The pursuit of selective two-electron oxygen reduction reaction to H2O2 in acids is demanding and largely hampered by the lack of efficient non-precious-metal-based electrocatalysts. Metal macrocycles hold promise, but have been relatively underexplored. Efforts are called for to promote their inherent catalytic activities and/or increase the surface exposure of active sites. In this contribution, we perform the high-throughput computational screening of thirty-two different metalloporphyrins by comparing their adsorption free energies towards key reaction intermediates. Cobalt porphyrin is revealed to be the optimal candidate with a theoretical overpotential as small as 40 mV. Guided by the computational predictions, we prepare hydrogen-bonded cobaltoporphyrin frameworks in order to promote the solution accessibility of catalytically active sites for H2O2 production in acids. The product features an onset potential at ~0.68 V, H2O2 selectivity of >90%, turnover frequency of 10.9 s−1 at 0.55 V and stability of ~30 h, the combination of which clearly renders it stand out from existing competitors for this challenging reaction.
Compared to the well-established anthraquinone oxidation process, the two-electron oxygen reduction reaction (2e-ORR) makes possible the on-site, on-demand H2O2 production, and has thereby attracted increasing attention1,2,3. Although it is kinetically favorable in alkaline solution4,5,6, 2e-ORR in acidic solution is much more scientifically important and practically applicable3,7,8. The state-of-the-art candidates in acids are Pd-Hg and Pt-Hg alloys9,10, followed by Au and its alloys11,12. They are unfortunately precious and sometimes toxic. The search for non-precious-metal-based candidates has been actively pursued with some encouraging progresses over the past several years13,14,15,16,17,18,19.
Among potential candidates, metal macrocycles such as porphyrins and phthalocyanines hold great promise, but have been relatively underexplored14,20,21,22. Their catalytic activities can be rationally tuned by changing the metal centers or modifying the macrocyclic ligands23,24,25. The well-defined molecular structures also represent ideal model systems to explore the structure-performance correlation for a range of catalytic processes26,27,28. In spite of great potential, the 2e-ORR performances of metal macrocycles remain largely unsatisfactory14,21. This is due to their low site-specific activities, and more importantly, their conjugated planar structures that readily agglomerate via intermolecular π-π stacking to form particles with few accessible surface sites26. Possible solutions include optimizing molecular structures to promote the inherent catalytic activity or constructing porous frameworks to increase the surface exposure of active sites29,30.
Hydrogen-bonded organic frameworks (HOFs) are a large family of materials that are self-assembled from functional building blocks to form porous two-dimensional (2D) or three-dimensional (3D) frameworks via hydrogen-bond interactions31,32. Having the advantages of high crystallinity, great surface areas, and abundant porosity, they have been extensively explored for gas separation and storage, chemical sensing, proton conduction, and optical applications32,33,34,35. HOFs generally have improved chemical stability than their cousin materials—metal organic frameworks in aqueous solution; the extended hydrogen-bond networks within HOFs may also render them more hydrophilic than covalent organic frameworks, and potentially more advantageous for electrochemical applications. Moreover, compared to popular single-atom catalysts (SACs), HOFs incorporated with transition metal macrocycles have well-defined active sites and present ideal model systems to explore the structure-performance correlation. Unfortunately, there are very few investigations about the electrochemical applications of HOFs.
In this study, we perform the high-throughput computational screening for metalloporphyrins with various metal centers using density functional theory (DFT) calculations, and identify cobalt porphyrin to have the best 2e-ORR activity and selectivity. As guided by the theoretical predictions, we accordingly prepare several hydrogen-bonded metalloporphyrin frameworks with similar topology but different metal cores. The cobaltoporphyrinic HOF demonstrates an optimal performance with H2O2 selectivity of >90% over a broad potential window and catalytic turnover frequency (TOF) of 10.9 s−1 at 0.55 V in acids exceeding those of precious metal benchmarks.
High-throughput DFT screening and calculations
High-throughput computational screening is an effective method for rapid catalyst exploration and can significantly reduce the time to discovery36,37. Here, we constructed metal porphyrins with various metal centers, and compared their structural stability and electrocatalytic performances using high-throughput DFT calculations (see Method for details). The structural model is depicted in Supplementary Fig. S1. Note that the nominal oxidation state of the metal cores is +2 in order to maintain the overall charge neutrality. The formation energy (Eform) is first derived for different metal porphyrins, and summarized in Fig. 1a according to the position of the metals in the periodic table. The negative value of Eform implies that metal atoms are energetically favorable to form metal porphyrins instead of self-aggregating to clusters. Here, the Eform values of all the metalloporphyrins are calculated to be negative in the range between −2 and −7 eV, indicating that they are thermodynamically stable for catalytic applications.
