Abstract
Perovskite light emitting diodes suffer from poor operational stability, exhibiting a rapid decay of external quantum efficiency within minutes to hours after turn-on. To address this issue, we explore surface treatment of perovskite films with phenylalkylammonium iodide molecules of varying alkyl chain lengths. Combining experimental characterization and theoretical modelling, we show that these molecules stabilize the perovskite through suppression of iodide ion migration. The stabilization effect is enhanced with increasing chain length due to the stronger binding of the molecules with the perovskite surface, as well as the increased steric hindrance to reconfiguration for accommodating ion migration. The passivation also reduces the surface defects, resulting in a high radiance and delayed roll-off of external quantum efficiency. Using the optimized passivation molecule, phenylpropylammonium iodide, we achieve devices with an efficiency of 17.5%, a radiance of 1282.8 W sr−1 m−2 and a record T50 half-lifetime of 130 h under 100 mA cm−2.
Similar content being viewed by others
Introduction
In the past few years, the technology of perovskite light emitting diodes (PeLEDs) has developed rapidly, exhibiting highly attractive properties such as high efficiency, high luminance and radiance, excellent color tunability and purity, etc.1,2,3,4,5. The rapid advancement of PeLEDs is partially owing to the extensive material design and processing experience gained from the perovskite solar cell research6. However, in addition to the stability issues present in solar cells, there are several unique challenges associated with PeLEDs, such as the imbalanced charge injection, shunts associated with the very thin film thickness, and the rapid degradation of electroluminescence during operation7,8,9. In particular, due to intrinsic defects10, ion migration11,12, a poor temperature tolerance13,14, and the film morphology15,16, most PeLEDs degrade quickly, within several minutes to several hours of operation/after turn-off, even under a low current density less than 10 mA cm−2 (ref. 17,18). Such poor operational stability is a major bottleneck for the commercialization of this technology.
Major research efforts have been made to improve the stability of PeLEDs. For instance, layered two-dimensional (2D) perovskites were incorporated in PeLEDs in consideration of their superior thermal and structural stability compared to the three-dimensional (3D) perovskites19,20. Although this strategy has led to a T50 (the time it takes for external quantum efficiency (EQE) to drop to half of its maximum) of 100 h under 25 mA cm−2 (ref. 20), the EQE of such devices is somewhat compromised due to the poor charge transport between the inorganic layers21,22. Moreover, due to the enlarged band gaps of the 2D perovskites, the emission wavelength of these LEDs cannot yet reach the infrared range. Mixed 2D/3D perovskites have also been introduced to improve the stability of PeLEDs while maintaining high device performance23,24, achieving an estimated T50 > 200 h under initial radiance of about 10 W sr−1 m−2. Recently, there have been a few studies aiming to directly enhance the stability of pure 3D PeLEDs. Li et al. provided direct experimental evidence for an ion-migration induced device degradation mechanism and demonstrated largely improved stability of 3D FAPbI3-based PeLEDs by simultaneous incorporation of Cs and Rb cations in the perovskite lattice11. Another approach is the passivation of the perovskite surface defects, by introducing additives in the precursor solution. For instance, Wang et. al. introduced trifluoroacetate anions in the precursor solution to passivate the surface defects of CsPbBr3 perovskite films and achieved a T50 of 250 h at a low luminance of 100 cd m−2 (ref. 25). Park et al. introduced an organic semiconducting additive (2,2ʹ,2″-(1,3,5-benzinetriyl)-tris(1-phenyl-1-H-benzimidazole), TPBi) in the precursor and proposed that a perovskite/organic core–shell structure is formed and accounts for the improvement of the stability26. Miao et al. introduced benzylamine in the precursor and achieved PeLEDs with a T50 of 23.7 h at a high current density of 100 mA cm−2 (ref. 27). In our previous study28, we found that the ion diffusion at the interface between the perovskite and its top neighboring organic hole-transporting layer plays a critical role in the degradation process of PeLEDs. It is worth noting that to date almost all surface passivation or ligand engineering research of PeLEDs focuses on defect passivation, instead of ion-blocking. And different from solar cells, the fabrication of the perovskite emissive layer in PeLEDs involves the use of largely excess organic halide salts, which induces additional sources of mobile ions in PeLEDs. More importantly, the electric-field across the very thin perovskite layer in a PeLED is much higher than that in a solar cell. Therefore, ion migration is a much more difficult challenge to address in the field of PeLEDs. Developing an effective surface passivation method to suppress the ion-migration and its subsequent device degradation is critical for improving the stability of 3D perovskite-based PeLEDs.
