Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Characterisation of oxygen defects and nitrogen impurities in TiO2 photocatalysts using variable-temperature X-ray powder diffraction

Abstract

TiO2-based powder materials have been widely studied as efficient photocatalysts for water splitting due to their low cost, photo-responsivity, earthly abundance, chemical and thermal stability, etc. In particular, the recent breakthrough of nitrogen-doped TiO2, which enhances the presence of structural defects and dopant impurities at elevated temperatures, exhibits an impressive visible-light absorption for photocatalytic activity. Although their electronic and optical properties have been extensively studied, the structure-activity relationship and photocatalytic mechanism remain ambiguous. Herein, we report an in-depth structural study of rutile, anatase and mixed phases (commercial P25) with and without nitrogen-doping by variable-temperature synchrotron X-ray powder diffraction. We report that an unusual anisotropic thermal expansion of the anatase phase can reveal the intimate relationship between sub-surface oxygen vacancies, nitrogen-doping level and photocatalytic activity. For highly doped anatase, a new cubic titanium oxynitride phase is also identified which provides important information on the fundamental shift in absorption wavelength, leading to excellent photocatalysis using visible light.

Introduction

TiO2-based materials are widely studied as efficient photocatalysts since the first photoelectrochemical (PEC) water-splitting system was demonstrated in 1972. They have found use in a wide range of applications including the photocatalytic hydrogen evolution reaction, pollutant degradation1,2, and dye-sensitised photocatalysis3, due to their characteristic strong photo-responsive, low cost, high natural abundance, and high chemical and thermal stability.

There are many polymorphs of TiO2, including anatase (A), rutile (R) and brookite, which all exist naturally in minerals. There is a consensus from experimental evidence that anatase is the most active for photocatalysis, there is no in-depth understanding of its structure-activity relationship. In addition, the wide bandgap of TiO2 anatase limits its absorption of visible light in photocatalysis, which has driven the development of many modifications of TiO2-based photocatalyst materials. Cation-doping or anion-doping of the oxide is presently regarded as a highly effective approach for enhancing the utilisation of visible light4,5,6,7, among which nitrogen-doping has received significant attention as it reduces the band gap for photo-excitation, enabling the absorption of the plentiful visible-light region of the solar-irradiance spectrum, thus resulting in enhanced photocatalytic performance. The electronic factors that contribute to the photocatalytic activity of TiO2, with and without doping, have been researched for some years, but the underlying mechanism is still not yet clear. Generally, it is thought that the extraction of neutral oxygen atoms, results in electron transfer to the Ti cationic band structure resulting in n-type doping8, which may occur in both the bulk and on the surface of TiO2 crystals. However, photocatalytic water splitting is a surface phenomenon that takes place by the direct interaction of water molecules with the catalyst. Thus, only the excited Ti sites and holes that are on the surface are directly involved in the processes of proton reduction and hydroxide oxidation, which form hydrogen and oxygen gas, respectively, from dissociated water. Nonetheless, there is still a lack of detail with respect to the structure-activity relationship of this unique phase-boundary, and the exact way in surface and bulk structure affects the system is still far from well-understood. Early reports of TiO2-based photocatalysts concede that the enhanced photocatalytic activity cannot be directly correlated to changes in bulk structure by crystallographic methods, as such small changes cannot be easily resolved4. On the other hand, the formation of defects during photocatalysis, such as interstitial ions and vacancies with unpaired electrons, can be observed by EPR measurements6,9. The surface defects in the photocatalytically active anatase (101) facet have been visualised by STEM, but the surface concentration is found to be too low at room temperature to account for photocatalysis10. On the other hand, total defects, that is to say irrespective of depth (surface, sub-surface and bulk), may be characterised by resonant photoemission spectroscopy (RESPES) and X-ray absorption spectroscopy (XAS). It has been shown that the polymorph and exposed facets of TiO2 materials significantly affect the concentration of total oxygen vacancies11. Proportionate to photocatalytic activity, the anatase (101) surface supports a very high bulk concentration, which indicates oxygen vacancies beyond the surface; meanwhile rutile (110) and anatase (001) have very low concentrations of total vacancies. This finding was further supported by interrogating the energies of various oxygen vacancy sites by first-principles DFT caluculations12. Though these reports all highlight the nature and importance of surface structural change of TiO2 powder, they make no reference to the parent bulk structure, which along with an atomic understanding of structure, is the key to understanding surface photocatalysis.

TiO2 structures also display rich phase-variation across temperature and pressure, adopting many common mineral structures13: monoclinic Pbmm tungsten bronze (TiO2(B),)14, monoclinic P21/c ZrO2 baddeleyite (TiO2(MI),)15, orthorhombic Pbcn columbite (TiO2(OI))16, orthorhombic Pnma PbCl2 cotunnite TiO2(OII)17, cubic Fm\(\overline 3\)m CaF2 (TiO2(C1))18,19,20. In addition, orthorhombic Pbnm MnO2 ramsdellite (TiO2(R))21 and monoclinic I2/m hollandite (TiO2(H))22 structures can also be formed by the complete oxidation of lithium-doped and potassium-doped titania, respectively.

Treating anatase powder with ammonia at elevated temperature has been experimentally shown to yield full conversion of tetragonal anatase to cubic titanium nitride, which has itself been researched as a photocatalyst, particularly due to its broad absorption in the visible region23,24,25. Titanium nitride consists of titanium in an oxidation state of +3 and nitrogen in an oxidation state of −3, arranged in the Fm\(\overline 3\)m rock-salt structure. The material is widely recognised as a material for bio-electrical components26. Thin films can be synthesised using solid-liquid solvothermal conditions27, IVD (ion vapour deposition) or CVD (chemical vapour deposition)28. Instead of total nitridation of TiO2, there are several reports of the formation of titanium oxynitride for application in photocatalytic and photonic materials29. However, though phase identification for complex poly-phasic TiO2 powders yielded by ammonia/argon treatment have been reported30,31, the structures of titanium oxynitride remain largely inferred and uncharacterised. Do et al. report the tuneable non-stoichiometric composition of titanium oxynitride, TiNxOy, between the end-phases of pure TiO2 and TiN32. Across reports, it is generally noted that these intermediate phases have an intermediate lattice parameter between the two end-composition Fm\(\overline 3\)m phases of titanium(II) oxide (4.185 Å) and titanium nitride (4.241 Å)27,32. Some have used this observation to apply the linear Vegard’s law and assume substitutional doping to yield values for composition27. Despite this, there are no complete structure solutions for the oxygen site within the nitride structure so far. In addition, the nitrogen-doping promotes the formation of oxygen vacancies in TiO27,33. We have previously reported that oxygen vacancies formed during nitrogen-doping at elevated temperature greatly contribute to improved visible-light absorption and act as the surface active sites, leading to enhanced photocatalytic water splitting activities and quantum efficiencies34. However, the in-depth structural characterisations of the doped nitrogen atoms and oxygen vacancies, and their relationship to the photocatalytic mechanism are still urgently required to inform further catalyst development and fundamental understanding.

X-ray diffraction is a well-known technique for monitoring changes in crystalline structures, but often suffers from a lack of chemical hypothesis related to photocatalysis, and in particular interrogation of the effect of defects and impurities on the derivative of lattice parameter against temperature35,36. Despite these structural investigations into the promotion of photocatalytic activity of TiO2 based materials, it is imperatively important to gain understanding on the structural-activity relationship: namely which phases are relevant to the photocatalysis and the fundamental underlying principles for the strong photocatalytic effect at different concentrations of impurities and at different temperatures.

Herein, we have presented a detailed study of the photocatalytic activity of N–TiO2 materials under visible light, and analysed structural changes using variable-temperature synchrotron X-ray powder diffraction (VT-SXPD), showing bulk reorganisation at dynamic equilibrium as a result of sub-surface oxygen vacancy formation. We report that there is a significant change in the c-axis lattice expansion in anatase under elevated temperature, resulting in a unique non-linear expansion due to the Jahn–Teller effect. However, as surface oxygen vacancies are formed at temperatures above 200 °C, a concomitant decrease in the c-axis expansion in lattice is observed, which we have shown to be correlated to photocatalytic activity. We demonstrate oxygen-vacancy mobility from the disordered surface to form ordered sub-surface vacancies, as resolved by SXPD. The technique clearly indicates that photocatalysis in anatase is greatly facilitated by large quantities of oxygen vacancies and Ti3+ beyond the surface trilayer, particularly in comparison to the inactive rutile polymorph. The inclusion of nitrogen can clearly increase the quantity of sub-surface oxygen vacancies and stabilise the anatase phase as reflected by the different degrees of observed unit-cell distortion. By doping high levels of nitrogen into anatase, a new cubic titanium oxynitride phase is identified, which provides an additional component in the fundamental understanding of the bandgap modification in N–TiO2 materials, and will inform wider hypotheses and perspectives on this system. Consequently, we present important links for the first time between structure, sub-surface oxygen vacancies, nitrogen-doping, and photocatalytic activity of anatase catalysts at various temperatures. Ultimately, we report the influence of well-characterised structural modifications on electronic phenomena in this photocatalytic hydrogen-evolution powder catalyst.

