixture of 1 G and 1 S were prepared (Supplementary Note 3.4). The molecular weights of the corresponding poly (PC/1/TPA) (Mw = 19.4 kg mol−1, Ɖ = 3.11) and poly (PC/1/FDCA) (Mw = 20.8 kg mol−1, Ɖ = 3.34) were somewhat lower than the polyesters prepared from pure PC (Table 2, Entries 9, 10 versus Entries 1, 4). This is reasonable, given that in the biomass-derived streams a mixture of PC (82% purity) and diol 1 is used for the copolymerization, whereby diol 1 bears an extra –OCH3, which may influence reactivity. Therefore, future studies should elucidate the effect of the diol 1 comonomer on the polymer properties, and optimize the molecular weight by careful selection of reaction conditions. Also, further distillative purification of PC may be attempted on a larger scale.
A comprehensive biorefinery strategy from beech wood to PET analogues and complementary products
To show the scalability of our method in a comprehensive biorefinery context, we demonstrated access to PET analogues and complementary product streams such as light and heavy hydrocarbons as shown in Fig. 5 (see also Supplementary Note 3.5). Applying the previously developed two-step catalytic sequence (Cu20-PMO/methanol and Raney Ni/isopropanol) using 10 g beech lignocellulose, crude aliphatic bio-oil was obtained and was then subjected to careful fractional distillation (1 mpa, 100–120 °C) to deliver three distinct Fractions (A, B, and C), consisting of three specific product streams: 4-alkyl cyclohexanols (A), cyclohexane-diol derivatives PC and 1 (B), and higher boiling point dimers and oligomers (C).
Considering raw woody biomass as substrate, the number and difficulty of reaction and product isolation/purification steps will largely influence the overall feasibility of a biorefinery strategy. Here we demonstrate that the polymer building block PC can be obtained in a straightforward manner and high yield from raw biomass. In fact, Fraction B (Supplementary Fig. 77) obtained directly upon fractional distillation from EtOAc extracts, only consisted of diol PC and 1 in high purity (>99%), representing 15.3 wt% yield based on lignin content and could be directly subjected to copolymerization with methyl ester of FDCA to give poly (PC/1/FDCA), that showed excellent and comparable molecular weight (Mw = 27.5 kg mol−1, Ɖ = 2.35) (Table 2, Entry 11) and thermal properties (Tg = 74 °C and T5% = 295 °C), as poly (PC/FDCA) that was prepared using pure PC (for characterizations by 1H-NMR (Supplementary Fig. 78), GPC (Supplementary Fig. 79), TGA (Supplementary Fig. 80), and DSC (Supplementary Fig. 81).
Given that Fractions A and C consisted of more components, we aimed for extensive hydrodeoxygenation (HDO) to alkanes over Raney Ni and HZSM-5 co-catalyst at 220 °C, using cyclohexane as solvent. Thus, Fraction A was converted to gasoline range C7-C9 cyclic hydrocarbons, a mixture of 4-methyl-,4-ethyl-, and 4-propylcyclohexane (Supplementary Fig. 76). The heavier Fraction C was characterized by 1H-NMR (Supplementary Fig. 83), 2D-HSQC (Supplementary Fig. 85), and GC-FID (Supplementary Fig. 82), which confirmed the presence of oxygenated aliphatic dimers and oligomers. These were obtained from the extensive hydrogenation of the lignin-derived dimers and smaller oligomers present in the EtOAc extracts, originating from the β-1, β-5, β-β, and 5-5 linked aromatic dimer units present in hardwood53,54. Analysis of the products obtained upon HDO of Fraction C by 1H, DEPT NMR (Supplementary Figs. 83,84), 2D-HSQC (Supplementary Fig. 86), and GC-FID (Supplementary Fig. 82), revealed successful removal of aliphatic –OH as well as –OMe groups to deliver higher Mw cyclic liquid hydrocarbons (only signals at 0.5–2.0 ppm observed). Further GC-MS analysis confirmed the presence of predominantly bicyclic hydrocarbons and a small amount of tricyclic and polycyclic hydrocarbons (Supplementary Fig. 82). These were quantified by the ECN method. Overall, from 50 mg Fraction C, 18.6 mg crude alkane product was obtained, consisting of predominately 1.2 mg Hβ-1, 2.3 mg Hβ-5, 5.3 mg Hβ-β, 0.8 mg H5-5, and c.a. 3.1 mg unidentified dimers or oligomers.