In this work, we explore the surface treatment of 3D perovskite films with phenylalkylammonium iodides. By systematically varying the alkyl chain length, we investigate how the steric and Coulomb interactions of the ammonium passivation molecules affect the stability and electronic properties of the perovskite films and devices. Combining X-ray photo-electron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), and theoretical modeling, we show that the phenylalkylammonium groups can stabilize the perovskite lattice through suppression of iodide ion migration. Very interestingly, the stabilization effect is enhanced with increasing chain length due to the stronger bonding of the passivating molecule to the perovskite surface and the increased steric hindrance for diffusion of iodide (I−) on the perovskite surface. With the optimized passivation molecule, phenylpropylammonium iodide (PPAI), we achieve a record T50 lifetime of 130 h under 100 mA cm−2, together with an EQE of 17.5% and a record radiance of 1282.8 W sr−1 m−2 on glass substrates.
Results
Passivation effects on films
We use FA0.83Cs0.17PbI3 as a model composition for 3D perovskites. After the formation of the perovskite film, a surface treatment by phenylalkylammonium iodide is applied by spin-coating of the iodide salt solution (in chloroform) on the perovskite film, followed by an annealing process to remove the solvent (see “Methods” for the detailed fabrication process). Figure 1a illustrates the schematic diagram of the phenylalkylammonium-passivated perovskite lattice. In order to understand how the steric and Coulomb interactions of the molecules affect the passivation results, we investigate four molecular cations with the same end groups but different alkyl chain lengths, namely phenylmethylammonium iodide (PMAI, n = 1), phenethylammonium iodide (PEAI, n = 2), PPAI (n = 3), and phenylbutanammonium iodide (PBAI, n = 4), as shown in Fig. 1b.
The presence of the passivation layer and its bonding to the perovskite lattice are confirmed by the contact angle measurement (Supplementary Fig. 1), which reveals an increasing contact angle as the chain length increases, and XPS. As shown in the XPS spectra (Fig. 1c, d), the binding energies corresponding to the I 3d and Pb 4d core levels of the passivated samples all slightly shift to higher values compared to the control sample, an indication of enhanced binding of the iodide and lead ions on the perovskite surface29. We also note that the shifts are more pronounced in the n = 3 and n = 4 samples. (The comparison between the I 3d spectra of the pure passivation molecules and the passivated perovskites (shown in Supplementary Fig. 2) confirms that high-energy shift of the passivated films originates from the interactions between the passivation molecules and the perovskite lattice rather than the passivation molecules themselves.) Apart from the surface interaction, the morphology of the perovskite films shows no obvious change after the surface treatment (Supplementary Fig. 3) which is different from the impact introduced by passivating polymers30. The X-ray diffraction (XRD) data also suggest that the treatment does not change the crystallinity or the lattice structure of the perovskite films (Supplementary Fig. 4). Accordingly, the UV–Vis absorption spectra of the perovskite films remain almost unchanged (Supplementary Fig. 5) after the treatment. It is worth noting that no XRD signals corresponding to 2D perovskite phases are observed, although we cannot exclude that there might be an ultrathin layer of 2D phase present at the 3D perovskite surface.
We then examine the electronic properties of the perovskite films before and after surface treatment by ultraviolet photoelectron spectroscopy (UPS) and photoluminescence (PL) measurements. The UPS result shown in Supplementary Fig. 6 suggests that the treatment slightly raises the energy levels of the perovskite by 0.1 eV–0.3 eV. The treatment also enhances the PL intensity of the perovskite films except for the n = 4 case (Fig. 1e). Through the time-resolved photoluminescence (TRPL) measurements (Fig. 1f and Supplementary Fig. 7), we observe a consistent trend that surface treatments by PMAI (n = 1), PEAI (n = 2), and PPAI (n = 3) all increase the carrier lifetime in the perovskite films while the treatment by PBAI (n = 4) shortens the carrier lifetime. (Note that the steady-state PL is performed with a lower excitation intensity compared to TRPL and therefore reveals a more pronounced difference among the samples.) The TRPL data can be well fitted assuming a combination of monomolecular recombination k1 (trap-assisted recombination), bimolecular recombination k2 (band-to-band recombination), and Auger recombination k3 (refs. 31,32) (fitting parameters shown in Supplementary Table 1). In general, the PL measurements suggest that (1) surface treatment by PMAI (n = 1), PEAI (n = 2), or PPAI (n = 3) can all reduce non-radiative recombination by passivating the surface defects of the perovskite films, corresponding to reduced k1 values and that (2) surface treatment by PBAI (n = 4) slightly suppresses PL, possibly due to a low anchoring density (i.e., the density of the molecules that are effectively bonded to the perovskite surface) of the passivation molecules and/or the treatment causing formation of new recombination centers that accelerate non-radiative recombination.