Results and discussion

Synthesis and XPS and EPR characterisation

An initial study was carried out on the commercially available P25 TiO2 powder, which consists of approximately 75%wt anatase and 25%wt rutile. The degree of nitrogen-doping was controlled by treating the P25 in NH3 flow at different temperatures. The analysis by TEM and HAADF-STEM micrographs indicates the successful formation of TiO2-based nanoparticles (Fig. S2 and S3). Elemental analysis by ICP-MS shows there is a non-linear proportionate relationship between NH3 treatment temperature and the nitrogen content at each temperature. The trend of increasing nitrogen content with temperature was also observed by XPS in the increasing N 1s signal (Fig. 1). The nitrogen-composition values yielded by elemental analysis are consistently higher than those derived from XPS. The small disagreement is attributed to differences in the penetration depth of the techniques; XPS only probes the surface, whereas elemental analysis reflects total composition. Hence, the discrepancy indicates non-homogeneous elemental distribution with respect to depth, namely lower nitrogen composition at the surface. The titanium and oxygen signals were observed as expected. Two peaks corresponding to Ti 2p3/2 and Ti 2p1/2 were observed at the binding energies of 458 eV and 464 eV, respectively, which can be attributed to the main characteristic peaks of Ti4+ in TiO2 materials. The O 1s peak at 530 eV is the characteristic peak of oxygen in the TiO2 lattice and N-doped TiO2. The N 1s XPS spectra shows clearly two characteristic peaks, located at 396 eV and 401 eV, which can be assigned to substitutional N (Ns) on O sites, and interstitial N atoms in the lattice (Ni), respectively6,9. It is known that synthesis precursors, conditions, and stoichiometry have significant impact on the resulting Ni:Ns ratio37. As summarised in Table 1, from pristine P0 to P1, ammonia treatment at (550 °C) is shown to result in 0.5%wt nitrogen-doping; this occurs primarily at the interstitial site (Ni:Ns = 2.54). For P2 (600 °C), the signal for substitutionally-doped nitrogen increases whilst the interstitial signal remains approximately unchanged (Ni:Ns = 1.16). The treatment temperature of 620 °C for P3 results in a significantly greater nitrogen composition of 4.6%wt, which significantly favours occupancy of substitutional sites (Ni:Ns = 0.39). This is in agreement with the literature, in that substitutional doping requires higher temperatures38.

Fig. 1: Electronic properties of N-doped P25.
figure1

XPS spectra of N-doped P25 TiO2 treated with ammonia flow at different temperatures: (a) Ti 2p, (b) O 1s and (c) N 1s. Photo-absorption properties characterised by (d) UV-vis absorption spectra, (e) corresponding Tauc plots and average band gaps with fitting errors obtained, and (f) Raman spectra.

Table 1 Nitrogen concentration in P25 samples by XPS and ICP-MS; substitutional nitrogen (Ns) and interstitial nitrogen (Ni) in lattice.

As has long been known, increasing the nitrogen content in anatase reduces the band gap, which is advantageous, in that the absorption profile is shifted to include more of the visible spectrum. We have shown this for P25 by UV-vis spectroscopy, in that in addition to the absorption edge at 390 nm, an additional broadened edge at 500 nm is observed for samples P1-3 (d). Higher temperature ammonia treatment leads to significant broadening, shifting the additional absorption edge to the visible and infrared regions. Tauc plots show that nitrogen-doping reduces the band gap from 3.18 eV to 1.22 eV (e), making it easier to form the active Ti3+ state, and leading to greater utilisation of the solar spectrum. The photo-excitation of these colour centres and defects as extra intra-band levels to the conduction band can therefore contribute to the visible-light absorption of the N-doped TiO25,7. This wavelength of the absorption lengthens from 390 nm to 1000 nm, resulting in near-complete absorption of the visible spectrum (380–740 nm). P2 and P3 even show quite strong absorption in the near-IR region (700–1000 nm). This was also seen by a colour change from white pristine samples to the darker, grey of the intermediate _1 and _2 samples and black _3 samples. Five major peaks that represent Eg, Eg, B1g, A1g and Eg Raman-active vibrational modes are located at 144, 196, 396, 544 and 636 cm−1, respectively (Fig. 2f), indicating that the predominant phase of the N-doped TiO2 is anatase39,40, which is consistent with the XRD results (Fig. S4). The peaks of N-doped samples exhibit weakening and broadening, due to decreasing crystallinity caused by both interstitial and substitutional nitrogen-dopant and the formation of oxygen vacancies41,42.

Fig. 2: Photocatalytic water splitting activity study of the N-doped TiO2 samples.
figure2

Photocatalytic water splitting activities over all the as-prepared N-doped TiO2 samples at 270 °C under visible-light irradiation (red: P25; blue: anatase; yellow: rutile). Error bars indicate the standard deviation.

Study of photocatalytic water splitting at elevated temperature

In order to obtain a clear understanding of the behaviours of different phases, the constituent P25 phases of anatase and rutile were treated in their pure phases with ammonia using the same procedure. Catalytic testing of all samples was carried out at 270 °C. For the undoped samples, no activity was observed under visible light. Though when the irradiation spectrum was broadened to UV/visible light, the pristine samples were shown to be photocatalytically responsive to UV light (Fig. S5). This is in agreement with the photo-absorption studies of P25 materials above. However, even under UV/visible light, the activity of the non-doped samples were reasonably low (<600 μmol g−1 h−1). On the other hand, the N-doped catalysts are highly active under visible light only (Fig. 2). In order to show that this reaction is photocatalytic in nature, control tests were carried out, which used (1) no catalyst, (2) no UV or visible light (P3 catalyst used), and (3) no catalyst and no UV or visible light. These control tests yielded zero hydrogen evolution, clearly showing that both light and the N–TiO2 catalyst are required for hydrogen evolution to occur. Furthermore, GC analysis was carried out over a multi-cycle test and a long duration test. Firstly, a P3 catalyst was reused over five 4-h batch reactions, and showed to yield H2 and O2 in a 2:1 ratio which is indicative of the stoichiometric splitting of water (Fig. S6). These observations were consistent over all cycles with no evidence of the stoichiometric consumption of the catalyst through decreasing yields. Similarly, we have also carried out a single 50-h test in which the stoichiometric H2:O2 production is shown to be highly stable over the P3 and A3 N–TiO2 catalysts (Fig. S7). In addition, no N2 was observed in either experiment, which confirms that the nitrogen dopant is not being used as a stoichiometric hole scavenger. Furthermore, it is known that that N3− electro-oxidation to N2 despite its high concentration still requires significantly higher applied potential than that of OH to take place and the nitride oxidation can only be favourable in molten medium in the total absence of water43. Hence, it is shown that the hydrogen evolution is the product of photocatalytic water splitting, and that the N–TiO2 is not consumed stoichiometrically with hydrogen yield.

The effect of polymorph and nitrogen-doping on activity will be discussed. From P0 being an inactive catalyst under visible light, the addition of nitrogen in P1, P2 and P3 leads to increasing photocatalytic activity. We attribute this activity directly to increasing concentrations of oxygen vacancies. It is widely known that nitrogen-doping in TiO2 results in the formation energy for oxygen vacancies to decrease, as well as the decrease in band gap shown by the photo-absorption studies above. These oxygen vacancies result in lattice reduction and provide unpaired electrons to be trapped for eventual photo-excitation and proton reduction via excited Ti3+ species5. Hence nitrogen-doping is known to increase the number of excitable charge carriers and provide a lower energy transition. Hence, it is predicted that there will be a correlation between the concentration of oxygen vacancies and photocatalytic hydrogen evolution. Actually, it has also been reported that the oxygen vacancies can interact with the surrounding water molecules, resulting in different adsorption and dissociation pathways44,45.

In order to deconvolute the constituent phases of P25, the N-doped rutile and anatase catalysts were analysed by electron paramagnetic resonance (EPR), which is able to observe surface active sites through the characteristic unpaired electron signal at g = 2.003 of molecular oxygen from air occupying an oxygen vacancy as O246,47,48. This signal is evidently present in both rutile and anatase materials indicating the presence of oxygen vacancies (Fig. 3). The signal was observed for the undoped R0 catalyst, which is attributed to the ease of formation of surface oxygen defects during synthesis. According to DFT calculations by Cheng and Selloni11, 3.68 eV is required to create surface oxygen vacancies on rutile (110), which is more favourable than 4.15 eV of anatase (101). The signal increases considerably following initial nitrogen-doping yielding an oxygen vacancy concentration of 2.18 × 1014 g−1 for R1. However, for higher nitrogen-composition rutile catalysts, the signal does not continue to increase significantly, with R3 not exceeding an oxygen-vacancy concentration of 2.6 × 1014 g−1 (Table 2). This indicates that the oxygen vacancies are mainly created on the local surface with no formation or migration to deeper layers, causing a limiting concentration. This again matches with the prohibitively high Vo value of 5 eV in creating sub-surface oxygen vacancy in rutile11. As predicted, the low concentration of oxygen vacancies is correlated with the poor rate of hydrogen evolution for these catalysts (<1000 μmol g−1 h−1).

