Abstract
Operating fuel cells in alkaline environments permits the use of platinum-group-metal-free (PGM-free) catalysts and inexpensive bipolar plates, leading to significant cost reduction. Of the PGM-free catalysts explored, however, only a few nickel-based materials are active for catalyzing the hydrogen oxidation reaction (HOR) in alkali; moreover, these catalysts deactivate rapidly at high anode potentials owing to nickel hydroxide formation. Here we describe that a nickel–tungsten–copper (Ni5.2WCu2.2) ternary alloy showing HOR activity rivals Pt/C benchmark in alkaline electrolyte. Importantly, we achieved a high anode potential up to 0.3 V versus reversible hydrogen electrode on this catalyst with good operational stability over 20 h. The catalyst also displays excellent CO-tolerant ability that Pt/C catalyst lacks. Experimental and theoretical studies uncover that nickel, tungsten, and copper play in synergy to create a favorable alloying surface for optimized hydrogen and hydroxyl bindings, as well as for the improved oxidation resistance, which result in the HOR enhancement.
Similar content being viewed by others
Introduction
Over the past 30 years, the proton exchange membrane fuel cell (PEMFC) technology has developed rapidly, resulting in the first commercial sales of fuel-cell powered cars in 2015 (ref. 1). Although great success, the mass market penetration by such zero-emission vehicles is currently hindered by the absence of inexpensive materials to replace costly platinum (Pt)-based catalysts, which are responsible for ~46% of the stack cost2. Extensive research has been conducted using various strategies to reduce the Pt loading3,4,5, but the acidic environment largely constrains the choice of catalytic materials that perform stably in PEMFCs. This shortcoming can be overcome by switching the operating environment from an acid to alkaline one-the resultant anion exchange membrane fuel cells (AEMFCs) allow for the use of platinum group metal-free (PGM-free) catalysts, thus enabling significant cost reduction6. Indeed, some PGM-free materials have been observed to catalyze the oxygen reduction reaction (ORR) comparable to Pt for the AEMFC cathode7,8,9,10. However, at the AEMFC anode, the activity of the hydrogen oxidation reaction (HOR) on Pt is inherently slower by ~100 times than that in acidic environment11,12, which demands much higher Pt loadings (0.4 mgPt cm−2 at AEMFC anode versus 0.03 mgPt cm−2 at PEMFC anode) to reach similar fuel cell performance13. At present, the lack of highly active and stable PGM-free HOR catalysts in alkaline environments hampers the progress towards the AEMFC implementation14.
Substantial effort has been devoted to searching HOR catalysts composed solely of earth-abundant elements, whereas PGM-free catalysts that show HOR activity in alkali are rather rare15. Nickel (Ni)-based compounds are currently the materials with the most promise as catalysts that drive the HOR in alkaline environments16. In 1960s, Raney Ni was first explored as HOR catalyst in liquid alkaline fuel cells under extreme alkalinity (6M KOH), but its activity was very low17,18,19. Since then, the HOR performance of Ni-based catalysts has been gradually improved via diverse methods, yielding catalysts such as CoNiMo20, MoNi4 and WNi421, NiMo/C22, Ni/NiO/C23, Ni/N-doped carbon nanotubes13, CeO2/Ni heterostructures24, Cr-modified Ni25, and Ni3N nanoparticles26,27. Despite marked progress, many of these Ni-based HOR catalysts deactivate quickly above 0.1 V versus reversible hydrogen electrode (RHE) owing to the formation of surface hydroxides28. To generate adequate power density, however, HOR catalysts should remain stable to at least 0.3 V versus RHE2, which could also largely mitigate the risk of passivation of the stack under transient conditions. Unfortunately, there is no PGM-free HOR catalyst with operating stability up to 0.3 V versus RHE has been reported thus far.
Here we report that Ni5.2WCu2.2 nanotubes (NTs)—a ternary nickel–tungsten–copper alloy—can catalyze the HOR in alkaline electrolyte highly efficient and stable. We find that the Ni5.2WCu2.2 catalyst achieves higher HOR activity than a commercial Pt/C counterpart. Importantly, stability window up to 0.3 V versus RHE was realized on this catalyst. At this potential, a considerable current density of 16.5 mA cm−2 could be held over 20 hours without notable decay. Moreover, this alloyed catalyst also exhibits high tolerance to 20,000 ppm CO impurity. The extraordinary efficiency of Ni5.2WCu2.2 exceeds that of previously reported PGM-free HOR catalysts.
Results
Synthesis and characterization of catalyst
Very recently, our group has reported bimetallic MoNi4 and WNi4 nanoalloys with notable activity toward the alkaline HOR, but such binary alloys lose activity above 0.2 V versus RHE owing to the surface oxidation21. Previous studies suggested an alloying-based approach for improved stability of catalysts by tuning the microstructures of the host metals29,30,31,32. For examples, alloying Mo with Pt3Ni (111) can mitigate the Ni leaching during electrochemical process, enabling greatly enhanced ORR stability31. Chorkendorff et al. identified that alloys of Pt and rare earths are stable ORR catalysts because of their very negative alloying energy Ea that limits dissolution32. We thus seek to widen the stability window of binary Ni-W catalyst through alloying with additional element to form new structure that resists surface oxidation during HOR operation. Prior studies have shown that HOR activity and stability can be improved largely in alkaline electrolytes when using Cu to partially replace noble metals (e.g., PdCu nanoparticles33 and Pt/Cu nanowires34). Moreover, Dekel et al. reported that Cu in alloys often dissolves at higher anode potentials as compared to other metals such as Mo28. We thus speculate that Cu may play an important role in enhancing the HOR activity and stability. Hence, we decide to introduce Cu to form ternary Ni-W-Cu alloy and explore its alkaline HOR property.