Passivation effects on devices
In order to examine the effect of the surface treatment on the PeLED performance, we fabricate PeLED devices with a structure of gold (Au)/molybdenum oxide (MoO3)/poly(9,9-dioctylflu-16orene-co-N-(4-butylphenyl)diphenylamine) (TFB)/passivation molecule-perovskite/polyethyleneimine (PEIE)/zinc oxide (ZnO)/indium tin oxide (ITO). In this structure, TFB works as the hole-transporting layer and PEIE-modified ZnO works as the electron-transporting layer. The performances of the devices with and without passivation are characterized and illustrated in Fig. 2. It can be seen that except for n = 4, all devices show similar peak EQE (Fig. 2a) and electroluminescence peak (Supplementary Fig. 8); however, the roll-off of the EQE in the passivated devices is much less severe than that of the untreated (control) device. For the PBAI (n = 4)-treated sample, a reduced EQE is observed, which is consistent with the PL measurement results.
In contrast to the moderate variation in EQE, the operational stability of the PeLEDs is changed drastically after the surface treatment. Figure 2d shows the EQE decay of the control and passivated devices during a stability test under a constant biasing current density of 100 mA cm−2. The stability of all passivated devices is substantially enhanced. It is also noted that the efficiency of the PeLEDs exhibits an initial rise before the prolonged decay process starts. This phenomenon is commonly observed in PeLEDs13,33,34,35,36 and is so far speculated to be related to ion migration36 or trap filling/defect annihilation37. Note that the time scale of this initial rise is much longer than the step size of the EQE measurements; therefore this rise behavior does not affect the accuracy of the EQE measurements. More importantly, the enhancement of the operation lifetime depends highly on the value of n. The underlying mechanism for such strong chain length-dependence will be discussed in the next section.
Based on our overall evaluation of the device performance and stability, we propose PPAI (n = 3) as the optimal passivation molecule, among the ones studied here. The champion device with the PPAI treatment exhibits a peak EQE of 17.5%, a record high radiance of 1282.8 W sr−1 m−2 achieved on glass substrates (Fig. 2a–c). The histogram of the peak EQE based on 50 individual devices is shown in Fig. 2e, suggesting an average EQE of 15.87%. A long-term stability test under a constant current density of 100 mA cm−2 suggests a remarkable T50 lifetime of 130 h at high brightness (Fig. 2e). Table 1 provides a detailed comparison on the stability and performances of our device and other state-of-the-art PeLEDs with either high brightness or good stability. It can be seen that the PPAI-treated device represents the most stable high-radiance PeLEDs reported to date.
Mechanism of stability improvement
Based on the stability behavior, in the following, we categorize the devices into three groups: (1) untreated, (2) treated with a short alkyl chain ammonium (n = 1 and n = 2), and (3) treated with a long alkyl chain ammonium (n = 3 and n = 4). We focus on the comparison of the control, n = 1 (representing Group 2), and n = 3 (representing Group 3) samples to investigate the mechanism of the surface treatment-induced stability enhancement.
As ion migration is found to be a major cause of degradation for PeLEDs38,39, we first perform ToF-SIMS to examine the ion distribution in the devices before and after bias stressing (stress current density: 100 mA cm−2; stress time: 16 h). In the control sample (Fig. 3a and Supplementary Fig. 9a), a clear accumulation of iodide ions close to gold is found after bias stressing, revealing severe iodide ion migration during device operation. Such behavior is partially suppressed in the PMAI (n = 1)-treated device (Fig. 3b and Supplementary Fig. 9b), while for the PPAI (n = 3)-treated device, we observe a complete suppression of this behavior, with the fresh and aged devices showing almost identical iodide distribution profiles (Fig. 3c and Supplementary Fig. 9c).