Fig. 3: EPR spectra and their hydrogen evolution activity of rutile and anatase materials.
figure3

EPR spectra for (a) rutile and (b) anatase materials. c Hydrogen evolution of anatase catalysts under visible light against EPR-derived oxygen vacancy concentration. Error bars indicate the standard deviation.

Table 2 Oxygen vacancy concentrations derived from EPR spectra of rutile and anatase materials.

In contrast, the strength of the signal for anatase is clearly proportionate with the nitrogen content, indicating that the concentration of surface oxygen vacancies is governed by the concentration of dopant atoms. It is significant that the signal for anatase is over 100-times that of the highest rutile sample, reaching a concentration of 339 × 1014 g−1 for A3. At this concentration, the catalytic activity is far above any rutile catalyst, exhibiting the highest activity reported in this work (4000 μmol g−1 h−1). In fact, for anatase it is shown that a highly linear correlation exists between oxygen-vacancy concentration and photo catalytic activity (Fig. 3c). Hence, it is observed that oxygen-vacancy concentration increases with nitrogen-doping for both phases, with anatase exhibiting a much larger absolute concentration, which has a stronger non-limited dependence on nitrogen composition and a highly linear correlation with photocatalytic activity.

The mixture of anatase and rutile phases in P25 leads to an intermediate catalytic performance for P3; though interestingly, the activity of P1 and P2 are greater than A1 and A2, respectively. This improved performance is indicative of improved exciton separation by band-bending mechanisms which are often reported in rutile−anatase mixtures49,50. The higher work function of anatase is likely to result in downward bending and accommodation of electrons, facilitating hydrogen reduction. Inversely, the rutile accepts holes, facilitating oxygen evolution.

In summary, generally it has been shown that greater temperature ammonia treatment leads to higher nitrogen composition, which leads to lower formation energy and greater concentration of oxygen vacancies at a given temperature, which leads to increased photocatalytic hydrogen evolution. The catalysts P3, A3 and R3 were also tested under combined UV/visible irradiation, with the absorption of visible light increasing the photocatalytic activity by approximately 50% (Fig. S5).

In the diffraction patterns for all nitrogen-doped anatase samples, anatase is the only phase present, which shows that these levels of nitrogen-doping do not cause major structural change. Despite the failure to detect bulk structural change by XRD, there are clearly indications that oxygen-vacancy formation is facilitated by nitrogen-doping at low nitrogen content. In order to detect changes in the sub-surface or bulk over this powder, we then studied the change in lattice parameters with respect to temperature by VT-SXPD.

Anisotropic thermal expansion of anatase

A discussion into the errors associated with this study is presented in the Supplementary Information (Tables S1 and S2, Fig. S7), including aspects of temperature-calibration, structure refinement, and data handling. Error bars are plotted on all graphs; the apparent absence of error bars is due to negligible errors.

Pristine and highly-doped P25 samples, P0 and P3, were analysed by high-resolution SXPD at various temperatures under atmospheric conditions. A Rietveld refinement was used to obtain the change in lattice parameter with respect to temperature. Fitting all patterns using a biphasic anatase-rutile model yielded a good fit, Rwp < 5%, GoF < 4 (Table S3). To a certain extent, the lattice parameters exhibit typical thermal expansions reported previously in the literature35,36. The rutile phase indeed displays highly linear expansion, but interestingly the expansion of the anatase phase is distinctly non-linear (Fig. 4).

Fig. 4: Thermal expansion of pristine and highly-doped P25 powders.
figure4

a Lattice parameters of anatase and rutile phases for P0 and P3 from room temperature to 500 °C. b Linear thermal expansion coefficient α for the a-axis and c-axis of the anatase phase in P0 and P3. Error bars indicate the standard deviation.

In order to see the distinctive temperature effect on the lattice parameters of anatase, the linear thermal expansion coefficients, α, were calculated, in which x is the lattice parameter and T is the temperature (Eq. 1).

$$\alpha _x = \frac{1}{x}\left( {\frac{{{\mathrm{d}}x}}{{{\mathrm{d}}T}}} \right)$$
(1)

Both αa and αc generally increase with increasing temperature, giving typical positive thermal expansion coefficients (Fig. 4b). Excitingly, centred around 200 °C, an unusual behaviour is clearly observed. At 150 °C, αa starts to experience a dramatic decrease; meanwhile at the same temperature, αc increases. Both changes peak at 200 °C, after which the trends gradually lessen until 350 °C after which the typical linear increase in thermal expansion is again observed. This behaviour occurs again when repeated with the same sample and with other samples. The similar onset and fading temperatures of the features indicate a common mechanism for both P0 and P3 but with the latter exhibiting greater deviations, which are confirmed to be real by the distinct separation of the values including their error. We attribute this anisotropic linear thermal expansion to the structural reorganisation of anatase caused by oxygen vacancy formation.

As is well-known, in the anatase structure titanium is coordinated by six oxygen atoms coordinate sites as a Ti–O octahedron, for which tetragonal asymmetric is evident in the two distinct Ti–O bonds: four short equatorial bonds (ab-plane), and two slightly longer axial bonds (c-axis). This is in part due to inequivalent electron sharing between Ti–O, as the electron occupancy in e2 orbitals undergoes Jahn–Teller like distortions. The thermal treatment of anatase induces greater vibration and weakening in the longer axial bond, causing a higher degree of increase in αc than αa. This change in ligand environment will induce a contractive force on the equatorial bonds because the electron density of the titanium atom is sought to be maintained. As a result, the ab plane experiences an unusual decrease in thermal expansion coefficient over this temperature regime. Thus, this first mechanism accounts for the onset of anisotropic behaviour in anatase.

However, at higher temperatures of 200 °C, the inverse anisotropic behaviour is observed and the counter-distortion of which is caused by the formation of surface oxygen vacancies in the anatase phase. This is supported by the findings of our previous publication34, in which we showed by variable-temperature EPR that oxygen vacancies begin to form at 200 °C (Fig. S8). Specifically, we believe that these are ordered sub-surface oxygen vacancies in P25 as measurable by VT-SXPD, which exist within the lattice under dynamic equilibrium with surface oxygen vacancies. The under-coordinated titanium sites that result from oxygen vacancies are namely two square pyramids with the vacancy in the ab plane, TiV,eq,, and one with the vacancy in the c-axis, TiV,ax. The two electrons retained by the lattice following oxygen evolution (Oo → VO2+ + ½ O + 2 e) are known to become localised in two separate Ti 3d orbitals forming two reduced Ti3+ species51. We suggest that these three square pyramids in anatase structure, two of which are reduced (d1), distort the bulk enough to be observed here at 200 °C. So above 200 °C, fully coordinated TiO6 octahedra contribute by the first mechanism, while distorted and reduced polyhedra contribute a counter distortion by the second mechanism. These balance above 350 °C where both thermal expansion coefficients return to a linear increase (Fig. 4b).

N–TiO2 is also known to increase photocatalytic ability due to the increase in oxygen-vacancy concentration (see catalytic results at later section), which is achieved by a vastly decreased formation energy of oxygen vacancies33. As seen from the study of the temperature dependence of N–TiO2 lattice parameters in P25 (Fig. 4b), there are small but significant differences between doped and non-doped samples. It is important to note that the anisotropic temperature effect of intrinsic (undoped) oxygen-vacancy formation is clearly smaller than that of extrinsic (dopant-facilitated) oxygen-vacancy formation. Hence, the difference between the curves yields the effect of extrinsic oxygen-vacancy formation from nitrogen doping. The magnitude of the anisotropy for the doped sample is anticipated to be larger than the non-doped material for both (ab and c) axes because in substitutionally doped anatase the Ti–N bond distance is larger than Ti–O33. For interstitial doping, the interstitial nitrogen N3− can also facilitate oxygen-vacancy formation and the accompanying reduction of Ti4+ to Ti3+, which are thought to be the active centres in photocatalysis. Also, the valence band of interstitial N3− lies above that of O2−, allowing lower energy photoexcitation from diamagnetic nitrogen to Ti 3d orbitals33, which is seen in the significant reduction in band gap discussed earlier. Thus, this observation is also consistent with the effects of higher degree of oxygen-vacancy formation to counteract the Jahn-Teller distortions at and above 200 °C.

We acknowledge that the presence of water could affect the adsorptive properties of surface oxygen vacancies in the samples, as well as the relative stability of the sub-surface vacancies44,45. Hence, the ex-situ powder diffraction may not be representative of the experimental conditions. However, we have previously reported that the EPR signals for N–TiO2 materials increase in a similar way when in the presence of water vapour, liquid water, and in pure N2, which suggests that the oxygen vacancies are still, at least regenerated at elevated temperatures under the photocatalytic water splitting conditions34. However, the exact nature of the water-adsorption effect is beyond the scope of this report so will not be discussed at great length.