We next simulated the ORR process on metal porphyrins via either the two-electron pathway to form H2O2 or the four-electron pathway to form H2O. All the reaction intermediates (e.g., *OOH, *O, and *OH) prefer to adsorb on the metal centers instead of interacting with porphyrin rings or peripheries. Worth noting is that the adsorption free energy of *OOH (ΔG*OOH) is an important descriptor for 2e-ORR as first advised by Rossmeisl et al.9. Its optimal value is 4.22 eV at U = 0 V (or 3.52 eV at U = 0.70 V). Figure 1b illustrates the free-energy diagram for 2e-ORR on different metal porphyrins at U = 0.70 V. Among all the catalysts investigated, cobalt porphyrin exhibits the best activity with its ΔG*OOH slightly more positive (~0.04 eV) than the ideal value. The inset of Fig. 1b illustrates the corresponding adsorption configuration of *OOH on cobalt porphyrin. The ΔG*OOH value reflects the adsorption strength of *OOH on metal porphyrins, which is closely related to the Bader charge of the metal centers. As shown in Fig. 1c, there is a roughly linear correlation between them: metal centers with more positive charges generally have stronger adsorption strengths towards *OOH. It is worth highlighting that cobalt with the optimal ΔG*OOH value is determined to have a Bader charge of 1.0 e. Its charge density distribution is shown in the inset of Fig. 1c. The projected density of states (PDOS) analysis further unveils the electronic properties of cobalt porphyrin (Fig. 1d). The metal center is strongly anchored by nitrogen atoms through the electronic coupling between the N 2p orbital and the Co 3d orbital. Upon the *OOH adsorption, the electronic overlap between the bonded-O 2p orbital of *OOH and the Co 3d orbital is observed, evidencing their direct interaction.
Moreover, we define the thermodynamic limiting potential (UL) as the highest reduction potential where all the reaction steps become downhill in free energy, and use this metric to estimate the relative activities for 2e-ORR and 4e-ORR. A good catalyst would have a positive UL close to the equilibrium potential of Uo(O2/H2O2) = 0.70 V for 2e-ORR or Uo(O2/H2O) = 1.23 V for 4e-ORR. Fig. 1e presents the calculated UL(O2/H2O2) and UL(O2/H2O) values of different metal porphyrins in a 2D map. The reaction selectivity can be readily estimated by comparing the theoretical overpotential (η = Uo – UL) of the two reaction pathways. Catalysts located in the upper left corner have great 2e-ORR selectivity, whereas those located in the lower right corner have great 4e-ORR selectivity. It can be thereby determined that cobalt porphyrin best favors 2e-ORR with η(O2/H2O2) = 0.04 V, and that rhodium porphyrin best favors 4e-ORR with η(O2/H2O) = 0.23 V. The combination of great 2e-ORR activity and selectivity of cobalt porphyrin revealed from our high-throughput computations encourages us to experimentally pursue this candidate as would be shown in the following.
Material synthesis and characterization
Since small-molecule porphyrins tend to agglomerate via intermolecular π-π interactions, we incorporated these functional moieties into porous frameworks. Hydrogen-bonded cobaltoporphyrin frameworks (PFC-72-Co) were prepared through self-assembling 5,10,15,20-(tetra-4-carboxyphenyl) porphyrin (TCPP-Co) in N,N-dimethylformamide (DMF) and 1,2,4-trichlorobenzene (TCB) at 100 °C as schematically illustrated in Fig. 2a (see Method for details)38. The single-crystal X-ray diffraction (XRD) analysis of PFC-72-Co reveals that it has a 2D square layer topology with opening channels of 18.6 × 15.7 Å2 (Fig. 2b and Supplementary Table S1). Individual cobaltoporphyrin unit connects with its four neighbors through the carboxyl groups via O–H···O hydrogen bonds. Adjacent layers are stacked in the AA’ mode with an interlayer distance of 3.62 Å (Supplementary Fig. S2). The porphyrin moiety in PFC-72-Co is experimentally determined to be non-planar and slightly bent as illustrated in Supplementary Fig. S3a. This configuration somewhat deviates from the ideal planar configuration adopted in our DFT calculations but is determined to have little impact on the electrocatalytic activity (Supplementary Fig. S3b). The powdery PXRD pattern of PFC-72-Co exhibits pronounced diffraction peaks in accordance with the standard pattern (simulated based on the crystal structure derived from single-crystal XRD), which evidence its great crystallinity and highly ordered molecular structure (Fig. 3a). The actual Co content in PFC-72-Co measured by inductively coupled plasma – mass spectrometry is close to the theoretical value (Supplementary Table S2). For control experiments, we also prepared isoreticular HOFs based on metal-free porphyrin (PFC-71), nickel porphyrin (PFC-73-Ni), and copper porphyrin (PFC-73-Cu). They have identical topologies but slightly different interlace modes (Supplementary Figs. S2 and S4).