To synthesize the catalyst, Cu foam was immersed in 1M KOH for an anodization process to grow Cu(OH)2 nanowires throughout the substrate (Supplementary Figs. 1 and 2). The resulting indigo foam was consequently treated hydrothermally with Ni(NO3)2 · 6H2O, (NH4)6H2W12O40 · xH2O, and CO(NH2)2 in deionized water at 130 °C for 8 h. Then, the obtained green NiW-Cu(OH)2 precursor (Supplementary Figs. 3 and 4) was annealed in hydrogen/argon (H2/Ar: 5/95) atmosphere at 500 °C for 1 h to yield ternary Ni-W-Cu alloy (Fig. 1a). This simple synthetic approach provides good scalability. We synthesized a 3 cm × 10 cm Ni-W-Cu alloy foam by using scaled-up reactors, which shows good fidelity of the product, implying a potential industry-level use (Fig. 1b and Supplementary Fig. 5).
The achieved electrode consists of numerous uniform Ni-W-Cu alloy nanofibers with length up to 10 μm when imaged by scanning electron microscopy (SEM) (Fig. 2a and Supplementary Fig. 6). Each fiber possesses a very rough surface that is made up of whiskerette particles. Low-resolution transmission electron microscopy (TEM) unveils that the center of a representative fiber appears brighter, demonstrating that it is hollow (Fig. 2b). The formation of hollow-fibers was caused by the outward diffusion of Cu in the NiW-Cu(OH)2 precursor to produce Ni-W-Cu alloy during annealing process. Selected-area electron diffraction (SAED) analysis of a whisker reveals its high-crystalline structure (Up inset in Fig. 2b), which agrees with our atomic-resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) result that shows continuous lattice fringes without surface defects (Down inset in Fig. 2b). In Fig. 2c, the STEM measurements reveal that alloyed whiskerette particles bounded closely to form distinct grain boundaries. Energy-dispersive X-ray (EDX) spectrum elemental mapping displays a uniform, uncorrelated spatial distribution of Ni, W, and Cu (Fig. 2c and Supplementary Fig. 7). The weak O signal could originate from the adsorbed O and slight surface oxidation when exposing the sample in the air (Supplementary Fig. 8).
We performed X-ray diffraction (XRD) measurements of the collected Ni-W-Cu alloy powder and observed a high-crystallinity face-centred cubic structure (Fig. 2d). Compared to (111), (200), and (220) reflections of Ni nanoparticles, the diffraction peaks are shifted to lower angles in Ni-W-Cu alloy, indicating a higher lattice parameter caused by the addition of atoms with larger radius. Using similar synthetic method, we also prepared Ni-W alloy with cubic Ni17W3 phase (Fig. 2d and Supplementary Fig. 9), whose diffraction peaks sit between those of Ni nanoparticles (Fig. 2d and Supplementary Fig. 10) and Ni-W-Cu alloy. Given that the atomic radius follows the sequence of Ni < Cu < W, we predict more W atoms in Ni-W-Cu than in Ni17W3. Our inductively coupled plasma atomic emission spectroscopy (ICP-AES) analysis gives a Ni:W:Cu ratio of 5.2:1:2.2 for Ni-W-Cu alloy, which agrees well with EDX measurements and confirms our speculation. Thereafter, we assign the obtained ternary alloy as Ni5.2WCu2.2.
Alloying-based design has been demonstrated to alter catalytic properties by modulating the electronic structures of host and alloyed metals, leading to a cooperative interplay that tunes the adsorption energies of critical intermediates for enhanced catalytic reactivity35,36,37. We probed the work function of Ni5.2WCu2.2, Ni17W3 and Ni catalysts by Kelvin probe force microscopy38,39 (KPFM; Supplementary Fig. 11). A clean highly oriented pyrolytic graphite (HOPG) with work function value of 4.6 eV was used as a reference39. Figure 2e presents the measured surface potentials for the studied samples, which correspond to a work function value of 4.54 for Ni5.2WCu2.2, versus 4.71 eV for Ni17W3 and 4.80 eV for Ni (Inset in Fig. 2e), consistent with our calculated results (Supplementary Fig. 12). The lower work function of Ni5.2WCu2.2 suggests its modified electronic structure that allows for a faster electron transfer and thus enhanced catalytic ability40. To reveal the impact of ternary alloy effect on the chemical and structural environments of Ni, we performed the X-ray absorption spectroscopy. Figure 2f shows the X-ray absorption near-edge spectroscopy measurements of the Ni K-edge from Ni5.2WCu2.2, Ni17W3, and freshly-prepared Ni samples, as well as that from a Ni foil used for comparison. Adsorption features that are present in the spectra of our freshly-prepared Ni and Ni foil reference are similar. By contrast, a substantial increase in the white lines was observed for Ni5.2WCu2.2 and Ni17W3, indicating electron donation from Ni to W and Cu upon alloying41. We probed the radial structure function around Ni by Fourier transform (FT) of extended X-ray absorption fine-structure (EXAFS) spectra (Fig. 2g, Supplementary Fig. 13). A profound peak at ~2.1 Å can be attributable to the Ni-Ni and Ni-W/Cu bonds in Ni5.2WCu2.2 and Ni17W3 alloys21,42. The intensity of this peak decreases upon alloying Ni with W and Cu to form Ni5.2WCu2.2, which represents damped coordination structure of Ni. Furthermore, our Ni K-edge EXAFS fittings reveal that the first-shell Ni-W/Cu coordination number decreases from freshly-prepared Ni (~10.8) to Ni17W3 (~9.0) and then to Ni5.2WCu2.2 (~8.7) (Fig. 2h, Supplementary Fig. 14, Supplementary Table 1). We surmise the lower coordination number attributable to the highly nanostructured hollow structure of Ni5.2WCu2.2, and estimate that more active sites exist on the ternary alloy that would modify the adsorption ability of HOR intermediates.