Our ToF-SIMS results suggest that the length of the alkyl chain plays an important role in blocking the ion migration. In order to gain an atomistic insight, we perform density functional theory (DFT) calculations to investigate the interactions between the passivation molecules (with alkyl chain n = 1–4) and the perovskite surface. First, we determine the adsorption geometry of phenylalkylammonium iodide passivation molecules with alkyl chain lengths from n = 1 to n = 4. We use the most stable Pb–I terminated perovskite surface and then investigate three different adsorption geometries for each molecule (Supplementary Fig. 10). We conclude that in all cases the most favorable geometry is similar to those depicted in Fig. 4b (the left row). Specifically, the iodide anion adsorbs on top of Pb, while the NH3 group of the molecular cations points to the corner Pb atom and forms hydrogen bonds with the surface iodide ions. The alkyl chain extends in the direction normal to the perovskite surface with the benzene ring pointing out of plane.
Having determined the adsorption geometry, we proceed with calculating the binding energy of the passivation molecules with alkyl chain n = 1–4 on the perovskite surface. The binding energy Eb, calculated as Eb = | EFAPbI3 + Emol – Emol/FAPbI3 | (1), is shown in Fig. 4a. We note that the formamidinium iodide (FAI)-terminated perovskite surface is also studied, where FAI binds to a Pb–I surface and we use this as a reference (n = 0). For all the examined values of n, the adsorption of the corresponding molecules on the perovskite surface is favorable, with binding energies ranging from 2.12 to 2.39 eV, considerably larger than the 1.92 eV of FAI (n = 0). Moreover, it is evident that the binding energy increases with increasing n, which indicates a stronger interaction between the larger molecules and the perovskite. The trend agrees well with the XPS results. This observation is further validated by the sum of bond orders, between the molecules and the perovskite (Fig. 4a). From Supplementary Table 2, we can conclude that the main difference in the binding strength comes from the hydrogen bonds between the NH3 group and I− ions. With increasing n, the bond order of these H–I bonds increases (with the rest being almost constant), which geometrically is demonstrated by shorter H–I bond length (left column in Fig. 4b).
Next, we study the role of the passivation molecules in suppressing the iodide migration. We built an iodide diffusion pathway by moving one iodide ion away, step-by-step, from the perovskite surface. Figure 4c summarizes the relative energies of all configurations along the iodide diffusion path for each molecule (n = 0–4), and Fig. 4b shows the corresponding molecular configurations for n = 0, n = 1, and n = 3. The energy landscapes clearly show that larger molecules make the extraction of I− from the perovskite surface much more difficult. Careful investigation of the positions of the species near the moving I− (Fig. 4b) reveals an interesting effect: the NH3 group tends to move along with the migrating I− because of the strong hydrogen bond formed between the two (I–H). This is especially evident in the case of a moderate displacement of I−, e.g. at 3 Å. However, molecules with shorter chains (n = 0 or n = 1) are much easier to rotate due to smaller steric hindrance, and they can more easily reposition after the extraction of an I− ion, as can be confirmed with the newly formed hydrogen bonds between the molecules and I− at relatively short distances of less than 2.7 Å (Supplementary Fig. 11). The repositioning leads to (new) lowest energy states. It is worth noting that the enhanced hydrogen bond between the NH3 group of the passivation molecules and the I− ion subsequently pulled the I− ion to a closer distance to the surface Pb ion. From the calculation results shown in Fig. 4b and Supplementary Table 3, one can see that the Pb–I bond is shortened from 3.17 Å (for an unpassivated surface) to 3.07 Å (for a passivated surface). Accordingly the bond order is increased from 0.46 to 0.53 (Supplementary Table 4), suggesting a stronger Pb–I bond. This observation agrees well with the XPS results, where simultaneous shifts to higher energy values were found for the core levels of both I and Pb. In contrast, such repositioning is not feasible for larger molecules due to a larger steric hindrance; therefore, they retain a similar position before and after the extraction of I−. This effect becomes more dominant when I− is placed further away from the surface, i.e. at 5 Å (as can be seen in the configurations without hydrogen bonds in Supplementary Fig. 11), leading to the largest energy for the longest molecule.
Altogether, our analysis indicates a strong binding of the passivation molecules and the perovskite surface via enhanced hydrogen bonds, and the layer of molecules acting as passivation agent to prevent the diffusion of the surface I−. More importantly, the strength of such passivation largely depends on the alkyl chain length: the longer the chain length, the larger the steric hindrance and thus the stronger the resistance to rotation and reposition to accommodate the migrating I− ions. These results agree well with our experimental observation that the PPAI (n = 3) treatment is much more effective than the PMAI (n = 1) treatment in suppressing the iodide migration.