DFT study of oxygen vacancies in anatase

In order to rationalise the anisotropic thermal properties of anatase, a small anatase supercell (space group: P1) was modelled and optimised by ab-initio DFT simulations (see DFT in SI). The supercell was orientated with the dominant (101) surface exposed to vacuum by terminating oxygen sites. The slab contained three layers of TiO2 units labelled s (surface), ss (sub-surface), and b (bulk); the slab thickness was approximately 8.85 Å. In anatase (101) there are four oxygen environments and two titanium environments in each tri-layer stacked along the c-axis labelled O_1, O_2, O_3 and O_4 and two inequivalent titanium atoms labelled Ti_1, Ti_2 (Fig. 5). (Though relative to the vacancy, all sites are inequivalent.)

Fig. 5: The model of titanium oxide nanoparticle showing different oxygen species on surface, subsurface and bulk.
figure5

Pristine anatase (101) supercell showing assigned depth environments and inequivalent (relative to surface, not vacancy) oxygen (red) and titanium (blue) sites in each. Depth: s (surface); ss (sub-surface); b (bulk). Volume of vacuum not shown. Note, there is no Os4 due to surface termination.

The calculated lattice parameters of pristine anatase structure matched with diffraction data taken account of the temperature factors (a = b = 3.810 Å, +0.63%; c = 9.440 Å, −0.68%). Oxygen-vacancy structures were optimised by removing atoms from Os1, Os2, Os3 and Oss3 (Table 3); the vacancy structures will be referred to as VOs1, VOs2, VOs3 and VOss3, respectively.

Table 3 DFT results showing the absolute energy, relative energy to minimum structure VOss3, and changes in local bond distances and bond angles relative to the pristine anatase (101) slab.

It is interesting to note from the optimised slab energies that the lowest energy vacancy-structure is that of the ordered sub-surface vacancy (VOss3) rather those with surface vacancies (VOs1, VOs2, VOs3). The difference in stability between the two lowest energy structures (VOs3 and VOss3) is 0.37 eV. Anatase (101) has a relatively low surface energy compared to other facets, which requires more energy to create surface vacancies. Consequently, in contrast to other TiO2 facets, as well as other oxides, we and others have shown that sub-surface oxygen-vacancy formation is more energetically favourable. This was also demonstrated by Cheng and Selloni12 who reported a stability difference between these sites of 0.46 eV, corresponding to a relative probability of a surface vacancy of 4.0 × 10−9 and 1.6 × 10−3 at 300 K and 900 K, respectively. Their results support our simulations that the lowest energy vacancy-structure is yielded by removing the Oss3 sub-surface oxygen than surface oxygen. In addition, they demonstrated that the next-deeper site of Ob3 is similarly stable to Oss3, and in contrast that all sub-surface and bulk vacancies in rutile are highly disfavoured. It is the stable sub-surface/bulk oxygen vacancies that are believed to be crucial in the superior photoactivity of anatase (101), as it allows the mobility of vacancies away from the surface, delimiting the total concentration of vacancies. Indeed, according to the calculations by Fiscaro et al.52, oxygen vacancies can travel along the P1 c-axis from a higher energy Os1 vacancy to the global-minimum vacancy at Oss3. Elsewhere, the surface to sub-surface (Os1 → Oss3) oxygen-diffusion activation energy is calculated to be 67 kJ mol−1 11, which matches well with our EPR-derived activation energy of 63 kJ mol−1 (Fig. S9).

We acknowledge that our calculations use the conventional PBE functional53 with a dispersion correction scheme54, which lack some of the computationally intensive and complex recent improvements in the modelling of TiO255. With respect to hybrid potentials, in a study by Li et al.56, they showed that a PBE functional and a hybrid functional yielded similar results and identical conclusions. As for the Hubbard factor, it has been reported that standard DFT can adequately predict structural and optical properties in a range of TiO2 materials57 and specifically for the anatase (101) surface58. In addition, elsewhere it has been conceded that a universal value for U cannot reproduce TiO2 properties, often leading to worsening of the accuracy of the crystal structure59. The energies of the various optimised structures and sites reported in this work agree with previous reports, and support our observations by EPR, SXPD and photocatalytic activity, which have been discussed above. Hence, our simple and computationally efficient calculations can be considered sufficient for this system.

The structural effects of the Oss3 vacancy will now be interrogated, as we show here significant reorganisation occurs in the surrounding atoms in order to stabilise the vacancy. Interestingly, the Ti–Ti distances in the ab-plane are elongated (+0.714 Å) causing ab-expansion; meanwhile TiO2 along with c-axis is contracted (−0.152 Å) causing c-contraction. It is these changes that we also observed in the anisotropic thermal expansion activity due to oxygen vacancy formation above 200 °C by the SXPD. The low energy for the sub-surface oxygen-vacancy formation can facilitate oxygen-vacancy formation and mobility, as indicated by EPR (Fig. 3), resulting in highly efficient surface photocatalytic activity. These distortions will then counteract the c-axis thermal expansion in bulk with increasing temperature. We also note that the low energy sub-surface VOss3 structure yields a highly distorted O1–TiO2 moiety (Δθ = +72.7°) (Table 3). Further explanation of this structural distortion is discussed in Fig. S10.

Crystallographic techniques are generally unable to detect disordered surface oxygen vacancies; however, the surface oxygen vacancies in nanocrystalline TiO2 anatase (101) structure are clearly unstable with respect to sub-surface ordered oxygen vacancies. Hence significant oxygen mobility from sub-surface sites to surface vacancy sites under dynamic equilibrium is anticipated. This accounts for subtle structural change in the sub-surface lattice which has been observed by VT-SXPD as anisotropic thermal expansion of the anatase phase in P25. This can be directly correlated to the oxygen-vacancy concentration of the anatase phase, nitrogen doping and temperature.

This combined study by DFT and VT-SXPD has revealed the significant ‘storage’ of sub-surface vacancies formed by fast oxygen transfer between surface sites in anatase at elevated temperature, which are important for interaction with excitons during photo-excitation in the whole structure. We suggest that the large sub-surface oxygen-vacancy storage and facile oxygen mobility clearly indicates that the anatase phase is a superior photocatalyst for water splitting to H2 and O2, especially compared with rutile which only has limited and immobile surface vacancies12. However, catalysis is highly facet-sensitive and site-sensitive and is unlikely the same for both facile reduction and oxidation reactions. It is still not conclusively known it is not yet clear whether surface or lattice oxygen vacancies (sub-surface) play the key role in catalysis over N–TiO2. It is important to note that the anisotropic thermal expansion was observed in both pure TiO2 and N–TiO2. These computational results also indicate that it is favourable for sub-surface oxygen vacancy formation in pure TiO2. But, we have also shown that the nitrogen-doping of N–TiO2, either as an interstitial or substitutional dopant, can narrow the band gap and increase the concentration of the oxygen vacancies, resulting in increased photocatalytic water splitting by visible light. This can demonstrate the unique roles of N doping in the N–TiO2 for the photocatalytic water splitting at elevated temperature.

Here the in-depth structural study of rutile, anatase and mixed phase P25, with and without nitrogen-doping, by variable-temperature synchrotron X-ray powder diffraction (VT-SXPD) indicates that there exists a direct correlation between the anisotropic thermal expansion in lattice parameters and activity with respect to temperature.

A new titanium oxynitride structure

High-resolution SXPD of the pure anatase and pure rutile samples was carried out at BL02B2 at SPring-8, Japan. The patterns for the rutile samples that were nitrogen-doped at different temperatures did not significant differences, only small non-systematic variation in lattice parameter and increasing particle size with increased temperature conditions due to microcrystalline sintering (Fig. S11). Thus, the rutile phase in P25 is a minor or spectator phase during nitrogen-doping. Apart from the low level of nitrogen-doping in anatase (N–TiO2), by adapting the same doping procedure, we show that it was possible to derive the structure in a high level of nitrogen doping at high temperature ammonia treatments. On the other hand, pure anatase and P25 materials exhibited additional peaks that are consistent with a cubic Fm\(\overline 3\)m rock-salt phase. As discussed earlier in this report, XPS suggested the presence of both interstitial and substitutional nitrogen in this sample (Fig. 1). These reflections grew in intensity as the doping temperature was increased for pure anatase and P25 materials, hence are correlated with nitrogen composition. The phase strongly resembled titanium nitride Ti3+N3− which is formed by nitridation of anatase accompanied by oxygen evolution. For very high temperature nitridation of anatase at 750 °C (A4), the peaks become more dominant and narrower due to microcrystalline sintering (Fig. 6). However, the A4 TiN reflections were shifted to low angle in comparison to the low nitrogen-doped materials, indicating an expanded unit cell. Of additional note, the presence of rutile was not observed in the diffraction patterns, despite the prolonged thermal treatment at 750 °C being sufficient for the conversion of anatase into rutile which relative to anatase is the more thermodynamically stable polymorph, as previously seen in XRD studies30.