Evaluation of HOR performance
We evaluated HOR activity and stability of the ternary Ni5.2WCu2.2 alloy in a standard three-electrode setup (Supplementary Fig. 15), using H2-saturated 0.1 M aqueous KOH as the electrolyte. The working electrode cuts from large-area Ni5.2WCu2.2 monolith with a geometric surface area of ~1 cm2 (catalyst loading: ~9.2 mg cm−2). Reference measurements of Ni17W3, Ni, and commercial Pt/C (20 wt%) catalysts were similarly performed for comparison. We used a slow sweep rate of 1 mV s−1 to minimize the capacitive contribution and to guarantee a steady-state measurement. Unless otherwise stated, all electrochemical data were measured without electrode rotation and were iR-corrected (i, current; R, resistance) for the uncompensated Ohmic drop.
As shown by the linear sweep voltammetry (LSV) curve of Ni5.2WCu2.2 in 0.1 M KOH, the onset potential for generating HOR current is as low as 0 V versus RHE, beyond which a sharp increase in anodic current was observed, demonstrating its exceptional energetics for HOR (Fig. 3a). By contrast, Ni5.2WCu2.2 gives almost no current-voltage feature in 0.1 M KOH saturated by Ar (Supplementary Fig. 16), further confirming that HOR catalysis occurs on this alloy catalyst. Figure 3a also shows that Ni5.2WCu2.2 can reach a diffusion-limiting HOR current density of ~20 mA cm−2, whereas Ni17W3 exhibits much inferior HOR activity and the single Ni is almost HOR inactive. Remarkably, the Ni5.2WCu2.2 catalyst even surpasses the commercial Pt/C catalyst from the kinetic to diffusion-limiting regions. We note that no rotation was applied to our bulky electrodes, suggesting that the Levich equation would not take effect43. As a result, the measured diffusion-limiting HOR currents on different catalysts deviate from the theoretical value. We measured a half-wave potential of 39 mV for Ni5.2WCu2.2, versus 44 mV for Pt/C catalyst. The observed striking HOR activity on Ni5.2WCu2.2 agrees well with the electrochemical impedance spectroscopy measurements that yield a small charge transfer resistance of ~3.0 Ohms at 30 mV overpotential (Supplementary Fig. 17).
In Fig. 3a, we show another important observation that we want to highlight in this work: that is, our nanostructured Ni5.2WCu2.2 catalyst can sustain HOR reactivity without deactivation up to 0.3 V versus RHE. Previously, most Ni-based HOR catalysts have been witnessed to lose activity rapidly above 0.1 V versus RHE owing to hydroxide formation13,28. Indeed, scanning LSV positively displays two pronounced peaks starting from 0.2 V versus RHE for Ni17W3 and 0.18 V versus RHE for Ni (Inset in Fig. 3a), which correspond to the formation of Ni(OH)2 (ref. 44). The limited tolerance to anode overpotentials poses significant risk of passivation under high current operation, leading to unsatisfied power output2. The stability window up to 0.3 V versus RHE for our Ni5.2WCu2.2 catalyst has not yet been achieved on previous PGM-free HOR catalysts (Fig. 3b), which would largely mitigate the risk of passivation under transient conditions.
We now extract the exchange current density (j0)—the most inherent measure of HOR activity—of various catalysts from linear fitting of micro-polarization regions (−5 to 5 mV; Supplementary Fig. 18). The geometric j0 of 11.36 mA cm−2 for Ni5.2WCu2.2 largely surpasses the values of 1.23 mA cm−2 for Ni17W3, 0.14 mA cm−2 for freshly prepared Ni, and 4.99 mA cm−2 for Pt/C catalyst (Fig. 3c, Supplementary Table 2). By fitting Bulter-Volmer equation in the Tafel regions, similar values were obtained (Fig. 3d, Supplementary Table 2 and Methods). To further quantify the intrinsic HOR activity, the j0 is renormalized by the electrochemical active surface area (ECSA; see “Methods”, Supplementary Fig. 19 and Table 3 for details), yielding a value of 0.014 mA cm−2 for Ni5.2WCu2.2, which is 1.96 times higher than Ni17W3 and 4.31 times higher than Pt/C catalyst (Fig. 3c). We also carried out the feed ratio-, temperature-, and time-dependent control experiments and unveiled that the optimized HOR activity was obtained on Ni-W-Cu alloy that was synthesized with Ni:W atomic ratio of 4:1 and then annealed at 500 °C for 1 h (Supplementary Figs. 20–24).
We next report that our ternary Ni5.2WCu2.2 alloy shows good resistance to CO poisoning. It is well known that PGM catalysts (such as Pt) are poisoned very rapidly in the presence of CO because of its preferential adsorption on Pt that blocks the active sites45. In Fig. 3e, we find that the Pt/C catalyst loses HOR activity completely with 20,000 ppm CO in the H2 fuel. By stark contrast, the Ni5.2WCu2.2 catalyst can retain high HOR activity with the same level of CO contamination, exhibiting its remarkable CO-tolerant ability. Besides, our results further show that the HOR activity decreases on both Ni5.2WCu2.2 and Pt/C catalysts when having 20,000 ppm CO2 in the H2 fuel (Supplementary Fig. 25). The detailed poison mechanism is unclear and needs further investigations.
Apart from activity and CO tolerance, another critical metric for the application of Ni5.2WCu2.2 alloy as a PGM-free anode is the long-term stability—especially the stability at high anode potentials. To assess this, we performed two sets of stability tests on our Ni5.2WCu2.2 alloy catalyst. We first performed accelerated durability tests (ADT) by applying linear potential sweeps between −0.2 and 0.2 V at 200 mV s−1 in H2-saturated 0.1 M KOH electrolyte. After 5,000 cycles, the Ni5.2WCu2.2 alloy shows a 1.4 mV increase in half-wave potential, versus 26.3 mV observed on Pt/C catalyst (Fig. 3f), implying that Ni5.2WCu2.2 alloy has stability better than Pt/C catalyst. Then, we evaluated the ability of Ni5.2WCu2.2 alloy to continuously catalyze the HOR using chronoamperometry (j ~ t) at a high anode potential of 0.3 V versus RHE. As shown in Fig. 3g, the current density (~20 mA cm−2) generated from Ni5.2WCu2.2 decreases to 16.5 mA cm−2 after 2 h, followed by slow degradation over the next 18 h. This degradation was likely caused by selective W leaching (Supplementary Fig. 26). By contrast, Pt/C catalyst delivers a current density of mere 10 mA cm−2 at the beginning, which decreases progressively to about 4.3 mA cm−2 over a 20 h of operation. After aggressive stability tests, the crystal phase, structure and composition of the Ni5.2WCu2.2 alloy remained almost unchanged (Supplementary Figs. 27–29), whereas Pt/C catalyst suffered from agglomeration and even detachment of Pt nanoparticles (Supplementary Fig. 30). These results reveal superior HOR stability of Ni5.2WCu2.2 alloy compared with Pt/C catalyst.