We carried out a multitude of spectroscopic characterizations to confirm the successful preparation of HOFs. The Fourier-transform infrared spectroscopy (FTIR) spectra of metal-free TCPP and PFC-71 are in perfect agreement with previous reports (Supplementary Fig. S5)39. Compared to them, the spectra of metalloporphyrins (TCPP-Co/Ni/Cu) and corresponding HOFs (PFC-72-Co, PFC-73-Ni, and PFC-73-Cu) display a new peak around 1000 cm−1 (assignable to the stretching vibration of N-M, M = Co, Ni or Cu), whereas the peak around 963 cm−1 (assignable to the stretching vibration of N-H) vanishes. The 1H nuclear magnetic resonance (NMR) spectra of metal-free TCPP and PFC-71 show the characteristic inner amino proton (N-H) signal at −2.94 ppm, which is however absent in metalloporphyrins and corresponding HOFs (Supplementary Fig. S6), which are consistent with previous reports40,41. Raman spectra of TCPP-Co and PFC-72-Co display signature vibration bands of porphyrins as reported in previous works (Supplementary Fig. S7)42. The band at 1017 cm−1 corresponds to the Co-N stretching vibration. TCPP-Ni/Cu and their corresponding HOFs exhibit similar spectral features as those of TCPP-Co and PFC-72-Co. From the ultraviolet-visible (UV-vis) spectra, all the metalloporphyrins and HOFs exhibit absorption peaks characteristic of porphyrins (Supplementary Fig. S8).
Our products were further characterized by their microstructures. Scanning electron microscopy (SEM) shows that all of them are microsized particles with well-defined shapes and edges (Supplementary Fig. S9). From the broken edges, these particles are observed to consist of stacking laminates. In spite of their slightly different topologies as illustrated in Supplementary Fig. S2, the N2 sorption isotherms of our samples reveal comparably high Brunauer–Emmett–Teller surface areas in the range of 1690–1790 m2 g−1 and prominent channel sizes around ~18.4 Å according to the pore size distribution curves (Fig. 3b, c). Transmission electron microscopy (TEM) image of PFC-72-Co evidences the clear fringes of ~1.9 nm in line with its in-plane lattice spacing (Fig. 3d). Moreover, the coordination environment of the metal center in PFC-72-Co was probed using X-ray absorption (XAS) analysis at the Co K edge. From its X-ray absorption near edge structure (XANES), the white-line peak of PFC-72-Co is observed to locate between those of the Co foil and the CoO reference and much closer to the latter, indicating that the valence state of the Co center in PFC-72-Co is approximately +2 (Fig. 3e). The pre-edge peak at 7715 eV is assignable to the 1s→4pz shakedown transition (inset of Fig. 3e)43. The Fourier-transform extended X-ray absorption fine structure (EXAFS) of PFC-72-Co exhibits a major peak at 1.5 Å corresponding to the Co-N coordination (Fig. 3f). The formation of metallic clusters is excluded by the absence of the Co-Co signal at 2.2 Å. All the above spectroscopic and microscopic results unambiguously support the formation of hydrogen-bonded porphyrin frameworks with high crystallinity and metallization of their porphyrin cores.
Electrochemical performance for 2e-ORR
We next interrogated the electrochemical performances of PFC-72-Co for 2e-ORR to H2O2 in 0.1 M HClO4. Catalyst powders were loaded onto a rotating ring disk electrode (RRDE) to form smooth thin films with a typical loading of 10 μg cm−2 (see Method for details). When the electrolyte is saturated with Ar, no current response is recorded (Fig. 4a). When the electrolyte is saturated with O2, metal-free PFC-71 exhibits a negligible cathodic activity until at <0.1 V versus reversible hydrogen electrode (RHE). By stark contrast, the cathodic current density of PFC-72-Co is observed to take off at ~0.68 V (corresponding to ~20 mV overpotential), which is in perfect agreement with the theoretical overpotential of η = 40 mV predicted by our DFT calculations. Since the onset, its current density gradually rises and reaches ~3.0 mA cm−2 at the working potential of 0 V and the electrode rotation speed of 1600 rpm. The potential-dependent evolution of the disk current density is synchronized with the evolution of the ring current from the electrochemical re-oxidation of H2O2 on the Pt ring (Fig. 4b). The corresponding H2O2 selectivity is calculated to be >90% between 0.1 and 0.5 V. Furthermore, PFC-72-Co is assessed at different electrode rotation speeds from 400 to 2500 rpm as shown in Fig. 4c. By fitting J−1 ~ ɷ−1/2 using the Koutecky–Levich equation (Supplementary Fig. S10), the reaction electron transfer number is estimated to be ~2.2 (Fig. 4c), again corroborating the predominant 2e-ORR selectivity of PFC-72-Co. For comparison, TCPP-Co—in spite of its identical catalytic species with PFC-72-Co—exhibits inferior 2e-ORR activity and selectivity, which highlights the indispensable contribution from the reticular structure of PFC-72-Co during electrocatalysis. PFC-73-Ni and PFC-73-Cu demonstrate even worse activities generally consistent with our theoretical predictions (Supplementary Fig. S11). The electrochemical impedance spectroscopy analysis of PFC-72-Co, TCPP-Co, and PFC-71 unveils that PFC-72-Co has the smallest charge transfer resistance at 0.5 V in line with its greatest electrocatalytic activity (Supplementary Fig. S12). The H2O2 selectivity of PFC-72-Co (~90%) is jointly contributed by its high production rate and low degradation rate. Negligible cathodic current density is measured on PFC-72-Co during the H2O2 reduction experiment (Supplementary Fig. S13). In addition, we investigate the effect of the catalyst loading and find that higher loading adversely compromises the H2O2 selectivity (Supplementary Fig. S14). We also explore the effect of the electrolyte pH and observe that hydrogen bonds in PFC-72 start to dissociate at pH >5 so that it only works in acidic or weakly acidic solution.
In order to elucidate the site-specific activity of PFC-72-Co, we calculated its TOF at different working potentials by normalizing the kinetic current density over the number of electrochemically accessible active sites (Supplementary Fig. S15). It is worth noting that the number of active sites can be estimated by integrating the total charges associated with the CoII/CoIII oxidation wave during the anodic polarization under N2, which is found to be the most reliable method available so far. Fig. 4d depicts the potential-dependent TOF values of PFC-72-Co alongside the typical data of Pt/Pd-Hg alloys9,10, Pt/Pd-based SACs44,45, Co-based SACs16,17,46,47 and Co-based molecules from recent literatures29,30. The TOF value of PFC-72-Co is determined to be 0.74 s−1 at 0.65 V and 10.9 s−1 at 0.55 V, far superior to all of its organic or inorganic competitors as well as the state-of-the-art Pt/Pd-Hg alloys in acids, and underlining its potential for this challenging reaction.
At last, we investigated the potentiostatic stability of PFC-72-Co using RRDE at 1600 rpm in O2-satuated 0.1 M HClO4. As shown in Fig. 4e, when biased at 0.1 V, the disk and ring currents decline at the beginning and then gradually level off during the first hour. After that, the test is suspended and the electrolyte is bubbled again with O2. When the test is resumed, the disk and ring currents go back to the original values, indicating no loss of the catalyst activity. The potentiostatic test can be repeated again and again, and the corresponding H2O2 selectivity remains >90% during the stability test. Negligible catalyst dissolution or demetallization is observed since the Co concentration of the electrolyte is measured to have no obvious change before and after the test (Supplementary Table S3). Here, we kept the stability test on RRDE relatively short because it is harmful and potentially hazardous for the instrument to continuously rotate for a longer period. The long-term stability of PFC-72-Co was instead pursed by loading the catalyst on a carbon fiber paper electrode in an H-cell. After 30 h operation, the current density remains at ∼5 mA cm−2 and the H2O2 selectivity stays over 85% at 0.1 V (Supplementary Fig. S16). Characterizations of the catalyst after the stability test reveal minimum structural and compositional changes, thereby evidencing its great structural integrity (Supplementary Fig. S17).
In summary, using high-throughput DFT calculations, we screened 32 different kinds of metal porphyrins for 2e-ORR to H2O2. Among them, cobalt porphyrin was identified to have the optimal activity and selectivity with the theoretical overpotential as low as 0.04 V. Guided by the theoretic predictions, we prepared hydrogen-bonded cobaltoporphyrin frameworks through the self-assembly of TCPP-Co in solution. PFC-72-Co featured high structural crystallinity, large surface areas, and abundant catalytic sites. The product could enable efficient and stable H2O2 production in 0.1 M HClO4 with an onset potential of ~0.68 V and >90% H2O2 selectivity over a broad potential window. Besides, its TOF value was estimated to be 10.9 s−1 at 0.55 V, far superior to its organic or inorganic competitors as well as the state-of-the-art Pt/Pd-Hg alloys in acids. As far as we are aware, our study here represents a demonstration of hydrogen-bonded metalloporphyrin frameworks for electrocatalysis that may expand the potential applications of these interesting materials.