Overall, this strategy leads to an excellent valorization of beech lignocellulose by converting the lignin component to gasoline (C7–C9 hydrocarbons), high energy density alkane jet fuel (C14–C17 hydrocarbons), and PET analogue, accounting for an overall 29.5% carbon yield based on isolated yields (Supplementary Note 6).
Concerning the carbohydrate fractions, a sieve fractionation protocol to separate the catalyst from the cellulose residues was developed. Next, the catalyst-free solids (mainly containing cellulose), were subjected to a sequence of reaction steps to result in FDCA in a total mass yield of 32.7 wt%, part of which can be used to cover the FDCA necessary for the polymer synthesis (Supplementary Note 7). Alternatively, the surplus of cellulose could be also converted to bioethanol55, or EG22,23 while hemicellulose could be converted to valuable C5 platform chemicals such as furfural, or EG24 (Supplementary Note 1).
On the basis of the experimental data, a preliminary techno-economic assessment (TEA) of the proposed biorefinery strategy shown in Fig. 5 (Supplementary Note 8) was performed, including the catalytic processing of beech lignocellulose by RCF, followed by the fractionation of the obtained bio-oil and the catalytic processing of the respective fractions to final products.
Considering this early process stage, few basic assumptions with regard to fixed operating costs, utility costs and annual capital cost and solvent recovery, have been made in line with recent literature39,56,57. Gratifyingly, along with these mentioned assumptions and with the currently achieved product yields, the techno-economic evaluation shows a positive balance. More specifically, a 6.4% rate of return can be achieved at 99% solvent recovery. Returns are particularly sensitive to methanol and isopropanol recovery at 96 and 98% respectively. Overall, our analysis indicates that catalysts and solvent costs are the main drivers of operating cost, which is not surprising considering the lab-scale development stage of the process. FDCA and furfural form the most important revenue streams whilst fuels are neglectable in both volume and value. Hence, the profitability of the process is particularly dependent on future FDCA price assumptions. Since no mature FDCA market is yet existing, literature estimated revenue values were used58,59,60.
Scale-up would focus on optimization of solvent demand and recovery as well as product yields. Here, especially the RCF step has the potential to be further optimized either in batch61,62 or in continuous flow fashion63,64 leading to both optimal solvent recoveries as well as near-theoretical 1 G/1 S yields that would lead to an estimated doubling of PC yield upon catalytic funneling. In addition, the yield of FDCA can also be further optimized to about 80% based on literature65,66. In fact, such an increase in yields would enable a profitable (7% return) operation of the process even under the assumption of the lowest possible FDCA prices discussed in the literature58. Another important aspect is to carefully assess the benefits of bio-based products compared to fossil-based ones, especially in relation to carbon neutrality and climate benefits. Current prices of fossil-based products PET or fuels we are aiming to substitute are still rather low and difficult to compete with, although this situation may gradually change in the future. However, assuming emission pricing in the range of 50 to 100 Euros per ton CO2 released would add between 2 and 4% to the overall profitability.
Circular economy approaches
The recyclability of poly (PC/TPA) was evaluated by subjecting the material to alcoholysis using methanol, ethanol, 1-propanol, or n-butanol at 180 °C for 4 h, without any additives (Supplementary Note 4.1). The best results were obtained in methanol at 180 °C where 80% of PC and 85% of the methyl ester of TPA (DMTA) could be recovered. A lower yield (<40%) of PC and the corresponding ethyl and propyl terephthalates were obtained in ethanol and 1-propanol (Supplementary Fig. 88A) and no reactivity was found in n-butanol. Gratifyingly, methanolysis of poly (PC/TPA) at 190 °C resulted in 90 and 92% isolated yields of PC and DMTA obtained (Supplementary Fig. 88B).
With the optimized conditions in hand, this polymer was subjected to recycling (Supplementary Note 4.2). As shown in Fig. 6, poly (PC/TPA) was first synthesized and molded for possible applications. Then the produced material was subjected to methanolysis at 190 °C to give a crude mixture of PC and DMTA, characterized by GC-FID (Supplementary Fig. 90) and 1H-NMR (Supplementary Fig. 91). Next, the crude mixture was repolymerized under the original conditions (1 mol% Zn(OAc)2 catalyst, 190 °C °C N2/1 h, 230 °C under vacuum (1 mPa/1 h) to regain poly (PC, TPA), which showed structural and thermal properties (Mw = 16 kg mol−1, Tg = 72 °C, T5% = 319 °C) similar to the virgin polymer (Supplementary Figs. 92–94). These experiments demonstrate the feasibility of our PET analogs for the circular economy.