Discussion
In summary, we explored surface passivation of 3D perovskite films with a series of phenylalkylammonium iodides of varying alkyl chain lengths. Combining experimental characterization and theoretical modeling, we show that the phenylalkylammonium groups can stabilize the perovskite surface through the suppression of iodide ion migration. More importantly, the stabilization effect is enhanced with increasing alkyl chain length, due to the stronger binding of the passivating molecule on the perovskite surface and the increased steric hindrance to reconfiguration required to accommodate I− migration. Using the optimized passivation molecule, PPAI, we achieve PeLEDs with an EQE of 17.5%, a record radiance of 1282.8 W sr−1 m−2 on glass substrates, and a record T50 half-lifetime of 130 h under 100 mA cm−2. Our work highlights the importance of the chain length effect in suppressing the ion migration, revealing that a very small variation in the surface molecular structure can result in a remarkable improvement in device stability and sheds light on the design of new passivation molecules that could render highly efficient and stable perovskite LEDs.
Methods
Materials
Cesium iodide (CsI), FAI, and 5-ammonium valeric acid iodide (5AVAI) were purchased from Greatcellsolar. Lead iodide (PbI2) and PEAI (2-phenethylammonium iodide) were purchased from Tokyo Chemical Industry Co. LTD. PMAI, PPAI, and PBAI were bought from Xi’an Polymer Light Technology Corp. ZnO nanocrystals were synthesized according to the published recipe40. The other chemicals were purchased from Sigma-Aldrich.
Device fabrication
ITO substrate was cleaned in Hellmanex water solution by sonication for 30 min, and subsequently cleaned with deionized water, acetone, isopropanol in sequence by sonication for 15 min, and treated by UV-Ozone for 15 min before use. Then, the ZnO layer was spun on the substrate at 6000 r.p.m. for 40 s and annealed at 150 °C for 30 min. PEIE (3.9 mg mL−1 in 2-methoxyethanol) layer was spun on ZnO at 5000 r.p.m. for 40 s and annealed at 90 °C for 10 min to modify the work function of ZnO and enhance the wettability. Then a 0.15 mmol mL−1 perovskite precursor (n(CsI):n(FAI):n(PbI2):n(Pb(SCN)2):n(5AVAI)) = 0.17:1.23:0.8:0.2:0.1) was spun on the substrates at 500 r.p.m. for 3 s and 8000 r.p.m. for 45 s, respectively. The 120 μL chlorobenzene was dripped on the substrate after 16 s, and then the film was annealed at 100 °C for 15 min. For the surface treatment, 0.5 mg molecules were added in 1 mL chloroform and the solution was filtered before diluting the solution with threefold chloroform. Then the solution was deposited at 6000 r.p.m. for 30 s on the perovskite films and the treated film was annealed at 100 °C for 3 min to volatilize remnant solvent. After cooling down to room temperature, the TFB (15 mg mL−1 in m-xylene) layer was spun on perovskite layer at 2500 r.p.m. for 30 s. Finally, 7 nm of MoO3 and 50 nm of Au were evaporated on the top by thermal evaporator through a shadow mask defining an electrode area of 2.25 mm2.
Characterization
The XRD was tested with a Rigaku ru-300 diffractometer (Cu Kα irradiation, λ = 1.5406 Å). The SEM test was performed by HR-FESEM, FEI, Quanta 400. The XPS was conducted by Al Kα X-ray gun (hv = 1486.6 eV) with a VG ESCALAB 220i-XL surface analysis system. For the characterization of device performance, the J–V curves, radiance, and EQE were all carried out in nitrogen-filled glovebox through a QE-Pro spectrometer coupled with a fiber integration sphere (FOIS-1) and a Keithley 2400 source meter. The TRPL was taken on an Edinburgh Instruments spectrometer (FLS1000) with a 405-nm pulsed laser (75 ps, 0.5 MHz). The instrument resolution was less than 20 ps with the response function (IRF) less than 130 ps. And the tested perovskite films were fabricated on the ZnO/PEIE substrate. The ToF-SIMS test was taken on Model TOF‐SIMS 5 with the pulsed primary ions of a Bi+ (30 keV, 1 pA) ion gun for the sputtering and an O+ pulsed secondary ion beam for the analysis (0.5 keV, 100 nA) with an analysis area of 96 µm × 96 µm. The stability test was taken on the EQE test platform and calibrated by commercialization system made by Guangzhou Jinghe Ltd.