Surface structure and chemistry of catalyst
The formation of a ternary Ni5.2WCu2.2 alloy enables a HOR catalyst that shows high activity and stability at large anode potential, as well as good resistance to CO poisoning. In this section, we study the structural and chemical characters that affect and determine these performances. X-ray photoelectron spectroscopy (XPS) analysis of the studied samples showed that Ni, Ni17W3, and Ni5.2WCu2.2 are all metallic in nature with certain surface oxidation (Fig. 4a and b). We note that some degree of surface oxidation is nearly inevitable when these Ni-based compounds are exposed to air, analogous to our previous observation21. XPS measurements also revealed that the Ni 2p binding energies of Ni5.2WCu2.2 shifted 0.3 eV to higher energy with respect to Ni17W3 (Fig. 4a). Meanwhile, the W 4f XPS of Ni5.2WCu2.2 showed a shift of the W core levels to lower binding energies compared with Ni17W3 (Fig. 4b). These results indicated electron donation from Ni to W once Cu participate in the alloy, leading to modulated electronic structure. Our Bader analyses further confirm such charge redistribution after incorporating Cu into the alloy structure (Supplementary Fig. 31).
To further probe the surface features, we conducted CO-stripping (CO electrooxidation) experiments on Ni17W3 and Ni5.2WCu2.2 with Pt/C catalyst as a reference. Results shown in Fig. 4c display that the oxidation of adsorbed CO (CO*) occurs at 0.69 V for Pt/C catalyst, which is in agreement with prior reports46. By contrast, Ni17W3 oxidizes CO* at a much lower potential of 0.48 V, and Ni5.2WCu2.2 has a CO-stripping peak located in the middle (0.62 V). These results indicate that both Ni17W3 and Ni5.2WCu2.2 have a much lower CO adsorption ability compared with the Pt/C catalyst, leading to the good CO-tolerance property observed in Fig. 3e. Moreover, in alkaline electrolytes, because the OH adsorption can facilitate the removal of the CO* (ref. 47), our CO-stripping results thus offer additional surface information that Ni17W3 and Ni5.2WCu2.2 possess stronger OH adsorption than Pt/C catalysts following the order of Ni17W3 > Ni5.2WCu2.2 > Pt/C.
Surface analysis of the studied samples was also carried out using cyclic voltammetry in 0.1 M KOH electrolyte that saturated by Ar and H2, respectively. At a large sweep rate of 50 mV s−1, the oxidation curve of Ni5.2WCu2.2 appears at higher anode potential than that of Ni and Ni17W3 (Fig. 4d), suggesting its superior oxidation-tolerant ability27. Intriguingly, we find that the oxidation peak of Ni5.2WCu2.2 in H2-saturated 0.1 M KOH exhibits a 58 mV positive shift relative to that in Ar-saturated 0.1 M KOH (Fig. 4d). Similar positive shifts were also observed on Ni (45 mV) and Ni17W3 (40 mV) but with smaller values. The notable shift of oxidation peak in H2- and Ar-saturated electrolytes likely result from the various degrees of H2 adsorbed on these Ni-based catalysts, which indicates that the adsorption of H2 decreases in the order of Ni17W3 > Ni > Ni5.2WCu2.2.
Computational studies
With these experimental information in hand, we now turn to perform density functional theory (DFT) to gain fundamental insight into mechanisms responsible for the excellent activity and stability, as well as the good CO-tolerance property (see Methods). We constructed and optimized crystal models of Ni5.2WCu2.2(111), Ni17W3(111), Ni(111), and Pt(111) to represent the catalytic surfaces (see Methods; Supplementary Figs. 32–36). According to the DFT calculations, O-species prefer to adsorb on Ni (0.133 eV) and Ni17W3 (0.22 eV), whereas such adsorption on Ni5.2WCu2.2 (0.31 eV) is considerably weak (Fig. 5a). These results predict that the oxidation of Ni5.2WCu2.2 is more difficult to occur as compared to Ni and Ni17W3 (refs. 48,49), consistent with our experimentally observed HOR stability at higher anode potential. Additionally, our DFT simulations reveal that Pt possesses a much higher CO adsorption strength (−1.78 eV) than that of Ni17W3 (−1.42 eV) and Ni5.2WCu2.2 (−1.55 eV) (Fig. 5b), which explain the marked CO-tolerance ability of Ni5.2WCu2.2 and agree well with above CO-stripping trend (Fig. 4c).
Although the HOR mechanism in alkaline electrolytes is still debated6,50,51,52, recent research has gradually led to agreement that hydrogen binding energy (HBE) and OH binding energy (OHBE)/oxophilicity both serve as descriptor for HOR performance27,50,53. With DFT calculations (Fig. 5c), we revealed that although the HBE of Pt(111) is optimum, whereas the adsorption energy of OH is too weak on Pt(111). As to Ni(111) facet, the HBE value is −0.58 eV, which means a too strong H-binding that hampers HOR catalysis, agreeing with previous study23. Our DFT results further show that ternary Ni5.2WCu2.2 alloy yields a HBE close to Pt(111); moreover, the hydroxyl adsorption on Ni5.2WCu2.2(111) is significantly enhanced compared with Pt(111). Thus, this ternary-alloy-designed Ni5.2WCu2.2 gives rise to near-optimal HBE and OHBE that promote the HOR kinetics. We also computed the HBE and OHBE of Ni17W3 for comparison (Fig. 5c). Despite this catalyst exhibits stronger OHBE than Pt(111), its HBE is unfortunately strong, thus showing inferior HOR activity. The optimized HBE and OHBE that enabled by the synergy of Ni, W, and Cu in the ternary alloy can be further verified by our projected density of states (PDOS) analyses (Supplementary Fig. 37).