Reductive catalytic fractionation (RCF) is able to convert raw lignocellulosic biomass into phenolic monomers, aromatic C–C bonded dimers, oligomers, and high quality (hemi)cellulose streams. This work demonstrates an RCF-based biorefinery approach to produce PET analogues made entirely of wood, together with gasoline and jet-range fuels and fuel additives. Central to the strategy is the catalytic funneling of aromatic monophenols 1 G and 1 S into 4-(3-hydroxypropyl) cyclohexan-1-ol (PC) by highly selective Ni-catalyzed hydrogenation/defunctionalization. When applying this method to the complex bio-oil obtained upon RCF from native lignin, a mixture of PC and other cyclic and bicyclic aliphatic alcohols are obtained in the same pot, which are separated by fractional distillation into three distinct cuts based on their boiling point. Thus, PC along with diol 1 (PC, 78% and 1, 22%) are isolated in high purity and copolymerized with cellulose-derived methyl esters of FDCA and TPA. The lighter and heavier fractions can be further processed by HDO to petrol and jet-fuel range alkanes, respectively. Overall, an estimated lignin utilization efficiency of 29.5% can be reached based on isolated product yields, which may be further improved by adjusting the RCF step at the front end of the process. An interesting research direction would be to attempt the use of Cu20-PMO or other suitable catalysts in a continuous flow operation63,64, thereby focusing on maximizing yield and selectivity of 1 G and 1 S to afford near-theoretical yield of PC and optimal solvent consumption and recovery. In fact, the Ni-catalyzed funneling strategy developed here can be used for any bio-oil obtained from RCF58 or other prominent cutting-edge depolymerization efforts59.
In addition, FDCA can be obtained directly from the catalyst-free cellulose-rich residues in up to 33% yield (cellulose basis), matching or surpassing the needed amount for the copolymerization. Besides, any surplus of carbohydrates could be converted to ethylene glycol, or other aliphatic diols, which may be used as a comonomer to improve the mechanical properties of the obtained polymer.
The overall lignocellulose processing approach presented here, consisting of industrially feasible catalytic steps and purification methods, enables the smooth processing of complex raw biomass feed into PC diol which can be readily incorporated into the fully bio-based polyesters poly (PC/1/TPA) and poly (PC/1/FDCA). These polymers display molecular weight range and thermal properties comparable to or better than conventional PET and can be recycled into the virgin monomers. Preliminary studies indicate that further optimization of the mechanical properties is necessary, for example by incorporating of other bio-based diacids or diols or other suitable plasticizers. Also, the optimization of the molecular weights and polydispersity should be carried out with further purified PC diol. Nonetheless, the already measured competitive physical and chemical properties of the polymers, together with the favorable techno-economic assessment, in addition to the straightforward method of producing PC that avoids any extensive purification effort or column chromatography, makes this process interesting for considering future upscaling and the proposed PET and PEF analogues derived entirely from non-edible sources, may become promising candidates for the circular economy.
Materials and reagents
Pine lignocellulose was purchased from Bemap Houtmeel B.V. Poplar and beech lignocellulose were obtained from a local woodshop (Dikhout, Groningen, the Netherlands). Chemicals were used as received unless otherwise specified. Raney Ni 4200, Palladium on carbon, Nickel on carbon, Ruthenium on carbon, 65% Ni/SiO2-Al2O3, Titanium (IV) butoxide (TBT), Zn(OAc)2 were purchased from Sigma-Aldrich, 10% Ni/ɤ-Al2O3 was purchased from Riogen, USA.
Preparation of Cu20-PMO catalyst
Synthesis of Cu20-PMO catalyst was prepared according to our previously reported procedure1. In a typical procedure, a solution containing AlCl3·6H2O (12.07 g, 0.05 mol), Cu(NO3)2·2.5H2O (6.98 g, 0.03 mol), and MgCl2·6H2O (24.4 g, 0.12 mol) in deionized water (200 mL) was dropwise added to a solution containing Na2CO3 (5.30 g, 0.05 mol) in water (300 mL) at 60 °C under vigorous stirring. The pH value was always kept between 9 and 10 by the addition of small portions of a 1 M solution of NaOH. The mixture was vigorously stirred at 60 °C for 72 h. After cooling to RT, the light blue solid was filtered and resuspended in a 2 M solution of Na2CO3 (300 mL) and stirred overnight at 40 °C. The catalyst precursor was filtered and washed with deionized water until chloride free. After drying the solid for 6 h at 100 °C followed by the calcination at 460 °C for 24 h in air, 9.5 g of Cu20-PMO was obtained.