Fig. 6: SXRD patterns of anatase with different N contents.
figure6

SXPD patterns of anatase samples A0–A3, as well as a high-temperature sample A4 prepared at 750 °C. Intensities normalised due to different data-collection parameters.

This assumption was applied to a biphasic Rietveld refinement of A4 comprising a tetragonal I41/amd anatase phase and a cubic Fm\(\overline 3\)m titanium nitride phase. The model yielded chemically reasonable lattice parameters for anatase (aana = 3.7852 Å, cana = 9.5106 Å); though the value for ‘titanium nitride’ phase (aTiN = 4.1843 Å) was actually lower than the known lattice parameter in pure phase (4.235 Å60). This unit cell is notably more similar to that of Fm\(\overline 3\)m titanium(II) oxide (4.184 Å61) which is formed at high temperatures from titanium(IV) oxide and titanium metal. Overall the fitting was reasonable (Rwp = 3.38%, GoF = 1.98) (Table S3). However, though the Ti3+ occupancy refined to near unity (0.9998), the occupancy of the nitrogen atom refined to a chemically unreasonable value of 1.48 (see Fourier difference electron density map for unity occupancy in Fig. S12). This is due to nitrogen being in the N3− anion in the structure rather than the neutral atom used (10 electrons rather than 7) since the fitting depends critically on both electron density of atom and site occupancy. As the atomic scattering factors for N3− are unavailable in the refinement programme, the isoelectronic O2− was used instead (slightly differing electron density). The occupancy of this atom then refined to a more chemically sensible value of 1.01 (Rwp = 3.39%, GoF = 1.99).

The phase information derived from the Rietveld refinement was applied to the observed structure factors in order to synthesise electron density maps (Fig. 7a). The rock-salt structure of highly electron dense titanium Ti3+ and lower-density nitrogen N3− is expected. However, unexpected electron density is also observed at the tetrahedral hole positions (0.25, 0.25, 0.25) (Wyckoff: 8c). This is more clearly observed in the Fourier difference electron density map, shown in 2D and 3D (Fig. 7b, c). Introducing a neutral oxygen atom into the tetrahedral hole further improves the fit (Rwp = 3.35%, GoF = 1.96) (d) and the Fourier difference map becomes more homogeneous (Fig. S13). The resulting fluorite structure is displayed in Fig. 8e. The occupancy of the site is 0.03 resulting in the formula Ti3+0.95N3−1.07O0.03, which has a net charge of −0.38 e. Refinements yield slightly better fits when titanium atoms are modelled as tetravalent Ti4+ rather than trivalent Ti3+ showing a degree of charge transfer from Ti to O when O is interstitially added. It is therefore conceivable that significant N3− inclusion in the previously discussed N–TiO2 anatase phase by high temperature ammonia nitridation generates significant concentrations of Ti3+ and VO2+, which can create the new nitride ‘Ti3+N3−’ phase with residual O to occupy the interstitial sites. Although the main phase corresponds to anatase for the former and nitride for the latter, both can thus be regarded as oxynitride structures.

Fig. 7: Phase identification of TiNOx by Rietveld refinement.
figure7

Electron density maps of the TiNOx unit cell: 2D cross-sections of electron density derived from the Fourier transform of (a) Fobs at one unit cell length a from the origin along (011); (b) Fdiff (=FobsFcalc) at 0.25a along (001); (c) iso-surface of electron density at 0.1 (red); grey: titanium, blue: nitrogen. d Fitting of Rietveld refinement of A4 at room temperature consisting of an anatase phase and a titanium oxynitride phase: nitrogen atom is modelled as O2− and interstitial oxygen anion modelled as O atom at tetrahedral hole. e Corresponding structure solution for TiNOx: blue: titanium, red: nitrogen, white: oxygen.

Fig. 8: Crystallographic variable temperature analysis of A4.
figure8

a In-situ VT-SXPD patterns; (bd) enlarged regions showing the decomposition of TiNOx and increase in anatase intensity; (e) intensity of anatase (101) and TiN (200) plotted against temperature (negligible standard deviation not plotted).

VT-SXPD data was also collected on beamline BL02B2, SPring-8 for the thermal oxidation of A4 in air from room temperature to 580 °C. The sample was composed of 67.8%wt anatase (N-TiO2) and 32.2%wt TiNOx phases. The TiNOx is stable until 240 °C, after which the peaks of this structure decrease in intensity until the complete disappearance of any reflections by 520 °C (Fig. 8) (refined values for powder composition shown in Fig. S14a). Anatase is shown to be the dominant decomposition product of TiNOx phase in air by losing nitrogen and gaining oxygen, shown by the highly correlated increase in the intensity of the anatase phase (likely the reverse of the process that formed this phase, i.e., nitridation of anatase by ammonia). Indeed, by the same refinement it is shown that the occupancy of interstitial oxygen from refinement is indeed gradually increasing before the phase conversion (Fig. S14c). Thus, this clearly shows that the interchangeable phase between anatase and nitride is dependent on nitrogen and oxygen availability in the oxynitride structures at elevated temperature.

According to the catalysis study reported in the next section, the modified oxynitride structure of TiN can also contribute to the high photocatalytic activity under visible light of highly nitrogen-doped composite TiO2 materials.

Temperature dependence of catalytic activity

All catalytic data up to this point has been carried out at 270 °C. Here, the temperature dependence of photocatalytic activity of all nitrogen-doped catalysts were studied at different temperatures. The effect of temperature was first investigated over samples of highest nitrogen-doping, A3, R3 and P3. For A3 and P3 there is a clear onset of photocatalytic activity at 200 °C with exponential increase in the rate under visible light with temperature (Fig. 9). Meanwhile, the activities of R3, although slightly increased at elevated temperatures, remained at a low level. This onset in activity coincides with the counter Jahn–Teller mechanism shown in Fig. 4b attributed to the onset of oxygen-vacancy formation in the asymmetric nitrogen-doped anatase phase at 200 °C. Indeed, the activation barrier for hydrogen evolution has been calculated to be 60.6 kJ mol−1, which is in good agreement with the activation barrier for oxygen-vacancy formation of 62.5 kJ mol−1, which we derived from variable-temperature EPR (Figs. S8 and S9). In addition this formation energy is in good agreement with the reported activation energy for oxygen-vacancy mobility in anatase of 67.5 kJ mol−1 11, which indicates that the formation of oxygen vacancies in anatase is limited by the diffusion of vacancies into the sub-surface.

Fig. 9: Photocatalytic water splitting activity study of the N-doped TiO2 samples.
figure9

Photocatalytic water-splitting activities over P3, A3 and R3 photocatalysts at different temperatures under visible-light illumination (red: P25; blue: anatase; yellow: rutile). Error bars indicate the standard deviation.

It is clear that the photocatalytic performance is clearly found to be strongly dependent on the nitrogen-doping levels and sub-surface oxygen-vacancy concentration, since the photocatalytic activities of the nitrogen-doped P25 and anatase samples significantly increase with greater nitrogen-doping; meanwhile all nitridation temperatures for nitrogen-doped rutile exhibited similar activities due to similar oxygen-vacancy concentrations as shown in the EPR results.

At low N-doping, the interstitial/substitutional N3− in N–TiO2 increases the concentration of VO2+ and Ti3+ and also reduces the band gap to the visible light regime, as previously demonstrated. Although it is beyond the scope of this study how one could feasibly control the ratio of interstitial and substitutional doping, Lynch37 and Zhang38 are amongst the researchers to report fine control. Nevertheless, the formation of H2 is attributed to H+ reduction of water on surface excited electrons trapped at surface Ti3+, and O2 formation attributed to oxidation of hydroxyl ions (OH) from water over surface VO2+ during photolysis, which are in equilibrium with the sub-surface/bulk defects in such oxynitride structure. Similarly, at high N loading, OH from water over unfilled interstitial sites in TiNOx phase can be oxidised to O2 and provide electrons to regenerate Ti4+ to Ti3+ after H2 formation from H+ reaction allowing the same pathway for photoexcitation in band gap modification in the oxynitride structures. The dissociated H+ and OH ions that are adsorbed on the surface, the concentrations of which are dependent on pH, can generate a local electric field, which prolongs the lifetime of surface excitons, as we have confirmed by time-resolved photoluminescence spectroscopy (Fig. S15). Therefore, the enhanced photocatalytic performances are attributed to the suppressed electron-hole recombination process, which we have discussed in more detail elsewhere34. We also postulate that the anatase-oxynitride mixture may benefit from band-bending effects, which result in stronger charge separation, greater exciton lifetime and enhanced catalytic activity, as has been shown for other anatase systems49,50. Like rutile, the work function of titanium nitride is lower than anatase. This indicates that the titanium-nitride-like oxynitride phase will confer similar charge separation as discussed for P1 and P2 samples earlier here.