We note that our theoretically predicted trend of OH adsorption and CO adsorption perfectly match with CO-stripping results (Fig. 4c). Moreover, the free energy diagrams that we computed for the reaction pathways on various catalysts are presented in Fig. 5d. Results show that both H and OH adsorptions on Ni17W3 and Ni5.2WCu2.2 are exergonic, whereas the H2O formation and desorption steps on the two catalysts are endothermic. By contrast, H adsorption and H2O desorption on Ni are exergonic, but OH adsorption and H2O formation on Ni are endothermic. Our calculations thus predict that H2O formation (i.e., Volmer step) is the rate-determining step, showing energy barriers of 0.45, 0.43, and 0.28 eV for the Ni, Ni17W3 and Ni5.2WCu2.2 catalysts, respectively. The much lower energy barrier obtained on Ni5.2WCu2.2 contributes to its exceptional HOR performance. Altogether, our experimental and computational studies reveal that the synergy among Ni, W, and Cu—a multiple-element alloying effect—enables the optimized HBE and OHBE that improve the energetics for HOR, as well as the wide stability window up to 0.3 V versus RHE.
Discussion
To conclude, this work demonstrates a multiple-element Ni-based alloy strategy for creating HOR catalyst that makes use of earth-abundant elements, showing exceptional activity and stability in alkaline electrolyte. This notable HOR performance can be explained by the alloying effect among nickel, tungsten and copper, which work in synergy to enable optimized hydrogen and hydroxyl bindings, as well as the improved resistance against surface oxidation. Our study calls for further exploration of multiple-element alloys composed of other cheap metals, thereby aiding the development of more efficient HOR catalysts for AEMFC anodes.
Methods
Synthesis of Cu(OH)2 nanowires on Cu foam
The Cu(OH)2 NWs were grown on commercial Cu foam via a simple anodization method. Prior to the growth of nanowires, a piece of Cu foam (1 cm × 3 cm) was ultrasonically cleaned by hydrochloric acid solution, ethanol and deionized water, respectively, which was then immersed into a two-electrode system using Pt foil as the counter electrode in 1 M NaOH solution. The anodization was carried out at a constant current of 60 mA for 20 min to obtain Cu(OH)2 nanowires on Cu foam.
Synthesis of Ni5.2WCu2.2, Ni17W3 and Ni
Firstly, Ni(NO3)2 · 6H2O (581.6 mg), (NH4)6H2W12O40 · xH2O (123.2 mg) and CO(NH2)2 (360.4 mg) were dissolved in 30 mL deionized water, and then transferred into a 50 mL Teflon-lined stainless-steel autoclave. The as-synthesized indigo Cu(OH)2 NWs on Cu foam was immersed into the solution and placed against the wall of autoclave. Subsequently, the autoclave was maintained at 130 °C for 8 h. The foam was taken out and washed by deionized water several times to obtain NiW-Cu(OH)2 NWs precursor. Finally, the precursor was annealed at 500 °C for 1 h with a heating rate of 5 °C under 5 % H2/Ar atmosphere to obtain Ni5.2WCu2.2 alloys. The mass loading of Ni5.2WCu2.2 alloys was ~9.2 mg cm−2 as determined by weighing the mass of Cu foam before anodization and after the annealing process.
By comparison, Ni17W3 and Ni precursors were directly grown on a clean Ni foam (1 cm × 3 cm) that was not anodized in prior. To obtain NiW precursors, Ni(NO3)2 · 6H2O (581.6 mg), (NH4)6H2W12O40 · xH2O (123.2 mg) and CO(NH2)2 (360.4 mg) were dissolved in 30 mL deionized water, and then transferred into a 50 mL Teflon-lined stainless-steel autoclave. The pure Ni foam was immersed into the solution and placed against the wall of autoclave. The Ni precursors were obtained under the same conditions without the addition of (NH4)6H2W12O40 · xH2O. The hydrothermal process was all performed under 130 °C for 8 h. Then the foam was taken out and washed by deionized water several times followed by an annealing process at 500 °C for 1 h with a heating rate of 5 °C under 5 % H2/Ar atmosphere to obtain Ni17W3 and Ni nanoparticles.
Material characterizations
The obtained samples were examined by multiple analytic techniques. Optical microscope images were obtained with a polarizing microscope (Leica DM2700P, Germany) equipped with a Leica MC190 HD camera. The morphology of the samples was determined by SEM (Zersss Supra 40) and TEM (JEOL 2010F(s)). The STEM and HRTEM images, and EDX elemental mappings were taken on JEMARM 200 F Atomic Resolution Analytical Microscope with an acceleration voltage of 200 kV. The KPFM characterization was carried out with Atom Force Microscope (Dimension Icon). ICP-AES data was obtained by an Optima 7300 DV instrument. XRD was performed on a Japan Rigaku DMax-γA X-ray diffractometer with Cu Kα radiation (λ = 1.54178 Å). XPS was taken on an X-ray photoelectron spectrometer (ESCALab MKII) with an X-ray source (Mg Kα hυ = 1253.6 eV).
XAFS measurements
The XAFS spectra (Ni K-edge) were collected at 1W1B station in Beijing Synchrotron Radiation Facility (BSRF). The storage rings of BSRF were operated at 2.5 GeV with an average current of 250 mA. Using Si(111) double-crystal monochromator, the data collection was carried out in transmission/fluorescence mode using ionization chamber. All spectra were collected in ambient conditions. The k3-weighted EXAFS spectra were obtained by subtracting the post-edge background from the overall absorption and then normalizing with respect to the edge-jump step. Subsequently, k3-weighted χ(k) data of Ni K-edge were Fourier transformed to real (R) space using a hanning windows (dk = 1.0 Å−1) to separate the EXAFS contributions from different coordination shells. To obtain the quantitative structural parameters around central atoms, least-squares curve parameter fitting was performed using the ARTEMIS module of IFEFFIT software packages54.