The high-throughput computations were performed using DFT as implemented in the Vienna Ab-initio Simulation Package code48,49. The projector augmented wave method was used to describe the ion-electron interactions50,51. The Perdew–Burke–Ernzerhof functional within the generalized gradient approximation was used to describe the electron exchange–correlation interactions52,53. Metal porphyrins with different metal centers were considered as depicted in Supplementary Fig. S1. The structural model contained 91 atoms and had a size of 15 Å × 15 Å. It was placed in a cubic supercell with lattice parameters of 25 Å × 25 Å × 20 Å to minimize the interaction from periodic images. Only Γ-point was adopted for sampling the Brillouin zone. The kinetic energy cutoff for the plane wave was set to be 520 eV. All the geometries were fully optimized until the maximal components of the force on each atom were converged to less than 3 × 10−2 eV Å−1. Spin-polarization effects were also included throughout the calculations. The calculated electronic energies were converted to free energies by adding zero-point energies and entropic contributions of adsorbates obtained from a harmonic oscillator simulation at 298.15 K. Free-energy corrections for gaseous molecules were summarized in Supplementary Table S4, which were calculated by the ideal gas approximation under the pressure of 101,325 and 3167 Pa for H2 and H2O, respectively.
The structural stability of metal porphyrins was evaluated from its formation energy (Eform) defined as:
where EM-P and EP represent the total energies of metal porphyrins and metal-free porphyrins, respectively, and EM is the energy of metal atom in the bulk phase.
ORR can take place via the four-electron pathway or the two-electron pathway54,55,56. 4e-ORR consists of four reaction steps as shown below:
2e-ORR consists of two reaction steps as shown below:
where * denotes the adsorption site, and *OOH, *O, and *OH denote different adsorbed intermediates. For each step, the Gibbs free energy ΔG under the given potential U relative to RHE was calculated using the following expression:
where ΔE is the total energy difference between the reactant and product during the reaction, and ΔZPE and TΔS are the changes in the zero-point energy and the entropic contribution, respectively.
Preparation of 5,10,15,20-tetrakis(4-methoxycarbonylphenyl)porphyrin (TPPCOOMe)
Six gram of pyrrole and 12 g of methyl p-formylbenzoate were added into 100 mL of propionic acid contained in a 500-mL three-neck flask. The reaction solution was refluxed at 140 °C for 12 h in darkness. After cooling down to room temperature, the solid product was collected via suction-filtration in the form of purple crystals.
Preparation of [5,10,15,20-tetrakis(4-methoxycarbonylphenyl)porphyrinato]-Co(II) (TPPCOOMe-Co), TPPCOOMe-Ni, and TPPCOOMe-Cu
0.854 g of TPPCOOMe and 3.1 g of CoCl2·6H2O were dissolved in 100 mL of DMF and refluxed at 140 °C for 8 h. After cooling back to room temperature, the reaction solution was added with 150 mL of H2O. The resultant precipitate was filtered and washed with H2O twice. It was then re-dissolved in CHCl3, and washed with water for three times. The organic layer was dried over anhydrous MgSO4 and evaporated to yield red powders (TPPCOOMe-Co). TPPCOOMe-Ni and TPPCOOMe-Cu were prepared by replacing CoCl2·6H2O with 3.1 g of NiCl2·6H2O or 2.2 g of CuCl2·2H2O, respectively.
Preparation of [5,10,15,20-tetrakis(4-carboxyphenyl)porphyrinato]-Co(II) (TCPP-Co), TCPP-Ni, TCPP-Cu, and TCPP
0.75 g of as-prepared TPPCOOMe-M (M = Co, Ni, or Cu) was dissolved in 25 mL of tetrahydrofuran (THF) and 25 mL of methanol, and added with 25 mL of 1.88 M KOH aqueous solution. This mixture was refluxed at 85 °C for 12 h. After cooling down to room temperature, THF and methanol were removed via evaporation. The resultant suspension was added with additional water until the complete dissolution of the solid. It was then acidified with 1 M HCl until no further precipitate was detected. The solid product was collected by filtration, washed with water, and dried in a vacuum. Metal-free TCPP was prepared by replacing TPPCOOMe-M with TPPCOOMe.
Preparation of PFC-72-Co, PFC-73-Ni, PFC-73-Cu and PFC-71
Twenty milligrams of TCPP-Co was dissolved in 2 mL of DMF contained in a 15-mL uncapped glass bottle. It was added with 4 mL of TCB, and heated at 100 °C for 3 days. The sample was washed with CH2Cl2 for three times and then soaked in CH2Cl2 for 96 h. The supernatant was replaced by fresh CH2Cl2 several times during the process to exchange and remove nonvolatile solvents (TCB and DMF). Finally, the solid product was collected by vacuum filtration at room temperature, and dried at 100 °C for 8 h. PFC-73-Ni, PFC-73-Cu, and PFC-71 were prepared by replacing TCPP-Co with TCPP-Ni, TCPP-Cu, or TCPP, respectively.
Single-crystal XRD was collected at 100 or 150 K on a Bruker D8 Venture diffractometer using the Mo-Kα radiation (λ = 0.71073 Å). Powder PXRD was carried out on a Rikagu Miniflex 600 Benchtop X-ray diffractometer. FTIR spectra were collected on a VERTEX70 series FTIR spectrometer in the ATR mode. 1H-NMR spectra were recorded on a Bruker AVANCE III 400 MHz NMR spectrometer. Raman spectra were measured on a Horiba Labram HR800 Raman spectrometer under the 633 nm laser excitation. UV-Vis spectra were collected on a Shimadzu UV-2550 spectrophotometer. SEM images were obtained from a Zeiss Ultra 55 scanning electron microscope. TEM imaging was performed using an FEI TALOS-200X scanning/transmission electron microscope under the accelerating voltage of 200 kV. Gas sorption experiments were conducted using a Micrometrics ASAP 2460 analyzer. Co K-edge XAS spectra were collected in the transmission mode at the beamline 1W1B of the Beijing Synchrotron Radiation Facility (BSRF, China).
0.5 mg of PFC-72-Co (or other catalysts) and 2 mg of carbon black (Ketjen Black) were first dispersed in 990 µL of ethanol and 10 µL of 5 wt% Nafion solution, and ultrasonicated for 1 h to form a homogeneous catalyst link. 5 µL of the catalyst ink was then dropcast onto the glassy carbon disk (0.2475 cm2) of a RRDE electrode (catalyst loading ~10 μg cm−2), and dried at room temperature. The loadings for other control catalysts were also ~10 μg cm−2 unless otherwise stated. Electrochemical experiments were carried out in a standard three-electrode system controlled by a CHI 760 bipotentiostat and with the RRDE working electrode, a saturated calomel reference electrode (SCE), and a graphite rod counter electrode. The electrolyte was Ar- or O2-saturated 0.1 M HClO4. All the potential readings were measured against SCE and then converted against RHE. No iR compensation was performed throughout our study. RRDE voltammetry was collected at 10 mV s−1 under 1600 rpm. The H2O2 selectivity was estimated from the oxidation current of the Pt ring (held constant at 1.2 V vs. RHE for the oxidation of H2O2) using the following equation:
where Ir is the ring current, Id is the disk current, and N (~0.33) is the current collection efficiency of the Pt ring calibrated by a standard ferricyanide system.
All data supporting the findings of this study are available from the Source Data. Crystallographic data for the structures reported in this article have been deposited at the Cambridge Crystallographic Data Centre, under deposition numbers CCDC 2107777 (PFC-71), 2107780 (PFC-72-Co), and 2107778 (PFC-73-Cu). Copies of the data can be obtained free of charge via https://www.ccdc.cam.ac.uk/structures/. Source Data are provided with this paper.
The codes developed in this study are available from the authors upon reasonable request.
Campos-Martin, J. M., Blanco-Brieva, G. & Fierro, J. L. G. Hydrogen peroxide synthesis: an outlook beyond the anthraquinone process. Angew. Chem. Int. Ed. Engl. 45, 6962–6984 (2006).
Perry, S. C. et al. Electrochemical synthesis of hydrogen peroxide from water and oxygen. Nat. Rev. Chem. 3, 442–458 (2019).
Yang, S. et al. Toward the decentralized electrochemical production of H2O2: a focus on the catalysis. ACS Catal. 8, 4064–4081 (2018).
Lu, Z. Y. et al. High-efficiency oxygen reduction to hydrogen peroxide catalysed by oxidized carbon materials. Nat. Catal. 1, 156–162 (2018).
Li, L. Q. et al. Tailoring selectivity of electrochemical hydrogen peroxide generation by tunable pyrrolic-nitrogen-carbon. Adv. Energy Mater. 10, 2000789 (2020).
Tang, C. et al. Coordination tunes selectivity: two-electron oxygen reduction on high-loading molybdenum single-atom catalysts. Angew. Chem. Int. Ed. Engl. 59, 9171–9176 (2020).
Pang, Y. Y., Xie, H., Sun, Y., Titirici, M. M. & Chai, G. L. Electrochemical oxygen reduction for H2O2 production: catalysts, pH effects and mechanisms. J. Mater. Chem. A 8, 24996–25016 (2020).
Gao, J. J. et al. Enabling direct H2O2 production in acidic media through rational design of transition metal single atom catalyst. Chem 6, 658–674 (2020).
Siahrostami, S. et al. Enabling direct H2O2 production through rational electrocatalyst design. Nat. Mater. 12, 1137–1143 (2013).
Verdaguer-Casadevall, A. et al. Trends in the electrochemical synthesis of H2O2: enhancing activity and selectivity by electrocatalytic site engineering. Nano Lett. 14, 1603–1608 (2014).
Jirkovsky, J. S. et al. Single atom hot-spots at Au–Pd nanoalloys for electrocatalytic H2O2 production. J. Am. Chem. Soc. 133, 19432–19441 (2011).
Zhao, X., Yang, H., Xu, J., Cheng, T. & Li, Y. G. Bimetallic PdAu nanoframes for electrochemical H2O2 production in acids. ACS Mater. Lett. 3, 996–1002 (2021).
Siahrostami, S. et al. A review on challenges and successes in atomic-scale design of catalysts for electrochemical synthesis of hydrogen peroxide. ACS Catal. 10, 7495–7511 (2020).
Wang, N., Ma, S. B., Zuo, P. J., Duan, J. Z. & Hou, B. R. Recent progress of electrochemical production of hydrogen peroxide by two-electron oxygen reduction reaction. Adv. Sci. 8, 2100076 (2021).
Zhao, X. et al. Selective electrochemical production of hydrogen peroxide at zigzag edges of exfoliated molybdenum telluride nanoflakes. Natl Sci. Rev. 7, 1360–1366 (2020).
Sun, Y. Y. et al. Activity-selectivity trends in the electrochemical production of hydrogen peroxide over single-site metal-nitrogen-carbon catalysts. J. Am. Chem. Soc. 141, 12372–12381 (2019).
Jung, E. et al. Atomic-level tuning of Co-N-C catalyst for high-performance electrochemical H2O2 production. Nat. Mater. 19, 436–442 (2020).
Sheng, H. Y. et al. Stable and selective electrosynthesis of hydrogen peroxide and the electro-Fenton process on CoSe2 polymorph catalysts. Energy Environ. Sci. 13, 4189–4203 (2020).
Tang, C. et al. Tailoring acidic oxygen reduction selectivity on single-atom catalysts via modification of first and second coordination spheres. J. Am. Chem. Soc. 143, 7819–7827 (2021).
Machan, C. W. Advances in the molecular catalysis of dioxygen reduction. ACS Catal. 10, 2640–2655 (2020).
Wang, Y. L., Waterhouse, G. I. N., Shang, L. & Zhang, T. R. Electrocatalytic oxygen reduction to hydrogen peroxide: from homogenous to heterogenous electrocatalysis. Adv. Energy Mater. 11, 2003323 (2021).
Wang, Y. H., Mondal, B. & Stahl, S. S. Molecular cobalt catalysts for O2 reduction to H2O2: Benchmarking catalyst performance via rate-overpotential correlations. ACS Catal. 10, 12031–12039 (2020).
Sorokin, A. B. Phthalocyanine metal complexes in catalysis. Chem. Rev. 113, 8152–8191 (2013).
Brown, C. J., Toste, F. D., Bergman, R. G. & Raymond, K. N. Supramolecular catalysis in metal-ligand cluster hosts. Chem. Rev. 115, 3012–3035 (2015).
Pegis, M. L., Wise, C. F., Martin, D. J. & Mayer, J. M. Oxygen reduction by homogeneous molecular catalysts and electrocatalysts. Chem. Rev. 118, 2340–2391 (2018).
Lv, F. et al. Transition metal macrocycles for heterogeneous electrochemical CO2 reduction. Coord. Chem. Rev. 422, 213435 (2020).
Elouarzaki, K., Kannan, V., Jose, V., Sabharwal, H. S. & Lee, J. M. Recent trends, benchmarking, and challenges of electrochemical reduction of CO2 by molecular catalysts. Adv. Energy Mater. 9, 1900090 (2019).
Dey, S. et al. Molecular electrocatalysts for the oxygen reduction reaction. Nat. Rev. Chem. 1, 0098 (2017).
Smith, P. T., Kim, Y., Benke, B. P., Kim, K. & Chang, C. J. Supramolecular tuning enables selective oxygen reduction catalyzed by cobalt porphyrins for direct electrosynthesis of hydrogen peroxide. Angew. Chem. Int. Ed. Engl. 59, 4902–4907 (2020).
Liu, C. et al. Intrinsic activity of metal centers in metal-nitrogen-carbon single-atom catalysts for hydrogen peroxide synthesis. J. Am. Chem. Soc. 142, 21861–21871 (2020).
Hisaki, I., Xin, C., Takahashi, K. & Nakamura, T. Designing hydrogen-bonded organic frameworks (HOFs) with permanent porosity. Angew. Chem. Int. Ed. Engl. 58, 11160–11170 (2019).
Lin, R. B. et al. Multifunctional porous hydrogen-bonded organic framework materials. Chem. Soc. Rev. 48, 1362–1389 (2019).
Wang, B., Lin, R. B., Zhang, Z. J., Xiang, S. C. & Chen, B. L. Hydrogen-bonded organic frameworks as a tunable platform for functional materials. J. Am. Chem. Soc. 142, 14399–14416 (2020).
Yin, Q. et al. An ultra-robust and crystalline redeemable hydrogen-bonded organic framework for synergistic chemo-photodynamic therapy. Angew. Chem. Int. Ed. Engl. 57, 7691–7696 (2018).