The use of elevated temperature and nitrogen-doping have been empirically shown to increase TiO2 photocatalytic activity, with the latter broadening the absorption profile from UV to the near-IR region51. In a recent investigation34 and review62 of ours, the use of elevated temperature was reported to facilitate the oxygen-vacancy regeneration of nitrogen-doped TiO2 photocatalysts, and enhance the photo-generated charge separation via surface polarisation, both of which contribute to improved kinetics. It was also shown that elevated temperature is a more effective method of increasing H+ concentration than varying the pH of the water. Though elevated temperatures may seem impractical and cost-inefficient, we reported a complete and efficient visible-light-driven water splitting system, in which only light is required to reach the high temperature by using an optical floating-zone light furnace. This method and other light concentrator configurations, primarily compound parabolic cylinder reflectors63, can provide enhanced light irradiation and temperature for small/medium size applications, which include photo-voltaic cells64, photomicroreactors65, photocatalytic waste degradation66,67,68, and photocatalytic hydrogen evolution by TiO2 materials34,69, with fully sunlight dependent hydrogen evolution photocatalysts reported70.

With respect to the photocatalytic configuration, other preliminary study are being carried out to further improve the efficiency of this process. The possibility of using water vapour instead of liquid water, which possesses lower heat capacity and yields lower pressures at a given temperature, is highly promising. In addition it makes the reaction more practical, controllable and easier to operate. Further studies on this subject will be carried out.

In summary, an unusual anisotropic thermal expansion of anatase has been observed at 150 °C, namely that the c-axis exhibits increased thermal expansion while that of the a-axis decreases. This has been attributed to the increased weakening of the long Ti–Oax bond. At 200 °C the phenomenon is countered which is attributed to the Jahn–Teller contraction of 5-fold coordinated Ti3+ polyhedra formed by oxygen vacancies. The orthogonal distortions appears to balance by 350 °C. For low levels of nitrogen-doping in N–TiO2 anatase the inclusion of nitrogen atoms, either as an interstitial or substitutional dopant, can increase the concentration of oxygen vacancies and Ti3+, and narrow the band gap resulting in photocatalytic water splitting by visible light. At high N-doping, a new phase of cubic titanium nitride with interstitial oxygen at high temperature ammonia decomposition on anatase is for the first time identified. Both structures can be described as oxynitrides, are crystallographic related, and share the same photocatalytic mechanism. They are active and kinetically stable in photocatalysis at elevated temperatures of below 300 °C, in comparison to the photocatalytically inert rutile.

Methods

Materials

Analytical grade fine powder titanium dioxide (Degussa P25, 75% anatase, 25% rutile); Anatase TiO2 (IshiharaSangyo, Japan); Rutile TiO2 (99.995%, Sigma-Aldrich); Ammonia gas (anhydrous, BOC) were used without further purification.

Synthesis of N-doped TiO2

Phase pure anatase TiO2 powder (denoted as A0) was nitrogen-doped using an ammonia treatment by annealing under ammonia flow at temperatures between 550 °C and 620 °C for 8 h. The degree of nitrogen doping was controlled by the temperature of the reaction which was set at 550 °C, 600 °C and 620 °C yielding samples denoted as A1, A2 and A3, respectively. Likewise, the ammonia treatment at different temperatures was also performed on rutile TiO2 (R0) and P25 TiO2 (P0) powder samples. R0 was treated with ammonia flow at 650 °C, 700 °C and 750 °C, which are denoted as R1, R2 and R3, while P0 at 550 °C, 600 °C and 620 °C, denoted as P1, P2 and P3.

Photocatalytic water-splitting activity tests

The photocatalytic performances were evaluated by measuring the amount of hydrogen and oxygen evolved from the water splitting reaction, which were carried out in a closed 25 mL stainless-steel autoclave equipped with two quartz windows (10 mm in diameter, 18 mm in thickness). Typically, 5 mg of photocatalyst was added to 10 mL of Milli-Q H2O under vigorous magnetic stirring (750 rpm); after being sealed the system was pressurised with 2 bar of Ar gas. The reactor was heated to the designated temperature, after which a tungsten light (70 W, Glamox Professional 2000) was applied through the quartz windows to provide visible-light irradiation. After 2 h of reaction, the autoclave was cooled naturally to room temperature. The amounts of hydrogen and oxygen were measured by gas chromatography (GC) equipped with thermoconductivity detectors (TCD).

Thermal expansion of anatase, N-anatase, P25 and N-P25

Synchrotron X-ray powder diffraction (SXPD) data was collected at the High Resolution Powder Diffraction beamline I11 at Diamond Light Source, UK (DLS)71. The energy was specified as 15 keV, with the wavelength calculated to be 0.824875(1) Å (~15.031 keV) and the angular zero-error to be +0.004675° in 2θ by using a NIST silicon standard. Samples of P25 and N-P25 were loaded into borosilicate capillaries of diameter 0.5 mm, and analysed by Debye-Sherrer geometry using a multi-analyser crystal (MAC) diffractometer over an angular range of 2–150° in 2θ over a 30-min exposure period. Scans were conducted at room temperature and 50 °C intervals between 100 °C and 500 °C. Heating was conducted using a hot-air blower at 10 °C min−1, with an equilibration time of 2 min allowed before each scan. The calibration of the sample temperature was conducted prior to investigation by using the well-known thermal expansion of platinum72 (Tables S1 and S2, Fig. S1). The experiment was repeated using N-P25 (P3).

Phase analysis of high temperature synthesis

SXPD data of pristine and nitrogen-doped anatase, rutile and P25 were also collected at beamline BL02B2 at SPring-8, Japan73. Samples were loaded into borosilicate capillaries of diameter 0.5 mm, and analysed by Debye-Sherrer geometry using a position-sensitive MYTHEN detector over an angular range of 4–78° in 2θ over a 10-min exposure period (sum of 2 × 5 min). The beam energy was shown to be 17.98029(9) keV by refinement of a ceria standard, with an angular zero-error of −0.0015°. Each sample was scanned at room temperature and at high temperature 500 °C.

A high degree of nitrogen-doping was achieved for anatase (A4) by increasing the nitrogen temperature to 750 °C from the previous highest temperature of 650 °C. The sample was scanned over an exposure time of 2 × 100 s at room temperature and between 60 °C and 580 °C at 20 °C intervals. All structural refinements were carried out in TOPAS74, and VESTA75 was used for electron-density visualisation.

DFT calculations

Spin-polarised density function theory (DFT) calculations were performed by using the Vienna Ab-initio Simulation Package (VASP) programme76,77 within the projector-augmented wave (PAW)78 to explore geometries and electronic properties of the (101) facet of TiO2 anatase. The exchange-correlation interactions were described with the generalised gradient approximation (GGA)79 in the form of the Perdew, Burke and Ernzernhof (PBE) functional53. The kinetic energy cut-off for the plane-wave basis set was set as 450 eV, and the distance of vacuum layer was set to be more than 15 Å, which is sufficiently large to avoid interlayer interactions. The Grimme van-der-Waals/dispersion-correction scheme DFT-D354 was applied on the anatase TiO2 (101) surface. The pristine slab contained three TiO2 layers, totalling 108 atoms: 36 Ti and 72 O atoms. The electronic self-consistent field (SCF) tolerance was set to 10−5 eV. Fully relaxed geometries and lattice parameters were obtained by optimising all atomic positions until the Hellmann–Feynman forces were less than 0.02 eV Å−1. The k-points samplings with a gamma-centred Monkhorst–Pack scheme80 were 8 × 8 × 1 for structural optimisations.

Data availability

The authors declare that the data supporting the findings of this study are available within the paper and its supplementary information files. All relevant data are available from the authors.

References

  1. 1.

    Ani, I. J., Akpan, U. G., Olutoye, M. A. & Hameed, B. H. Photocatalytic degradation of pollutants in petroleum refinery wastewater by TiO2- and ZnO-based photocatalysts: recent development. J. Clean. Prod. 205, 930–954 (2018).

    CAS  Article  Google Scholar 

  2. 2.

    Verbruggen, S. W. TiO2 photocatalysis for the degradation of pollutants in gas phase: from morphological design to plasmonic enhancement. J. Photochem. Photobiol. C. Photochem. Rev. 24, 64–82 (2015).

    CAS  Article  Google Scholar 

  3. 3.

    Wang, Z. & Lang, X. Visible light photocatalysis of dye-sensitized TiO2: the selective aerobic oxidation of amines to imines. Appl. Catal. B Environ. 224, 404–409 (2018).

    CAS  Article  Google Scholar 

  4. 4.

    Asahi, R., Morikawa, T., Ohwaki, T., Aoki, K. & Taga, Y. Visible-light photocatalysis in nitrogen-doped titanium oxides. Science 293, 269–271 (2001).

    CAS  PubMed  Article  Google Scholar 

  5. 5.

    Livraghi, S. et al. Origin of photoactivity of nitrogen-doped titanium dioxide under visible light. J. Am. Chem. Soc. 128, 15666–15671 (2006).

    CAS  PubMed  Article  Google Scholar 

  6. 6.

    Di Valentin, C., Pacchioni, G., Selloni, A., Livraghi, S. & Giamello, E. Characterization of paramagnetic species in N-doped TiO2 powders by EPR spectroscopy and DFT calculations. J. Phys. Chem. B 109, 11414–11419 (2005).