Electrochemical measurements
A standard three-electrode set-up was applied to perform the HOR electrochemical measurements on the VSP-300 Potentiostat (Bio-Logic, France). Carbon rod was used as the counter electrode and all potentials were measured against an Ag/AgCl reference electrode (saturated in 3.0 M KCl) and converted to the RHE reference scale using following equation:
The as-synthesized Ni5.2WCu2.2, Ni17W3 and Ni catalysts on Cu foam were directly used as working electrodes. After the annealing process, they were cut into 1 cm × 1 cm pieces for electrochemical tests. The commercial Pt/C was coated on a pure Cu foam (1 cm × 1 cm) with optimized loading of 1.5 mg cm−2 (Supplementary Fig. 38). Before HOR measurements, the electrolyte (0.1 M KOH) was bubbled with H2 gas for at least 30 min. The EIS measurement was performed at 30 mV overpotential and an amplitude of the sinusoidal voltage of 5 mV (frequency range: 100 kHz to 40 mHz). All the linear sweep voltammetry (LSV), cyclic voltammetry (CV), and chronoamperometry (CA) curves were iR-corrected.
The exchange current density (j0) can be obtained by fitting kinetic current density (jk) versus the overpotential (η) using the following Butler–Volmer equation:
where α is the charge transfer coefficient, η is the overpotential, R is the ideal gas constant (8.314 J mol−1 K−1), T is the experimental temperature (298 K), and F is the Faraday’s constant (96,485 C mol−1).
CO stripping was performed by holding the electrode potential at 0.1 V versus RHE for 10 min in the purged CO to adsorb CO on the metal surface, followed by Ar purging for another 30 min to remove residual CO in the electrolyte. The CO stripping current was obtained via cyclic voltammetry in a potential region from 0 to 1.2 V at a sweep rate of 20 mV s−1.
DFT calculations
We carried out DFT calculations using the Vienna ab initio simulation package (VASP)55,56 program with projector augmented wave (PAW)57,58 method. The Perdew-Burke-Ernzerhof (PBE)59 generalized gradient approximation (GGA) exchange-correlation functional was used throughout. A 500 eV plane-wave kinetic energy cutoff was chosen, and a 5 × 5 × 1 Monhorst-Pack k-point sampling was adopted for the structure relaxation. The convergence criterion for the electronic self-consistent iteration was set to be 10−4 eV. A residual force threshold of 0.02 eV Å−1 was set for geometry optimizations. The calculations were conducted on (111) surface of Ni, Ni17W3, Ni5.2WCu2.2, and Pt models. Hubbard U corrections were applied to transition metal d-electrons and the values of U–J parameters for Ni (3.80), W (6.20) and Cu (3.08) atoms were taken from the references60,61,62. The vacuum layer was set to be 15 Å to ensure the separation between slabs.
The key reaction steps in alkaline HOR:
The Gibbs free energy changes are calculated as follows:
The G values are calculated by:
EDFT is the total energy from the DFT calculation. EZPE is the zero-point energy, S is the entropy and T is the temperature (298 K).
The adsorption energies (ΔEad) for O and CO were calculated by the following equations:
The O adsorption energies were calculated by:
The CO adsorption energies were calculated by:
The HBE and OHBE can be calculated by following equations:
The HBE were calculated by:
The OHBE were calculated by:
Note: EO@cat., ECO@cat., EH@cat., and EOH@cat. represent the energies of metals or alloy slabs with the adsorbed O, CO, H, and OH species; the Ecat., EO, ECO, EH, and EOH represent the energies of the metals or alloys slabs, the O atoms, the CO species, the H atoms, and OH species, respectively. Since the ground state of O2 molecule is poorly described by DFT calculations, we thus used gas-phase H2O and H2 as references to calculate the EO (EO = EH2O-EH2). As to the EOH, it can be obtained by EOH = EH2O -1/2 EH2. We calculated the Gibbs free energy changes of G(OH−), G(H2) and G(H2O) according to a recent literature63.
Data availability
All experimental data within the article and its Supplementary Information are available from the corresponding author upon reasonable request.
References
Yoshida, T. & Kojima, K. Toyota MIRAI fuel cell vehicle and progress toward a future hydrogen society. Interface Mag. 24, 45–49 (2015).
Setzler, B. P., Zhuang, Z., Wittkopf, J. A. & Yan, Y. Activity targets for nanostructured platinum-group-metal-free catalysts in hydroxide exchange membrane fuel cells. Nat. Nanotechnol. 11, 1020–1025 (2016).
Ott, S. et al. Ionomer distribution control in porous carbon-supported catalyst layers for high-power and low Pt-loaded proton exchange membrane fuel cells. Nat. Mater. 19, 77–85 (2020).
Garsany, Y., Atkinson, R. W., Gould, B. D. & Swider-Lyons, K. E. High power, Low-Pt membrane electrode assemblies for proton exchange membrane fuel cells. J. Power Sources 408, 38–45 (2018).
Ohma, A. et al. Analysis of proton exchange membrane fuel cell catalyst layers for reduction of platinum loading at Nissan. Electrochim. Acta 56, 10832–10841 (2011).
Strmcnik, D. et al. Improving the hydrogen oxidation reaction rate by promotion of hydroxyl adsorption. Nat. Chem. 5, 300–306 (2013).
Wang, Y. et al. Synergistic Mn-Co catalyst outperforms Pt on high-rate oxygen reduction for alkaline polymer electrolyte fuel cells. Nat. Commun. 10, 1506 (2019).
Liang, Y. et al. Co3O4 nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. Nat. Mater. 10, 780–786 (2011).