Reductive catalytic fractionation of lignocellulose
Reductive catalytic fractionation of lignocellulosic biomass was carried out in a 100 mL high-pressure Parr autoclave equipped with an overhead stirrer. Typically, the autoclave was charged with 0.4 g of Cu20-PMO catalyst, 2 g of lignocellulose (beech, pine, or poplar), and methanol (20 mL) as a solvent. The reactor was sealed and pressurized with H2 (40 bar) at RT. The reactor was heated to 180 °C and stirred at 400 rpm for 18 h. After completion of the reaction, the reactor was cooled to RT. Then 0.1 mL solution was collected through a syringe and injected into GC-MS or GC-FID after filtration through a PTFE filter (0.45 µm). The solid was separated from the solution by centrifugation and subsequent decantation and additionally washed with methanol (3 × 20 mL). The methanol extracts were combined in a round bottom flask and the solvent was removed in vacuo. The crude aromatic bio-oil was dried in a desiccator in vacuo overnight and was further used as specified below.
Fractionation of crude aromatic bio-oil
To the obtained crude aromatic bio-oil EtOAc (20 mL) was added and it was stirred overnight at RT, which resulted in precipitation of a brownish-colored solid. The suspension was then transferred into a 20 mL centrifuge tube. The solid was separated by centrifugation and decantation and additionally washed with EtOAc (2 × 20 mL). The EtOAc soluble fractions were combined in a round bottom flask and the solvent was removed in vacuo. The soluble and insoluble fractions were additionally dried in vacuo under constant weight. The soluble fraction was washed with a small amount of saturated NaHCO3 (1 × 10 mL) and brine (2 × 10 mL) and dried over anhydrous MgSO4 and further used as specified below.
Catalytic demethoxylation and hydrogenation of model compound 1G
Demethoxylation/hydrogenation of model compound 1 G to PC was carried out in a 100 mL high-pressure Parr autoclave equipped with an overhead stirrer. Typically, the autoclave was charged with 1 g wet Raney Ni catalyst, 0.2 g (1.1 mmol) 1 G, 15 mL isopropanol, and 20 mg dodecane as internal standard. The reactor was sealed and pressurized with H2 (10 bar) at RT. The reactor was heated to 120 °C and stirred at 400 rpm for 2 h. After completion of the reaction, the reactor was cooled to RT. Then 0.1 mL solution was collected through a syringe and injected into GC-MS or GC-FID after filtration through a PTFE filter (0.45 µm). The Raney Ni was separated from the solution by centrifugation and subsequent decantation and additionally washed with isopropanol (3 × 20 mL). Then the isopropanol soluble fractions were combined in a round bottom flask and the solvent was removed in vacuo. The crude product was dried in a desiccator in vacuo overnight and was further used as specified below.
Synthesis of PET analogues derived from PC and comonomer DMFD or DMTA
Copolymerization of model compound PC with DMFD and DMTA was performed using an equal molar ratio of PC and DMTA or DMFD over Zn(OAc)2 or Titanium (IV) butoxide (TBT) catalyst. For example, a 100 mL three-neck flask equipped with a magnetic stirrer and reflux condenser was charged with 0.53 g (3.35 mmol) of PC diol, 0.66 g (3.35 mmol) of DMTA, and 1 mol% (0.0057 g) Zn(OAc)2 catalyst. The esterification reaction was performed at 190 °C for 1 h under nitrogen flow. Then, the reaction temperature was increased to 230 °C, the pressure was reduced to 1 mPa using an oil pulp for 1 and 3 h, respectively. After that, the reaction mixture was cooled down to RT and the pressure was returned to atmospheric pressure by introducing nitrogen. The obtained solid was characterized by NMR, DSC, TGA, FT-IR, and GPC.
Methanolysis of poly (PC/TPA)
Chemical recycling of the synthesized poly (PC/TPA) was carried out in a 100 mL high-pressure Parr autoclave equipped with an overhead stirrer. Typically, the autoclave was charged with poly (PC/TPA) (0.2 g), dodecane (20 mg), and methanol (30 mL). The reactor was sealed and flushed with N2 three times. The reactor was heated to 190 °C and stirred at 400 rpm for 4 h. After completion of the reaction, the reactor was cooled to RT. The PC-rich mixture was then isolated and purified by column chromatography using EtOAc/n-hexane (1:2 to 1:1 to 2:1).