Wu, Y. L. et al. 2D molecular sheets of hydrogen-bonded organic frameworks for ultrastable sodium-ion storage. Adv. Mater. 33, 2106079 (2021).
Colon, Y. J. & Snurr, R. Q. High-throughput computational screening of metal-organic frameworks. Chem. Soc. Rev. 43, 5735–5749 (2014).
Jain, A., Shin, Y. & Persson, K. A. Computational predictions of energy materials using density functional theory. Nat. Rev. Mater. 1, 15004 (2016).
Yin, Q. et al. Metallization-prompted robust porphyrin-based hydrogen-bonded organic frameworks for photocatalytic CO2 reduction. Angew. Chem. Int. Ed. Engl. 61, e202115854 (2022).
Jahan, M., Bao, Q. L. & Loh, K. P. Electrocatalytically active graphene-porphyrin MOF composite for oxygen reduction reaction. J. Am. Chem. Soc. 134, 6707–6713 (2012).
Keum, Y., Park, S., Chen, Y. P. & Park, J. Titanium-carboxylate metal-organic framework based on an unprecedented ti-oxo chain cluster. Angew. Chem. Int. Ed. Engl. 57, 14852–14856 (2018).
Ning, X. M. et al. An efficient strategy for boosting photogenerated charge separation by using porphyrins as interfacial charge mediators. Angew. Chem. Int. Ed. Engl. 58, 16800–16805 (2019).
Han, Y. et al. Two-dimensional flower-like cobalt-porphyrin MOF/rGO composite anodes for high-performance Li-ion batteries. J. Alloy. Compd. 881, 160531 (2021).
Alves, M. C. M., Dodelet, J. P., Guay, D., Ladouceur, M. & Tourillon, G. Origin of the electrocatalytic properties for O2 reduction of some heat-treated polyacrylonitrile and phthalocyanine cobalt compounds adsorbed on carbon black as probed by electrochemistry and X-ray absorption spectroscopy. J. Phys. Chem. 96, 10898–10905 (1992).
Choi, C. H. et al. Tuning selectivity of electrochemical reactions by atomically dispersed platinum catalyst. Nat. Commun. 7, 10922 (2016).
Ledendecker, M. et al. Isolated Pd sites as selective catalysts for electrochemical and direct hydrogen peroxide synthesis. ACS Catal. 10, 5928–5938 (2020).
Zhang, Q. R. et al. Direct insights into the role of epoxy groups on cobalt sites for acidic H2O2 production. Nat. Commun. 11, 4181 (2020).
Li, B. Q., Zhao, C. X., Liu, J. N. & Zhang, Q. Electrosynthesis of hydrogen peroxide synergistically catalyzed by atomic Co-Nx-C sites and oxygen functional groups in noble-metal-free electrocatalysts. Adv. Mater. 31, 1808173 (2019).
Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Furthmuller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Blochl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P. & Wang, Y. Accurate and simple analytic representation of the electron-gas correlation energy. Phys. Rev. B 45, 13244–13249 (1992).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Norskov, J. K. et al. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 108, 17886–17892 (2004).
Viswanathan, V., Hansen, H. A., Rossmeisl, J. & Norskov, J. K. Unifying the 2e- and 4e- reduction of oxygen on metal surfaces. J. Phys. Chem. Lett. 3, 2948–2951 (2012).
Kulkarni, A., Siahrostami, S., Patel, A. & Norskov, J. K. Understanding catalytic activity trends in the oxygen reduction reaction. Chem. Rev. 118, 2302–2312 (2018).
We acknowledge the support from the Ministry of Science and Technology of China (2017YFA0204800 and 2018YFA0208600), the National Natural Science Foundation of China (U2002213, 52161160331, 22071246, and 22005305), the Science and Technology Development Fund Macau SAR (0077/2021/A2), the Collaborative Innovation Center of Suzhou Nano Science and Technology, the 111 Project and Joint International Research Laboratory of Carbon-Based Functional Materials and Devices. The authors thank SSRF (beamline 11B) and BSRF (beamline 1W1B) for the allocation of synchrotron beamtime.
The authors declare no competing interests.
Peer review information
Nature Communications thanks Shizhang Qiao, Pascal Van Der Voort, and the other, anonymous, reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhao, X., Yin, Q., Mao, X. et al. Theory-guided design of hydrogen-bonded cobaltoporphyrin frameworks for highly selective electrochemical H2O2 production in acid. Nat Commun 13, 2721 (2022). https://doi.org/10.1038/s41467-022-30523-0
This article is cited by
Recent Advances of Electrocatalyst and Cell Design for Hydrogen Peroxide Production
Nano-Micro Letters (2023)
Tuning the ratio of Bi/Bi2O3 in Bi/PNC nanosheet for high-efficiency electrosynthesis hydrogen peroxide
Nano Research (2023)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.