Abstract
Adsorption plays vital roles in many processes including catalysis, sensing, and nanomaterials design. However, quantifying molecular adsorption, especially at the nanoscale, is challenging, hindering the exploration of its utilization on nanomaterials that possess heterogeneity across different length scales. Here we map the adsorption of nonfluorescent small molecule/ion and polymer ligands on gold nanoparticles of various morphologies in situ under ambient solution conditions, in which these ligands are critical for the particles’ physiochemical properties. We differentiate at nanometer resolution their adsorption affinities among different sites on the same nanoparticle and uncover positive/negative adsorption cooperativity, both essential for understanding adsorbate-surface interactions. Considering the surface density of adsorbed ligands, we further discover crossover behaviors of ligand adsorption between different particle facets, leading to a strategy and its implementation in facet-controlled synthesis of colloidal metal nanoparticles by merely tuning the concentration of a single ligand.
Similar content being viewed by others
Introduction
Adsorption plays vital roles in many processes in daily life, research, and industry applications, e.g., in purification, separation, or decontamination via differentiated adsorption affinities or kinetics; in catalysis for reactant activation or catalyst poisoning; and in sensing via adsorption-induced physicochemical changes1,2,3,4,5,6. On nanoparticles, adsorption of molecules can stabilize their solution dispersion, control their morphology during synthesis, enhance their surface functionality, or limit their catalytic performance3,4,5,6. To improve these applications or explore new ones, it is essential to understand quantitatively the adsorption behaviors of molecules on surfaces. However, many aspects make it challenging, including the differentiation between adsorbed and free molecules, the often-miniature amounts of adsorbates, the interference from solvents, and the inhomogeneities of the adsorbent surfaces across different length scales. For adsorption on nanoparticles, their small sizes, multiplicity of surface facets, and intrinsic heterogeneity present further challenges, for which high-resolution, high-sensitivity, and quantitative measurements are needed7,8,9, whereas traditional bulk measurements average over many particles, masking adsorption differences at single-particle or subparticle level10. Here, using COMPEITS (COMPetition-Enabled Imaging Technique with Super-resolution) that is capable of imaging nonfluorescent surface processes in situ and at nanometer resolution11, we map the adsorption of small molecule/ion and polymer ligands on individual gold (Au) nanoparticles of various morphologies under ambient solution conditions (Fig. 1a). These ligands play critical roles in the shape-controlled synthesis, solution stabilization, surface functionalization, and catalytic poisoning of nanoparticles of various compositions3,4,5,6,12. We quantify their adsorption affinity and uncover positive/negative adsorption cooperativity, both of which can even differ among different sites on the same nanoparticle. We further discover crossover behaviors of ligand adsorption between different nanoparticle facets, leading to a strategy and its implementation in facet-tuned synthesis of colloidal metal nanoparticles.
COMPEITS11 is based on competitive adsorption that suppresses the rate of a surface-catalyzed fluorogenic auxiliary reaction, whose products are imaged, counted, and localized with nanometer precision via single-molecule fluorescence microscopy13,14,15 (Fig. 1a, Supplementary Information section 1.7). COMPEITS not only has super-optical resolution (down to ~10 nm; Supplementary Information section 3.1 and Supplementary Fig. 10b) but also probes specifically the first-layer surface adsorption of the competitor because multi-layer adsorption provides no further suppression of the auxiliary reaction rate. We used the catalytic reduction of resazurin (R) by NH2OH to fluorescent resorufin in aqueous solutions as the auxiliary reaction (Supplementary Fig. 3a), which follows the Langmuir–Hinshelwood mechanism on Au particle surfaces14. In the presence of excess NH2OH and a competing ligand (L), the (specific) reaction rate (vR) of the auxiliary reaction follows (Eq. S11):
Here kR is a (specific) rate constant; KR and KL are the adsorption equilibrium constants of R and L, respectively; and h = 1 when L follows Langmuir adsorption. If L adsorption is cooperative, h deviates from 1 and is the Hill coefficient of cooperativity: h > 1 for positive cooperativity; h < 1 for negative cooperativity16,17.