Comprehensive biorefinery strategy for the conversion of beech wood to PET analogs and complementary products
A large-scale reductive catalytic fractionation (RCF) setup using beech wood was carried out over Cu20-PMO catalyst under the following reaction conditions: 10 g beech wood, 2 g catalyst, 180 °C, 120 mL methanol, 40 bar H2, 18 h. RCF of beech wood gave crude depolymerized lignin oil (1531 mg). To the crude depolymerized lignin oil 100 mL of EtOAc was added and the suspension was stirred overnight. Lignin residues and small amounts of sugars were precipitated as brownish-colored solid and separated by centrifugation, decantation and washed with EtOAc (20 mL). The EtOAc soluble fraction was washed immediately with small amount of saturated NaHCO3 (1 × 10 mL) and brine (2 × 20 mL) to deliver EtOAc extracts. Then the EtOAc extracts were transferred in a round bottom flask and the solvent was removed in vacuo. The EtOAc extracts was dried in a desiccator in vacuo overnight and was further used as specified below.
The catalytic funneling of EtOAc extracts were carried out in a 100 mL high-pressure Parr autoclave with an overhead stirrer. Typically, the autoclave was charged with 2 g Raney Ni catalyst, 1120 mg of EtOAc washings, and 20 mL isopropanol. The reactor was sealed and pressurized with H2 (30 bar). The reactor was heated and stirred at 150 °C for 10 h. After the reaction, the reactor was cooled to room temperature and the solvent was removed in vacuo to deliver an aliphatic alcohol mixture. The aliphatic alcohol mixture was subjected to distillation at a temperature range between 100–120 °C using the Kugelrohr apparatus under vacuum 1 mPa, to provide Fraction A, Fraction B, and Fraction C.
To the Fraction, B was added 322 mg (1.75 mmol) of DMFD and 1 mol% TBT catalyst in a 100 mL three-neck round bottom flask. Then the crude mixture was heated to 190 °C for 1 h under nitrogen flow. The pressure was slightly reduced to 1 mPa using an oil pulp and the mixture was heated to 230 °C. The reaction was considered to be complete under vacuum for 3 h. Finally, 406 mg (81.5% yield) of poly (PC/1/FDCA) was obtained. The Fraction A were selectively hydrodeoxygenated (200 mg wet Raney Ni, 100 mg HZSM-5, 20 mL cyclohexane, 220 °C, 30 bar H2, 4 h), to give predominately 4-ethyl cyclohexane (C8) and 4-propyl cyclohexane (C9), as well as a small amount of 4-methyl cyclohexane (C7). The fraction C was subjected to hydrodeoxygenation (HDO), over Raney Ni and HZSM-5 co-catalyst (200 mg wet Raney Ni, 100 mg HZSM-5, 20 mL cyclohexane, 220 °C, 30 bar H2, 6 h) to give predominately dicyclohexane derivatives. The amount of the respective hydrocarbons was determined by the ECN method where the response factor was assumed as 1.0.
The authors declare that all of the data that support the findings of this study are available within the article and its Supplementary Information files or from the corresponding author upon reasonable request.
PP-Admin. PET – A review of material developments. https://www.hbmedia.info/petplanet/2019/09/04/pet-a-review-of-material-developments/ (2020).
Geyer, R., Jambeck, J. R. & Law, K. L. Production, use, and fate of all plastics ever made. Sci. Adv. 3, e1700782 (2017).
Law, K. L. et al. The United States’ contribution of plastic waste to land and ocean. Sci. Adv. 6, eabd0288 (2020).
Jambeck, J. R. et al. Plastic waste inputs from land into the ocean. Science 347, 768–771 (2015).
Ravindranath, K. & Mashelkar, R. A. Polyethylene terephthalate-chemistry, thermodynamics and transport properties. Chem. Eng. Sci. 41, 2197–2214 (2015).
Tang, X. Y. & Chen, E. Y. X. Toward infinitely recyclable plastics derived from renewable cyclic esters. Chem. 5, 284–312 (2019).
Hatti-Kaul, R., Nilsson, L. J., Zhang, B. Z., Rehnberg, N. & Lundmark, S. Designing biobased recyclable polymers for plastics. Trends Biotechnol. 38, 50–67 (2020).