First-principles calculation
DFT calculations were performed using the Projector Augmented Wave (PAW) method as implemented in the Vienna Ab-Initio Simulation Package (VASP)41,42,43,44. The electronic exchange-correlation interaction was described by the functional of Perdew, Burke, and Ernzerhof (PBE) within the spin-polarized generalized gradient approximation (GGA)45. Energy and force convergence criteria of 10−5 eV and 10−1 eV Å−1, respectively, were used in all calculations. The D3 correction46 was employed to account for the van der Waals interactions due to the presence of the organic molecules.
For the geometry optimization and the calculation of the binding energies and the bond orders, 9-layer Pb–I-terminated FAPbI3 slabs were used (cubic unit cell with a fixed lattice parameter of a = 6.36 Å) and a vacuum region of ~30 Å separating the slabs. To model the passivation effect of the molecules, CH5(CH2)nNH3I molecules were put on top of the above-mentioned Pb–I-terminated slab. The calculations were performed with a 3 × 3 × 1 Γ-centered k-point grid and a kinetic energy cutoff of 500 eV. A dipole correction was employed to avoid interaction between periodic images47. During the geometry optimization, all the atoms were allowed to relax in a fixed cell.
The binding energies Eb of the passivation molecules on FAPbI3 were calculated as:
where Emol/FAPbI3, EFAPbI3, and Emol are the total energies of FAPbI3 with an adsorbed passivation molecule per surface unit cell, the clean FAPbI3 surface, and the CH5(CH2)nNH3I, respectively. For the calculation of the bond orders, the density-derived electrostatic and chemical (DDEC6) method was used48,49,50. The bond order is a measure of the strength of a covalent bond, where larger the bond order corresponds to stronger bond.
In order to study the effect of the passivation molecules on the migration of I ions, 2 × 2 supercells of the 9-layer slabs were used and optimized by using one k-point (Γ point). To determine the energies of several configurations with a migrating I ion, the top two layers of the FAPbI3 slab could relax, while the bottom seven layers and the position of the “migrating” I ions were fixed.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
References
Song, J. et al. Quantum dot light-emitting diodes based on inorganic perovskite cesium lead halides (CsPbX3). Adv. Mater. 27, 7162–7167 (2015).
Kovalenko, M. V., Protesescu, L. & Bodnarchuk, M. I. Properties and potential optoelectronic applications of lead halide perovskite nanocrystals. Science 358, 745–750 (2017).
Akkerman, Q. A., Rainò, G., Kovalenko, M. V. & Manna, L. Genesis, challenges and opportunities for colloidal lead halide perovskite nanocrystals. Nat. Mater. 17, 394–405 (2018).
Yu, J. C. et al. Effect of the solvent used for fabrication of perovskite films by solvent dropping on performance of perovskite light-emitting diodes. Nanoscale 9, 2088–2094 (2017).
Kim, Y. H. et al. Multicolored organic/inorganic hybrid perovskite light-emitting diodes. Adv. Mater. 27, 1248–1254 (2015).
Kim, H. B. et al. Peroptronic devices: perovskite-based light-emitting solar cells. Energy Environ. Sci. 10, 1950–1957 (2017).
Zhang, L. et al. Ultra-bright and highly efficient inorganic based perovskite light-emitting diodes. Nat. Commun. 8, 1–8 (2017).
Zhang, X. et al. Thin film perovskite light-emitting diode based on CsPbBr3 powders and interfacial engineering. Nano Energy 37, 40–45 (2017).
Prakasam, V., Tordera, D., Bolink, H. J. & Gelinck, G. Degradation mechanisms in organic lead halide perovskite light-emitting diodes. Adv. Opt. Mater. 7, 1–7 (2019).
Huang, Y., Yin, W. J. & He, Y. Intrinsic point defects in inorganic cesium lead iodide perovskite CsPbI3. J. Phys. Chem. C 122, 1345–1350 (2018).
Li, N. et al. Stabilizing perovskite light-emitting diodes by incorporation of binary alkali cations. Adv. Mater. 32, 1907786 (2020).
Wang, Q. et al. Efficient sky-blue perovskite light-emitting diodes via photoluminescence enhancement. Nat. Commun. 10, 5633 (2019).
Zou, C., Liu, Y., Ginger, D. S. & Lin, L. Y. Suppressing efficiency roll-off at high current densities for ultra-bright green perovskite light-emitting diodes. ACS Nano 14, 6076–6086 (2020).