Suntivich, J. et al. Design principles for oxygen-reduction activity on perovskite oxide catalysts for fuel cells and metal–air batteries. Nat. Chem. 3, 546–550 (2011).
Dekel, D. R. Review of cell performance in anion exchange membrane fuel cells. J. Power Sources 375, 158–169 (2018).
Sheng, W., Gasteiger, H. A. & Shao-Horn, Y. Hydrogen oxidation and evolution reaction kinetics on platinum: acid vs alkaline electrolytes. J. Electrochem. Soc. 157, B1529–B1536 (2010).
Durst, J. et al. New insights into the electrochemical hydrogen oxidation and evolution reaction mechanism. Energy Environ. Sci. 7, 2255–2260 (2014).
Zhuang, Z. et al. Nickel supported on nitrogen-doped carbon nanotubes as hydrogen oxidation reaction catalyst in alkaline electrolyte. Nat. Commun. 7, 10141 (2016).
Gottesfeld, S. et al. Anion exchange membrane fuel cells: current status and remaining challenges. J. Power Sources 375, 170–184 (2018).
Davydova, E. S., Mukerjee, S., Jaouen, F. & Dekel, D. R. Electrocatalysts for hydrogen oxidation reaction in alkaline electrolytes. ACS Catal. 8, 6665–6690 (2018).
Oshchepkov, A. G., Braesch, G., Bonnefont, A., Savinova, E. R. & Chatenet, M. Recent advances in the understanding of nickel-based catalysts for the oxidation of hydrogen-containing fuels in alkaline media. ACS Catal. 10, 7043–7068 (2020).
Mund, K., Richter, G. & von Sturm, F. Titanium-containing raney nickel catalyst for hydrogen electrodes in alkaline fuel cell systems. J. Electrochem. Soc. 124, 1–6 (1977).
Kenjo, T. Doping effects of transition metals on the polarization characteristics in raney nickel hydrogen electrodes. Electrochim. Acta 33, 41–46 (1988).
Kiros, Y., Majari, M. & Nissinen, T. A. Effect and characterization of dopants to Raney nickel for hydrogen oxidation. J. Alloy. Compd. 360, 279–285 (2003).
Sheng, W. et al. Non-precious metal electrocatalysts with high activity for hydrogen oxidation reaction in alkaline electrolytes. Energy Environ. Sci. 7, 1719–1724 (2014).
Duan, Y. et al. Bimetallic nickel-molybdenum/tungsten nanoalloys for high-efficiency hydrogen oxidation catalysis in alkaline electrolytes. Nat. Commun. 11, 4789 (2020).
Kabir, S. et al. Platinum group metal-free NiMo hydrogen oxidation catalysts: high performance and durability in alkaline exchange membrane fuel cells. J. Mater. Chem. A 5, 24433–24443 (2017).
Yang, Y. et al. Enhanced electrocatalytic hydrogen oxidation on Ni/NiO/C derived from a Nickel-based metal–organic framework. Angew. Chem. Int. Ed. 58, 10644–10649 (2019).
Yang, F. et al. Boosting hydrogen oxidation activity of Ni in alkaline media through oxygen-vacancy-rich CeO2/Ni heterostructures. Angew. Chem. Int. Ed. 58, 14179–14183 (2019).
Lu, S., Pan, J., Huang, A., Zhuang, L. & Lu, J. Alkaline polymer electrolyte fuel cells completely free from noble metal catalysts. Proc. Natl Acad. Sci. USA 105, 20611 (2008).
Wang, T. et al. Weakening hydrogen adsorption on nickel via interstitial nitrogen doping promotes bifunctional hydrogen electrocatalysis in alkaline solution. Energy Environ. Sci. 12, 3522–3529 (2019).
Ni, W. et al. Ni3N as an active hydrogen oxidation reaction catalyst in alkaline medium. Angew. Chem. Int. Ed. 58, 7445–7449 (2019).
Davydova, E. S., Speck, F. D., Paul, M. T. Y., Dekel, D. R. & Cherevko, S. Stability limits of Ni-based hydrogen oxidation electrocatalysts for anion exchange membrane fuel cells. ACS Catal. 9, 6837–6845 (2019).
Mao, J. et al. Design of ultrathin Pt-Mo-Ni nanowire catalysts for ethanol electrooxidation. Sci. Adv. 3, e1603068 (2017).
Gao, L. et al. Unconventional p–d hybridization interaction in PtGa ultrathin nanowires boosts oxygen reduction electrocatalysis. J. Am. Chem. Soc. 141, 18083–18090 (2019).
Huang, X. et al. High-performance transition metal–doped Pt3Ni octahedra for oxygen reduction reaction. Science 348, 1230 (2015).
Escudero-Escribano, M. et al. Tuning the activity of Pt alloy electrocatalysts by means of the lanthanide contraction. Science 352, 73 (2016).
Qiu, Y. et al. BCC-phased PdCu alloy as a highly active electrocatalyst for hydrogen oxidation in alkaline electrolytes. J. Am. Chem. Soc. 140, 16580–16588 (2018).
Alia, S. M., Pivovar, B. S. & Yan, Y. Platinum-coated copper nanowires with high activity for hydrogen oxidation reaction in base. J. Am. Chem. Soc. 135, 13473–13478 (2013).
Wang, H. & Abruña, H. D. IrPdRu/C as H2 oxidation catalysts for alkaline fuel cells. J. Am. Chem. Soc. 139, 6807–6810 (2017).
Wang, H. & Abruña, H. D. Rh and Rh alloy nanoparticles as highly active H2 oxidation catalysts for alkaline fuel cells. ACS Catal. 9, 5057–5062 (2019).
Wang, Y. et al. Pt–Ru catalyzed hydrogen oxidation in alkaline media: oxophilic effect or electronic effect? Energy Environ. Sci. 8, 177–181 (2015).
Cheon, J. Y. et al. Intrinsic relationship between enhanced oxygen reduction reaction activity and nanoscale work function of doped carbons. J. Am. Chem. Soc. 136, 8875–8878 (2014).