Rorrer, N. A. et al. Combining reclaimed PET with bio-based monomers enables plastics upcycling. Joule 3, 1006–1027 (2019).
Nguyen, H. T. H., Qi, P. X., Rostagno, M., Feteha, A. & Miller, S. A. The quest for high glass transition temperature bioplastics. J. Mater. Chem. A 6, 9298–9331 (2018).
Nakajima, H., Dijkstra, P. & Loos, K. The recent developments in biobased polymers toward general and engineering applications: polymers that are upgraded from biodegradable polymers, analogous to petroleum-derived polymers, and newly developed. Polymers 9, 523 (2017).
Li, H. et al. Carbon-increasing catalytic strategies for upgrading biomass into energy-intensive fuels and chemicals. ACS Catal. 8, 148–187 (2018).
Stahel, W. R. The circular economy. Nature 531, 435 (2016).
Sardon, H. & Li, Z. C. Introduction to plastics in a circular economy. Polym. Chem. 11, 4828–4829 (2020).
Sheldon, R. A. & Norton, M. Green chemistry and the plastic pollution challenge: towards a circular economy. Green. Chem. 22, 6310–6322 (2020).
Colorado, G. Plastics for a Circular Economy Workshop: Summary Report. (U.S. Department of Energy, 2019) https://www.energy.gov/sites/default/files/2020/08/f77/beto-amo-mars-plastics-wksp-rpt-final.pdf.
Stadler, B. M., Wulf, C., Werner, T., Tin, S. & de Vries, J. G. Catalytic approaches to monomers for polymers based on renewables. ACS Catal. 9, 8012–8067 (2019).
De Clercq, R., Dusselier, M. & Sels, B. F. Heterogeneous catalysis for bio-based polyester monomers from cellulosic biomass: advances, challenges and prospects. Green. Chem. 19, 5012–5040 (2017).
Jing, Y. X. et al. Towards the circular economy: converting aromatic plastic waste back to arenes over a Ru/Nb2O5 catalyst. Angew. Chem. Int. Ed. 133, 5587–5595 (2021).
Guo, Z., Yan, N. & Lapkin, A. A. Towards circular economy: integration of bio-waste into chemical supply chain. Curr. Opin. Chem. Eng. 26, 148–156 (2019).
de Jong, E., Visser, H. A., Dias, A. S., Harvey, C. & Gruter, G. J. M. The road to bring FDCA and PEF to the market. Polymers 14, 943 (2022).
Motagamwala, A. H. et al. Toward biomass-derived renewable plastics: Production of 2, 5-furandicarboxylic acid from fructose. Sci. adv. 4, eaap9722 (2018).
Ji, N. et al. Direct catalytic conversion of cellulose into ethylene glycol using nickel‐promoted tungsten carbide catalysts. Angew. Chem. Int. Ed. 120, 8638–8641 (2008).
Wang, A. Q. & Zhang, T. One-pot conversion of cellulose to ethylene glycol with multifunctional tungsten-based catalysts. Acc. Chem. Res. 46, 1377–1386 (2013).
Song, S., Zhang, J. G., Gözaydın, G. & Yan, N. Production of terephthalic acid from corn stover lignin. Angew. Chem. Int. Ed. 58, 4934–4937 (2019).
Pang, J. F. et al. Synthesis of ethylene glycol and terephthalic acid from biomass for producing PET. Green. Chem. 18, 342–359 (2016).
Patet, R. E. et al. Kinetic regime change in the tandem dehydrative aromatization of furan Diels–Alder products. ACS Catal. 5, 2367–2375 (2015).
Pacheco, J. J. & Davis, M. E. Synthesis of terephthalic acid via Diels-Alder reactions with ethylene and oxidized variants of 5-hydroxymethylfurfural. Proc. Natl Acad. Sci. USA 111, 8363–8367 (2014).
Nguyen, H. T. H., Short, G. N., Qi, P. & Miller, S. A. Copolymerization of lactones and bioaromatics via concurrent ring-opening polymerization/polycondensation. Green. Chem. 19, 1877–1888 (2017).
Nguyen, H. T. H., Reis, M. H., Qi, P. & Miller, S. A. Polyethylene ferulate (PEF) and congeners: polystyrene mimics derived from biorenewable aromatics. Green. Chem. 17, 4512–4517 (2015).
Abu-Omar, M. M. et al. Guidelines for performing lignin-first biorefining. Energ. Environ. Sci. 14, 262–292 (2021).