Zhao, L., Lee, K. M., Roh, K., Khan, S. U. Z. & Rand, B. P. Improved outcoupling efficiency and stability of perovskite light-emitting diodes using thin emitting layers. Adv. Mater. 31, 1–6 (2019).
Zou, Y. et al. Boosting perovskite light-emitting diode performance via tailoring interfacial contact. ACS Appl. Mater. Interfaces 10, 24320–24326 (2018).
Ma, D. et al. Chloride insertion-immobilization enables bright, narrowband, and stable blue-emitting perovskite diodes. J. Am. Chem. Soc. 142, 5126–5134 (2020).
Tan, Y. et al. Highly luminescent and stable perovskite nanocrystals with octylphosphonic acid as a ligand for efficient light-emitting diodes. ACS Appl. Mater. Interfaces 10, 3784–3792 (2018).
Shi, Y. et al. Rubidium doping for enhanced performance of highly efficient formamidinium-based perovskite light-emitting diodes. ACS Appl. Mater. Interfaces 10, 9849–9857 (2018).
Deng, W. et al. 2D Ruddlesden–Popper perovskite nanoplate based deep-blue light-emitting diodes for light communication. Adv. Funct. Mater. 29, 1–9 (2019).
Shang, Y. et al. Highly stable hybrid perovskite light-emitting diodes based on Dion-Jacobson structure. Sci. Adv. 5, eaaw8072 (2019).
Abbas, M. S. et al. Orientationally engineered 2D/3D perovskite for high efficiency solar cells. Sustain. Energy Fuels 4, 324–330 (2019).
Wang, Z. et al. Efficient ambient-air-stable solar cells with 2D-3D heterostructured butylammonium-caesium-formamidinium lead halide perovskites. Nat. Energy 2, 1–10 (2017).
Han, T. H. et al. Surface-2D/Bulk-3D heterophased perovskite nanograins for long-term-stable light-emitting diodes. Adv. Mater. 32, 1–10 (2020).
Li, C. et al. Understanding the improvement in the stability of a self-assembled multiple-quantum well perovskite light-emitting diode. J. Phys. Chem. Lett. 10, 6857–6864 (2019).
Wang, H. et al. Trifluoroacetate induced small-grained CsPbBr3 perovskite films result in efficient and stable light-emitting devices. Nat. Commun. 10, 665 (2019).
Park, M. H. et al. Efficient perovskite light-emitting diodes using polycrystalline core–shell-mimicked nanograins. Adv. Funct. Mater. 29, 1–9 (2019).
Miao, Y. et al. Stable and bright formamidinium-based perovskite light-emitting diodes with high energy conversion efficiency. Nat. Commun. 10, 1–7 (2019).
Guo, Y. et al. Degradation mechanism of perovskite light-emitting diodes: an in situ investigation via electroabsorption spectroscopy and device modelling. Adv. Funct. Mater. 30, 1–8 (2020).
Wang, H. et al. Molecule-induced p-doping in perovskite nanocrystals enables efficient color-saturated red light-emitting diodes. Small 16, 1–7 (2020).
Zhao, B. et al. High-efficiency perovskite–polymer bulk heterostructure light-emitting diodes. Nat. Photonics 12, 783–789 (2018).
Droseros, N. et al. Origin of the enhanced photoluminescence quantum yield in MAPbBr3 perovskite with reduced crystal size. ACS Energy Lett. 3, 1458–1466 (2018).
Xing, G. et al. Transcending the slow bimolecular recombination in lead-halide perovskites for electroluminescence. Nat. Commun. 8, 14558 (2017).
Cao, Y. et al. Perovskite light-emitting diodes based on spontaneously formed submicrometre-scale structures. Nature 562, 249–253 (2018).
Wang, H. et al. Perovskite-molecule composite thin films for efficient and stable light-emitting diodes. Nat. Commun. 11, 1–9 (2020).
Lin, K. et al. Perovskite light-emitting diodes with external quantum efficiency exceeding 20 per cent. Nature 562, 245–248 (2018).
Fang, T. et al. Perovskite QLED with an external quantum efficiency of over 21% by modulating electronic transport. Sci. Bull. 66, 36–43 (2020).
Zhong, Y., Luna, C. A. M., Hildner, R., Li, C. & Huettner, S. In situ investigation of light soaking in organolead halide perovskite films. APL Mater. 7, 041114 (2019).
Chen, M., Shan, X., Geske, T., Li, J. & Yu, Z. Manipulating ion migration for highly stable light-emitting diodes with single-crystalline organometal halide perovskite microplatelets. ACS Nano 11, 6312–6318 (2017).
Li, C. et al. Real-time observation of iodide ion migration in methylammonium lead halide perovskites. Small 13, 1–10 (2017).
Wang, J. et al. Interfacial control toward efficient and low-voltage perovskite light-emitting diodes. Adv. Mater. 27, 2311–2316 (2015).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B Condens. Matter Mater. Phys. 54, 11169–11186 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Neugebauer, J. & Scheffler, M. Adsorbate-substrate and adsorbate-adsorbate interactions of Na and K adlayers on Al(111). Phys. Rev. B 46, 16067–16080 (1992).
Manz, T. A. & Limas, N. G. Introducing DDEC6 atomic population analysis: part 1. Charge partitioning theory and methodology. RSC Adv. 6, 47771–47801 (2016).
Limas, N. G. & Manz, T. A. Introducing DDEC6 atomic population analysis: part 2. Computed results for a wide range of periodic and nonperiodic materials. RSC Adv. 6, 45727–45747 (2016).
Manz, T. A. Introducing DDEC6 atomic population analysis: part 3. Comprehensive method to compute bond orders. RSC Adv. 7, 45552–45581 (2017).
Yuan, Z. et al. Unveiling the synergistic effect of precursor stoichiometry and interfacial reactions for perovskite light-emitting diodes. Nat. Commun. 10, 1–9 (2019).
Xu, W. et al. Rational molecular passivation for high-performance perovskite light-emitting diodes. Nat. Photonics 13, 418–424 (2019).
Yusoff, A. R. B. M. et al. High-efficiency, solution-processable, multilayer triple cation perovskite light-emitting diodes with copper sulfide–gallium–tin oxide hole transport layer and aluminum-zinc oxide–doped cesium electron injection layer. Mater. Today Chem. 10, 104–111 (2018).
Cheng, G. et al. Efficient all-inorganic perovskite light-emitting diodes with improved operation stability. ACS Appl. Mater. Interfaces 12, 18084–18090 (2020).
Fang, Z. et al. Dual passivation of perovskite defects for light-emitting diodes with external quantum efficiency exceeding 20%. Adv. Funct. Mater. 30, 1–9 (2020).
Acknowledgements
This work was supported by the General Research Fund (RGC Ref No. 14307819) and NSFC/RGC Joint Research Scheme (Ref No. N_CUHK449/19) from the Research Grants Council of Hong Kong. The work done in the Netherlands was supported by funding from NWO START-UP and Computational Sciences for Energy Research (CSER) tenure track program of Shell and NWO (Project No. 15CST04-2). We would like to thank Mr. Xingwei Zeng, Ms. Mengna Zhao, Ms. Yujing Wang, and Prof. Qian Miao for their helpful suggestions regarding material characterizations and Mr. Shirong Qiu for his help in time-resolved photoluminescence analysis.
Author information
Authors and Affiliations
Contributions
Y.G. and S.A. contributed equally to this work. N.Z. and S.T. supervised the execution of the project. Y.G. and N.Z. designed the experiments. Y.G. fabricated the devices and performed the characterization of PeLEDs. S.A., G.B., and S.T. conducted the density functional theory (DFT) calculations. N.L. and M.C. helped in the designing of surface treatment and device fabrication protocol. C.Y., Z.Y., and F.G. contributed to the TRPL measurement and analysis. F.X. carried out the UPS and XPS measurements and analysis. All authors participated in the discussions for manuscript preparation.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Stefano Bellucci, Dawei Di and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Guo, Y., Apergi, S., Li, N. et al. Phenylalkylammonium passivation enables perovskite light emitting diodes with record high-radiance operational lifetime: the chain length matters. Nat Commun 12, 644 (2021). https://doi.org/10.1038/s41467-021-20970-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-20970-6
This article is cited by
-
Switchable interfacial reaction enables bright and stable deep-red perovskite light-emitting diodes
Nature Photonics (2024)
-
Redox mediator-stabilized wide-bandgap perovskites for monolithic perovskite-organic tandem solar cells
Nature Energy (2024)
-
Vapour-deposited perovskite light-emitting diodes
Nature Reviews Materials (2024)
-
Luminescent metal-halide perovskites: fundamentals, synthesis, and light-emitting devices
Science China Chemistry (2024)
-
Lattice reconstruction for mixed-halide blue perovskite light-emitting diodes with high brightness, outstanding color stability and low efficiency roll-off
Science China Materials (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.