    PubMed  Article  CAS  Google Scholar 

  7. 7.

    Wang, J. et al. Origin of photocatalytic activity of nitrogen-doped TiO2 nanobelts. J. Am. Chem. Soc. 131, 12290–12297 (2009).

    CAS  PubMed  Article  Google Scholar 

  8. 8.

    Ganduglia-Pirovano, M., Hofmann, A. & Sauer, J. Oxygen vacancies in transition metal and rare earth oxides: current state of understanding and remaining challenges. Surf. Sci. Rep. 62, 219–270 (2007).

    ADS  CAS  Article  Google Scholar 

  9. 9.

    Jiang, J. et al. In situ Ti3+/N-codoped three-dimensional (3D) urchinlike black TiO2 architectures as efficient visible-light-driven photocatalysts. Ind. Eng. Chem. Res. 56, 7948–7956 (2017).

    CAS  Article  Google Scholar 

  10. 10.

    Diebold, U. The surface science of titanium dioxide. Surf. Sci. Rep. 48, 53–229 (2003).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Thomas, A. G. et al. Comparison of the electronic structure of anatase and rutile TiO2 single-crystal surfaces using resonant photoemission and x-ray absorption spectroscopy. Phys. Rev. B 75, 035105 (2007).

    ADS  Article  CAS  Google Scholar 

  12. 12.

    Cheng, H. & Selloni, A. Surface and subsurface oxygen vacancies in anatase TiO2 and differences with rutile. Phys. Rev. B 79, 092101 (2009).

    ADS  Article  CAS  Google Scholar 

  13. 13.

    Zhu, T. & Gao, S.-P. The stability, electronic structure, and optical property of TiO2 polymorphs. J. Phys. Chem. C. 118, 11385–11396 (2014).

    CAS  Article  Google Scholar 

  14. 14.

    Liu, Z. et al. Nanostructured TiO2(B): the effect of size and shape on anode properties for Li-ion batteries. Prog. Nat. Sci. Mater. Int. 23, 235–244 (2013).

    Article  Google Scholar 

  15. 15.

    Sato, H., Endo, S., Sugiyama, M., Kikegawa, T. & Shimomura, O. Baddeleyite-type high-pressure phase of TiO2. Science 251, 786–788 (1991).

    ADS  CAS  PubMed  Article  Google Scholar 

  16. 16.

    Dubrovinskaia, N. A. et al. Experimental and theoretical identification of a new high-pressure TiO2 polymorph. Phys. Rev. Lett. 87, 275501 (2001).

    CAS  PubMed  Article  Google Scholar 

  17. 17.

    Dubrovinsky, L. S. et al. The hardest known oxide. Nature 410, 653–654 (2001).

    ADS  CAS  PubMed  Article  Google Scholar 

  18. 18.

    Mattesini, M. et al. Cubic TiO2 as a potential light absorber in solar-energy conversion. Phys. Rev. B 70, 115101 (2004).

  19. 19.

    Mattesini, M. et al. High-pressure and high-temperature synthesis of the cubic TiO2 polymorph. Phys. Rev. B 70, 212101 (2004).

    ADS  Article  CAS  Google Scholar 

  20. 20.

    Niu, M., Cheng, D. & Cao, D. Fluorite TiO2(111) surface phase for enhanced visible-light solar energy conversion. J. Phys. Chem. C. 118, 20107–20111 (2014).

    CAS  Article  Google Scholar 

  21. 21.

    Akimoto, J. et al. Topotactic oxidation of ramsdellite-type Li0.5TiO2, a new polymorph of titanium dioxide: TiO2(R). J. Solid State Chem. 113, 27–36 (1994).

    ADS  CAS  Article  Google Scholar 

  22. 22.

    Latroche, M., Brohan, L., Marchand, R. & Tournoux, M. New hollandite oxides: TiO2(H) and K0.06TiO2. J. Solid State Chem. 81, 78–82 (1989).

    ADS  CAS  Article  Google Scholar 

  23. 23.

    Clatworthy, E. B. et al. Enhanced photocatalytic hydrogen evolution with TiO2–TiN nanoparticle composites. J. Phys. Chem. C. 123, 3740–3749 (2019).

    CAS  Article  Google Scholar 

  24. 24.

    Ishii, S., Shinde, S. L., Jevasuwan, W., Fukata, N. & Nagao, T. Hot electron excitation from titanium nitride using visible light. ACS Photon. 3, 1552–1557 (2016).

    CAS  Article  Google Scholar 

  25. 25.

    Barragan, A. A. et al. Photochemistry of plasmonic titanium nitride nanocrystals. J. Phys. Chem. C. 123, 21796–21804 (2019).

    CAS  Article  Google Scholar 

  26. 26.

    Sait, R., Govindarajan, S. & Cross, R. Nitridation of optimised TiO2 nanorods through PECVD towards neural electrode application. Materialia 4, 127–138 (2018).

    Article  Google Scholar 

  27. 27.

    Yang, X., Li, C., Yang, B., Wang, W. & Qian, Y. Optical properties of titanium oxynitride nanocrystals synthesized via a thermal liquid–solid metathesis reaction. Chem. Phys. Lett. 383, 502–506 (2004).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    Satou, M. et al. Coating films of titanium nitride prepared by ion and vapor deposition method. Jpn. J. Appl. Phys. 24, 656 (1985).

    ADS  CAS  Article  Google Scholar 

  29. 29.

    Kharitonov, A., Kharintsev, S. & Kharintsev, S. Tunable optical materials for multi-resonant plasmonics: from TiN to TiON [Invited]. Opt. Mater. Express 10, 513–531 (2020).

    ADS  CAS  Article  Google Scholar 

  30. 30.

    Zhang, Z. et al. Photocatalytic activities of N-doped nano-titanias and titanium nitride. J. Eur. Ceram. Soc. 29, 2343–2353 (2009).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Yoo, J. B. et al. Titanium oxynitride microspheres with the rock-salt structure for use as visible-light photocatalysts. J. Mater. Chem. A 4, 869–876 (2016).

    CAS  Article  Google Scholar 

  32. 32.

    Do, H. et al. Structure and property of epitaxial titanium oxynitride grown on MgO(001) substrate by pulsed laser deposition. Surf. Coat. Technol. 214, 91–96 (2013).

    CAS  Article  Google Scholar 

  33. 33.

    Di Valentin, C. et al. N-doped TiO2: theory and experiment. Chem. Phys. 339, 44–56 (2007).

    Article  CAS  Google Scholar 

  34. 34.

    Li, Y. et al. Photocatalytic water splitting by N-TiO2 on MgO (111) with exceptional quantum efficiencies at elevated temperatures. Nat. Commun. 10, 4421 (2019).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  35. 35.

    Hummer, D. R., Heaney, P. J. & Post, J. E. Thermal expansion of anatase and rutile between 300 and 575 K using synchrotron powder X-ray diffraction. Powder Diffr. 22, 352–357 (2007).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Ling, W., Wang, H.-J. & Li, T. In situ high temperature X-ray diffraction study of anatase and rutile. Acta Phys. Sin. 62, 146402 (2013).

    Google Scholar 

  37. 37.

    Lynch, J. et al. Substitutional or interstitial site-selective nitrogen doping in TiO2 nanostructures. J. Phys. Chem. C. 119, 7443–7452 (2015).

    CAS  Article  Google Scholar 

  38. 38.

    Zhang, Z. et al. Nitrogen-doped titanium dioxide visible light photocatalyst: spectroscopic identification of photoactive centers. J. Catal. 276, 201–214 (2010).

    CAS  Article  Google Scholar 

  39. 39.

    Savio, A. K. P. D. et al. Environmentally effective photocatalyst CoO–TiO2 synthesized by thermal precipitation of Co in amorphous TiO2. Appl. Catal. B Environ. 182, 449–455 (2016).

    CAS  Article  Google Scholar 

  40. 40.

    Ren, Z. et al. TiO2/C composites nanorods synthesized by internal-reflux method for lithium-ion battery anode materials. Mater. Lett. 117, 124–127 (2014).

    CAS  Article  Google Scholar 

  41. 41.

    Liu, X. et al. Fabrication of 3D flower-like black N-TiO2-x@MoS2 for unprecedented-high visible-light-driven photocatalytic performance. Appl. Catal. B Environ. 201, 119–127 (2017).

    CAS  Article  Google Scholar 

  42. 42.

    Zhang, K. et al. Self-floating amphiphilic black TiO2 foams with 3D macro-mesoporous architectures as efficient solar-driven photocatalysts. Appl. Catal. B Environ. 206, 336–343 (2017).

    CAS  Article  Google Scholar 

  43. 43.

    Ito, Y. & Goto, T. Electrochemistry of nitrogen and nitrides in molten salts. J. Nucl. Mater. 344, 128–135 (2005).

    ADS  CAS  Article  Google Scholar 

  44. 44.

    Zhao, W.-N. & Liu, Z.-P. Mechanism and active site of photocatalytic water splitting on titania in aqueous surroundings. Chem. Sci. 5, 2256–2264 (2014).