Questell-Santiago, Y. M., Galkin, M. V., Barta, K. & Luterbacher, J. S. Stabilization strategies in biomass depolymerization using chemical functionalization. Nat. Rev. Chem. 4, 311–330 (2020).
Renders, T., Van den Bossche, G., Vangeel, T., Van Aelst, K. & Sels, B. F. Reductive catalytic fractionation: state of the art of the lignin-first biorefinery. Curr. Opin. Biotechnol. 56, 193–201 (2019).
Galkin, M. V. & Samec, J. S. Lignin valorization through catalytic lignocellulose fractionation: a fundamental platform for the future biorefinery. ChemSusChem 9, 1544–1558 (2016).
Schutyser, W. et al. Selective nickel‐catalyzed conversion of model and lignin‐derived phenolic compounds to cyclohexanone‐based polymer building blocks. ChemSusChem 8, 1805–1818 (2015).
Schutyser, W. et al. Selective conversion of lignin-derivable 4-alkylguaiacols to 4-alkylcyclohexanols over noble and non-noble-metal catalysts. ACS Sustain. Chem. Eng. 4, 5336–5346 (2016).
Koelewijn, S. F. et al. Sustainable bisphenols from renewable softwood lignin feedstock for polycarbonates and cyanate ester resins. Green. Chem. 19, 2561–2570 (2017).
Koelewijn, S. F. et al. Promising bulk production of a potentially benign bisphenol A replacement from a hardwood lignin platform. Green. Chem. 20, 1050–1058 (2018).
Wang, S., Shuai, L., Saha, B., Vlachos, D. G. & Epps, T. H. III From tree to tape: direct synthesis of pressure sensitive adhesives from depolymerized raw lignocellulosic biomass. ACS Cent. Sci. 4, 701–708 (2018).
Liao, Y. H. et al. A sustainable wood biorefinery for low–carbon footprint chemicals production. Science 367, 1385–1390 (2020).
Linger, J. G. et al. Lignin valorization through integrated biological funneling and chemical catalysis. Proc. Natl Acad. Sci. USA 111, 12013–12018 (2014).
Schutyser, W. et al. Chemicals from lignin: an interplay of lignocellulose fractionation, depolymerisation, and upgrading. Chem. Soc. Rev. 47, 852–908 (2018).
Perez, J. M. et al. Funneling aromatic products of chemically depolymerized lignin into 2-pyrone-4-6-dicarboxylic acid with Novosphingobium aromaticivorans. Green. Chem. 21, 1340–1350 (2019).
Sun, Z. H. et al. Complete lignocellulose conversion with integrated catalyst recycling yielding valuable aromatics and fuels. Nat. Catal. 1, 82–92 (2018).
Wang, X. Y. & Rinaldi, R. Exploiting H-transfer reactions with RANEY (R) Ni for upgrade of phenolic and aromatic biorefinery feeds under unusual, low-severity conditions. Energ. Environ. Sci. 5, 8244–8260 (2012).
Wu, X. Y., Galkin, M. V. & Barta, K. A well-defined diamine from lignin depolymerization mixtures for constructing bio-based polybenzoxazines. Chem. Catal. 1, 1466–1479 (2021).
Sun, Z. H., Zhang, Z. H., Yuan, T. Q., Ren, X. H. & Rong, Z. M. Raney nickel as a versatile catalyst for biomass conversion. ACS Catal. 11, 10508–10536 (2021).
Elangovan, S. et al. From wood to tetrahydro-2-benzazepines in three waste-free steps: modular synthesis of biologically active lignin-derived scaffolds. ACS Cent. Sci. 5, 1707–1716 (2019).
Mialon, L., Pemba, A. G. & Miller, S. A. Biorenewable polyethylene terephthalate mimics derived from lignin and acetic acid. Green. Chem. 12, 1704–1706 (2010).
Papageorgiou, G. Z., Papageorgiou, D. G., Terzopoulou, Z. & Bikiaris, D. N. Production of bio-based 2,5-furan dicarboxylate polyesters: recent progress and critical aspects in their synthesis and thermal properties. Eur. Polym. J. 83, 202–229 (2010).
Scifiner, Search. C-NMR for 1,4-Benzenedicarboxylic acid, 1,4-dicyclohexyl ester (CAS Registry Number 18699-51-9) https://scifinder.cas.org/scifinder/view/scifinder/scifinderExplore.jsf.