Fernández Garrillo, P. A., Grévin, B. & Chevalier, N. & Borowik, Ł. Calibrated work function mapping by Kelvin probe force microscopy. Rev. Sci. Instrum. 89, 043702 (2018).
Gao, F.-Y. et al. High.-curvature Transit.-Met. chalcogenide Nanostruct. a pronounced proximity Eff. enable fast selective CO2 electroreduction. Angew. Chem. Int. Ed. 55, 8706–8712 (2019).
Shan, J. et al. NiCu single atom alloys catalyze the CH bond activation in the selective non- oxidative ethanol dehydrogenation reaction. Appl. Catal., B-Environ. 226, 534–543 (2018).
Zhang, T. et al. Atomically dispersed nickel(I) on an alloy-encapsulated nitrogen-doped carbon nanotube array for high-performance electrochemical CO2 reduction reaction. Angew. Chem. Int. Ed. 59, 12055–12061 (2020).
Zheng, J., Yan, Y. & Xu, B. Correcting the hydrogen diffusion limitation in rotating disk electrode measurements of hydrogen evolution reaction kinetics. J. Electrochem. Soc. 162, F1470–F1481 (2015).
Oshchepkov, A. G. et al. Nanostructured nickel nanoparticles supported on vulcan carbon as a highly active catalyst for the hydrogen oxidation reaction in alkaline media. J. Power Sources 402, 447–452 (2018).
Valdés-López, V. F., Mason, T., Shearing, P. R. & Brett, D. J. L. Carbon monoxide poisoning and mitigation strategies for polymer electrolyte membrane fuel cells—A review. Prog. Energy Combust. Sci. 79, 100842 (2020).
Li, J. et al. Experimental proof of the bifunctional mechanism for the hydrogen oxidation in alkaline media. Angew. Chem. Int. Ed. 56, 15594–15598 (2017).
Zhang, Z.-C. et al. Engineering phase and surface composition of Pt3Co nanocatalysts: A strategy for enhancing CO tolerance. Nano Energy 34, 224–232 (2017).
Dou, Y. et al. Approaching the activity limit of CoSe2 for oxygen evolution via Fe doping and Co vacancy. Nat. Commun. 11, 1664 (2020).
Siahrostami, S. et al. Enabling direct H2O2 production through rational electrocatalyst design. Nat. Mater. 12, 1137–1143 (2013).
Davydova, S. E., Zaffran, J., Dhaka, K., Toroker, C. M. & Dekel, R. D. Hydrogen oxidation on Ni-based electrocatalysts: the effect of metal doping. Catalysts 8, 454 (2018).
Sheng, W. et al. Correlating hydrogen oxidation and evolution activity on platinum at different pH with measured hydrogen binding energy. Nat. Commun. 6, 5848 (2015).
Zheng, J., Sheng, W., Zhuang, Z., Xu, B. & Yan, Y. Universal dependence of hydrogen oxidation and evolution reaction activity of platinum-group metals on pH and hydrogen binding energy. Sci. Adv. 2, e1501602 (2016).
McCrum, I. T. & Koper, M. T. M. The role of adsorbed hydroxide in hydrogen evolution reaction kinetics on modified platinum. Nat. Energy 5, 891–899 (2020).
Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2005).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Cockayne, E. & Nelson, E. B. Density functional theory meta-GGA + U study of water incorporation in the metal-organic framework material Cu-BTC. J. Chem. Phys. 143, 024701 (2015).
Zhao, S. et al. Ultrathin metal–organic framework nanosheets for electrocatalytic oxygen evolution. Nat. Energy 1, 16184 (2016).
Zhang, B. et al. High-valence metals improve oxygen evolution reaction performance by modulating 3d metal oxidation cycle energetics. Nat. Catal. 3, 985–992 (2020).
Liu, M. et al. Enhanced electrocatalytic CO2 reduction via field-induced reagent concentration. Nature 537, 382–386 (2016).
Acknowledgements
This work is supported by the National Basic Research Program of China (Grant 2018YFA0702001), the National Natural Science Foundation of China (Grants 21975237 and 51702312), the Anhui Provincial Research and Development Program (Grant 202004a05020073), the Fundamental Research Funds for the Central Universities (Grant WK2340000101), the USTC Research Funds of the Double First-Class Initiative (Grant YD2340002007), and the Recruitment Program of Global Youth Experts. Y.D. acknowledges the China Postdoctoral Science Foundation (2020M682008, 2020TQ0309).
Author information
Authors and Affiliations
Contributions
M.R.G. conceived and supervised the project. S.Q. and Y.D. performed the experiments, collected and analyzed the data. X.L.Z carried out the DFT calculations. X.S.Z. and J.F.Z. performed XPS measurements. L.-R.Z. collected and analyzed the XANES data. F.Y.G., P.P.Y., Z.Z.N., R.L., and Y.Y. helped with electrochemical data collection and analysis. M.R.G. and S.Q. co-wrote the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Dario Dekel, Yun Wang, and other, anonymous, reviewers for their contributions to the peer review of this work. Peer review reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Qin, S., Duan, Y., Zhang, XL. et al. Ternary nickel–tungsten–copper alloy rivals platinum for catalyzing alkaline hydrogen oxidation. Nat Commun 12, 2686 (2021). https://doi.org/10.1038/s41467-021-22996-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-22996-2
This article is cited by
-
Metal-support interaction boosts the stability of Ni-based electrocatalysts for alkaline hydrogen oxidation
Nature Communications (2024)
-
Tuning the apparent hydrogen binding energy to achieve high-performance Ni-based hydrogen oxidation reaction catalyst
Nature Communications (2024)
-
Embedding oxophilic rare-earth single atom in platinum nanoclusters for efficient hydrogen electro-oxidation
Nature Communications (2023)
-
Electrodeposited Ternary CuNiMo Catalysts for Alkaline Hydrogen Oxidation
Electronic Materials Letters (2023)
-
Towards reliable assessment of hydrogen oxidation electrocatalysts for anion-exchange membrane fuel cells
Nano Research (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.