Results
Cooperative ligand adsorption on single nanoparticles
We chose to study Au nanoparticles for their wide applications as catalysts or probes and for their availability in variable sizes and shapes18,19,20. We first examined the adsorption of cetyltrimethylammonium bromide (CTAB), a ligand widely used in Au nanoparticle synthesis and surface modification5,18, on pseudospherical 5-nm Au nanoparticles using COMPEITS. The fluorogenic reaction rate vR on a single nanoparticle decreases with increasing [CTAB] (up to 5 μM, below CTAB’s critical micelle concentration of 0.96 mM at 25 °C21) (Fig. 1b), confirming CTAB’s competition with resazurin adsorption on the nanoparticle. Control experiments show that this decrease is not due to catalyst deactivation (Supplementary Information section 3.3) nor to displacement of the excess co-reactant NH2OH (Supplementary Fig. 9m). Equation (1) satisfactorily fits the vR-vs-[CTAB] titration, giving KCTAB = 0.80 ± 0.03 μM−1 for this nanoparticle (Fig. 1b, red line). (kR and KR were determined in earlier titration of [R] on the same nanoparticle without CTAB; Supplementary Fig. 10k). Strikingly, the extracted Hill coefficient hCTAB is 2.2 ± 0.1 (Fig. 1e), significantly greater than 1, indicating positive cooperativity in the first-layer CTAB adsorption on the particle surface, whereas forcing hCTAB = 1 cannot fit the data (Fig. 1b, blue line). This cooperativity is also apparent in the linear Hill plot of the data, with the slope being hCTAB ~2.2 (Fig. 1b, inset), reflecting that ~2 CTAB molecules adsorb concurrently. This positive adsorption cooperativity, important for high adsorption efficacy1,6,22 and revealed here on nanoparticles, possibly stems from attractive hydrophobic interactions between the alkyl chains of CTA+, as in self-assembled monolayers23 (Br− contribution is small; see later).
To achieve statistical significance, we studied 50 nanoparticles. On average, KCTAB ~0.65 μM−1; more important, they all show positive cooperativity (gray points, Fig. 1b), with the Hill coefficient hCTAB ~2.0 (Fig. 1e); and the particle-averaged behavior agrees with bulk measurements (Supplementary Fig. 9a). Notably, with increasing KCTAB, hCTAB of individual particles approaches 1 (Fig. 1i), consistent with that stronger adsorbate–surface interactions should lead to weaker adsorbate–adsorbate interactions1 and thus weaker cooperativity. We further studied cetyltrimethylammonium hydroxide (CTAOH) and cetyltrimethylammonium chloride (CTAC) to test the generality of positive adsorption cooperativity. Their adsorptions on 5-nm nanoparticles follow KCTAB < KCTAOH < KCTAC in affinity and they both show positive cooperativity (h > 1) like CTAB (Fig. 1f; Supplementary Information section 3.4).
We next studied the adsorption on 5-nm Au nanoparticles of poly-N-vinylpyrrolidone (PVP). Compared with CTAB/CTAOH/CTAC, PVP is a polymer with a much larger molecular weight, more flexible in molecular conformation, and also commonly used in shape-controlled nanoparticle synthesis24. For PVP55k (average molecular weight ~55k g/mol), its competitive adsorption is clear in single-particle reaction rate titrations (Fig. 1c). On average, KPVP55k = 2.4 ± 0.3 nM−1 (Fig. 1e). More strikingly, its Hill coefficient hPVP55k = 0.75 ± 0.09 (Fig. 1e), clearly smaller than 1, demonstrating PVP55k’s negative adsorption cooperativity, unseen previously for synthetic polymers and particularly on nanoparticles. This negative cooperativity possibly stems from direct electrostatic repulsions between positively charged PVP chains at pH ~7.4 (N-alkylpyrrolidone has a pKb of ~3.5)25 or from that hydrophilic PVP chains prefer interactions with water than with themselves24. Among 36 nanoparticles, with increasing KPVP55k, hPVP55k approaches 1 (Fig. 1j), corroborating that stronger adsorbate–surface interactions are associated with weaker cooperativity. Moreover, PVP’s adsorption affinity decreases with smaller molecular weight (Fig. 1g), suggesting its multivalency-enhanced adsorption, whereas its Hill coefficient stays at ~0.7, suggesting that their inter-chain interactions are dominated by sub-chain structures, like thermal blobs, which are similar regardless of molecular weights26.
Considering CTA+ and PVP being relatively large, we hypothesized that small ligands might not show cooperative adsorption because they are less likely to feel each other on surfaces. We chose halides (I− and Br−) and a small thiol β-mercaptoethanol (BME) as representatives for their wide applications in nanoparticle chemistry (e.g., in surface functionalization and self-assembled monolayers)3,23. Indeed, COMPEITS titrations on single 5-nm Au nanoparticles give h = 1 for all three, indicating no adsorption cooperativity (Fig. 1d and Supplementary Fig. 12g–i), besides their adsorption affinities (Fig. 1h). We note KBr− is only ∼0.2% of KCTAB, confirming that CTAB adsorption is dominated by its CTA+ cation. The counter-cation K+ for I− and Br− has insignificant adsorption (Supplementary Information section 2). The noncooperative adsorption of BME is consistent with bulk measurements of 4-aminothiolphenol adsorption on pseudospherical Au nanoparticles17; notably, when these particles were roughened to create highly concave surfaces, positive cooperativity of 4-aminothiolphenol adsorption (h ~2) emerged concurrently with >101 times weaker affinity17, consistent with our observation that weaker adsorbate–surface interactions can lead to stronger adsorbate–adsorbate interactions.
Sub-particle/facet variations of adsorption affinity and cooperativity
The tens-of-nanometer spatial resolution of COMPEITS enabled examining sub-particle-level ligand adsorption behaviors on larger, anisotropically shaped particles like triangular/hexagonal Au nanoplates, which are inaccessible to bulk measurements. These nanoplates are micrometers wide and ~14 nm thick, with {111} flat facets and {110} side facets (Supplementary Fig. 2a)27, offering an effective platform for studying facet-dependent molecular adsorption behaviors. We further coated them with mesoporous silica (Fig. 2d and Supplementary Fig. 1a–f) to stabilize them upon removing their capping ligands that remained from the synthesis, and to prepare them for ligand adsorption studies (Supplementary Information section 1.2.3).
We first mapped CTAB adsorption as a representative for positive cooperativity. The COMPEITS image, which is the inverse difference Δ(n−1) between the super-resolution images of the fluorogenic auxiliary reaction in the absence and presence of CTAB (Eq. S13), directly resolves adsorption differences at the corner (c), edge (e), and flat-facet (f) regions on any nanoplate in correlation with its SEM image (Fig. 2a–d, and Supplementary Information section 1.8.4). Titrations of vR-vs-[CTAB] gave the respective adsorption equilibrium constant K and Hill coefficient h of each region on each of 55 nanoplates. They show clear site-dependent CTAB adsorption affinity, with Kc > Ke > Kf (Fig. 2e), which we attribute to that CTAB binds on Au{110} more strongly than on Au{111} (i.e., \({K}_{{\rm{CTAB}}}^{\{110\}} > {K}_{{\rm{CTAB}}}^{\{111\}}\)) and that corner regions have a higher {110} portion than edge regions (see Supplementary Information section 5.5 on discussions of under-coordinated atom contributions). This trend is consistent with that EELS imaging detected more adsorbed CTAB on Au{110} than Au{111}20—it is worth noting that the adsorbed amount does not necessarily report affinity (see later) and EELS is an ex situ measurement. More important, the cooperativity follows 1 < hc < he < hf (Fig. 2e), reflecting a facet-dependent cooperativity (i.e., 1 < \({h}_{{\rm{CTAB}}}^{\{110\}} < {h}_{{\rm{CTAB}}}^{\{111\}}\)), here within a single particle. Again, h is anti-correlated with K as earlier (Fig. 2e; same for individual nanoplates, Fig. 2h).
We note that the mesoporous silica shell here does not render the cooperativity, nor should it bias the trends of cooperativity across different regions because of the following: (1) Cooperativity is observed directly on uncoated 5-nm nanoparticles (Fig. 1). (2) All h values here suggest cooperative adsorption of two CTAB molecules (the width of a stretched CTA+ is below 1 nm and its length is ~2 nm28,29), which are smaller than the pores of the shell (~3.5 nm on average30). (3) The anti-correlation between K and h for CTAB adsorption is persistently observed in the absence (i.e., 5-nm nanoparticles) or presence (i.e., nanoplates here and nanorods later) of the shell. (4) The Au{111} facet shows stronger cooperativity than the Au{110} facet, regardless of whether the {111} facet is located dominantly at low curvature regions (i.e., the top flat facet of nanoplates) or high curvature regions (i.e., at the tips of nanorods; later) of the particle. (See more discussion on the insignificant role of the shell in cooperativity in Supplementary Information section 1.2.3).
The nanoplate’s large flat {111} facet further allowed for dissecting it into three radial segments: inner (i), middle (m), and outer (o) (Fig. 2d). We previously established that on the flat {111} facet, the structural defects decrease in density from the center toward the periphery because of their seeded growth mechanism31. The determined CTAB affinity follows this trend of defect densities (Fig. 2e), attributable to CTAB’s preferred binding to structural defects. Interestingly, hi > hm > ho, an observation of sub-facet cooperativity differences, is positively correlated with the affinity trend of Ki > Km > Ko, opposite to that among the corner, edge, and facet regions (Fig. 2e). Here, we attribute that the inner segment has a higher defect density (the underlying reason of larger K), and consequently a higher density and shorter inter-distances of adsorbed CTAB; this shorter inter-distances should render more adsorbate–adsorbate interactions, dominating over the adsorbate–surface interactions within the same facet, and thus overall stronger cooperativity.
We then studied PVP55k on nanoplates as a representative for negative cooperativity. At the sub-particle level, Kc > Ke > Kf (Fig. 2f), indicating PVP’s preferred binding to Au{110} than Au{111} (i.e., \({K}_{{\rm{PVP}}}^{\{110\}} > {K}_{{\rm{PVP}}}^{\{111\}}\)), similar to CTAB; this trend is also consistent with that ex situ NanoSIMS imaging detected more adsorbed PVP on {110}19, although the adsorbed amount does not reliably reflect affinity. Concurrently, 1 > hc > he > hf (Fig. 2f), showing less cooperativity with stronger binding facets as earlier (also Fig. 2i), i.e., 1 > \({h}_{{\rm{PVP}}}^{\{110\}} > {h}_{{\rm{PVP}}}^{\{111\}}\). At the sub-facet level within {111}, PVP displays the same variations in affinity and cooperativity as CTAB, with Ki > Km > Ko and hi < hm < ho < 1 (Fig. 2f). PVP10k shows identical trends (Supplementary Fig. 15g).
As comparisons, we studied I−, Br−, and BME that show no adsorption cooperativity. For I−, Kc < Ke < Kf (Fig. 2g), opposite to CTAB and PVP, likely because iodide prefers the coordination geometry on Au{111} than on Au{110} (i.e., \({K}_{{I}^{-}}^{\{110\}} < {K}_{{I}^{-}}^{\{111\}}\)). This result is supported by calculations32 and agrees with NanoSIMS measurements19. Its sub-facet variation of K within {111} is like CTAB and PVP (Fig. 2g). Br− shows the same trends as I− (Supplementary Fig. 15h). In contrast, BME shows non-differentiating adsorption: Kc = Ke = Kf, and Ki = Km = Ko (Fig. 2g). This structural insensitivity of BME adsorption likely stems in part from its exceptionally strong affinity toward Au and underlies the wide-spread usage of thiols in stabilizing pseudospherical nanoparticles33 and in surface-functionalizing particles non-discriminatingly30.
Compared with nanoplates, penta-twinned Au nanorods also feature an anisotropic morphology but possess complementary facets, with the larger side facets and two tips covered by {110} and {111} facets, respectively34 (Supplementary Information section 1.3 and 1.4 and Supplementary Fig. 2b). We studied penta-twinned Au nanorods of ~1000 nm in length and ~35 nm in diameter35, also coated with mesoporous silica (~40 nm thick; Supplementary Fig. 1g–k), for adsorbing molecules with distinctive cooperativities. COMPEITS imaging in correlation with SEM directly resolves differences in adsorption behavior at the two tip regions (T) vs. the side facets (S) (Fig. 3a–c and Supplementary Fig. 7c). Titration analysis gave K and h values at respective regions of each nanorod: KT < KS for CTAB and PVP (Fig. 3d, e) and KT > KS for I− and Br− (Fig. 3f), consistent with and further corroborating our earlier attribution that K{110} > K{111} for CTAB/PVP and opposite for I−/Br−19,20. Consistently, for CTAB and PVP, stronger binding leads to weaker cooperativity between different facets both on average (Fig. 3d, e) and at the single-particle level (Fig. 3g, h).
To study the sub-facet dependence on single nanorods, we further dissected the {110} sides into inner (I), middle (M), and outer (O) regions from the center toward the tips (Fig. 3b and Supplementary Fig. 7c). We previously established that on the side facets of these nanorods, surface defect densities decrease from the center toward the two tips resulting from their seeded-growth synthesis36. For CTAB, PVP, and I− and Br−, we observed KI > KM > KO (Fig. 3d–f), likely dictated by the decreasing defect density away from the center. Within the {110} side facets, h becomes closer to 1 and thus less cooperative with increasing K (Fig. 3d, e), similar to the trend observed within the {111} flat facets of nanoplates. These consistent results further corroborate our attribution that the defect density gradient underlies the differences in affinity and cooperativity within the same facet on a single particle, regardless of the underlying facet being {111} for nanoplate’s flat facets or {110} for nanorod’s side facets.
Crossover behavior of ligand adsorption between different facets
Provided the adsorption affinity and cooperativity, one can determine the density of adsorbed ligands (ρ) on any facet at any [L]:
where ρmax is the ligand’s maximal packing density on the facet. ρ is a measure of a facet’s stabilization by ligand adsorption and of its accessibility to other reagents. Larger ρ is often presumed to reflect stronger adsorption affinity on a facet5,19,20. However, even for Langmuir adsorption (i.e., non-cooperative with h = 1), the density of adsorbed ligands (ρstrong) on a stronger-binding facet (Kstrong) vs. that (ρweak) on a weaker-binding facet (Kweak) can have complex behaviors. Only when \({{\rho }}_{{\max }}^{\text{strong}}{\rm{\ge }}{{\rho }}_{{\max }}^{\text{weak}}\), the presumption is valid and ρstrong ≥ ρweak at any [L] (Fig. 4a, b). But, when \({{\rho }}_{{\max }}^{\text{strong}}\, < \,{{\rho }}_{{\max }}^{\text{weak}}\), the two ρ-vs-[L] curves cross over at a critical ligand concentration (cx) (Supplementary Eq. S23), defining two distinct regimes (Fig. 4c): at [L] < cx, ρstrong > ρweak because the adsorption affinity plays a dominant role; at [L] > cx, ρstrong < ρweak because ρmax limits the amount of adsorbates. This crossover behavior stems from the interplay between multiple factors (e.g., adsorption affinity, density, and/or cooperativity) that determine the overall molecular adsorption properties. This behavior also predicts that the relative stabilization and accessibility of various facets on a nanoparticle can markedly change depending on the ligand concentration, which has many possible applications in materials design, surface modification, and catalysis (Supplementary Information section 6.6).
One possible application of this crossover behavior would be facet control in colloidal nanoparticle synthesis—one could shift the dominance between different facets by simply tuning the concentration of a single ligand. We therefore proceeded to synthesize colloidal Au nanoparticles in the presence of increasing [CTAB], via reduction of HAuCl4 by ascorbic acid (AA) in aqueous solutions in one pot, where [HAuCl4] and [AA] were fixed and their adsorptions on the nanoparticle are insignificant comparatively (Supplementary Information section 1.9 and 6.1–6.2). We chose CTAB because it is redox-inert and a facet-directing stabilizer for Au nanoparticle synthesis4, whereas PVP is oxidizable24 and halides are ineffective stabilizers3. As \({K}_{{\rm{CTAB}}}^{\{110\}} > {K}_{{\rm{CTAB}}}^{\{111\}}\) and if the crossover behavior applies here \(({\rm{i}}.{\rm{e}}{., \,}{{\rho}}_{{\rm{max }}}^{\{110\}}{ < }{{\rho}}_{{\rm{max }}}^{\{111\}})\), one predicts that Au{110} would be the prevalent facet at low [CTAB] whereas Au{111} would dominate at high [CTAB] (Fig. 4c). Excitingly, when [CTAB] increases from ~0.2 to ~3 mM (below CTAB’s critical micelle concentration at the synthesis temperature of 85 °C; Supplementary Information section 6.3)21,37, the synthesized nanoparticles indeed show a shape progression: initially irregular in shape, then a mixture of irregular-shaped nanoparticles and hexagonal nanoplates, and eventually high-purity nanoplates (Fig. 4d–i). The prevalence of {111}-dominated nanoplates at high [CTAB] directly supports the existence of crossover behavior of CTAB adsorption on Au nanoparticle surfaces.
To quantify facet distributions on these samples, we performed electrochemical Pb underpotential deposition, whose deposition potentials on Au{111} and Au{110} are resolvable in cyclic voltammetry (CV) at ~0.38 and ~0.53 V vs. RHE, respectively38. Indeed, the {110} deposition peak in CV gradually diminishes while the {111} peak grows across the set of Au nanoparticles synthesized at increasing [CTAB] (Fig. 4d–i). Consistently, the corresponding two facet-fraction-vs.-[CTAB] curves intersect at ~2 mM CTAB (Fig. 4j), below which {110} dominates and above which {111} dominates. This intersection verifies CTAB’s crossover adsorption behavior and its ability in controlling facet distributions.
Discussion
Understanding molecular adsorption quantitatively, especially at the nanoscale, is of great significance owing to its decisive role in determining the efficacy of processes such as in materials control, catalysis, and separation. The high-resolution, quantitative knowledge from nanoscale imaging offers not only molecular insights (e.g., adsorption cooperativity and crossover) but also control parameters for facet-controlled syntheses of colloidal nanoparticles. One could also envision a myriad of other potential applications, e.g., in nanoparticle surface carving via selective etching, ligand-induced galvanic replacement in generating hollow nanostructures, facet-selective deposition on solid particles, tunable surface functionalization, catalysis selectivity control, and catalyst poisoning mitigation (see discussions in Supplementary Information section 6.6). For all of these, we believe that the approaches untaken and the molecular insights gained here should open windows into uncharted scientific territories.
Methods
Bulk measurements of resazurin reduction and ligand adsorption competition on Au nanoparticles
Bulk experiments were performed based on the titration of catalytic activities of Au nanoparticles in the absence (and then presence) of ligands. Specifically, pseudo-spherical colloidal Au nanoparticles, 5 nm in diameter nominally (Ted Pella 15702-20), were used to catalyze the reduction of resazurin (R) to resorufin by NH2OH, which was provided in excess (Supplementary Fig. 3a), and monitored by UV–Vis absorption spectrometry. Typically, 100 μL of the 5-nm Au suspension (0.010–0.10 nM based on the number of particles) was added to a premixed 7 mM phosphate butter solution (pH = 7.4) containing different amounts of R (1.0–10 µM) and an excess amount of NH2OH (1 mM). The reaction mixture turned gradually from blue to red, and the absorption peak at 602 nm (R) decreased while the absorption peak at 572 nm (resorufin) increased (Supplementary Fig. 3b). For the COMPEITS experiments, the reaction conditions were kept the same except that [R] was fixed while ligands with increasing concentrations were added into the reaction mixtures. The ligand concentration ranges from nM to mM depending on the ligand adsorption affinity. Typically, at least 3 concentrations of R and 4 concentrations of ligands are included for the extraction of ligand adsorption affinity and cooperativity.
Syntheses and characterization of mesoporous-silica-coated Au nanoplates and nanorods
Au nanoplates were synthesized following a procedure modified from previous reports31,39 (Supplementary Information section 1.2.1). Penta-twinned Au nanorods were synthesized in a three-step seed-mediated growth method following the literature35 (Supplementary Information section 1.3.1). The as-synthesized Au nanoplates and nanorods were coated with mesoporous silica in three major steps as previously reported30,31,36,40,41 (Supplementary Information section 1.2.2). The morphology and shape yield of the mSiO2-coated nanoplates and nanorods were examined by both TEM and SEM.
Electrochemical underpotential deposition of Pb on Au nanoparticles for facet determination
The underpotential deposition (UPD) of Pb on Au nanoparticles were carried out in a three-electrode cell using an electrochemical workstation (CHI 1200a potentiostat) following literature38,42. A Ag/AgCl electrode and a Pt wire served as the reference and counter electrodes, respectively. The as-synthesized Au nanoparticles with various morphologies were drop-casted on a glassy-carbon electrode and used as the working electrode. Before the cyclic voltammetry (CV) measurements, each sample was first subjected to potential cycling from ‒0.2 to ‒0.7 V (vs. Ag/AgCl) at a scan rate of 100 mV s‒1 until the voltammograms were stable. Afterward, three cycles of CV curves were recorded in potentials ranging from ‒0.2 to ‒0.7 V at a scan rate of 50 mV s‒1 in a mixture containing 0.1 M NaOH and 1 mM Pb(NO3)2 at ambient conditions. The third cycle of the CV curves was used to calculate the areas of deposition peaks of various facets for quantitative comparisons38,42. The charge values associated with the deposition of a monolayer of Pb are 444 and 330 μC cm−2 for Au{111} and Au{110} facets, respectively. The potentials involved in this work were derived in reference to E(Ag/AgCl) and presented as in reference to E(RHE) in the main text, where RHE denotes the reversible hydrogen electrode, according to the formula E(RHE) = E(Ag/AgCl) + 0.1976 + 0.05916 × pH. The deposition and stripping of Pb on Au{111} and Au{110} show as two pairs of distinctive reduction–oxidation peaks at 0.38 and 0.45 V and 0.53 and 0.67 V, respectively, as reported by Wuttig et al.38.
COMPEITS imaging experiments and data analysis
All single-molecule fluorescence microscopy experiments for COMPEITS imaging were carried out on a home-built prism-type wide-field total internal reflection fluorescence (TIRF) microscope (Supplementary Information section 1.7).
Information of single-molecule catalysis was extracted using a home-written MATLAB program from the fluorescence images in the movies, ‘subtraction iQPALM’ (image-based quantitative photo-activated localization microscopy, see Supplementary Software 1), which was expanded from iqPALM43,44 and whose major steps of data analysis were described and employed in our previous work11. See more details in Supplementary Information section 1.8.
Facet-controlled synthesis of colloidal Au nanoparticles using CTAB as the ligand
Au nanoparticles were synthesized via reduction of HAuCl4 by AA in the presence of various [CTAB] in aqueous solution, modified from an earlier protocol45. In a typical synthesis, 42 μL of 10 mM aqueous HAuCl4 solution was added into 716 μL of CTAB aqueous solution in a plastic tube. The mixture was shaken by hand for a few times before leaving undisturbed. After 15 min, 42 μL of 10 mM aqueous AA solution was added into the tube in one shot, followed by rapid inversion for 10 times. The concentration of CTAB in the final mixture ranges from 0.26 to 3.12 mM. The tube was then placed in a water bath at 85 °C for 1 h. The products were collected via centrifugation, washed with a mixture of DI water and ethanol (1:1 v/v) followed by centrifugation at 100 g for three times, and then re-dispersed in DI water for further characterizations.
Data and materials availability
All data are available in the main text or the supplementary materials. Raw data supporting the findings of this study and home-synthesized Au particles are available upon reasonable request.
Code availability
MATLAB codes are included in the Supplementary Software 1.
References
Somorjai, G. A. & Li, Y. Introduction to Surface Chemistry and Catalysis (John Wiley & Sons, 2010).
Singh, N. et al. Quantifying adsorption of organic molecules on platinum in aqueous phase by hydrogen site blocking and in situ X-ray absorption spectroscopy. ACS Catal. 9, 6869–6881 (2019).
Ghosh, S. & Manna, L. The many “facets” of halide ions in the chemistry of colloidal inorganic nanocrystals. Chem. Rev. 118, 7804–7864 (2018).
Yang, T.-H., Shi, Y., Janssen, A. & Xia, Y. Surface capping agents and their roles in shape-controlled synthesis of colloidal metal nanocrystals. Angew. Chem. Int. Ed. 59, 15378–15401 (2020).
Lohse, S. E., Burrows, N. D., Scarabelli, L., Liz-Marzán, L. M. & Murphy, C. J. Anisotropic noble metal nanocrystal growth: the role of halides. Chem. Mater. 26, 34–43 (2014).
Reed, D. A. et al. A spin transition mechanism for cooperative adsorption in metal–organic frameworks. Nature 550, 96–100 (2017).
Delen, G., Monai, M., Meirer, F. & Weckhuysen, B. M. In situ nanoscale Infrared spectroscopy of water adsorption on nano-islands of surface-anchored metal-organic frameworks. Angew. Chem. Int. Ed. https://doi.org/10.1002/anie.202011564 (2020).
Wu, C.-Y. et al. High-spatial-resolution mapping of catalytic reactions on single particles. Nature 541, 511–515 (2017).
Heylman, K. D. et al. Optical microresonators as single-particle absorption spectrometers. Nat. Photonics 10, 788–795 (2016).
Chen, Z., Chang, J. W., Balasanthiran, C., Milner, S. T. & Rioux, R. M. Anisotropic growth of silver nanoparticles is kinetically controlled by polyvinylpyrrolidone binding. J. Am. Chem. Soc. 141, 4328–4337 (2019).
Mao, X., Liu, C., Hesari, M., Zou, N. & Chen, P. Super-resolution imaging of non-fluorescent reactions via competition. Nat. Chem. 11, 687–694 (2019).
Chen, Y., Xianyu, Y. & Jiang, X. Surface modification of gold nanoparticles with small molecules for biochemical analysis. Acc. Chem. Res. 50, 310–319 (2017).
Roeffaers, M. B. J. et al. Spatially resolved observation of crystal-face-dependent catalysis by single turnover counting. Nature 439, 572–575 (2006).
Xu, W., Kong, J. S., Yeh, Y.-T. E. & Chen, P. Single-molecule nanocatalysis reveals heterogeneous reaction pathways and catalytic dynamics. Nat. Mater. 7, 992–996 (2008).
Naito, K., Tachikawa, T., Fujitsuka, M. & Majima, T. Real-time single-molecule imaging of the spatial and temporal distribution of reactive oxygen species with fluorescent probes: applications to TiO2 photocatalysts. J. Phys. Chem. C. 112, 1048–1059 (2008).
Hill, A. V. The possible effects of the aggregation of the molecules of haemoglobin on its dissociation curves. J. Physiol. 40, 4–7 (1910).
Villarreal, E., Li, G. G., Zhang, Q., Fu, X. & Wang, H. Nanoscale surface curvature effects on ligand–nanoparticle interactions: a plasmon-enhanced spectroscopic study of thiolated ligand adsorption, desorption, and exchange on gold nanoparticles. Nano Lett. 17, 4443–4452 (2017).
Langille, M. R., Personick, M. L., Zhang, J. & Mirkin, C. A. Defining rules for the shape evolution of gold nanoparticles. J. Am. Chem. Soc. 134, 14542–14554 (2012).
Zhai, Y. et al. Polyvinylpyrrolidone-induced anisotropic growth of gold nanoprisms in plasmon-driven synthesis. Nat. Mater. 15, 889–895 (2016).
Janicek, B. E. et al. Quantitative imaging of organic ligand density on anisotropic inorganic nanocrystals. Nano Lett. 19, 6308–6314 (2019).
Okuda, H., Imae, T. & Ikeda, S. The adsorption of cetyltrimethylammonium bromide on aqueous surfaces of sodium bromide solutions. Colloids Surf. 27, 187–200 (1987).
Kim, E. J. et al. Cooperative carbon capture and steam regeneration with tetraamine-appended metal–organic frameworks. Science 369, 392–396 (2020).
Love, J. C., Estroff, L. A., Kriebel, J. K., Nuzzo, R. G. & Whitesides, G. M. Self-assembled monolayers of thiolates on metals as a form of nanotechnology. Chem. Rev. 105, 1103–1170 (2005).
Koczkur, K. M., Mourdikoudis, S., Polavarapu, L. & Skrabalak, S. E. Polyvinylpyrrolidone (PVP) in nanoparticle synthesis. Dalton Trans. 44, 17883–17905 (2015).
Lide David, R. CRC Handbook of Chemistry and Physics (CRC Press, 2005).
Rubinstein, M. & Colby, R. H. in Polymer Physics (Oxford University Press, 2021).
Grzelczak, M., Pérez-Juste, J., Mulvaney, P. & Liz-Marzán, L. M. Shape control in gold nanoparticle synthesis. Chem. Soc. Rev. 37, 1783–1791 (2008).
Gómez-Graña, S. et al. Surfactant (bi)layers on gold nanorods. Langmuir 28, 1453–1459 (2012).
Sau, T. K. & Murphy, C. J. Self-assembly patterns formed upon solvent evaporation of aqueous cetyltrimethylammonium bromide-coated gold nanoparticles of various shapes. Langmuir 21, 2923–2929 (2005).
Botella, P., Corma, A. & Navarro, M. T. Single gold nanoparticles encapsulated in monodispersed regular spheres of mesostructured silica produced by pseudomorphic transformation. Chem. Mater. 19, 1979–1983 (2007).
Andoy, N. M. et al. Single-molecule catalysis mapping quantifies site-specific activity and uncovers radial activity gradient on single 2D nanocrystals. J. Am. Chem. Soc. 135, 1845–1852 (2013).
Almora-Barrios, N., Novell-Leruth, G., Whiting, P., Liz-Marzán, L. M. & López, N. Theoretical description of the role of halides, silver, and surfactants on the structure of gold nanorods. Nano Lett. 14, 871–875 (2014).
Brust, M., Walker, M., Bethell, D., Schiffrin, D. J. & Whyman, R. Synthesis of thiol-derivatised gold nanoparticles in a two-phase liquid–liquid system. J. Chem. Soc. Chem. Commun. 801–802 (1994).
Gai, P. L. & Harmer, M. A. Surface atomic defect structures and growth of gold nanorods. Nano Lett. 2, 771–774 (2002).
Scarabelli, L., Sánchez-Iglesias, A., Pérez-Juste, J. & Liz-Marzán, L. M. A “Tips and Tricks” practical guide to the synthesis of gold nanorods. J. Phys. Chem. Lett. 6, 4270–4279 (2015).
Zhou, X. et al. Quantitative super-resolution imaging uncovers reactivity patterns on single nanocatalysts. Nat. Nanotechnol. 7, 237–241 (2012).
Cookey, G. A. & Obunwo, C. C. Effects of sodium bromide salt and temperature on the behaviour of aqueous solution of cetyltrimethylammonium bromide. IOSR J. Appl. Chem. 7, 34–38 (2014).
Wuttig, A., Yaguchi, M., Motobayashi, K., Osawa, M. & Surendranath, Y. Inhibited proton transfer enhances Au-catalyzed CO2-to-fuels selectivity. Proc. Natl Acad. Sci. U.S.A. 113, E4585–E4593 (2016).
Shankar, S. S. et al. Biological synthesis of triangular gold nanoprisms. Nat. Mater. 3, 482–488 (2004).
Stöber, W., Fink, A. & Bohn, E. Controlled growth of monodisperse silica spheres in the micron size range. J. Colloid Interface Sci. 26, 62–69 (1968).
Liz-Marzán, L. M., Giersig, M. & Mulvaney, P. Synthesis of nanosized gold−silica core−shell particles. Langmuir 12, 4329–4335 (1996).
Herrero, E., Buller, L. J. & Abruña, H. D. Underpotential deposition at single crystal surfaces of Au, Pt, Ag and other materials. Chem. Rev. 101, 1897–1930 (2001).
Chen, P. & Chen, T.-Y. MATLAB code package: iQPALM (image-based quantitative photo-activated localization microscopy). https://doi.org/10.6084/m9.figshare.12642617.v1 (2020).
Chen, T.-Y. et al. Concentration- and chromosome-organization-dependent regulator unbinding from DNA for transcription regulation in living cells. Nat. Commun. 6, 7445 (2015).
Chen, S. et al. Rapid seedless synthesis of gold nanoplates with microscaled edge length in a high yield and their application in SERS. Nanomicro. Lett. 8, 328–335 (2016).
Acknowledgements
We thank M. Hesari for helping with imaging and C. Liu for discussions. The research is primarily supported by the Army Research Office (grant no. W911NF-17-1-0590). The study on halides is supported by the Center for Alkaline-based Energy Solutions (CABES), an Energy Frontier Research Center of U.S. Department of Energy under Award DE-SC0019445. The research used Cornell Center for Materials Research Shared Facilities supported by NSF (grant no. DMR-1719875). R.Y. thanks Cornell Presidential Postdoctoral Fellowship for support.
Author information
Authors and Affiliations
Contributions
R.Y. designed imaging experiments, synthesized particles, performed bulk titration and single-molecule imaging experiments, derived kinetic models, wrote computer codes, and analyzed results. M.Z. designed and performed facet-controlled particle synthesis, performed structural and electrochemical characterizations, and analyzed results. X.M. wrote computer codes, discussed experiments and results, and contributed to manuscript revisions. Z.W. contributed to imaging experiments. D.A.G. and H.P. contributed to particle synthesis and bulk kinetic measurements. Z.Z. contributed to data visualization. R.Y., M.Z., and P.C. discussed results and wrote the manuscript. P.C. directed research.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Bert Weckhuysen, Duncan Ryan and the other, anonymous, reviewer for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ye, R., Zhao, M., Mao, X. et al. Nanoscale cooperative adsorption for materials control. Nat Commun 12, 4287 (2021). https://doi.org/10.1038/s41467-021-24590-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-24590-y
This article is cited by
-
Atomically precise nanoclusters predominantly seed gold nanoparticle syntheses
Nature Communications (2023)
-
The influence of nano filter elements on pressure drop and pollutant elimination efficiency in town border stations
Scientific Reports (2023)
-
Direct observation of the plasmon-enhanced palladium catalysis with single-molecule fluorescence microscopy
Nano Research (2023)
-
The many facets of cooperativity
Nature Reviews Materials (2021)