Nishii, Y., Hirai, T., Fernandez, S., Knochel, P. & Mashima, K. Zinc-catalyzed esterification of N-β-hydroxyethylamides: removal of directing groups under mild conditions. Eur. J. Org. Chem. 2017, 5010–5014 (2017).
Demirel, B., Yaras, A. & Elçiçek, H. Crystallization behavior of PET materials. BAÜ Fen. Bil. Enst. Derg. Cilt, 13, 26–35 (2011).
Yue, F. X., Lu, F. C., Regner, M., Sun, R. C. & Ralph, J. Lignin-derived thioacidolysis dimers: reevaluation, new products, authentication, and quantification. ChemSusChem 10, 830–835 (2017).
Van den Bosch, S. et al. Reductive lignocellulose fractionation into soluble lignin-derived phenolic monomers and dimers and processable carbohydrate pulps. Energ. Environ. Sci. 8, 1748–1763 (2015).
Van den Bosch, S. et al. Integrating lignin valorization and bio-ethanol production: on the role of Ni-Al2O3 catalyst pellets during lignin-first fractionation. Green. Chem. 19, 3313–3326 (2017).
Couper, J. R., Hertz, D. W. & Smith, F. L. in Perry’s Chemical Engineering’s Handbook (eds Green, D. W. & Southard, M. Z.) Section 9 (McGraw-Hill Education, 1997).
Lee, Y., Park, H., Han, J. & Lee, J. Economically-feasible production of a nylon monomer using RANEY® catalysts. React. Chem. Eng. 6, 225–234 (2021).
Dubbink, G. H. C. et al. Furfural to FDCA: systematic process design and techno-economic evaluation. Biofuel Bioprod. Bior. 15, 1021–1030 (2021).
Triebl, C., Nikolakis, V. & Ierapetritou, M. Simulation and economic analysis of 5-hydroxymethylfurfural conversion to 2,5-furandicarboxylic acid. Comput. Chem. Eng. 52, 26–34 (2013).
Dessbesell, L. et al. Production of 2,5-furandicarboxylic acid (FDCA) from starch, glucose, or high-fructose corn syrup: techno-economic analysis. Biofuel Bioprod. Bior. 13, 1234–1245 (2019).
Anderson, E. M. et al. Differences in S/G ratio in natural poplar variants do not predict catalytic depolymerization monomer yields. Nat. Commun. 10, 1–10 (2019).
Chen, X., Zhang, K., Xiao, L. P., Sun, R. C. & Song, G. Total utilization of lignin and carbohydrates in Eucalyptus grandis: an integrated biorefinery strategy towards phenolics, levulinic acid, and furfural. Biotechnol. Biofuels 13, 1–10 (2020).
Anderson, E. M. et al. Flow through reductive catalytic fractionation of biomass. Joule 1, 613–622 (2017).
Kumaniaev, I. et al. Lignin depolymerization to monophenolic compounds in a flow-through system. Green. Chem. 19, 5767–5771 (2017).
Yan, L. S. et al. Ruthenium trichloride catalyzed conversion of cellulose into 5-hydroxymethylfurfural in biphasic system. Bioresour. Technol. 279, 84–91 (2019).
Wang, Y. B. et al. Basicity-tuned hydrotalcite-supported Pd catalysts for aerobic oxidation of 5-hydroxymethyl-2-furfural under mild conditions. ACS Sustain. Chem. Eng. 4, 4752–4761 (2016).
K.B. is grateful for financial support from the European Research Council, ERC Starting Grant 2015 (CatASus) 638076, and ERC Proof of Concept Grant 2019 (PURE) 875649. This work is part of the research program Talent Scheme (Vidi) with project number 723.015.005, which is partly financed by The Netherlands Organization for Scientific Research (NWO). X.W. is grateful for financial support from the China Scholarship Council (grant number 201808330391). T.S. thanks COST Action FUR4Sustain- European network of FURan-based chemicals and materials FOR a Sustainable development, CA18220, supported by COST (European Cooperation in Science and Technology).
The authors declare no competing interests.
Peer review information
Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Wu, X., Galkin, M.V., Stern, T. et al. Fully lignocellulose-based PET analogues for the circular economy. Nat Commun 13, 3376 (2022). https://doi.org/10.1038/s41467-022-30735-4
This article is cited by
Closed-loop chemical recycling of cross-linked polymeric materials based on reversible amidation chemistry
Nature Communications (2022)