    CAS  Article  Google Scholar 

  45. 45.

    Hussain, H. et al. Structure of a model TiO2 photocatalytic interface. Nat. Mater. 16, 461–466 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  46. 46.

    Tryba, B. et al. Influence of an electronic structure of N-TiO2 on its photocatalytic activity towards decomposition of acetaldehyde under UV and fluorescent lamps irradiation. Catalysts 8, 85 (2018).

    Article  CAS  Google Scholar 

  47. 47.

    Yang, G., Jiang, Z., Shi, H., Xiao, T. & Yan, Z. Preparation of highly visible-light active N-doped TiO2 photocatalyst. J. Mater. Chem. 20, 5301–5309 (2010).

    CAS  Article  Google Scholar 

  48. 48.

    Misra, S. K. et al. Study of paramagnetic defect centers in as-grown and annealed TiO2 anatase and rutile nanoparticles by a variable-temperature X-band and high-frequency (236 GHz) EPR. J. Magn. Magn. Mater. 401, 495–505 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  49. 49.

    Ohno, T., Tokieda, K., Higashida, S. & Matsumura, M. Synergism between rutile and anatase TiO2 particles in photocatalytic oxidation of naphthalene. Appl. Catal. Gen. 244, 383–391 (2003).

    CAS  Article  Google Scholar 

  50. 50.

    Nagaraj, B. & Devi, L. G. Silver metalized mixed phase manganese-doped titania: Variation of electric field and band bending within the space charge region with respect to the silver content. J. Mol. Catal. Chem. 390, 142–151 (2014).

    CAS  Article  Google Scholar 

  51. 51.

    Schneider, J. et al. Understanding TiO2 photocatalysis: mechanisms and materials. Chem. Rev. 114, 9919–9986 (2014).

    CAS  Article  Google Scholar 

  52. 52.

    Fisicaro, G. et al. Wet environment effects for ethanol and water adsorption on anatase TiO2 (101) surfaces. J. Phys. Chem. C. 124, 2406–2419 (2020).

    CAS  Article  Google Scholar 

  53. 53.

    Perdew, J. P., Ernzerhof, M. & Burke, K. Rationale for mixing exact exchange with density functional approximations. J. Chem. Phys. 105, 9982–9985 (1996).

    ADS  CAS  Article  Google Scholar 

  54. 54.

    Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).

    ADS  Article  CAS  Google Scholar 

  55. 55.

    Orhan, O. K. & O’Regan, D. D. First-principles Hubbard U and Hund’s J corrected approximate density functional theory predicts an accurate fundamental gap in rutile and anatase TiO2. Phys. Rev. B 101, 245137 (2020).

    ADS  CAS  Article  Google Scholar 

  56. 56.

    Li, H., Guo, Y. & Robertson, J. Calculation of TiO2 surface and subsurface oxygen vacancy by the screened exchange functional. J. Phys. Chem. C. 119, 18160–18166 (2015).

    CAS  Article  Google Scholar 

  57. 57.

    Samat, M. H., Ali, A. M. M., Taib, M. F. M., Hassan, O. H. & Yahya, M. Z. A. Hubbard U calculations on optical properties of 3d transition metal oxide TiO2. Results Phys. 6, 891–896 (2016).

    ADS  Article  Google Scholar 

  58. 58.

    Olinto da Silva, G. & Martins, J. B. L. Effect of Hubbard parameter and semi-empirical van der Waals correction on benzene adsorption over anatase TiO2 (1 0 1) surface. Comput. Theor. Chem. 1164, 112552 (2019).

    CAS  Article  Google Scholar 

  59. 59.

    Arroyo-de Dompablo, M. E., Morales-García, A. & Taravillo, M. DFT+U calculations of crystal lattice, electronic structure, and phase stability under pressure of TiO2 polymorphs. J. Chem. Phys. 135, 054503 (2011).

    ADS  CAS  PubMed  Article  Google Scholar 

  60. 60.

    Hasegawa, M. & Yagi, T. Systematic study of formation and crystal structure of 3d-transition metal nitrides synthesized in a supercritical nitrogen fluid under 10 GPa and 1800K using diamond anvil cell and YAG laser heating. J. Alloy. Compd. 403, 131–142 (2005).

    CAS  Article  Google Scholar 

  61. 61.

    Banus, M. D., Reed, T. B. & Strauss, A. J. Electrical and magnetic properties of TiO and VO. Phys. Rev. B 5, 2775–2784 (1972).

    ADS  Article  Google Scholar 

  62. 62.

    Li, Y. & Tsang, S. C. E. Recent progress and strategies for enhancing photocatalytic water splitting. Mater. Today Sustain. 9, 100032 (2020).

    Article  Google Scholar 

  63. 63.

    Pinaud, B. A. et al. Technical and economic feasibility of centralized facilities for solar hydrogen production via photocatalysis and photoelectrochemistry. Energy Environ. Sci. 6, 1983–2002 (2013).

    CAS  Article  Google Scholar 

  64. 64.

    Lu, Y. et al. Effect of grid and optimization on improving the electrical performance of compound parabolic concentrator photovoltaic cells. Sol. Energy 196, 607–615 (2020).

    ADS  CAS  Article  Google Scholar 

  65. 65.

    Zhao, F. et al. Scale-up of a luminescent solar concentrator-based photomicroreactor via numbering-up. ACS Sustain. Chem. Eng. 6, 422–429 (2018).

    CAS  PubMed  Article  Google Scholar 

  66. 66.

    Blanco, J. et al. Compound parabolic concentrator technology development to commercial solar detoxification applications. Sol. Energy 67, 317–330 (1999).

    ADS  CAS  Article  Google Scholar 

  67. 67.

    Keane, D. A. et al. Solar photocatalysis for water disinfection: materials and reactor design. Catal. Sci. Technol. 4, 1211–1226 (2014).

    CAS  Article  Google Scholar 

  68. 68.

    Sacco, O., Vaiano, V. & Sannino, D. Main parameters influencing the design of photocatalytic reactors for wastewater treatment: a mini review. J. Chem. Technol. Biotechnol. 95, 2608–2618 (2020).

    CAS  Google Scholar 

  69. 69.

    Abdel-Maksoud, Y., Imam, E. & Ramadan, A. TiO2 solar photocatalytic reactor systems: selection of reactor design for scale-up and commercialization—analytical review. Catalysts 6, 138 (2016).

    Article  CAS  Google Scholar 

  70. 70.

    Li, J. et al. A full-sunlight-driven photocatalyst with super long-persistent energy storage ability. Sci. Rep. 3, 2409 (2013).

    PubMed  PubMed Central  Article  Google Scholar 

  71. 71.

    Thompson, S. P. et al. Beamline I11 at diamond: a new instrument for high resolution powder diffraction. Rev. Sci. Instrum. 80, 075107 (2009).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  72. 72.

    Arblaster, J. W. Crystallographic properties of platinum. Platin. Met. Rev. 41, 12 (1997).

    CAS  Google Scholar 

  73. 73.

    Kawaguchi, S. et al. High-throughput powder diffraction measurement system consisting of multiple MYTHEN detectors at beamline BL02B2 of SPring-8. Rev. Sci. Instrum. 88, 085111 (2017).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  74. 74.

    Coelho, A. A. TOPAS and TOPAS-Academic: an optimization program integrating computer algebra and crystallographic objects written in C++. J. Appl. Crystallogr. 51, 210–218 (2018).

    CAS  Article  Google Scholar 

  75. 75.

    Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).

    CAS  Article  Google Scholar 

  76. 76.

    Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    ADS  CAS  Article  Google Scholar 

  77. 77.

    Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  78. 78.

    Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).

    ADS  Article  Google Scholar 

  79. 79.

    Perdew, J. P. Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  Article  Google Scholar 

  80. 80.

    Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).

    ADS  MathSciNet  Article  Google Scholar 

Download references

Acknowledgements

The support for this project from the EPSRC in the United Kingdom (Grant EP/K040375/1) is gratefully acknowledged. We thank Qingming Deng of Huaiyin Normal University, China for the DFT calculations.

Author information

Affiliations

Authors

Contributions

C.F. prepared and characterised all Ti containing catalysts by XPS, EPR, and VT-SXPD and refinements. Y.L. performed photocatalytic experiments and analysed TRPL data. T.C. characterised the samples by electron microscopy. S.D. and C.T. assisted in VT-SXPD collected at both Diamond Light Source, UK and SPring-8, Japan. C.F., Y.L. and S.C.E.T. wrote the paper in discussion with S.D. and C.T. S.C.E.T. supervised the overall project.

Corresponding author

Correspondence to Shik Chi Edman Tsang.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Dorian Hanaor, Cecilia Morgade, and other, anonymous, reviewers for their contributions to the peer review of this work. Peer review reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Foo, C., Li, Y., Lebedev, K. et al. Characterisation of oxygen defects and nitrogen impurities in TiO2 photocatalysts using variable-temperature X-ray powder diffraction. Nat Commun 12, 661 (2021). https://doi.org/10.1038/s41467-021-20977-z

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing